KR950000592A - 밀봉용 무연유리 - Google Patents
밀봉용 무연유리 Download PDFInfo
- Publication number
- KR950000592A KR950000592A KR1019940013944A KR19940013944A KR950000592A KR 950000592 A KR950000592 A KR 950000592A KR 1019940013944 A KR1019940013944 A KR 1019940013944A KR 19940013944 A KR19940013944 A KR 19940013944A KR 950000592 A KR950000592 A KR 950000592A
- Authority
- KR
- South Korea
- Prior art keywords
- lead
- mol
- phosphate glass
- free tin
- tin phosphate
- Prior art date
Abstract
산화물을 기준으로 하여 0-25% Li2O,0-25% Na2O 및 0-25% K2O로 구성된 최대 25몰%의 R2O와 최대 20몰%의 B2O3, 최대 5몰%의 Al2O3,최대 5몰%의 SiO2및 최대 5몰%의 WO3로 구성된 군으로 부터 선택된 일정 비율의 적어도 하나의 안정화 산화물이 총 25몰%까지 유효량으로 포함되고, 25-50몰%의 P2O5, 30-70몰%의 SnO,0-15몰%의 ZnO로 필수적으로 이루어지며, 상기 SnO/ZnO의 몰비가 5:1 이상인 것을 특징으로 하는 무연 인산염 주석 유리에 관한 것이다. 특히 본 발명의 유리는 전기와 전자 소자의 구성 부품을 결합시키기 위해 사용되는 밀봉재료의 밀봉유리 프릿으로써 유용하다. 밀봉 유리 재료에는 120×10-7/。C 이하의 열팽창계수를 지니는 강도 보강 첨가제 뿐만 아니라, 밀봉시 열팽창계수를 낮추기 위한 밀 첨가제가 첨가될 수 있다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (10)
- 산화물을 기준하여 0-25% Li2O,0-25% Na2O 및 0-25% K2O로 구성된 R2O 최대 25몰%와, B2O3최대 20몰%, Al2O3최대 5몰%, SiO2최대 5몰% 및 WO3최대 5몰%로 구성된 군으로 부터 선택된 상기 비율의 적어도 하나의 안정화 산화물이 총 25몰%까지 유효량으로 포함되고, 25-50몰%의 P2O5, 30-70몰%의 SnO, 0-15몰%의 ZnO로 필수적으로 이루어지며 상기 SnO/ZnO의 몰비가 5:1 이상인 것을 특징으로 하는 무연 주석 인산염 유리.
- 제 1 항에 있어서, 상기 선택된 안정화 산화물이 B2O3또는 Al2O3인 것을 특징으로 하는 무연 주석인산염 유리.
- 제 1 항에 있어서, 상기 P2O5의 함량이 29-35몰%인 것을 특징으로 하는 무연 주석 인산염 유리.
- 제 3 항에 있어서, 상기 P2O5가 약 33몰%인 것을 특징으로 하는 무연 주석 인산염 유리.
- 제 1 항에 있어서, 최대 5몰%의 WO3, 최대 5몰%의 MoO3, 최대 0.10몰%의 Ag 금속으로 구성된 군에서 선택된 상기 비율의 적어도 하나의 밀봉 접착 촉진제를 유효량 함유시킨 것을 특징으로 하는 무연주석 인산염 유리.
- 제 1 항 내지 제 5 항중 어느 한 항에 있어서, 융해밀봉 프릿의 열팽창계수를 낮추기 위해 낮은 열팽창계수를 지닌 밀 첨가제를 부가적으로 함유시킨 것을 특징으로 하는 무연 주석 인산염 유리.
- 제 6 항에 있어서, 밀 첨가제가 Mg+2와CO+2로 구성된 군에서 선택된 적어도 하나의 양이온을 가진 피로인산염이나 마그네슘 피로인산염 결정 물질과 리튬 알루미노 실리케이트 유리-세라믹 및 코디어라이트로 구성된 군으로 부터 선택된 것을 특징으로 하는 무연 주석 인산염 유리.
- 제 1 항 내지 제 7 항중 어느 한 항에 있어서, 팽창계수가 120×10-7/。C보다 낮은 강도 보강 충진제가 함유된 것을 특징으로 하는 무연 주석 인산염 유리.
- 제 8 항에 있어서, 강도 보강 충진제가 알루미나와 지르콘으로 구성된 군에서 선택되는 것을 특징으로 하는 무연 주석 인산염 유리.
- 융해 밀봉 재료에 의해 제공되는 융해 밀봉에 의해 연결되는 적어도 2가지 구성부품으로 이루어진 합성제품 또는 밀봉 재료를 활성 성분으로 사용하는 것을 특징으로 하는 제 1 항 내지 제 9 항중 어느 한 항에 따른 유리.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.