KR850002407A - 안티몬 함유금속산화물 촉매 제조방법 - Google Patents
안티몬 함유금속산화물 촉매 제조방법 Download PDFInfo
- Publication number
- KR850002407A KR850002407A KR1019840005910A KR840005910A KR850002407A KR 850002407 A KR850002407 A KR 850002407A KR 1019840005910 A KR1019840005910 A KR 1019840005910A KR 840005910 A KR840005910 A KR 840005910A KR 850002407 A KR850002407 A KR 850002407A
- Authority
- KR
- South Korea
- Prior art keywords
- antimony
- acid
- hydrolysis
- metal oxide
- containing metal
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1A도 내지 제1C도는 실시예1의 촉매 제조과정중에 채취된 샘플의 X-선 회절도(Coka). 제1D도는 비교예 2의 촉매 제조과정중에 채취된 샘플의 X-선 회절도(Coka).
Claims (26)
- (1)안티몬 성분, 다가 금속화합물 및 실리카졸을 필수 성분으로서 함유한 수성 슬러리를 준비하고, (2) 상기 슬러리를 가열 걷조하여고 체물질을 형성하고 (3) 상기 고체물질을 소성하며, 이때 상기 단계(1)의 안티몬 성분으로서 (A)안티몬산, 폴리 안티몬산 및 그염의 적어도 하나와, (B) 3산화 안티몬이 사용되며, (A)와(B)의 혼합 공정은 수성슬러리 상태에서 3상화 안티몬에 의해 제공된 안티몬이 안티몬전양의 0.1내지 70원자%로 이루어지도록 된 것이 특징인 안티몬 함유 금속산화물 촉매 제조방법.
- 제1항에 있어서, (A)안티몬산, 폴리 안티몬산 및 그 염과, (B)3산화 안티몬을 함유하는 슬러리를 단계(2)의 가열 건조전에 약150℃이하의 온도로 0.1내지 50시간 유지하는 것을 특징으로 하는 안티몬함유 금속산화물 촉매 제조방법.
- 제1항에 있어서, 고체물질의 소성은 약500내지 950℃에서 향해지는 것이 특징인 안티몬 함유 금속산화물 촉매 제조방법.
- 제2항에 있어서, 고체물질의 소성은 약500내지 950℃에서 향해지는 것이 특징인 안티몬 함유 금속산화물 촉매 제조방법.
- 제1항에 있어서, 나가 금속 화합물이 철, 코발트, 니켈, 주석, 우라늄, 크롬, 구리, 망간 티타늄, 바나듈, 몰티브덴, 텅스텐, 텔루트, 비스무스, 비소, 토륨 및 세륨으로 된 균으로부터 선택된 적어도 한 종류의 원소의 화합물인 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제2항에 있어서, 다가 금속 화합물이 철, 코발트, 니켈, 주석, 우라늄, 크롬, 구리, 망간, 티타늄, 바나듈, 몰티브덴, 텅스텐, 텔루트, 비스무스, 비소, 토륨 및 세륨으로 된 균으로부터 선택된 적어도 한 종류의 원소의 화합물인 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제3항에 있어서, 다가 금속 화합물이 철, 코발트, 니켈, 주석, 우라늄, 크롬, 구리, 망간 티타늄, 바나듈, 몰티브덴, 텅스텐, 텔루트, 비스무스, 비소, 토륨 및 세륨으로 된 균으로부터 선택된 적어도 한 종류의 원소의 화합물인 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제4항에 있어서, 다가 금속 화합물이 철, 코발트, 니켈, 주석, 우라늄, 크롬, 구리, 망간, 티타늄, 바나, 맨티브덴, 텅스텐, 텔루트, 비스무스, 비소, 토륨 및 세륨으로 된 군으로부터 선택된 적어도 한 종류의 원소의 화합물인 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제1항에 있어서, 안티몬산, 또는 폴리안티몬산이 다음의 어떤 방법에 의해서도 즉,(i)안티몬 산염의 산에 의한 가수분해. (ii)5할로겐화 안티몬의 염기에 의한 가수분해. (iii)3할로겐화 안티몬 질산 산화물의 염기에 의한 가수분해. (iv)3산화 안티몬의 3가철 이온 공전하에서의 질산 산화. (v)3산화 안티몬의 과산화수소 산화에 의해서 제조되는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제2항에 있어서, 안티몬산, 또는 폴리안티몬산이 다음의 어떤 방법에 의해서도 즉,(i)안티몬 산염의 산에 의한 가수분해. (ii)5할로겐화 안티몬의 염기에 의한 가수분해. (iii)3할로겐화 안티몬 질산 산화물의 염기에 의한 가수분해. (iv)3산화 안티몬의 3가철 이온 공존하에서의 질산 산화. (v)3산화 안티몬의 과산화수소 산화에 의해서 제조되는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제3항에 있어서, 안티몬산, 또는 폴리안티몬산이 다음의 어떤 방법에 의해서도 즉,(i)5안티몬 산염의 산에 의한 가수분해. (ii)5할로겐화 안티몬의 염기에 의한 가수분해. (iii)3할로겐화 안티몬 질산 산화물의 염기에 의한 가수분해. (iv)3산화 안티몬의 3가철 이온 공전하에서의 질산 산화.(v)3산화 안티몬의 과산화수소 산화에 의해서 제조되는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제4항에 있어서, 안티몬산, 또는 폴리안티몬산이 다음의 어떤 방법에 의해서도 즉,(i)안티몬 산염의 산에 의한 가수분해. (ii)5할로겐화 안티몬의 염기에 의한 가수분해. (iii)3할로겐화 안티몬 질산 산화물의 염기에 의한 가수분해. (iv)3산화 안티몬의 3가철 이온 공존하에서의 질산 산화. (v)3산화 안티몬의 과산화수소 산화에 의해서 제조되는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제5항에 있어서, 안티몬산, 또는 폴리안티몬산이 다음의 어떤 방법에 의해서도 즉,(i)안티몬 산염의 산에 의한 가수분해. (ii)5할로겐화 안티몬의 염기에 의한 가수분해. (iii)3할로겐화 안티몬 질산 산화물의 염기에 의한 가수분해. (iv)3산화 안티몬의 3가철 이온 공전하에서의 질산 산화. (v)3산화 안티몬의 과산화수소 산화에 의해서 제조되는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제6항에 있어서, 안티몬산, 또는 폴리안티몬산이 다음의 어떤 방법에 의해서도 즉,(i)안티몬 산염의 산에 의한 가수분해. (ii)5할로겐화 안티몬의 염기에 의한 가수분해. (iii)3할로겐화 안티몬 질산 산화물의 염기에 의한 가수분해. (iii)3산화 안티몬의 3가철 이온 공존하에서의 질산 산화. (v)3산화 안티몬의 과산화수소 산화에 의해서 제조되는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제7항에 있어서, 안티몬산, 또는 폴리안티몬산이 다음의 어떤 방법에 의해서도 즉,(i)안티몬 산염에 의한 가수분해. (ii)5할로겐화 안티몬의 염기에 의한 가수분해. (iii)3할로겐화 안티몬 질산 산화물의 염기에 의한 가수분해. (iv)3산화 안티몬의 3가철 이온 공존하에서의 질산 산화. (v)3산화 안티몬의 과산화수소 산화에 의해서 제조되는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제8항에 있어서, 안티몬산, 또는 폴리안티몬산이 다음의 어떤 방법에 의해서도 즉,(i)안티몬 산염의 산에 의한 가수분해. (ii)5할로겐화 안티몬의 염기에 의한 가수분해. (iii)3할로겐화 안티몬 질산 산화물의 염기에 의한 가수분해. (iv)3산화 안티몬의 3가철 이온 공전하에서의 질산 산화. (v)3산화 안티몬의 과산화수소 산화에 의해서 제조되는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.
- 제1항에 있어서, 실리카졸이 5내지 90%중량의 실리카를 함유하는 수성졸인 것이 특징인 안티몬 함유 산화물 촉매의 제법.
- 제1항에 있어서, 상기 안티몬 함유 금속 산화물 촉매가 하기 실험식으로 표시되는 조성을 가지는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.MeaSbbXcQdReOf(SiO2)g다만 상기식에 있어서Me=Fe,Co,Ni,Sn,n,Cr,Cu,MnTi및 Ce으로 된 균으로부터 선택된 적어도 한 종류의 원소.X=V,Mo및 W로 된 군으로부터 선택된 적어도 한 종류의 원소.Q=Li,Na,K,Rb,Cs,Be,Mg,‘Ca,Sr,Ba,Y,La,Zr,Th,Hf,Nb,Ta,Cr,Re,Ru,Os,Ru,Os,Rh,Ir,Pd,Pt,Ag,Zn,Cd,Al,'Ga,In,Tl,Ge,Pb,As및 Se로 된 군으로부터 선택된 적어도 한 종류의 원소.R=B,P,Te및 Bi로 된 군으로보터 선택된 적어도 한 종류의 원소.첨자 a,b,c,d,e,f및 g는 원자비를 나타내고, 각각 다음의 범위에 있다.a=5내지 15, b=5내지 100, c=0내지 15, d=0내지 50, e=0 내지 10, f=상기 각 성분이 결합하여 상성하는 산화물에 대응하는 수, g=10내지 200.
- 제2항에 있어서, 상기 안티몬 함유 금속 산화물 촉매가 하기 실험식으로 표시되는 조성을 가지는 것이 특징인 안티몬 함유 금속 산화물 촉매 제조방법.MeaSbbXcQdReOf(SiO2)g다만 상기식에 있어서,Me=Fe,Co,NT,Sn,U,Cr,Cu,M|n,Ti및 Ce으로 된 균으로부터 선택된 적어도 한 종류의 원소.X=V,Mo및 W로 된 군으로부터 선택된 적어도 한 종류의 원소.Q=Li,Na,K,Rb,Cs,Be,Mg,Ca,S|r,Ba,Y,La,Zr,Th,Hf,Nb,T|a,Cr,Re,Rn,Os,Rb,Os,Rb,Ir,Pd,Pt,Ag,Zn,Cd,Al,Ga,In,Tl,G|e,Pb,As및 Se로 된 군으로부터 선택된 적어도 한 종류의 원소.R=B,P,Te및 Bi로 된 군으로보터 선택된 적어도 한 종류의 원소.첨자 a,b,c,d,e,f 및 g는 원자비를 나타내고, 각각 다음의 범위에 있다.a=5내지 15, b=5내지 100, c=0내지 15, d=0내지 50, e=0 내지 10, f=상기 각 성분이 결합하여 생성하는 산화물에 대응하는 수. g=10내지 200.
- 제1항에 있어서, 단계(2)에서 가열 분문건조하고, 단계(3)에서 소성하여 고체 촉매 입자를 얻는 것을 특징으로 하는 안티몬 함유 금속 산화물 촉매제조방법.
- 제2항에 있어서, 단계(2)에서 가열 분문건조하고, 단계(3)에서 소성하여 고체 촉매 입자를 얻는 것을 특징으로 하는 안티몬 함유 금속 산화물 촉매제조방법.
- 제18항에 있어서, 단계(2)에서 가열 분문건조하고, 단계(3)에서 소성하여 고체 촉매 입자를 얻는 것을 특징으로 하는 안티몬 함유 금속 산화물 촉매제조방법.
- 제2항에 있어서, 상기 생성물의 소성은 유동소성로중에서 촉매가 유동화되도록 행해짐으로써 유동베드 촉매를 제조하는 것을 특징으로 하는 안티몬 함유 금속산화물 촉매 제조방법.
- 제21항에 있어서, 상기 생성물의 소성은 유동소성로중에서 촉매가 유동화되도록 행해짐으로써 유동베드 촉매를 제조하는 것을 특징으로 하는 안티몬 함유 금속산화물 촉매 제조방법.
- 제22항에 있어서, 상기 생성물의 소성은 유동소성로 중에서 촉매가 유동화되도록 행해짐으로써 유동베드 촉매를 제조하는 것을 특징으로 하는 안티몬 함유 금속산화물 촉매 제조방법.
- (1)안티몬 성분, 다가 금속화합물 및 실리카졸을 필수 성분으로서 함유한 수성 슬러리를 준비하고, (2)상기 슬러리를 가열 건조하여 고체물질을 형성하고, (3) 상기 고체물질을 소성하며, 이때 상기 단계(1)의 안티몬 성분으로서(A)안티몬산, 폴리 안티몬산 및 그 염의 적어도 하나와, (B)3산화 안티몬이 사용되며, (A)와 (B)의 혼합 공정은 수성 슬러리상태에서 3산화 안티몬에 의해 제공된 안티몬이 아티몬 전양의 0.1내지 70원자%로 이루어져 얻어지는 것이 특징인 안티몬 함유 금속산화물 촉매.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.