KR20130062865A - 발광물질을 포함하는 광학필름 및 이를 포함하는 광학 디스플레이 장치 - Google Patents
발광물질을 포함하는 광학필름 및 이를 포함하는 광학 디스플레이 장치 Download PDFInfo
- Publication number
- KR20130062865A KR20130062865A KR1020120102164A KR20120102164A KR20130062865A KR 20130062865 A KR20130062865 A KR 20130062865A KR 1020120102164 A KR1020120102164 A KR 1020120102164A KR 20120102164 A KR20120102164 A KR 20120102164A KR 20130062865 A KR20130062865 A KR 20130062865A
- Authority
- KR
- South Korea
- Prior art keywords
- optical film
- optical
- meth
- acrylate
- film
- Prior art date
Abstract
본 발명은 광학필름 및 이를 포함하는 광학 디스플레이 장치에 관한 것이다. 보다 구체적으로 본 발명은 기재필름; 및 상기 기재필름 위에 형성된 광기능성층을 포함하고, 상기 기재필름과 상기 광기능성층 중 하나 이상은 발광물질을 포함하고, 상기 발광물질은 형광 물질과 인광 물질 중 하나 이상을 포함하는 광학필름 및 이를 포함하는광학 디스플레이 장치에 관한 것이다.
Description
본 발명은 광학필름 및 이를 포함하는 광학 디스플레이 장치에 관한 것이다. 보다 구체적으로 본 발명은 발광물질을 포함하는 광학필름 및 이를 포함하는 광학 디스플레이 장치에 관한 것이다.
액정 표시 장치(LCD)에 있어서, 광학필름을 사용하는 영상표시 수단의 성능은 백라이트 유닛(Back-Light Unit)의 성능에 크게 영향을 받는다. 이는 광학필름을 통해 빛을 반사하거나 투과시켜 빛의 양을 조절하는 방식이 기본이 되기 때문이다.
영상표시 수단에 효과적으로 적용하기 위해 광학적 성능이 우수한 다양한 광학필름이 제시되어 왔다. 이러한 광학필름 중 프리즘 시트는 액정표시장치(LCD)의 휘도를 향상시키기 위한 필름이다. 액정표시장치(LCD)는 스스로 빛을 낼 수 없기 때문에 광원(CCFL 또는 LED)을 사용하여 광을 얻고, 이 광을 도광판을 통해 전체 면적으로 분포시키고, 확산시트를 이용하여 보다 균일한 밝기의 면광원으로 변형시킨다. 이러한 과정에서 초기 광원으로부터 출사된 광의 효율은 점점 떨어지게 된다. 프리즘 시트는 측광(side light)을 정면광으로 바꾸고 반사광을 집광시켜 휘도를 높일 수 있다.
이와 같이 집광 시트로서 프리즘 시트는 박막 유연성을 갖는 광학필름으로서, 한쪽 면에 프리즘 형상이 선형 배열로 구조화된 광학 패턴을 형성하여 휘도를 증가시키는 역할을 한다.
굴절률이 높을수록 프리즘 필름의 성능이 향상되어 높은 휘도를 구현할 수 있다. 종래 대표적으로 사용되는 고굴절률 수지로는 브롬이 치환된 에폭시수지가 많이 이용되고 있다. 예를 들면 테트라브로모 비스페놀 A형의 에폭시 수지와 비스페놀 A형 에폭시 수지에 아크릴산을 부가하고 여기에 스틸렌, 디비닐벤젠, 벤질메타아크릴레이트 등을 혼합하여 제조된 에폭시 수지를 이용한다.
그러나, 상기 에폭시 수지는 굴절률이 1.590으로 여전히 낮은 수치를 나타내고 있다. 또한, 아베수 역시 32 정도로 낮아서 광학용으로는 개선의 여지가 많았다. 또한, 상기 할로겐계 수지는 연소시 폴리할로겐화 아로마 다이옥신(Polyhalogenated aromatic dioxin) 또는 폴리할로겐화 디벤조퓨란(polyhalogenated dibenzofuran)등의 유독성 발암물질이 발생할 우려가 있고, 브롬화수소나 염화수소 등과 같이 연소시 발생되는 가스가 인체 및 환경에 악영향을 미친다는 문제점이 있었다.
또한, 황원자를 함유하는 방향족 폴리이소시아네이트, 폴리올, 폴리티올인 활성수소 화합물과의 혼합물에 내부 이형제를 첨가하여 주형 중합된 우레탄 결합 또는 티오카르 바인산 S-알킬에스테르 결합을 가진 광학용 소재가 개발되고 있다. 그러나, 열안정성이 낮아서 하드 코팅시 광학제품이 부분 변형되는 문제점이 있다.
또한, 상기 열거된 대다수의 고굴절률 수지는 고점도, 고가격, 순도 문제 등으로 인해 양산 및 생산적용이 어려운 문제점이 있다.
이와 관련하여, 미국공개특허 2009-0220742호는 휘도가 향상된 반사필름으로서, 폴리아크릴레이트 수지를 포함할 수 있고, 적어도 하나의 아크릴 또는 아크릴레이트 단량체를 포함하는 자외선 경화 수지를 포함하는 반사필름을 개시하고 있다.
본 발명의 목적은 고굴절율 및 고휘도를 가지고, 내스크래치성이 우수한 광학필름을 제공하는 것이다.
본 발명의 다른 목적은 휘도와 시야각이 모두 높은 광학필름을 제공하는 것이다.
본 발명의 또 다른 목적은 광원의 효율을 증가시킬 수 있는 광학필름을 제공하는 것이다.
본 발명의 또 다른 목적은 저굴절률의 자외선 경화형 불포화 화합물로 제조되더라도 고휘도를 갖는 광학필름을 제공하는 것이다.
본 발명의 또 다른 목적은 무기 형광물질을 포함하는 광학필름의 분산성과 색좌표 균일성 문제점을 해결할 수 있는 광학필름을 제공하는 것이다.
본 발명의 또 다른 목적은 취급성이 좋고 저가로 제조 가능한 광학필름을 제공하는 것이다.
본 발명의 또 다른 목적은 열안정성이 우수하고, 인각롤과의 이형성 등 신뢰성이 우수하며, 백라이트 조립 시 내마모성이나 이물에 의한 불량률을 최소화할 수 있는 광학필름을 제공하는 것이다.
본 발명의 또 다른 목적은 상기 광학필름을 포함하는 광학 디스플레이 장치를 제공하는 것이다.
본 발명의 일 관점인 광학필름은 기재필름; 및 기재필름 위에 형성된 광기능성층을 포함하고, 기재필름과 광기능성층 중 하나 이상은 발광물질을 포함하고, 상기 발광물질은 형광 물질과 인광 물질 중 하나 이상을 포함할 수 있다.
상기 발광 물질은 흡수 파장이 240~380nm 또는 420~480nm이고, 발광 파장이 520~580nm가 될 수 있다.
상기 발광 물질은 자외선 경화형 작용기를 포함할 수 있다.
상기 광학필름은 플루오렌 기를 포함할 수 있다.
본 발명의 다른 관점인 광학 디스플레이 장치는 상기 광학필름을 포함할 수 있다.
본 발명은 고굴절율 및 향상된 높은 휘도를 갖고, 내스크래치성이 우수하며, 기재필름과의 접착력이 우수하고, 광학필름 제조 공정에 적합한 점도 특성을 갖고, 친환경적인 비할로겐계 광학필름용 수지 조성물을 제공하고, 열안정성이 우수하고, 인각롤과의 이형성 등 신뢰성이 우수하며, 백라이트 조립 시 내마모성이나 이물에 의한 불량률을 최소화할 수 있는 광학필름 및 그 제조방법을 제공하였다.
도 1은 본 발명 일 구체예의 광학필름의 사시도이다.
100:광학필름, 110:기재필름, 120:광 기능성층
100:광학필름, 110:기재필름, 120:광 기능성층
본 명세서에서 '광학필름'은 기재필름 및 상기 기재필름 위에 적층되어 있는 광기능성층을 포함할 수 있다.
도 1은 본 발명의 광학필름의 일 구쳬예를 나타낸 것이다. 도 1에 따르면, 광학필름(100)은 기재필름(110) 및 상기 기재필름(110) 위에 적층되어 있는 광 기능성층(120)을 포함할 수 있다.
본 발명의 일 관점인 광학필름은 형광 물질, 인광 물질 중 하나 이상의 발광 물질을 포함할 수 있다. 발광 물질은 광학필름의 기재필름, 광기능성층 중 하나 이상에 포함될 수 있다. 발광 물질은 광원의 특정 영역의 빛을 흡수함으로써 광학필름의 휘도를 향상시킬 수 있고, 굴절률이 높아 기존의 고굴절률 수지를 사용할 필요가 없게 할 수 있다.
발광 물질은 백라이트 유닛에 광원으로 사용되는 CCFL 또는 LED 램프의 발광 파장대에 의해 여기되어 발광 특성을 갖는 물질을 포함할 수 있다.
발광 물질은 청색 영역 또는 자외선 파장 영역의 에너지를 흡수하고 녹색 영역의 에너지를 발광할 수 있다. 구체적으로 발광 물질은 흡수 파장이 240~380nm 또는 420~480nm이고, 발광 파장 520~580nm가 될 수 있다. 흡수 파장과 발광 파장은 低농도(통상 샘플기준으로 0.02g/100ml 샘플)로 THF, CH2Cl2, 또는 이들의 혼합 용매에서 측정된 것이다.
광학필름에 포함되는 발광 물질의 종류는 광학필름이 포함되는 백라이트유닛의 광원 종류에 따라 달라질 수 있다. 왜냐하면, 백라이트유닛의 광원으로부터 나온 광이 광학필름을 통해 반사되거나 투과되어 빛의 양이 조절되기 때문이다. 백라이트유닛의 광원으로는 LED 램프 또는 CCFL이 사용될 수 있다.
백라이트유닛에서 광원이 LED 램프일 때, 발광 물질은 청색 영역의 에너지를 흡수하고 녹색 영역의 에너지를 발광하는 물질로서, 흡수 파장이 420~480nm, 발광 파장이 520~580nm인 발광 물질이 사용될 수 있다. 백라이트유닛에서 광원이 CCFL일 때, 발광 물질은 자외선 파장 영역의 에너지를 흡수하고 녹색 영역의 에너지를 발광하는 발광 물질로서, 흡수 파장이 240~380nm, 발광 파장이 520~580nm인 발광 물질이 사용될 수 있다.
발광 물질은 유기 형광 또는 인광 물질, 또는 유기-무기 하이브리드 형광 또는 인광 물질이 될 수 있다. 상기 유기-무기 하이브리드 형광 또는 인광 물질은 하나의 물질에 유기 성분과 무기 성분이 동시에 포함되는 발광 물질을 의미한다.
무기 형광 또는 인광 물질은 광원 예를 들면 LED 램프의 광에서 R,G,B 중 특정 영역만을 흡수할 수 있다. 따라서, 광원 효율을 높이기 위해서는 R,G,B 각각에 대한 파장 흡수를 보완하기 위해 복수 개의 무기 형광 물질을 사용해야 한다. 그러나, 무기 형광 물질을 수지에 복수 개 포함시킬 경우 분산성, 색좌표 균일성에 문제가 있다. 반면에, 유기 발광 물질은 단독으로 R,G,B에 대한 파장 흡수 보완 효과를 나타낼 수 있다.
상기 형광 물질은 쿠마린 유도체, 피란 유도체, 퀴나크리돈 유도체, 아미노안트라센 유도체, 나프타센 유도체, 페닐렌 비닐렌, 플루오렌 유도체, 나프탈렌 비닐렌, 페리-나프탈렌 중 하나 이상을 포함할 수 있다. 구체적으로, 2,3,6,7-Tetrahydro-1,1,7,7,-tetramethyl-1H,5H,11H-10-(2-benzothiazolyl)quinolizino[9,9a,1gh]coumarin(제품명 C545T)(화학식 1), 4-(Dicyanomethylene)-2-tert-butyl-6-(1,1,7,7-tetramethyl julolidin-4-yl-vinyl)-4H-pyran(E), N,N'-Dimethyl-quinacridone(제품명 DMQA)(화학식 2), 9,10-bis[N,N-di-(p-tolyl)-amino]anthracene(제품명 TTPA)(화학식 3), 9,10-bis[phenyl(m-tolyl)-amino]anthracene(제품명 TPA)(화학식 4), (5,6,11,12)-테트라페닐나프타센((5,6,11,12)-Tetraphenylnaphthacene, 제품명 Rubrene)(화학식 5), PPV(poly(p-phenylene vinylene))(화학식 6), Polyfluorene, PNV(poly(naphthalene vinylene), PPN(poly peri-naphthalene) 또는 이들의 혼합물이 될 수 있다.
상기 인광 물질은 피리딘 이리듐 유도체를 포함할 수 있다. 구체적으로, Tris[2-(p-tolyl)pyridine]iridium(III); Ir(mppy)3) (화학식 7), Ir(piq)3 (화학식 8), Bis[3,5-difluoro-2-(2-pyridyl)phenyl-(2-carboxypyridyl)iridium(III)(제품명 Firfic)(화학식 9), Tris(2-phenylpyridine)iridium(III)(제품명 Ir(ppy)3)(화학식 10) 또는 이들의 혼합물이 될 수 있다.
<화학식 1>
<화학식 2>
<화학식 3>
<화학식 4>
<화학식 5>
<화학식 6>
(n은 100-500의 정수이다)
<화학식 7>
<화학식 8>
<화학식 9>
<화학식 10>
발광물질은 자외선 경화형 불포화 작용기를 포함할 수 있다. 자외선 경화형 불포화 작용기는 비닐기 등이 될 수 있지만 이에 제한되지 않는다. 자외선 경화형 불포화 작용기 포함시 하기 자외선 경화형 불포화 화합물과 경화 반응을 수행함으로써, 휘도 향상 효과와 함께 광학필름의 강도와 내구성을 개선할 수 있다.
발광 물질은 광학필름 중 0.001-0.5중량%, 바람직하게는 0.001-0.1중량%로 포함될 수 있다. 상기 범위 내에서, 휘도 상승효과가 있을 수 있다.
발광 물질은 기재필름 중 0.001-0.5중량%, 바람직하게는 0.001-0.1중량%로 포함될 수 있다. 상기 범위 내에서, 휘도 상승효과가 있을 수 있다.
발광 물질은 광기능성층 중 0.001-0.5중량%, 바람직하게는 0.001-0.1중량%로 포함될 수 있다. 상기 범위 내에서, 휘도 상승효과가 있을 수 있다.
광기능성층은 발광 물질을 포함하는 수지 조성물의 경화물이 될 수 있다. 수지 조성물은 하기에서 상술될 자외선 경화형 불포화 화합물, 개시제 등을 포함할 수 있다. 특히, 자외선 경화형 불포화 화합물서 플루오렌 유도체 불포화 수지와 페녹시벤질 (메타)아크릴레이트, 페닐페녹시에틸 (메타)아크릴레이트, 에톡시레이티드 티오디페닐 디(메타)아크릴레이트, 페닐티오에틸 (메타)아크릴레이트 단량체 또는 이들의 올리고머를 포함함으로써, 기재필름과의 접착력을 높이고, 광기능성층의 표면 경도를 향상시킬 수 있다.
광기능성층은 광을 집광, 확산, 투과, 굴절 또는 반사시키는 기능을 갖는 층으로, 이로부터 광학필름은 프리즘 시트, 확산 시트, 도광판 등의 용도를 가질 수 있다.
광기능성층은 광의 집광, 확산, 굴절 등의 기능을 갖기 위해 광학패턴을 포함할 수 있다. 광학패턴은 프리즘, 렌티큘러 렌즈, 마이크로렌즈, 엠보 형상 중 하나 이상을 포함할 수 있지만, 이에 제한되지 않는다.
광기능성층에 있어서 광원으로부터 멀어질수록 발광 물질의 농도는 증가할 수 있다.
광기능성층의 두께(또는 높이)는 1㎛~1,000㎛, 바람직하게는 1㎛~300㎛가 될 수 있다.
기재필름은 투명 재질의 수지 필름으로서, 유리, 투명 합성수지 등이 사용될 수 있다. 일반적으로는 폴리에틸렌테레프탈레이트 재질 등을 포함하는 투명 합성수지를 사용할 수 있다.
기재필름의 두께는 30㎛-300㎛가 될 수 있다.
광학필름은 광학필름용 수지 조성물을 사용하여 제조될 수 있다. 예를 들면, 일 구체예에서
(a) 광학필름용 수지 조성물을 몰드 인각롤에 도포하여 코팅층을 형성하는 단계; (b) 상기 코팅층에 기재필름의 일면을 접촉시키는 단계; (c) 상기 기재필름에 자외선을 조사하여 상기 코팅층을 경화시키는 단계; 및 (d) 상기 기재필름에 접착되고 경화된 코팅층을 상기 몰드 인각롤로부터 분리시키는 단계를 포함하는 것일 수 있다.
상기 코팅층의 두께는 0.1㎛~1,000㎛, 바람직하게는 1㎛~300㎛, 0.1㎛-50㎛, 20㎛~50㎛, 더 바람직하게는 35㎛-40㎛가 될 수 있다.
다른 구체예에서, (a) 광학필름용 수지 조성물을 이형필름에 도포하여 도포층을 제조하는 단계, (b) 광기능성층용 수지 조성물을 몰드 인각롤에 도포하여 코팅층을 형성하는 단계; (c) 상기 코팅층을 상기 도포층의 일면에 접촉시키는 단계; (c) 상기 도포층 또는 코팅층에 자외선을 조사하여 경화시키는 단계; 및 (d) 상기 경화된 코팅층을 상기 몰드 인각롤로부터 분리시키는 단계를 포함할 수 있다.
상기 기재필름은 그 용도를 고려할 때 투명 기재필름이 될 수 있다.
상기 광기능성층용 수지 조성물은 자외선 경화형 불포화 화합물과 개시제를 포함하는 것으로서, 통상적으로 알려진 광을 집광, 확산, 투과, 굴절 또는 반사시키는 필름 제조에 사용되는 것이라면 제한되지 않는다.
광학필름용 수지 조성물 또는 광기능성층용 수지 조성물의 경화는 190nm~400nm 파장의 자외선, 150-500mJ/cm2의 에너지를 조사하여 수행될 수 있지만, 이들에 제한되는 것은 아니다.
상기 광학필름용 수지 조성물은 발광 물질, 자외선 경화형 불포화 화합물 및 개시제를 포함할 수 있다.
발광 물질은 하기 자외선 경화형 불포화 화합물 100중량부에 대해 0.001-0.5 중량부, 바람직하게는 0.001-0.1중량부, 0.01-0.1중량부, 0.005-0.07중량부로 포함할 수 있다. 상기 범위 내에서, 색좌표의 변화없이(x : ±30/1000, y : ±30/1000) 충분한 발광 효과에 의한 휘도 향상 효과를 얻을 수 있다.
발광 물질은 고형분 기준으로 조성물 100중량부 중 0.001-0.5중량부, 바람직하게는 0.001-0.1중량부, 더 바람직하게는 0.005-0.1중량부로 포함될 수 있다. 상기 범위 내에서, 휘도 상승 효과가 있다.
자외선 경화형 불포화 화합물은 독립적인 단독 성분일 수도 있고, 상기 발광물질과 화학적으로 결합한 복합 성분이 될 수도 있다.
자외선 경화형 불포화 화합물은 굴절률이 1.61 이하, 바람직하게는 1.52-1.605가 될 수 있다.
자외선 경화형 불포화 화합물은 아베수가 1.45-1.60이 될 수 있다.
자외선 경화형 불포화 화합물은 단관능 또는 다관능 자외선 경화형 모노머 또는 그의 올리고머를 포함할 수 있다. 이로써 소프트 몰드 또는 니켈이 도금된 금속 몰드의 인각롤과의 이형성이 향상되고, 경화 후 상온 또는 고온/고습에서 투명기재필름과의 접착력이 향상되고, 프리즘 형상의 표면 경도를 향상시킬 수 있다.
자외선 경화형 불포화 화합물은 단관능 또는 다관능의 (메타)아크릴레이트계 올리고머, 단관능 또는 다관능의 (메타)아크릴레이트계 모노머, 또는 이들의 혼합물이 될 수 있다.
(메타)아크릴레이트계 올리고머는 통상의 (메타)아크릴레이트 올리고머를 제한없이 사용할 수 있다. 예를 들면, 중량평균분자량이 1,000-100,000g/mol인 올리고머를 사용할 수 있다.
(메타)아크릴레이트계 올리고머는 플루오렌계 (메타)아크릴레이트, 우레탄계 (메타)아크릴레이트, 에폭시계 (메타)아크릴레이트, 폴리에스테르계 (메타)아크릴레이트, 불소계 (메타)아크릴레이트, 실리콘계 (메타)아크릴레이트, 인산계 (메타)아크릴레이트, 말레이미드 개질 (메타)아크릴레이트, 아크릴레이트(메타크릴레이트) 등을 각각 단독 또는 2 종 이상 혼합하여 사용할 수 있다.
플루오렌계 (메타)아크릴레이트는 플루오렌계 구조를 포함하고 불포화기로 (메타)아크릴레이트기를 갖는 올리고머(플루오렌 유도체 불포화 수지)를 포함할 수 있다.
우레탄계 (메타)아크릴레이트는 폴리올, 이소시아네이트계 화합물 및 (메타)아크릴레이트로 합성된, 분자 구조 중에 우레탄 결합을 갖는 올리고머를 포함할 수 있다. 상기 폴리올은 폴리에스테르 폴리올, 폴리에테르 폴리올, 폴리카보네이트 폴리올, 폴리카프로락톤 폴리올, 링 개환 테트라하이드로퓨란 프로필렌옥사이드 공중합체, 폴리부타디엔디올, 폴리디메틸실록산디올, 에틸렌 글리콜, 프로필렌 글리콜, 1,4-부탄디올, 1,5-펜탄디올, 1,6-헥산디올, 네오펜틸 글리콜, 1,4-시클로헥산 디메탄올, 비스페놀-A, 수소화된 비스페놀-A 또는 이들의 혼합물을 사용할 수 있다. 상기 이소시아네이트계 화합물은 2,4-톨루엔 디이소시아네이트, 1,3-자일렌 디이소시아네이트, 1,4-자일렌 디이소시아네이트, 1,5-나프탈렌 디이소시아네이트, 1,6-헥산 디이소시아네이트, 이소포론 디이소시아네이트 또는 이들의 혼합물을 사용할 수 있다. (메타)아크릴레이트는 탄소수 1~50의 알킬기 및 히드록시기를 갖는 (메타)아크릴레이트를 사용할 수 있다.
에폭시계 (메타)아크릴레이트는 중간의 분자 구조가 2-브로모히드로퀴논, 레졸시놀, 카테콜, 비스페놀 A, 비스페놀 F, 비스페놀 AD, 비스페놀 S 등의 비스페놀류, 4,4'-디히드록시비페닐, 비스(4-히드록시페닐)에테르 등의 골격으로 되어진 (메타)아크릴레이트 올리고머, 또는 알킬기, 아릴기, 메틸올기, 알릴기, 환상 지방족기, 할로겐(테트라브로모비스페놀 A 등), 니트로기 등으로 이루어진 (메타)아크릴레이트 올리고머군으로부터 선택되는 것을 사용할 수 있다.
말레이미드 개질 (메타)아크릴레이트는 말레이미드기를 적어도 2개 이상 함유하는 화합물, 예를 들어 1-메틸-2,4-비스말레이미드벤젠, N,N'-m-페닐렌비스말레이미드, N,N'-p-페닐렌비스말레이미드, N,N'-m-톨릴렌비스말레이미드, N,N'-4,4-비페닐렌비스말레이미드, N,N'-4,4-(3,3'-디메틸비페닐렌)비스말레이미드, N,N'-4,4-(3,3'-디메틸디페닐메탄) 비스말레이미드, N,N'-4,4-(3,3'-디에틸디페닐메탄)비스말레이미드, N,N'-4,4-디페닐메탄비스말레이미드, N,N'-4,4-디페닐프로판비스말레이미드, N,N'-4,4-디페닐에테르비스말레이미드, 2,2-비스(4-(4-말레이미드페녹시)페닐)프로판, 2,2-비스(3-t-부틸-4-(4-말레이미드페녹시)페닐)프로판, 1,1-비스(4-(4-말레이미드페녹시)페닐)데칸, 4,4'-시클로헥실리덴비스(1-(4-말레이미드페녹시)-2-시클로헥실벤젠, 2,2-비스(4-(4-말레이미드페녹시)페닐)헥사플루오르프로판 및 이들의 혼합물로 이루어지는 군으로부터 선택되는 1종 이상과 (메타)아크릴레이트, 예를 들면 탄소수 1~50의 알킬기를 갖는 (메타)아크릴레이트로부터 제조된 올리고머를 사용할 수 있다.
바람직하게는, (메타)아크릴레이트계 올리고머는 플루오렌계 (메타)아크릴레이트 올리고머를 포함할 수 있다.
(메타)아크릴레이트계 모노머는 통상의 (메타)아크릴레이트 모노머들을 제한없이 사용할 수 있다.
예를 들어, (메타)아크릴레이트 모노머는 벤질 (메타)아크릴레이트, 페녹시벤질 (메타)아크릴레이트, 페닐페녹시에틸 (메타)아크릴레이트, 1,6-헥산디올 모노(메타)아크릴레이트, 2-히드록시에틸 (메타)아크릴레이트, 2-히드록시프로필 (메타)아크릴레이트, 2-히드록시부틸 (메타)아크릴레이트, 2-히드록시-3-페닐옥시프로필 (메타)아크릴레이트, 1,4-부탄디올 (메타)아크릴레이트, 2-히드록시에틸 (메타)아크릴로일 포스페이트, 4-히드록시 사이클로헥실 (메타)아크릴레이트, 네오펜틸글리콜 모노(메타)아크릴레이트, 트리메틸올에탄 디(메타)아크릴레이트, 트리메틸올프로판 디(메타)아크릴레이트, 펜타에리스리톨 트리(메타)아크릴레이트, 펜타에리스리톨 테트라(메타)아크릴레이트, 디펜타에리스리톨 펜타(메타)아크릴레이트, 디펜타에리트리톨 헥사(메타)아크릴레이트, 글리세린 디(메타)아크릴레이트, 테트라하이드로퍼퓨릴 (메타)아크릴레이트, iso-데실 (메타)아크릴레이트, 2-(2-에톡시에톡시) 에틸 (메타)아크릴레이트, 스테아릴 (메타)아크릴레이트, 라우릴 (메타)아크릴레이트, 2-페녹시에틸 (메타)아크릴레이트, 이소보르닐 (메타)아크릴레이트, 트리데실 (메타)아크릴레이트, 에톡시부가형 노닐페놀 (메타)아크릴레이트, 에틸렌글리콜 디(메타)아크릴레이트, 디에틸렌글리콜 디(메타)아크릴레이트, 트리에틸렌글리콜 디(메타)아크릴레이트, t-에틸렌글리콜 디(메타)아크릴레이트, 폴리에틸렌글리콜 디(메타)아크릴레이트, 1,3-부틸렌글리콜 디(메타)아크릴레이트, 트리프로필렌글리콜 디(메타)아크릴레이트, 에톡시 부가형 비스페놀-A 디(메타)아크릴레이트, 사이클로헥산디메탄올 디(메타)아크릴레이트, 페녹시-t-글리콜 (메타)아크릴레이트, 2-메타아크릴로일록시에틸 포스페이트, 디메틸올 트리사이클로 데케인 디(메타)아크릴레이트, 트리메틸올프로판벤조에이트 아크릴레이트, 플루오렌계 (메타)아크릴레이트, 비스페놀 F계 (메타)아크릴레이트, 비스페놀 A계 에폭시 (메타)아크릴레이트, 노볼락계 에폭시 (메타)아크릴레이트, 페닐페녹시에틸 (메타)아크릴레이트, 에톡시레이티드 티오 디페닐 디(메타)아크릴레이트, 페닐티오에틸 (메타)아크릴레이트 및 이들의 혼합물로 이루어지는 군으로부터 선택되는 1종 이상을 사용할 수 있다.
일 실시예에서, 자외선 경화형 불포화 화합물은 (메타)아크릴레이트계 올리고머와 (메타)아크릴레이트계 모노머의 혼합물을 포함할 수 있다. 바람직하게는, (메타)아크릴레이트계 올리고머는 플루오렌 유도체 불포화 수지, (메타)아크릴레이트계 모노머는 페녹시 벤질 (메타)아크릴레이트, 페닐 페녹시 에틸 (메타)아크릴레이트, 에톡시레이티드 티오 디페닐 디(메타)아크릴레이트, 페닐 티오 에틸 (메타)아크릴레이트 또는 이들의 혼합물이 될 수 있다.
상기 혼합물에서, 상기 (메타)아크릴레이트계 모노머 대비 상기 (메타)아크릴레이트계 올리고머를 동일 또는 더 많이 포함시켜, (메타)아크릴레이트계 모노머에 대한 상기 (메타)아크릴레이트계 올리고머의 중량비는 1 이상, 바람직하게는 1-2가 될 수 있다.
한 구체예에서, 자외선 경화형 불포화 화합물은 상기 (메타)아크릴레이트계 올리고머 100중량부, 및 상기 (메타)아크릴레이트계 모노머 또는 이로부터 형성된 올리고머 30-100중량부, 바람직하게는 50-100중량부로 포함할 수 있다. 상기 범위 내에서, 공정에 적합한 1000cPs이하의 점도 특성을 갖고, 굴절율 저하가 방지되고, 고분자 주쇄의 유연성이 확보되어 필름 제조 후 크랙 발생을 방지할 수 있다.
자외선 경화형 불포화 화합물은 고형분 기준으로 조성물 100중량부 중 90-99중량부, 바람직하게는 95-98중량부로 포함될 수 있다. 상기 범위 내에서, 휘도 상승효과가 있을 수 있다.
개시제는 광학필름용 수지 조성물을 경화시켜 광학필름을 제조하게 한다. 개시제는 광중합 개시제, 라디칼 개시제 등을 사용한다. 상기 개시제로는 프로파논계, 케톤계, 포스핀옥사이드계, 포르메이트계, 포스페이트계 등을 사용할 수 있으며, 반드시 이에 제한되는 것은 아니다.
개시제는 자외선 경화형 불포화 화합물 100중량부에 대해 0.01-10중량부, 바람직하게는 0.1-10중량부, 더 바람직하게는 2-5중량부로 포함될 수 있다. 상기 범위 내에서, 광반응성이 높아 광학 필름의 기계적 강도가 저하되지 않고 잔량의 개시제가 남아 광학 특성이 저하되는 것을 막을 수 있다.
개시제는 조성물 100중량부 중 0.5-9.5중량부, 바람직하게는 1-4중량부로 포함할 수 있다. 상기 범위 내에서, 충분한 광반응성에 의한 프리즘의 기계적 특성이 확보되고, 광학필름의 황변성 등 광학적 특성 저하가 방지될 수 있다.
광학필름용 수지 조성물은 에스테르계 반응성 첨가제를 더 포함할 수 있다.
에스테르계 반응성 첨가제는 광학필름용 수지 조성물의 경화 후 투명 기재 필름과의 접착력을 향상시킬 수 있다.
에스테르계 반응성 첨가제의 예로는 에스테르계 (메타)아크릴레이트로서, 폴리에스테르계 변성 폴리실록산, 폴리에스테르계 하이드록시 다이메틸폴리실록산, 또는 이들의 혼합물 등이 사용할 수 있으며, 이에 제한되는 것은 아니다. 상업적으로는 COGNIS사의 ECX4114, ECX5031, ECX6025, PHOTOMER4846 등을 사용할 수 있다.
에스테르계 반응성 첨가제는 상기 자외선 경화형 불포화 화합물 100중량부에 대해 0.5-5중량부, 바람직하게는 0.6-3중량부로 포함할 수 있다. 상기 범위 내에서, 광학필름용 수지 조성물의 경화 후 투명 기재 필름과의 접착력 향상 효과를 얻을 수 있고, 프리즘 필름의 굴절률 저하를 방지할 수 있다.
광학필름용 수지 조성물은 실리콘계 반응형 수지를 더 포함할 수 있다.
실리콘계 반응형 수지는 광학필름용 수지 조성물과 금형 몰드와의 이형성을 높일 수 있다.
실리콘계 반응형 수지는 통상적으로 폴리에테르 실록산 공중합체나 유기변성 폴리실록산계가 많이 사용되는데, 상업적으로 시판되는 제품은 예를 들면 BYK사의 BYK UV-3500, BYK UV-3530, 또는, TEGO사의 TEGO Glide-100, TEGO Glide-ZG400, TEGO Glide-450 등으로 이루어진 군으로부터 1종 이상을 사용할 수 있다.
실리콘계 반응형 수지는 조성물의 고형분 기준으로 0.01-8중량%로 포함될 수 있다. 상기 범위 내에서, 금형 몰드와의 이형성이 향상될 수 있고 고온, 고습 환경에서의 계면간의 부착성 및 프리즘의 기계적 광학적 특성이 저하되지 않을 수 있다. 바람직하게는, 0.01-2중량%로 포함될 수 있다.
광학필름용 수지 조성물은 통상의 첨가제를 더 포함할 수 있다.
첨가제로는 대전 방지제, 항산화제, 자외선 흡수제, 광안정제, 중합 방지제, 레벨링제, 계면활성제 및 윤활제로 이루어진 군으로부터 선택될 수 있다.
광학필름용 수지 조성물은 589.3nm의 D광선 나트륨램프에 측정된 굴절률이 1.55 이상, 바람직하게는 1.556-1.582가 될 수 있다.
광학필름용 수지 조성물은 25℃에서 점도가 100-1000cps가 될 수 있다.
본 발명의 다른 관점인 광학 디스플레이 장치는 상기 광학필름을 포함할 수 있다. 광학 디스플레이 부재에서 상기 광학필름은 프리즘 시트, 확산 시트 또는 도광판으로 포함될 수 있다. 광학 디스플레이 장치는 액정표시장치를 포함할 수 있고, 액정표시장치에서 광원은 LED 램프 또는 CCFL이 포함될 수 있다.
이하, 본 발명의 바람직한 실시예를 통해 본 발명의 구성 및 작용을 더욱 상세히 설명하기로 한다. 다만, 이는 본 발명의 바람직한 예시로 제시된 것이며 어떠한 의미로도 이에 의해 본 발명이 제한되는 것으로 해석될 수는 없다. 여기에 기재되지 않은 내용은 이 기술 분야에서 숙련된 자이면 충분히 기술적으로 유추할 수 있는 것이므로 그 설명을 생략하기로 한다.
하기 실시예와 비교예에서 사용된 성분의 구체적인 사양은 다음과 같다.
(A)발광 물질:
(A1)N,N'-디메틸-퀸아크리돈(N,N'-Dimethyl-quinacridone, DMQA, LT-E503), 흡수파장 294.510nm(in THF), 광발광 파장 523nm(in THF).
(A2)9,10-비스[N,N-디-(p-톨릴)-아미노]안트라센(9,10-bis[N,N-di-(p-tolyl)-amino]anthracene, TTPA, LT-N507), 흡수파장 294.471nm(in CH2Cl2), 광발광 파장 554nm(in CH2Cl2)
(A3)9,10-비스[페닐(m-톨릴)-아미노]안트라센(9,10-bis[phenyl(m-tolyl)-amino]anthracene, TPA, LT-N508), 흡수파장 292.458nm(in CH2Cl2), 광발광 파장 532nm(in CH2Cl2)
(A4)2,3,6,7-테트라히드로-1,1,7,7-테트라메틸-1H,5H,11H,10-[2-벤조티아졸릴]퀴놀리지노[9,9a,1gh]쿠마린(2,3,6,7-tetrahydro-1,1,7,7-tetramethyl-1H,5H,11H,10-[2-benzothiazolyl]quinolizino[9,9a,1gh]coumarin, C545T, LT-E502), 흡수파장 473nm(in THF), 광발광 파장 506nm(in THF)
(A5)트리스 [2-(p-톨릴)피리딘]이리듐(III)(Tris[2-(p-tolyl)pyridine]iridium(III); Ir(mppy)3)
(B)자외선 경화형 불포화 화합물:
(B1)플루오렌계 유도체 불포화 수지(BPF-022, 한농화성, 굴절률:1.601)
(B21)페녹시벤질 아크릴레이트(굴절률:1.56)
(B22)페닐페녹시에틸 아크릴레이트(굴절률:1.54)
(C)개시제:
(C1)Irgacure 184
(C2)Darocure TPO
(C3)Irgacure 1174
(D)에스테르계 반응성 첨가제:에스테르계 아크릴레이트(ECX4114)
(E)무기 형광 물질:덕산하이메탈생산품
(E1)DPP-201R(조성은 (Y,Gd) BO3 : Eu , 발광 파장은 Red, 593nm)
(E2)DPP-501B (조성은 BaMgAl10O17 :Eu, 발광 파장은 Blue,450nm)
실시예
1-12
하기 표 1-2에 기재된 함량에 따라 자외선 경화형 불포화 화합물과 개시제를 혼합하고, 여기에 발광 물질을 첨가하고, 교반기로 혼합하여 광학필름용 수지 조성물을 제조하였다.
비교예
1
상기 실시예 1에서 발광물질을 사용하지 않은 것을 제외하고는 동일한 방법을 실시하여 조성물을 제조하였다.
비교예
2-3
상기 실시예 1에서 발광 물질 대신에 무기 형광 물질 B-1(비교예 2), B-2(비교예 3)을 각각 사용한 것을 제외하고는 동일한 방법을 실시하여 광학필름용 수지 조성물을 제조하였다.
비교예
4
상기 실시예 9에서 발광물질을 사용하지 않은 것을 제외하고는 동일한 방법을 실시하여 조성물을 제조하였다.
광학필름 제조
상기 제조한 광학필름용 수지 조성물을 프리즘 층이 인각된 금속 몰드에 도포하고, 투명기재 PET필름(폴리에틸렌테레프탈레이트 필름)의 일면을 상기 금속 몰드에 도포된 코팅면과 접촉시킨 상태에서, 190~400㎚ 파장의 자외선을 무전극형 자외선 조사 장치(600W/inch)에 D타입 벌브 (Type-D bulb) 장착하여 250-500 mJ/㎠의 에너지로 조사)하여 코팅된 조성물을 경화시켰다. 투명 기재 필름에 접착되어 경화된 코팅층을 금속 몰드로부터 분리시킴으로써, 투명 기재 필름의 일면에 프리즘층이 형성된 광학 필름을 제조하였다. 광학필름 층의 높이는 35-40㎛가 되도록 하였다.
상기 제조한 광학필름에 대해 하기의 물성을 평가하고 그 결과를 표 1-2에 나타내었다.
(1)굴절률:굴절계(모델명 : 1T, 일본 ATAGO ABBE)를 사용하여 조성물의 굴절율을 측정하였다. 측정을 위한 광원은 589.3nm의 D광선 나트륨램프를 이용하였다.
(2)휘도:32 인치 액정디스플레이 패널용 백라이트 유닛에 상기 제작된 프리즘 필름을 고정하고, 휘도계 (모델명 : SR3,일본 TOPCON사)를 사용하여 13 지점 및 5 지점의 휘도를 측정하여 평균값을 구하였다. 이때 백라이트 유닛은 LED 램프(휘도 1)와 CCFL 램프(휘도 2)를 각각 구분하여 측정하였다. 또한, 15.6 인치 액정디스플레이 패널용 백라이트 유닛에 상기 제작된 프리즘 필름을 고정하고, 휘도계 (모델명 : BM-7,일본 TOPCON사)를 사용하여 13 지점 및 5 지점의 휘도를 측정하여 평균값을 구하였다(휘도 3).
(3)시야각: 시야각 역시 휘도 장비와 동일한 장비를 사용하여 좌우(0도에서 180도) 기울기를 가하면서 측정하였다. 이때 백라이트 유닛은 LED 램프(시야각 1)와 CCFL 램프(시야각 2)를 각각 구분하여 측정하였다.
(4)분산성: 기존 UV수지 조성물에 형광 첨가제를 혼합하거나, 극성이 강한 모노머로 형광첨가제를 원심 분리기 또는 교반기를 사용하여 분산시킨 다음 수지 조성비로 조성물을 혼합하여 상온 24시간후 침전물의 유무를 통해 분산성을 확인하였다. 분산성이 좋은 경우 O, 좋지 않은 경우 X로 평가한다.
(5)색좌표: 색좌표는 2번 방법에서 사용된 휘도 측정기에서 휘도 측정과 동시에 측정하였다.
(6)자외선 황변: 황변 측정기 SMCM-H5K1(세명백트론)을 이용하여 상온 조건하에서 340nm 파장을 갖는 UV램프를 사용하여 125J, 68mW/m2에서 UV 광 조사후 1시간 방치후 색좌표를 측정하였다.
(7)접착력:투명 PET 기재필름에 조성물을 코팅한 후 경화한 다음, 기재필름을 제거한 후 경화된 두께만을 1010의 영역 내에서 100개의 매트릭스 구조로 절개한 후, 그 위에 테이프를 접착하고 수직으로 강하게 이형하면서 떨어져 나온 매트릭스의 개수로 측정하여 접착력이 좋은 경우 O, 접착력이 좋지 않은 경우 X로 평가하였다.
(8)이형성:프리즘 형상이 새겨진 금속 몰드와 폴리에스터 기재 필름 사이에 본 발명의 실시예에서 언급한 광경화형 수지 조성물을 투입하여 라미네이션 이후 금형 몰드에서 기재 필름이 이형되는 순간의 이형소리 등의 공정성을 0 ~ 10점의 이형성 점수로 나타내었다. 10점이 우수한 이형 특성을 보이는 것으로 정의하였다.
(9)내스크래치성(g):투명 PET 기재필름에 조성물을 코팅한 후 경화한 다음, 경화된 프리즘 층이 Anti-Glare 면에 접촉하도록 뒤집어 놓고, 0 ~ 100 g 사이의 분동을 올린 상태에서 5 cm 간격으로 3회 왕복시킨 후 프리즘이 손상되기 시작한 무게를 측정한다.
실시예 | 비교예 | |||||||||||
1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 1 | 2 | 3 | ||
A | A1 | 0.1 | 0.01 | - | - | - | - | - | - | - | - | - |
A2 | - | - | 0.1 | 0.01 | - | - | - | - | - | - | - | |
A3 | - | - | - | - | 0.1 | 0.01 | - | - | - | - | - | |
A4 | - | - | - | - | - | - | 0.1 | 0.01 | - | - | - | |
A5 | - | - | - | - | - | - | - | - | - | - | - | |
B | B1 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 |
B21 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | |
B22 | 30 | 30 | 30 | 30 | 30 | 30 | 30 | 30 | 30 | 30 | 30 | |
C | C1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 |
C2 | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 3 | |
C3 | - | - | - | - | - | - | - | - | - | - | - | |
D | - | - | - | - | - | - | - | - | - | - | - | |
E | E1 | - | - | - | - | - | - | - | - | - | 0.1 | - |
E2 | - | - | - | - | - | - | - | - | - | - | 0.1 | |
굴절률 | 1.558 | 1.556 | 1.558 | 1.556 | 1.558 | 1.556 | 1.558 | 1.556 | 1.556 | 1.558 | 1.558 | |
휘도 1(cd/cm2) | 6450 | 5940 | 6350 | 5870 | 6560 | 5960 | 6535 | 5865 | 5450 | 4500 | 4200 | |
휘도 2 (cd/cm2) |
5900 | 5300 | 5950 | 5350 | 6000 | 5400 | 6150 | 5500 | 4950 | 4500 | 4200 | |
시야각 1 (좌/우)각도 |
65 | 65 | 65 | 65 | 65 | 65 | 65 | 65 | 65 | 65 | 65 | |
시야각 2 (좌/우)각도 |
65 | 65 | 65 | 65 | 65 | 65 | 65 | 65 | 65 | 65 | 65 | |
분산성 | O | O | O | O | O | O | O | O | O | x | x | |
색좌표 (△y) |
8/100 | 9/1000 | 8/1000 | 5/1000 | 9/100 | 8/1000 | 9/1000 | 5/1000 | 3/1000 | 7/100 | 3/100 |
상기 표 1에서 나타난 바와 같이, 본 발명의 광학 필름은 무기 형광 물질을 포함하는 비교예 대비 휘도가 높고 무기 형광 물질의 분산성 또는 색좌표의 균일성 문제가 없었다.
실시예 | 비교예 | |||||
9 | 10 | 11 | 12 | 4 | ||
A | A1 | - | - | - | - | - |
A2 | - | - | - | - | - | |
A3 | - | - | - | - | - | |
A4 | 0.1 | 0.01 | - | 0.1 | - | |
A5 | - | - | 0.1 | - | - | |
B | B1 | 100 | 100 | 100 | 80 | 100 |
B21 | 20 | 20 | 20 | 30 | 20 | |
B22 | 30 | 30 | 30 | 40 | 30 | |
C | C1 | - | - | - | - | - |
C2 | 3 | 3 | 3 | 3 | 3 | |
C3 | 2 | 2 | 2 | 2 | 2 | |
D | 1.3 | 1.3 | 1.3 | 1.3 | 1.3 | |
E | E1 | - | - | - | - | - |
E2 | - | - | - | - | - | |
굴절률 | 1.559 | 1.559 | 1.559 | 1.558 | 1.559 | |
휘도 3(cd/cm2) | 6540 | 6450 | 5870 | 5450 | 5540 | |
자외선 황변(△YI) | 8.0 | 7.6 | 8.2 | 8.3 | 8.5 | |
접착력 | 0 | 0 | 0 | 0 | 0 | |
이형성 | 9 | 9 | 9 | 9 | 9 | |
내스크래치성(g) | 5 | 5 | 5 | 15 | 5 |
상기 표 2에서 보듯이, 본 발명의 발광 물질을 포함하는 수지 조성물을 이용하여 프리즘 박막을 형성한 실시예 9 ~ 11의 경우는 비교예 4에 비해 약 6% ~ 25 %가 상승한 높은 휘도를 갖는 것을 알 수 있다. 굴절율, 황변, 접착력 이형성 등은 발광 물질을 포함하지 않는 경우와 동등 수준을 나타내어, 공정 조건에 적합한 점도 특성을 부여하여 인각롤과의 이형성 등의 면에서 우수한 신뢰성을 갖는 효과를 보이고 있는 것으로부터, 높은 점도의 고굴절 수지를 굳이 사용하지 않아도 높은 휘도 결과를 얻을 수 있음을 알 수 있다. 실시예 12의 경우는 비교예 4에 비교하여 휘도는 동등한 수준을 갖으나, 내스크래치성이 월등하게 향상됨을 알 수 있다. 발광물질에 의한 휘도 상승 효과에 따라 내스크래치성이 취약한 고굴절 플로우렌 유도체 불포화 수지를 함량을 낮추어 내스크래치성을 향상 시키며 이에 대비 휘도는 낮아지지 않음을 확인할 수 있다.
이상 본 발명의 실시예들을 설명하였으나, 본 발명은 상기 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 제조될 수 있으며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야 한다.
Claims (14)
- 기재필름; 및 상기 기재필름 위에 형성된 광기능성층을 포함하고,
상기 기재필름과 상기 광기능성층 중 하나 이상은 발광 물질을 포함하고,
상기 발광 물질은 형광 물질과 인광 물질 중 하나 이상을 포함하는 광학필름. - 제1항에 있어서, 상기 발광 물질은 흡수 파장이 240~380nm 또는 420~480nm이고, 발광 파장이 520~580nm인 광학필름.
- 제1항에 있어서, 상기 발광 물질은 자외선 경화형 작용기를 포함하는 광학필름.
- 제1항에 있어서,
상기 형광 물질은 2,3,6,7-Tetrahydro-1,1,7,7,-tetramethyl-1H, 5H,11H-10-(2-benzothiazolyl)quinolizino[9,9a,1gh]coumarin, 4-(Dicyanomethylene)-2-tert-butyl-6-(1,1,7,7-tetramethylejulolidin-4-yl-vinyl)-4H-pyran(E), N,N'-Dimethyl-quinacridone, 9,10-bis[N,N-di-(p-tolyl)-amino]anthracene, 9,10-bis[phenyl(m-tolyl)-amino]anthracene, 5,6,11,12-Tetraphenylnaphthacene, PPV(poly(p-phenylene vinylene)), Polyfluorene, PNV(poly(naphthalene vinylene), PPN(poly peri nanphthalene), 또는 이들의 혼합물이고,
상기 인광 물질은 Tris[2-(p-tolyl)pyridine]iridium(III), Bis[3,5-difluoro-2-(2-pyridyl)phenyl-(2-carboxypyridyl)iridium(III), Tris(2-phenylpyridine)iridium(III) 또는 이들의 혼합물인 광학필름. - 제1항에 있어서, 상기 광학필름은 플루오렌 기를 포함하는 광학필름.
- 제1항에 있어서, 상기 발광물질은 상기 광학필름 중 0.001-0.5중량%로 포함되는 광학필름.
- 제1항에 있어서, 상기 광기능성층은 프리즘, 렌티큘러 렌즈, 마이크로렌즈, 엠보 형상 중 하나 이상의 광학패턴을 포함하는 광학필름.
- 제1항에 있어서, 상기 광학필름은 프리즘 시트, 확산시트, 또는 도광판으로 사용되는 광학필름.
- 제1항에 있어서, 상기 광학필름은 상기 발광 물질, 자외선 경화형 불포화 화합물 및 개시제를 포함하는 광학필름용 수지 조성물의 경화물을 포함하는 광학필름.
- 제9항에 있어서, 상기 자외선 경화형 불포화 화합물은 플루오렌계 불포화 수지; 및 페녹시벤질 (메타)아크릴레이트, 페닐페녹시에틸 (메타)아크릴레이트, 페닐티오에틸 (메타)아크릴레이트 또는 이들의 혼합물을 포함하는 광학필름.
- 제9항에 있어서, 상기 조성물은 에스테르계 반응성 첨가제, 실리콘계 반응형 수지 중 하나 이상을 더 포함하는 광학필름.
- 형광 물질과 인광 물질 중 하나 이상을 포함하는 발광 물질;
자외선 경화형 불포화 화합물; 및
개시제를 포함하는 광학필름용 수지 조성물. - 제12항에 있어서, 상기 조성물은 에스테르계 반응성 첨가제, 실리콘계 반응형 수지 중 하나 이상을 더 포함하는 광학필름용 수지 조성물.
- 제1항의 광학필름을 포함하는 광학 디스플레이 장치.