KR20220137477A - 유기발광소자 봉지용 조성물 및 이를 포함하는 유기발광 표시장치 - Google Patents
유기발광소자 봉지용 조성물 및 이를 포함하는 유기발광 표시장치 Download PDFInfo
- Publication number
- KR20220137477A KR20220137477A KR1020210043620A KR20210043620A KR20220137477A KR 20220137477 A KR20220137477 A KR 20220137477A KR 1020210043620 A KR1020210043620 A KR 1020210043620A KR 20210043620 A KR20210043620 A KR 20210043620A KR 20220137477 A KR20220137477 A KR 20220137477A
- Authority
- KR
- South Korea
- Prior art keywords
- meth
- acrylate
- group
- light emitting
- organic light
- Prior art date
Abstract
본 발명은 유기발광소자 봉지용 조성물 및 이를 포함하는 유기발광 표시장치에 관한 것으로서, 외부로부터 유기발광 표시장치로 유입되는 수분 또는 산소를 효과적으로 차단하여 유기발광소자의 성능 및 수명을 확보할 수 있을 뿐만 아니라, 터치패널의 터치감도가 우수할 수 있도록 저유전율 특성을 갖는 유기발광소자 봉지용 조성물 및 이를 포함하는 유기발광 표시장치에 관한 것이다.
Description
본 발명은 터치패널의 터치감도 향상을 위해 저유전율 특성을 갖는 유기발광소자 봉지용 조성물 및 이를 포함하는 유기발광 표시장치에 관한 것이다.
유기발광소자를 구성하는 유기층 재료, 전극 등은 외부의 수분이나 산소에 의해 그 발광 특성 및 수명이 열화되는 문제가 있다. 따라서 유기 재료 및 전극 등을 보호해줄 수 있는 보호층이 필요하다. 이러한 보호층은 외부의 수분이나 산소를 효과적으로 차단하기 위해 통상적으로 1개 이상의 유기층과 무기층이 적층구조로 형성된다.
최근 유기발광소자가 적용된 정전용량 방식의 터치패널이 많이 채용하고 있다. 이러한 정전용량 방식의 터치패널은 도전체가 터치패널에 접촉하게 되면 정전용량의 변화에 의해 터치를 감지하는 방식이며, 높은 유전율 재료의 경우 외부 전기장이 주어졌을 때, 분극이 많이 발생하게 되어 터치감도가 감소된다는 경향이 있다. 따라서, 터치패널의 터치감도가 우수한 저유전율 특성을 갖는 적층구조에 사용되는 유기층의 봉지용 조성물의 개발이 요구되고 있는 상황이다.
본 발명은 외부로부터 유기발광 표시장치로 유입되는 수분 또는 산소를 효과적으로 차단하여 유기발광소자의 성능 및 수명을 확보할 수 있을 뿐만 아니라, 터치패널의 터치감도가 우수할 수 있도록 저유전율 특성을 갖는 유기발광소자 봉지용 조성물 및 이를 포함하는 유기발광 표시장치를 제공하는데 목적이 있다.
본 발명은, 상기한 문제를 해결하기 위하여, 본 발명은 서로 다른 2 이상의 광경화 단량체 및 광중합 개시제를 포함하는 100Khz 내지 1MHz 영역의 주파수에서 유전율 3.0 이하인 유기발광소자 봉지용 조성물로서, 상기 광경화 단량체는 하기 화학식 1로 표시되는 모노(메트)아크릴레이트; 및 하기 화학식 2로 표시되는 디(메트)아크릴레이트로 이루어진 군 중에서 선택된다.
[화학식 1]
[화학식 2]
상기 화학식 1에서,
R1은 치환 또는 비치환된 C2-20의 알킬기, 치환 또는 비치환된 C6-20의 아릴기, 치환 또는 비치환된 C2-20의 알킬옥시기 및 C6-20의 아릴옥시기로 이루어진 군으로부터 선택되고,
R2는 수소, 치환 또는 비치환된 C1-60의 알킬기, 치환 또는 비치환된 C3-30의 사이클로알킬기, 치환 또는 비치환된 C2-60의 알케닐기, 치환 또는 비치환된 C1-60의 알콕시기 및 하이드록시기 중 어느 하나로 선택되며,
상기 화학식 2에서,
R3은 치환 또는 비치환된 C10-20의 알킬렌기이고,
R4와 R5는 각각 독립적으로 수소, 치환 또는 비치환된 C1-60의 알킬기, 치환 또는 비치환된 C3-30의 사이클로알킬기, 치환 또는 비치환된 C2-60의 알케닐기, 치환 또는 비치환된 C1-60의 알콕시기 및 하이드록시기 중 어느 하나로 선택된다.
상기 유기발광소자 봉지용 조성물은 점도 10 내지 30cPs 일 수 있다.
상기 광경화 단량체는 조성물 총 중량을 기준으로 20 내지 99 중량% 포함할 수 있다.
상기 모노(메트)아크릴레이트는 데실(메트)아크릴레이트, 이소데실(메트)아크릴레이트, 4-메틸-2-프로필헥실(메트)아크릴레이트, 이소보르닐(메트)아크릴레이트, 도데실(메트)아크릴레이트, 펜타데실(메트)아크릴레이트, 헥사데실(메트)아크릴레이트, 옥타데실(메트)아크릴레이트, 이소옥타데실(메트)아크릴레이트, 2-헵틸운데실(메트)아크릴레이트, 디사이크로펜타닐(메트)아크릴레이트, 아데멘틸(메트)아크릴레이트, 아데멘틸프로필(메트)아크릴레이트, 에틸아데멘틸(메트)아크릴레이트, 메틸아데멘틸(메트)아크릴레이트, 이소보닐(메트)아크릴레이트, 에틸트리사이클로데실(메트)아크릴레이트, 메틸트리사이클로데실(메트)아크릴레이트, 2-페녹시에틸(메트)아크릴레이트 및 2-페닐페녹시에틸(메트)아크릴레이트로 구성된 군으로부터 1종 이상 선택될 수 있다.
상기 디(메트)아크릴레이트는 1,10-데칸디올디(메트)아크릴레이트, 1,9-데칸디올디(메트)아크릴레이트, 1,11-운데칸디올디(메트)아크릴레이트, 1,12-도데칸디올디(메트)아크릴레이트, 1,13-트리데칸디올디(메트)아크릴레이트, 1,14-테트라데칸디올디(메트)아크릴레이트, 1,15-펜타데칸디올디(메트)아크릴레이트, 1,16-헥사데칸디올디(메트)아크릴레이트, 1,17-헵타데칸디올디(메트)아크릴레이트, 1,18-옥타데칸디올디(메트)아크릴레이트, 1,19-노나데칸디올디(메트)아크릴레이트 및 1,20-아이코산디올디(메트)아크릴레이트로 구성된 군으로부터 1종 이상 선택될 수 있다.
상기 광중합 개시제는 트리아진계, 아세토페논계, 벤조페논계, 티오크산톤계, 벤조인계, 인계, 옥심계 및 이들의 혼합물로 이루어진 군으로부터 1종 이상 선택될 수 있으며, 조성물 총 중량을 기준으로, 0.1 내지 10 중량% 포함할 수 있다.
또한, 상기 유기발광소자 봉지용 조성물은 계면활성제, 경화촉진제 및 산화방지제로 이루어진 군으로부터 1종 이상 선택되는 첨가제를 더 포함할 수 있다.
또 본 발명은 상기 유기발광소자 봉지용 조성물을 함유하는 봉지부를 포함하는 유기발광 표시장치를 제공한다.
상기 봉지부는 상기 조성물을 포함하는 하나 이상의 유기장벽층 외에 하나 이상의 무기장벽층을 더 포함할 수 있다.
본 발명에 따른 유기발광소자 봉지용 조성물을 이용하여 유기발광 표시장치의 봉지부를 형성할 경우, 외부로부터 유입되는 수분 또는 산소를 효과적으로 차단하여 유기발광소자의 성능 및 수명을 확보할 수 있을 뿐만 아니라, 저유전율 특성을 가지므로 터치패널의 터치감도 역시 우수한 효과를 가진다.
도 1은 본 발명의 일 실시예에 따른 유기발광 표시장치의 예시도이다.
이하, 본 발명의 실시예를 첨부된 도면을 참조하여 상세하게 설명한다.
각 도면의 구성요소들에 참조부호를 부가함에 있어서, 동일한 구성요소들이 비록 다른 도면상에 표시되더라도 가능한 한 동일한 참조부호를 부여고 있음에 유의해야 한다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그에 관한 상세한 설명은 생략한다.
어떤 구성 요소가 다른 구성요소에 “연결”, “결합” 또는 “접속” 된다고 기재된 경우, 그 구성 요소는 그 다른 구성요소에 직접적으로 연결되거나 또는 접속될 수 있지만, 각 구성 요소 사이에 또 다른 구성 요소가 “연결”, “결합” 또는 “접속”될 수도 있다. 또한, 층, 막, 영역, 판 등의 구성 요소가 다른 구성 요소 “위에” 또는 “상에” 있다고 하는 경우, 이는 다른 구성 요소 “바로 위에” 있는 경우 뿐만 아니라 그 중간에 또 다른 구성 요소가 있는 경우도 포함할 수 있다. 반대로, 어떤 구성 요소가 다른 부분 “바로 위에” 있다고 하는 경우에는 중간에 또 다른 부분이 없는 것을 의미한다.
본 명세서에서 사용된 용어 “(메트)아크릴”은 아크릴(acryl) 및/또는 메타크릴(methacryl)을 의미한다.
본 명세서에서 사용된 용어 “알킬기”는 다른 설명이 없는 한 단일결합으로 연결된 1 내지 60의 탄소를 가지며, 직쇄 알킬기, 분지쇄 알킬기, 사이클로알킬(지환족)기, 알킬-치환된 사이클로알킬기, 사이클로알킬-치환된 알킬기를 비롯한 포화 지방족 작용기의 라디칼을 의미한다.
본 명세서에서 사용된 용어 “알킬옥시기”는 산소 라디칼이 결합된 알킬기를 의미한다.
본 명세서에서 사용된 용어 “알킬렌기”는 이중결합 없이 포화된 탄화수소로 연결된 알칸디일기(alkanediyl groups)를 의미하며, 연결기가 2개를 가지는 것을 의미한다.
또한 명시적인 설명이 없는 한, 본 명세서에서 사용된 용어 “치환 또는 비치환된”에서 “치환”은 중수소, 할로겐, 아미노기, 니트릴기, 니트로기, C1-C20의 알킬기, C1-C20의 알콕시기, C1-C20의 알킬아민기, C1-C20의 알킬티오펜기, C6-C20의 아릴티오펜기, C2-C20의 알케닐기, C2-C20의 알킨일기, C3-C20의 사이클로알킬기, C6-C20의 아릴기, 중수소로 치환된 C6-C20의 아릴기, C8-C20의 아릴알케닐기, 실란기, 붕소기 및 O, N, S, Si 및 P로 이루어진 군에서 선택된 적어도 하나의 헤테로원자를 포함하는 C2-C20의 헤테로고리기로 이루어진 군으로부터 선택되는 1개 이상의 치환기로 치환될 수 있음을 의미하나, 반드시 이들 치환기로 제한되는 것은 아니다.
본 명세서에서 사용된 용어 “유전율”은 상기 본 발명에 따른 유기발광소자 봉지용 조성물을 포함하는 유기층에 대해 전기 용량법으로 측정된 값을 의미한다.
본 명세서에서 사용된 용어 “점도”는 상기 본 발명에 따른 유기발광소자 봉지용 조성물을 포함하는 유기층에 대해 회전형 방식의 점도계를 사용하여 측정된 값을 의미한다.
본 발명에 따른 유기발광소자 봉지용 조성물은 (a)서로 다른 2 이상의 광경화 단량체 및 (b)광중합 개시제를 포함하며, 100Khz 내지 1MHz 영역의 주파수에서 유전율 3.0 이하인 특징을 가지며, 상기 조성물의 점도는 10 내지 30cPs 일 수 있다.
상기 (a)서로 다른 2이상의 광경화 단량체는 하기 화학식 1로 표시되는 모노(메트)아크릴레이트 및 하기 화학식 2로 표시되는 디(메트)아크릴레이트를 포함하는 군 중에서 적어도 2 이상 선택될 수 있다.
[화학식 1]
[화학식 2]
R1은 치환 또는 비치환된 C2-20의 알킬기, 치환 또는 비치환된 C6-20의 아릴기, 치환 또는 비치환된 C2-20의 알킬옥시기 및 C6-20의 아릴옥시기로 이루어진 군으로부터 선택되고,
R2는 수소, 치환 또는 비치환된 C1-60의 알킬기, 치환 또는 비치환된 C3-30의 사이클로알킬기, 치환 또는 비치환된 C2-60의 알케닐기, 치환 또는 비치환된 C1-60의 알콕시기 및 하이드록시기 중 어느 하나로 선택되며,
상기 화학식 2에서,
R3은 치환 또는 비치환된 C10-20의 알킬렌기이고,
R4와 R5는 각각 독립적으로 수소, 치환 또는 비치환된 C1-60의 알킬기, 치환 또는 비치환된 C3-30의 사이클로알킬기, 치환 또는 비치환된 C2-60의 알케닐기, 치환 또는 비치환된 C1-60의 알콕시기 및 하이드록시기 중 어느 하나로 선택된다.
상기 (a)광경화 단량체는 필요에 따라 치환 또는 비치환된 방향족 탄화수소기를 가지는 단량체를 더 포함할 수 있다.
상기 광경화 단량체는 상기 광경화 단량체의 총 중량을 기준으로 20 내지 99 중량% 포함하는 것이 바람직하다.
보다 구체적으로,
상기 모노(메트)아크릴레이트는 데실(메트)아크릴레이트, 이소데실(메트)아크릴레이트, 4-메틸-2-프로필헥실(메트)아크릴레이트, 이소보르닐(메트)아크릴레이트, 도데실(메트)아크릴레이트, 펜타데실(메트)아크릴레이트, 헥사데실(메트)아크릴레이트, 옥타데실(메트)아크릴레이트, 이소옥타데실(메트)아크릴레이트, 2-헵틸운데실(메트)아크릴레이트, 디사이크로펜타닐(메트)아크릴레이트, 아데멘틸(메트)아크릴레이트, 아데멘틸프로필(메트)아크릴레이트, 에틸아데멘틸(메트)아크릴레이트, 메틸아데멘틸(메트)아크릴레이트, 이소보닐(메트)아크릴레이트, 에틸트리사이클로데실(메트)아크릴레이트, 메틸트리사이클로데실(메트)아크릴레이트, 2-페녹시에틸(메트)아크릴레이트 및 2-페닐페녹시에틸(메트)아크릴레이트로 구성된 군으로부터 1종 이상 선택될 수 있으나, 반드시 이에 한정되는 것은 아니다.
또한, 상기 디(메트)아크릴레이트는 1,10-데칸디올디(메트)아크릴레이트, 1,9-데칸디올디(메트)아크릴레이트, 1,11-운데칸디올디(메트)아크릴레이트, 1,12-도데칸디올디(메트)아크릴레이트, 1,13-트리데칸디올디(메트)아크릴레이트, 1,14-테트라데칸디올디(메트)아크릴레이트, 1,15-펜타데칸디올디(메트)아크릴레이트, 1,16-헥사데칸디올디(메트)아크릴레이트, 1,17-헵타데칸디올디(메트)아크릴레이트, 1,18-옥타데칸디올디(메트)아크릴레이트, 1,19-노나데칸디올디(메트)아크릴레이트 및 1,20-아이코산디올디(메트)아크릴레이트로 구성된 군으로부터 1종 이상 선택될 수 있으나, 반드시 이에 한정되는 것은 아니다.
본 발명에 따른 유기발광소자 봉지용 조성물은 상기 광경화 단량체를 UV 조사 등을 통해 경화시킬 수 있는 (b)광중합 개시제를 포함한다. 상기 광중합 개시제는 광경화성 반응을 수행할 수 있는 통상의 광중합 개시제이면 특별히 제한되지 않는다. 일 예로, 상기 광중합 개시제는 트리아진계, 아세토페논계, 벤조페논계, 티오크산톤계, 벤조인계, 인계, 옥심계 또는 이들의 혼합물을 포함할 수 있다.
상기 트리아진계로는 2,4,6-트리클로로-s-트리아진, 2-페닐-4,6-비스(트리클로로 메틸)-s-트리아진, 2-(3',4'-디메톡시 스티릴)-4,6-비스(트리클로로 메틸)-s-트리아진, 2-(4'-메톡시 나프틸)-4,6-비스(트리클로로 메틸)-s-트리아진, 2-(p-메톡시 페닐)-4,6-비스(트리클로로 메틸)-s-트리아진, 2-(p-톨릴)-4,6-비스(트리클로로 메틸)-s-트리아진, 2-비페닐-4,6-비스(트리클로로 메틸)-s-트리아진, 비스(트리클로로 메틸)-6-스티릴-s-트리아진, 2-(나프토-1-일)-4,6-비스(트리클로로 메틸)-s-트리아진, 2-(4-메톡시 나프토-1-일)-4,6-비스(트리클로로 메틸)-s-트리아진, 2,4-트리클로로 메틸(피페로닐)-6-트리아진, 2,4-(트리클로로 메틸(4'-메톡시 스티릴)-6-트리아진 또는 이들의 혼합물이 될 수 있다.
상기 아세토페논계로는, 2,2'-디에톡시 아세토페논, 2,2'-디부톡시 아세토페논, 2-[0230] 히드록시-2-메틸 프로피오페논, pt-부틸 트리클로로 아세토페논, p-t-부틸 디클로로 아세토페논, 4-클로로[0231] 아세토페논, 2,2'-디클로로-4-페녹시 아세토페논, 2-메틸-1-(4-(메틸티오)페닐)-2-모폴리노 프로판-1-온, 2-벤질-2-디메틸 아미노-1-(4-모폴리노 페닐)-부탄-1-온, 또는 이들의 혼합물이 될 수 있다.
상기 벤조페논계로는 벤조페논, 벤조일 안식향산, 벤조일 안식향산 메틸, 4-페닐 벤조페논, 히드록시 벤조페논, 아크릴화 벤조페논, 4,4'-비스(디메틸 아미노)벤조페논, 4,4'-디클로로 벤조페논, 3,3'-디메틸-2-메톡시 벤조페논 또는 이들의 혼합물이 될 수 있다.
상기 티오크산톤계로는 티오크산톤, 2-메틸 티오크산톤, 이소프로필 티오크산톤, 2,4-디에틸 티오크산톤, 2,4-디이소프로필 티오크산톤, 2-클로로 티오크산톤 또는 이들의 혼합물이 될 수 있다.
상기 벤조인계로는 벤조인, 벤조인 메틸 에테르, 벤조인 에틸 에테르, 벤조인 이소프로필 에테르, 벤조인 이소부틸에테르, 벤질 디메틸 케탈 또는 이들의 혼합물이 될 수 있다.
상기 인계로는 비스벤조일페닐 포스핀옥시드, 벤조일디페닐 포스핀옥시드 또는 이들의 혼합물이 될 수 있다.
상기 옥심계로는 2-(o-벤조일옥심)-1-[4-(페닐티오)페닐]-1,2-옥탄디온 및 1-(o-아세틸옥심)-1-[9-에틸-6-(2-메틸벤조일)-9H-카르바졸-3-일]에탄온, 또는 이들의 혼합물이 될 수 있다.
상기 광중합 개시제는 조성물 총 중량을 기준으로, 0.1 내지 10 중량% 포함하는 것이 바람직한데, 이는 상기 광중합 개시제가 상기 함량 범위로 포함되는 경우 노광 시에 광중합이 충분히 일어날 수 있을 뿐만 아니라, 광중합 이후 남은 미반응 개시제로 인하여 아웃가스 발생 및 신뢰성이 이 저하되는 것을 막을 수 있기 때문이다.
본 발명에 따른 유기발광소자 봉지용 조성물은 추가적으로 계면활성제, 경화촉진제 및 산화방지제로 이루어진 군으로부터 1종 이상 선택되는 첨가제를 더 포함할 수 있다. 특별히 계면활성제는 조성물의 분산을 유도하는데 유리하다.
본 발명에 따른 유기발광소자 봉지용 조성물은 100Khz 내지 1MHz 영역의 주파수에서 유전율 3.0 이하인 저 유전율 특성을 가지므로, 상기 봉지용 조성물이 터치패널에 적용될 경우 터치감도가 매우 우수한 효과를 가지게 된다.
또한, 본 발명에 따른 유기발광소자 봉지용 조성물은 점도 10 내지 30cPs인 것 바람직한데, 이는 상기 점도 범위에서 조성물의 공정성이 보다 향상될 수 있기 때문이다.
또 다른 본 발명인 유기발광 표시장치는 상기 유기발광소자 봉지용 조성물을 함유하는 봉지부를 포함한다.
도 1은 본 발명의 일 실시예에 따른 유기발광 표시장치의 예시도이다. 도 1에 개시된 유기발광 표시장치는 기판(110), 기판(110)상에 배치된 유기발광소자(200) 및 유기발광소자(200) 상에 배치된 봉지부(300)를 포함한다. 이때 상기 봉지부(300)는 제 1봉지층(310) 및 제 2 봉지층(320)으로 구성되는 다중층으로 개시하고 있으나, 본 발명은 봉지부(300)가 2층 또는 4층 이상인 구성을 모두 포함할 수 있다. 봉지부(300)가 2층의 다중층으로 구성될 경우 무기장벽층과 유기장벽층을 포함할 수 있다. 예를 들면, 제 1봉지층(310)이 무기장벽층일 경우, 제 2봉지층(320)은 유기장벽층일 수 있으나, 적층 순서가 이에 국한되는 것은 아니다.
상기 봉지부(300)는 유기발광 표시장치의 봉지 또는 캡슐화 용도로써 유기장벽층을 형성할 수 있으며, 상기 유기장벽층은 본 발명에 따른 유기발광소자 봉지용 조성물을 광경화시켜 형성할 수 있다.
상기 봉지용 조성물(유기장벽층 물질)은 잉크젯, 진공 증착, 스핀코팅 또는 슬릿코팅 방법에 의하여 도포될 수 있으며, 광경화 시 개시제를 사용할 수 있다.
이하, 본 발명에 따른 유기발광소자 봉지용 조성물에 관한 실시예를 들어 본 발명을 구체적으로 설명하지만, 본 발명이 하기의 실시예로 한정되는 것은 아니다.
[실시예]
서로 다른 2 이상의 광경화 단량체 및 광개시제(BAPO) 및 계면활성제를 하기 표 1의 중량비로 혼합하여 실시예 1 내지 46 및 비교예 1 내지 2의 유기발광소자 봉지용 조성물을 제조하였다.
이후 상기 제조한 조성물을 12시간 교반하여, Pore size: 0.45㎛ PTFE 필터로 여과하였다.
상기 여과한 유기발광소자 봉지용 조성물을 스핀코팅 방식으로 5.0㎛ 이상의 두께를 형성한 후 UV 노광기를 이용하여 1J의 광량을 조사하여 봉지막을 형성하였다. 유전율 및 점도는 아래와 방법으로 측정하였다.
유전율 : 유기발광소자 봉지용 조성물을 하부전극 위에 5.0㎛ 이상의 두께로 코팅 및 경화한다. 이 후, 상부전극을 1,000Å두께로 증착한다. 제작된 시편에 대해 KEYSIGHT社, E4980A 로 측정한 후, 유전상수를 계산하였다.
점도 : 액상의 유기발광소자 봉지용 조성물을 회전형 방식의 점도계를 사용하여 점도를 측정하였다.
그 결과, 본 발명에 따른 실시예 1 내지 46의 유기발광소자 봉지용 조성물로 형성한 봉지막의 유전율은 모두 3.0 F/m 이하의 값을 얻었으나, 비교예 1 내지 2로 형성한 봉지막의 유전율은 3.0 F/m 을 초과하였다. 따라서, 본 발명에 따라 제조한 봉지막이 적용된 터치패널의 경우, 보다 우수한 터치감도의 효과를 얻을 수 있다.
[표 1]
* DDMA : 1,12-Dodecanediol Dimethacrylate (72829-09-5)
* ISBA : Isobornyl Acrylate (5888-33-5)
* OPPEA : 2-Phenylphenoxyethyl acrylate (91442-24-9)
* HFB-MA : 2,2,3,4,4,4-Hexafluorobuyl methacrylate (36405-47-7)
* L-DAIC : 1,3-diallyl-5-dodecyl-1,3,5-triazinane-2,4,6-trione (66747-68-0)
* FA-513AS : Octahydro-4,7-methano-1H-indenyl acrylate (79637-74-4)
* FA-513M : Dicyclopentanyl methacrylate (34759-34-7)
* TDMA : 1,14-Tetradecanediol dimethacrylate (168473-14-1)
* ISTA : Isooctadecyl acrylate (93841-48-6)
* PHEA : 2-Phenoxyethyl Acrylate (48145-04-6)
* U-847 : 2-Propenoic acid, 2-methyl-,1,1'[(3-heptyl-4-pentyl-1,2-cyclohexanediyl)bis(9,1-nonanediyliminocarbonyloxy-2,1- ethanediyl)]ester (86499-57-3)
이상의 설명은 본 발명을 예시적으로 설명한 것에 불과한 것으로, 본 발명에 속하는 기술분야에서 통상의 지식을 가지는 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 변형이 가능할 것이다. 따라서, 본 명세서에 개시된 실시예들은 본 발명을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 사상과 범위가 한정되는 것은 아니다. 본 발명의 보호범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 모든 기술은 본 발명의 권리범위에 포함하는 것으로 해석되어야 할 것이다.
100 : 기판
200 : 유기발광소자
300 : 봉지부
310 : 제1봉지부
320 : 제2봉지부
200 : 유기발광소자
300 : 봉지부
310 : 제1봉지부
320 : 제2봉지부
Claims (9)
- 서로 다른 2 이상의 광경화 단량체 및 광중합 개시제를 포함하는 100Khz 내지 1MHz 영역의 주파수에서 유전율 3.0 이하인 유기발광소자 봉지용 조성물로서,
상기 광경화 단량체는 하기 화학식 1로 표시되는 모노(메트)아크릴레이트; 및 하기 화학식 2로 표시되는 디(메트)아크릴레이트로 이루어진 군 중에서 선택되는, 유기발광소자 봉지용 조성물:
[화학식 1]
[화학식 2]
상기 화학식 1에서,
R1은 치환 또는 비치환된 C2-20의 알킬기, 치환 또는 비치환된 C6-20의 아릴기, 치환 또는 비치환된 C2-20의 알킬옥시기 및 C6-20의 아릴옥시기로 이루어진 군으로부터 선택되고,
R2는 수소, 치환 또는 비치환된 C1-60의 알킬기, 치환 또는 비치환된 C3-30의 사이클로알킬기, 치환 또는 비치환된 C2-60의 알케닐기, 치환 또는 비치환된 C1-60의 알콕시기 및 하이드록시기 중 어느 하나로 선택되며,
상기 화학식 2에서,
R3은 치환 또는 비치환된 C10-20의 알킬렌기이고,
R4와 R5는 각각 독립적으로 수소, 치환 또는 비치환된 C1-60의 알킬기, 치환 또는 비치환된 C3-30의 사이클로알킬기, 치환 또는 비치환된 C2-60의 알케닐기, 치환 또는 비치환된 C1-60의 알콕시기 및 하이드록시기 중 어느 하나로 선택된다.
- 제1항에 있어서,
상기 유기발광소자 봉지용 조성물은 점도 10 내지 30cPs 인, 유기발광소자 봉지용 조성물.
- 제1항에 있어서,
상기 광경화 단량체는 조성물의 총 중량을 기준으로 20 내지 99 중량% 포함하는, 유기발광소자 봉지용 조성물.
- 제1항에 있어서,
상기 모노(메트)아크릴레이트는 데실(메트)아크릴레이트, 이소데실(메트)아크릴레이트, 4-메틸-2-프로필헥실(메트)아크릴레이트, 이소보르닐(메트)아크릴레이트, 도데실(메트)아크릴레이트, 펜타데실(메트)아크릴레이트, 헥사데실(메트)아크릴레이트, 옥타데실(메트)아크릴레이트, 이소옥타데실(메트)아크릴레이트, 2-헵틸운데실(메트)아크릴레이트, 디사이크로펜타닐(메트)아크릴레이트, 아데멘틸(메트)아크릴레이트, 아데멘틸프로필(메트)아크릴레이트, 에틸아데멘틸(메트)아크릴레이트, 메틸아데멘틸(메트)아크릴레이트, 이소보닐(메트)아크릴레이트, 에틸트리사이클로데실(메트)아크릴레이트, 메틸트리사이클로데실(메트)아크릴레이트, 2-페녹시에틸(메트)아크릴레이트 및 2-페닐페녹시에틸(메트)아크릴레이트로 구성된 군으로부터 1종 이상 선택되는, 유기발광소자 봉지용 조성물.
- 제1항에 있어서,
상기 디(메트)아크릴레이트는
1,10-데칸디올디(메트)아크릴레이트, 1,9-데칸디올디(메트)아크릴레이트, 1,11-운데칸디올디(메트)아크릴레이트, 1,12-도데칸디올디(메트)아크릴레이트, 1,13-트리데칸디올디(메트)아크릴레이트, 1,14-테트라데칸디올디(메트)아크릴레이트, 1,15-펜타데칸디올디(메트)아크릴레이트, 1,16-헥사데칸디올디(메트)아크릴레이트, 1,17-헵타데칸디올디(메트)아크릴레이트, 1,18-옥타데칸디올디(메트)아크릴레이트, 1,19-노나데칸디올디(메트)아크릴레이트 및 1,20-아이코산디올디(메트)아크릴레이트로 구성된 군으로부터 1종 이상 선택되는, 유기발광소자 봉지용 조성물.
- 제1항에 있어서,
상기 광중합 개시제는 트리아진계, 아세토페논계, 벤조페논계, 티오크산톤계, 벤조인계, 인계, 옥심계 및 이들의 혼합물로 이루어진 군으로부터 1종 이상 선택되는, 유기발광소자 봉지용 조성물.
- 제1항에 있어서,
상기 광중합 개시제는 조성물 총 중량을 기준으로, 0.1 내지 10 중량% 포함하는, 유기발광소자 봉지용 조성물.
- 제1항에 있어서,
상기 유기발광소자 봉지용 조성물은 계면활성제, 경화촉진제 및 산화방지제로 이루어진 군으로부터 1종 이상 선택되는 첨가제를 더 포함하는, 유기발광소자 봉지용 조성물.
- 제 1항 내지 제 8항 중 어느 한 항에 따른 조성물을 함유하는 봉지부를 포함하는 유기발광 표시장치.