KR900016461A - 우수한 자기특성과 필름특성을 가진 방향성 전기강판의 제조방법 - Google Patents

우수한 자기특성과 필름특성을 가진 방향성 전기강판의 제조방법 Download PDF

Info

Publication number
KR900016461A
KR900016461A KR1019890005445A KR890005445A KR900016461A KR 900016461 A KR900016461 A KR 900016461A KR 1019890005445 A KR1019890005445 A KR 1019890005445A KR 890005445 A KR890005445 A KR 890005445A KR 900016461 A KR900016461 A KR 900016461A
Authority
KR
South Korea
Prior art keywords
weight percent
annealing
gas
strip
ppm
Prior art date
Application number
KR1019890005445A
Other languages
English (en)
Other versions
KR930001332B1 (ko
Inventor
히사시 고바야시
가쯔로 구로끼
마사요시 미나구찌
겐이찌 야가시로
Original Assignee
사이또오 유다까
신닛뽄 세이데쓰 가부시끼가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 사이또오 유다까, 신닛뽄 세이데쓰 가부시끼가이샤 filed Critical 사이또오 유다까
Publication of KR900016461A publication Critical patent/KR900016461A/ko
Application granted granted Critical
Publication of KR930001332B1 publication Critical patent/KR930001332B1/ko

Abstract

내용 없음.

Description

우수한 자기특성과 필름특성을 가진 방향성 전기강판의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 질화처리를 했을 때 관찰된 질화시간과 강중의 질소함량간의 관계를 나타내는 것으로서 가스 혼합물의 종류와 양에 대하여 도시되었다.
제2도는 H2가스와 NH3가스로 이루어 진 가스혼합물로 30초동안 질화처리한 시료가 마무리 소둔후 양호한 2차 재경정을 나타내는 영역을 도시한 것으로서, 질화온도와 암모니아 농도에 대해 도시되었다.
제3도는 양호한 2차 재결정을 제공하는 지역을 나타낸 것으로서 마무리 소둔로내의 가스분위기와 강중의 질소함량에 대해 도시되었다.

Claims (6)

  1. 0.025내지 0.075중량%의 C,2.5내지 4.5중량%의 Si, 0.012중량%까지 S, 0.010내지 0.060중량%이 산가용성 N, 0.010중량%까지의 N, 0.08내지 0.45중량%의 Mn, 0.015내지 0.045중량%의 P와 Fe와 불가피한 불순물로 구성되는 잔부로 이루어지는 전기강슬랩을 1200℃보다 낮은 온도로 가열하고, 슬랩을 열간압연하고, 1회 또는 그사이에 중간소둔을 끼워넣은 적어도 2회의 냉간압연함으로써, 두께를 최종 두께로 감소시키고, 탈탄소둔을 시행하고, 스티립을 이동시키면서 질화처리를 시행하고, 스트립위에 소둔분리제를 도포하고, 도포된 스트립을 고온 마무리 소둔하는 것으로 이루어지는 것을 특징으로 하는, 우수한 자기특성과 필름특성을 가진 방향성 전기강판을 제조하는 방법.
  2. 제1항에 있어서, 스트립을 이동시키면서 행하는 질화처리를 NH3가스 농도가 1000ppm내지 10%이고, N2가스에 대한 H2가스의 혼합비율이 적어도 50%인 분위기 속에서 15내지 60초 동안 500내지 900℃외 온도에서 수행하는 것을 특징으로 하는 방법.
  3. 제1항 또는 제2항에 있어서, 고온 마무리 소둔을 600내지 850℃의 온도로, 약산화 분위기내에서 수행하는 것을 특징으로 하는 방법.
  4. 제3항에 있어서, 질소를 강중에 적어도 100ppm의 양으로 존재하도록 하고 나서 고온 마무리 소둔을 수행하는 것을 특징으로 하는 방법.
  5. 제3항에 있어서, 질소를 강중에 적어도 180ppm의 양으로 존재하도록 하고나서 고온 마무리 소둔을 수행하는 것을 특징으로 하는 방법.
  6. 제1항에 있어서, 스트립을 이동시키면서 행하는 질화처리를 산화 포텐샬 pH2O/pH2가 0.04까지인, 수소가스와 질소가스로 이루어지는 가스혼합물 또는 수소가스속에 최소한 1000ppm외 NH3를 함유시킴으로써 형성된 분위기속에서 500내지 900℃의 온도로 수행하는 것을 특징으로 하는 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019890005445A 1988-04-25 1989-04-25 자기특성과 피막특성이 우수한 일방향성 전자강판의 제조방법 KR930001332B1 (ko)