KR930005663A - 다공성 중공 섬유막 및 그 제조 방법 - Google Patents
다공성 중공 섬유막 및 그 제조 방법 Download PDFInfo
- Publication number
- KR930005663A KR930005663A KR1019910016713A KR910016713A KR930005663A KR 930005663 A KR930005663 A KR 930005663A KR 1019910016713 A KR1019910016713 A KR 1019910016713A KR 910016713 A KR910016713 A KR 910016713A KR 930005663 A KR930005663 A KR 930005663A
- Authority
- KR
- South Korea
- Prior art keywords
- hollow fiber
- fiber membrane
- coagulation
- viscosity
- solvent
- Prior art date
Abstract
이 발명은 내표면은 치밀성이 없는 다공성 구조로 되어 있고 외표면은 미세기공의 치밀한 스킨층이 발달되어 있으며, 내부에는 내표면 근처로 다공성 구조로 이루고 치밀층과의 근처에 공동으로 이루어진 방사 구조를 갖는 중공 섬유막 및 그 제조방법을 제공한다. 이 발명에 의하여 제조된 중공 섬유막은 기존의 중공 섬유막에 비하여 높은 투수성과 내구성, 내압성등 기계적 성질이 뛰어나고 내산성, 내약품성 등 화학적 성질이 우수하며 모듈의 제작시 손상되지 않고 취급이 용이하여 의료용, 식품공업용, 정수처리용 등의 공업적 목적으로의 활용이 촉망된다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 이 발명의 한 실시예에 의해 얻어진 중공 섬유막의 단면도,
제2도는 실시예 3의 방법에 의하여 제조된 중공 섬유막의 막 두께에 따른 투수성 변화를 나타내며,
제3도는 비교예 1의 방법에 의하여 제조된 중공 섬유막의 막 두께에 따른 투수성 변화를 나타낸다.
Claims (19)
- 망상 구조를 갖는 중공 섬유막으로서, 그 내표면은 치밀성이 없는 다공성 구조로 되어 있고, 막 내부의 내표면 근처에는 다공성 구조를 이루나 외표면 근처에는 치밀한 스킨층이 존재하고 외표면 인접 부분의 가운데에 다수의 공동을 갖고 있으며 막 외표면은 치밀한 미세 기공으로 형성되는 것을 특징으로 하는 중공 섬유막.
- 제1항에 있어서, 중공 섬유막의 재질은 폴리설폰, 폴리에테르설폰, 폴리이미드, 폴리아미드, 폴리아크릴로니트릴, 또는 셀룰로오스 아세테이트로 이루어지는 것을 특징으로 하는 중공 섬유막.
- 제1항에 있어서, 중공 섬유막 내표면의 다공성 구조는, 지름 0.5㎛∼10㎛의 원형, 더욱 바람직하게는 0.5㎛∼5㎛의 슬릿트형의 기공으로 이루어지는 것을 특징으로 하는 중공 섬유막.
- 제1항에 있어서, 중공 섬유막 내부는 망상 구조로 되어 있고, 막 외표면 근처에 치밀층이 있고 그 인접 안쪽에 폭 5∼15㎛의 공동들이 용적비 20∼50％로 존재하는 것을 특징으로 하는 중공 섬유막.
- 제1항에 있어서, 중공 섬유사 외표면은 지름 0.02∼0.1㎛의 미공으로 이루어진 치밀한 스킨층이 0.1∼1㎛의 두께로 형성되어 있음을 특징으로 하는 중공 섬유막.
- 제1항에 있어서, 주공 섬유막은 강도 0.3g/den, 습윤강도 60％ 이상인 것을 특징으로 하는 중공 섬유막.
- 제1항에 있어서, 중공 섬유막은 단위면적당 투수성이 1,000∼9,000ℓ/m2·hr·atm인 것을 특징으로 하는 중공 섬유막.
- 폴리설폰수지와 수용성 고분자 및 이들의 공통 용매로 이루어진 방사원액을 2중관형 노줄의 외측관형을 통하여 압출하고 동시에 내부 응고액을 내측 관형에 주입하면서 계속적으로 공기 중에서 방사하고 외부 응고액에서 완전 상전이 된 후 수세하여 건조하는 것을 특징으로 하는 다공성 중공섬유막의 제조방법.
- 제8항에 있어서, 방사 원액은 폴리설폰 10∼25중량％, 수용성 고분자 5∼35중량％의 농도으로 공통의 용매에 첨가하여 소정의 점도로 제도되는 것을 특징으로 하는 방법.
- 제8항 또는 제9항에 있어서,수용성 고분자는 폴리에틸렌글리콜, 폴리비닐알콜, 폴리비닐피톨리돈 중에서 ]단독 또는 2종 이상 혼합하여 사용되는 것을 특징으로하는 방법.
- 제8항 또는 제9항에 있어서,공통 용매는 m-크레졸, 클로로벤젠, N-메틸-2-피톨리돈, 디메틸설폭사이드, 디메틸아세트아마이드, 디메틸포롬아마이드 중에서 단독 또는 2종 이상 혼합하여 사용함을 특징으로 하는 방법.
- 제8항 또는 제9항에 있어서, 방사 원액의 점도는 2,000∼60,000 센티포아스인 것을 특징으로 하는 방법.
- 제8항에 있어서, 내부 응고액은 폴리설폰에 대하여 양용매(good solvent)와 지점도, 저응고가의 비용매(poor solvent)및 고점도, 고응고가의 비용매의 3성분으로 혼합됨을 특징으로 하는 방법.
- 제8항 또는 제13항에 있어서, 내부 응고액은 응고가 10∼30이고, 점도가가 15∼20 센티포아스인 것을 특징으로 하는 방법.
- 제8항 또는 제13항에 있어서, 양 용매는 m-크레졸, 클로로벤젠, N-메틸-2-피롤리돈, 디메틸설폭사이드, 디메틸아세트아마이드, 디메틸포롬아마이드 중에서하나 이상 선택되어지는 것을 특징으로 하는 방법.
- 제8항 또는 제13항에 있어서, 저점도, 저응고가의 비용매는 점도가 3∼10 셀티포아스이고, 응고가가 7∼10인 물, 메탄올, 에탄올 중에서 하나 이상 선택되어지는 것을 특징으로 하는 방법.
- 제8항과 또는 제13항에 있어서, 고점도, 고응고가의 용매는 점도가 30∼100 센티포아스이고, 응고가가 8∼30인 에틸렌글리콜, 프로필렌글리콜, 글리세린, 부타디올 중에서 하나 이상 선택 되어지는 것을 특징으로 하는 방법.
- 제8항에 있어서, 응고 원액의 공기중 방사 높이는 5∼50cm인 것을 특징으로 하는 방법.
- 제8항에 있어서, 외부 응고액은 상기의 제16항에서의 지점도 저응고가 용매의 단독 또는 상기의 제15항에서의 양 용매와 혼합하여 응고가가 13인 것을 특징으로 하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.