KR950032669A - 구리-니켈-실리콘 합금의 제조방법 및 그 합금의 사용방법 - Google Patents
구리-니켈-실리콘 합금의 제조방법 및 그 합금의 사용방법 Download PDFInfo
- Publication number
- KR950032669A KR950032669A KR1019950008328A KR19950008328A KR950032669A KR 950032669 A KR950032669 A KR 950032669A KR 1019950008328 A KR1019950008328 A KR 1019950008328A KR 19950008328 A KR19950008328 A KR 19950008328A KR 950032669 A KR950032669 A KR 950032669A
- Authority
- KR
- South Korea
- Prior art keywords
- alloy
- nickel
- copper
- silicon
- producing
- Prior art date
Abstract
본 발명은Cu(밸런스), Ni 1.5∼5.5%(이하 중량%), Si 0.2-0.1%, Fe 0-0.5% 및 Mg 0-0.1%의 조성의 구리-니켈-실리콘 합금의 제조방법 및 압력-인글레이저블(englazable) 케이싱용의 합금의 사용방법에 관한 것이다. 제조방법은 합금이 매우 높은 탄성 임계, 매우 양호한 도전성 및 양호한 냉간변형성을 갖도록 할 수 있고, 선행의 냉간압연처리후 약 950℃로 가열하고, 매우 신속히 냉각시키는 것이 종래의 합금의 제조방법과는 다르다. 특성의 향상은 300-600℃에서 수시간 동안 합금을 숙성함으로써 달성될수 있다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 탄성임계와 니켈함유량 사이의 관계를 나타낸 도면, 제2도는 도전성과 니켈함유량 사이의 관계를 나타낸 도면, 제3도는 일정한 Si 0.7%시 냉각변형성, 탄성임계 및 니켈함유량 사이의 관계를 나타낸 도면.
Claims (10)
- Cu(밸런스), Ni 1.5∼5.5%(이하 중량%), Si 0.2-0.1%, Fe 0-0.5% 및 Mg 0-0.1%의 조성의 구리-니켈-실리콘 합금의 제조방법에 있어서, a)합금을 주조하고, b)700-900℃에서 14-1시간동안 용해처리하고, c)최소한 80%의 환원으로 냉간압연하고, d)950℃로 가열하고 e)최대 100℃/min에서 최소 350℃로 냉각하는 단계로 이루어지는 것을 특징으로 하는 구리-니켈-실리콘 합금의 제조방법.
- Cu(밸런스), Ni 1.5∼5.5%, Si 0.2-0.1%, Fe 0-0.5% 및 Mg 0-0.1%의 조성의 구리-니켈-실리콘 합금의 제조방법에 있어서, a)합금을 주조하고, b)700-900℃에서 14-1시간동안 용해처리하고, c)최소한 80%의 환원으로 냉간압연하고, d)950℃로 가열하고 e)최대 100℃/min에서 최소 350℃로 냉각하고 f)300-600℃에서 8-1시간동안 합금을 숙성하는 단계로 이루어지는 것을 특징으로 하는 구리-니켈-실리콘 합금의 제조방법.
- Cu(밸런스), Ni 1.5∼5.5%, Si 0.2-0.1%, Fe 0-0.5% 및 Mg 0-0.1%의 조성의 구리-니켈-실리콘 합금의 제조방법에 있어서, a)합금을 주조하고, b)700-900℃에서 14-1시간동안 용해처리하고, c)최소한 90%의 환원으로 냉간압연하고, g)400-750℃에서 8시간-1분동안 소프트어닐링하고 h)디프 드로잉하고, d)950℃로 가열하고 e)30-40℃/mon에서 최소 350℃로 냉각하고 f)300-600℃에서 8-1시간동안 합금을 숙성하는 단계로 이루어지는 것을 특징으로 하는 구리-니켈-실리콘 합금의 제조방법.
- 제1항 내지 제3항중 어느 한항에 있어서, 단계 a) 또는 b)후에 i)열변형시키는 단계를 포함하는 것을 특징으로 하는 구리-니켈-실리콘 합금의 제조방법.
- 제3항 또는 제4항에 있어서 단계 g)와 h)대신에, hh)단조하는 단계를 포함하는 것을 특징으로 하는 구리-니켈-실리콘 합금의 제조방법.
- 제1항 내지 제5항중 어느 한항에 있어서, 상기 단계가 Cu(밸런스), Ni 1.8∼4.7%, Si 0.4-0.9%, 및 Fe 0-0.1% 의 조성의 합금에 적용되는 것을 특징으로 하는 구리-니켈-실리콘 합금의 제조방법.
- 제1항 내지 제5항중 어느 한항에 있어서, 상기 단계가 Cu(밸런스), Ni 2.3∼4.5%, Si 0.4-0.9%, 의 조성의 합금에 적용되는 것을 특징으로 하는 구리-니켈-실리콘 합금의 제조방법.
- 제1항 내지 제5항중 어느 한항에 있어서, 상기 단계가 Cu(밸런스), Ni 2.9 및 Si 0.7%의 조성의 합금에 적용되는 것을 특징으로 하는 구리-니켈-실리콘 합금의 제조방법.
- 제1항 내지 제8항중 어느 한 항에 따른 방법에 의하여 제조된 합금을 압력-인글레저블케이싱의 제조에 사용하는 것을 특징으로 하는 구리-니켈-실리콘의 합금의 사용방법.
- 제1항 내지 제8항중 어느 한 항에 따른 방법에 의하여 제조된 합금을 전자부품소자용 압력-인글레저블공기차단시일케이싱의 제조에 사용하는 것을 특징으로 하는 구리-니켈-실리콘의 합금의 사용방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.