KR20060111714A - 콘택트렌즈 세정용 시트 - Google Patents
콘택트렌즈 세정용 시트 Download PDFInfo
- Publication number
- KR20060111714A KR20060111714A KR1020067017076A KR20067017076A KR20060111714A KR 20060111714 A KR20060111714 A KR 20060111714A KR 1020067017076 A KR1020067017076 A KR 1020067017076A KR 20067017076 A KR20067017076 A KR 20067017076A KR 20060111714 A KR20060111714 A KR 20060111714A
- Authority
- KR
- South Korea
- Prior art keywords
- cleaning
- sheet
- contact lens
- washing
- woven fabric
- Prior art date
Abstract
본 발명의 목적은, 콘택트렌즈에 부착 내지는 침착된 단백질 등의 더러움을 간단한 세정 조작으로 효과적으로 제거할 수 있으며, 세정 후의 콘택트렌즈를 그대로 착용해도 눈에 대한 자극이 실질적으로 없는 콘택트렌즈 세정용 시트를 제공하는 것에 있다. 즉, 본 발명은 헥사메틸렌비구아니드 유도체를 함유하는 세정액을, 부직포 또는 직편물에 함침시켜 이루어지는 것을 특징으로 하는 콘택트렌즈용 시트를 제공한다.
헥사메틸렌비구아니드 유도체, 부직포
Description
본 발명은 콘택트렌즈 세정용 시트에 관한 것이다.
현재, 콘택트렌즈로는, 착용감이 우수한 함수성 소프트 콘택트렌즈, 고산소 투과성을 갖는 하드 콘택트렌즈 등이 일반적으로 널리 사용되고 있다. 이들 콘택트렌즈는 모두 착용 후에 세정 등의 손질을 필요로 하고, 특히 함수성(含水性) 소프트 콘택트렌즈는 세균, 곰팡이 등의 미생물에 의한 오염을 방지하기 위해 소독 처리를 필요로 한다. 콘택트렌즈를 세정하는 방법으로는, 계면 활성제나 연마제 등을 함유한 세정액 또는 최근 소프트 콘택트렌즈용으로서 보급되고 있는 다목적 타입의 세정ㆍ소독ㆍ보존액을 사용하여 손끝으로 문질러 세정하는 방법이나, 과산화수소나 단백질 분해 효소를 함유하는 세정액에 담궈 두고 세정하는 방법이 알려져 있다.
그러나, 손끝으로 문질러 세정하여 충분한 세정 효과를 얻기 위해서는, 수 회∼수십 회 문지르는 횟수가 필요하고, 손끝을 세정액으로 적시지 않으면 안 되어, 조작이 번잡하고 귀찮다. 또, 문질러 세정할 때에 렌즈를 손톱 등으로 손상시키거나 파손시키는 경우가 있다. 이 때문에, 손끝으로 문질러 세정하는 것을 게을리하는 사람이 많아, 단백질 등의 오물의 축적이나 소독 효과의 저하를 일 으킬 우려가 있다.
과산화수소나 단백질 분해 효소를 함유하는 세정액에 담궈 두어 세정하는 것은, 세정 효과가 나타날 때까지 장시간이 걸리기 때문에, 긴급을 요하는 경우에는 사용할 수 없어 불편하다.
그래서, 이들 단백질의 더러움 등의 세정을 개선하기 위해, 부직포 웹이나 흡수성 재료에 계면 활성제와 방부제를 함유하는 세정액을 함침시킨 콘택트렌즈 세정 시트 (예를 들면, 특허 문헌 1, 2, 3 참조) 가 제안되어 있다. 그러나, 이들 기술에서는, 세정액에 함유되는 눈에 자극을 주는 성분, 방부제 등, 특히 방부제, 예를 들면, 염화벤잘코늄, 염화벤제토늄, 클로르헥시딘염, 소르브산 및 그 나트륨염 등이 콘택트렌즈에 부착되거나 흡착되거나 하는 문제가 있다.
또, 단백질에 대해 친화성이 있는 섬유로 이루어지는 부직포 또는 직포체에, 계면 활성제, 방부제, 단백질 용해제, 단백질 연화제, 연마 입자, 효소, 환원제, 과산화물, 킬레이트제, 염류 (무기염, 유기염), pH 조정제, 완충제 등을 배합한 세정액을 함침 처리한 세정 시트 (예를 들면, 특허 문헌 4, 5, 6, 7, 8 참조) 가 개시되어 있다. 그러나, 이들 세정 시트에는, 눈에 자극을 주는 방부제, 예를 들면, 벤조산나트륨, 4-히드록시벤조산메틸, 소르브산칼륨 등이 콘택트렌즈에 부착되거나 흡착되거나 하기 때문에, 세정액 성분을 헹굼물로 충분히 헹구어 세정할 필요가 있고, 물을 사용할 수 없는 경우에는 사용할 수 없다는 문제가 있다.
게다가, 흡수성 시트재(材)에, 염화나트륨과 염화칼륨 중 어느 하나와, 방부제 또는 방부제 및 에탄올수(水)를 함유하는 청정액을 함침시킨 것을 특징으로 하 는 콘택트렌즈용 클리너 (예를 들면, 특허 문헌 9, 10 참조) 가 개시되어 있다. 그러나, 이들 기술에서는, 이 방부제로서, 일반적으로 방부 성분으로서 알려진 파라옥시벤조산메틸, 파라옥시벤조산에틸, 파라옥시벤조산프로필, 소르브산, 소르브산칼륨, 소르브산나트륨 등, 일반적으로 살균 성분으로서 알려진 클로로헥시딘산염, 염화벤잘코늄, 염화벤제토늄, 염화세틸피리디늄, 브롬화세틸트리메틸암모늄 등이 사용되고 있다. 이들 방부제는, 이 클리너에 사용되는 흡수성 시트재의 정균성(靜菌性), 무균성을 확보하기 위해 사용되고 있지만, 콘택트렌즈에 방부제가 부착되어, 안구 자극을 일으키고 있었다.
특허 문헌 1:일본 특허공보 평1-46047호
특허 문헌 2:일본 특허공개공보 평6-317769호
특허 문헌 3:일본 특허공보 평7-74865호
특허 문헌 4:일본 특허공개공보 2000-19464호
특허 문헌 5:일본 특허공개공보 2000-19465호
특허 문헌 6:일본 특허공개공보 2000-19466호
특허 문헌 7:일본 특허공개공보 2000-19467호
특허 문헌 8:일본 특허공개공보 2000-19468호
특허 문헌 9:일본 특허공개공보 2002-296550호
특허 문헌 10:일본 특허공개공보 2002-296551호
발명의 개시
발명이 해결하고자 하는 과제
그러나, 본 발명의 목적은, 콘택트렌즈에 부착 내지는 침착된 단백질 등의 더러움을 간단한 세정 조작으로 효과적으로 제거할 수 있으며, 세정 후의 콘택트렌즈를 그대로 착용해도 눈에 대한 자극이 실질적으로 없는 콘택트렌즈 세정용 시트를 제공하는 것에 있다.
과제를 해결하기 위한 수단
그래서, 본 발명자들은, 콘택트렌즈 세정용 시트에 사용되는 부직포 또는 직편물의 무균성을 확보할 수 있고, 또한 세정용 시트로 콘택트렌즈를 세정할 때, 콘택트렌즈에 부착되지 않는 방부제나 살균제에 대하여 예의 검토한 결과, 후술하는 일반식 (Ⅰ) 로 나타나는 헥사메틸렌비구아니드 유도체가, 의외로 부직포 또는 직편물의 소재에 흡착되기 쉬운 성질을 갖고 있고, 이 유도체를 함유하는 세정액과 부직포 또는 직편물을 조합하여 세정용 시트를 제작한 결과, 부직포 또는 직편물의 무균성을 확보할 수 있으며, 게다가 이 세정용 시트로 콘택트렌즈를 세정할 때, 이 유도체가 콘택트렌즈로 이행되기 어렵다는 것을 발견하여, 본 발명을 완성하기에 이르렀다.
즉, 본 발명은,
[1] 이하의 일반식 (Ⅰ) :
(식 중, X 및 Y 는 동일해도 되고 상이해도 되며, 각각
으로 나타나는 기를 나타내고, n 은 1∼500 의 수를 나타낸다.)
로 나타나는 헥사메틸렌비구아니드 유도체를 함유하는 세정액을, 부직포 또는 직편물에 함침시켜 이루어지는 것을 특징으로 하는 콘택트렌즈 세정용 시트 ;
[2] 세정액 중의 헥사메틸렌비구아니드 유도체의 함유량이 0.1∼10ppm 인 상기 [1] 에 기재된 시트 ;
[3] 헥사메틸렌비구아니드 유도체가 폴리헥사메틸렌비구아니드인 상기 [1] 또는 [2] 에 기재된 시트 ;
[4] 부직포 또는 직편물이 그 재질에 폴리올레핀, 폴리에스테르 및 폴리아미드로 이루어지는 군에서 선택되는 적어도 1 종을 함유하는 상기 [1]∼[3] 중 어느 하나에 기재된 시트 ;
[5] 부직포 또는 직편물이 그 재질에 폴리에스테르와 폴리아미드를 함유하는 상기 [4] 에 기재된 시트 ;
[6] 부직포 또는 직편물이 평균 섬유 직경 0.3∼10㎛ 의 섬유를 함유하는 상기 [4] 또는 [5] 에 기재된 시트 ;
[7] 부직포 또는 직편물이, 비환형 단면의 섬유를 함유하는 상기 [4]∼[6] 중 어느 하나에 기재된 시트 ;
[8] 부직포 또는 직편물이 코어-쉘 구조를 갖는 바인더 섬유를 함유하는 것인 상기 [4]∼[7] 중 어느 하나에 기재된 시트 ;
[9] 상기 [1] 에 기재된 세정액과 부직포 또는 직편물을 구비하여 이루어지는 콘택트렌즈 세정용 키트
를 제공하는 것이다.
발명의 효과
본 발명에 의하면, 콘택트렌즈를 가볍게 문지르는 것만으로, 콘택트렌즈 표면 상에 침착 내지 부착된 단백질 등의 더러움을 효과적으로 제거할 수 있으며, 게다가 세정 후의 콘택트렌즈를 그대로 착용해도 눈에 대해 실질적으로 자극을 주는 일이 없는 콘택트렌즈 세정용 시트를 얻을 수 있다.
발명을 실시하기
위한 위한
최선의 형태
이하에 본 발명에 대하여 상세하게 설명한다. 본 발명의 콘택트렌즈 세정용 시트 (이하, 세정용 시트라고 하는 경우가 있음) 는, 세정액을 부직포 또는 직편물에 함침시켜 이루어지는 것으로서, 이 세정액이 상기 일반식 (Ⅰ) 로 나타나는 헥사메틸렌비구아니드 유도체를 함유하여 이루어지는 것인 것을 하나의 큰 특징으로 한다.
우선, 세정액의 상세한 것에 대하여 설명한다. 본 발명의 세정액은, 용매인 물에 이하에 서술하는 바와 같은 각종 성분을 통상적인 방법에 의해 혼합하여 용해시켜 조제할 수 있다. 물로는 특별히 한정되는 것은 아니며, 수돗물, 증류수, 정제수 등의 임의의 물을 사용할 수 있다. 또한, 용매로서의 물에는, 눈의 자극을 실질적으로 일으키지 않는 범위라면, 물 이외의 용매 성분이 함유되어 있어도 된다. 용매는 세정액 중에서 각종 성분을 제외한 잔부를 구성한다.
상기 일반식 (Ⅰ) 로 나타나는 헥사메틸렌비구아니드 유도체는, 본 발명에서 방부제 또는 살균제로서 사용된다.
이 헥사메틸렌비구아니드 유도체에는, 헥사메틸렌비구아니드 및 헥사메틸렌비구아니드의 폴리머 (즉, 폴리헥사메틸렌비구아니드) 가 함유된다. 여기에서, 폴리머란, 헥사메틸렌비구아니드 유도체의 중합도를 나타내는, 상기 일반식 (Ⅰ) 에 있어서의 n 이 2 이상인 것을 말한다. 당해 n 으로는, 바람직하게는 2∼500 의 범위이고, 보다 바람직하게는 2∼300 의 범위이며, 더욱 바람직하게는 4∼200 의 범위이다. n 은 콘택트렌즈를 구성하는 수지의 폴리머 사슬 사이로의 이 유도체의 삽입이 실질적으로 없다는 점에서 2 이상인 것이 바람직하고, 한편 양호한 살균 성능을 얻는다는 관점에서, 500 이하인 것이 바람직하다. 따라서, 본 발명의 헥사메틸렌비구아니드 유도체로는, 폴리헥사메틸렌비구아니드인 것이 바람직하다. 또한, 이 유도체는 염산염, 붕산염, 아세트산염, 글루콘산염, 술폰산염, 타르타르산염, 시트르산 등의 염이어도 된다.
본 발명에서 사용하는 헥사메틸렌비구아니드 유도체는 시판되고 있으므로, 그것을 사용할 수 있다. 시판품으로는, 예를 들면, 「Arlagard E」,「Cosmocil CQ」,「Proxel IB」,「Vantocil IB」〔이상, 아비시아 (주) 제조, 상품명〕「Mikrokill」,「Mikrokill 20」〔이상, 브룩스(Brooks)사 제조, 상품명〕등을 들 수 있다. 또한, 이들 시판품 중의 헥사메틸렌비구니아드 유도체의 n 은 약 12 이다.
상기 헥사메틸렌비구아니드유도체는 임의의 것을 단독으로 또는 2 종 이상을 혼합하여 사용할 수 있다.
본 발명의 세정액 중의 상기 헥사메틸렌비구아니드 유도체의 함유량으로는, 양호한 살균 작용을 발현시키고, 또한 충분히 눈의 자극을 억제하는 관점에서, 바람직하게는 0.1~10ppm 의 범위이고, 보다 바람직하게는 0.5∼5ppm 의 범위이다. 또한,「ppm」이란, 세정액 100 만 중량부 중의 이 유도체의 중량부로 나타낸 이 유도체의 농도를 나타낸다.
본 발명의 헥사메틸렌비구아니드 유도체는 본 발명에 사용하는 부직포 또는 직편물에 대해 흡착 작용을 나타내고, 나아가서는 부직포 또는 직편물의 감균 작용을 발현시킨다. 또, 흡착된 이 유도체는 본 발명에 사용하는 부직포 또는 직편물로부터 탈착되기 어렵기 때문에, 본 발명의 세정용 시트를 구성하는 부직포 또는 부직물로부터의 용출이 적고, 따라서, 본 발명의 세정용 시트로 세정한 후에 물로 헹구어 세정하지 않고 바로 콘택트렌즈를 착용해도 눈의 자극은 실질적으로 발생하지 않는다. 또, 이 유도체가 콘택트렌즈에 축적되는 일도 실질적으로 없다.
본 발명의 세정액에는, 콘택트렌즈와 세정용 시트의 마찰을 적게 하여 렌즈가 파손되는 것을 보다 충분히 방지한다는 관점에서, 증점성을 높이는 성질을 갖는 고분자 화합물을 첨가해도 된다. 이 고분자 화합물로는, 폴리비닐피롤리돈계 중합체, 폴리비닐 알코올계 중합체 등의 비닐계 중합체, 히드록시프로필메틸셀룰로오스, 히드록시에틸셀룰로오스, 메틸셀룰로오스 등의 셀룰로오스 유도체, 젤라틴 등의 수용성 고분자를 들 수 있다. 이들 고분자 화합물은 단독으로 또는 2 종 이상을 혼합하여 사용할 수 있다. 본 발명의 세정액 중의 이 고분자 화합물의 함유량으로는, 바람직하게는 0.01∼1 중량%, 보다 바람직하게는 0.05∼0.3 중량% 이다.
일반적으로 인간의 누액(淚液)의 pH 는 약 7, 침투압은 약 290mOsm 이다. 본 발명의 세정용 시트로 세정한 콘택트렌즈를 그대로 착용하는 경우, 소량의 세정액이 눈에 들어가게 된다. 그러므로, 세정액은 누액에 가까운 pH 및/또는 침투압으로 조절해 두는 것이 바람직하다.
본 발명의 세정액의 pH 로는, 눈에 대한 충분한 안전성을 확보하는 관점에서, 바람직하게는 6∼8 의 범위이고, 보다 바람직하게는 6.5∼7.5 의 범위이다. 세정액의 pH 의 조정에는 적어도 1 종의 완충제를 사용하는 것이 바람직하다. 이러한 완충제로는 특별히 제한은 없고, 공지된 것 중에서 적당히 선택하면 된다. 완충제로는, 예를 들면, 붕산 완충제, 시트르산 완충제, 글리신 완충제, 트리스 완충제〔트리스(히드록시메틸)아미노메탄 완충제〕, 인산 완충제, 탄산 완충제 등을 들 수 있다. 이들 중에서도 눈에 대한 자극이 낮은 점 및 콘택트렌즈에 대한 영향이 적다는 점에서 인산 완충제가 바람직하다. 인산 완충제로는, 인산2수소나트륨, 인산수소2나트륨, 인산2수소칼륨, 인산수소2칼륨이 일반적으로 널리 사용되고 있고, 입수가 용이하기 때문에, 본 발명에서 적합하게 사용된다. 이들 완충제는 단독으로 또는 2 종 이상을 혼합하여 사용할 수 있다. 세정액 중의 완충제의 함유량은, 원하는 효과가 얻어지도록 적당히 선택하면 된다.
한편, 본 발명의 세정액의 침투압으로는, pH 와 동일한 관점에서, 바람직하게는 200∼400mOsm 의 범위이고, 보다 바람직하게는 250∼350mOsm 의 범위이다. 세정액의 침투압의 조정에는 등장화제를 사용하는 것이 바람직하다. 이러한 등장화제로는, 안과적으로 허용할 수 있는 화합물이면 특별히 제한은 없고, 염화나트륨, 염화칼륨, 탄산수소나트륨 등의 무기염류 ; 글리세린, 프로필렌글리콜, 에틸렌글리콜 등의 글리콜류 ; 이들 글리콜류의 평균 분자량 1000 이하의 중합체 등의 비이온성 유기 화합물 ; 및 이들을 조합한 것을 들 수 있다. 세정액 중의 등장화제의 함유량은, 원하는 효과가 얻어지도록 적당히 선택하면 된다.
또, 착용된 콘택트렌즈의 표면 상에, 본 발명의 세정용 시트에 의한 세정 전에 침착되어 있는 다가 금속 이온을 제거할 목적으로, 본 발명의 세정액에 금속 이온 봉쇄제를 첨가해도 된다. 금속 이온 봉쇄제로는, 안과적으로 허용되는 화합물이라면 특별히 제한은 없고, 예를 들면, 에틸렌디아민4아세트산, 글루콘산, 시트르산, 타르타르산 등의 다가 카르복실산 및 이들의 나트륨염, 칼륨염 등의 염 등을 들 수 있다. 이들 금속 이온 봉쇄제는 단독으로 또는 2 종 이상을 혼합하여 사용할 수 있다. 세정액 중의 금속 이온 봉쇄제의 함유량은, 원하는 효과가 얻어지도록 적당히 선택하면 된다.
콘택트렌즈에 부착된 더러움을 보다 효과적으로 세정ㆍ제거하는 등의 관점에서, 본 발명의 세정액에, 콘택트렌즈와의 적합성이 허용되는 범위에서 적당히 계면 활성제를 첨가할 수 있다. 여기에서,「콘택트렌즈와의 적합성이 허용되는 범위」란, 눈의 자극이 실질적으로 없고, 렌즈에 대한 흡착이나 렌즈의 형상 변화가 실질적으로 생기지 않는 범위를 말한다. 첨가할 수 있는 계면 활성제로는 임의의 비이온성 계면 활성제를 들 수 있다. 그 중에서도, 폴리에틸렌옥사이드와 폴리프로필렌옥사이드의 블록 공중합체가 적합하게 적용된다. 비이온성 계면 활성제는 각각 단독으로 또는 2 종 이상을 혼합하여 사용할 수 있다. 세정액 중의 비이온성 계면 활성제의 함유량은, 원하는 효과가 얻어지도록 적당히 선택하면 된다. 또한, 본 발명의 원하는 효과의 발현을 저해하지 않는 범위라면, 양이온성 계면 활성제나 음이온성 계면 활성제가 함유되어 있어도 된다.
또, 본 발명의 세정액에, 세정력을 보다 향상시키기 위해, 효소나 단백질 연화제를 첨가해도 된다. 콘택트렌즈의 표면에 침착된 단백질 등의 더러움은 세정액에 함유된 효소나 단백질 연화제에 의해 분해될 수 있어, 콘택트렌즈의 청정성이 향상된다. 이러한 효소나 단백질 연화제로는, 안과적으로 허용되는 화합물이라면 특별히 제한은 없고, 예를 들면, 안과 영역에서 공지된 프로테아제, 리파아제, 우레아, 글리신 등을 들 수 있다. 효소나 단백질 연화제는 각각 단독으로 또는 2 종 이상을 혼합하여 사용할 수 있다. 세정액 중의 이들의 함유량은, 원하는 효과가 얻어지도록 적당히 선택하면 된다.
또, 본 발명의 세정액에는, 상기 성분 이외에, 소망에 따라, 공지된 향료, 청량화제, 연마제 등을 적당히 첨가해도 된다.
다음으로, 본 발명에 사용되는 부직포 또는 직편물에 대하여 설명한다. 부직포 또는 직편물은 본 발명의 세정액의 지지체로서 기능하기 때문에, 이하에서는, 양자를 합쳐 지지체라고 하는 경우가 있다.
본 발명의 부직포 또는 직편물은, 일반적으로는 주체 섬유, 또는 주체 섬유와 바인더 섬유의 혼합물로 구성된다. 주체 섬유란, 본 발명의 부직포 또는 직편물을 구성하는 섬유 중, 바인더 섬유 이외의 섬유를 말한다. 또, 본 명세서에서 섬유라는 기재는, 특별히 바인더 섬유라고 기재하는 것 이외에는, 통상적으로 주체 섬유를 가리키는 것으로 한다.
본 발명의 세정용 시트의 지지체의 형상으로는 특별히 한정되는 것은 아니지만, 사용의 편리성을 고려하면, 얇은 시트 형상, 예를 들면, 두께가 바람직하게는 0.001∼3㎜, 보다 바람직하게는 0.01∼1㎜, 세로 길이가 바람직하게는 10∼200㎜, 보다 바람직하게는 30∼100㎜, 가로 길이가 바람직하게는 10∼200㎜, 보다 바람직하게는 30∼100㎜ 의 시트 형상인 것이 바람직하다. 또, 지지체의 단위 면적당 중량으로는, 통상적으로 10∼100g/㎡ 정도인 것이 바람직하다.
지지체로는, 공지된 임의의 부직포 또는 직편물을 사용할 수 있으며, 그 제조 방법은 특별히 한정되지 않는다. 대량이면서 또한 저렴하게 지지체를 제조하는 관점에서, 지지체로는 부직포가 바람직하다.
주체 섬유 단독 또는 주체 섬유 및 바인더 섬유의 혼합물을 기계적으로 뜨거나, 또는 짜 직편물을, 섬유를 적층하여 접착 또는 뒤엉키게 함으로써 부직포를 얻을 수 있다.
부직포를 제조할 때에, 섬유 (주체 섬유와 바인더 섬유의 혼합물인 경우를 포함함) 를 적층시키는 방법으로는, 건식법〔단섬유 (25∼100m/m) 를, 카드라고 하는 기계나 에어레이라고 하는 공기 흐름에 의해 섬유를 일정 방향 또는 랜덤하게 나열하여 적층체를 형성하는 방법〕, 습식법 (종이를 제조하는 경우와 동일하게, 유리 섬유나 펄프 원료와 같은 매우 짧은 섬유를 수중에 분산시키고 망 형상의 네트로 떠내어 적층체를 형성하는 방법), 스판 본드법 또는 멜트 블로우법 (용해시킨 원료 수지를 노즐의 끝에서부터 용출ㆍ방사(紡絲)시켜, 네트 상에서 연속된 긴 섬유의 적층체를 직접 형성하는 방법) 등을 들 수 있다.
또, 웹 (섬유로 이루어지는 적층체) 끼리 접착시키는 방법으로는, 케미컬본드 법 (에멀젼계의 접착 수지를 함침 또는 스프레이 등의 방법으로 웹에 부착시키고, 가열하여 섬유의 교점을 접착시키는 방법), 서멀 본드법 (열융착의 하나로서, 열융착 섬유를 혼합한 웹을 열 압착 또는 열 처리하여 섬유끼리 접착시키는 방법이며, 구체적으로는, 에어 스루법, 플랫 카렌다법, 엠보스 카렌다법 등을 들 수 있다), 니들 펀치법 (웹을 경색되고 상하로 움직이는 니들(바늘)로 반복해서 찔러 섬유를 뒤엉키게 하여 결합하는 방법인데, 이 방법만으로 제품화하는 것은 적으며, 통상적으로 다른 접착법과 조합하여 사용된다), 수류 낙합법(水流絡合法) (웹에 고압의 수류를 기둥 형상으로 분사하여 섬유를 뒤엉키게 하여 결합하는 방법) 등을 들 수 있다.
지지체를 구성하는 섬유의 재질도 특별히 한정되는 것은 아니다. 본 발명의 지지체의 재질로는, 예를 들면, 코튼, 레이온, 폴리올레핀 (폴리에틸렌, 폴리프로필렌, 폴리메틸펜텐), 폴리비닐알코올계 중합체 (폴리비닐알코올, 에틸렌 변성 폴리비닐알코올 등), 폴리아미드 (PA6, PA66, PA6-12, 각종 나일론 등), 폴리에스테르 (폴리에틸렌테레프탈레이트, 폴리부틸렌테레프탈레이트, 폴리락트산 등), 폴리아크릴로니트릴, 폴리우레탄의 1 또는 2 종 이상으로 이루어지는 것을 들 수 있다. 본 발명의 지지체는 이들 재질로 이루어지는 섬유를 단독으로 또는 임의의 비율로 혼합하여 조제할 수 있다. 또한,이들 재료는 임의로 변성 처리된 것이어도 된다.
폴리올레핀, 폴리아미드 및 폴리에스테르는 상기 헥사메틸렌비구아니드 유도체를 보다 용이하게 흡착시킨다는 점에서, 지지체의 재질로는, 폴리올레핀, 폴리아미드 및 폴리에스테르로 이루어지는 군에서 선택되는 적어도 1 종을 함유하는 것이 바람직하다. 따라서, 이러한 바람직한 재질의 섬유로 이루어지는 부직포 또는 직편물에 대해 헥사메틸렌비구아니드 유도체를 함유하는 세정액을 함침시켜 본 발명의 세정용 시트를 제작하는 것이 보다 바람직하다. 그로 인하여, 세정용 시트를 구성하는 부직포 또는 직편물을 위생적으로 유지할 수가 있고, 또 상기 헥사메틸렌비구아니드 유도체의 부직포 또는 직편물로부터 용출량을 현저히 저감시킬 수 있어, 눈의 자극을 보다 효과적으로 억제할 수 있다. 또한, 지지체의 재질 중에 함유되는, 폴리올레핀, 폴리아미드 및 폴리에스테르의 합계 함유량으로는, 바람직하게는 10∼100 중량%, 보다 바람직하게는 30∼100 중량% 이다.
또, 세정용 시트 및 그것을 구성하는 부직포 또는 직편물을 더욱 높은 레벨로 위생적으로 유지하기 위해서는, 부직포 또는 직편물에 세정액을 함침시킨 후, 멸균 처리를 실시해도 된다. 멸균 방법으로는 한정되지 않지만, 간편성 등의 관점에서 오토클레이브 멸균이 일반적으로 사용된다. 그 때의 부직포 또는 직편물의 재질로는, 양호한 내멸균성을 발휘시키게 하는 관점에서, 폴리아미드 및/또는 폴리에스테르를 함유하는 것이 바람직하다. 폴리아미드 및 폴리에스테르의 합계 함유량으로는, 바람직하게는 20∼100 중량%, 보다 바람직하게는 50∼100 중량% 이다.
게다가, 지지체에 세정액을 보다 용이하게 함침시키고, 또한 얻어지는 세정용 시트의 강도를 높이는 관점에서, 지지체의 재질로는 폴리아미드와 폴리에스테르를 함유하는 것이 보다 바람직하다. 폴리아미드와 폴리에스테르의 합계 함유량으로는, 바람직하게는 20∼100 중량%, 보다 바람직하게는 50∼100 중량% 이다. 또, 부직포 또는 직편물에 함유되는 폴리에스테르와 폴리아미드의 중량비 (폴리에스테르:폴리아미드) 로는 4:1∼1:4 인 것이 바람직하고 2:1∼1:2 인 것이 보다 바람직하다.
또한, 지지체의 내멸균성, 흡수성 및 강도의 향상이라는 관점에서, 폴리에스테르로는 폴리에틸렌테레프탈레이트, 폴리부틸렌테레프탈레이트 등이 바람직하고, 폴리아미드로는 PA6, PA66 등이 바람직하다.
또, 지지체를 구성하는 섬유에 평균 섬유 직경이 바람직하게는 0.3∼10㎛, 보다 바람직하게는 0.3∼7㎛ 의 극세 섬유를 사용함으로써, 지지체에 대한 세정액의 함침량을 많게 할 수 있으며, 지지체에 보다 높은 유연성을 부여할 수 있다. 극세 섬유를 제조하는 방법으로는, 해도(海島) 구조의 섬유의 해(海) 성분을 제거하는 방법, 또는 분할성 섬유를 수류 등으로 할섬(割纖)하여 얻는 방법이 알려져 있는데, 후자의 방법이 일반적으로 사용된다. 또한, 평균 섬유 직경은 섬유 단면적과 동일한 면적을 갖는 원의 직경으로 환산하여 구한다. 지지체 중의 이 극세 섬유의 함유량으로는 바람직하게는 50∼100 중량%, 보다 바람직하게는 70∼100 중량% 이다.
게다가 지지체의 와이핑성 (더러움을 제거하는 능력) 을 높이는 관점에서, 지지체를 구성하는 섬유에 비환형 단면의 섬유를 함유하는 것이 바람직하고, 비환형 단면의 상기 극세 섬유를 함유하는 것이 보다 바람직하다. 여기에서, 「비환형 단면」이란 엄밀한 것이 아니라, 예를 들면, 전자 현미경 (배율:3000 배 정도) 에 의해 섬유 단면을 관찰했을 때에 일견하여 환형이 아니라, 예를 들면, 각을 적어도 3 개 이상 갖는 형상이며, 보다 구체적으로는 삼각형, 사각형 등의 다각형, 또는 타원 등의 편평한 형상으로 판단할 수 있는 정도의 형상을 말한다. 지지체 중의 비환형 단면의 섬유의 함유량으로는, 바람직하게는 50∼100 중량%, 보다 바람직하게는 70∼100 중량% 이다.
본 발명의 세정용 시트에서는, 콘택트렌즈의 더러움을 닦아냈을 때, 세정용 시트로부터 이탈된 섬유 (린트) 가 콘택트렌즈에 부착되는 것을 피하는 것이 바람직하다. 이 목적을 위해서는 지지체로서 장섬유로 이루어지는 직편물 또는 스판본드 부직포를 사용하는 것이 바람직하다. 또, 단섬유로 이루어지는 부직포를 사용하는 경우에는, 수류 낙합 등의 낙합 처리나, 바인더 섬유를 사용하여, 닦아 낼 때 린트가 발생하는 것을 억제할 수 있다.
바인더 섬유로는, 코어-쉘 구조 (코어:섬유 형성성 수지, 쉘:바인더 수지) 를 갖고 있는 것이 바람직하고, 또 쉘 성분 수지로는, 코어 성분보다 낮은 융점을 갖는 수지, 또는 유리 전이 온도가 낮고, 또한 열접착성을 갖는 것이 바람직하다. 바인더 섬유는 특별히 한정되지 않지만, 코어 성분이 폴리에틸렌테레프탈레이트, 또한 쉘 성분이 변성 폴리에틸렌테레프탈레이트인 것이나, 코어 성분이 폴리프로필렌, 또한 쉘 성분이 폴리에틸렌인 것 등이 일반적으로 사용된다. 바인더 섬유로서 구체적으로는, (주) 쿠라레사 제조의「소핏트 N720」 (상품명) 등을 들 수 있다.
바인더 섬유는 지지체에 임의로 혼합하여 사용하면 되는데, 세정용 시트의 강도를 양호하게 유지하고, 또한 린트의 발생을 충분히 억제하는 관점에서, 바인더 섬유의 함유량으로는, 지지체 중, 바람직하게는 5∼30 중량%, 보다 바람직하게는 5∼25 중량% 이다. 따라서, 이 경우, 지지체 중의 주체 섬유의 함유량으로는, 바람직하게는 70∼95 중량%, 보다 바람직하게는 75∼95 중량% 이다. 또한, 지지체에 바인더 섬유가 함유되는지 아닌지에 관계없이, 상기한 바와 같이, 오토클레이브 멸균 등의 처리를 적당히 실시해도 된다.
본 발명의 부직포 또는 직편물로는, 주체 섬유가, 그 재질에 폴리에스테르와 폴리아미드를 함유하는 평균 섬유 직경 0.3∼10㎛, 특히 비환형 단면의 극세 섬유로 이루어지고, 게다가 코어-쉘 구조를 갖는 바인더 섬유를 함유하는 것이 특히 적합하다.
본 발명의 세정용 시트의 흡수성으로는 특별히 한정되는 것은 아니지만, 지지체에 세정액을 함침시켜 얻어지는 세정용 시트의 유연성의 향상이라는 관점에서, 바람직하게는 100∼5000%, 보다 바람직하게는 700∼1400% 정도이다. 또한, 세정용 시트의 흡수성이란, 구체적으로는 지지체의 흡수성을 말한다. 흡수성은 후술하는 실시예에 기재된 방법에 의해 구해진다.
본 발명의 세정용 시트는, 상기 헥사메틸렌비구아니드 유도체를 함유하는 세정액을 원하는 형태를 가지는 부직포 또는 직편물에 공지된 방법에 의해 함침시킴으로써 얻어진다. 함침의 형태로는, 세정액이 부직포 또는 직편물 전체에 균일하게 함침되어 있는 것이 바람직하다. 세정용 시트에 있어서의 세정액의 함유량은, 사용하는 부직포 또는 직편물의 상기 흡수성 등을 고려하여 적당히 설정할 수 있다.
이상과 같이 하여 얻어지는 본 발명의 세정용 시트는, 콘택트렌즈에 직접 대어 가볍게 문질러 사용된다. 이로 인하여, 이 콘택트렌즈에 부착 내지는 침착된 단백질 등의 더러움을 효과적으로 제거할 수가 있으며, 게다가 세정 후에는 그대로 눈에 착용할 수 있다. 또, 원하는 바에 따라, 콘택트렌즈를 본 발명의 세정용 시트에 끼운 상태로 보존하거나, 계속해서 시판되는 렌즈 케이스와 세정액 등을 사용하여 소독이나 보존 등을 실시할 수 있다.
본 발명의 세정용 시트에 대해, 원하는 바에 따라, 멸균 조작이나 포장 등을 실시할 수 있다. 본 발명의 세정용 시트는, 포장재에 수납하여 밀봉된 형태로 하고, 사용시에 개봉하여 꺼낼 수 있는 것으로 하면, 함침된 세정액의 세정용 시트로부터의 건조가 방지되고, 사용의 간편성이 우수하고 휴대성도 양호하여 편리하다. 이러한 세정용 시트와 그것을 수납하는 포장재로 이루어진 세정 용구에 있어서, 포장재의 형태는 특별히 한정되는 것은 아니지만, 봉지 형상인 것이 휴대성 면에서 바람직하고, 또 포장재의 소재로는, 세정용 시트의 건조 방지면 및 개봉용이성면에서 수증기 투과성이 낮은 필름인 것이 바람직하다. 상기 세정용 시트를 포장재에 수납하여 이루어지는 세정 용구에서는, 포장재 중의 세정액의 전체량이, 상기의 세정용 시트의 흡수성을 초과하는 양이어도 된다. 포장재 중에 세정액이 세정용 시트의 흡수성을 초과하는 양으로 함유되는 경우, 이 포장재는, 본 발명의 세정용 시트 (지지체 및 세정액) 와 잉여 세정액을 수납하게 된다. 따라서, 상기 세정 용구에 있어서, 포장재 중에 존재하는 세정액의 전체량은, 넓은 범위에서 임의로 선택할 수 있지만, 통상적으로 세정용 시트의 지지체 (부직포 또는 직편물) 100 중량부에 대해 100∼10000 중량부가 바람직하고, 100∼5000 중량부가 보다 바람직하며, 300∼2000 중량부가 더욱 바람직하다. 이러한 세정 용구의 제조 방법으로는 특별히 제한은 없지만, 예를 들면, 1. 헥사메틸렌비구아니드 유도체를 함유하는 세정액을 원하는 형태를 갖는 부직포 또는 직편물에 미리 첨가하고, 함침시킨 후에 포장하는 방법, 2. 원하는 형태를 갖는 부직포 또는 직편물을 미리 포장재에 충전한 후에, 포장재에 헥사메틸렌비구아니드 유도체를 함유하는 세정액을 첨가하는 방법 등을 들 수 있다.
또, 본 발명의 일 태양으로서, 상기 세정액과, 부직포 또는 직편물 (바람직하게는 시트형상) 을 구비하여 이루어지는 콘택트렌즈 세정용 키트를 제공한다. 이러한 키트는 그 사용시에, 세정액을 부직포 또는 직편물에 적당량 함침시켜 본 발명의 세정용 시트를 얻고, 사용할 수 있다. 또한, 이 키트에는 사용 방법 등을 기재한 설명서 등을 임의로 포함시켜도 된다.
본 발명의 세정용 시트 또는 키트의 사용 대상인 콘택트렌즈로는 특별히 한정되지 않으며, 착용감이 우수한 소프트 콘택트렌즈, 고산소 투과성을 갖는 하드 콘택트렌즈, 비함수 콘택트렌즈 등을 들 수 있다.
이하, 본 발명을 실시예 등에 의해 구체적으로 설명하지만, 본 발명은 그들에 의해 전혀 한정되지 않는다. 이하의 실시예 등에 있어서 사용한 측정 방법 또는 평가 방법을 정리하여 나타낸다.
(1) 눈의 자극성
콘택트렌즈 협회 자율 기준에 준하여, 소프트 콘택트 렌즈, (쿠라레 메디컬 사 제조, 상품명「쿠라라 소프트 파실」; 도수 -3.00, 직경 14.0㎜, 베이스 커브 8.70m m ) 및 하드 콘택트렌즈 (쿠라레 메디컬 사 제조, 상품명「쿠라라 슈퍼오 EX」; 도수 -3.00, 직경 8.8㎜, 베이스 커브 7.75㎜) (이하, 양자를 합쳐 콘택트렌즈라고 하는 경우가 있음) 에 대해, 제작한 세정용 시트로 1 개월간 세정을 실시한 상태에 상당하는 상태를 형성하는 처리를 실시하였다. 처리 후의 콘택트렌즈를 생리 식염수에 의한 추출 조작에 제공하고, 얻어진 추출액에 대하여 드레이즈법에 의한 집토끼 눈의 자극 시험을 실시하였다.
(2) 세정용 시트 보존 중의 균의 발생
일본 약국방 무균 시험 및 보존 효력 시험에 준하여 세정용 시트 보존 중의 균의 발생을 평가했다.
(3) 단백질 더러움의 세정 효과
(단백질 더러움 콘택트렌즈의 제작)
바이알병 (5mL 용량) 중에 이하의 조성이 되는 인공 누액 (2mL) 및 콘택트 렌즈를 넣어 2 시간에 걸쳐 침지 및 가열 (100℃) 처리를 실시해 단백질 더러움 콘택트렌즈를 제작하였다.
인공 누액 조성 (인공 모델 혼합 더러움액):
난백 알부민 0.38 중량%, 리조침 0.12 중량%, 소 혈청 γ-글로불린 0.16 중량%, 정제수 잔부.
(세정력 시험)
단백질 오염 콘택트렌즈를 세정용 시트에 끼우고, 세정용 시트 위에서부터 5초간 문질러 세정한 후, 단백질 추출 시약 (1% SDS/1% NA2CO3) 에 이 콘택트렌즈를 18 시간에 걸쳐 침지시켜 단백질을 추출하고, 얻어진 추출액의 단백질 농도 (㎍/mL) 를 BCA법으로 측정하였다. 이어서 이하의 식 :
세정력 (%)=
〔1-(세정 후 렌즈에서의 단백질 농도/오염 렌즈에서의 단백질 농도)〕×100
에 의해, 세정용 시트에 의한 콘택트렌즈의 세정력(%)을 구하고, 얻어진 세정력의 값에 의해, 이하의 평가 기준에 따라 세정용 시트의 단백질 더러움의 세정 효과를 평가하였다.
〔평가 기준〕
×:세정력 (%) 이 0∼50%
△:세정력 (%) 이 51∼80%
○:세정력 (%) 이 80% 이상
(4) 세정용 시트 중의 살균 성분 또는 방부 성분의 함유량 및 용출량
세정용 시트 중의 살균 성분 또는 방부 성분의 함유량은, 이하의 식:
함유량 (㎍)=
세정액 중의 살균 성분 또는 방부 성분의 농도 (ppm)×함침 세정액량 (mL)
에 의해 구하였다. 또, 제작한 세정용 시트를 개방 시스템에서 실온 (25℃) 에서 2 시간 보존한 후, 각 세정용 시트를 10mL 의 생리 식염수 안에 넣어 2 시간에 걸쳐 실온에서 교반하였다. 이 생리 식염수에 대해 자외 가시 흡광도 측정 (흡광도: 237nm) 을 실시하고, 미리 작성해 둔 검량선을 기초로 생리 식염수 중의 살균 성분 또는 방부 성분의 농도를 구하였다. 이어서, 이하의 식:
용출량 (㎍)=
생리 식염수 중의 살균 성분 또는 방부 성분의 농도 (ppm)×생리 식염수량 (mL)
에 의해 살균 성분 또는 방부 성분의 용출량을 구하였다.
(5) 내멸균성
세정용 시트를 내오토클레이브성을 갖는 포장 자재로 포장하고, 121℃, 1.2×105 Pa 에서 40 분간, 오토클레이브 멸균 처리를 실시하고, 이하의 평가 기준에 의해 내멸균성을 평가하였다.
〔평가 기준〕
×:세정용 시트에 변형이 관찰된다
△:세정용 시트에 변형은 관찰되지 않지만, 포장 용기에 대한 부착이 관찰된다.
○:세정용 시트에 변형도, 포장 용기에 대한 부착도 관찰되지 않는다.
(6) 흡수성
세정용 시트에 지지체로서 사용하는 시트 소재를 약 0.1g 씩 재단하고, 그 중량 (W0) 을 측정하였다. 재단한 시트 소재에 대해, 재단 전의 이 시트 소재 1㎠ 당 1.2mL에 상당하는 양의 증류수를 첨가하고, 실온 (25℃) 에서 평형이 될 때까지 습도를 조정하지 않은 개방 시스템으로 방치하였다 (약 30 분간 정도). 그 후, 핀셋으로 시트의 모서리를 들어올려 액을 제거 (약 30 초 정도) 한 후, 팽윤된 시트 소재의 중량 (W1) 을 측정하였다. 또한, 흡수성은 이하의 식에 의해 산출했다.
흡수성 (%)=((W)1-W0 )/W0)×100
(7) 손상성
콘택트렌즈 협회 자율 기준에 준하여, 하드 콘택트렌즈 (쿠라레 메디컬 사 제조, 상품명 「쿠라라 슈퍼오 EX」; 도수 -3.00, 직경 8.8㎜, 베이스 커브 7.75㎜ ) 에 대해, 제작한 세정용 시트로 1 개월간 세정을 실시한 상태에 상당하는 상태를 형성하는 처리를 실시하였다. 이하의 평가 기준에 의해, 세정용 시트에서의 세정에 의한 콘택트렌즈의 손상성을 평가하였다.
〔평가 기준〕
×:육안으로 흠집을 확인할 수 있다.
△:루페 (배율:10 배) 로 흠집이 관찰된다.
○:상처가 인정되지 않는다.
(8) 세정용 시트의 파손
콘택트렌즈 협회 자율 기준에 준하여, 하드 콘택트렌즈 (쿠라레 메디컬 사 제조, 상품명 「쿠라라 슈퍼 오 EX」; 도수 -3.00, 직경 8.8㎜, 베이스 커브 7.75㎜ ) 에 대해, 제작한 세정용 시트로 1 개월간 세정을 실시한 상태에 상당하는 상태를 형성하는 처리를 실시하였다. 이하의 평가 기준에 의해, 세정에 사용한 후의 세정용 시트의 파손 정도에 대하여 평가하였다.
〔평가 기준〕
×:육안으로 파손을 확인할 수 있다.
△:루페 (배율:10 배) 로 미소한 파손이 관찰된다.
○:파손이 관찰되지 않는다.
(9) 린트의 부착
소프트 콘택트렌즈 (존슨앤드존슨사 제조, 상품명 「2week 아큐뷰」; 도수 -3.00, 직경 14.0㎜, 베이스 커브 8.70㎜) 를 10분간 세정용 시트로 문질렀다. 이하의 평가 기준에 의해 렌즈에 대한 세정용 시트에서 탈락된 섬유 (린트) 의 부착 정도를 평가하였다.
〔평가 기준〕
×:육안으로 린트의 부착이 관찰된다.
△:루페 (배율: 10 배) 로 린트의 부착이 관찰된다.
○:린트의 부착이 관찰되지 않는다.
참고예 1
에틸렌 변성 폴리비닐알코올 (EVAL)〔(주) 쿠라레 제조, E112YS, 에틸렌 함량 44 몰, MI 12g/10 분〕과 폴리프로필렌(PP)〔이데미츠 석유화학 (주) 제조, Y3002G, MI 30g/10 분〕을 표 1 에 나타낸 비율로 혼합한 것을 원료로 한 11층의 접착형 분할 섬유의 숏 컷 (섬유 직경 10㎛, 컷 길이 5㎜) 을 이용하고, 초지(抄紙) 후 수류 낙합 처리를 실시하여, 평균 섬유 직경이 약 0.9㎛, 단위 면적당 중량 약 60g/㎡ 의 습식 스판 레이스 (EVAL/PP) 를 제작하였다. 또한, 구성 섬유의 단면은 비환형 (보다 상세하게는, 편평한 사각형) 이였다.
참고예 2
폴리프로필렌 (PP)〔이데미츠 석유 화학 (주) 제조, Y3002G, MI 30g/10 분〕을 섬(島) 성분, 열가소성 폴리 비닐 알코올〔(주) 쿠라레 제조, 에그세발 CP4104B2〕을 해 성분으로 하고, 해도 중량 비율이 70:30 인 36 도의 해도 복합 섬유의 필라멘트 (섬유 직경 20㎛, 컷 길이 5㎜) 를 제사(製絲)하여 편지로 한 후에 90℃ 의 열수로 해 성분을 용해 제거하여 평균 섬유 직경 0.4㎛ 인 극세 폴리프로필렌 섬유로 이루어지는, 단위 면적당 중량 85g/㎡ 의 편지 (PP) 를 제작하였다.
참고예 3
참고예 2 에서 사용한 폴리프로필렌 대신에, 폴리에틸렌테레프탈레이트〔고유 점도 0.51 (페놀/테트라클로로에탄의 등(等)중량 혼합 용매로 30℃ 에서 측정) 〕, 또 열가소성 폴리비닐알코올 대신에 저밀도 폴리에틸렌 (미츠이 화학 (주) 제조, 미라손 FL60, MI70g/10 분) 을 사용한 것 이외에는, 참고예 2 와 동일하게 하여 편지로 하고, 90℃ 의 톨루엔으로, 해 성분을 용해 제거하여 평균 섬유 직경 약 0.4㎛ 인 극세 폴리에틸렌테레프탈레이트 섬유로 이루어지는, 단위 면적당 중량 85g/㎡ 의 편지 (PET) 를 제작하였다.
참고예 4
참고예 2 에 사용한 폴리프로필렌 대신에 나일론 6 (우베 흥산사 제조, UBE 나일론, 1013BK1) 을 사용하고, 또 열가소성 폴리비닐알코올 대신에 고유 점도 0.51 (페놀/테트라클로로에탄의 등중량 혼합 용매로 30℃ 에서 측정) 로 술포이소프탈산 5 몰%, 에틸렌글리콜 4 몰% 변성의 폴리에틸렌테레프탈레이트를 사용한 것 이외에는, 참고예 2 와 동일하게 하여 편지로 한 후에, 98℃ 의 40g/L의 수산화나트륨 수용액으로 해 성분을 용해 제거하여 평균 섬유 직경 약 0.4㎛ 인 극세 나일론 6 섬유로 이루어지는, 단위 면적당 중량 85g/㎡ 의 편지(Ny) 를 제작하였다.
참고예 5
참고예 1 의 에틸렌 변성 폴리비닐알코올 및 폴리프로필렌을 사용하는 대신에, 참고예 3 과 4 에서 각각 사용한 폴리에틸렌테레프탈레이트 및 나일론 6 을 표 1 에 나타낸 비율로 사용하고, 방사 조건을 적당히 변경한 것 이외에는 참고예 1 과 동일하게 하여 11 층의 접착형 분할 섬유의 숏 컷 (섬유 길이 20㎛, 컷길이 5㎜) 을 사용하고, 초지 후 수류 낙합 처리를 실시하여, 평균 섬유 직경이 약 1.8㎛, 단위 면적당 중량 약 60g/㎡ 인 습식 스판 레이스 (PET/Ny) 를 제작했다. 또 한, 구성 섬유의 단면은 비환형 (보다 상세하게는 편평한 사각형) 이었다.
참고예 6
참고예 5 에 준하여, 폴리에틸렌테레프탈레이트와 나일론 6 을 표 1 에서 나타내는 각 비율로 사용하여 제작한 폴리에틸렌테레프탈레이트와 나일론 6 의 11 층의 접착형 분할 섬유, 및 바인더 섬유〔(주) 쿠라레 사 제조, 소핏트 N720〕를 표 1 에 나타내는 비율로 사용하고, 초지 후 수류 낙합 처리를 실시하여, 평균 섬유 직경이 약 1.8㎛, 단위 면적당 중량 약 60g/㎡ 인 습식 스판 레이스(PET/Ny)를 제작하였다. 또한, 구성 섬유의 단면은 비환형 (보다 상세하게는 편평한 사각형) 이었다.
참고예 7
참고예 6 에 사용한 폴리에틸렌테레프탈레이트와 나일론 6 의 11 층의 접착형 분할 섬유 대신에 폴리에틸렌테레프탈레이트와 참고예 2 와 동일한 폴리프로필렌의 11 층의 접착형 분할 섬유를 사용한 것 이외에는, 참고예 6 에 준하여, 초지 후 수류 낙합 처리를 실시하여, 평균 섬유 직경이 약 1.8㎛, 단위 면적당 중량 약 60g/㎡ 인 습식 스판 레이스(PET/PP)를 제작하였다. 또한, 구성 섬유의 단면은 비환형 (보다 상세하게는 편평한 사각형) 이였다.
참고예 8
코튼을 원료로 한 부직포〔아사히카세이 섬유 (주) 제조, 벤리제 SP-204〕를 지지체로서 사용했다.
실시예 1∼18 및 비교예 1∼7
이하의 표 1 에 나타내는 참고예의 각 시트 소재 (5cm×5cm, 두께 0.5㎜) 에, 이하의 표 2 에 나타내는 조성〔표 중, 물 1 (L) 란 세정액의 전체를 물로 1L 로 한 것을 의미하고, PHMB란 폴리헥사메틸렌비구니아드를 나타내고, 아비시아 (주) 제조, 상품명 「Cosmocil CQ」를 사용하였다〕을 갖는 세정액 각 1mL 를 함침시켜, 실시예 1∼18 및 비교예 1∼7 의 세정용 시트를 각각 제작하였다. 이 세정용 시트에 대하여, (1) 눈의 자극성, (2) 세정용 시트 보존 중의 균의 발생, (3) 단백질 더러움의 세정 효과, 및 (4) 세정용 시트 중의 살균 성분 또는 방부 성분의 함유량 및 용출량에 대하여 측정 또는 평가하였다. 이들의 결과를 이하의 표 3 에 나타낸다. 또한, 표중, 「SCL」란 소프트 콘택트렌즈를, 「HCL」란 하드 콘택트렌즈를 나타낸다.
또, 실시예 9∼18 의 세정용 시트에 대하여, (5) 내멸균성, (6) 흡수성, (7) 손상성 (8) 시트의 파손, (9) 린트의 부착에 대하여 측정 또는 평가하였다. 이 결과를 이하의 표 4 에 나타낸다.
비교예 8
이하의 표 2 에 나타내는 조성을 갖는 살균 성분 또는 부패 성분을 함유하지 않는 세정액을 조제하고, 부직포 또는 직편물을 함침시키지 않은 상태에서 사용하여 이 세정액의 (1) 눈의 자극성을 평가하였다. 또, 부직포 또는 직편물을 사용하지 않고, 이 세정액 3mL 으로 단백질 오염 콘택트렌즈를 헹구어 세정한 후, 세정액 3mL 에 실온에서 4 시간 침지하여, (3) 단백질 더러움 세정 효과를 평가하였다. 이 결과를 이하의 표 3 에 나타낸다.
표 3 의 결과로부터, 본 발명품인 실시예 1∼18 의 헥사메틸렌비구아니드 유도체 (PHMB) 를 함유하는 세정액을 부직포 또는 직편물에 함침시켜 이루어지는 세정용 시트는, PHMB 의 용출량이 적고 눈의 자극이 없으며, 균의 발생이 없고, 세정 성능도 우수하다는 것을 알 수 있다.
한편, 세정액 중에 염화벤잘코늄을 50㎍ 함유하는 비교예 1 및 5 에서는, 콘택트렌즈에 살균 성분이 이행되어 버려, 눈의 자극을 야기시키고 만다. 게다가, 비교예 1 로부터 염화벤잘코늄의 함유량을 5㎍ 까지 저하시킨 비교예 2 에 있어서도, 콘택트렌즈에 염화 벤잘코늄이 부착되어 버려, 눈의 자극을 야기시키고 만다. 또, 세정액 중에 소르브산나트륨을 700㎍ 함유하는 비교예 3 및 6 에서는, 콘택트렌즈에 소르브산나트륨이 부착되어 버려, 눈의 자극을 야기킬 뿐만 아니라, 부직포 또는 직편물의 무균성도 확보되지 않는다. 게다가, 세정액 중에 살균 성분이나 방부 성분이 함유되지 않은 비교예 4 및 비교예 7 에서는, 눈의 자극은 없지만, 부직포 또는 직편물의 무균성이 확보되지 않는다. 또한, 비교예 8 의 경우에서는 세정 효과를 얻을 수 없었다.
게다가, 표 4 의 결과로부터, PET/Ny 의 극세 섬유를 사용한 실시예 9∼15 에서는 높은 내멸균성을 나타냈다. PET/Ny의 조성비가 2/1∼1/2 인 실시예 9, 11, 12, 14 및 15 는 우수한 흡수성을 나타냄과 함께, 시트의 파손도 관찰되지 않아, 세정용 시트로서 우수한 성능을 나타냈다. 게다가, 바인더 섬유를 10∼20 중량% 배합한 실시예 11, 12 및 14 는 린트의 부착도 관찰되지 않고, 손상성도 양호하여 세정용 시트로는 가장 우수한 성능을 나타냈다.
이상부터, 본 발명의 세정용 시트는 콘택트렌즈의 세정 수단으로서 매우 우수한 것인 것이 분명하다.
본 발명에 의해, 콘택트렌즈에 부착 내지는 침착된 단백질 등의 더러움을 간단한 세정 조작으로 효과적으로 제거할 수 있으며, 세정 후의 콘택트렌즈를 그대로 착용해도 눈에 대한 자극이 실질적으로 없는 콘택트렌즈 세정용 시트가 제공된다.
Claims (9)
- 제 1 항에 있어서,세정액 중의 헥사메틸렌비구아니드 유도체의 함유량이 0.1∼10ppm 인 시트.
- 제 1 항 또는 제 2 항에 있어서,헥사메틸렌비구아니드 유도체가 폴리헥사메틸렌비구아니드인 시트.
- 제 1 항 내지 제 3 항 중 어느 한 항에 있어서,부직포 또는 직편물이 그 재질에 폴리올레핀, 폴리에스테르 및 폴리아미드 로 이루어지는 군에서 선택되는 적어도 1 종을 함유하는 시트.
- 제 4 항에 있어서,부직포 또는 직편물이 그 재질에 폴리에스테르와 폴리아미드를 함유하는 시트.
- 제 4 항 또는 제 5 항에 있어서,부직포 또는 직편물이 평균 섬유 직경 0.3∼10㎛ 의 섬유를 함유하는 시트.
- 제 4 항 내지 제 6 항 중 어느 한 항에 있어서,부직포 또는 직편물이 비환형 단면의 섬유를 함유하는 시트.
- 제 4 항 내지 제 7 항 중 어느 한 항에 있어서,부직포 또는 직편물이 코어-쉘 구조를 갖는 바인더 섬유를 함유하는 시트.
- 제 1 항에 기재된 세정액과 부직포 또는 직편물을 구비하여 이루어지는 콘택트렌즈 세정용 키트.