MX2016002449A - Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma. - Google Patents
Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.Info
- Publication number
- MX2016002449A MX2016002449A MX2016002449A MX2016002449A MX2016002449A MX 2016002449 A MX2016002449 A MX 2016002449A MX 2016002449 A MX2016002449 A MX 2016002449A MX 2016002449 A MX2016002449 A MX 2016002449A MX 2016002449 A MX2016002449 A MX 2016002449A
- Authority
- MX
- Mexico
- Prior art keywords
- steel sheet
- strength hot
- dip galvanized
- galvanized steel
- imn
- Prior art date
Abstract
Un objetivo de la invención es proporcionar una lámina de acero galvanizada de alta resistencia con base en una lámina de acero que contiene Si y Mn y que tiene un excelente aspecto de superficie sin defectos de puntos pelados o ampolladuras, y proporcionar un método para la fabricación de tal lámina de acero. La lámina de acero galvanizada de alta resistencia incluye una lámina de acero base que tiene una composición química específica y una capa de recubrimiento de zinc dispuesta sobre la superficie de la lámina de acero base en un peso de recubrimiento por cada lado de 20 g/m2 a 120 g/m2, en donde la cantidad de hidrógeno medido mediante un método específico es de 0.05 ppm en masa a 0.40 ppm en masa; ISi sur/ISi sur /Si flotación e IMn sur/IMn flotación calculadas mediante un método específico son de no más de 2.0 y no más de 3.0, respectivamente.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2013174197 | 2013-08-26 | ||
PCT/JP2014/004338 WO2015029404A1 (ja) | 2013-08-26 | 2014-08-22 | 高強度溶融亜鉛めっき鋼板及びその製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2016002449A true MX2016002449A (es) | 2016-06-24 |
Family
ID=52585994
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2016002449A MX2016002449A (es) | 2013-08-26 | 2014-08-22 | Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma. |
Country Status (7)
Country | Link |
---|---|
US (1) | US9895863B2 (es) |
EP (1) | EP3040440B1 (es) |
JP (1) | JP6128223B2 (es) |
KR (1) | KR101824823B1 (es) |
CN (1) | CN105531388A (es) |
MX (1) | MX2016002449A (es) |
WO (1) | WO2015029404A1 (es) |
Families Citing this family (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN106756555A (zh) * | 2016-12-19 | 2017-05-31 | 武汉钢铁股份有限公司 | 一种屈服强度为160MPa级的铁‑锌镀层钢板及生产方法 |
JP6323617B1 (ja) * | 2017-02-10 | 2018-05-16 | Jfeスチール株式会社 | 高強度亜鉛めっき鋼板及びその製造方法 |
EP3550050B1 (en) * | 2017-02-10 | 2021-07-28 | JFE Steel Corporation | High strength galvanized steel sheet and production method therefor |
US11492677B2 (en) | 2017-12-27 | 2022-11-08 | Jfe Steel Corporation | High-strength steel sheet and method for producing the same |
CN111601906B (zh) * | 2018-01-17 | 2022-05-31 | 杰富意钢铁株式会社 | 高强度合金化电镀锌钢板及其制造方法 |
CN111936648B (zh) * | 2018-03-30 | 2021-11-02 | 杰富意钢铁株式会社 | 高强度镀锌钢板、高强度部件及其制造方法 |
US11795531B2 (en) | 2018-03-30 | 2023-10-24 | Jfe Steel Corporation | High-strength galvanized steel sheet, high strength member, and method for manufacturing the same |
WO2019189849A1 (ja) * | 2018-03-30 | 2019-10-03 | Jfeスチール株式会社 | 高強度亜鉛めっき鋼板、高強度部材およびそれらの製造方法 |
CN111936649B (zh) | 2018-03-30 | 2022-05-03 | 杰富意钢铁株式会社 | 高强度镀锌钢板、高强度部件和它们的制造方法 |
TW201945559A (zh) * | 2018-05-01 | 2019-12-01 | 日商日本製鐵股份有限公司 | 鋅系鍍敷鋼板及其製造方法 |
CN112041475B (zh) | 2018-05-01 | 2021-09-17 | 日本制铁株式会社 | 镀锌钢板及其制造方法 |
WO2020170542A1 (ja) * | 2019-02-22 | 2020-08-27 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
MX2023000705A (es) * | 2020-07-14 | 2023-02-14 | Jfe Steel Corp | Metodo de deshidrogenacion para material de acero y producto de acero, y metodo de produccion para material de acero y producto de acero. |
KR102461161B1 (ko) * | 2020-12-13 | 2022-11-02 | 주식회사 포스코 | 도금품질이 우수한 고강도 용융아연도금강판, 도금용 강판 및 이들의 제조방법 |
KR102493977B1 (ko) * | 2020-12-13 | 2023-01-31 | 주식회사 포스코 | 도금품질이 우수한 고강도 용융아연도금강판, 도금용 강판 및 이들의 제조방법 |
CN113265512B (zh) * | 2021-05-17 | 2022-08-12 | 山西太钢不锈钢股份有限公司 | 一种消除电渣马氏体锻圆机加工表面色差的方法 |
DE102022104228A1 (de) | 2022-02-23 | 2023-08-24 | Thyssenkrupp Steel Europe Ag | Verfahren zur Herstellung eines kaltgewalzten Stahlflachprodukts mit niedrigem Kohlenstoffgehalt |
KR20230161661A (ko) * | 2022-05-19 | 2023-11-28 | 현대제철 주식회사 | 용접성이 우수한 초고강도 아연도금강판 및 그 제조방법 |
Family Cites Families (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS54130443A (en) * | 1978-03-31 | 1979-10-09 | Sumitomo Metal Ind Ltd | Manufacture of zinc plated steel sheet |
JPH02267251A (ja) * | 1989-04-07 | 1990-11-01 | Nkk Corp | 気泡状電着塗膜欠陥発生を防止可能とした塗装適合性に優れた高耐食性複層めっき鋼板 |
CA2030812A1 (en) | 1989-04-07 | 1990-10-08 | Hiroshi Miwa | High corrosion resistant multi-layer coated steel sheets having excellent paintability by enabling the prevention of occurrence of bubble-like ed paint defects, and producing method thereof |
JPH0713285B2 (ja) * | 1990-04-25 | 1995-02-15 | 新日本製鐵株式会社 | 加工性に優れた溶融合金化亜鉛めっき鋼板 |
JPH05295483A (ja) * | 1992-04-23 | 1993-11-09 | Kawasaki Steel Corp | 耐ブリスター性に優れた溶融亜鉛めっき鋼板 |
JP3403859B2 (ja) * | 1995-04-26 | 2003-05-06 | 帝人株式会社 | 離型フイルム |
JP3403869B2 (ja) * | 1995-06-27 | 2003-05-06 | 日新製鋼株式会社 | ブリスターのない溶融Znめっき熱延鋼板の製造方法 |
JPH09118968A (ja) * | 1995-10-24 | 1997-05-06 | Nisshin Steel Co Ltd | ブリスターの発生しない溶融亜鉛めっき熱延鋼板 |
JP3211695B2 (ja) * | 1997-01-16 | 2001-09-25 | 日本鋼管株式会社 | めっきふくれのない溶融亜鉛めっき熱延鋼板 |
US6398884B1 (en) | 1999-02-25 | 2002-06-04 | Kawasaki Steel Corporation | Methods of producing steel plate, hot-dip steel plate and alloyed hot-dip steel plate |
JP3835083B2 (ja) | 1999-02-25 | 2006-10-18 | Jfeスチール株式会社 | 冷延鋼板および溶融めっき鋼板ならびにそれらの製造方法 |
JP4500124B2 (ja) * | 2004-07-23 | 2010-07-14 | 新日本製鐵株式会社 | ホットプレス用めっき鋼板の製造方法 |
JP5040093B2 (ja) * | 2004-10-07 | 2012-10-03 | Jfeスチール株式会社 | 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板 |
JP5000367B2 (ja) * | 2007-04-13 | 2012-08-15 | 新日本製鐵株式会社 | 耐水素脆化特性に優れた高強度亜鉛めっきボルト |
WO2010114142A1 (ja) * | 2009-03-31 | 2010-10-07 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5593771B2 (ja) | 2009-03-31 | 2014-09-24 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
JP5552864B2 (ja) | 2009-03-31 | 2014-07-16 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
KR101250101B1 (ko) | 2010-03-10 | 2013-04-03 | 제이에프이 스틸 가부시키가이샤 | 강의 연속 주조 방법 및 강판의 제조 방법 |
BR112014007483B1 (pt) * | 2011-09-30 | 2019-12-31 | Nippon Steel & Sumitomo Metal Corp | chapa de aço galvanizado a quente e processo de fabricação da mesma |
JP5799819B2 (ja) * | 2012-01-13 | 2015-10-28 | 新日鐵住金株式会社 | めっき濡れ性及び耐ピックアップ性に優れる溶融亜鉛めっき鋼板の製造方法 |
-
2014
- 2014-08-22 WO PCT/JP2014/004338 patent/WO2015029404A1/ja active Application Filing
- 2014-08-22 MX MX2016002449A patent/MX2016002449A/es unknown
- 2014-08-22 KR KR1020167007924A patent/KR101824823B1/ko active IP Right Grant
- 2014-08-22 EP EP14840002.1A patent/EP3040440B1/en active Active
- 2014-08-22 JP JP2015533985A patent/JP6128223B2/ja active Active
- 2014-08-22 US US14/914,803 patent/US9895863B2/en active Active
- 2014-08-22 CN CN201480047552.6A patent/CN105531388A/zh active Pending
Also Published As
Publication number | Publication date |
---|---|
KR101824823B1 (ko) | 2018-02-01 |
KR20160048882A (ko) | 2016-05-04 |
US20160214351A1 (en) | 2016-07-28 |
CN105531388A (zh) | 2016-04-27 |
EP3040440B1 (en) | 2019-03-06 |
EP3040440A4 (en) | 2016-08-17 |
JP6128223B2 (ja) | 2017-05-17 |
EP3040440A1 (en) | 2016-07-06 |
US9895863B2 (en) | 2018-02-20 |
JPWO2015029404A1 (ja) | 2017-03-02 |
WO2015029404A1 (ja) | 2015-03-05 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2016002449A (es) | Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma. | |
TR201904325T4 (tr) | Sıcak baskıda kullanım için alaşımlı sıcak daldırma galvanize çelik levha ve çelik parça üretimi için yöntem. | |
IN2014DN07662A (es) | ||
MX2015004736A (es) | Lamina de acero galvanizada por inmersion en caliente aleada y metodo para manufacturar la misma. | |
BR112014007509A2 (pt) | folha de aço fornecida com camada galvanizada por imersão a quente excelente em umectabilidade de galvanização e adesão de galvanização e método de produção da mesma | |
MY168717A (en) | Method for manufacturing hot-pressed members | |
MY156310A (en) | Surface-treated steel sheet and method of manufacturing the same | |
MY166781A (en) | High-corrosion-resistance hot-dip galvanized steel sheet having excellent appearance uniformity and manufacturing method thereof | |
EP2798094A4 (en) | HIGH-FIXED FIRE-GRAINED STEEL PLATE WITH EXCELLENT PLATING SURFACE QUALITY AND LIABILITY AND MANUFACTURING METHOD THEREFOR | |
MY160991A (en) | Hot-dip galvanized steel sheet and method for producing the same | |
MX2015001687A (es) | Plancha de acero chapada con zinc para moldeo a presion en caliente. | |
MX355496B (es) | Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas. | |
MX2014006508A (es) | Composicion de revestimiento para una lata de alimentos o bebidas. | |
MX2017005503A (es) | Hoja de acero galvanizada por inmersion en caliente. | |
SG11201908425UA (en) | Coated steel sheet | |
MX344265B (es) | Lámina de acero magnetico con recubrimiento de aislante semi-organico. | |
MY170554A (en) | Hot-dip al-zn alloy coated steel sheet and method for producing same | |
MX2016003143A (es) | Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas. | |
MX348834B (es) | Lámina de acero galvanizada. | |
MX2016010001A (es) | Lamina de acero galvano-recocida y metodo para la produccion de la misma. | |
MX2015013517A (es) | Lamina de acero recubierta de aleacion de ai-zn por inmersion en caliente y metodo para la produccion de la misma. | |
MY174906A (en) | Al-based alloy plated steel material having excellent post-coating corrosion resistance | |
MX2015015064A (es) | Lamina de acero galvanizado y metodo para producir el mismo. | |
IN2013CH00957A (es) | ||
MY161932A (en) | Hot-dip zinc-aluminium alloy coated steel sheet having high corrosion resistance and formability and method for producing the same |