KR101085797B1 - 고 용융 유동 속도를 갖는 폴리프로필렌 동종중합체 또는 랜덤 공중합체를 제조하기 위한 지글러-나타 촉매의 용도 - Google Patents
고 용융 유동 속도를 갖는 폴리프로필렌 동종중합체 또는 랜덤 공중합체를 제조하기 위한 지글러-나타 촉매의 용도 Download PDFInfo
- Publication number
- KR101085797B1 KR101085797B1 KR1020087025728A KR20087025728A KR101085797B1 KR 101085797 B1 KR101085797 B1 KR 101085797B1 KR 1020087025728 A KR1020087025728 A KR 1020087025728A KR 20087025728 A KR20087025728 A KR 20087025728A KR 101085797 B1 KR101085797 B1 KR 101085797B1
- Authority
- KR
- South Korea
- Prior art keywords
- melt flow
- propylene polymer
- weight
- article
- propylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Links
- 239000003054 catalyst Substances 0.000 title claims description 13
- 229920005629 polypropylene homopolymer Polymers 0.000 title 1
- 229920005630 polypropylene random copolymer Polymers 0.000 title 1
- -1 magnesium halide Chemical class 0.000 claims abstract description 39
- 238000000034 method Methods 0.000 claims abstract description 30
- 150000001875 compounds Chemical class 0.000 claims abstract description 20
- QQONPFPTGQHPMA-UHFFFAOYSA-N propylene Natural products CC=C QQONPFPTGQHPMA-UHFFFAOYSA-N 0.000 claims abstract description 18
- 125000004805 propylene group Chemical group [H]C([H])([H])C([H])([*:1])C([H])([H])[*:2] 0.000 claims abstract description 18
- 230000008569 process Effects 0.000 claims abstract description 14
- 239000011954 Ziegler–Natta catalyst Substances 0.000 claims abstract description 12
- 229920005604 random copolymer Polymers 0.000 claims abstract description 10
- 229910052749 magnesium Inorganic materials 0.000 claims abstract description 8
- 239000011777 magnesium Substances 0.000 claims abstract description 8
- 238000001746 injection moulding Methods 0.000 claims abstract description 7
- 239000010936 titanium Substances 0.000 claims abstract description 7
- 229910052719 titanium Inorganic materials 0.000 claims abstract description 7
- 229910052736 halogen Inorganic materials 0.000 claims abstract description 6
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 claims abstract description 5
- 230000000379 polymerizing effect Effects 0.000 claims abstract description 5
- 229920001155 polypropylene Polymers 0.000 claims description 53
- 238000006116 polymerization reaction Methods 0.000 claims description 31
- 239000000155 melt Substances 0.000 claims description 18
- 229920000642 polymer Polymers 0.000 claims description 16
- VGGSQFUCUMXWEO-UHFFFAOYSA-N Ethene Chemical compound C=C VGGSQFUCUMXWEO-UHFFFAOYSA-N 0.000 claims description 15
- 239000005977 Ethylene Substances 0.000 claims description 15
- 238000004519 manufacturing process Methods 0.000 claims description 12
- 229910052739 hydrogen Inorganic materials 0.000 claims description 9
- 239000001257 hydrogen Substances 0.000 claims description 9
- 238000004806 packaging method and process Methods 0.000 claims description 9
- 239000003795 chemical substances by application Substances 0.000 claims description 8
- 239000000178 monomer Substances 0.000 claims description 6
- 229910052782 aluminium Inorganic materials 0.000 claims description 5
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims description 5
- 150000003609 titanium compounds Chemical class 0.000 claims description 5
- 239000004711 α-olefin Substances 0.000 claims description 5
- 238000002347 injection Methods 0.000 claims description 4
- 239000007924 injection Substances 0.000 claims description 4
- 125000000217 alkyl group Chemical group 0.000 claims description 3
- 125000004432 carbon atom Chemical group C* 0.000 claims description 3
- 125000004122 cyclic group Chemical group 0.000 claims description 3
- 125000000753 cycloalkyl group Chemical group 0.000 claims description 3
- 238000012360 testing method Methods 0.000 claims description 3
- 150000005840 aryl radicals Chemical class 0.000 claims description 2
- 229910052799 carbon Inorganic materials 0.000 claims description 2
- 238000000748 compression moulding Methods 0.000 claims description 2
- 238000010102 injection blow moulding Methods 0.000 claims description 2
- 238000010103 injection stretch blow moulding Methods 0.000 claims description 2
- 238000009512 pharmaceutical packaging Methods 0.000 claims description 2
- 125000003367 polycyclic group Chemical group 0.000 claims description 2
- OAICVXFJPJFONN-UHFFFAOYSA-N Phosphorus Chemical compound [P] OAICVXFJPJFONN-UHFFFAOYSA-N 0.000 claims 1
- 150000001721 carbon Chemical group 0.000 claims 1
- 239000003623 enhancer Substances 0.000 claims 1
- 229910052698 phosphorus Inorganic materials 0.000 claims 1
- 239000011574 phosphorus Substances 0.000 claims 1
- 239000003039 volatile agent Substances 0.000 abstract description 8
- 238000002360 preparation method Methods 0.000 abstract description 3
- 229920001384 propylene homopolymer Polymers 0.000 abstract description 2
- 239000004743 Polypropylene Substances 0.000 description 26
- CTQNGGLPUBDAKN-UHFFFAOYSA-N O-Xylene Chemical compound CC1=CC=CC=C1C CTQNGGLPUBDAKN-UHFFFAOYSA-N 0.000 description 8
- 239000008096 xylene Substances 0.000 description 8
- 239000000203 mixture Substances 0.000 description 7
- 239000006227 byproduct Substances 0.000 description 6
- 150000001451 organic peroxides Chemical class 0.000 description 6
- 239000002195 soluble material Substances 0.000 description 6
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 description 5
- 150000002978 peroxides Chemical class 0.000 description 5
- 229920000098 polyolefin Polymers 0.000 description 5
- VXNZUUAINFGPBY-UHFFFAOYSA-N 1-Butene Chemical compound CCC=C VXNZUUAINFGPBY-UHFFFAOYSA-N 0.000 description 4
- DKGAVHZHDRPRBM-UHFFFAOYSA-N Tert-Butanol Chemical compound CC(C)(C)O DKGAVHZHDRPRBM-UHFFFAOYSA-N 0.000 description 4
- 238000006243 chemical reaction Methods 0.000 description 4
- 239000007788 liquid Substances 0.000 description 4
- 239000002861 polymer material Substances 0.000 description 4
- 150000004756 silanes Chemical class 0.000 description 4
- 239000000654 additive Substances 0.000 description 3
- 238000000354 decomposition reaction Methods 0.000 description 3
- 150000002170 ethers Chemical class 0.000 description 3
- 229930195733 hydrocarbon Natural products 0.000 description 3
- 239000002667 nucleating agent Substances 0.000 description 3
- 239000012629 purifying agent Substances 0.000 description 3
- 239000002904 solvent Substances 0.000 description 3
- LIKMAJRDDDTEIG-UHFFFAOYSA-N 1-hexene Chemical compound CCCCC=C LIKMAJRDDDTEIG-UHFFFAOYSA-N 0.000 description 2
- KWKAKUADMBZCLK-UHFFFAOYSA-N 1-octene Chemical compound CCCCCCC=C KWKAKUADMBZCLK-UHFFFAOYSA-N 0.000 description 2
- AFABGHUZZDYHJO-UHFFFAOYSA-N 2-Methylpentane Chemical compound CCCC(C)C AFABGHUZZDYHJO-UHFFFAOYSA-N 0.000 description 2
- CSCPPACGZOOCGX-UHFFFAOYSA-N Acetone Chemical compound CC(C)=O CSCPPACGZOOCGX-UHFFFAOYSA-N 0.000 description 2
- 238000010521 absorption reaction Methods 0.000 description 2
- 230000009471 action Effects 0.000 description 2
- 230000015556 catabolic process Effects 0.000 description 2
- 230000003197 catalytic effect Effects 0.000 description 2
- 238000006731 degradation reaction Methods 0.000 description 2
- 238000009826 distribution Methods 0.000 description 2
- 238000004817 gas chromatography Methods 0.000 description 2
- 150000002430 hydrocarbons Chemical class 0.000 description 2
- 239000011159 matrix material Substances 0.000 description 2
- 238000005259 measurement Methods 0.000 description 2
- 230000006911 nucleation Effects 0.000 description 2
- 238000010899 nucleation Methods 0.000 description 2
- 238000005453 pelletization Methods 0.000 description 2
- YWAKXRMUMFPDSH-UHFFFAOYSA-N pentene Chemical compound CCCC=C YWAKXRMUMFPDSH-UHFFFAOYSA-N 0.000 description 2
- 125000005498 phthalate group Chemical class 0.000 description 2
- 239000000843 powder Substances 0.000 description 2
- 239000000047 product Substances 0.000 description 2
- 239000012429 reaction media Substances 0.000 description 2
- 239000011342 resin composition Substances 0.000 description 2
- 238000003756 stirring Methods 0.000 description 2
- 239000000126 substance Substances 0.000 description 2
- 231100000331 toxic Toxicity 0.000 description 2
- 230000002588 toxic effect Effects 0.000 description 2
- FMZUHGYZWYNSOA-VVBFYGJXSA-N (1r)-1-[(4r,4ar,8as)-2,6-diphenyl-4,4a,8,8a-tetrahydro-[1,3]dioxino[5,4-d][1,3]dioxin-4-yl]ethane-1,2-diol Chemical class C([C@@H]1OC(O[C@@H]([C@@H]1O1)[C@H](O)CO)C=2C=CC=CC=2)OC1C1=CC=CC=C1 FMZUHGYZWYNSOA-VVBFYGJXSA-N 0.000 description 1
- OUPPKRIDJAMCCA-UHFFFAOYSA-N 1-methoxy-2-(methoxymethyl)-2,3-dimethylbutane Chemical compound COCC(C)(C(C)C)COC OUPPKRIDJAMCCA-UHFFFAOYSA-N 0.000 description 1
- BHPDSAAGSUWVMP-UHFFFAOYSA-N 3,3-bis(methoxymethyl)-2,6-dimethylheptane Chemical compound COCC(C(C)C)(COC)CCC(C)C BHPDSAAGSUWVMP-UHFFFAOYSA-N 0.000 description 1
- PVWCLOAAEFMTLH-UHFFFAOYSA-N 4,4-bis(methoxymethyl)-2,6-dimethylheptane Chemical compound COCC(COC)(CC(C)C)CC(C)C PVWCLOAAEFMTLH-UHFFFAOYSA-N 0.000 description 1
- ZWINORFLMHROGF-UHFFFAOYSA-N 9,9-bis(methoxymethyl)fluorene Chemical compound C1=CC=C2C(COC)(COC)C3=CC=CC=C3C2=C1 ZWINORFLMHROGF-UHFFFAOYSA-N 0.000 description 1
- 239000004215 Carbon black (E152) Substances 0.000 description 1
- ZAMOUSCENKQFHK-UHFFFAOYSA-N Chlorine atom Chemical compound [Cl] ZAMOUSCENKQFHK-UHFFFAOYSA-N 0.000 description 1
- 229920000089 Cyclic olefin copolymer Polymers 0.000 description 1
- FYYHWMGAXLPEAU-UHFFFAOYSA-N Magnesium Chemical compound [Mg] FYYHWMGAXLPEAU-UHFFFAOYSA-N 0.000 description 1
- XMYDKOZNENQEHO-UHFFFAOYSA-N [1-methoxy-2-(methoxymethyl)-3-methylbutan-2-yl]cyclopentane Chemical compound COCC(COC)(C(C)C)C1CCCC1 XMYDKOZNENQEHO-UHFFFAOYSA-N 0.000 description 1
- 239000002253 acid Substances 0.000 description 1
- 150000001298 alcohols Chemical class 0.000 description 1
- 150000001412 amines Chemical class 0.000 description 1
- 238000004458 analytical method Methods 0.000 description 1
- 239000003963 antioxidant agent Substances 0.000 description 1
- 125000004429 atom Chemical group 0.000 description 1
- 150000001558 benzoic acid derivatives Chemical class 0.000 description 1
- 229910052801 chlorine Inorganic materials 0.000 description 1
- 239000000460 chlorine Substances 0.000 description 1
- 239000003086 colorant Substances 0.000 description 1
- 239000012967 coordination catalyst Substances 0.000 description 1
- 229920001577 copolymer Polymers 0.000 description 1
- 238000007334 copolymerization reaction Methods 0.000 description 1
- 125000001511 cyclopentyl group Chemical group [H]C1([H])C([H])([H])C([H])([H])C([H])(*)C1([H])[H] 0.000 description 1
- 239000007857 degradation product Substances 0.000 description 1
- 230000001627 detrimental effect Effects 0.000 description 1
- 239000003085 diluting agent Substances 0.000 description 1
- KZGGTNFGWNUXOC-UHFFFAOYSA-L disodium;bicyclo[2.2.1]heptane-3,4-dicarboxylate Chemical class [Na+].[Na+].C1CC2(C([O-])=O)C(C(=O)[O-])CC1C2 KZGGTNFGWNUXOC-UHFFFAOYSA-L 0.000 description 1
- 239000003814 drug Substances 0.000 description 1
- 229940079593 drug Drugs 0.000 description 1
- 238000005516 engineering process Methods 0.000 description 1
- 150000002148 esters Chemical class 0.000 description 1
- 239000007789 gas Substances 0.000 description 1
- 238000010438 heat treatment Methods 0.000 description 1
- 150000002391 heterocyclic compounds Chemical class 0.000 description 1
- 238000003780 insertion Methods 0.000 description 1
- 230000037431 insertion Effects 0.000 description 1
- 150000002576 ketones Chemical class 0.000 description 1
- 239000004611 light stabiliser Substances 0.000 description 1
- 239000000314 lubricant Substances 0.000 description 1
- 229910052751 metal Inorganic materials 0.000 description 1
- 239000002184 metal Chemical class 0.000 description 1
- 230000005012 migration Effects 0.000 description 1
- 238000013508 migration Methods 0.000 description 1
- 238000002156 mixing Methods 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- TVMXDCGIABBOFY-UHFFFAOYSA-N n-Octanol Natural products CCCCCCCC TVMXDCGIABBOFY-UHFFFAOYSA-N 0.000 description 1
- 125000004433 nitrogen atom Chemical group N* 0.000 description 1
- 229910052760 oxygen Inorganic materials 0.000 description 1
- 125000004430 oxygen atom Chemical group O* 0.000 description 1
- 239000008188 pellet Substances 0.000 description 1
- 125000001997 phenyl group Chemical group [H]C1=C([H])C([H])=C(*)C([H])=C1[H] 0.000 description 1
- XNGIFLGASWRNHJ-UHFFFAOYSA-L phthalate(2-) Chemical compound [O-]C(=O)C1=CC=CC=C1C([O-])=O XNGIFLGASWRNHJ-UHFFFAOYSA-L 0.000 description 1
- 239000004033 plastic Substances 0.000 description 1
- 229920003023 plastic Polymers 0.000 description 1
- 239000002685 polymerization catalyst Substances 0.000 description 1
- 229920005990 polystyrene resin Polymers 0.000 description 1
- 230000005855 radiation Effects 0.000 description 1
- 238000010992 reflux Methods 0.000 description 1
- 229920005989 resin Polymers 0.000 description 1
- 239000011347 resin Substances 0.000 description 1
- 150000003839 salts Chemical class 0.000 description 1
- 239000002002 slurry Substances 0.000 description 1
- 239000000243 solution Substances 0.000 description 1
- 238000010561 standard procedure Methods 0.000 description 1
- 239000000454 talc Chemical class 0.000 description 1
- 229910052623 talc Inorganic materials 0.000 description 1
- 230000008685 targeting Effects 0.000 description 1
- 125000000999 tert-butyl group Chemical group [H]C([H])([H])C(*)(C([H])([H])[H])C([H])([H])[H] 0.000 description 1
- 230000007704 transition Effects 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
- C08F10/04—Monomers containing three or four carbon atoms
- C08F10/06—Propene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F4/00—Polymerisation catalysts
- C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
- C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
- C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
- C08F4/62—Refractory metals or compounds thereof
- C08F4/64—Titanium, zirconium, hafnium or compounds thereof
- C08F4/642—Component covered by group C08F4/64 with an organo-aluminium compound
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F4/00—Polymerisation catalysts
- C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
- C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
- C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
- C08F4/62—Refractory metals or compounds thereof
- C08F4/64—Titanium, zirconium, hafnium or compounds thereof
- C08F4/647—Catalysts containing a specific non-metal or metal-free compound
- C08F4/649—Catalysts containing a specific non-metal or metal-free compound organic
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
- C08F210/04—Monomers containing three or four carbon atoms
- C08F210/06—Propene
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
- Transition And Organic Metals Composition Catalysts For Addition Polymerization (AREA)
- Wrappers (AREA)
- Injection Moulding Of Plastics Or The Like (AREA)
Applications Claiming Priority (5)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| EP06113011A EP1857475A1 (en) | 2006-04-24 | 2006-04-24 | Use of Ziegler-Natta catalyst to make a polypropylene homopolymer or random copolymer having a high melt flow rate |
| EP06113011.8 | 2006-04-24 | ||
| EP06122764.1 | 2006-10-23 | ||
| EP06122764A EP1916264A1 (en) | 2006-10-23 | 2006-10-23 | Process for the production of propylene polymers having a low ash content |
| PCT/EP2007/054005 WO2007122239A1 (en) | 2006-04-24 | 2007-04-24 | Use of a ziegler-natta catalyst to make a polypropylene homopolymer or random copolymer having a high melt flow rate |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| KR20090005025A KR20090005025A (ko) | 2009-01-12 |
| KR101085797B1 true KR101085797B1 (ko) | 2011-11-22 |
Family
ID=38441921
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| KR1020087025728A Active KR101085797B1 (ko) | 2006-04-24 | 2007-04-24 | 고 용융 유동 속도를 갖는 폴리프로필렌 동종중합체 또는 랜덤 공중합체를 제조하기 위한 지글러-나타 촉매의 용도 |
Country Status (8)
| Country | Link |
|---|---|
| US (1) | US7772338B2 (enExample) |
| EP (1) | EP2013249B1 (enExample) |
| JP (1) | JP5394231B2 (enExample) |
| KR (1) | KR101085797B1 (enExample) |
| DK (1) | DK2013249T3 (enExample) |
| ES (1) | ES2545773T3 (enExample) |
| PL (1) | PL2013249T3 (enExample) |
| WO (1) | WO2007122239A1 (enExample) |
Families Citing this family (39)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP2147939A1 (en) * | 2008-07-22 | 2010-01-27 | Borealis AG | Polypropylene composition with improved optics for film and moulding applications |
| EP2226337A1 (en) * | 2009-03-02 | 2010-09-08 | Borealis AG | Process for the production of polypropylene random copolymers for injection moulding applications |
| BRPI1014019B1 (pt) * | 2009-06-19 | 2019-10-22 | Basell Poliolefine Italia Srl | processo para a preparação de composições de polímeros de propileno resistentes ao impacto |
| ES2399330T3 (es) | 2010-10-06 | 2013-03-27 | Borealis Ag | Polipropileno con propiedades de bisagras flexible |
| EP2610274A1 (en) * | 2011-12-30 | 2013-07-03 | Borealis AG | Propylene random copolymer |
| BR112015006121B1 (pt) | 2012-09-19 | 2021-04-27 | Ineos Europe Ag | Composição de copolímero de propileno-etileno randomizado, artigo moldado por injeção compreendendo a referida composição e processo para produção da mesma |
| CN104736627B (zh) * | 2012-10-03 | 2018-04-17 | 胜亚诺盟股份有限公司 | 蒸煮膜用丙烯树脂组合物 |
| US9522968B2 (en) | 2012-11-26 | 2016-12-20 | Lummus Novolen Technology Gmbh | High performance Ziegler-Natta catalyst systems, process for producing such MgCl2 based catalysts and use thereof |
| US9481741B2 (en) | 2012-11-26 | 2016-11-01 | Lummus Novolen Technology Gmbh | High performance Ziegler-Natta catalyst systems, process for producing such supported catalysts and use thereof |
| BR112015028319B8 (pt) * | 2013-05-22 | 2021-07-06 | Borealis Ag | copolímero de propileno, artigo moldado por injeção, embalagem com pequena espessura e processo de produção do copolímero |
| BR112015030327B1 (pt) * | 2013-06-03 | 2020-12-01 | Lummus Novolen Technology Gmbh | sistema de catalisador útil para a polimerização de propileno ou copolímeros de propileno, processos para a produção de tais sistemas catalisadores, e polímero obtido |
| ES2651456T3 (es) | 2013-08-14 | 2018-01-26 | Borealis Ag | Composición de propileno con mejor resistencia al impacto a baja temperatura |
| EA031054B1 (ru) | 2013-08-21 | 2018-11-30 | Бореалис Аг | Композиция полиолефина с высокой текучестью, жесткостью и ударной вязкостью |
| CN105452363B (zh) | 2013-08-21 | 2018-06-12 | 博里利斯股份公司 | 具有高刚性和韧性的高流动聚烯烃组合物 |
| PL2853563T3 (pl) | 2013-09-27 | 2016-12-30 | Folie odpowiednie do przetwarzania BOPP z polimerów o wysokiej XS i wysokiej Tm | |
| ES2568615T3 (es) | 2013-10-11 | 2016-05-03 | Borealis Ag | Película para etiquetas orientada en la dirección de la máquina |
| CN105612188B (zh) | 2013-10-24 | 2018-09-28 | 北欧化工公司 | 具有高含量的区域错误和高分子量的低熔点pp均聚物 |
| ES2574428T3 (es) | 2013-10-24 | 2016-06-17 | Borealis Ag | Artículo moldeado por soplado basado en copolímero al azar bimodal |
| CN105722869B (zh) | 2013-10-29 | 2017-09-12 | 北欧化工公司 | 具有高聚合活性的固体单点催化剂 |
| US9217049B2 (en) | 2013-11-19 | 2015-12-22 | Chevron Phillips Chemical Company Lp | Dual catalyst systems for producing polymers with a broad molecular weight distribution and a uniform short chain branch distribution |
| US9303109B2 (en) | 2013-11-19 | 2016-04-05 | Chevron Phillips Chemical Company Lp | Catalyst systems containing boron-bridged cyclopentadienyl-fluorenyl metallocene compounds with an alkenyl substituent |
| US9540465B2 (en) | 2013-11-19 | 2017-01-10 | Chevron Phillips Chemical Company Lp | Boron-bridged metallocene catalyst systems and polymers produced therefrom |
| US9303110B2 (en) | 2013-11-19 | 2016-04-05 | Chevron Phillips Chemical Company Lp | Boron-bridged bis-indenyl metallocene catalyst systems and polymers produced therefrom |
| WO2015075088A1 (en) * | 2013-11-22 | 2015-05-28 | Borealis Ag | Low emission propylene homopolymer with high melt flow |
| EP3071607B1 (en) | 2013-11-22 | 2018-05-09 | Borealis AG | Low emission propylene homopolymer |
| EP3077426B1 (en) | 2013-12-04 | 2022-10-05 | Borealis AG | Phthalate-free pp homopolymers for meltblown fibers |
| JP6203405B2 (ja) | 2013-12-18 | 2017-09-27 | ボレアリス エージー | 剛性／靭性バランスが改良されたｂｏｐｐフィルム |
| CN105829364B (zh) | 2014-01-17 | 2017-11-10 | 博里利斯股份公司 | 用于制备丙烯/1‑丁烯共聚物的方法 |
| ES2827285T3 (es) | 2014-02-06 | 2021-05-20 | Borealis Ag | Copolímeros blandos con alta resistencia al impacto |
| PL3102634T3 (pl) | 2014-02-06 | 2020-11-16 | Borealis Ag | Miękkie i przezroczyste kopolimery odporne na uderzenia |
| EP2907841A1 (en) | 2014-02-14 | 2015-08-19 | Borealis AG | Polypropylene composite |
| EP2947118B1 (en) | 2014-05-20 | 2017-11-29 | Borealis AG | Polypropylene composition for automotive interior applications |
| KR101621001B1 (ko) | 2014-11-28 | 2016-05-13 | 롯데케미칼 주식회사 | 폴리올레핀 중합용 촉매 조성물, 고체 촉매의 제조방법, 및 이를 이용한 폴리올레핀의 제조방법 |
| CN108026680B (zh) * | 2015-10-02 | 2020-12-08 | 博里利斯股份公司 | 具有改进性能的熔喷网 |
| US10883197B2 (en) | 2016-01-12 | 2021-01-05 | Chevron Phillips Chemical Company Lp | High melt flow polypropylene homopolymers for fiber applications |
| CN110248968B (zh) | 2016-12-12 | 2022-05-27 | Sabic环球技术有限责任公司 | 制造低排放均聚物或无规聚丙烯的方法 |
| CA3102001A1 (en) * | 2018-06-11 | 2019-12-19 | W.R. Grace & Co.-Conn | Propylene-ethylene random copolymers with low xs/et ratio and high mfr |
| WO2019241063A1 (en) * | 2018-06-11 | 2019-12-19 | W.R. Grace & Co.-Conn. | Propylene-ethylene copolymer compositions suitable for hot fill packaging of foodstuffs |
| US20230143086A1 (en) * | 2021-11-05 | 2023-05-11 | Formosa Plastics Corporation, Usa | Catalyst components for the preparation of highly isotactactic polypropylene polymer with broad molecular weight distribution |
Family Cites Families (10)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP0309138A3 (en) | 1987-09-21 | 1991-08-07 | Exxon Chemical Patents Inc. | Random copolymer polypropylene container and method for producing the same |
| WO1997045463A1 (en) * | 1996-05-27 | 1997-12-04 | Mitsui Chemicals, Inc. | Crystalline polypropylene, process for preparing the same, polypropylene composition, and thermoformed article |
| US6403708B2 (en) * | 1996-05-27 | 2002-06-11 | Mitsui Chemicals Inc | Crystalline polypropylenes, process for preparing thereof, polypropylene compositions, and thermoformed products |
| JPH11349747A (ja) * | 1998-06-05 | 1999-12-21 | Mitsubishi Chemical Corp | プロピレン系樹脂組成物 |
| JP2002173504A (ja) | 2000-11-29 | 2002-06-21 | Basell Technology Co Bv | オレフィン重合用触媒およびオレフィン重合方法 |
| US6657025B2 (en) * | 2001-01-12 | 2003-12-02 | Fina Technology, Inc. | Production of ultra high melt flow polypropylene resins |
| US6476172B1 (en) | 2001-07-27 | 2002-11-05 | Fina Technology, Inc. | Metallocene catalyzed propylene-α-olefin random copolymer melt spun fibers |
| US7220696B2 (en) * | 2002-04-04 | 2007-05-22 | Mitsui Chemicals, Inc. | Solid titanium catalyst component for olefin polymerization, catalyst for olefin polymerization, and process for olefin polymerization |
| JP2004002742A (ja) * | 2002-04-04 | 2004-01-08 | Mitsui Chemicals Inc | オレフィン重合用固体状チタン触媒成分、オレフィン重合用触媒およびオレフィンの重合方法 |
| KR20060013486A (ko) * | 2003-02-24 | 2006-02-10 | 차이나 페트로리움 앤드 케미컬 코포레이션 | 프로필렌 중합용 촉매의 복합 담체, 촉매 성분 및 이를포함하는 촉매 |
-
2007
- 2007-04-24 PL PL07728461T patent/PL2013249T3/pl unknown
- 2007-04-24 DK DK07728461.0T patent/DK2013249T3/en active
- 2007-04-24 US US12/298,063 patent/US7772338B2/en active Active
- 2007-04-24 JP JP2009507065A patent/JP5394231B2/ja not_active Expired - Fee Related
- 2007-04-24 KR KR1020087025728A patent/KR101085797B1/ko active Active
- 2007-04-24 EP EP07728461.0A patent/EP2013249B1/en active Active
- 2007-04-24 WO PCT/EP2007/054005 patent/WO2007122239A1/en not_active Ceased
- 2007-04-24 ES ES07728461.0T patent/ES2545773T3/es active Active
Also Published As
| Publication number | Publication date |
|---|---|
| ES2545773T3 (es) | 2015-09-15 |
| DK2013249T3 (en) | 2015-09-07 |
| JP2009534512A (ja) | 2009-09-24 |
| KR20090005025A (ko) | 2009-01-12 |
| PL2013249T3 (pl) | 2015-11-30 |
| EP2013249B1 (en) | 2015-06-03 |
| EP2013249A1 (en) | 2009-01-14 |
| JP5394231B2 (ja) | 2014-01-22 |
| US20090264607A1 (en) | 2009-10-22 |
| US7772338B2 (en) | 2010-08-10 |
| WO2007122239A1 (en) | 2007-11-01 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| KR101085797B1 (ko) | 고 용융 유동 속도를 갖는 폴리프로필렌 동종중합체 또는 랜덤 공중합체를 제조하기 위한 지글러-나타 촉매의 용도 | |
| KR101414916B1 (ko) | 프로필렌의 (공)중합용 촉매 조성물 | |
| KR101414848B1 (ko) | 프로필렌의 공중합용 촉매 조성물 | |
| CN101432321B (zh) | 使用齐格勒-纳塔催化剂制造具有高熔体流动速率的聚丙烯均聚物或无规共聚物 | |
| KR101260153B1 (ko) | 사출 성형 용도를 위한 개선된 특성을 갖는 헤테로상 프로필렌 공중합체 | |
| JP4480116B2 (ja) | 剛性と衝撃強さの調和がとれたポリオレフィン組成物 | |
| KR101224792B1 (ko) | 개선된 크리프 거동을 가진 헤테로상 프로필렌 공중합체 | |
| KR101222344B1 (ko) | 골판형 시트 및 캐스트 필름 적용물을 위한 헤테로상 프로필렌 공중합체 | |
| KR20100074339A (ko) | 넓은 분자량 분포 및 낮은 회분 함량을 가진 프로필렌 중합체의 제조 방법 | |
| KR20100074338A (ko) | 회분 함량이 적은 바이모달 폴리프로필렌의 제조 방법 | |
| KR101167875B1 (ko) | 강성과 충격 강도의 균형이 우수한 폴리올레핀 조성물 | |
| MX2012014289A (es) | Copolimeros de impacto de propileno de alto impacto, de alta rigidez. | |
| CN103492432B (zh) | 具有高热变形温度、高刚性和流动性的聚丙烯均聚物 | |
| KR20240013822A (ko) | 고 유동성 폴리프로필렌 수지 조성물 및 그로부터 제조된 성형품 | |
| EP1857476A1 (en) | Catalyst composition for the (co)polymerization of propylene | |
| TWI296002B (en) | Soft polyolefin compositions | |
| CZ20002844A3 (cs) | Polyolefinový materiál | |
| CN106459530A (zh) | 乙烯聚合物组合物及其在聚烯烃组合物中的用途 |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| PA0105 | International application |
Patent event date: 20081021 Patent event code: PA01051R01D Comment text: International Patent Application |
|
| A201 | Request for examination | ||
| PA0201 | Request for examination |
Patent event code: PA02012R01D Patent event date: 20081223 Comment text: Request for Examination of Application |
|
| PG1501 | Laying open of application | ||
| E902 | Notification of reason for refusal | ||
| PE0902 | Notice of grounds for rejection |
Comment text: Notification of reason for refusal Patent event date: 20101223 Patent event code: PE09021S01D |
|
| E701 | Decision to grant or registration of patent right | ||
| PE0701 | Decision of registration |
Patent event code: PE07011S01D Comment text: Decision to Grant Registration Patent event date: 20110818 |
|
| GRNT | Written decision to grant | ||
| PR0701 | Registration of establishment |
Comment text: Registration of Establishment Patent event date: 20111116 Patent event code: PR07011E01D |
|
| PR1002 | Payment of registration fee |
Payment date: 20111116 End annual number: 3 Start annual number: 1 |
|
| PG1601 | Publication of registration | ||
| FPAY | Annual fee payment |
Payment date: 20141112 Year of fee payment: 4 |
|
| PR1001 | Payment of annual fee |
Payment date: 20141112 Start annual number: 4 End annual number: 4 |
|
| FPAY | Annual fee payment |
Payment date: 20151106 Year of fee payment: 5 |
|
| PR1001 | Payment of annual fee |
Payment date: 20151106 Start annual number: 5 End annual number: 5 |
|
| FPAY | Annual fee payment |
Payment date: 20161104 Year of fee payment: 6 |
|
| PR1001 | Payment of annual fee |
Payment date: 20161104 Start annual number: 6 End annual number: 6 |
|
| FPAY | Annual fee payment |
Payment date: 20171103 Year of fee payment: 7 |
|
| PR1001 | Payment of annual fee |
Payment date: 20171103 Start annual number: 7 End annual number: 7 |
|
| FPAY | Annual fee payment |
Payment date: 20181113 Year of fee payment: 8 |
|
| PR1001 | Payment of annual fee |
Payment date: 20181113 Start annual number: 8 End annual number: 8 |
|
| PR1001 | Payment of annual fee |
Payment date: 20221104 Start annual number: 12 End annual number: 12 |