KR860007017A - 촉매 지지체용 고표면적 집괴의 제조방법 및 상기 집괴를 함유하는 모노 리드식 지지체 구조물의 제조방법 - Google Patents

촉매 지지체용 고표면적 집괴의 제조방법 및 상기 집괴를 함유하는 모노 리드식 지지체 구조물의 제조방법 Download PDF

Info

Publication number
KR860007017A
KR860007017A KR1019860001320A KR860001320A KR860007017A KR 860007017 A KR860007017 A KR 860007017A KR 1019860001320 A KR1019860001320 A KR 1019860001320A KR 860001320 A KR860001320 A KR 860001320A KR 860007017 A KR860007017 A KR 860007017A
Authority
KR
South Korea
Prior art keywords
alumina
mixture
support
phase
surface area
Prior art date
Application number
KR1019860001320A
Other languages
English (en)
Other versions
KR930005311B1 (ko
Inventor
마르틴 골리노 카를로
마르틴 골리노 카를로 (외 1)
모리스 라크만 어윈
Original Assignee
코오닝 글라스 워크스
알프레드 엘. 마이클슨
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코오닝 글라스 워크스, 알프레드 엘. 마이클슨 filed Critical 코오닝 글라스 워크스
Publication of KR860007017A publication Critical patent/KR860007017A/ko
Application granted granted Critical
Publication of KR930005311B1 publication Critical patent/KR930005311B1/ko

Abstract

내용 없음

Description

촉매 지지체용 고표면적 집괴의 제조방법 및 상기 집괴를 함유하는 모노 리드식 지지체 구조물의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (28)

  1. 고표면적 집괴를 제조하는데 있어서, (a) (i) 알루미나, 실리카, 스피넬, 티타니아, 제올라이트, 지르코니아 및 이들의 혼합물로부터 선택된 최소한 20m2/g의 표면적을 갖는 다공성 산화물, 및 (ii) 산화물용 결합제를 실질적으로 균질인 혼합물로 혼합하고, (b) 상기 혼합물을 건조시키고, 및 (c) 건조된 혼합물을 50~250미크론의 평균 직경을 갖는 입자로 형성시킴을 특징으로 하는 방법.
  2. 제1항에 있어서, 혼합공정(a)를 다공성 산화물 100중량부당 결합제 5~60중량부를 사용하여 수행함을 특징으로 하는 방법.
  3. 제1항에 있어서, 결합제가 실리콘수지, 중합된 푸르푸릴알코올, 메틸셀룰로스, 폴리비닐알코올 또는 이들의 혼합물임을 특징으로 하는 방법.
  4. 제2항에 있어서, 다공성 산화물이 스피넬 또는 알루미나와 실리카의 혼합물이고, 결합제가 중합된 푸르푸릴알코올이며, 및 혼합공정(a)가 (1) 알루미나와 실리카를 푸르푸릴 알코올의 단량체와 혼합하고, 및 (2) 형성된 혼합물을 무기산 수용액과 접촉시켜 알코올을 중합하는 세부공정으로 이루어짐을 특징으로 하는 방법.
  5. 제2항에 있어서, 다공성 산화물이 스피넬 또는 알루미나와 실리카의 혼합물이고, 이때 결합제는 메틸셀룰로스임을 특징으로 하는 방법.
  6. 제2항에 있어서, 다공성 산화물이 단위중량그람당 최소한 60평방미터의 표면적을 갖음을 특징으로 하는 방법.
  7. 실질적으로 연속인 제1 세라믹 지지체상 및 상기 제1 지지체상내에 매립된 고표면적의 제2 불연속 지지체상을 갖는 모노리드식 촉매지지체를 제조하는데 있어서, (a) (i) 알루미나, 실리카, 스피넬, 티타니아, 제올라이트, 지르코니아, 및 이들의 혼합물; 및 (ii) 상기 산화물용 결합제를 실질적으로 균질인 혼합물로 혼합하고, (b) 상기 혼합물을 건조시키고; (c) 건조된 혼합물을 50~250미크론의 평균직경을 갖는 입자로 형성시키고; (d) 형성된 입자 15~50중량부를 특정한 형태의 세라믹 지지체물질 50~85중량부와, 및 3~20중량부의 결합제와 혼합하고; (e) 공정(d)의 혼합물을 벌집형태로 형성시키고; 및 (f) 성형된 혼합물을 세라믹 물질을 소결시키기에 충분한 온도에서 가열함을 특징으로 하는 방법.
  8. 제7항에 있어서, 결합제가 실리콘수지, 중합된 푸르푸릴알코올, 메틸셀룰로스, 폴리비닐알코올 또는 이들의 혼합물임을 특징으로 하는 방법.
  9. 제7항에 있어서, 세라믹물질이 코오디어라이트, 멀라이트, 점토, 활석, 지르코니아, 지르코니아-스피넬, 알루미나, 실리카, 리듐알루미노실리케이트, 알루미나-지르코니아 복합체 또는 이들의 혼합물이며 이때 세라믹 물질은 200메시보다 미세한 입지크기를 갖음을 특징으로 하는 방법.
  10. 제9항에 있어서, 공정(d)의 지지체 물질이 코오디어라이트이고, 공정(a)의 다공성 산화물이 스피넬 또는 알루미나와 알리카의 혼합물이며, 공정(a)의 결합제는 중합된 푸르푸릴 알코올이고, 이때 공정(a)는 (1) 알루미나와 실리카를 푸르푸릴 알코올의 단량체와 혼합하고, 및 (2) 형성된 혼합물을 무기산 수용액과 접촉시켜 알코올을 중합하는 세부-공정으로 이루어짐을 특징으로 하는 방법.
  11. 제9항에 있어서, 공정(a)의 다공성 산화물이 스피넬 또는 알루미나와 실리카의 혼합물이고, 공정(a)의 결합제가 메틸셀룰로스이며, 및 공정(d)의 지지체 물질이 코오디어라이트임을 특징으로 하는 방법.
  12. 제7항에 있어서, 세라믹 물질이 세라믹 지지체상내에 미균열을 유발시킬 수 있는 성분을 함유함을 특징으로 하는 방법.
  13. 실질적으로 연속인 제1 세라믹 지지체상 및 상기 제1 지지체상내에 매립된 고표면적의 제2 불연속 지지체상을 갖는 모노리드식 촉매지지체를 제조하는데 있어서, (a) (i) 알루미나, 실리카, 스피넬, 티타니아, 제올라이트, 지르코니아 및 이들의 혼합물; 및 (ii) 상기 산화물용 결합제를 실질적으로 균질인 혼합물로 혼합하고, (d) 상기 혼합물을 건조시키고; (c) 건조된 혼합물을 50~250미크론의 평균 직경을 갖는 입자로 형성시키고; (d) 형성된 입자 15~50중량부를 특정한 형태의 세라킥 지지체 물질 50~85중량부 및 3~20중량부의 결합제와 혼합하고; (e) 공정 (d)의 혼합물을 벌집형태로 형성시키고; 및 (f) 성형된 혼합물을 세라믹 물질을 소결시키기에 충분한 온도에서 가열하는 방법에 의해 제조됨을 특징으로 하는 촉매지지체.
  14. 제13항에 있어서, 결합제가 실리콘수지, 중합된 푸르푸릴 알코올, 메틸셀룰로스, 폴리비닐 알코올 또는 이들의 혼합물인 방법에 의해 제조됨을 특징으로 하는 촉매지지체.
  15. 제13항에 있어서, 세라믹물질이 코오디어라이트, 멀라이트, 점토, 활석, 지르코니아, 지르코니아-스피넬, 알루미나, 실리카, 리튬알루미노실리케이트, 알루미나-지르코니아 복합체 또는 이들의 혼합물이며, 이때 세라믹 물질은 200메시보다 미세한 입자크기를 갖는 방법에 의해 제조됨을 특징으로 하는 촉매 지지체.
  16. 제15항에 있어서, 공정(d)의 지지체물질이 코오디어라이트이고, 공정(a)의 다공성 산화물이 스피넬 또는 알루미나와 실리카의 혼합물이며, 공정(a)의 결합제는 중합된 푸르푸릴 알코올이고, 이때 공정(a)는 (1) 알루미나와 실리카를 푸르푸릴 알코올의 단량체와 혼합하고, 및 (2) 형성된 혼합물을 무기산 수용액과 접촉시켜 알코올을 중합하는 세부-공정으로 이루어진 방법에 의해 제조됨을 특징으로 하는 촉매지지체.
  17. 제15항에 있어서, 공정(a)의 다공성 산화물이 스피넬 또는 알루미나와 실리카의 혼합물이고, 공정(a)의 결합제가 메틸셀룰로스이며, 및 공정(d)의 지지체물질이 코오디어라이트인 방법에 의해 제조됨을 특징으로 하는 촉매지지체.
  18. 제13항에 있어서, 세라믹 물질이 세라믹 지지체상내에 미균열을 유발시킬 수 있는 성분을 함유하는 방법에 의해 제조됨을 특징으로 하는 촉매지지체.
  19. 실질적으로 연속인 제1 세라믹 지지체상 및 상기 제1 지지체상내에 매립된 고표면적을 갖는 제2 불연속상을 갖는 모노리드식 촉매지지체를 제조하는데 있어서, (a) (i) 알루미나, 실리카, 스피널, 티타니아, 제올라이트, 지르코니아 및 이들의 혼합물로 구성된 군으로부터 선택된 최소한 20m2/g의 표면적을 갖는 다공성 산화물로 이루어진 평균 직경 50~250미크론을 갖는 입자 15~50중량부, (ii) 특정한 형태의 세라믹 지지체물질 50~85중량부 및 (iii) 결합제 3~20중량부를 혼합하고; (b) 혼합물을 벌집형태로 성형시키고; (c) 성형된 혼합물을 세라믹물질을 소결시키기에 충분한 온도에서 가열함을 특징으로 하는 방법.
  20. 실질적으로 연속인 제1 세라믹 지지체상 및 상기 제1 지지체상내에 매립된 고표면적을 갖는 제2 불연속상을 갖는 모노리드식 촉매지지체를 제조하는데 있어서, (a) (i) 알루미나, 실리카, 스피넬, 티타니아, 제올라이트, 지르코니아 및 이들의 혼합물로 구성된 군으로부터 선택된 최소한 20m2/g의 표면적을 갖는 다공성 산화물로 이루어진 평균 직경 50~250미크론을 갖는 입자 15~50중량부, (ii) 특정한 형태의 세라믹 지지체물질 50~85중량부, 및 (iii) 결합제 3~20중량부를 혼합하고; (b) 혼합물을 벌집형태로 성형시키고; (c) 성형된 혼합물을 세라믹 물질을 소결시키기에 충분한 온도에서 가열하는 방법에 의해 제조됨을 특징으로 하는 촉매지지체.
  21. 실질적으로 연속인 제1 세라믹상 및 상기 제1 세라믹상내에 매립된 고표면적을 갖는 제2 불연속지지체상을 갖으며, (1) 상기 고표면적 지지체상이 알루미나, 스피넬, 실리카, 티타니아, 제올라이트, 지르코니아 또는 이들의 혼합물로 구성되고, (2) 상기 고표면적 지지체상이 평균 직경 50~250미크론 및 최소한 20m2/g의 표면적을 갖는 집괴의 형태이며, 및 (3) 촉매지지체가 50~85중량부의 세라믹상 및 15~50 중량부의 고표면적상을 함유함을 특징으로 하는 촉매지지체.
  22. 제21항에 있어서, 소결된 세라믹상이 코오디어라이트, 멀라이트, 점토, 활석, 지르코니아, 지르코니아-스피넬, 알루미나, 실리카, 리튬알루미노실리케이트, 알루미나-지르코니아 복체, 또는 이들의 혼합물로 이루어짐을 특징으로 하는 촉매지지체.
  23. 제21항에 있어서, 세라믹상이 코오디어라이트임을 특징으로 하는 촉매지지체.
  24. 제22항에 있어서, 고표면적상이 알루미나, 실리카, 스피넬 또는 이들의 혼합물로 이루어짐을 특징으로 하는 촉매지지체.
  25. 제23항에 있어서, 고표면적상이 알루미나, 실리카, 스피넬 또는 이들의 혼합물로 이루어짐을 특징으로 하는 촉매지지체.
  26. 제25항에 있어서, 고표면적상이 알루미나임을 특징으로 하는 촉매지지체.
  27. 제25항에 있어서, 고표면적상이 스피넬임을 특징으로 하는 촉매지지체.
  28. 제25항에 있어서, 고표면적상이 알루미나와 실리카의 혼합물임을 특징으로 하는 촉매지지체.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019860001320A 1985-03-18 1986-02-25 촉매 지지체용 고표면적 집괴의 제조방법 및 상기 집괴를 함유하는 모노리드식 지지체 구조물의 제조방법 KR930005311B1 (ko)