KR970707253A - 알파 알루미나 연마재 그릿, 이의 제조방법, 및 이를 포함하는 연마재 및 연마재 공구 - Google Patents

알파 알루미나 연마재 그릿, 이의 제조방법, 및 이를 포함하는 연마재 및 연마재 공구

Info

Publication number
KR970707253A
KR970707253A KR1019970703319A KR19970703319A KR970707253A KR 970707253 A KR970707253 A KR 970707253A KR 1019970703319 A KR1019970703319 A KR 1019970703319A KR 19970703319 A KR19970703319 A KR 19970703319A KR 970707253 A KR970707253 A KR 970707253A
Authority
KR
South Korea
Prior art keywords
grit
alumina
abrasive
weight
group
Prior art date
Application number
KR1019970703319A
Other languages
English (en)
Other versions
KR100201521B1 (ko
Inventor
에이. 케이. 가그
Original Assignee
보스트 스티븐 엘.
쌩-고뱅/노튼 인더스트리얼 세라믹스 코포레이션
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=23336825&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=KR970707253(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 보스트 스티븐 엘., 쌩-고뱅/노튼 인더스트리얼 세라믹스 코포레이션 filed Critical 보스트 스티븐 엘.
Publication of KR970707253A publication Critical patent/KR970707253A/ko
Application granted granted Critical
Publication of KR100201521B1 publication Critical patent/KR100201521B1/ko

Abstract

하나 이상의 이트리아, 및 마그네시아 및/또는 전이원소의 산화물 하나 이상으로 개질시킨 과립 경계부를 갖는 알루미나 연마재 그릿(alpha alumina abrasive grit)은, 이트리아 및/또는 희토류 금속 산화물 개질 제의 그릿 몸체내부에서의 농도가 그릿 표면에서 보다 높거나 동일한 경우, 증강된 수준으로 작업을 수행한다.

Description

알파 알루미나 연마재 그릿, 이의 제조방법, 및 이를 포함하는 연마재 및 연마재 공구
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (22)

  1. 알루미나가 필수적으로 균일한 결정성 형태학을 보유하는 알파 알루미나 연마재 그릿(alpha alumina abrasive grit)으로서, 그릿(grit)이 이트리아 및 희토류 금속 중의 하나 이상(a)과 마그네슘, 티탄, 크롬, 망간, 철, 코발트, 니켈, 아연 및 리튬으로 이루어진 그룹으로부터 선택된 금속의 산화물 하나 이상(b)을 개질 성분으로서 포함하고 그릿 내부에서의 그룹(a)로부터 개질 성분(들)의 평균 농도가 그릿 표면의 20미크론 이내에서의 농도보다 높거나 동일한 알파 알루미나 연마재 그릿.
  2. 제1항에 있어서, 그룹(a)로부터 선택된 개질 성분이 그릿 내부에서 필수적으로 균일하게 분포되어 있는 연마재 그릿.
  3. 제1항에 있어서, 모든 개질 성분이 그릿 내부에서 필수적으로 균일하게 분포되어 있는 연마재 그릿.
  4. 제1항에 있어서, 희토류 금속 산화물이 란타나인 연마재 그릿.
  5. 제1항에 있어서, 개질 성분의 총량이 알파 알루미나 중량의 약 0.01 내지 약 2중량%이고 각각의 개별 그룹(a)의 성분이 알파 알루미나 중량의 약 0.02 내지 약 0.35%인 연마재 그릿.
  6. 제1항에 있어서, 이트리아 및 란타나 각각 0.02 내지 약 0.2중량% 최대 0.2중량% 이하와 마그네슘, 티탄, 크롬, 망간, 철, 코발트, 니켈 및 아연으로 이루어진 그룹로부터 선택된 금속의 산화물 하나 이상 약 0.01 내지 약 0.4중량%, 최대 혼합 중량 약 1.5중량% 이하를 포함하는 연마재 그릿.
  7. 제1항에 있어서, 알루미나 상이 미크론 단위 이하의 결정성 구조를 보유하는 연마재 그릿.
  8. 알루미나가 필수적으로 균일한 미크론 단위 이하의 결정성 형태학을 취하는 알파 알루미나 연마재 그릿으로서, 그릿이 이트리아 및 란타나(a)와 마그네슘, 티탄, 크롬, 망간, 철, 코발트, 니켈, 아연 및 리튬으로 이루어진 그룹으로부터 선택된 금속의 산화물 하나 이상(b)을 개질 성분으로서 포함하고 그룹(a)로부터 선택된 하나 이상의 개질 성분(들)이 필수적으로 그릿 내부에서 균일하게 분포되어 있는 알파 알루미나 연마재 그릿.
  9. 제8항에 있어서, 이트륨 및 란탄 각각 0.02 내지 약 0.2중량%, 최대 약 0.22중량% 이하와 마그네슘, 티탄, 크롬, 망간, 철, 코발트, 니켈, 아연 으로 이루어진 그룹으로부터 선택된 금속의 산화물 하나 이상 약 0.01 내지 약 0.2중량%, 최대 약 0.8중량%를 포함하는 연마재 그릿.
  10. 알파 알루마나 전구체의 겔을 다공성 알루미나 상이 생성될 때까지 건조 및 소성시키는 단계, 다공성 알루미나를 염기 생성 첨가제와 함께 가용성 열분해 가능한 염 형태의 개질 성분 용액으로 침윤시켜 염기를 생성시키고 파쇄시켜, 알파 알루미나가 반응에서 생성되는 온도 미만에서 휘발성 가스를 형성시키는 단계 및 충분히 높은 온도로 소성시켜 다공성 알루미나를 알파 상으로 전환시키는 단계를 포함하여, 개질 성분〔여기서, 개질 성분은 이트리아 및 희토류 금속 하나 이상(a)과 마그네슘, 티탄, 크롬, 망간, 철, 코발트, 니켈, 아연 및 리튬으로 이루어진 그룹으로부터 선택된 금속의 산화물 하나 이상(b)이다〕을 도입시킴으로써 개질된 알파 연마재 그릿을 제조하는 방법.
  11. 제10항에 있어서, 그룹(a)로부터 선택된 개질제의 양이, 그릿 내부에서의 평균 농도가 그릿 표면의 20미크론 이내에서의 평균 농도보다 높거나 동일하게 되도록 하는 양인 방법.
  12. 제11항에 있어서, 첨가되는 개질 성분의 양이, 모든 개질 성분이 그릿 내부에서 필수적으로 균일하게 분포되도록 하는 양인 방법.
  13. 제10항에 있어서, 염기 생성 첨가제가 포름아미드, 에세트아미드 및 우레아로 이루어진 그룹으로부터 선택되는 방법.
  14. 제10항에 있어서, 첨가되는 개질 성분의 총량이, 알루미나의 중량을 기준으로 하여, 약 1.5% 미만인 방법.
  15. 제10항에 있어서, 다공성 알루미나 물질에 대하여 진공이 회수되면서 침윤이 수행되는 방법.
  16. 제10항에 있어서, 알루미나 겔이 알파 알루미나로의 전이온도를 저하시키고 미크론 단위 이하의 알루미나 결정성 구조를 생성하기에 유효한 핵 형성제를 추가로 포함하는 방법.
  17. 제16항에 있어서, 첨가되는 개질 성분의 총량이, 알루미나의 중량을 기준으로 하여, 약 1.0% 미만인 방법.
  18. 제16항에 있어서, 염기 생성 첨가제가 포름아미드, 아세트아미드 및 우레아로 이루어진 그룹으로부터 선택되는 방법.
  19. 제1항에 따르는 연마재 그릿을 포함하는 피복 연마재.
  20. 제1항에 따르는 연마재 그릿을 포함하는 결합 연마재 공구.
  21. 제8항에 따르는 연마재 그릿을 포함하는 피복 연마재.
  22. 제8항에 따르는 연마재 그릿을 포함하는 결합 연마재 공구.
    ※ 참고사항 : 최초출원 내용에 의하여 공개되는 것임.
KR1019970703319A 1994-11-17 1995-08-30 알파 알루미나 연마재 그릿,이의 제조방법,및 이를 포함하는 연마재 및 연마재 공구 KR100201521B1 (ko)