KR970043239A - 항균성이 향상된 스테인레스강 및 그 제조방법 - Google Patents
항균성이 향상된 스테인레스강 및 그 제조방법 Download PDFInfo
- Publication number
- KR970043239A KR970043239A KR1019960064591A KR19960064591A KR970043239A KR 970043239 A KR970043239 A KR 970043239A KR 1019960064591 A KR1019960064591 A KR 1019960064591A KR 19960064591 A KR19960064591 A KR 19960064591A KR 970043239 A KR970043239 A KR 970043239A
- Authority
- KR
- South Korea
- Prior art keywords
- less
- stainless steel
- weight
- ratio
- matrix
- Prior art date
Abstract
스테인레스강은 0.4-5.0중량%의 Cu의 첨가와 0.2체적%이상의 비율의 Cu-리치상의 석출에 의하여 항균성이 향상된다. Cu-리치상은, 500-900℃의 온도에서 어닐링 또는 시효처리와 같은 열처리에 의하여 표면층 뿐만 아니라 내부에서도, 매트릭스에 균일하게 분산된 미세입자로 석출된다. 항균성이 물질 자체로부터 유도되었으므로 연마되고나 기계적으로 작업되어도 본 스테인레스강은 탁월한 항균성을 잃지 않는다. 항균성 때문에 본 스테인레스강은 주방기구, 전기가정용품, 의료도구 및 기구, 빌딩의 부분 또는 내부, 전철 또는 버스의 손잡이나 막대와 같은 위생적은 환경을 요하는 여러 분야에서의 재료로서 유용하다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 투과전자현미경에 의해 관찰된, 800℃의 온도에서 1시간동안 시효처리된 Cu 함유 페라이트계 스테인레스강의 금속야금학적 구조를 나타내고 있다.
Claims (13)
- Cu; 0.4-5.0중량%를 함유하고, Cu를 주로하여 구성되는 2차 상이 매트릭스(matrix)에서 0.2체적%이상의 비율로 석출되는 구조를 가지는 것을 특징으로 하는 항균성이 탁월한 스테인레스강.
- Cu; 0.4-5.0중량%를 함유하는 스테인레스강을 제조하는 단계; 및 매트리스에서 0.2체적%이상의 비율로 Cu를 주로하여 구성되는 2차상을 석출하기에 충분한 시간동안 200-900℃의 온도에서 상기의 스테인레스강을 가열하는 단계;를 포함하는 것을 특징으로 하는 항균성이 탁월한 스테인레스강의 제조방법.
- 중량%로, C: 0.1%이하, Si: 2%이하, Mn: 2%이하, Cr: 10-30%, Cu: 0.4-3%와 잔부 Fe 및 기타 불가피하게 함유되는 불순물로 구성되는 조성 및 Cu를 주로하여 구성되는 2차상이 매트릭스에서 0.2체적%이상의 비율로 석출되는 구조를 가지는 것을 특징으로 하는 항균성이 탁월한 페라이트계 스테인레스강.
- 제3항에 있어서, 0.002-1중량%의 Nb및/또는 Ti를 더 함유하는 것을 특징으로 하는 페라이트계 스테인레스강.
- 제3항 또는 제4항에 있어서, 중량%로, Mo: 3%이하, Aℓ; 1%이하, Zr; 1%이하, V; 1%이하, B; 0.05%이하 그리고 회토류금속: 0.05%이하 중에서 적어도 하나를 더 함유하는 것을 특징으로 하는 페라이트계 스테인레스강.
- 중량%로, C: 0.1%이하, Si: 2%이하, Mn: 2%이하, Cr: 10-30%, Cu: 0.4-3% 선택적으로 Nb및/또는 Ti; 0.02-1%, Mo: 3%이하, Aℓ; 1%이하, Zr; 1%이하, V; 1%이하, B; 0.05%이하 그리고 회토류금속: 0.05%이하 군에서 선택된 하나 이상의 원소 및 잔부 Fe 및 기타 불가피하게 함유되는 불순물로 구성되는 조성을 가지는 페라이트계 스테인레스강을 제조하는 단계; 상기 페라이트계 스테인레스강을 냉간압연하는 단계; 최후로 냉간압연하는 강판을 어닐링(annealing)하는 단계; 및 매트릭스에서 0.2체적%이상의 비율로 Cu를 주로하여 구성되는 2차 상을 석출시키기 위하여, 500-800℃의 온도에서 어닐링된 강판을 시효처리(aning)하는 단계;를 포함하는 것을 특징으로 하는 항균성이 탁월한 페라이트계 스테인레스강의 제조방법.
- 중량%로, C: 0.1%이하, Si: 2%이하, Mn: 5%이하, Cr: 10-30%, Ni; 5-15% Cu: 1.0-5.0% 와 잔부 Fe 및 기타 불가피하게 함유되는 불순물로 구성되는 조성 및Cu를 주로하여 구성되는 2차상이 매트릭스에서 0.2체적%이상의 비율로 석출되는 구조를 가지는 것을 특징으로 하는 항균성이 탁월한 페라이트계 스테인레스강.
- 제7항에 있어서, 중량%로 Nb및/또는 Ti; 0.02-1%, Mo: 3%이하, Aℓ; 1%이하, Zr; 1%이하, V; 1%이하, B; 0.05%이하 및 회토류금속: 0.05%이하 중에서 하나이상을 더 함유하는 것을 특징으로 하는 오스테나이트계 스테인레스강.
- 중량%로, C: 0.1%이하, Si: 2%이하, Mn: 5%이하, Cr: 10-30%, Ni; 5-15% Cu: 1.0-5.0% 선택적으로 Nb및/또는 Ti; 0.02-1%, Mo: 3%이하, Aℓ; 1%이하, Zr; 1%이하, V; 1%이하, B; 0.05%이하 그리고 회토류금속: 0.05%이하 군에서 선택된 하나 이상의 원소 및 잔부 Fe 및 기타 불가피하게 함유되는 불순물로 구성되는 조성을 가지는 페라이트계 스테인레스강을 제조하는 단계; 상기 페라이트계 스테인레스강을 열간압연하는 단계; 및 매트릭스에서 0.2체적%이상의 비율로, Cu를 주로하여 구성되는 2차 상을 석출시키기 위하여, 500-800℃의 온도에서 최소한 한번 이상 강판을 열처리하는 단계;를 포함하는 것을 특징으로 하는 항균성이 탁월한 오스테나이트계 스테인레스강의 제조방법.
- 중량%로, C: 0.8%이하, Si: 3%이하, Cr: 10-20%, Cu: 0.4-5.0%와 잔부 Fe 및 기타 불가피하게 함유하는 불순물로 구성되는 조성 및 Cu를 주로하여 구성되는 2차상이 매트릭스에서 0.2체적%이상의 비율로 석출되는 구조를 가지는 것을 특징으로 하는 항균성이 탁월한 오스테나이트계 스테인레스강.
- 제10항에 있어서, Mo: 4중량%이하와 V; 1중량%이하중의 하나 또는 모두를 더 함유하는 것을 특징으로 하는 오스테나이트계 스테인레스강.
- 중량%로, C: 0.8%이하, Si: 3%이하, Cr: 10-20%, Cu: 0.4-5.0% 선택적으로 Mo: 4%이하와 V; 1%이하중와 하나 또는 모두와 잔부 Fe 및 기타 불가피하게 함유하는 불순물로 구성되는 조성을 가지는 마르텐사이트계 스테인레스강을 제조하는 단계; 상기 마르텐나이트계 스테인레스강을 열간압연하는 단계; 열간압연된 강판을 어닐링하는 단계; 및 매트릭스에서 0.2체적%이상의 비율로, Cu를 주로하여 구성되는 2차상을 석출시키기 위하여, 1시간 이상동안 500-900℃의 온도에서 상기의 강판이 가열되는 배치형(batch-type) 어닐링에, 어닐링된 강판을 처리시키는 단계;를 포함하는 것을 특징으로 하는 하는 항균성이 탁월한 마르텐사이트계 스테인레스강의 제조방법.
- 제12항에 있어서, 배치형 어닐링후에 강판을 냉간압연하는 단계; 및 계속하겨 700-900℃의 온도에서 냉간압연된 강판을 어닐링하는 단계;를 포함하는 것을 특징으로 하는 항균성이 탁월한 마르텐사이트계 스테인레스강의 제조방법.