KR950032340A - 블록 공중합체 및 청색 수지성 블록 공중합체의 제조 방법 - Google Patents
블록 공중합체 및 청색 수지성 블록 공중합체의 제조 방법 Download PDFInfo
- Publication number
- KR950032340A KR950032340A KR1019950006111A KR19950006111A KR950032340A KR 950032340 A KR950032340 A KR 950032340A KR 1019950006111 A KR1019950006111 A KR 1019950006111A KR 19950006111 A KR19950006111 A KR 19950006111A KR 950032340 A KR950032340 A KR 950032340A
- Authority
- KR
- South Korea
- Prior art keywords
- monomer
- conjugated diene
- monovinylaromatic
- copolymer
- monomers
- Prior art date
Abstract
적어도 하나의 모노비닐 방향족 단량체 및 적어도 하나의 공액 디엔 단량체를 중합 조건하에 순차적으로 적하한 후 적어도 하나의 커플링제와 함께 반응 혼합물을 적하하는 것으로 구성되는 투명한 청색 제품을 제조할 수 있는 블록 공중합체 제조 방법으로서, 상기에서 적어도 하나의 제1단량체 적하물은 개시제 존재하에 중합된 모노비닐방향족 단량체이고; 상기에서 개시제 존재하에 중합된 적어도 하나의 다른 적하물은 공액 디엔 단량체 및 모노비닐방향족 및 공액 디엔 단량체의 혼합물의 군으로부터 선택된 단량체이고; 상기에서 최종 적하물이 공액 디엔 적하물이다. 본 발명의 적하물은 다른 물리적 및 기계적 특성과의 큰 절충없이 투명한 청색 외관이 요구되는 포장, 전시 기구, 장난감 및 장식품과 같은 적용에 특히 유용하다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (24)
- 적어도 하나의 모노비닐방향족 단량체 및 적어도 하나의 공액 디엔 단량체를 순차적으로 증합시키는 것으로 구성된 청색 수지성 블록 공중합체 제조 방법으로서, 상기 적어도 하나의 공액 디엔 단량체의 적어도 하나의 적하물이 개시제 존재하에 중합하므로써 공액디엔 말단 블록을 갖는 적어도 하나의 중합체 종을 생성하는 방법.
- 제1항에 있어서서, 개시제 존재하에 중합하는 상기 모노비닐방향족 단량체의 적어도 제1적하물; 개시제 존재하에 중합하는 공액 디엔 단량체 또는 모노비닐방향족 단량체와 공액디엔 단량체의 혼합물로 구성되어 적어도 하나의 다른 단량체 적하물; 및 공액디엔 적하물인 최종 단량체 적하물을 순차적으로 적하하고 상기 최종 단량체 적하물 후에 적어도 하나의 커플링제를 적하하는 것으로 구성되는 방법.
- 제2항에 있어서, 하기를 랜덤화재 존재하에 순차적으로 접촉시키는 것으로 구성되는 방법: (a)모노비닐 방향족 단량체 및 개시제; 이후(b) 모노비닐방향족 단량체 및 개시제; 이후 (c)공액 디엔; 이후 (d) 모노비닐 방향족 단량체와 공액 디엔 단량체의 혼합물 및 개시제; 이후 (e)공액 디엔; 및 이후 (f)커플링제.
- 제2항에 있어서, 하기를 랜덤화제 존재하에 순차적으로 접촉시키는 것으로 구성되는 방법: (a)모노비닐 방향족 단량체 및 개시제; 이후(b)모노비닐방향족 단량체 및 개시제; 이후 (c)공액 디엔 단량체; 이후(d)공액 디엔 단량체 및 개시제; 이후 (e)모노비닐방향족 단량체; 이후 (f) 공액 디엔; 및 이후(g)커플링제.
- 제3항 또는 4항에 있어서, 각 단량체 적하물의 중합을 각 후속 단계의 적하물을 제조하기 전 필수적으로 자유 단량체가 존재하지 않을 때까지 수행시키는 방법.
- 제1항에 있어서, (a)모노비닐방향족 단량체 및 개시제; 이후 (b) 모노비닐방향족 단량체 및 개시제; 이후 (c)공액 디엔 단량체; 이후 (d)모노비닐방향족 단량체 및 개시제; 이후 (e)공액 디엔 단량체; 및 이후 (f)커플링제를 랜덤화제 존재하에 순차적으로 접촉시키는 것으로 구성되고, 이때 단계(d)의 적하물은 단계(c)에서 제조된 적하물의 중합이 완결되기전 제조하는 방법.
- 제6항에 있어서, 단계(a),(b),(d)및 (e)에서 각 단량체 적하물의 중합을 각 후속 단계의 적하물이 제조되기전 자유라디칼이 존재하지 않을때까지 발생시키는 방법.
- 제2항에 있어서, 하기를 랜덤화제 존재하에 순차적으로 접촉시키는 것으로 구성되는 방법: (a)모노비닐 방향족 단량체 및 개시제; 이후 (b) 모노비닐방향족 단량체와 공액 디엔 단량체의 혼합물 및 개시제; 이후 (c)공액 디엔 단량체; 이후 (d)모노비닐방향족 단량체 및 개시제; 이후 (e)공액 디엔 단량체; 및 이후 (f)커플링제.
- 제2항에 있어서, 하기를 랜덤화제 존재하에 순차적으로 접촉시키는 것으로 구성되는 방법: (a)모노비닐방향족 단량체 및 개시제; 이후(b) 공액 디엔 단량체 및 개시제; 이후 (c)모노비닐방향족 단량체; 이후 (d)공액 디엔 단량체; 이후 (e)모노비닐방향족 단량체 및 개시제; 이후 (f)공액 디엔 단량체; 및 이후(g)커플링제.
- 제8 또는 9항에 있어서, 각 적하물의 중합을 각 후속 단계의 적하물을 제조하기전 자유 단량체가 존재하지 않을 때까지 발생시키는 방법.
- 제1 또는 2항에 있어서, 상기 모노비닐방향족 단량체 각각이 8-12개 탄소원자를 함유하고 상기 공액 디엔 각각이 4-6개 탄소원자를 함유하고, 상기 단량체를 모노비닐방향족 단량체 약 55-약 95중량% 및 공액 디엔 단량체 약5-약 45중량%의 비율로 첨가하여, 수지성 블록 공중합체를 제공하는 방법.
- 제11항에 있어서, 상기 단량체를 모노비닐방향족 단량체의 약60-약 90중량%및 공액 디엔 단량체 약 10-약 40중량%의 비율로 첨가하는 방법.
- 제12항에 있어서, 상기 단량체를 모노비닐방향족 단량체 약 65-약 85중량%및 공액 디엔 단량체 15-35중량%의 비율로 첨가하는 방법.
- 제1 또는 2항에 있어서, 상기 개시제를 유효량으로 적하하여 상기 중합체 또는 상기 중합체와 폴리스티렌의 블렌드로 제조한 제품이 높은 청색도를 갖도록 상기 중합체내 비례량의 중합체를 제공하는 방법.
- 제1 또는 2항에 있어서, 상기 각 공액 디엔 단량체가 부타디엔이고, 상기 각 모노비닐방향족 단량체가 스티렌이고, 상기 유기모노알칼리 금속 개시제가 n-부틸리튬이고, 상기 랜덤화제가 테트라히드로퓨란, 디에틸 에테르 또는 칼륨-t-아밀레이트이고, 상기 커플링제가 에폭시드화 식물섬유인 방법.
- 제1 또는 2항에 있어서, 중합을 실질적으로 산소 및 물없이 약 -10℃-약 150℃ 범위내 온도에서 탄화수소 희석제 내에서 수행하고; 상기 커플링제가 상기 중합의 생성물과 반응한 후, 시스템을 종결제 및 안정화제로 처리하고; 및 상기 종결제 및 상기 안정화제의 첨가후, 임의의 잔류 탄화수소 희석제를 플래슁시키는 방법.
- 모노비닐방향족 화합물 및 공액디엔의 다정형 커플링된 수지성 블록 공중합체로서, 상기 공중합체내 단량체의 총중량을 기준으로 하여 약 55-약 95중량%의 중합된 모노비닐 방향족 화합물을 갖고; 및 하기 중합체종:S-S-B-B/S-B-LiS-B-B/S-B-LiB/S-B-Li(상기에서 S=모노비닐방향족 블록 B=공액디엔 블록 B/S=테이퍼드 블록 Li=리빙중합체 부위 또는 커플링 부위)을 커플링시킴으로써 결과 얻어지는 중합체 사슬을 갖는 공중합체.
- 모노비닐방향족 화합물 및 공액 디엔의 다정형 커플링된 수지성 블록 공중합체로서, 상기 공중합체내 단량체의 총 중량을 기준으로 하여 약 55-약 95중량%의 중합된 모노비닐방향족 화합물을 갖고; 및 하기 중합체 종:S-S-B-B-S-B-LiS-B-B-S-B-LiB-S-B-Li(상기에서 S=모노비닐방향족 블록 B=공액디엔 블록 Li=리빙중합체 부위 또는 커플링 부위)을 커플링시킴으로써 결과 얻어지는 중합체 사슬을 갖는 공중합체.
- 모노비닐방향족 화합물 및 공액디엔의 다정형 커플링된 수지성 블록 공중합체로서, 상기 공중합체내 단량체의 총 중량을 기준으로 하여 약 55-약 95중량%의 중합된 모노비닐방향족 화합물을 갖고; 및 하기 중합체종:S-S-B-B/S-B-LiS-B-B/S-B-LiB/S-B-Li(상기에서 S=모노비닐방향족 블록 B=공액디엔 블록 B/S=테이퍼드 블록 Li=리빙 중합체 부위 또는 커플링 부위)을 커플링시킴으로써 결과 얻어지는 중합체 사슬 갖는 공중합체.
- 모노비닐방향족 화합물 및 공액 디엔의 다정형 커플링된 수지성 블록 공중합체로서, 상기 공중합체내 단량체의 총 중량을 기준으로 하여 약 55-약 95중량%의 중합된 모노비닐 방향족 화합물을 갖고; 및 하기 중합체 종:S-B/S-B-S-B-LiB/S-B-S-B-LiS-B-Li(상기에서 S=모노비닐방향족 블록 B=공액 디엔 블록 B/S=테이퍼드 블록 Li=리빙중합체 부위 또는 커플링 부위)을 커플링시킴으로써 결과 얻어지는 중합체 사슬을 갖는 공중합체.
- 모노비닐방향족 화합물 및 공액디엔의 다정형 커플링된 수지성 블록 공중합체로서, 상기 공중합체내 단량체의 총 중량을 기준으로 하여 약 55-약 95중량%의 중합된 모노비닐방향족 화합물을 갖고; 및 하기 중합체종:S-B-S-B-S-B-LiB-S-B-S-B-LiS-B-Li(상기에서 S=모노비닐방향족 블록 B=공액 디엔 블록 B/S=테이퍼드 블록 Li=리빙 중합체 부위 또는 커플링 부위)을 커플링시킴으로써 결과 얻어지는 중합체 사슬을 갖는 공중합체.
- 제17항에 있어서,상기 공중합체내 단량체의 총 중량을 기준으로 하여 약 60-약 90중량%의 중합된 모노비닐방향족 화합물을 갖는 공중합체.
- 제22항에 있어서,상기 공중합체내 단량체의 총 중량을 기준으로 하여 약 65-약 85중량%의 중합된 모노비닐방향족 화합물을 갖는 공중합체.
- 제1 또는 2항에 따른 방법에 의해 제조된 청색 수지성 블록 공중합체.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.