JPWO2019044138A1 - 感光性転写材料及びその製造方法、並びに、回路配線の製造方法 - Google Patents
感光性転写材料及びその製造方法、並びに、回路配線の製造方法 Download PDFInfo
- Publication number
- JPWO2019044138A1 JPWO2019044138A1 JP2019539008A JP2019539008A JPWO2019044138A1 JP WO2019044138 A1 JPWO2019044138 A1 JP WO2019044138A1 JP 2019539008 A JP2019539008 A JP 2019539008A JP 2019539008 A JP2019539008 A JP 2019539008A JP WO2019044138 A1 JPWO2019044138 A1 JP WO2019044138A1
- Authority
- JP
- Japan
- Prior art keywords
- polymer
- mass
- resin composition
- ultraviolet absorbing
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
一般的にパターン化した層の形成には、必要とするパターン形状を得るための工程数が少ないといったことから、感光性転写材料を用いて任意の基板上に設けた感光性樹脂組成物の層に対して、所望のパターンを有するマスクを介して露光した後に現像する方法が広く使用されている。
本発明の他の一実施形態が解決しようとする課題は、転写性及び得られるパターンの直線性に優れる感光性転写材料の製造方法を提供することである。
また、本発明の更に他の一実施形態が解決しようとする課題は、上記感光性転写材料を用いた回路配線の製造方法を提供することである。
<1> 仮支持体上に、感光性樹脂組成物層、及び、紫外線吸収層を有し、上記感光性樹脂組成物層が、酸分解性基で保護された酸基を有する構成単位を有する重合体A1と、光酸発生剤とを含み、上記紫外線吸収層が、有機紫外線吸収剤と重合体A2とを含むか、又は、紫外線吸収能を有する重合体A3を含み、上記紫外線吸収層に含まれる、上記重合体A2のガラス転移温度又は上記重合体A3のガラス転移温度が、90℃以下であるポジ型感光性転写材料。
<2> 上記重合体A1のガラス転移温度が、上記重合体A2のガラス転移温度又は上記重合体A3のガラス転移温度よりも高い上記<1>に記載のポジ型感光性転写材料。
<3> 上記重合体A1のガラス転移温度が、上記重合体A2のガラス転移温度又は上記重合体A3のガラス転移温度よりも10℃以上50℃以下高い温度である上記<1>又は<2>に記載のポジ型感光性転写材料。
<4> 上記重合体A1のガラス転移温度が、120℃以下である上記<1>〜<3>のいずれか1つに記載のポジ型感光性転写材料。
<5> 上記重合体A2のガラス転移温度又は上記重合体A3のガラス転移温度が、−20℃以上60℃以下である上記<1>〜<4>のいずれか1つに記載のポジ型感光性転写材料。
<6> 上記紫外線吸収層が、紫外線吸収能を有する重合体A3を含む上記<1>〜<5>のいずれか1つに記載のポジ型感光性転写材料。
<7> 感光性樹脂組成物層上に、水性塗布液を用いて塗布及び乾燥して紫外線吸収層を形成する工程を含む上記<1>〜<6>のいずれか1つに記載のポジ型感光性転写材料の製造方法。
<8> 上記水性塗布液が、アルカリ性である上記<7>に記載のポジ型感光性転写材料の製造方法。
<9> 仮支持体S1上に形成された感光性樹脂組成物層と、仮支持体S2上に形成された紫外線吸収層とを貼り合わせる工程を含む上記<1>〜<6>のいずれか1つに記載のポジ型感光性転写材料の製造方法。
<10> 基板に対し、上記<1>〜<6>のいずれか1つに記載のポジ型感光性転写材料の上記紫外線吸収層を上記基板に接触させて貼り合わせる工程と、上記貼り合わせる工程後の上記感光性転写材料の上記感光性樹脂組成物層をパターン露光する工程と、上記露光する工程後の露光部を現像してパターンを形成する工程と、上記パターンが配置されていない領域における上記基板をエッチング処理する工程と、をこの順に含む回路配線の製造方法。
本発明の他の一実施形態によれば、転写性及び得られるパターンの直線性に優れる感光性転写材料の製造方法を提供することができる。
また、本発明の更に他の一実施形態によれば、上記感光性転写材料を用いた回路配線の製造方法を提供することができる。
また、本明細書において「〜」を用いて表される数値範囲は、「〜」の前後に記載される数値を下限値及び上限値として含む範囲を意味する。
また、本明細書において、「(メタ)アクリル」はアクリル及びメタクリルの双方、又は、いずれかを表し、「(メタ)アクリレート」はアクリレート及びメタクリレートの双方、又は、いずれかを表す。
更に、本明細書において組成物中の各成分の量は、組成物中に各成分に該当する物質が複数存在する場合、特に断らない限り、組成物中に存在する該当する複数の物質の合計量を意味する。
本明細書において「工程」との語は、独立した工程だけでなく、他の工程と明確に区別できない場合であっても工程の所期の目的が達成されれば、本用語に含まれる。
本明細書において「全固形分」とは、組成物の全組成から溶剤を除いた成分の総質量をいう。また、「固形分」とは、上述のように、溶剤を除いた成分であり、例えば、25℃において固体であっても、液体であってもよい。
本明細書における基(原子団)の表記において、置換及び無置換を記していない表記は、置換基を有さないものと共に置換基を有するものをも包含するものである。例えば「アルキル基」とは、置換基を有さないアルキル基(無置換アルキル基)のみならず、置換基を有するアルキル基(置換アルキル基)をも包含するものである。
また、本明細書における化学構造式は、水素原子を省略した簡略構造式で記載する場合もある。
本開示において、「質量%」と「重量%」とは同義であり、「質量部」と「重量部」とは同義である。
また、本開示において、2以上の好ましい態様の組み合わせは、より好ましい態様である。
また、本開示における重量平均分子量(Mw)及び数平均分子量(Mn)は、特に断りのない限り、TSKgel GMHxL、TSKgel G4000HxL、TSKgel G2000HxL(何れも東ソー(株)製の商品名)のカラムを使用したゲルパーミエーションクロマトグラフィ(GPC)分析装置により、溶媒THF(テトラヒドロフラン)、示差屈折計により検出し、標準物質としてポリスチレンを用いて換算した分子量である。
本開示に係るポジ型感光性転写材料(以下、単に「感光性転写材料」ともいう。)は、仮支持体上に、感光性樹脂組成物層、及び、紫外線吸収層を有し、上記感光性樹脂組成物層が、酸分解性基で保護された酸基を有する構成単位を有する重合体A1と、光酸発生剤とを含み、上記紫外線吸収層が、有機紫外線吸収剤と重合体A2とを含むか、又は、紫外線吸収能を有する重合体A3を含み、上記紫外線吸収層に含まれる、上記重合体A2のガラス転移温度又は上記重合体A3のガラス転移温度が、90℃以下である。
また、本開示に係るポジ型感光性転写材料は、仮支持体上に、感光性樹脂組成物層、及び、紫外線吸収層をこの順で有することが好ましい。
また、単に感光性転写材料に反射防止層を設けただけでは、転写性が不十分となる場合があることを本発明者らは見出した。
本発明者らは鋭意検討を重ねた結果、上記構成のポジ型感光性転写材料とすることにより、上記紫外線吸収層を有するため、得られるパターンの直線性に優れるとともに、上記紫外線吸収層が、有機紫外線吸収剤と重合体A2とを含むか、又は、紫外線吸収能を有する重合体A3を含み、上記紫外線吸収層に含まれる、上記重合体A2のガラス転移温度又は上記重合体A3のガラス転移温度を90℃以下とすることにより、転写性にも優れると本発明者らは推定している。
感光性樹脂組成物層12は、酸分解性基で保護された酸基を有する構成単位を有する重合体と、光酸発生剤とを含有する。
紫外線吸収層14は、有機紫外線吸収剤と重合体A2とを含むか、又は、紫外線吸収能を有する重合体A3を含み、上記紫外線吸収層に含まれる、上記重合体A2のガラス転移温度又は上記重合体A3のガラス転移温度が、90℃以下である。
以下、本開示に係る感光性転写材料の構成材料等について説明する。なお、本開示における上記構成について本明細書では以下のように称する場合がある。
酸分解性基で保護された酸基を有する構成単位を有する重合体を「重合体A1」と称する場合がある。
上記感光性樹脂組成物層は、ポジ型の感光性樹脂組成物層であり、「ポジ型感光性樹脂組成物層」と称する場合がある。
仮支持体は、感光性樹脂組成物層及び紫外線吸収層を支持し、感光性樹脂組成物層又は紫外線吸収層から剥離可能な支持体である。
本開示に用いられる仮支持体は、感光性樹脂組成物層をパターン露光する際に仮支持体を介して感光性樹脂組成物層を露光し得る観点から光透過性を有することが好ましい。
光透過性を有するとは、パターン露光に使用する光の主波長の透過率が50%以上であることを意味し、パターン露光に使用する光の主波長の透過率は、露光感度向上の観点から、60%以上が好ましく、70%以上がより好ましい。透過率の測定方法としては、大塚電子(株)製MCPD Seriesを用いて測定する方法が挙げられる。
仮支持体としては、ガラス基板、樹脂フィルム、紙等が挙げられ、強度及び可撓性等の観点から、樹脂フィルムが特に好ましい。樹脂フィルムとしては、ポリエチレンテレフタレートフィルム、トリ酢酸セルロースフィルム、ポリスチレンフィルム、ポリカーボネートフィルム等が挙げられる。中でも、2軸延伸ポリエチレンテレフタレートフィルムが特に好ましい。
仮支持体の厚みは、支持体としての強度、回路配線形成用基板との貼り合わせに求められる可撓性、最初の露光工程で要求される光透過性などの観点から、材質に応じて選択すればよい。
本開示に係る感光性転写材料は、仮支持体上に、感光性樹脂組成物層、及び、紫外線吸収層を有し、上記感光性樹脂組成物層が、酸分解性基で保護された酸基を有する構成単位を有する重合体A1と、光酸発生剤とを含む。
また、本開示における感光性樹脂組成物層は、ポジ型感光性樹脂組成物層であり、化学増幅ポジ型感光性樹脂組成物層であることが好ましい。
後述するオニウム塩やオキシムスルホネート化合物等の光酸発生剤は、活性放射線(活性光線)に感応して生成される酸が、上記重合体A1中の保護された酸基の脱保護に対して触媒として作用するので、1個の光量子の作用で生成した酸が、多数の脱保護反応に寄与し、量子収率は1を超え、例えば、10の数乗のような大きい値となり、いわゆる化学増幅の結果として、高感度が得られる。
一方、活性放射線に感応する光酸発生剤としてキノンジアジド化合物を用いた場合、逐次型光化学反応によりカルボキシ基を生成するが、その量子収率は必ず1以下であり、化学増幅型には該当しない。
上記感光性樹脂組成物層は、酸分解性で保護された酸基を有する構成単位(「構成単位A」ともいう。)を有する重合体A1(単に「重合体A1」ともいう。)を含む。
また、上記感光性樹脂組成物層は、構成単位Aを有する重合体A1に加え、他の重合体を含んでいてもよい。本開示においては、構成単位Aを有する重合体A1及び他の重合体をあわせて、「重合体成分」ともいう。
上記重合体A1は、露光により生じる触媒量の酸性物質の作用により、重合体A1中の酸分解性で保護された酸基を有する構成単位Aが脱保護反応を受け酸基となる。この酸基により、硬化反応が可能となる。
以下に構成単位Aの好ましい態様について説明する。
また、上記重合体成分に含まれる全ての重合体がそれぞれ、後述する酸基を有する構成単位を少なくとも有する重合体であることが好ましい。
また、上記感光性樹脂組成物は、更に、これら以外の重合体を含んでいてもよい。本開示における上記重合体成分は、特に述べない限り、必要に応じて添加される他の重合体を含めたものを意味するものとする。なお、後述する架橋剤及び分散剤に該当する化合物は、高分子化合物であっても、上記重合体成分に含まないものとする。
上記感光性樹脂組成物層に含まれる重合体A1は、1種のみであっても、2種以上であってもよい。
上記重合体成分は、酸分解性で保護された酸基を有する構成単位Aを少なくとも有する重合体A1を含む。上記重合体成分が構成単位Aを有する重合体を含むことにより、極めて高感度な化学増幅ポジ型の感光性樹脂組成物層とすることができる。
本開示における「酸分解性で保護された酸基」は、酸基及び酸分解性基として公知のものを使用でき、特に限定されない。具体的な酸基としては、カルボキシル基、及び、フェノール性水酸基が好ましく挙げられる。また、酸分解性で保護された酸基としては、酸により比較的分解し易い基(例えば、式A1で表される基で保護されたエステル基、テトラヒドロピラニルエステル基、又は、テトラヒドロフラニルエステル基等のアセタール系官能基)や酸により比較的分解し難い基(例えば、tert−ブチルエステル基等の第三級アルキル基、tert−ブチルカーボネート基等の第三級アルキルカーボネート基)を用いることができる。
これらの中でも、上記酸分解性基としては、アセタールの形で保護された構造を有する基であることが好ましい。
上記酸分解性基で保護された酸基を有する構成単位Aは、感度及び解像度の観点から、下記式A1で表される構成単位であることが好ましい。
式A1中、R33は、アルキル基又はアリール基を表し、炭素数1〜10のアルキル基が好ましく、炭素数1〜6のアルキル基がより好ましい。
また、R31〜R33におけるアルキル基及びアリール基は、置換基を有していてもよい。
式A1中、R31又はR32と、R33とが連結して環状エーテルを形成してもよく、R31又はR32と、R33とが連結して環状エーテルを形成することが好ましい。環状エーテルの環員数は特に制限はないが、5又は6であることが好ましく、5であることがより好ましい。
式A1中、X0は単結合又はアリーレン基を表し、単結合が好ましい。アリーレン基は、置換基を有していてもよい。
上記式A1で表される構成単位は、酸分解性基で保護されたカルボキシ基を有する構成単位である。重合体A1が式A1で表される構成単位を含むことで、パターン形成時の感度に優れ、また、解像度より優れる。
より具体的には、重合体A1に含まれる式A1で表される構成単位の全量に対し、式AにおけるR34が水素原子である構成単位は20質量%以上であることが好ましい。
なお、式A1で表される構成単位中の、式A1におけるR34が水素原子である構成単位の含有量(含有割合:質量比)は、13C−核磁気共鳴スペクトル(NMR)測定から常法により算出されるピーク強度の強度比により確認することができる。
式A2中、R34は水素原子が好ましい。
式A2中、R35〜R41は、水素原子が好ましい。
式A3中、RB3は、アルキル基又はアリール基を表し、炭素数1〜10のアルキル基が好ましく、炭素数1〜6のアルキル基がより好ましい。
また、RB1〜RB3におけるアルキル基及びアリール基は、置換基を有していてもよい。
式A3中、RB1又はRB2と、RB3とが連結して環状エーテルを形成してもよく、RB1又はRB2と、RB3とが連結して環状エーテルを形成することが好ましい。環状エーテルの環員数は特に制限はないが、5又は6であることが好ましく、5であることがより好ましい。
式A3中、XBは単結合又は二価の連結基を表し、単結合又はアルキレン基、−C(=O)O−、−C(=O)NRN−、−O−又はこれらの組み合わせが好ましく、単結合がより好ましい。アルキレン基は、直鎖状でも分岐を有していても環状構造を有していてもよく、置換基を有していてもよい。アルキレン基の炭素数は1〜10が好ましく、1〜4がより好ましい。XBが−C(=O)O−を含む場合、−C(=O)O−に含まれる炭素原子と、RB4が結合した炭素原子とが直接結合する態様が好ましい。XBが−C(=O)NRN−を含む場合、−C(=O)NRN−に含まれる炭素原子と、RB4が結合した炭素原子とが直接結合する態様が好ましい。RNはアルキル基又は水素原子を表し、炭素数1〜4のアルキル基又は水素原子が好ましく、水素原子がより好ましい。
式A3中、RB1〜RB3を含む基と、XBとは、互いにパラ位で結合することが好ましい。
式A3中、RB12は置換基を表し、アルキル基又はハロゲン原子が好ましい。アルキル基の炭素数は、1〜10が好ましく、1〜4がより好ましい。
式A3中、nは0〜4の整数を表し、0又は1が好ましく、0がより好ましい。
より具体的には、重合体A1に含まれる構成単位Aの全含有量に対し、式A3におけるRB4が水素原子である構成単位は20質量%以上であることが好ましい。
なお、構成単位A中の、式A3におけるRB4が水素原子である構成単位の含有量(含有割合:質量比)は、13C−核磁気共鳴スペクトル(NMR)測定から常法により算出されるピーク強度の強度比により確認することができる。
式A4中、RB4は水素原子が好ましい。
式A4中、RB5〜RB11は、水素原子が好ましい。
式A4中、RB12は置換基を表し、アルキル基又はハロゲン原子が好ましい。アルキル基の炭素数は、1〜10が好ましく、1〜4がより好ましい。
式A4中、nは0〜4の整数を表し、0又は1が好ましく、0がより好ましい。
重合体A1における構成単位Aの含有量は、重合体A1の全質量に対して、20質量%以上であることが好ましく、20質量%〜90質量%であることがより好ましく、30質量%〜70質量%であることが更に好ましい。
重合体A1における構成単位Aの含有量(含有割合:質量比)は、13C−NMR測定から常法により算出されるピーク強度の強度比により確認することができる。
また、全ての重合体成分を構成単位(モノマー単位)に分解したうえで、構成単位Aの割合は、重合体成分の全質量に対して、5質量%〜80質量%であることが好ましく、10質量%〜80質量%であることがより好ましく、30質量%〜70質量%であることが特に好ましい。
上記重合体A1は、酸基を有する構成単位Bを含むことが好ましい。
構成単位Bは、保護基、例えば、酸分解性基で保護されていない酸基、すなわち、保護基を有さない酸基を有する構成単位である。重合体A1が構成単位Bを含むことで、パターン形成時の感度が良好となり、パターン露光後の現像工程においてアルカリ性の現像液に溶けやすくなり、現像時間の短縮化を図ることができる。
本明細書における酸基とは、pKaが12以下のプロトン解離性基を意味する。酸基は、通常、酸基を形成しうるモノマーを用いて、酸基を有する構成単位(構成単位B)として、重合体に組み込まれる。感度向上の観点から、酸基のpKaは、10以下が好ましく、6以下がより好ましい。また、酸基のpKaは、−5以上であることが好ましい。
重合体A1への酸基を有する構成単位の導入は、酸基を有するモノマーを共重合させること又は酸無水物構造を有するモノマーを共重合させ酸無水物を加水分解することで行うことができる。
構成単位Bである、酸基を有する構成単位は、スチレン化合物に由来する構成単位若しくはビニル化合物に由来する構成単位に対して酸基が置換した構成単位、又は、(メタ)アクリル酸に由来する構成単位であることがより好ましい。具体的には、カルボキシ基を有するモノマーとしては、アクリル酸、メタクリル酸、イタコン酸、クロトン酸、マレイン酸、フマル酸、4−カルボキシスチレン等が挙げられ、フェノール性水酸基を有するモノマーとしてはp−ヒドロキシスチレン、4−ヒドロキシフェニルメタクリレート等が挙げられ、酸無水物を有するモノマーとしては、無水マレイン酸等が挙げられる。
構成単位Bを形成しうる酸基を有するモノマーは既述の例に限定されない。
重合体A1は、重合体A1の全質量に対し、酸基を有する構成単位(構成単位B)を0.1質量%〜20質量%含むことが好ましく、0.5質量%〜15質量%含むことがより好ましく、1質量%〜10質量%含むことが更に好ましい。上記範囲であると、パターン形成性がより良好となる。
重合体A1における構成単位Bの含有量(含有割合:質量比)は、13C−NMR測定から常法により算出されるピーク強度の強度比により確認することができる。
重合体A1は、既述の構成単位A及び構成単位B以外の、他の構成単位(以下、構成単位Cと称することがある。)を、本開示に係る感光性転写材料の効果を損なわない範囲で含んでいてもよい。
構成単位Cを形成するモノマーとしては、特に制限はなく、例えば、スチレン類、(メタ)アクリル酸アルキルエステル、(メタ)アクリル酸環状アルキルエステル、(メタ)アクリル酸アリールエステル、不飽和ジカルボン酸ジエステル、ビシクロ不飽和化合物、マレイミド化合物、不飽和芳香族化合物、共役ジエン系化合物、不飽和モノカルボン酸、不飽和ジカルボン酸、不飽和ジカルボン酸無水物、脂肪族環式骨格を有する基、その他の不飽和化合物を挙げることができる。
構成単位Cを用いて、種類及び含有量の少なくともいずれかを調整することで、重合体A1の諸特性を調整することができる。特に、構成単位Cを適切に使用することで、重合体A1のTgを容易に調整することができる。
ガラス転移温度を120℃以下とすることで、重合体A1を含有するポジ型感光性樹脂組成物層は、転写性、仮支持体からの剥離性を良好なレベルに維持しつつ、パターン形成時の解像度及び感度がより良好となる。
重合体A1は、構成単位Cを1種のみ含んでもよく、2種以上含んでいてもよい。
中でも、重合体A1は、構成単位Bとして、カルボン酸基を有する構成単位を含み、更に、カルボン酸エステル基を含む構成単位Cを共重合成分として含むことが好ましく、例えば、(メタ)アクリル酸由来の構成単位Bと、(メタ)アクリル酸シクロヘキシル、(メタ)アクリル酸2−エチルヘキシル又は(メタ)アクリル酸n−ブチル由来の構成単位(c)とを含む重合体がより好ましい。
以下、本開示における重合体A1の好ましい例を挙げるが、本開示は以下の例示に限定されない。なお、下記例示化合物における構成単位の比率、重量平均分子量は、好ましい物性を得るために適宜選択される。
本開示における重合体A1のガラス転移温度(Tg)は、転写性の観点から、120℃以下であることが好ましく、20℃以上90℃以下であることがより好ましい。
具体的な測定方法は、JIS K 7121(1987年)又はJIS K 6240(2011年)に記載の方法に順じて行った。本明細書におけるガラス転移温度は、補外ガラス転移開始温度(以下、Tigと称することがある)を用いている。
ガラス転移温度の測定方法をより具体的に説明する。
ガラス転移温度を求める場合、予想される重合体のTgより約 50℃低い温度にて装置が安定するまで保持した後、加熱速度:20℃/分で、ガラス転移が終了した温度よりも約30℃高い温度まで加熱し、示差熱分析(DTA)曲線又はDSC曲線を描かせる。
補外ガラス転移開始温度(Tig)、すなわち、本明細書におけるガラス転移温度Tgは、DTA曲線又はDSC曲線における低温側のベースラインを高温側に延長した直線と、ガラス転移の階段状変化部分の曲線の勾配が最大になる点で引いた接線との交点の温度として求める。
FOX式について
重合体に含まれる第1の構成単位の単独重合体のTgをTg1、第1の構成単位の共重合体における質量分率をW1とし、第2の構成単位の単独重合体のTgをTg2とし、第2の構成単位の共重合体における質量分率をW2としたときに、第1の構成単位と第2の構成単位とを含む共重合体のTg0(K)は、以下の式にしたがって推定することが可能である。
FOX式:1/Tg0=(W1/Tg1)+(W2/Tg2)
既述のFOX式を用いて、共重合体に含まれる各構成単位の種類と質量分率を調整して、所望のTgを有する共重合体を得ることができる。
また、重合体の重量平均分子量を調整することにより、重合体のTgを調整することも可能である。
重合体A1の酸価は、現像性及び転写性の観点から、0mgKOH/g以上200mgKOH/g以下であることが好ましく、5mgKOH/g以上100mgKOH/g以下であることがより好ましい。
A=56.11×Vs×0.1×f/w
A:酸価(mgKOH/g)
Vs:滴定に要した0.1mol/l水酸化ナトリウム水溶液の使用量(mL)
f:0.1mol/l水酸化ナトリウム水溶液の力価
w:測定サンプルの質量(g)(固形分換算)
重合体A1の分子量は、ポリスチレン換算重量平均分子量で、60,000以下であることが好ましい。重合体A1の重量平均分子量が60,000以下であることで、感光性樹脂組成物層の溶融粘度を低く抑え、上記基板と貼り合わせる際において低温(例えば130℃以下)での貼り合わせを実現することができる。
また、重合体A1の重量平均分子量は、2,000〜60,000であることが好ましく、3,000〜50,000であることがより好ましい。
なお、重合体の重量平均分子量は、GPC(ゲルパーミエーションクロマトグラフィー)によって測定することができ、測定装置としては、様々な市販の装置を用いることができ、装置の内容、及び、測定技術は同当業者に公知である。
ゲルパーミエーションクロマトグラフィ(GPC)による重量平均分子量の測定は、測定装置として、HLC(登録商標)−8220GPC(東ソー(株)製)を用い、カラムとして、TSKgel(登録商標)Super HZM−M(4.6mmID×15cm、東ソー(株)製)、Super HZ4000(4.6mmID×15cm、東ソー(株)製)、Super HZ3000(4.6mmID×15cm、東ソー(株)製)、Super HZ2000(4.6mmID×15cm、東ソー(株)製)をそれぞれ1本、直列に連結したものを用い、溶離液として、THF(テトラヒドロフラン)を用いることができる。
また、測定条件としては、試料濃度を0.2質量%、流速を0.35ml/min、サンプル注入量を10μL、及び測定温度を40℃とし、示差屈折率(RI)検出器を用いて行うことができる。
検量線は、東ソー(株)製の「標準試料TSK standard,polystyrene」:「F−40」、「F−20」、「F−4」、「F−1」、「A−5000」、「A−2500」及び「A−1000」の7サンプルのいずれかを用いて作製できる。
重合体A1の製造方法(合成法)は特に限定されないが、一例を挙げると、式Aで表される構成単位Aを形成するための重合性単量体、酸基を有する構成単位Bを形成するための重合性単量体、更に必要に応じて、その他の構成単位Cを形成するための重合性単量体を含む有機溶剤中、重合開始剤を用いて重合することにより合成することができる。また、いわゆる高分子反応で合成することもできる。
また、上記感光性樹脂組成物層は、上記基板に対して良好な密着性を発現させる観点から、感光性樹脂組成物層の全固形分に対し、上記重合体A1を50質量%〜99.9質量%の割合で含むことが好ましく、70質量%〜98質量%の割合で含むことがより好ましい。
上記感光性樹脂組成物層は、重合体成分として、重合体A1に加え、本開示に係る感光性転写材料の効果を損なわない範囲において、式Aで示される構成単位(a)を含まない重合体(「他の重合体」と称する場合がある。)を更に含んでいてもよい。上記感光性樹脂組成物層が他の重合体を含む場合、他の重合体の配合量は、全重合体成分中、50質量%以下であることが好ましく、30質量%以下であることがより好ましく、20質量%以下であることが更に好ましい。
他の重合体として、例えばポリヒドロキシスチレンを用いることができ、市販されている、SMA 1000P、SMA 2000P、SMA 3000P、SMA 1440F、SMA 17352P、SMA 2625P、及び、SMA 3840F(以上、サートマー社製)、ARUFON UC−3000、ARUFON UC−3510、ARUFON UC−3900、ARUFON UC−3910、ARUFON UC−3920、及び、ARUFON UC−3080(以上、東亞合成(株)製)、並びに、Joncryl 690、Joncryl 678、Joncryl 67、及び、Joncryl 586(以上、BASF社製)等を用いることもできる。
上記感光性樹脂組成物層は、光酸発生剤を含有する。
本開示で使用される光酸発生剤としては、紫外線、遠紫外線、X線、及び、荷電粒子線等の放射線を照射することにより酸を発生することができる化合物である。
本開示で使用される光酸発生剤としては、波長300nm以上、好ましくは波長300nm〜450nmの活性光線に感応し、酸を発生する化合物が好ましいが、その化学構造は制限されない。また、波長300nm以上の活性光線に直接感応しない光酸発生剤についても、増感剤と併用することによって波長300nm以上の活性光線に感応し、酸を発生する化合物であれば、増感剤と組み合わせて好ましく用いることができる。
本開示で使用される光酸発生剤としては、pKaが4以下の酸を発生する光酸発生剤が好ましく、pKaが3以下の酸を発生する光酸発生剤がより好ましく、pKaが2以下の酸を発生する光酸発生剤が特に好ましい。pKaの下限値は特に定めないが、例えば、−10.0以上であることが好ましい。
また、光酸発生剤としては、感度及び解像度の観点から、後述するオニウム塩化合物、及び、後述するオキシムスルホネート化合物よりなる群から選ばれた少なくとも1種の化合物を含むことが好ましく、オキシムスルホネート化合物を含むことがより好ましい。
R21のアルキル基としては、炭素数1〜10の、直鎖状又は分岐状アルキル基が好ましい。R21のアルキル基は、炭素数6〜11のアリール基、炭素数1〜10のアルコキシ基、シクロアルキル基(7,7−ジメチル−2−オキソノルボルニル基などの有橋式脂環基を含む、好ましくはビシクロアルキル基等)、又は、ハロゲン原子で置換されてもよい。
R21のアリール基としては、炭素数6〜18のアリール基が好ましく、フェニル基又はナフチル基がより好ましい。R21のアリール基は、炭素数1〜4のアルキル基、アルコキシ基及びハロゲン原子よりなる群から選ばれた1つ以上の基で置換されてもよい。
上記感光性樹脂組成物層における光酸発生剤の含有量は、感度、解像度の観点から、上記感光性樹脂組成物層の全質量に対して、0.1質量%〜10質量%であることが好ましく、0.5質量%〜5質量%であることがより好ましい。
上記感光性樹脂組成物層は、溶剤を含んでいてもよい。
また、上記感光性樹脂組成物層を形成する感光性樹脂組成物は、上記感光性樹脂組成物層を容易に形成するため、一旦溶剤を含有させて感光性樹脂組成物の粘度を調節し、溶剤を含む感光性樹脂組成物を塗布及び乾燥して、上記感光性樹脂組成物層を好適に形成することができる。
本開示に使用される溶剤としては、公知の溶剤を用いることができる。溶剤としては、エチレングリコールモノアルキルエーテル類、エチレングリコールジアルキルエーテル類、エチレングリコールモノアルキルエーテルアセテート類、プロピレングリコールモノアルキルエーテル類、プロピレングリコールジアルキルエーテル類、プロピレングリコールモノアルキルエーテルアセテート類、ジエチレングリコールジアルキルエーテル類、ジエチレングリコールモノアルキルエーテルアセテート類、ジプロピレングリコールモノアルキルエーテル類、ジプロピレングリコールジアルキルエーテル類、ジプロピレングリコールモノアルキルエーテルアセテート類、エステル類、ケトン類、アミド類、及び、ラクトン類等が例示できる。また、溶剤の具体例としては特開2011−221494号公報の段落0174〜段落0178に記載の溶剤も挙げられ、これらの内容は本明細書に組み込まれる。
溶剤は、1種のみ用いてもよく、2種以上を使用してもよい。
本開示に用いることができる溶剤は、1種単独で用いてもよく、2種を併用することがより好ましい。溶剤を2種以上使用する場合には、例えば、プロピレングリコールモノアルキルエーテルアセテート類とジアルキルエーテル類との併用、ジアセテート類とジエチレングリコールジアルキルエーテル類との併用、又は、エステル類とブチレングリコールアルキルエーテルアセテート類との併用が好ましい。
沸点130℃以上160℃未満の溶剤としては、プロピレングリコールモノメチルエーテルアセテート(沸点146℃)、プロピレングリコールモノエチルエーテルアセテート(沸点158℃)、プロピレングリコールメチル−n−ブチルエーテル(沸点155℃)、及び、プロピレングリコールメチル−n−プロピルエーテル(沸点131℃)が例示できる。
沸点160℃以上の溶剤としては、3−エトキシプロピオン酸エチル(沸点170℃)、ジエチレングリコールメチルエチルエーテル(沸点176℃)、プロピレングリコールモノメチルエーテルプロピオネート(沸点160℃)、ジプロピレングリコールメチルエーテルアセテート(沸点213℃)、3−メトキシブチルエーテルアセテート(沸点171℃)、ジエチレングリコールジエチエルエーテル(沸点189℃)、ジエチレングリコールジメチルエーテル(沸点162℃)、プロピレングリコールジアセテート(沸点190℃)、ジエチレングリコールモノエチルエーテルアセテート(沸点220℃)、ジプロピレングリコールジメチルエーテル(沸点175℃)、及び、1,3−ブチレングリコールジアセテート(沸点232℃)が例示できる。
また、上記感光性樹脂組成物層における溶剤の含有量は、上記感光性樹脂組成物層の全質量に対し、2質量%以下であることが好ましく、1質量%以下であることがより好ましく、0.5質量%以下であることが更に好ましい。
本開示における上記感光性樹脂組成物層は、重合体A1及び光酸発生剤に加え、必要に応じて公知の添加剤を含むことができる。
上記感光性樹脂組成物層は、可塑性を改良する目的で、可塑剤を含有してもよい。
上記可塑剤は、重合体A1よりも重量平均分子量が小さいことが好ましい。
可塑剤の重量平均分子量は、可塑性付与の観点から500以上10,000未満が好ましく、700以上5,000未満がより好ましく、800以上4,000未満が更に好ましい。
可塑剤は、重合体A1と相溶して可塑性を発現する化合物であれば特に限定されないが、可塑性付与の観点から、可塑剤は、分子中にアルキレンオキシ基を有することが好ましい。可塑剤に含まれるアルキレンオキシ基は下記構造を有することが好ましい。
上記感光性樹脂組成物層は、可塑剤を1種のみを含んでいてもよく、2種以上を含んでいてもよい。
上記感光性樹脂組成物層は、増感剤を更に含むことができる。
増感剤は、活性光線を吸収して電子励起状態となる。電子励起状態となった増感剤は、光酸発生剤と接触して、電子移動、エネルギー移動、及び、発熱などの作用が生じる。これにより光酸発生剤は化学変化を起こして分解し、酸を生成する。
増感剤を含有させることで、露光感度を向上させることができる。
アントラセン誘導体としては、アントラセン、9,10−ジブトキシアントラセン、9,10−ジクロロアントラセン、2−エチル−9,10−ジメトキシアントラセン、9−ヒドロキシメチルアントラセン、9−ブロモアントラセン、9−クロロアントラセン、9,10−ジブロモアントラセン、2−エチルアントラセン、又は、9,10−ジメトキシアントラセンが好ましい。
上記感光性樹脂組成物層は、塩基性化合物を更に含むことが好ましい。
塩基性化合物としては、化学増幅レジストで用いられる塩基性化合物の中から任意に選択して使用することができる。例えば、脂肪族アミン、芳香族アミン、複素環式アミン、第四級アンモニウムヒドロキシド、及び、カルボン酸の第四級アンモニウム塩等が挙げられる。これらの具体例としては、特開2011−221494号公報の段落0204〜段落0207に記載の化合物が挙げられ、これらの内容は本明細書に組み込まれる。
芳香族アミンとしては、例えば、アニリン、ベンジルアミン、N,N−ジメチルアニリン、及び、ジフェニルアミンなどが挙げられる。
複素環式アミンとしては、例えば、ピリジン、2−メチルピリジン、4−メチルピリジン、2−エチルピリジン、4−エチルピリジン、2−フェニルピリジン、4−フェニルピリジン、N−メチル−4−フェニルピリジン、4−ジメチルアミノピリジン、イミダゾール、ベンズイミダゾール、4−メチルイミダゾール、2−フェニルベンズイミダゾール、2,4,5−トリフェニルイミダゾール、ニコチン、ニコチン酸、ニコチン酸アミド、キノリン、8−オキシキノリン、ピラジン、ピラゾール、ピリダジン、プリン、ピロリジン、ピペリジン、ピペラジン、モルホリン、4−メチルモルホリン、1,5−ジアザビシクロ[4.3.0]−5−ノネン、及び、1,8−ジアザビシクロ[5.3.0]−7−ウンデセンなどが挙げられる。
第四級アンモニウムヒドロキシドとしては、例えば、テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシド、テトラ−n−ブチルアンモニウムヒドロキシド、及び、テトラ−n−ヘキシルアンモニウムヒドロキシドなどが挙げられる。
カルボン酸の第四級アンモニウム塩としては、例えば、テトラメチルアンモニウムアセテート、テトラメチルアンモニウムベンゾエート、テトラ−n−ブチルアンモニウムアセテート、及び、テトラ−n−ブチルアンモニウムベンゾエートなどが挙げられる。
塩基性化合物の含有量は、上記感光性樹脂組成物層の全質量に対して、0.001質量%〜5質量%であることが好ましく、0.005質量%〜3質量%であることがより好ましい。
本開示における感光性樹脂組成物層は、ヘテロ環状化合物を含むことができる。
本開示におけるヘテロ環状化合物には、特に制限はない。例えば、以下に述べる分子内にエポキシ基又はオキセタニル基を有する化合物、アルコキシメチル基含有ヘテロ環状化合物、その他、各種環状エーテル、環状エステル(ラクトン)などの含酸素モノマー、環状アミン、オキサゾリンといった含窒素モノマー、更には珪素、硫黄、リンなどのd電子をもつヘテロ環モノマー等を添加することができる。
その他の市販品として、ADEKA RESIN EP−4000S、同EP−4003S、同EP−4010S、同EP−4011S(以上、(株)ADEKA製)、NC−2000、NC−3000、NC−7300、XD−1000、EPPN−501、EPPN−502(以上、(株)ADEKA製)、デナコールEX−611、EX−612、EX−614、EX−614B、EX−622、EX−512、EX−521、EX−411、EX−421、EX−313、EX−314、EX−321、EX−211、EX−212、EX−810、EX−811、EX−850、EX−851、EX−821、EX−830、EX−832、EX−841、EX−911、EX−941、EX−920、EX−931、EX−212L、EX−214L、EX−216L、EX−321L、EX−850L、DLC−201、DLC−203、DLC−204、DLC−205、DLC−206、DLC−301、DLC−402、EX−111,EX−121、EX−141、EX−145、EX−146、EX−147、EX−171、EX−192(以上ナガセケムテック製)、YH−300、YH−301、YH−302、YH−315、YH−324、YH−325(以上、新日鐵住金化学(株)製)セロキサイド2021P、2081、2000、3000、EHPE3150、エポリードGT400、セルビナースB0134、B0177((株)ダイセル製)などが挙げられる。
分子内にエポキシ基を有する化合物は1種単独で用いてもよく、2種以上を併用してもよい。
上記感光性樹脂組成物層は、アルコキシシラン化合物を含有してもよい。アルコキシシラン化合物としては、トリアルコキシシラン化合物が好ましく挙げられる。
アルコキシシラン化合物としては、例えば、γ−アミノプロピルトリメトキシシラン、γ−アミノプロピルトリエトキシシラン、γ−グリシドキシプロピルトリアルコキシシラン、γ−グリシドキシプロピルアルキルジアルコキシシラン、γ−メタクリロキシプロピルトリアルコキシシラン、γ−メタクリロキシプロピルアルキルジアルコキシシラン、γ−クロロプロピルトリアルコキシシラン、γ−メルカプトプロピルトリアルコキシシラン、β−(3,4−エポキシシクロヘキシル)エチルトリアルコキシシラン、ビニルトリアルコキシシランが挙げられる。これらのうち、γ−グリシドキシプロピルトリアルコキシシラン又はγ−メタクリロキシプロピルトリアルコキシシランがより好ましく、γ−グリシドキシプロピルトリアルコキシシランが更に好ましく、3−グリシドキシプロピルトリメトキシシランが特に好ましい。これらは1種単独又は2種以上を組み合わせて使用することができる。
上記感光性樹脂組成物層は、膜厚均一性の観点から界面活性剤を含有することが好ましい。界面活性剤としては、アニオン系、カチオン系、ノニオン系(非イオン系)、又は、両性のいずれでも使用することができるが、好ましい界面活性剤はノニオン界面活性剤である。
ノニオン系界面活性剤の例としては、ポリオキシエチレン高級アルキルエーテル類、ポリオキシエチレン高級アルキルフェニルエーテル類、ポリオキシエチレングリコールの高級脂肪酸ジエステル類、シリコーン系、フッ素系界面活性剤を挙げることができる。また、以下商品名で、KP(信越化学工業(株)製)、ポリフロー(共栄社化学(株)製)、エフトップ(JEMCO社製)、メガファック(DIC(株)製)、フロラード(住友スリーエム(株)製)、アサヒガード、サーフロン(旭硝子(株)製)、PolyFox(OMNOVA社製)、及び、SH−8400(東レ・ダウコーニング(株)製)等の各シリーズを挙げることができる。
また、界面活性剤として、下記式I−1で表される構成単位A及び構成単位Bを含み、テトラヒドロフラン(THF)を溶剤とした場合のゲルパーミエーションクロマトグラフィーで測定されるポリスチレン換算の重量平均分子量(Mw)が1,000以上10,000以下である共重合体を好ましい例として挙げることができる。
界面活性剤の添加量は、上記感光性樹脂組成物層の全質量に対して、10質量%以下であることが好ましく、0.001質量%〜10質量%であることがより好ましく、0.01質量%〜3質量%であることが更に好ましい。
本開示における感光性樹脂組成物層には、金属酸化物粒子、酸化防止剤、分散剤、酸増殖剤、現像促進剤、導電性繊維、着色剤、熱ラジカル重合開始剤、熱酸発生剤、紫外線吸収剤、増粘剤、架橋剤、及び、有機又は無機の沈殿防止剤などの公知の添加剤を更に加えることができる。
その他の成分の好ましい態様については特開2014−85643号公報の段落0165〜段落0184にそれぞれ記載があり、この公報の内容は本明細書に組み込まれる。
各成分、及び、溶剤を任意の割合でかつ任意の方法で混合し、撹拌溶解して感光性樹脂組成物層を形成するための感光性樹脂組成物を調製することができる。例えば、各成分を、それぞれ予め溶剤に溶解させた溶液とした後、得られた溶液を所定の割合で混合して組成物を調製することもできる。以上の如くして調製した組成物は、孔径0.2μmのフィルター等を用いてろ過した後に、使用に供することもできる。
塗布方法は特に限定されず、スリット塗布、スピン塗布、カーテン塗布、インクジェット塗布などの公知の方法で塗布することができる。
なお、仮支持体上に後述のその他の層を形成した上に、感光性樹脂組成物層を塗布することもできる。
本開示に係る感光性転写材料は、仮支持体上に、感光性樹脂組成物層、及び、紫外線吸収層を有し、上記紫外線吸収層が、有機紫外線吸収剤と重合体A2とを含むか、又は、紫外線吸収能を有する重合体A3を含み、上記紫外線吸収層に含まれる、上記重合体A2のガラス転移温度又は上記重合体A3のガラス転移温度が、90℃以下である。
上記紫外線吸収層は、紫外線を吸収可能な層であればよく、本開示における紫外線吸収の波長領域は、波長450nm以下の紫外線であり、例えば、高圧水銀灯が発光するg線(435nm)、h線(405nm)、i線(365nm)、更に、j線(313nm)、等の紫外線、KrF露光装置での露光波長である248nm、ArF露光装置での露光波長である193nm等の波長の紫外線が挙げられる。
また、紫外線吸収層の露光波長における25℃の吸光度としては、0.2〜2.0がより好ましく、0.4〜1.0が特に好ましい。上記範囲とすることで、紫外線吸収剤の拡散による感度の低下や、ブリードアウトによる画質の低下を抑制することができる。
紫外線吸収層の上記吸光度は、感光性樹脂組成物層やその他の層と紫外線吸収層とを重層化したもの(例えば、本開示に係る感光性転写材料や、本開示に係る感光性転写材料から仮支持体を除去したもの)全体の紫外線吸収スペクトルを測定し、全体の吸光度を求めたのちに、感光性樹脂組成物層やその他の層の吸光度を差し引くことでも求めることができる。
一方、生産性の観点からは、上記紫外線吸収層は、有機紫外線吸収剤と重合体A2とを含むことが好ましい。
有機紫外線吸収剤としては、紫外線を吸収可能な有機化合物であり、上記重合体A3以外の化合物であればよい。なお、ガラス転移温度が90℃を超える紫外線吸収能を有する重合体は、上記有機紫外線吸収剤に含まれる。
上記紫外線吸収層が、ガラス転移温度が90℃を超える紫外線吸収能を有する重合体を含む場合、重合体A2の含有量は、ガラス転移温度が90℃を超える紫外線吸収能を有する重合体の含有量よりも多いことが好ましい。
したがって、使用する有機紫外線吸収剤は、使用する光酸発生剤の種類によって適宜選択することが好ましい。
また、有機紫外線吸収剤は使用する重合体A2に十分に溶解し、塗布乾燥後も濁りのない透明な膜を形成することが好ましい。使用する重合体A2に十分に溶解し、塗布乾燥後も濁りのない透明な膜を形成することで、光散乱による光学像の乱れが発生せず、直線性の良い高解像なレジストパターンを得ることができる。また、使用する重合体A2に十分に溶解し、塗布乾燥後も濁りのない透明な膜を形成することで、塗膜の熱接着性が損なわれることがなく、低温、高速での貼り合わせを行うことが可能となる。
また、使用する重合体A2に十分に溶解し、塗布乾燥後も濁りのない透明な膜を形成するためには、塗布液の状態で塗布に使用する溶剤に溶解していることが好ましい。
ベンゾトリアゾール系化合物としては、2−(2H−ベンゾトリアゾール−2−イル)−4,6−ジ−t−ペンチルフェノール(例えば、チバ・スペシャルティ・ケミカル社製の商品名「チヌビン328」)、2−(2H−ベンゾトリアゾール−2−イル)−4,6−ビス(1−メチル−1−フェニルエチル)フェノール、α−[3−[3−(2H−ベンゾトリアルゾール−2−イル)−5−(1,1−ジメチルエチル)−4−ヒドロキシフェニル]−1−オキソプロピル]−ω−ヒドロキシポリ(オキソ−1,2−エタンジイル)(例えば、チバ・スペシャルティ・ケミカル社製の商品名「チヌビン1130」)等が挙げられる。
また、ベンゾトリアゾール系化合物としては、クロロ基(塩素原子)を有するものも挙げられる。このようなクロロ基を有するベンゾトリアゾール系化合物としては、具体的には、オクチル−3−[3−t−ブチル−4−ヒドロキシ−5−(5−クロロ−2H−ベンゾトリアゾール−2−イル)フェニル]プロピオネート(例えば、チバ・スペシャルティ・ケミカル社製の商品名「チヌビン109」)、2−[5−クロロ(2H)−ベンゾトリアゾール−2−イル]−4−メチル−6−(t−ブチル)フェノール(例えば、チバ・スペシャルティ・ケミカル社製の商品名「チヌビン326」)、2,4−ジ−t−ブチル−6−(5−クロロベンゾトリアゾール−2−イル)フェノール(例えばチバ・スペシャルティ・ケミカル社製の商品名「チヌビン327」)等が挙げられる。
市販品としては、チバ・スペシャルティ・ケミカル社製の商品名「チヌビン400」(2−[4−[(2−ヒドロキシ−3−ドデシルオキシプロピル)オキシ]−2−ヒドロキシフェニル]−4,6−ビス(4,6−ビス(2,4−ジメチルフェニル)−1,3,5−トリアジンと、2−[4−[(2−ヒドロキシ−3−トリデシルオキシプロピル)オキシ]−2−ヒドロキシフェニル]−4,6−ビス(4,6−ビス(2,4−ジメチルフェニル)−1,3,5−トリアジンとの混合物)、「チヌビン411L」(2,4−ビス(2,4−ジメチルフェニル)−6−(2−ヒドロキシ−4−イソオクチルフェニル)−s−トリアジン)等を挙げることができる。
また、1−(4−t−ブチルフェニル)−3−(4−メトキシフェニル)−1,3−プロパンジオン(エスカロール517、アイエスピー・ジャパン(株)製)などのアボベンゾン系紫外線吸収剤を挙げることができる。
また、フェニルアゾレゾルシノール、チアゾリルアゾレゾルシノール等のアゾレゾルシノール系紫外線吸収剤を挙げることができる。
ポリマー型紫外線吸収剤を選択する場合、そのポリマーのガラス転移温度が90℃以下であること(重合体A3に該当する。)が好ましいが、ガラス転移温度が90℃以下である重合体A2と併用する場合には、ポリマー型紫外線吸収剤のガラス転移温度は90℃より高いものを用いることもできる。
有機紫外線吸収剤の含有量は、パターン形成性及び得られるパターンの直線性の観点から、上記紫外線吸収層の全質量に対して、5質量%〜50質量%であることが好ましく、10質量%〜40質量%であることがより好ましく、15質量%〜25質量%であることが特に好ましい。
また、上記紫外線吸収層における有機紫外線吸収剤の含有量は、パターン形成性及び得られるパターンの直線性の観点から、上記重合体A2の含有量よりも少ないことが好ましい。
重合体A2のガラス転移温度(Tg)は、90℃以下であり、転写性の観点から、−20℃〜60℃であることが好ましく、0℃〜50℃であることがより好ましく、20℃〜50℃であることが特に好ましい。
重合体A2は、直鎖状の重合体であることが好ましいが、その他の架橋構造を有する樹脂を用いてもよい。また、重合体A2は、付加重合型の樹脂であることが好ましく、(メタ)アクリル酸又はそのエステルに由来する構成単位を有する重合体であることがより好ましい。なお、(メタ)アクリル酸又はそのエステルに由来する構成単位以外の構成単位、例えば、スチレンに由来する構成単位や、ビニル化合物に由来する構成単位等を有していてもよい。
上記酸基としては、カルボキシ基、スルホンアミド基、ホスホン酸基、スルホン酸基、フェノール性水酸基、及び、スルホニルイミド基等が例示される。中でも、カルボキシ基又はフェノール性水酸基が好ましく、カルボキシ基が特に好ましい。
重合体A2への酸基を有する構成単位の導入は、酸基を有するモノマーを重合させること又は酸無水物構造を有するモノマーを共重合させ酸無水物を加水分解することで行うことができる。
上記酸基を有する構成単位は、スチレン化合物に由来する構成単位若しくはビニル化合物に由来する構成単位に対して酸基が置換した構成単位、又は、(メタ)アクリル酸に由来する構成単位であることが好ましく、(メタ)アクリル酸に由来する構成単位であることがより好ましい。具体的には、カルボキシ基を有するモノマーとしては、アクリル酸、メタクリル酸、イタコン酸、クロトン酸、マレイン酸、フマル酸、4−カルボキシスチレン等が挙げられ、フェノール性水酸基を有するモノマーとしてはp−ヒドロキシスチレン、4−ヒドロキシフェニルメタクリレート等が挙げられ、酸無水物を有するモノマーとしては、無水マレイン酸等が挙げられる。
重合体A2は、酸基を有する構成単位を、重合体A2の全質量に対し、0.1質量%〜20質量%含むことが好ましく、0.5質量%〜15質量%含むことがより好ましく、1質量%〜10質量%含むことが更に好ましい。上記範囲であると、パターン形成性がより良好となる。
重合体A2における酸基を有する構成単位の含有量(含有割合:質量比)は、13C−NMR測定から常法により算出されるピーク強度の強度比により確認することができる。
また、重合体A2は、酸分解性基で保護された酸基を有する構成単位を含有することもできる。
重合体A2における構成単位Cを形成するモノマーとしては、特に制限はなく、例えば、スチレン類、(メタ)アクリル酸アルキルエステル、(メタ)アクリル酸環状アルキルエステル、(メタ)アクリル酸アリールエステル、不飽和ジカルボン酸ジエステル、ビシクロ不飽和化合物、マレイミド化合物、不飽和芳香族化合物、共役ジエン系化合物、不飽和モノカルボン酸、不飽和ジカルボン酸、不飽和ジカルボン酸無水物、脂肪族環式骨格を有する基を有するエチレン性不飽和化合物、その他の不飽和化合物を挙げることができる。
中でも、重合体A2は、ガラス転移温度及び有機紫外線吸収剤の分散性の観点から、脂肪族環式骨格を有する基を有するエチレン性不飽和化合物により形成される構成単位を有することが好ましく、脂肪族環式骨格を有する基を有する(メタ)アクリレート化合物により形成される構成単位を有することがより好ましく、シクロヘキシル基を有する(メタ)アクリレート化合物により形成される構成単位を有することが特に好ましい。
構成単位Cを用いて、種類及び含有量の少なくともいずれかを調整することで、重合体A2の諸特性を調整することができる。特に、構成単位Cを適切に使用することで、重合体A2のTgを90℃以下に容易に調整することができる。
重合体A2は、構成単位Cを1種のみ含んでもよく、2種以上含んでいてもよい。
上記紫外線吸収層における重合体A2の含有量は、回路配線形成用基板に対して低温かつ高速で貼り合わせた場合でも良好な密着性を発現させる観点から、重合体A2の紫外線吸収層の全固形分に対し、50質量%〜99.9質量%であることが好ましく、70質量%〜98質量%であることがより好ましい。
上記紫外線吸収層は、保存安定性及び得られるパターンの直線性の観点から、紫外線吸収能を有する重合体A3を含むことが好ましい。
重合体A3のガラス転移温度は、90℃以下であり、転写性の観点から、−20℃〜60℃であることが好ましく、0℃〜50℃であることがより好ましく、20℃〜50℃であることが特に好ましい。
重合体A3は、直鎖状の重合体であることが好ましいが、その他の架橋構造を有する樹脂を用いてもよい。また、重合体A3は、付加重合型の樹脂であることが好ましく、(メタ)アクリル酸又はそのエステルに由来する構成単位を有する重合体であることがより好ましい。なお、(メタ)アクリル酸又はそのエステルに由来する構成単位以外の構成単位、例えば、スチレンに由来する構成単位や、ビニル化合物に由来する構成単位等を有していてもよい。
紫外線吸収性基を含む構成単位(「構成単位(a)」ともいう。)は、スチレン化合物に由来する構成単位、ビニル化合物に由来する構成単位、又は、(メタ)アクリレート化合物に由来する構成単位であることが好ましい。
紫外線吸収性基は、感光性樹脂組成物層に含有される光酸発生剤の感光波長の一部、又は、全ての波長を光吸収可能な紫外線吸収特性を有することが好ましい。
したがって、紫外線吸収性基は、使用する光酸発生剤の種類によって適宜選択することが好ましい。
例えば、365nm(i線)に光吸収性を有する紫外線吸収性基を有する(メタ)アクリレート化合物としては、具体的には以下の構造ものを挙げることができる。
2−[3−(2H−1,2,3−ベンゾトリアゾール−2−イル)−4−ヒドロキシフェニル]エチルメタクリレート(新中村化学工業(株)製)
重合体A3は、紫外線吸収性基を有する構成単位を、重合体A3の全質量に対し、10質量%〜99質量%含むことが好ましく、20質量%〜90質量%含むことがより好ましく、40質量%〜80質量%含むことが更に好ましい。上記範囲であると、アルカリ現像液への溶解性がよく、直線性もより良好となる。
上記酸基としては、カルボキシ基、スルホンアミド基、ホスホン酸基、スルホン酸基、フェノール性水酸基、及び、スルホニルイミド基等が例示される。中でも、カルボキシ基又はフェノール性水酸基が好ましく、カルボキシ基が特に好ましい。
重合体A3への酸基を有する構成単位の導入は、酸基を有するモノマーを重合させることで行うことができる。
上記酸基を有する構成単位は、スチレンに由来する構成単位若しくはビニル化合物に由来する構成単位に対して酸基が置換した構成単位、又は、(メタ)アクリル酸に由来する構成単位であることが好ましく、(メタ)アクリル酸に由来する構成単位であることがより好ましい。
重合体A3は、酸基を有する構成単位を、重合体A3の全質量に対し、0.1質量%〜20質量%含むことが好ましく、0.5質量%〜15質量%含むことがより好ましく、1質量%〜10質量%含むことが更に好ましい。上記範囲であると、パターン形成性がより良好となる。
重合体A3における酸基を有する構成単位の含有量(含有割合:質量比)は、13C−NMR測定から常法により算出されるピーク強度の強度比により確認することができる。
また、重合体A3は、酸分解性基で保護された酸基を有する構成単位を有していてもよい。
重合体A3における構成単位Cを形成するモノマーとしては、特に制限はなく、例えば、スチレン類、(メタ)アクリル酸アルキルエステル、(メタ)アクリル酸環状アルキルエステル、(メタ)アクリル酸アリールエステル、不飽和ジカルボン酸ジエステル、ビシクロ不飽和化合物、マレイミド化合物、不飽和芳香族化合物、共役ジエン系化合物、不飽和モノカルボン酸、不飽和ジカルボン酸、不飽和ジカルボン酸無水物、脂肪族環式骨格を有する基を有するエチレン性不飽和化合物、その他の不飽和化合物を挙げることができる。
構成単位Cを用いて、種類及び含有量の少なくともいずれかを調整することで、重合体A3の諸特性を調整することができる。特に、構成単位Cを適切に使用することで、重合体A3のTgを90℃以下に容易に調整することができる。
重合体A3は、構成単位Cを1種のみ含んでもよく、2種以上含んでいてもよい。
また、重合体A3中における構成単位Cの含有量は、1質量%〜70質量%が好ましく、5質量%〜60質量%がより好ましく、10質量%〜50質量%が更に好ましい。上記の数値範囲内であると、解像度及び密着性がより向上する。
上記紫外線吸収層における重合体A3の含有量は、回路配線形成用基板に対して低温かつ高速で貼り合わせた場合でも良好な密着性を発現させる観点から、重合体A2の紫外線吸収層の全固形分に対し、50質量%〜99.9質量%であることが好ましく、70質量%〜98質量%であることがより好ましい。
上記紫外線吸収層は、重合体成分として、既述の重合体A2又は重合体A3に加え、本開示における効果を損なわない範囲において、Tgが90℃より高い重合体(「他の重合体」と称する場合がある。)を更に含んでいてもよい。紫外線吸収層が他の重合体を含む場合、他の重合体の配合量は、全重合体成分中、50質量%以下であることが好ましく、30質量%以下であることがより好ましく、20質量%以下であることが更に好ましい。
紫外線吸収層を形成するための紫外線吸収層用組成物は、層を形成するための成分を溶剤に溶解した溶液として調製されることが好ましい。
紫外線吸収層を形成するための紫外線吸収層用組成物に使用される溶剤としては、公知の溶剤を用いることができる。溶剤としては、感光性樹脂組成物層において上述したものを好適に用いることができる。
紫外線吸収層を形成するために使用する溶剤は、1種単独で用いてもよく、2種を併用することがより好ましい。溶剤を2種以上使用する場合には、例えば、プロピレングリコールモノアルキルエーテルアセテート類とジアルキルエーテル類、ジアセテート類とジエチレングリコールジアルキルエーテル類、あるいは、エステル類とブチレングリコールアルキルエーテルアセテート類とを併用することが好ましい。
この場合、水だけでなく、炭素数1〜6のアルコール系溶剤を併用することが好ましい。炭素数1〜6のアルコール系溶剤を併用することで、乾燥が速くなり、表面張力が低下することで、高速塗布が可能となる。
上記紫外線吸収層は、必要に応じて公知の添加剤を含むことができる。
紫外線吸収層は、可塑性を改良する目的で、可塑剤を含有してもよい。なお、上記紫外線吸収層は、重合体A2又は重合体A3を含むことで可塑性に優れるため、可塑剤の含有は必須ではない。
紫外線吸収層に用いることができる可塑剤は、重合体A2又は重合体A3よりも重量平均分子量が小さいことが好ましい。
可塑剤の重量平均分子量は、可塑性付与の観点から500以上10,000未満が好ましく、700以上5,000未満がより好ましく、800以上4,000未満がより更に好ましい。
可塑剤は、重合体A2又は重合体A3と相溶して可塑性を発現する化合物であれば特に限定されない。
可塑剤としては、感光性樹脂組成物層において上述したものを好適に用いることができる。
紫外線吸収層が可塑剤を含む場合、1種のみを用いてもよく、2種以上を用いてもよい。
上記紫外線吸収層は、膜厚均一性の観点から界面活性剤を含有することが好ましい。
界面活性剤としては、感光性樹脂組成物層において上述したものを好適に用いることができる。
界面活性剤は、1種単独で用いてもよく、2種以上を併用してもよい。
紫外線吸収層における界面活性剤の添加量は、紫外線吸収層中の全固形分100質量部に対して、10質量部以下であることが好ましく、0.001質量部〜10質量部であることがより好ましく、0.01質量部〜3質量部であることが更に好ましい。
上記紫外線吸収層には、金属酸化物粒子、ヘテロ環状化合物以外の架橋剤、アルコキシシラン化合物、酸化防止剤、分散剤、酸増殖剤、現像促進剤、導電性繊維、着色剤、熱ラジカル発生剤、熱酸発生剤、紫外線吸収剤、増粘剤、及び、有機又は無機の沈殿防止剤などの公知の添加剤を更に含んでいてもよい。
その他の成分の好ましい態様については、特開2014−85643号公報の段落0165〜段落0184にそれぞれ記載があり、この公報の内容は本明細書に組み込まれる。
紫外線吸収層の厚みは、0.05μm〜2μmが好ましく、0.1μm〜1μmがより好ましく、0.1μm〜0.4μmが特に好ましい。紫外線吸収層の厚みが2μm以下であると、現像時に発生する紫外線吸収層の過剰な溶解を抑制することが可能となり、0.05μm以上であると、十分な紫外線吸収が可能となり、また、転写性も良好となり、レジストパターンの解像度が良好となり、パターン直線性の観点から好ましい。
各成分を所定の割合でかつ任意の方法で混合し、撹拌溶解して紫外線吸収層を形成するための紫外線吸収樹脂組成物を調製することができる。例えば、各成分を、それぞれ予め溶剤又は水に溶解又は分散させた液とした後、得られた液を所定の割合で混合して組成物を調製することもできる。以上の如くして調製した組成物は、孔径0.2μmのフィルター等を用いてろ過した後に、使用に供することもできる。
また、仮支持体S1上に感光性樹脂組成物を塗布し、乾燥させ、感光性樹脂組成物層を形成させた後に、その上に直接、紫外線吸収樹脂組成物を塗布し、乾燥させることで、本実施形態の感光性転写材料を得ることができる。塗布方法は特に限定されず、スリット塗布、スピン塗布、カーテン塗布、インクジェット塗布などの公知の方法で塗布することができる。
なお、仮支持体S1上に後述のその他の層を有する仮支持体S1とその他の層との積層体上に、感光性樹脂組成物層を塗布することもできる。
本開示に係る感光性転写材料は、上記感光性樹脂組成物層以外の層(以下、「その他の層」と称することがある)を有していてもよい。その他の層としては、コントラストエンハンスメント層、中間層、カバーフィルム、熱可塑性樹脂層等を挙げることができる。
本開示に係る感光性転写材料は、上記感光性樹脂組成物層に加え、コントラストエンハンスメント層を有することができる。
コントラストエンハンスメント層(Contrast Enhancement Layer;CEL)は、露光前には露光波長に対する吸収が大きいが、露光されるに伴って次第に吸収が小さくなる、すなわち、光の透過率が高くなる材料(光消色性色素成分と称する)を含有する層である。光消色性色素成分としては、ジアゾニウム塩、スチルバゾリウム塩、アリールニトロソ塩類等が知られている。被膜形成成分としては、フェノール系樹脂等が用いられる。
その他、コントラストエンハンスメント層としては、特開平6−97065号公報の段落0004〜段落0051、特開平6−332167号公報の段落0012〜段落0055、フォトポリマーハンドブック,フォトポリマー懇話会編,工業調査会(1989)、フォトポリマー・テクノロジー,山岡、永松編,(株)日刊工業新聞社(1988)に記載の材料を用いることができる。
上記感光性樹脂組成物層の上に、複数層を塗布する目的、及び塗布後の保存の際における成分の混合を防止する目的で、中間層を設けることができる。
中間層としては、特開2005−259138号公報の段落0084〜0087に記載の中間層を用いることができる。中間層としては、水又はアルカリ水溶液に分散又は溶解するものが好ましい。
中間層に用いられる材料としては、例えばポリビニルアルコール系樹脂、ポリビニルピロリドン系樹脂、セルロース系樹脂、アクリルアミド系樹脂、ポリエチレンオキサイド系樹脂、ゼラチン、ビニルエーテル系樹脂、ポリアミド樹脂、及びこれらの共重合体などの樹脂が挙げられる。中でも特に好ましいのはポリビニルアルコールとポリビニルピロリドンとの組み合わせである。
本開示に係る感光性転写材料は、転写性の観点から、上記仮支持体と上記感光性樹脂組成物層との間に、熱可塑性樹脂層を有していてもよい。
また、本開示に係る感光性転写材料は、上記感光性樹脂組成物層を保護する目的でカバーフィルムを有していてもよい。
熱可塑性樹脂層の好ましい態様については特開2014−85643号公報の段落0189〜段落0193、他の層の好ましい態様については特開2014−85643号公報の段落0194〜段落0196にそれぞれ記載があり、この公報の内容は本明細書に組み込まれる。
中でも、転写性の観点から、熱可塑性樹脂層が、アクリル樹脂及びスチレン/アクリル共重合体よりなる群から選ばれた少なくとも1種の熱可塑性樹脂を含むことが好ましい。
例えば、熱可塑性樹脂層及び中間層を有する本開示に係る感光性転写材料を作製する場合には、仮支持体上に、熱可塑性の有機高分子と添加剤とを溶解した溶解液(熱可塑性樹脂層用塗布液)を塗布し、乾燥させて熱可塑性樹脂層を設けた後、得られた熱可塑性樹脂層上に熱可塑性樹脂層を溶解しない溶剤に樹脂及び添加剤を加えて調製した調製液(中間層用塗布液)を塗布し、乾燥させて中間層を積層する。形成した中間層上に、更に、中間層を溶解しない溶剤を用いて調製した感光性樹脂組成物を塗布し、乾燥させて感光性樹脂組成物層を積層することによって、本開示に係る感光性転写材料を好適に作製することができる。
本開示に係るポジ型感光性転写材料の製造方法は、特に制限はないが、製造容易性及び製造適性の観点から、下記に示す第1の実施態様又は第2の実施態様であることが好ましく、第2の実施態様であることがより好ましい。
本開示に係るポジ型感光性転写材料の製造方法における第1の実施態様は、感光性樹脂組成物層上に、水性塗布液を用いて塗布及び乾燥して紫外線吸収層を形成する工程を含む。
また、本開示に係るポジ型感光性転写材料の製造方法における第2の実施態様は、仮支持体S1上に形成された感光性樹脂組成物層と、仮支持体S2上に形成された紫外線吸収層とを貼り合わせる工程を含む。
上記水性塗布液に用いられる有機紫外線吸収剤及び重合体A2、又は、重合体A3は、水溶性であることが好ましい。
また、上記水性塗布液は、重合体A2、又は、重合体A3の溶解を容易にするため、アルカリ性であることが好ましい。
上記水性塗布液のpHは、8以上14以下であることが好ましく、9以上12以下であることがより好ましい。
また、上記水性塗布液に用いられる塩基性化合物は、特に制限はなく、公知の塩基性化合物を用いることができるが、得られる紫外線吸収層への残留を抑制する観点から、アンモニアであることが好ましい。
上記水性塗布液は、有機紫外線吸収剤等の水性塗布液への溶解性を向上させる観点から、アルコール化合物等の水性有機溶剤を含むことが好ましい。
上記水性塗布液における水及び水性有機溶剤の総含有量は、水性塗布液の全質量に対し、70質量%〜99.5質量%であることが好ましく、80質量%〜99質量%であることがより好ましい。
上記水性塗布液を用いた感光性樹脂組成物層上への塗布方法及び乾燥方法は、特に制限はなく、公知の方法を用いることができる。
仮支持体S1上への感光性樹脂組成物層の形成方法、及び、仮支持体S2上への紫外線吸収層の形成方法は、特に制限はなく、上述した方法を好適に用いることができる。
上記貼り合わせは、上記感光性樹脂組成物層と上記紫外線吸収層と接触させ、貼り合せればよく、公知の方法、例えば、公知のラミネート方法を用いることができる。
上記貼り合わせ時の温度は、特に制限はないが、40℃〜120℃であることが好ましく、60℃〜100℃であることが更に好ましい。
仮支持体S1及び仮支持体S2は、特に制限はなく、上述した仮支持体をそれぞれ好適に用いることができる。仮支持体S1及び仮支持体S2は、材質及び厚さがそれぞれ異なるものであってもよい。
本開示に係る感光性転写材料を用いた、回路配線の製造方法の第1の実施態様について説明する。
回路配線の製造方法の第1の実施態様は、
基板に対し、本開示に係る感光性転写材料の上記紫外線吸収層を上記基板に接触させて貼り合わせる工程(貼り合わせ工程)と、
上記貼り合わせる工程後の上記感光性転写材料の上記感光性樹脂組成物層をパターン露光する工程(露光工程)と、
上記露光する工程後の露光部を現像してパターンを形成する工程(現像工程)と、
上記パターンが配置されていない領域における基板をエッチング処理する工程(エッチング工程)と、をこの順に含む。
回路配線の製造方法の第1の実施態様における基板は、ガラス、シリコン、フィルムなどの基材自体が基板であってもよく、ガラス、シリコン、フィルムなどの基材上に、必要により導電層などの任意の層が設けられた基板であってもよい。
回路配線の製造方法の第1の実施態様によれば、基板表面に微細パターンを形成することができる。
基材、及び、互いに構成材料が異なる第1導電層及び第2導電層を含む複数の導電層とを有し、上記基材の表面上に、上記基材の表面から遠い順に、最表面層である上記第1導電層及び上記第2導電層が積層されている基板に対し、本開示に係る感光性転写材料の上記紫外線吸収層を上記第1導電層に接触させて貼り合わせる貼り合わせ工程と、
上記貼り合わせ工程後の上記感光性転写材料の上記仮支持体を介して上記感光性樹脂組成物層をパターン露光する第1露光工程と、
上記第1露光工程後の感光性樹脂組成物層から上記仮支持体を剥離した後、上記第1露光工程後の露光部を現像して第1パターンを形成する第1現像工程と、
上記第1パターンが配置されていない領域における上記複数の導電層のうち少なくとも上記第1導電層及び上記第2導電層をエッチング処理する第1エッチング工程と、
上記第1エッチング工程後の上記第1パターンを上記第1パターンとは異なるパターンでパターン露光する第2露光工程と、
上記第2露光工程後の上記第1パターンを現像して第2パターンを形成する第2現像工程と、
上記第2パターンが配置されていない領域における上記複数の導電層のうち少なくとも上記第1導電層をエッチング処理する第2エッチング工程と、をこの順に含む。上記第2の実施形態としては、国際公開第2006/190405号を参考にすることができ、この内容は本明細書に組み込まれる。
以下、第2の実施形態を元に、各工程の詳細について説明する。
貼り合わせ工程の一例を、図2(a)に概略的に示した。
まず、貼り合わせ工程では、基材22と、互いに構成材料が異なる第1導電層24及び第2導電層26を含む複数の導電層とを有し、基材22の表面上に、基材22の表面から遠い順に、最表面層である第1導電層24と第2導電層26とが積層されている基板(回路配線形成用基板)20に対し、上述した本開示に係る感光性転写材料100の紫外線吸収層14を第1導電層24に接触させて貼り合わせる。なお、このような回路配線形成用基板と感光性転写材料との貼り合わせを「転写」又は「ラミネート」と称する場合がある。
感光性転写材料の第1導電層上への貼り合わせ(転写)は、感光性転写材料の紫外線吸収層側を第1導電層の上に重ね、ロール等による加圧及び加熱することに行われることが好ましい。貼り合わせには、ラミネータ、真空ラミネータ、及び、より生産性を高めることができるオートカットラミネーター等の公知のラミネータを使用することができる。
回路配線形成用基板の基材が樹脂フィルムである場合は、ロールツーロールでの貼り合わせも行うこともできる。
基材上に複数の導電層が積層された基板は、基材がガラス基材又はフィルム基材であることが好ましく、フィルム基材であることがより好ましい。本開示に係る回路配線の製造方法は、タッチパネル用の回路配線である場合、基材がシート状樹脂組成物であることが特に好ましい。
また、基材は透明であることが好ましい。
基材の屈折率は、1.50〜1.52であることが好ましい。
基材は、ガラス基材等の透光性基材で構成されていてもよく、コーニング社のゴリラガラスに代表される強化ガラスなどを用いることができる。また、前述の透明基材としては、特開2010−86684号公報、特開2010−152809号公報及び特開2010−257492号公報に用いられている材料を好ましく用いることができる。
基材としてフィルム基材を用いる場合は、光学的に歪みがない基材、及び、透明度が高い基材を用いることがより好ましく、具体的な素材には、ポリエチレンテレフタレート(polyethylene terephthalate;PET)、ポリエチレンナフタレート、ポリカーボネート、トリアセチルセルロース、シクロオレフィンポリマーをあげることができる。
基材上に形成されている複数の導電層としては、一般的な回路配線又はタッチパネル配線に用いられる任意の導電層を挙げることができる。
導電層の材料としては、金属及び金属酸化物などを挙げることができる。
金属酸化物としては、ITO(Indium Tin Oxide)、IZO(Indium Zinc Oxide)、SiO2等を挙げることができる。金属としては、Al、Zn、Cu、Fe、Ni、Cr、Mo等を挙げることができる。
導電層としては、静電容量型タッチパネルに用いられる視認部のセンサーに相当する電極パターン又は周辺取り出し部の配線であることが好ましい。
基材の表面に導電層を有する基板である。導電層をパターンニングすることで回路配線とする。本例では、PETなどのフィルム基材に金属酸化物や金属などの複数の導電層が設けられたものであることが好ましい。
上記第1の実施態様においては露光工程が、上記第2の実施態様においては第1露光工程が行われる。露光工程(第1露光工程)の一例を、図2(b)に概略的に示した。
露光工程(第1露光工程)では、貼り合わせ工程後の感光性転写材料の仮支持体10を介して感光性樹脂組成物層12をパターン露光する。
本実施形態においてパターンの詳細な配置及び具体的サイズは特に限定されない。本実施形態により製造される回路配線を有する入力装置を備えた表示装置(例えばタッチパネル)の表示品質を高め、また、取り出し配線の占める面積をできるだけ小さくしたいことから、パターンの少なくとも一部(特にタッチパネルの電極パターン及び取り出し配線の部分)は100μm以下の細線であることが好ましく、70μm以下の細線であることが更に好ましい。
ここで、露光に使用する光源としては、感光性転写材料の露光された箇所が現像液に溶解しうる波長域の光(例えば、365nm、405nmなど)を照射できれば適宜選定して用いることができる。具体的には、超高圧水銀灯、高圧水銀灯、メタルハライドランプ等が挙げられる。
露光量としては、5mJ/cm2〜200mJ/cm2であることが好ましく、10mJ/cm2〜100mJ/cm2であることがより好ましい。
また、露光後にパターンの矩形性、直線性を向上させる目的で、現像前に熱処理を行うことも好ましい。いわゆるPEB(Post Exposure Bake)と呼ばれる工程により、露光時に感光性樹脂組成物層中で生じた定在波によるパターンエッジの荒れを低減することが可能である。
上記第1の実施態様においては現像工程が、上記第2の実施態様においては第1現像工程が行われる。現像工程(第1現像工程)の一例を、図2(c)に概略的に示した。
現像工程(第1現像工程)では、露光工程(第1露光工程)後の感光性樹脂組成物層12から仮支持体10を剥離した後、露光工程(第1露光工程)後の感光性樹脂組成物層12及び紫外線吸収層14を現像して第1パターン12A及び14Aを形成する。
パターン露光された感光性樹脂組成物層の現像は、現像液を用いて行うことができる。
現像液としては、感光性樹脂組成物層(好ましくは感光性樹脂組成物層及び紫外線吸収層)の露光部分を除去することができれば特に制限はなく、例えば、特開平5−72724号公報に記載の現像液など、公知の現像液を使用することができる。なお、現像液は感光性樹脂組成物層の露光部が溶解型の現像挙動をする現像液が好ましい。例えば、pKa=7〜13の化合物を0.05mol/L(リットル)〜5mol/Lの濃度で含むアルカリ水溶液系の現像液が好ましい。現像液は、更に、水と混和性を有する有機溶剤、界面活性剤等を含有してもよい。本実施形態において好適に用いられる現像液としては、例えば、国際公開第2015/093271号の段落0194に記載の現像液が挙げられる。
ポストベークの加熱は8.1kPa〜121.6kPaの環境下で行うことが好ましく、506.6kPa以上の環境下で行うことがより好ましい。一方、1114.6kPa以下の環境下で行うことがより好ましく、101.3kPa以下の環境下で行うことが特に好ましい。
ポストベークの温度は、80℃〜250℃であることが好ましく、110℃〜170℃であることがより好ましく、130℃〜150℃であることが特に好ましい。
ポストベークの時間は、1分〜30分であることが好ましく、2分〜10分であることがより好ましく、2分〜4分であることが特に好ましい。
ポストベークは、空気環境下で行っても、窒素置換環境下で行ってもよい。
上記第1の実施態様においてはエッチング工程が、上記第2の実施態様においては第1エッチング工程が行われる。エッチング工程(第1エッチング工程)の一例を、図2(d)に概略的に示した。
エッチング工程(第1エッチング工程)では、第1パターン12A及び14Aが配置されていない領域における複数の導電層のうち少なくとも第1導電層24及び第2導電層26をエッチング処理する。エッチングにより、同じパターンを有する第1導電層24A及び第2導電層26Aが形成される。
酸性タイプのエッチング液としては、塩酸、硫酸、フッ酸、リン酸等の酸性成分単独の水溶液、酸性成分と塩化第二鉄、フッ化アンモニウム、過マンガン酸カリウム等の塩の混合水溶液等が例示される。酸性成分は、複数の酸性成分を組み合わせた成分を使用してもよい。
アルカリ性タイプのエッチング液としては、水酸化ナトリウム、水酸化カリウム、アンモニア、有機アミン、テトラメチルアンモニウムハイドロオキサイドのような有機アミンの塩等のアルカリ成分単独の水溶液、アルカリ成分と過マンガン酸カリウム等の塩の混合水溶液等が例示される。アルカリ成分は、複数のアルカリ成分を組み合わせた成分を使用してもよい。
上記第2の実施態様においては第2露光工程が行われる。第2露光工程の一例を、図2(e)に概略的に示した。
第1エッチング工程後、第1エッチング工程後の第1パターン12A及び14Aを第1パターンとは異なるパターンでパターン露光する。
第2露光工程におけるパターン露光は、第1露光工程で用いたマスク30とはパターンが異なるマスク40を用いること以外は第1露光工程におけるパターン露光と同じ方法を適用することができる。
上記第2の実施態様においては第2現像工程が行われる。第2現像工程の一例を、図2(f)に概略的に示した。
第2現像工程では、第2露光工程後の第1パターン12A及び14Aを現像して第2パターン12B及び14Bを形成する。
現像により、第1パターンのうち第2露光工程において露光された部分が除去される。
なお、第2現像工程では、第1現像工程における現像と同じ方法を適用することができる。
上記第2の実施態様においては第2露光工程が行われる。第2エッチング工程の一例を、図2(g)に概略的に示した。
第2エッチング工程では、第2パターン12B及び14Bが配置されていない領域における複数の導電層のうち少なくとも第1導電層24Aをエッチング処理する。
第2エッチング工程では、所望のパターンに応じて、第1エッチング工程よりも少ない導電層を選択的にエッチングすることが好ましい。例えば、図2に示すように、感光性樹脂組成物層が配置されていない領域において第1導電層24Bのみを選択的にエッチングするエッチング液を用いてエッチングを行うことで、第1導電層を第2導電層のパターンとは異なるパターンにすることができる。
第2エッチング工程の終了後、少なくとも2種類のパターンの導電層24B,26Aを含む回路配線が形成される。
感光性樹脂組成物層除去工程の一例を、図2(h)に概略的に示した。
第2エッチング工程の終了後、第1導電層24B上の一部には第2パターン12B及び14Bが残存している。感光性樹脂組成物層が不要であれば、残存する全ての感光性樹脂組成物層の第2パターン12B及び紫外線吸収層の第2パターン14Bを除去すればよい。
感光性樹脂組成物層及び紫外線吸収層の除去方法としては、好ましくは30℃〜80℃、より好ましくは50℃〜80℃にて撹拌中の剥離液に感光性樹脂組成物層などを有する基材を1分〜30分間浸漬する方法が挙げられる。
上記第2の実施態様において、第1エッチング工程の後、第2露光工程の前に、第1パターン上に、光透過性を有する保護フィルム(不図示)を貼り付ける工程を更に有してもよい。
この場合、第2露光工程において、保護フィルムを介して第1パターンをパターン露光し、第2露光工程後、第1パターンから保護フィルムを剥離した後、第2現像工程を行うことが好ましい。
本開示に係る回路配線の製造方法は、基材上の複数の導電層の一部又は全ての可視光線反射率を低下させる処理をする工程を含むことが可能である。
可視光線反射率を低下させる処理としては、酸化処理などを挙げることができる。例えば、銅を酸化処理して酸化銅とすることで、黒化することにより、可視光線反射率を低下させることができる。
可視光線反射率を低下させる処理の好ましい態様については、特開2014−150118号公報の段落0017〜段落0025、並びに、特開2013−206315号公報の段落0041、段落0042、段落0048及び段落0058に記載があり、この公報の内容は本明細書に組み込まれる。
本開示に係る回路配線の製造方法は、形成した回路配線上に絶縁膜を形成する工程と、絶縁膜上に新たな導電層を形成する工程を含むことも好ましい。
このような構成により、上述の第二の電極パターンを、第一の電極パターンと絶縁しつつ、形成することができる。
絶縁膜を形成する工程については、特に制限はなく、公知の永久膜を形成する方法を挙げることができる。また、絶縁性を有する感光性材料を用いて、フォトリソグラフィにより所望のパターンの絶縁膜を形成してもよい。
絶縁膜上に新たな導電層を形成する工程については、特に制限はない。導電性を有する感光性材料を用いて、フォトリソグラフィにより所望のパターンの新たな導電層を形成してもよい。
本開示に係る回路配線は、本開示に係る回路配線の製造方法により製造された回路配線である。
本開示に係る回路基板は、本開示に係る回路配線の製造方法により製造された回路配線を有する基板である。
本開示に係る回路基板の用途は限定されないが、例えば、タッチパネル用回路基板であることが好ましい。
本開示に係る回路配線の製造方法により製造される回路配線を備えた装置として、入力装置が挙げられる。
本実施形態における入力装置は、静電容量型タッチパネルであることが好ましい。
本実施形態における表示装置は、本実施形態における入力装置を備えることが好ましい。本実施形態における表示装置は、有機EL表示装置、及び、液晶表示装置等の画像表示装置であることが好ましい。
本開示に係るタッチパネルは、本開示に係る回路配線の製造方法により製造された回路配線を少なくとも有するタッチパネルである。また、本開示に係るタッチパネルは、透明基板と、電極と、絶縁層又は保護層とを少なくとも有することが好ましい。
本開示に係るタッチパネル表示装置は、本開示に係る回路配線の製造方法により製造された回路配線を少なくとも有するタッチパネル表示装置であり、本開示に係るタッチパネルを有するタッチパネル表示装置であることが好ましい。
本開示に係るタッチパネル又はタッチパネル表示装置の製造方法は、本開示に係る回路配線の製造方法を含むことが好ましい。
本開示に係るタッチパネル又はタッチパネル表示装置の製造方法は、感光性転写材料の製造方法により得られた感光性転写材料の上記感光性層を上記基板に接触させて貼り合わせる工程と、上記貼り合わせる工程後の上記感光性転写材料の上記感光性層をパターン露光する工程と、上記露光する工程後の感光性層を現像してパターンを形成する工程と、上記パターンが配置されていない領域における基板をエッチング処理する工程と、をこの順に含むことが好ましい。各工程の詳細は、上述の回路配線の製造方法における各工程の詳細と同義であり、好ましい態様も同様である。
本開示に係るタッチパネル及び本開示に係るタッチパネル表示装置のおける検出方法としては、抵抗膜方式、静電容量方式、超音波方式、電磁誘導方式、及び、光学方式など公知の方式いずれでもよい。中でも、静電容量方式が好ましい。
タッチパネル型としては、いわゆる、インセル型(例えば、特表2012−517051号公報の図5、図6、図7、図8に記載のもの)、いわゆる、オンセル型(例えば、特開2013−168125号公報の図19に記載のもの、特開2012−89102号公報の図1や図5に記載のもの)、OGS(One Glass Solution)型、TOL(Touch−on−Lens)型(例えば、特開2013−54727号公報の図2に記載のもの)、その他の構成(例えば、特開2013−164871号公報の図6に記載のもの)、各種アウトセル型(いわゆる、GG、G1・G2、GFF、GF2、GF1、G1Fなど)を挙げることができる。
本実施形態のタッチパネル及び本実施形態のタッチパネル表示装置としては、『最新タッチパネル技術』(2009年7月6日、(株)テクノタイムズ社発行)、三谷雄二監修、“タッチパネルの技術と開発”、シーエムシー出版(2004,12)、FPD International 2009 Forum T−11講演テキストブック、Cypress Semiconductor Corporation アプリケーションノートAN2292等に開示されている構成を適用することができる。
以下の合成例において、以下の略語はそれぞれ以下の化合物を表す。
ATHF:2−テトラヒドロフラニルアクリレート(合成品)
MATHF:2−テトラヒドロフラニルメタクリレート(合成品)
AA:アクリル酸(東京化成工業(株)製)
MAA:メタクリル酸(東京化成工業(株)製)
MMA:メチルメタクリレート(東京化成工業(株)製)
EA:エチルアクリレート(東京化成工業(株)製)
CHA:アクリル酸シクロヘキシル(東京化成工業(株)製)
CHMA:シクロヘキシルメタクリレート(東京化成工業(株)製)
UV1:2−[3−(2H−1,2,3−ベンゾトリアゾール−2−イル)−4−ヒドロキシフェニル]エチルメタクリレート(新中村化学工業(株)製)
UV2:2−[2−(2−ヒドロキシ−4−オクチルオキシフェニル)−2H−1,2,3−ベンゾトリアゾール−5−イルオキシ]エチルメタクリレート(新中村化学工業(株)製)
PGMEA(プロピレングリコールモノメチルエーテルアセテート):(昭和電工(株)製)
V−601:ジメチル 2,2’−アゾビス(2−メチルプロピオネート)(和光純薬工業(株)製)
3つ口フラスコにアクリル酸(72.1g、1.0mol)、ヘキサン(72.1g)を加え20℃に冷却した。カンファースルホン酸(7.0mg、0.03mmol)、2−ジヒドロフラン(77.9g、1.0mol)を滴下した後に、20℃±2℃で1.5時間撹拌した後、35℃まで昇温して2時間撹拌した。ヌッチェにキョーワード200(水酸化アルミニウム吸着剤、協和化学工業(株)製)、キョーワード1000(ハイドロタルサイト系吸着剤、協和化学工業(株)製)の順に敷き詰めた後、反応液をろ過することでろ過液を得た。得られたろ過液にヒドロキノンモノメチルエーテル(MEHQ、1.2mg)を加えた後、40℃で減圧濃縮することで、アクリル酸テトラヒドロフラン−2−イル(ATHF)140.8gを無色油状物として得た(収率99.0%)。
3つ口フラスコにメタクリル酸(86.1g、1.0mol)、ヘキサン(86.1g)を加え20℃に冷却した。カンファースルホン酸(7.0mg、0.03mmol)、2−ジヒドロフラン(70.1g、1.0mol)を滴下した後に、20℃±2℃で1.5時間撹拌した後、35℃まで昇温して2時間攪拌した。ヌッチェにキョーワード200、キョーワード1000の順に敷き詰めた後、反応液をろ過することでろ過液を得た。得られたろ過液にMEHQ(1.2mg)を加えた後、40℃で減圧濃縮することで、メタクリル酸テトラヒドロフラン−2−イル(MATHF)156.2gを無色油状物として得た(収率98.0%)。
3つ口フラスコにPGMEA(75.0g)を入れ、窒素雰囲気下において90℃に昇温した。MATHF(25.0g)、MAA(10.0g)、CHMA(35.0g)、CHA(30.0g)、V−601(4.1g)、PGMEA(75.0g)を加えた溶液を、90℃±2℃に維持した3つ口フラスコ溶液中に2時間かけて滴下した。滴下終了後,90℃±2℃にて2時間撹拌することで、重合体A−1(固形分濃度40.0%)を得た。
モノマーの種類等を下記表に示す通りに変更し、その他の条件については、A−1と同様の方法で合成した。重合体の固形分濃度は40質量%とした。表1に記載のモノマーの使用量は、得られる重合体における対応する構成単位の質量%で示している。
B−1:下記に示す構造の化合物(特開2013−047765号公報の段落0227に記載の化合物であり、段落0204に記載の方法に従って合成した。)
C−1:2,2’,4,4’−テトラヒドロキシベンゾフェノン(東京化成工業(株)製)、下記に示す構造の化合物
D−1:川崎化成工業(株)製アントラキュアー(登録商標)UVS−1331、下記化合物(なお、Buはブチル基を表す。)
E−1:下記に示す構造の化合物
F−1:下記に示す構造の化合物
<感光性樹脂組成物の調製>
以下の組成で調合し、孔径0.2μmのポリテトラフルオロエチレン製フィルターで濾過することで、感光性樹脂組成物を得た。
PGMEA:424.5質量部
重合体A1−1:237.0質量部
光酸発生剤B−1:5.0質量部
界面活性剤E−1:0.1質量部
塩基性化合物F−1:0.1質量部
以下の組成で調合し、孔径0.2μmのポリテトラフルオロエチレン製フィルターで濾過することで、紫外線吸収層用組成物を得た。
PGMEA:2,280.0質量部
重合体A2−1:200.0質量部
有機紫外線吸収剤C−1:20.0質量部
界面活性剤E−1:0.1質量部
仮支持体S1となる厚さ25μmのポリエチレンテレフタレートフィルムの上に感光性樹脂組成物を、スリット状ノズルを用いて乾燥膜厚が3.0μmとなるように塗布した。その後、100℃のコンベクションオーブンで2分間乾燥させ、感光性樹脂組成物層を有するフィルムAを作製した。
また、仮支持体S2となる16μmのポリエチレンテレフタレートフィルムの上に、紫外線吸収層用組成物を、スリット状ノズルを用いて乾燥膜厚が0.2μmとなるように塗布した。その後、100℃のコンベクションオーブンで2分間乾燥させ、紫外線吸収層を有するフィルムBを作製した。
最後にフィルムAの感光性樹脂組成物層とフィルムBの紫外線吸収層とを合わせる形でフィルムAとフィルムBとを90℃、5m/min.の速度で熱ラミネートして、感光性転写材料を作製した。
使用する樹脂、光酸発生剤、有機紫外線吸収剤及び重合体A2又は重合体A3、並びに、膜厚が表2の通りとなるように各組成物の組成、及び、各層の塗布厚を変更した以外は、実施例1と同様にして、感光性転写材料を作製した。
以下の感光性樹脂組成物を用いた以外は、実施例11と同様にして、感光性転写材料を作製した。
以下の組成で調合し、孔径0.2μmのポリテトラフルオロエチレン製フィルターで濾過することで、感光性樹脂組成物を得た。
PGMEA:424.5質量部
重合体A1−1:224.5質量部
光酸発生剤B−4:5.0質量部
増感剤D−1:5.0質量部
界面活性剤E−1:0.1質量部
塩基性化合物F−1:0.1質量部
以下の紫外線吸収層用樹脂組成物を用いた以外は、実施例1と同様にして、感光性転写材料を作製した。
以下の組成で調合し、孔径0.2μmのポリテトラフルオロエチレン製フィルターで濾過することで、紫外線吸収層用組成物を得た。
PGMEA:2,250.0質量部
表2に記載の重合体A2−5又は重合体A2−6:250.0質量部
界面活性剤E−1:0.1質量部
以下の紫外線吸収層用組成物を用いた以外は、実施例1と同様にして、感光性転写材料を作製した。
以下の組成で調合し、孔径0.2μmのポリテトラフルオロエチレン製フィルターで濾過することで、紫外線吸収層用組成物を得た。
PGMEA:2,216.7質量部
重合体A2−3:150.0質量部
有機紫外線吸収剤C−5:133.3質量部
界面活性剤E−1:0.1質量部
以下の組成で調合し、孔径0.2μmのポリテトラフルオロエチレン製フィルターで濾過することで、紫外線吸収層用組成物を得た。
アンモニア水(アンモニア10質量%含有):49.0質量部
重合体A2−3(ドライアップしたもの):1.6質量部
メタノール:49.0質量部
有機紫外線吸収剤C−1:0.4質量部
メガファックF444(DIC(株)製、界面活性剤):0.1質量部
仮支持体となる厚さ25μmのポリエチレンテレフタレートフィルムの上に、感光性樹脂組成物(実施例1で使用したものと同じ)を、スリット状ノズルを用いて乾燥膜厚が3.0μmとなるように塗布した。その後、100℃のコンベクションオーブンで2分間乾燥させ、次いで、紫外線吸収層用組成物を、スリット状ノズルを用いて乾燥膜厚が0.2μmとなるように塗布した。その後、100℃のコンベクションオーブンで2分間乾燥させ、最後にカバーフィルムとしてポリエチレンフィルム(トレデガー社製、OSM−N)を圧着して感光性転写材料を作製した。
重合体A2−3及び有機紫外線吸収剤の代わりに、重合体A2−5又はA2−6を2.0質量部と使用した以外は、実施例22と同様にして、感光性転写材料を作製した。
<紫外線吸収層用組成物の調製>
以下の組成で調合し、0.1μm径のジルコニアビーズとジルコニアビーズ:液=1:2の質量比で混合した液をペイントシェーカーを用いて室温(25℃)で2時間分散し、孔径1μmのポリテトラフルオロエチレン製フィルターで濾過することで、紫外線吸収層用組成物を得た。
PGMEA:2,280.0質量部
重合体A2−2:200.0質量部
カーボンブラック(#2600、三菱ケミカル(株)製):20.0質量部
界面活性剤E−1:0.1質量部
仮支持体S1となる厚さ25μmのポリエチレンテレフタレートフィルムの上に感光性樹脂組成物(実施例1で使用したものと同じ)を、スリット状ノズルを用いて乾燥膜厚が3.0μmとなるように塗布した。その後、100℃のコンベクションオーブンで2分間乾燥させフィルムAを作製した。
また、仮支持体S2となる16μmのポリエチレンテレフタレートフィルムの上に、紫外線吸収層用組成物をスリット状ノズルを用いて乾燥膜厚が0.2μmとなるように塗布した。その後、100℃のコンベクションオーブンで2分間乾燥させフィルムBを作製した。
最後にフィルムAの感光性樹脂組成物層とフィルムBの紫外線吸収層とを合わせる形でフィルムAとフィルムBとを90℃、5m/min.の速度で熱ラミネートして感光性転写材料を作製した。
<紫外線吸収層用組成物の調製>
以下の組成で調合し、0.1μm径のジルコニアビーズとジルコニアビーズ:液=1:2の質量比で混合した液をペイントシェーカーを用いて室温で2時間分散し、口径1μmのポリテトラフルオロエチレン製フィルターで濾過することで、紫外線吸収層用組成物を得た。
PGMEA:2325.0質量部
重合体A2−2:125.0質量部
カーボンブラック(#2600、三菱ケミカル(株)製):50.0質量部
界面活性剤E−1:0.1質量部
仮支持体となる厚さ25μmのポリエチレンテレフタレートフィルムの上に、感光性樹脂組成物(実施例1で使用したものと同じ)を、スリット状ノズルを用いて乾燥膜厚が3.0μmとなるように塗布した。その後、100℃のコンベクションオーブンで2分間乾燥させ、次いで、紫外線吸収層用組成物(比較例6で使用したもの)を、スリット状ノズルを用いて乾燥膜厚が0.2μmとなるように塗布した。その後、100℃のコンベクションオーブンで2分間乾燥させ、最後にカバーフィルムとしてポリエチレンフィルム(トレデガー社製、OSM−N)を圧着して感光性転写材料を作製した。
厚さ188μmのPETフィルム上に厚さ500nmでスパッタ法にて銅層を作製した銅層付きポリエチレンテレフタレート(PET)基板を使用した。
作製した感光性転写材料を50cm角にカットし、仮支持体S2を有する場合は仮支持体S2を剥がして、ロール温度90℃、線圧0.6MPa、線速度3.6m/min.のラミネート条件で銅層付きPET基板にラミネートした。紫外線吸収層が銅層に密着する面積を目視評価し、紫外線吸収層が密着した面積/カットした転写材料の面積(%)により密着した面積割合を求めた。
5:95%以上
4:90%以上95%未満
3:85%以上90%未満
2:80%以上85%未満
1:80%未満
作製した感光性転写材料を、線圧0.6MPa、線速度(ラミネート速度)3.6m/minのラミネート条件で銅層付きPET基板にラミネートした。なお、ロール温度90℃で転写性評価が4以下の場合、転写性評価が5判定になるまでラミロール温度を上げて試料を作製した。
仮支持体S1を剥離せずに線幅3〜20μmのラインアンドスペースパターン(Duty比 1:1)マスクを介して超高圧水銀灯で露光後、30分引き置いて仮支持体(仮支持体S1)を剥離して現像した。現像は28℃の1.0%炭酸ナトリウム水溶液を用い、シャワー現像で40秒行った。上記方法にて10μmのラインアンドスペースパターンを形成し、ライン幅とスペース幅の比が1:1になる露光量を求め、その露光量でパターン形成した試料を銅エッチング液(Cu−02:関東化学(株)製)により23℃で30秒エッチングし、PGMEAを用いてレジスト剥離して得た、銅配線の10μmのラインアンドスペースパターンのLWR(Line Width Roughness、線幅を250点計測した値の標準偏差)を求めることで直線性の評価を行った。3以上が実用可能レベルである。
5:LWRが140nm未満
4:LWRが140nm以上180nm未満
3:LWRが180nm以上200nm未満
2:LWRが200nm以上250nm未満
1:LWRが250nm以上
CB:カーボンブラック(#2600、三菱ケミカル(株)製)
100μm厚PET基材上に、第2層の導電性層として酸化インジウムスズ(ITO)をスパッタリングで150nm厚にて成膜し、その上に第1層の導電性層として銅を真空蒸着法で200nm厚にて成膜して、回路形成基板とした。
銅層上に実施例1で得た感光性転写材料の仮支持体S2を剥離し、ラミネートした(線圧0.8MPa、線速度3.0m/min、ロール温度90℃)。仮支持体S1を剥離せずに一方向に導電性層パッドが連結された構成を持つ図3に示すパターン(以下、「パターンA」とも称する。)を設けたフォトマスクを用いてコンタクトパターン露光した。
なお、図3に示すパターンAは、実線部SL及びグレー部Gが遮光部であり、点線部DLはアライメント合わせの枠を仮想的に示したものである。
その後仮支持体S1を剥離し、現像、水洗を行ってパターンAを得た。次いで銅エッチング液(関東化学(株)製Cu−02)を用いて銅層をエッチングした後、ITOエッチング液(関東化学(株)製ITO−02)を用いてITO層をエッチングすることで、銅(実線部SL)とITO(グレー部G)とが共にパターンAで描画された基板を得た。
なお、図4に示すパターンBは、グレー部Gが遮光部であり、点線部DLはアライメント合わせの枠を仮想的に示したものである。
その後、Cu−02を用いて銅層をエッチングし、残った感光性樹脂組成物層を剥離液(10質量%水酸化ナトリウム水溶液)を用いて剥離し、回路配線基板を得た。
これにより、回路配線基板を得た。顕微鏡で観察したところ、剥がれや欠けなどは無く、きれいなパターンであった。
Claims (10)
- 仮支持体上に、感光性樹脂組成物層、及び、紫外線吸収層を有し、
前記感光性樹脂組成物層が、酸分解性基で保護された酸基を有する構成単位を有する重合体A1と、光酸発生剤とを含み、
前記紫外線吸収層が、有機紫外線吸収剤と重合体A2とを含むか、又は、紫外線吸収能を有する重合体A3を含み、
前記紫外線吸収層に含まれる、前記重合体A2のガラス転移温度又は前記重合体A3のガラス転移温度が、90℃以下である
ポジ型感光性転写材料。 - 前記重合体A1のガラス転移温度が、前記重合体A2のガラス転移温度又は前記重合体A3のガラス転移温度よりも高い請求項1に記載のポジ型感光性転写材料。
- 前記重合体A1のガラス転移温度が、前記重合体A2のガラス転移温度又は前記重合体A3のガラス転移温度よりも10℃以上50℃以下高い温度である請求項1又は請求項2に記載のポジ型感光性転写材料。
- 前記重合体A1のガラス転移温度が、120℃以下である請求項1〜請求項3のいずれか1項に記載のポジ型感光性転写材料。
- 前記重合体A2のガラス転移温度又は前記重合体A3のガラス転移温度が、−20℃以上60℃以下である請求項1〜請求項4のいずれか1項に記載のポジ型感光性転写材料。
- 前記紫外線吸収層が、紫外線吸収能を有する重合体A3を含む請求項1〜請求項5のいずれか1項に記載のポジ型感光性転写材料。
- 感光性樹脂組成物層上に、水性塗布液を用いて塗布及び乾燥して紫外線吸収層を形成する工程を含む請求項1〜請求項6のいずれか1項に記載のポジ型感光性転写材料の製造方法。
- 前記水性塗布液が、アルカリ性である請求項7に記載のポジ型感光性転写材料の製造方法。
- 仮支持体S1上に形成された感光性樹脂組成物層と、仮支持体S2上に形成された紫外線吸収層とを貼り合わせる工程を含む請求項1〜請求項6のいずれか1項に記載のポジ型感光性転写材料の製造方法。
- 基板に対し、請求項1〜請求項6のいずれか1項に記載のポジ型感光性転写材料の前記紫外線吸収層を前記基板に接触させて貼り合わせる工程と、
前記貼り合わせる工程後の前記感光性転写材料の前記感光性樹脂組成物層をパターン露光する工程と、
前記露光する工程後の露光部を現像してパターンを形成する工程と、
前記パターンが配置されていない領域における前記基板をエッチング処理する工程と、をこの順に含む
回路配線の製造方法。