CN103710508B - 抗菌不锈钢线材的制造方法 - Google Patents

抗菌不锈钢线材的制造方法 Download PDF

Info

Publication number
CN103710508B
CN103710508B CN201310674977.7A CN201310674977A CN103710508B CN 103710508 B CN103710508 B CN 103710508B CN 201310674977 A CN201310674977 A CN 201310674977A CN 103710508 B CN103710508 B CN 103710508B
Authority
CN
China
Prior art keywords
stainless steel
steel wire
wire rod
manufacture method
treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310674977.7A
Other languages
English (en)
Other versions
CN103710508A (zh
Inventor
张瑞杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liucheng County Ding Ming Metal Products Co Ltd
Original Assignee
Liucheng County Ding Ming Metal Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liucheng County Ding Ming Metal Products Co Ltd filed Critical Liucheng County Ding Ming Metal Products Co Ltd
Priority to CN201310674977.7A priority Critical patent/CN103710508B/zh
Publication of CN103710508A publication Critical patent/CN103710508A/zh
Application granted granted Critical
Publication of CN103710508B publication Critical patent/CN103710508B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种抗菌不锈钢线材的制造方法，包括步骤：线材拉伸步骤：将含铜量为0.6-0.8wt%不锈钢线材进行拉伸到所需的外径；固溶处理步骤：将不锈钢线材进行固溶处理，处理工艺为：固溶温度为1180°C-1250°C。时效处理步骤：按分段时效进行处理：第一段在100-400，时间为0.5-3小时；第二段在400-600，时间为1-2小时；二次拉伸步骤：将时效处理后的线材再次进行拉伸，得到所需外径的线材。其优点是工艺简单实用，采用通用设备即可进行生产，生产成本低，抗菌效果好，抗菌时效长，不用添加其它化学成分，不会造成环境污染，抗菌率高。

Description

抗菌不锈钢线材的制造方法
技术领域
本发明涉及对不锈钢线材进行抗菌处理技术领域，特别涉及一种抗菌不锈钢线材的制造方法。
背景技术
目前抗菌不锈钢包括两大类：一类是通过炼钢、连铸及轧制工艺制造抗菌不锈钢，由于其工艺制造复杂，成本过高；另一类是通过表面处理的方式使不锈钢表面具有抗菌效果，但其表面磨损后，抗菌效果也随之消失。
发明内容
本发明的目的就是提供一种成本低，工艺简单的抗菌不锈钢线材的制造方法。
本发明的解决方案是这样的：
一种抗菌不锈钢线材的制造方法，包括步骤：
（1）、线材拉伸步骤：将含铜量为0.6-0.8wt%不锈钢线材进行拉伸到所需的外径；
（2）、固溶处理步骤：将不锈钢线材进行固溶处理，处理工艺为：固溶温度为1180°C-1250°C。
（3）、时效处理步骤：按分段时效进行处理：第一段在100-400，时间为0.5-3小时；第二段在400-600，时间为1-2小时。
更具体的技术方案还包括二次拉伸步骤：将时效处理后的线材再次进行拉伸，得到所需外径的线材。
进一步的：所述固溶处理步骤中，将不锈钢线材进行固溶处理，处理工艺为：固溶温度为1200°C-1250°C。
本发明的优点是工艺简单实用，采用通用设备即可进行生产，生产成本低，抗菌效果好，抗菌时效长，不用添加其它化学成分，不会造成环境污染，抗菌率高。
具体实施方式
实施例1：
一种抗菌不锈钢线材的制造方法，按下列步骤顺序进行制造：
（1）、线材拉伸步骤：将含铜量为0.6-0.8wt%不锈钢线材进行拉伸到所需的外径；
（2）、固溶处理步骤：将不锈钢线材进行固溶处理，处理工艺为：固溶温度为1000°C-1100°C；
（3）、时效处理步骤：按分段时效进行处理：第一段在100-400，时间为0.5-3小时；第二段在400-600，时间为1-2小时；
（4）、将时效处理后的线材再次进行拉伸，得到所需外径的线材。
实施例2：
一种抗菌不锈钢线材的制造方法，按下列步骤顺序进行制造：
（1）、固溶处理步骤：将含铜量为0.6-0.8wt%不锈钢线材进行固溶处理，处理工艺为：固溶温度为1155°C-1250°C；
（2）、线材拉伸步骤：将固溶处理后的线材拉伸到所需的外径；
（3）、时效处理步骤：按分段时效进行处理：第一段在100-400，时间为0.5-3小时；第二段在400-600，时间为1-2小时；
（4）、将时效处理后的线材再次进行拉伸，得到所需外径的线材。
实施例3：
一种抗菌不锈钢线材的制造方法，按下列步骤顺序进行制造：
（1）、固溶处理步骤：将含铜量为0.6-0.8wt%不锈钢线材进行固溶处理，处理工艺为：固溶温度为1180°C-1250°C；
（2）、时效处理步骤：按分段时效进行处理：第一段在100-400，时间为0.5-3小时；第二段在400-600，时间为1-2小时；
（3）、线材拉伸步骤：将时效处理后的不锈钢线材进行拉伸到所需的外径。
实施例4：
一种抗菌不锈钢线材的制造方法，按下列步骤顺序进行制造：
（1）、固溶处理步骤：将含铜量为0.6-0.8wt%不锈钢线材进行固溶处理，处理工艺为：固溶温度为1200°C-1250°C；
（2）、线材拉伸步骤：将固溶处理后的线材拉伸到所需的外径；
（3）、时效处理步骤：按分段时效进行处理：第一段在100-400，时间为0.5-3小时；第二段在400-600，时间为1-2小时。
实施例5：
一种抗菌不锈钢线材的制造方法，按下列步骤顺序进行制造：
（1）、固溶处理步骤：将含铜量为0.6-0.8wt%不锈钢线材进行固溶处理，处理工艺为：固溶温度为1230°C-1250°C；
（2）、线材拉伸步骤：将固溶处理后的线材拉伸到所需的外径；
（3）、时效处理步骤：按分段时效进行处理：第一段在100-400，时间为0.5-3小时；第二段在400-600，时间为1-2小时。
上述实施例制造的抗菌不锈钢，经抗菌检测，达到抗菌效果。

Claims (3)

1.一种抗菌不锈钢线材的制造方法，其特征在于：包括步骤：
（1）、线材拉伸步骤：将含铜量为0.6-0.8wt%不锈钢线材进行拉伸到所需的外径；
（2）、固溶处理步骤：将不锈钢线材进行固溶处理，处理工艺为：固溶温度为1180°C-1250°C；
（3）、时效处理步骤：按分段时效进行处理：第一段在100-400，时间为0.5-3小时；第二段在400-600，时间为1-2小时。
2.根据权利要求1所述的抗菌不锈钢线材的制造方法，其特征在于：
还包括步骤：还包括二次拉伸步骤：将时效处理后的线材再次进行拉伸，得到所需外径的线材。
3.根据权利要求1所述的抗菌不锈钢线材的制造方法，其特征在于：所述固溶处理步骤中，将不锈钢线材进行固溶处理，处理工艺为：固溶温度为1200°C-1250°C。
CN201310674977.7A 2013-12-13 2013-12-13 抗菌不锈钢线材的制造方法 Active CN103710508B (zh)