KR910008187A - 저수축, 고강력 폴리(헥사 메틸렌 - 아디프아미드)사 및 이의 제조 방법 - Google Patents
저수축, 고강력 폴리(헥사 메틸렌 - 아디프아미드)사 및 이의 제조 방법 Download PDFInfo
- Publication number
- KR910008187A KR910008187A KR1019900016760A KR900016760A KR910008187A KR 910008187 A KR910008187 A KR 910008187A KR 1019900016760 A KR1019900016760 A KR 1019900016760A KR 900016760 A KR900016760 A KR 900016760A KR 910008187 A KR910008187 A KR 910008187A
- Authority
- KR
- South Korea
- Prior art keywords
- yarn
- tension
- stretching
- temperature
- decrease
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본발명에 따른 바람직한 사를 제조하는데 유용한 방법의 모식도이다.
Claims (25)
- 약50이상의 상재점도, 적어도 약 9.5g/d의 강력, 적어도 약 30g/d의 모듈러스, 약 2%미만의 160℃에서이 수축율. 약 83이상의 결정 완전지수. 및 약 105A이상의 장주기 간격을 갖는 적어도 약 85%의 폴리(헥사메틸렌 아디프아미드)를 함유하는 폴리아미드사.
- 제1항에 있어서, 적어도 약 35g/d의 모듈러스를 갖는 사.
- 제1항에 있어서, 적어도 약 1.15g/cc의 밀도를 갖는 사.
- 제1항에 있어서, 약 0.056이상의 복굴절을 갖는 사.
- 제1항에 있어서, 약 2.7이상의 장주기 강도를 갖는 사.
- 제1항에 있어서, 강력이 적어도 약 10g/d인 사.
- 제1항에 있어서, 적어도 약 18%의 파단신도를 갖는 사.
- 제1항에 있어서, 약 200g/dㆍ%이상의 강인성을 갖는 사.
- 제1항에 있어서, 약 225g/dㆍ%이상의 강인성을 갖는 사.
- 제1항에 있어서, 상대 점도가 약 60이상인 사.
- 제1항에 있어서, 약 80g/d이상의 음파 모듈러스를 갖는 사.
- 제1항에 있어서, 약 0.37g/d미만의 최대 수축 장력을 갖는 사.
- 제1항에 있어서, 약 0.30g/d미만의 최대 수축 장력을 갖는 사.
- 제1항에 있어서, 폴리아미드가 단독 중합체 폴리(헥사메틸렌 아디프아미드)를 포하마하는 사.
- 제1항에 있어서, 100면에서 측정시 62A이상의 겉보기 결정크기를 갖는다.
- 내용 없음.
- 적어도 최종 연신단계에서 공급사를 연신시키고: 적어도 최종 연신단계 동안 공급사를 가열하며: 사가 적어도 약 190℃의 사연신 온도로 가열되는 경우 연신 장력이 적어도 약 3.8g/d에 도달할 때까지 공급사의 연신 및 가열을 계속하고: 연신 후, 사의 최대 길이에 대한 길이 감소가 약 13.5 내지 약 30%로 되도록 사에 대한 장력을 충분히 감소시키며: 장력의 감소 동안, 최대 길이 감소에 도달하는 경우 적어도 약 190℃의 사 이완 온도로 사용 가열한 다음: 장력의 감소 후 사를 냉각 및 패키징(packaging)함을 특징으로 하여, 연시, 부분-연신 및 미연신사로 구성된 부류중에서 선택된 공급사로부터, 적어도 약 9.0g/d의 강력, 약 2.0%미만의 수축율 및 적어도 약 30g/d의 모듈러스를 가지며 적어도 약 85중량%의 폴리(헥사메틸렌 아디프아미드)를 포함하는 폴리아미드사를 제조하는 방법.
- 제17항에 있어서, 사의 최대 길이 감소가 약 15 내지 약 25%가 되도록 장력을 충분히 감소시키는 방법.
- 제17항에 있어서, 장력의 감소 동안 사가 약 83이상의 결정 완전지수를 갖기에 충분한 기간 동안 가열을 계속하는 방법.
- 제17항에 있어서, 장력의 감소를. 길이에서 초기 감소를 야기시키는 적어도 초기 이완 증가에서 부분적으로 장력을 감소시키고 그후 사가 최종 이완 증가에서 최대 길이 축소로 길이가 감소되도록 장력을 추가로 감소시킴에 의해 수행하는 방법.
- 제17항에 있어서, 다수의 사 말단에 대해 150 내지 750mpm의 패키징 방법 속도에서 동시에 수행하는 방법.
- 제17항에 있어서, 공급사는 부분-연신 또는 미연신 공급사이고 또한 연신은 최종 연신 단계전에 적어도 하나의 초기 연신을 포함하는 방법.
- 제17항에 있어서, 사 연신 온도는 약 190 내지 약 240℃이고 사 이완 온도는 약 190 내지 약 240℃인 방법.
- 제23항에 있어서, 연신 동안 가열은 약 220 내지 약 320℃의 온도를 갖는 오븐에서 수행하고, 오븐에서의 체류시간은 약 0.5내지 약 1.0초인 방법.
- 제23항에 있어서, 장력의 감소동안. 약 220 내지 약 320℃의 온도를 갖는 오븐에서 수행하고, 오븐에서의 체류시간은 약 0.5내지 약 1.0초인 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.