ES2545773T3 - Uso de un catalizador Ziegler-Natta para producir un copolímero aleatorio de polipropileno con elevada velocidad de flujo del fundido - Google Patents

Uso de un catalizador Ziegler-Natta para producir un copolímero aleatorio de polipropileno con elevada velocidad de flujo del fundido Download PDF

Info

Publication number
ES2545773T3
ES2545773T3 ES07728461.0T ES07728461T ES2545773T3 ES 2545773 T3 ES2545773 T3 ES 2545773T3 ES 07728461 T ES07728461 T ES 07728461T ES 2545773 T3 ES2545773 T3 ES 2545773T3
Authority
ES
Spain
Prior art keywords
propylene
melt flow
ziegler
weight
flow rate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
ES07728461.0T
Other languages
English (en)
Inventor
Valérie Terreur
Jérôme GROMADA
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TotalEnergies One Tech Belgium SA
Original Assignee
Total Research and Technology Feluy SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=38441921&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=ES2545773(T3) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Priority claimed from EP06113011A external-priority patent/EP1857475A1/en
Priority claimed from EP06122764A external-priority patent/EP1916264A1/en
Application filed by Total Research and Technology Feluy SA filed Critical Total Research and Technology Feluy SA
Application granted granted Critical
Publication of ES2545773T3 publication Critical patent/ES2545773T3/es
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Procedimiento de producción de polímeros de propileno que tienen una velocidad de flujo del fundido que varía de 45 a 150 dg/min (ASTM D 1238 condición L) directamente en un reactor de polimerización sin el uso posterior de agentes de aumento de flujo del fundido, comprendiendo dicho procedimiento la etapa de polimerizar propileno y uno o más comonómeros en presencia de - un catalizador Ziegler-Natta que comprende un compuesto de titanio que tiene al menos un enlace titaniohalógeno y un compuesto de diéter como donante interno de electrones, ambos sobre un soporte de un haluro de magnesio en forma activa, - un compuesto de organoaluminio en una cantidad tal que la concentración de aluminio, en peso, respecto al(a los) monómero(s) añadido(s) en el medio de polimerización varía de 1 a 75 ppm, - un donante externo de electrones, e - hidrógeno, en el que la relación molar de compuesto de organoaluminio a donante externo de electrones varía de 1 a 20, en el que el polímero de propileno es un copolímero aleatorio de propileno y uno o más co-monómeros de alfa-olefina y además en el que el polímero de propileno comprende entre un 2% en peso y un 6 % en peso de comonómero.

Description

imagen1
imagen2
imagen3
imagen4
imagen5
E07728461
20-08-2015
(continuación)
Unidad
Ej. 1 (comp) Ej. 2 (comp) Ej. 3 Ej. 4
MFI
dg/min 32 39 90 80
Distribución de peso molecular
5,9 5,6 5,3 5,6
Etileno
% en peso 3,5 3,3 2,1 3,5
Solubles en xileno
% en peso 8,3 6,5 5,4 6,0
Módulo flexural
MPa 1127 1107 1224 1110
IZOD + 23 ºC (en probeta entallada)
kJ/m2 4,7 4,4 2,7 3,7
Agente de purificación
- si si no si
Los resultados muestran claramente que se puede alcanzar una reactividad catalítica elevada con donante externo con bajo contenido en solubles.
5 Volátiles
Se determina el contenido en volátiles en el polímero como se muestra a continuación. Se calientan las muestras poliméricas en un horno hasta 150 ºC. Se purgan los volátiles orgánicos del horno a través de un tubo absorbedor de Tenax a -30 ºC. Posteriormente, se inyectan los volátiles orgánicos en un cromatógrafo por medio de recalentamiento del cartucho de absorbedor hasta 240 ºC. Se llevó a cabo el análisis de los volátiles en un
10 cromatógrafo de gases en las respectivas condiciones convencionales.
Se analizó el contenido en volátiles orgánicos del polipropileno del ejemplo 4 y se comparó con un copolímero aleatorio de la técnica anterior de flujo del fundido 40 dg/min, designado como ejemplo 5, que se produjo por medio de reducción de viscosidad con un peróxido orgánico, y también un copolímero aleatorio de flujo del fundido 40 producido de acuerdo con la presente invención, es decir, sin reducción de viscosidad, designado como ejemplo 6.
15 La tabla II muestra los resultados.
Tabla II
Unidad
Ej. 5 (comp.) Ej. 6 (comp.) Ej. 4
MFI
dg/min 40 40 80
Etileno
% en peso 3 3,5 3,5
C3-C4 total
ppm 11 n.d. n.d.
Acetona
ppm 38 n.d. n.d.
n-pentano
ppm 2 n.d. n.d.
Terc-butanol
ppm 29 n.d. n.d.
C6 total
ppm 21 2 1
n.d. = no detectado, es decir, por debajo del límite de detección de 0,5 ppm.
Los resultados muestran que un polipropileno producido de acuerdo con la presente invención tiene un contenido en volátiles muy reducido.
7

Claims (1)

  1. imagen1
    imagen2
ES07728461.0T 2006-04-24 2007-04-24 Uso de un catalizador Ziegler-Natta para producir un copolímero aleatorio de polipropileno con elevada velocidad de flujo del fundido Active ES2545773T3 (es)