KR880000618B1 - 초단파 가열 유동상 반응에 의한 고순도 다결정 실리콘의 제조 방법 - Google Patents

초단파 가열 유동상 반응에 의한 고순도 다결정 실리콘의 제조 방법 Download PDF

Info

Publication number
KR880000618B1
KR880000618B1 KR1019850009938A KR850009938A KR880000618B1 KR 880000618 B1 KR880000618 B1 KR 880000618B1 KR 1019850009938 A KR1019850009938 A KR 1019850009938A KR 850009938 A KR850009938 A KR 850009938A KR 880000618 B1 KR880000618 B1 KR 880000618B1
Authority
KR
South Korea
Prior art keywords
silicon
reactor
fluidized bed
microwave
gas
Prior art date
Application number
KR1019850009938A
Other languages
English (en)
Other versions
KR870005910A (ko
Inventor
윤풍
송영목
Original Assignee
재단법인 한국화학연구소
채영복
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 재단법인 한국화학연구소, 채영복 filed Critical 재단법인 한국화학연구소
Priority to KR1019850009938A priority Critical patent/KR880000618B1/ko
Priority to JP61215588A priority patent/JPS6355112A/ja
Priority to GB08622195A priority patent/GB2185008A/en
Priority to KR1019860008505A priority patent/KR880001252B1/ko
Priority to US06/925,775 priority patent/US4900411A/en
Priority to IT22208/86A priority patent/IT1198065B/it
Priority to DE19863638931 priority patent/DE3638931A1/de
Priority to US07/008,899 priority patent/US4786477A/en
Publication of KR870005910A publication Critical patent/KR870005910A/ko
Application granted granted Critical
Publication of KR880000618B1 publication Critical patent/KR880000618B1/ko

Abstract

내용 없음.

Description

초단파 가열 유동상 반응에 의한 고순도 다결정 실리콘의 제조 방법
제1도는 본 발명을 구현하는 제조장치의 일예를 도시하는 개략 측면도.
제2도는 제1도의 요부 발췌도.
제3도는 제조장치의 다른 예를 도시하는 개략측면도.
* 도면의 주요부분에 대한 부호의 설명
1 : 가열로 2 : 반응기
3 : 개스 유출관 5 : 홀더
6 : 스프링 12 : 개스분산판
17 : 기화기/예열기 18 : 초단파 발생 장치
19, 20, 21 : 도파관 23 : 초단파 차폐관
24 : 초단파모드
본 발명은 고순도 다결정 실리콘의 제조방법에 관한 것이다. 더 상세히 설명하면 본 발명은 초단파에 의해 가열되는 유동상 반응기에서 고순도 실리콘 입자 상에 실란(SiH4), 2염화실란(SiH2Cl2), 3염화실란(SiHCl3)3 브롬화실란(SiHBr3)등과 같은 실리콘 함유 개스의 열분해나 수소환원 반응에 의한 화학 증착으로 실시콘을 석출하는 고순도 다결정 실리콘의 제조방법에 관한 것이다. 종래, 고순도 다결정을 제조하는 대표적인 방법으로서는 전기 저항에 의해 가열된 실리콘 봉상에서 3염화실란이나 2염화실란의 수소환원 반응에 의해 실리콘을 석출하는 시멘스 공정(Siemens Process)(참조 : 미합중국 특허 제3,268,085)과 실란의 열분해 반응에 의해 석출되는 고마쯔 공정(Komatsu Process)(참조 : 미합중국 특허 제4,147,814호, 동 제4,150,168호)에 의해 제조되어 왔다.
전자는 실리콘 봉이 저항 가열에 의해 1000~1200℃로 가열되며 후자는 열 분해 온도인 800℃로 가열된다. 그리고, 이들 두 공정에 사용된 반응기는 동일 형태로 석영이나 스텐 레스 벨 쟈(bell jar)로 물이나 공기등의 냉매에 의해 반응기 벽면이 300℃이하로 냉각되어 내벽면에 실리콘이 석출되지 않는 장점이 있으나, 이들 공정은 회분식공정으로, 실리콘 봉을 사용하기 때문에 석출 면적이 적어 단위 시간당 석출량이 적을 뿐 아니라 제조에 요하는 단위당 에너지 소모량이 많은 결점이 있다. 따라서, 이러한 문제점을 해결하기 위하여 석출 면적이 큰 입자상 실리콘 입자상에 석출시키는 방식, 즉 유동상을 이용하는 방식으로 개선되어 왔다. 그러나, 이러한 유동상을 가열시키는 장치로는 일반적으로 저항식 가열기 등에 의한 외부 가열 방식이 채택되었는데 (참조 : 미합중국 특허 제3,012,861호, 동 제3,012,862, 동 제4,207,360호, 동 제3,963,838호, 일본국 특허출원공개 소59-45916호, 동 소 59-45917호, 동 소57-135708호)이들을 피 가열물 보다 반응기 벽면온도가 높아 장치 재료의 내열성이 요구되며 또한 장치 외부로의 방열량 증대에 수반되는 열량 손실이 증가할 뿐 아니라, 한정된 전열 면적을 가지기 때문에 장치의 대형화가 어렵다. 특히, 실란의 열분해나 3염화 실란 또는 2염화 실란의 수소환원 반응에 의해 반응기 내 벽면에 실리콘이 석출되어 반응기 내부가 점점 협소하게 될 뿐 아니라 전열 상태가 불량해져서 종국에는 조업을 불가능하게 한다.
또한, 반응기 벽면으로 부터의 오염을 방지하기 위하여 사용되는 석영 반응관의 경우 반응기를 냉각시킬 때 석영반응관과 석출된 실리콘과의 열 팽창 차로 인해 반응관이 부서지는 현상(참조 : 미합중국 특허 제3,963,838호)이 발생한다. 이러한 결점을 제거하기 위하여 외부 가열 방식 대신 내부에 저항 가열기를 설치하는 내부 가열 방식이 고려 되었다. 그러나, 이 방식도 가열기 표면에 실리콘이 석출되기 때문에 장시간 사용이 불가능 할 뿐 아니라 가열기의 보수, 교환등의 구조적인 문제점을 안고 있다.(참조 : 일본국 특허출원 공개 소58-185427호)
특히, 원관형의 유동상은 피가열물인 입자의 유동상태를 양호하게 유지하여야 하기 때문에 내부에 가열기 설치는 제한을 받게 되며 전열 면적의 효과가 저하되는 문제점이 있다.
본 발명자들은 상기의 여러가지 단점을 제거하기 위하여 위해 예의, 인구 검토한 결과 가장 효과적인 가열 방식으로 초단파에 의한 직접 가열장치를 시도하였다. 초단파에 의해 형성되는 전자기장에서 피 가열물의 분극진동에 의해 야기되는 분자간의 마찰로 자체 열이 발생하는 반면에 석영 반응기는 초단파를 투과하기 때문에 자체 열이 발생되지 않으므로 반응기 벽면 온도를 피 가열물의 온도 보다 낮출수 있는 잇점이 있다. 또한, 가열로 내부에 냉매의 주입이 가능하여 반응기 벽면 온도를 원하는 온도로 냉각할 수 있어 내벽면에의 실리콘 석출을 방지할 수 있다. 그리고, 초단파는 유동상 반응기 내부에 있는 피 가열물에 직접 침투하여 전자기장을 형성시키므로 넓은 전열 면적을 가질 뿐 아니라 장치의 대형화 및 장기 운전이 가능해 연속적으로 대량의 고순도 다결정 실리콘을 제조할 수 있다.
이하 첨부된 도면에 의해 본 발명을 상세히 설명한다. 제1도는 본 발명 유동상 반응기의 새로운 가열 방식에 의한 고순도 다결정 실리콘 제조장치의 한 실시 태양을 나타낸다. 부호 1은 고온에 잘 견디고 초단파를 손실없이 반사시키는 금속, 예컨데, 스텐레스 스틸과 같은 금속재로 된 가열로이며 부호2는 가열로(1)의 중심부에 설치되는 원통형의 석영 반응기이다. 석영 반응기(2)의 상단은 가열로(1)의 내측 상부에서 개스 유출관(3) 접속된다. 개스유출관(3)은 가열로(1)의 외부로 도출되어지나 비고정상으로 설치되고, 석영 반응기(2)와의 연결부에는 그라파이트 가스켓(4)이 개재 된다. 그라파이트 가스켓(4)은 개스 유출관(3)측에 형성된 홀더(5)에 의해 위치 보전되는 한편 홀더(5)는 스프링(6)에 의해 축 방향으로 탄발력을 받기 때문에 석영 반응기(2)로 홀더(5)를 통해 스프링(6)의 압력이 가해져서 다소 유동하여도 연접부가 긴밀하게 압착되어지게 된다. 개스 유출관(3)의 내부에는 종자 주입관(7)이 삽통되며, 종자 주입관(7)의 일단을 석영반응기(2)의 내부로 연장시키고 타단은 가열로(1)의 외부로 돌출시켜 호퍼(3)에 연결된다.
가열로(1)에서 개스 유출관(3)이 관통 설치되는 부위에는 테프론 시일(9)이 장설되고 이를 차단 홀더(10)로 보전하여 기밀이 유지되도록 한다. 가열로(1)의 하측에는 개스 주입관(11)이 개설되며, 이개스 주입관(11)과 석영반응기(2)의 하단 사이에 개스분산판(12)이 개재된다. 개스 분산판(12)에는 냉매통로(13)를 보유한다. 석영 반응기(2)의 하측에는 입자 유출관(14)이 연통되어 외부의 실리콘 수거 용기(15)에 연관된다. 여기서 석영 반응기(2)에서 반응 개스가 가열로(1)로 누출되는 것을 방지하기 위하여 그라파이트 가스켓(16)을 개재시킨다.
한편, 전기한 개스 주입관(11)의 입구측에 기화기/예열기(17)가 장설된다. 가열로(1)의 양측방에는 통상적인 초단파 발생장치(18)가 설치된다. 초단파 발생장치(18)에서 연장된 도파관(19)은 가열로(1)의 하부 측방으로 E코너 도파관(20) 및 H코너 도파관(21)은 초단파 발생장치(18)의 마그테트론(도시생략)으로 부터 발진되는 초단파를 가열로(1)로 유도하기 위한 것이므로 초단파의 전송 손실이 극소한 알미늄과 같은 재질의 관을 사용하는 것이 바람직스럽다.
E코너 도파관(20)과 H코너 도파관(21)의 도중에는 개스 차단막(22)이 1이상 시설된다. 이 개스 차단막(22)은 가열로(1)에서 석영 반응기(2)의 벽면을 냉각하는 냉매가 초단파 발생장치(18)로 역류하는 것을 방지하는 것으로 초단파의 투과성 좋은 석영, 파이렉스 혹은 테프론과 같은 재질의 막을 채용하는 것이 좋다. 한편, 가열로 (1)의 내부 상측으로 초단파 차폐판(23)이 설치된다.
초단파 차폐판(23)은 초단파를 되 반사시켜 주는 금속으로 되어 있으며 이것에 의해 가열로(1)내에서 초단파 침투체적이 제한되어 지고 그 결과 초단파 침투밀도가 높아져서 양호한 초단파 가열이 행해질 수 있게 된다.
상술한 구성의 본 발명 장치에서 실리콘 종자는 호퍼(8)에서 종자 주입관(7)을 통해 석영 반응기(2)로 투입 공급되어 유동상 A를 형성하게 된다. 이 경우 초단파 발생장치(18)는 발진하여 가열로(1)의 내부로 초단파를 발사한다. 초단파는 가열로(1)내에서 석영반응기(2)를 투과 하면서 유동상A를 형성하고 있는 실리콘 종자내부에 침투하여 전자기장을 형성한다. 이 전자기장의 형성에 의해 실리콘 종자에는 분극진동 마찰이 발생하여 반응 온도인 600~1200℃까지 자체 가열된다. 이때 통상적으로 915MHz나 2450MHz의 초단파가 이용된다. 한편, 반응 캐스로서 실리콘 함유 개스는 수소 개스와 같은 운반 개스와 함께 기화기/예열기(17)을 거쳐 300℃정도로 예열된 후 개스 주입관 (11)을 통해 주입된다.
주입되는 반응 개스는 개스 분산판(12)에 의해 석영 반응기(2)의 내부로 확산되어 유동상 A에 혼입 유동화 된다. 이렇게 혼입 유동화 되는 반응 개스는 실리콘 종자와 접촉하면서 열 분해나 수소환원 반응이 일어나 석축되는 실리콘이 종자 표면에서 화학 증착하게 되고 이것은 점점 성장하게 된다. 이렇게 하여 충분히 성장한 입자는 입자 유출관(14)를 거쳐 실리콘 수거용기(15)로 수집된다.
상기 과정중에 실리콘 종자와 반응 개스는 연속적으로 공급될 수 있으므로 실리콘 입자는 연속적으로 제조될 수 있다. 그리고, 상기 반응에 의해 생성되는 부생 개스나 미반응 개스는 개스 유출관(3)을 통하여 유출되어 회수 장치(도시생략)에 의해 회수, 재 사용된다. 한편, 이들 반응이 진행되는 동안 고온의 실리콘 입자로 부터 전도 되는 열량에 의해 개스 분산판(12)이 가열되면 여기를 통과하는 반응 개스에 의해 개스 분산판(12)의 표면에 실리콘이 증착되어 유동상 A의 실리콘 입자를 정상적으로 유동화 시킬 수 없게 된다.
본 발명에서 이와 같은 문제점은 냉매통로(13)로 물이나 질소와 같은 냉매를 순환시켜 개스 분산판(12)의 온도를 400℃이하로 냉각시켜 주는 것에 의해 내부 면적이 협소해 지는 수가 있다. 이를 방지하기 위하여 가열로(1)의 내벽과 석영 반응기(2)의 외벽 사이로 형성되어진 냉각통로(25)에도 냉매를 주입 순환시켜 석영 반응기(2)의 내벽면을 실리콘 함유 개스의 반응 온도 이하로 냉각시켜 준다. 또한, 석영 반응기(2)는 2중관 형태의 별도의 냉각통로(26)를 보유할 수도 있다.
실리콘 종자가 석영 반응기(2) 내부에서 초단파에 의해 가열되면 석영 반응기(2)는 전도되는 열량에 의해 가열되어 열 팽창하게 된다. 그러나, 가열로(1)는 열 팽창이 되지 않으므로 이때 석영 반응기(2)가 파쇄되는 일이 생길 수 있다.
본 발명에서 석영 반응기(2)가 열 팽창에 의해 신장되면 개스 유출관(3)의 홀더(5)를 지지하는 스프링(6)이 압축되어서 석영 반응기(2)는 파쇄되는 일이 생기지 않는다.
상술한 본 발명 장치의 실시예는 초단파를 가열로(1)의 측방에서 투사해 주는 구성이기 때문에 균일한 가열을 도모하기 위하여 적어도 1쌍 이상의 초단파 발생장치(18)을 필요로 한다.
초단파를 가열로 (1)의 상방에서 투사할 때는 단일의 초단파 발생 장치만이 필요하게 될 것이다.
제2도는 가열로 (1)의 E코너 도파관(20)과 H코너 도파관(21)이 연관된 구성을 예시한다. E코너 도파관(20)과 H코너 도파관(21)은 단면이 직사각형을 이루고 이들은 반응기(2)의 양측에 상호 대향 설치한 양태로 되기 때문에 이들 연관 부위로 부터 가열로(1)에 유입되는 초단파 모드(24)는 상호 길이 방향으로 교차하여 상호 초단파가 역류되는 일이 없다. 또한 E코너 도파관(21)이 교차상으로 대향하여 설치된 것에 가열로(1) 내부로 효율적인 초단파 확산이 행해지게 되고, 그 결과 초단파 발생장치(18)의 용량을 줄어 에너지 절약을 도모할 수 있게 된다.
본 발명의 고순도 다결정 실리콘을 다량으로 제조하기 위하여 큰 용량의 반응관을 사용할 때는 복수의 E코너 도파관과 복수의 H코너 도파관을 대향하여 배설하거나 동일 모드 즉, E코너 도파관이나 H코너 도파관의 아느 한 모드만을 지그재그상으로 복수개 설치하여 초단파를 동시에 여러 부위에서 통과시켜 단시간에 다량의 실리콘을 제조할 수 있다.
제3도는 본 발명의 다른 일실시 태양으로서 가열로(1)의 상방에서 초단파를 투사하는 구성을 나타낸다. 제3도에는 상기 실시예와 동일한 부분에는 동일 부호가 부여된다.
도파관(19)는 가열로(1)의 상방에서 연관 접속된다. 이때 도파관(19)는 통상적으로 단면 직사각형 또는 원통형의 형태로 구성되어 있고 원통상의 도파관 형태의 가열로(1)에는 접속관(190)을 사용하여 연통시킨다. 개스 유출관(3)과 그 내부의 종자 주입관(7)은 도파관(19)를 관통하여 가열로(1) 내로 진입해서 석영반응기(2)와 연관되어 진다.
특히, 석영 반응기(2)의 상부는 개스 유출관(3)과 직통 연관되어 지고 하측은 반응 개스가 가열로(1)로 누설되지 않는 구조를 취한다. 즉, 가열로(1)의 하측 플랜지(100)과 석영 반응기(2)의 플랜지(200) 사이에 0링형으로 된 그라파이트 가스켓(300)을 개재시키고 또한 플랜지(200)과 개스 분산판(12) 사이에 그라파이트 가스켓(400)을 개재시켜 완벽하게 밀봉 처리한다.
상기한 실시예는 단일의 초단파 가열장치(18)만이 요구되므로 설비비와 보수관리 및 에너지 절감의 효과를 얻을 수 있다. 또한, 석영 반응기(2) 대신에 고순도 실리콘 반응기를 사용할 수 있다. 그러나, 이때에는 반응기 상부(30)를 석영재 또는 초단파가 투과할 수 있는 재료를 사용하여야 한다.
이하 본 발명 장치에 의해 제조되는 고순도 다결정 실리콘의 제조 방법 실시예를 상술한다.
[실시예 1]
48mmID, 두께 2.5mm, 높이 1000mm의 석영반응기가 제1도의 가열로 내부에 설치되며 가열 원인 초단파는 60/100 메쉬크기의 실리콘 입자가 내장된 유동상으로 석영 반응기 벽면을 통하여 공급되며 실리콘의 분극 진동 마찰에 유동상은 700℃ 유지된다.
한편 반응 개스는 실란 20몰 %와 수오 80몰 %가 혼합하여 상온에서 13.3ℓ/min 속도로 예열기를 거치면서 300℃로 예열된 후 물로 냉각되는 분산판을 통하여 유동상에 공급된다. 이때 가열로 내부에 적적한 양의 질소 개스를 주입하여 석영 반응관 벽면을 냉각하였다. 유동상 높이는 약 150mm로 유지시키면서 실리콘의 증착으로 증가되는 시릴콘 량은 유출관을 통하여 간헐적으로 유출하였다. 10시간의 조업으로 평균 162.5g/hr의 속도로 다결정 실리콘이 얻어졌으며 석영 반응기 벽면의 실리콘 증착은 거의 없었다.
[실시예 2]
실시예 1의 장치를 사용하고 반응 개스만 실란 10몰 %와 90몰 %로 혼합되어 상온에서 13.9ℓ/min속도로 예열기를 거치지 않고 바로 분산판을 통하여 유동상에 공급하는 것을 제어하고 실시예1과 동일하게 10시간의 조업결과 평균 82.8g/hr의 속도로 다결정 실리콘이 얻어졌다.
[실시예 3]
실시예 1의 장치를 사용하고 40/60 메쉬의 입경을 갖는 실리콘을 재장하고 유동상의 높이는 약 150mm로 유지하면서 실란 22몰 %, 수소 78몰 %의 혼합반응 개스를 36.4ℓ/min로 공급되며 예일기를 거쳐 300℃로 예열된 후 유동상에 공급되는 것 이외에는 실시예 1과 동일하게 10시간 조업결과 평균 268.1g/hr의 속도로 다결정 실리콘이 얻어졌다.
[실시예 4]
실시예 1의 장치를 사용하고 40/60메쉬의 입경을 갖는 실리콘을 내장하고 실리콘 유동상의 높이를 약 150mm로 유지하면서 실란 10몰 %, 수소 90몰 %의 혼합반응 개스를 11.5ℓ/min속도로 예열기를 거치지 않고 유동상에 공급하는 것 이외에는 실시예 1과 동일하게 20시간 조업결과 평균 63g/hr의 속도로 다결정 실리콘이 얻어졌다.
[실시예 5]
98mmID, 두께 3.0mm, 높이 1500mm의 석영 잔응기가 제3도의 가열로인 원통형 도파관 내부에 설치되며 가열 원인 초단파는 유동층 상부에서 공급된다.
한편 60/100 메쉬의 입경을 갖는 실리콘 2400g이 종자 주입관을 통하여 석영 반응기에 주입되어 유동상을 형성하며 유동상의 온도가 670℃로 유지된다. 그리고 반응 개스는 실란 10몰 %, 수소 90몰 %로 혼합되며 상온에서 22.8ℓ/min 속도로 예열기를 거쳐 유동상 내부에 공급된다. 이때 석영 반응기 벽면은 질소에 의해 냉각된다. 1시간의 조업 후 151g의 다결정 실리콘이 얻어졌다. 그리고, 석영 방응기 내벽면에의 실리콘 증착은 없었다.
[실시예 6]
실시예 5의 반응기를 사용하고 반응기 내부에 60/100 메쉬의 입경을 실리콘 3200g을 넣어 유동상을 형성하였으며 유동상의 온도는 700℃로 유지된다. 실란 20몰 %, 수소 80몰 %의 혼합반응 개스로 상온에서 31.9ℓ/min 속도로 예열기를 거쳐 유동상 내부에 공급된다. 이때 석영 반응기 벽면에는 냉각 개스에 의한 냉각은 없다. 1시간의 조업이 끝난 후 355g의 다결정 실리콘이 얻어졌다. 그러나 석영 반응기 벽면에 약간의 실리콘 증착이 확인 되었다.
[실시예 7]
실시예 5의 반응기를 사용하고 반응기 내부에 40/60 메쉬의 입경을 갖는 실리콘 3200g을 넣어 유동상을 형성하였으며 유동상 온도를 700℃로 유지된다. 실란 10몰 %, 수소 90몰 %의 혼합 개스로 상온에서 42.4ℓ/min 속도로 공급되며 예열기를 거쳐 350℃로 예열되어 유동상 내부에 공급된다. 이때 석영 반응기 벽면은 질소에 의해 냉각된다. 1실간의 조업이 끝난 후 270g의 다결정 실리콘이 얻어졌으며 석영 반응기의 내벽면에 실리콘 증착 흔적은 보이지 않는다.
본 발명은 범위는 첨부된 도면, 실시예, 발명의 설명에 포함되는 모든 기술뿐만 아니라 이와 직접 간접으로 관련되고 본 발명의 기술사상의 모든 기술을 포함한다.

Claims (2)

  1. 유동상 반응기를 이용하여 고순도 실리콘 입자상에 실란, 2염화실란, 3염화실란, 3브롬화실란과 같은 실리콘 함유 개스로부터 실리콘을 석출하여 고순도 다결정 실리콘을 제조하는 방법에 있어서, 유동상 반응기 내에 실리콘 종자를 주입하고 반응 개스 유입관을 통해 반응 개스를 주임함과 동시에 도파관을 통해 초단파를 발진하여 가열된 유동상의 실리콘 입자와 접촉시켜 실리콘을 석출시킴을 특징으로 하는 고순도 다결정 실리콘의 제조방법.
  2. 제1항에 있어서, 고순도 다결정 실리콘 입자를 초단파로 가열함을 특징으로 하는 방법.
KR1019850009938A 1985-12-28 1985-12-28 초단파 가열 유동상 반응에 의한 고순도 다결정 실리콘의 제조 방법 KR880000618B1 (ko)