KR910008185A - 고 강도, 고 모듈러스 폴리아미드사 및 이의 제조방법 - Google Patents

고 강도, 고 모듈러스 폴리아미드사 및 이의 제조방법 Download PDF

Info

Publication number
KR910008185A
KR910008185A KR1019900016758A KR900016758A KR910008185A KR 910008185 A KR910008185 A KR 910008185A KR 1019900016758 A KR1019900016758 A KR 1019900016758A KR 900016758 A KR900016758 A KR 900016758A KR 910008185 A KR910008185 A KR 910008185A
Authority
KR
South Korea
Prior art keywords
yarn
polyamide
tension
heated
temperature
Prior art date
Application number
KR1019900016758A
Other languages
English (en)
Other versions
KR0142181B1 (ko
Inventor
러셀 클라크 3세 토마스
아놀드 코퍼. 쥬니어 죠셉
Original Assignee
이. 아이. 듀퐁 드 네모아 앤드 캄파니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=23684116&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=KR910008185(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 이. 아이. 듀퐁 드 네모아 앤드 캄파니 filed Critical 이. 아이. 듀퐁 드 네모아 앤드 캄파니
Publication of KR910008185A publication Critical patent/KR910008185A/ko
Application granted granted Critical
Publication of KR0142181B1 publication Critical patent/KR0142181B1/ko

Abstract

내용 없음

Description

고 강도, 고 모듈러스 폴리아미드사 및 이의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명에 따라 바람직한 사를 제조하는데 유용한 방법을 도시한 것이다.

Claims (27)

  1. 포름산에 대한 상대 점도가 약 50이상인 폴리아미드로 이루어진 폴리아미드사에 있어서, 폴리아미드가 폴리(헥사메틸렌 애디프아미드) 및 폴리(ε－카프로아미드)중에서 선택된 폴리아미드 약 85중량%이상을 포함하고 사의 강도가 약 11.0g/d이상이며, 160℃에서의 건식 열－수축율이 약 6.5%미만이고 정련 수축율이 약 7%미만이며, 탄성계수가 약 35g/d이상이고, 복 굴절율이 약 0.060이상이며, 시차 복굴절율(D:△0.90－0.00)이 0이상이고, 음파계수가 약 90g/d이상임을 특징으로 하는 폴리아미드사.
  2. 제1항에 있어서, 탄성계수가 약 40g/d이상인 폴리아미드사.
  3. 제2항에 있어서, 탄성계수가 약 45g/d이상인 폴리아미드사.
  4. 제1항에 있어서, 장주기 스페이싱(spacing)이 약 100A이상인 폴리아미드사.
  5. 제1항에 있어서, 강도가 약 11.5g/d이상인 폴리아미드사.
  6. 제1항에 있어서, 결정화 지수(crystal perfection index)가 약 73 이상인 폴리아미드사.
  7. 제1항에 있어서, 파단 신도가 약 10%이상인 폴리아미드사.
  8. 제1항에 있어서, 파단 신도가 약 14%이상인 폴리아미드사.
  9. 제1항에 있어서, 상대 점도가 약 60이상인 폴리아미드사.
  10. 제1항에 있어서, 폴리아미드가 폴리(헥사메틸렌애디프아미드) 단독 중합체를 포함하는 폴리아미사.
  11. 제10항에 있어서, 가시적인 결정의 크기가 100－면에 대해 측정할 경우 약 53A이상인 폴리아믿사.
  12. 제1항에 있어서, 사의 표준화 탄성도가 약 0.55이상인 폴리아미드사.
  13. 제1항에 있어서, 사의 표준화 항복 응력이 약 0.78이상인 폴리아미드사.
  14. 제1항에 있어서, 밀도가 1.143g/cc이상인 폴리아미드사.
  15. 공급사를 적어도 최종 연신단계에서 연신시키고: 상기 공급사를 적어도 상기 최종 연신단계가 진행되는 동안 가열시키고: 상기 사를 약 185℃이상의 사－연산 온도로 가열시킬 경우 장력이 약 3.8g/d이상으로 도달될때까지 계속해서 상기 공급 사를 연신 및 가열시키고, 상기 사의 길이를 최대 길이 감소분이 약 2내지 13.5%이 되도록 감소시키기에 충분하게 연신시킨 후 상기 사의 장력을 감소시키고, 상기 최대 길이 감소분에 도달되었을 때, 장력이 감소되는 동안에 사를 약 185℃이상의 사－이완 온도를 가열시키고, 장력을 감소시킨 후에 사를 냉각 및 패키징시킴을 특징ㅇ로 하여, 연신되거나 일부－연신되거나, 비－연신된 폴리아미드사 중에서 선택된 공급사로부터, 강도가 약 11.0g/d이상이고, 건식 열－수축율이 약 6.5%이하이며, 탄성계수가 약 35g/d이상인 폴리아미드사를 제조하는 방법.
  16. 제15항에 있어서, 장력을 충분히 감소시키고 사를 가열시켜 최대 길이 감소분을 약2 내지 약 10%로 제공하는 방법.
  17. 제15항에 있어서, 장력이 3.8g/d이상일 경우, 연신시키는 동안 사를 190℃로 가열시키는 방법.
  18. 제15항에 있어서, 최대 길이 감소분에 도달되었을때, 장력을 감소시키는 동안 사를 약 190℃이상의 온도로 가열시키는 방법.
  19. 제15항에 있어서, 장력을 초기 이완 증가분 이상으로 부분적으로 감소시켜 초기 길이 감소분을 수득한 후, 장력을 최종 이완 증가분 이상으로 추가로 감소시켜 사의 길이를 그 최대 길이 감소분으로 추가로 감소시킴으로써 장력을 감소시키는 방법.
  20. 제15항에 있어서, 다수의 사말단에서 150내지 750ppm의 패키징 속도로 동시에 수행하는 방법.
  21. 제15항에 있어서, 공급사가 부분적으로 연신되거나 비－연신된 공급 사이고, 연신 단계가 최종 연신단계 전에 하나 이상의 초기 연신단계를 포함하는 방법.
  22. 제15항에 있어서, 폴리아미드가 폴리(헥사메틸렌애디프아미드) 85중량%이상이고, 사－연신 온도가 약 190내지 약 240℃인 방법.
  23. 제22항에 있어서, 연신시키는 동안 약 220 내지 약 320℃의 온도를 갖는 오븐내에서 약 0.5 내지 약 1.0초 동안 가열시키는 방법.
  24. 제22항에 있어서, 장력을 감소시키는 동안 약 220 내지 약 320℃의 온도를 갖는 오븐내에서 약 0.5 내지 약 1.0초 동안 가열시키는 방법.
  25. 제15항에 있어서, 폴리아미드가 폴리(ε카프로아미드)85중량%이상이고, 사－연신 온도가 약 185 내지 약 215℃이며, 사－이완 온도가 약 185 내지 약 215℃인 방법.
  26. 제25항에 있어서, 연신시키는 동안 약 220 내지 약 320℃의 온도를 갖는 오븐내에서 약 0.5 내지 약 1.0초 동안 가열시키는 방법.
  27. 제25항에 있어서, 장력을 감소시키는 동안 약 220 내지 약 320℃의 온도를 갖는 오븐내에서 약 0.5 내지 약 1.0초 동안 가열시키는 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019900016758A 1989-10-20 1990-10-20 고강도, 고모듈러스 폴리아미드사 및 이의 제조방법 KR0142181B1 (ko)