JPWO2019142936A1 - 紫外線透過ガラスおよび成形品 - Google Patents
紫外線透過ガラスおよび成形品 Download PDFInfo
- Publication number
- JPWO2019142936A1 JPWO2019142936A1 JP2019566541A JP2019566541A JPWO2019142936A1 JP WO2019142936 A1 JPWO2019142936 A1 JP WO2019142936A1 JP 2019566541 A JP2019566541 A JP 2019566541A JP 2019566541 A JP2019566541 A JP 2019566541A JP WO2019142936 A1 JPWO2019142936 A1 JP WO2019142936A1
- Authority
- JP
- Japan
- Prior art keywords
- glass
- ultraviolet
- less
- ultraviolet transmissive
- transmissive glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
τ350−400 ≧ 90 …(1)を満たすことを特徴とする。
τ300−350 ≧ 75 …(2)を満たすことを特徴とする。
τ260−300 ≧ 45 …(3)を満たすことを特徴とする。
本実施形態の紫外線透過ガラスは酸化物からなるガラス材料であって、紫外域の波長の光の透過率が良好なものである。
τ350−400 ≧ 90 …(1)を満たすものが挙げられる。
τ300−350 ≧ 75 …(2)を満たすものが挙げられる。
τ260−300 ≧ 45 …(3)を満たすものが挙げられる。
τ = exp[−dx×(lnT1−lnT2)/Δd] (a)
τ(10mm)=exp[−10×(lnT1−lnT2)/Δd](b)
本ガラス組成1は、酸化物基準のモル%表示で、B2O3:10〜80%、SiO2:0〜25%、La2O3:2〜32%、Y2O3:0〜20%を含有する組成である。
本ガラス組成2は、酸化物基準のモル%表示で、B2O3+SiO2+P2O5:40〜90%、Li2O+Na2O+K2O:0〜30%、MgO+CaO+SrO+BaO:0〜20%を含有する組成である。
本ガラス組成2において、ZnOはガラスの溶融性を改善するとともに、ガラス転移温度や軟化温度を下げることができる成分である。ZnO含有量は10%以下、好ましくは5%以下である。
本実施形態の紫外線透過ガラスの製造方法は、上記実施形態の紫外線透過ガラスを製造する方法である。この紫外線透過ガラスの製造方法は、基本的な操作は、従来公知のガラスの製造方法に基づくものであり、ガラス原料またはガラスカレットを溶融し、これにより得られたガラス溶融液を冷却して固化させるものである。その際、本実施形態においては、ガラス中の鉄含有量を低減するとともに、得られるガラス中に含まれる成分の酸化還元状態を制御して、良好な紫外線透過特性を得られるようにすることが好ましい。
本実施形態の成形品は、上記本実施形態の紫外線透過ガラス製であり、所望の形状に成形されてなる成形体である。ここで本実施形態の成形品は、その用途に応じて任意の形状に形成可能であり、成形品の製造は公知の方法により行えばよく、例えば、上記紫外線透過ガラスの製造方法において説明したような方法を用いればよい。また、リヒートプレスやリドロー加工といった熱間加工を後加工として施す場合もある。
表1に示す組成のガラスが得られるように各々相当する硝酸塩、硫酸塩、水酸化物、酸化物、ホウ酸などの原料を秤量し、十分混合した後、白金製坩堝に投入し、大気中1300℃で3時間加熱、溶解した。ガラス原料は、鉄やチタンといった不純物含有量が低いものを選んで使用した。
還元剤としてSnO2を添加して、表1に示す組成となるようにガラス原料を秤量した。例1−1と同様な溶解方法および成形方法により、鉄含有量が1.5質量ppm以下、Fe3+強度が0.0215以下のガラス2を得た。
還元剤としてSnO2を添加して、表1に示す組成となるようにガラス原料を秤量した。白金製坩堝に原料を投入し、窒素ガスで炉内を満たした溶解炉で1300℃にて3時間加熱、溶解した。その後、例1−1と同様の成形方法でガラス成形品を作成し、鉄含有量が1.5質量ppm以下、Fe3+強度が0.0215以下のガラス3を得た。
還元剤としてSnOを添加して、表1に示す組成となるようにガラス原料を秤量した。白金製坩堝に原料を投入し、窒素ガスで炉内を満たした溶解炉で1300℃にて3時間加熱、溶解した。その後、例1−1と同様の成形方法でガラス成形品を作成し、鉄含有量が1.5質量ppm以下、Fe3+強度が0.0215以下のガラス4を得た。
表1に示す組成となるようにガラス原料を秤量した。白金製坩堝に原料を投入し、還元剤として炭素粉を原料に外割0.4質量%分を添加し、窒素ガスで炉内を満たした溶解炉で1300℃にて3時間加熱、溶解した。その後、例1−1と同様の成形方法でガラス成形品を作成し、鉄含有量が1.5質量ppm以下、Fe3+強度が0.0215以下のガラス5を得た。なお、添加した炭素はガラス溶融時においてCO2となって揮散するため、ガラス成形品には残留していなかった。
還元剤としてSnO2を添加して、表1に示す組成となるようにガラス原料を秤量した。白金製坩堝に原料を投入し、窒素ガスで炉内を満たした溶解炉で1300℃にて3時間加熱、溶解した。その後、例1−1と同様の成形方法でガラス成形品を作成し、鉄含有量が1.5質量ppm以下、Fe3+強度が0.0215以下のガラス6を得た。
表1に示す組成となるようにガラス原料を秤量した。ガラス原料には、鉄含有量が多いものを用いた。例1−1と同様な溶解方法および成形方法により、ガラス7を得た。鉄含有量が多いガラス原料を用いることでガラスの鉄含有量が1.5質量ppm超となり、還元剤を添加しなかったためにFe3+強度が0.0215超となった。
得られたガラスについて、波長587.56nm(d線)における屈折率nd、外部透過率、着色度、内部透過率、T−Fe2O3、Fe3+強度を測定した。これらの測定方法を以下に述べる。
屈折率は、一辺5mm以上、厚み5mm以上の直方体形状に加工したサンプルを、精密屈折率計(島津製作所製、型式:KPR−200、KPR−2000)を用いて測定した。屈折率は、降温速度−60℃/hで徐冷して得られたサンプルについて測定した。
外部透過率は、厚さ1mmと10mmそれぞれのサンプルを、両面を研磨し、分光光度計(日立ハイテクノロジーズ社製、型式:U−4100)を用いて測定した。10mm厚での外部透過率から着色度を読み取り、外部透過率が70%になる波長λ70、外部透過率が5%になる波長λ5として表1に示す。また、波長260nmでの1mm厚の外部透過率をT260として表1に示す。
内部透過率は、厚さ1mmと10mmのサンプルについて外部透過率を測定し、既述した式(a)、式(b)によって厚さ10mmでの内部透過率τを求めた。波長350〜400nmの光に対する内部透過率τ350−400、波長300〜350nmの光に対する内部透過率τ300−350、波長260〜300nmの光に対する内部透過率τ260−300、をそれぞれ求め、表1には各波長範囲における最小値を示した。
全酸化鉄含有量(T−Fe2O3)はICP質量分析法によって以下の手順で測定した。粉砕したガラスにフッ化水素酸と硫酸の混酸を添加し加熱して分解した。分解後、塩酸を添加して一定量にし、ICP質量分析法でFeの濃度を測定した。濃度は標準液を用いて作製された検量線により計算される。この測定濃度とガラスの分解量より、ガラス中のT−Fe2O3を算出した。ICP質量分析計は、アジレント・テクノロジー社製Agilent8800を用いた。
Fe3+強度は、電子スピン共鳴法(ESR)によって以下の手順で測定した。粉砕したガラス0.3g秤量し、内標準としてICP用硝酸銅標準溶液を、Cu2+が30μg加わるように添加した。試料を約50℃で2時間ほど乾燥後、ESR用測定管に試料を充てんし、電子スピン共鳴スペクトルを測定した。装置は日本電子株式会社製ESR SPECTROMETERを使用した。ESRの測定条件を表2に示す。
Fe3+信号強度=(磁場157mT前後に出現するFe3+ピークの信号強度の極大値)−(磁場157mT前後に出現するFe3+ピークの信号強度の極小値)
Cu2+信号強度=(磁場310mT前後に出現するCu2+ピークの信号強度の極大値)−(磁場310mT前後に出現するCu2+ピークの信号強度の極小値)
Fe3+強度=(Fe3+信号強度/Fe3+信号強度測定時のアンプ倍率)/(Cu2+信号強度/Cu2+信号強度測定時のアンプ倍率)
SiO2が2.66モル%、B2O3が35.27モル%、La2O3が47.81モル%、Y2O3が14.25モル%の組成のガラスカレットを白金製坩堝に投入し、大気中1300℃で3時間加熱、溶解した。
SiO2が2.66モル%、B2O3が35.27モル%、La2O3が47.81モル%、Y2O3が14.25モル%の組成のガラスカレットを白金製坩堝に投入し、窒素ガスで満たした溶解炉で1300℃にて3時間加熱、溶解した。
厚さ10mm、両面を研磨したサンプルを、分光光度計(日立ハイテクノロジーズ社製、型式:U−4100)を用いて測定した。測定は、波長270nmの光に対する外部透過率を求め、図1、図2にプロットした結果を示す。
Claims (16)
- 多成分系酸化物からなり、
波長350nm〜400nmの光に対する10mm厚の内部透過率τ350−400(%)が、次の式(1)
τ350−400 ≧ 90 …(1)を満たすことを特徴とする紫外線透過ガラス。 - 多成分系酸化物からなり、
波長300nm〜350nmの光に対する10mm厚の内部透過率τ300−350(%)が、次の式(2)
τ300−350 ≧ 75 …(2)を満たすことを特徴とする紫外線透過ガラス。 - 多成分系酸化物からなり、
波長260nm〜300nmの光に対する10mm厚の内部透過率τ260−300(%)が、次の式(3)
τ260−300 ≧ 45 …(3)を満たすことを特徴とする紫外線透過ガラス。 - 前記紫外線透過ガラスは、Fe2O3に換算したガラス中の酸化鉄含有量T−Fe2O3が1.5質量ppm以下である請求項1〜3のいずれか1項に記載の紫外線透過ガラス。
- 前記紫外線透過ガラスは、SnO2およびSnOから選ばれる酸化スズを少なくとも1つ含んでおり、前記紫外線ガラス中における前記酸化スズの含有量が0.3質量%超3質量%以下である請求項1〜4のいずれか1項に記載の紫外線透過ガラス。
- 前記紫外線透過ガラスは、SnO2およびSnOから選ばれる酸化スズを少なくとも1つ含んでおり、前記紫外線ガラス中における前記酸化スズの含有量が0質量%超0.3質量%以下である請求項1〜4のいずれか1項に記載の紫外線透過ガラス。
- 前記紫外線透過ガラスの屈折率ndが、1.7以上である請求項1〜6のいずれか1項に記載の紫外線透過ガラス。
- 前記紫外線透過ガラスは、酸化物基準のモル%表示で、Bi2O3、TiO2、WO3およびGd2O3の含有量が3モル%以下である、請求項1〜7のいずれか1項に記載の紫外線透過ガラス。
- 前記紫外線透過ガラスは、酸化物基準のモル%表示で、Nb2O5の含有量が3モル%以下である、請求項8に記載の紫外線透過ガラス。
- 前記紫外線透過ガラスは、酸化物基準のモル%表示で、Ta2O5の含有量が3モル%以下である、請求項8または請求項9に記載の紫外線透過ガラス。
- 前記紫外線透過ガラスは、電子スピン共鳴法(ESR)で測定されるFe3+強度が0.0215以下である、請求項1〜10のいずれか1項に記載の紫外線透過ガラス。
- ガラス原料またはガラスカレットを溶融し、該ガラス溶融液を冷却させて固化する、請求項1〜4のいずれか1項に記載の紫外線透過ガラスの製造方法であって、
前記溶融にあたって、溶融雰囲気を大気雰囲気とし、前記ガラス原料または前記ガラスカレットに還元剤を含有させることを特徴とする紫外線透過ガラスの製造方法。 - 前記還元剤が、SnO2およびSnOから選ばれる少なくとも1つを含む酸化スズであって、該還元剤が前記紫外線透過ガラス中に0.3質量%超、3質量%以下含まれることを特徴とする請求項12に記載の紫外線透過ガラスの製造方法。
- ガラス原料またはガラスカレットを溶融し、該ガラス溶融液を冷却して固化させる、請求項1〜4のいずれか1項に記載の紫外線透過ガラスの製造方法であって、
前記溶融にあたって、溶融雰囲気を非酸化性雰囲気とし、前記ガラス原料または前記ガラスカレットに還元剤を含有させることを特徴とする紫外線透過ガラスの製造方法。 - 前記還元剤がSnO2およびSnOから選ばれる少なくとも1つを含む酸化スズであって、該還元剤が前記紫外線透過ガラス中に0質量%超、0.3質量%以下含まれることを特徴とする請求項14に記載の紫外線透過ガラスの製造方法。
- 請求項1〜11のいずれか1項に記載の紫外線透過ガラスからなり、所望の形状を有することを特徴とする成形品。