JPS62295950A - ポリカ−ボネ−ト樹脂組成物 - Google Patents
ポリカ−ボネ−ト樹脂組成物Info
- Publication number
- JPS62295950A JPS62295950A JP13912786A JP13912786A JPS62295950A JP S62295950 A JPS62295950 A JP S62295950A JP 13912786 A JP13912786 A JP 13912786A JP 13912786 A JP13912786 A JP 13912786A JP S62295950 A JPS62295950 A JP S62295950A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- parts
- polycarbonate resin
- butadiene
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
3、発明の詳細な説明
〔産業上の利用分野〕
本発明はポリカーボネート樹脂組成物に関するものであ
る。さらに詳しくいえば、本発明は、例えば自動車バン
パーなどの自動車分野成形品や家電分野成形品などの材
料として好適な、優れた熱安定性、低温耐衝撃性、漆黒
性、耐溶剤性などを有するポリカーボネート樹脂組成物
に関するものである。
る。さらに詳しくいえば、本発明は、例えば自動車バン
パーなどの自動車分野成形品や家電分野成形品などの材
料として好適な、優れた熱安定性、低温耐衝撃性、漆黒
性、耐溶剤性などを有するポリカーボネート樹脂組成物
に関するものである。
従来、ポリカーボネート樹脂は引張強度、曲げ強度、衝
撃強度などの機械的強度や耐熱性などに優れる上に、成
形精度の良好なエンジニアリング樹脂として知られてお
り、各種分野において幅広く用いられているが、低温耐
衝撃性、耐溶剤性、流動性に劣るなどの欠点を有してい
る。
撃強度などの機械的強度や耐熱性などに優れる上に、成
形精度の良好なエンジニアリング樹脂として知られてお
り、各種分野において幅広く用いられているが、低温耐
衝撃性、耐溶剤性、流動性に劣るなどの欠点を有してい
る。
ポリカーボネート樹脂のこのような欠点を改良するため
に、このポリカーボネート樹脂にアクリル系ゴムを配合
した組成物が知られている(特公昭43−18611号
公報、同4B−29308号公報、特開昭53−348
53号公報、同56−143239号公報)。
に、このポリカーボネート樹脂にアクリル系ゴムを配合
した組成物が知られている(特公昭43−18611号
公報、同4B−29308号公報、特開昭53−348
53号公報、同56−143239号公報)。
しかしながら、これらの組成物においては、耐溶剤性お
よび流動性はある程度改良されているものの、熱安定性
の低下、漆黒性の低下(着色外観がバール状になる)、
射出成形時の層状剥離などの問題があり、用途が制限さ
れるのを免れない。
よび流動性はある程度改良されているものの、熱安定性
の低下、漆黒性の低下(着色外観がバール状になる)、
射出成形時の層状剥離などの問題があり、用途が制限さ
れるのを免れない。
本発明の目的は、このような従来のアクリル系ゴムを配
合したポリカーボネート樹脂組成物が有する欠点を改良
し、熱安定性、低温耐衝撃性、漆黒性、耐溶剤性などに
優れる上に、射出成形時に層状剥離が生じることがない
など、優れた特徴を有するポリカーボネート樹脂組成物
を提供することにある。
合したポリカーボネート樹脂組成物が有する欠点を改良
し、熱安定性、低温耐衝撃性、漆黒性、耐溶剤性などに
優れる上に、射出成形時に層状剥離が生じることがない
など、優れた特徴を有するポリカーボネート樹脂組成物
を提供することにある。
本発明者らは、このような優れた特徴を有するポリカー
ボネート樹脂組成物を開発するために鋭意研究を重ねた
結果、ポリカーボネート樹脂に、特定の組成を有するア
クリレート・ブタジエン系グラフト共重合体を所定の割
合で配合することにより、その目的を達成しうろことを
見出し、この知見に基づいて本発明を完成するに至った
。
ボネート樹脂組成物を開発するために鋭意研究を重ねた
結果、ポリカーボネート樹脂に、特定の組成を有するア
クリレート・ブタジエン系グラフト共重合体を所定の割
合で配合することにより、その目的を達成しうろことを
見出し、この知見に基づいて本発明を完成するに至った
。
すなわち、本発明は、(A)ポリカーボネート樹脂10
0重量部に対し、(B)(イ)アクリル酸エステル55
〜95重量%とブタジェン45〜5重量%とからなる共
重合体100重量部の存在下に、(ロ)アクリル酸エス
テル、メタクリル酸エステル、芳香族モノビニル化合物
およびシアン化ビニル化合物の中から選ばれたビニル系
単量体の1種または2種以上20〜100重量部および
、(ハ)多官能性ビニル単量体0〜5重量部を重合させ
てなるアクリレート・ブタジエン系グラフト共重合体1
〜80重量部を配合したことを特徴とするポリカーボネ
ート樹脂組成物を提供するものである。
0重量部に対し、(B)(イ)アクリル酸エステル55
〜95重量%とブタジェン45〜5重量%とからなる共
重合体100重量部の存在下に、(ロ)アクリル酸エス
テル、メタクリル酸エステル、芳香族モノビニル化合物
およびシアン化ビニル化合物の中から選ばれたビニル系
単量体の1種または2種以上20〜100重量部および
、(ハ)多官能性ビニル単量体0〜5重量部を重合させ
てなるアクリレート・ブタジエン系グラフト共重合体1
〜80重量部を配合したことを特徴とするポリカーボネ
ート樹脂組成物を提供するものである。
本発明において(A)成分として用いるポリカーボネー
ト樹脂は、一般式、 (式中のZは単結合、エーテル結合あるいは炭素数1〜
8のアルキレン基、炭素数2〜8のアルキリデン基、炭
素数5〜15のシクロアルキレン基、炭素数5〜15の
シクロアルキリデン基、スルホニル基、チオニル基、カ
ルボニル基、または式、CHs CH。
ト樹脂は、一般式、 (式中のZは単結合、エーテル結合あるいは炭素数1〜
8のアルキレン基、炭素数2〜8のアルキリデン基、炭
素数5〜15のシクロアルキレン基、炭素数5〜15の
シクロアルキリデン基、スルホニル基、チオニル基、カ
ルボニル基、または式、CHs CH。
で示される基、Rは水素原子、塩素原子、臭素原子また
は炭素数1〜8の飽和アルキル基、mは0または1〜4
の整数である) で表される構造単位を有する重合体である。
は炭素数1〜8の飽和アルキル基、mは0または1〜4
の整数である) で表される構造単位を有する重合体である。
このポリカーボネート樹脂は溶剤法、すなわち塩化メチ
レンなどの溶剤中で公知の酸受容体、分子量調整剤の存
在下、二価フェノールとホスゲンのようなカーボネート
前駆体との反応または二価フェノールとジフェニルカー
ボネートのようなカーボネート前駆体とのエステル交換
反応によって製造することができる。
レンなどの溶剤中で公知の酸受容体、分子量調整剤の存
在下、二価フェノールとホスゲンのようなカーボネート
前駆体との反応または二価フェノールとジフェニルカー
ボネートのようなカーボネート前駆体とのエステル交換
反応によって製造することができる。
ここで、好適に使用しうる二価フェノールとしてはビス
フェノール類があり、特に2,2−ビス(4−ヒドロキ
シフェニル)プロパン(ビスフェノールA)が好ましい
。また、ビスフェノールAの一部または全部を他の二価
フェノールで置換したものであってもよい。ビスフェノ
ールA以外の二価フェノールとしては、例えばビスフェ
ノールA以外のビス(4−ヒドロキシフェニル)アルカ
ン、ハイドロキノン、4.4′−ジヒドロキシジフェニ
ル、ビス(4−ヒドロキシフェニル)シクロアルカン、
ビス(4−ヒドロキシフェニル)スルフィド、ビス(4
−ヒドロキシフェニル)スルホン、ビス(4−ヒドロキ
シフェニル)スルホキシド、ビス(4−ヒドロキシフェ
ニル)エーテルのようは化合物またはビス(3,5−ジ
ブロモ−4−ヒドロキシフェニル)プロパン、ビス(3
゜5−ジクロロ−4−ヒドロキシフェニル)プロパンの
ようなハロゲン化ビスフェノール類を挙げることができ
る、これら二価フェノールは二価フェノールのホモポリ
マーまたは2種以上のコポリマーもしくはブレンド物で
あってもよい。さらに、本発明で用いるポリカーボネー
ト樹脂は多官能性芳香族化合物を二価フェノールまたは
カーボネート前駆体あるいはその両方と反応させた熱可
塑性ランダム分枝ポリカーボネートであってもよい。
フェノール類があり、特に2,2−ビス(4−ヒドロキ
シフェニル)プロパン(ビスフェノールA)が好ましい
。また、ビスフェノールAの一部または全部を他の二価
フェノールで置換したものであってもよい。ビスフェノ
ールA以外の二価フェノールとしては、例えばビスフェ
ノールA以外のビス(4−ヒドロキシフェニル)アルカ
ン、ハイドロキノン、4.4′−ジヒドロキシジフェニ
ル、ビス(4−ヒドロキシフェニル)シクロアルカン、
ビス(4−ヒドロキシフェニル)スルフィド、ビス(4
−ヒドロキシフェニル)スルホン、ビス(4−ヒドロキ
シフェニル)スルホキシド、ビス(4−ヒドロキシフェ
ニル)エーテルのようは化合物またはビス(3,5−ジ
ブロモ−4−ヒドロキシフェニル)プロパン、ビス(3
゜5−ジクロロ−4−ヒドロキシフェニル)プロパンの
ようなハロゲン化ビスフェノール類を挙げることができ
る、これら二価フェノールは二価フェノールのホモポリ
マーまたは2種以上のコポリマーもしくはブレンド物で
あってもよい。さらに、本発明で用いるポリカーボネー
ト樹脂は多官能性芳香族化合物を二価フェノールまたは
カーボネート前駆体あるいはその両方と反応させた熱可
塑性ランダム分枝ポリカーボネートであってもよい。
本発明に用いるポリカーボネート樹脂は、機械的強度お
よび成形性の点から、その粘度平均分子量が10,00
0〜100.000のものが好ましく、特に20,00
0〜40.000のものが好適である。
よび成形性の点から、その粘度平均分子量が10,00
0〜100.000のものが好ましく、特に20,00
0〜40.000のものが好適である。
本発明において(B)成分として用いるアクリレート・
ブタジエン系グラフト共重合体は、(イ)アクリル酸エ
ステル55〜95重量%とブタシュフ45〜5重景%と
からなる共重合体100重量部の存在下に、(ロ)アク
リル酸エステル、メタクリル酸エステル、芳香族モノビ
ニル化合物およびシアン化ビニル化合物の中から選ばれ
たビニル系単量体の1種または2種以上20〜100重
量部を重合させたもの、あるいはこのビニル系単量体の
1種薫たは2種以上20〜100重量部および(ハ)多
官能性ビニル単量体5重量部以下を重合させたものであ
る。
ブタジエン系グラフト共重合体は、(イ)アクリル酸エ
ステル55〜95重量%とブタシュフ45〜5重景%と
からなる共重合体100重量部の存在下に、(ロ)アク
リル酸エステル、メタクリル酸エステル、芳香族モノビ
ニル化合物およびシアン化ビニル化合物の中から選ばれ
たビニル系単量体の1種または2種以上20〜100重
量部を重合させたもの、あるいはこのビニル系単量体の
1種薫たは2種以上20〜100重量部および(ハ)多
官能性ビニル単量体5重量部以下を重合させたものであ
る。
このアクリレート・ブタジエン系グラフト共電るポリカ
ーボネート樹脂組成物の熱安定性が低く、一方95重量
%を越えると低温耐衝撃性が低下する。また、(ロ)成
分のビニル系単量体の使用量が、(イ)成分の共重合体
100重量部に対して、20重量部未満では得られるグ
ラフト共重合体の樹脂組成物における分散性が悪くて、
該樹脂組成物の漆黒性および外観が不良となり、一方1
00重量部を越えると該樹脂組成物の耐衝撃性が低下す
る。さらに; (ハ)成分の多官能性ビニル単量体は該
樹脂組成物の低温耐衝撃性をさらに向上させるためのも
のであるが、(イ)成分の共重合体100重量部に対し
て、5重量部より多く用いても低温耐衝撃性は向上せず
、特に2重量部以下の使用量が好ましい。
ーボネート樹脂組成物の熱安定性が低く、一方95重量
%を越えると低温耐衝撃性が低下する。また、(ロ)成
分のビニル系単量体の使用量が、(イ)成分の共重合体
100重量部に対して、20重量部未満では得られるグ
ラフト共重合体の樹脂組成物における分散性が悪くて、
該樹脂組成物の漆黒性および外観が不良となり、一方1
00重量部を越えると該樹脂組成物の耐衝撃性が低下す
る。さらに; (ハ)成分の多官能性ビニル単量体は該
樹脂組成物の低温耐衝撃性をさらに向上させるためのも
のであるが、(イ)成分の共重合体100重量部に対し
て、5重量部より多く用いても低温耐衝撃性は向上せず
、特に2重量部以下の使用量が好ましい。
前記(イ)成分共重合体のアクリル酸エステルとしては
、例えばエチルアクリレート、°ブチルアクリレート、
2−エチルへキシルアクリレート、n−オクチルアクリ
レート、イソノニルアクリレート、メトキシエチルアク
リレート、ヒドロキシエチルアクリレートなどが挙げら
れ、これらの1種または2種以上を混合して使用しても
よい。
、例えばエチルアクリレート、°ブチルアクリレート、
2−エチルへキシルアクリレート、n−オクチルアクリ
レート、イソノニルアクリレート、メトキシエチルアク
リレート、ヒドロキシエチルアクリレートなどが挙げら
れ、これらの1種または2種以上を混合して使用しても
よい。
前記(ロ)成分のビニル系単量体として用いられるアク
リル酸エステルとしては、上記のアクリル酸エステルに
おいて列記したものを挙げることができる。また、メタ
クリル酸エステルとしては、例えばメチルメタクリレー
ト、エチルメタクリレート、ブチルメタクリレート、メ
トキシエチルメタクリレート、グリシジルメタクリレー
トなどが、芳香族モノビニル化合物としては、例えばス
チレン、α−メチルスチレン、ビニルトルエン、ビニル
キシレン、ハロゲン化スチレンなどが、シアン化ビニル
化合物としては、例えば、アクリロニトリル、メタクリ
レートリルなどが挙げられる。これらのビニル系単量体
はそれぞれ単独で用いてもよいし、2種以上組み合わせ
て用いてもよい。
リル酸エステルとしては、上記のアクリル酸エステルに
おいて列記したものを挙げることができる。また、メタ
クリル酸エステルとしては、例えばメチルメタクリレー
ト、エチルメタクリレート、ブチルメタクリレート、メ
トキシエチルメタクリレート、グリシジルメタクリレー
トなどが、芳香族モノビニル化合物としては、例えばス
チレン、α−メチルスチレン、ビニルトルエン、ビニル
キシレン、ハロゲン化スチレンなどが、シアン化ビニル
化合物としては、例えば、アクリロニトリル、メタクリ
レートリルなどが挙げられる。これらのビニル系単量体
はそれぞれ単独で用いてもよいし、2種以上組み合わせ
て用いてもよい。
さらに、(ハ)成分の多官能性ビニル単量体としては、
例えばジビニルベンゼン、ジビニルトルエン、エチレン
グリコールジアクリレート、エチレングリコールジメタ
クリレート、ポリエチレングリコールジアクリレート、
ポリエチレングリコールジメタクリレート、1.3−ブ
タンジオールジアクリレート、ジアリルフタレート、ト
リアリルトリメリテート、ジアリルマレート、トリメチ
ロールプロパントリメタクリレートなどが挙げられ、こ
れらはそれぞれ単独で用いてもよいし、2種以上組み合
わせて用いてもよい。
例えばジビニルベンゼン、ジビニルトルエン、エチレン
グリコールジアクリレート、エチレングリコールジメタ
クリレート、ポリエチレングリコールジアクリレート、
ポリエチレングリコールジメタクリレート、1.3−ブ
タンジオールジアクリレート、ジアリルフタレート、ト
リアリルトリメリテート、ジアリルマレート、トリメチ
ロールプロパントリメタクリレートなどが挙げられ、こ
れらはそれぞれ単独で用いてもよいし、2種以上組み合
わせて用いてもよい。
本発明において、(B)成分として用いるアクリレート
・ブタジエン系グラフト共重合体は、前記の(イ)成分
共重合体存在下に、(ロ)成分のビニル系単量体または
これと(ハ)成分の多官能性ビニル単量体を前記の割合
で用いて、例えば塊状重合、懸濁重合、乳化重合などの
公知の方法によって重合させることにより製造すること
ができる。前記重合方法の中では特に乳化重合が好適で
ある。
・ブタジエン系グラフト共重合体は、前記の(イ)成分
共重合体存在下に、(ロ)成分のビニル系単量体または
これと(ハ)成分の多官能性ビニル単量体を前記の割合
で用いて、例えば塊状重合、懸濁重合、乳化重合などの
公知の方法によって重合させることにより製造すること
ができる。前記重合方法の中では特に乳化重合が好適で
ある。
このようにして得られたアクリレート・ブタジエン系グ
ラフト共重合体の平均粒径は、特に限定されないが、該
樹脂組成物の低温耐衝撃性および耐溶剤性の点から、好
ましくは0.1〜3μm、特に好ましくは0.15〜0
.25μmの範囲にあることが好ましい。
ラフト共重合体の平均粒径は、特に限定されないが、該
樹脂組成物の低温耐衝撃性および耐溶剤性の点から、好
ましくは0.1〜3μm、特に好ましくは0.15〜0
.25μmの範囲にあることが好ましい。
本発明のポリカーボネート樹脂組成物においては、(A
)成分のポリカーボネート樹脂100重量部に対して、
(B)成分のアクリレート・ブタジエン系グラフト共重
合体を1〜80重量部、好ましくは2〜40重量部、さ
らに好ましくは2〜25重量部の割合で配合することが
必要である。
)成分のポリカーボネート樹脂100重量部に対して、
(B)成分のアクリレート・ブタジエン系グラフト共重
合体を1〜80重量部、好ましくは2〜40重量部、さ
らに好ましくは2〜25重量部の割合で配合することが
必要である。
(B)成分の量が1重量部未満では該樹脂組成物は低温
耐衝撃性、耐溶剤性、流動性に劣り、一方80重量部を
越えると剛性および漆黒性が低下する。
耐衝撃性、耐溶剤性、流動性に劣り、一方80重量部を
越えると剛性および漆黒性が低下する。
本発明のポリカーボネート樹脂組成物には、本発明の目
的を損なわない範囲で、例えば無機質充填剤、各種添加
剤、他の合成樹脂、エラストマーなどを必要に応じて配
合することができる。
的を損なわない範囲で、例えば無機質充填剤、各種添加
剤、他の合成樹脂、エラストマーなどを必要に応じて配
合することができる。
前記無機質充填剤はポリカーボネート樹脂組成物の機械
的強度や耐久性の向上または増量を目的として配合され
るものであり、このようなものとしては、例えばガラス
繊維、ガラスピーズ、ガラスフレーク、カーボンブラッ
ク、硫酸カルシウム、炭酸カルシウム、ケイ酸カルシウ
ム、酸化チタン、アルミナ、シリカ、アスベスト、タル
ク、クレー、マイカ、石英粉などが挙げられる。また、
前記各種添加剤としては、例えばヒンダードフェノール
系や、亜リン酸エステル系、リン酸エステル系などのリ
ン系、アミン系などの酸化防止剤、ベンゾトルアゾール
系やベンゾフェノン系などの紫外線吸収剤、脂肪族カル
ボン酸エステル系やパラフィン系などの外部滑剤、常用
の難燃化剤、離型剤、帯電防止剤、着色剤などが挙げら
れる。上記ヒンダードフェノール系酸化防止剤としては
、例えば2.6−ジ第三ブチル−p−クレゾール(BH
T)、イルガノックス1076 (チバガイギー社製、
商品名)、イルガノックス1010 (チバガイギー
社製、商品名)、エチル330 (エチル社製、商品名
)、スミライザーGM(住友化学■製、商品名〕などが
好ましく用いられる。また、その他の合成樹脂としては
、例えばポリエチレン、ポリプロピレン、ポリスチレン
、ASmJJW、ABS樹脂、ポリメチルメタクリレー
トなどの各樹脂を挙げることができる。また、エラスト
マーとしては、イソブチレン−イソプレンゴム、スチレ
ン−ブタジェンゴム、エチレン−プロピレンゴム、アク
リル系エラストマーなどが挙げられる。 本発明のポリ
カーボネート樹脂組成物は、ポリカーボネート樹脂に、
必須成分としてアクリレート・ブタジエン系グラフト共
重合体を、さらに所望に応じ前記各成分を所定の割合で
配合し、混練することにより調製することができる。こ
の配合、混練は、通常用いられている方法、例えばリボ
ンブレンダー、ヘンシェルミキサー、バンバリーミキサ
−、ドラムタンブラ−1車軸スクリユ一押出機、2軸ス
クリユ一押出機、コニーダ、多軸スクリュー押出機など
を用いる方法により行うことができる。混練に際しての
加熱温度は通常250〜300℃の範囲が適当である。
的強度や耐久性の向上または増量を目的として配合され
るものであり、このようなものとしては、例えばガラス
繊維、ガラスピーズ、ガラスフレーク、カーボンブラッ
ク、硫酸カルシウム、炭酸カルシウム、ケイ酸カルシウ
ム、酸化チタン、アルミナ、シリカ、アスベスト、タル
ク、クレー、マイカ、石英粉などが挙げられる。また、
前記各種添加剤としては、例えばヒンダードフェノール
系や、亜リン酸エステル系、リン酸エステル系などのリ
ン系、アミン系などの酸化防止剤、ベンゾトルアゾール
系やベンゾフェノン系などの紫外線吸収剤、脂肪族カル
ボン酸エステル系やパラフィン系などの外部滑剤、常用
の難燃化剤、離型剤、帯電防止剤、着色剤などが挙げら
れる。上記ヒンダードフェノール系酸化防止剤としては
、例えば2.6−ジ第三ブチル−p−クレゾール(BH
T)、イルガノックス1076 (チバガイギー社製、
商品名)、イルガノックス1010 (チバガイギー
社製、商品名)、エチル330 (エチル社製、商品名
)、スミライザーGM(住友化学■製、商品名〕などが
好ましく用いられる。また、その他の合成樹脂としては
、例えばポリエチレン、ポリプロピレン、ポリスチレン
、ASmJJW、ABS樹脂、ポリメチルメタクリレー
トなどの各樹脂を挙げることができる。また、エラスト
マーとしては、イソブチレン−イソプレンゴム、スチレ
ン−ブタジェンゴム、エチレン−プロピレンゴム、アク
リル系エラストマーなどが挙げられる。 本発明のポリ
カーボネート樹脂組成物は、ポリカーボネート樹脂に、
必須成分としてアクリレート・ブタジエン系グラフト共
重合体を、さらに所望に応じ前記各成分を所定の割合で
配合し、混練することにより調製することができる。こ
の配合、混練は、通常用いられている方法、例えばリボ
ンブレンダー、ヘンシェルミキサー、バンバリーミキサ
−、ドラムタンブラ−1車軸スクリユ一押出機、2軸ス
クリユ一押出機、コニーダ、多軸スクリュー押出機など
を用いる方法により行うことができる。混練に際しての
加熱温度は通常250〜300℃の範囲が適当である。
このようにして得られたポリカーボネート樹脂組成物は
既知の種々の成形方法、例えば射出成形4券、押出成形
、圧縮成形、カレンダー成形、回転成形などを適用して
自動車用バンパーなど自動車分野の成形品や家電分野な
どの成形品を製造することができる。
既知の種々の成形方法、例えば射出成形4券、押出成形
、圧縮成形、カレンダー成形、回転成形などを適用して
自動車用バンパーなど自動車分野の成形品や家電分野な
どの成形品を製造することができる。
次に実施例により本発明をさらに詳細に説明するが、本
発明はこれらの例によってなんら限定されるものではな
い。
発明はこれらの例によってなんら限定されるものではな
い。
なお、樹脂組成物の物性は次のようにして求めた。
(1) アイシフト衝撃強さ
ASTM D 256に準拠して求めた(温度=3
0℃)。
0℃)。
(2)熱安定性
メルトインデクサ−内で300℃、15分間滞留させた
のち、押出したストランドの状態を目視で判定した。
のち、押出したストランドの状態を目視で判定した。
O: 良好
△: 発泡、変色が若干ある
×: 発泡、変色が激しい
(3)耐溶剤性
1/4楕円法(中辻他、色材、第39巻、第455ペー
ジ、1966年)に準拠して求めた。トルエン/イソオ
クタン/メタノール= 42.5 / 42.5/15
(容量%)の混合溶剤に5分間浸せきしたのちの限界歪
を示す。
ジ、1966年)に準拠して求めた。トルエン/イソオ
クタン/メタノール= 42.5 / 42.5/15
(容量%)の混合溶剤に5分間浸せきしたのちの限界歪
を示す。
(4)漆黒性
組成物100重量部にカーボンブランク0.3重量部を
添加し、射出成形して縦80mm、横80m。
添加し、射出成形して縦80mm、横80m。
厚み3.2Hの平板を製造し、その外観を目視で判定し
た。
た。
○: 黒色度が高く、色調が均一
△: 黒色度が普通で、色調にややむらがある
×: 黒色度が低く、色調にむらがある耐圧反応釜に、
イオン交換水200重量部、ドデシルジフェニルエーテ
ルジスルホン酸ナトリウム2重量部、過硫酸カリウム0
.1重量部、硫酸ナトリウム0.5重量部およびブチル
アクリレート80重量部を仕込み、十分窒素置換したの
ち、ブタジェン20重量部を投入し、50℃まで昇温し
で30時間重合した。
イオン交換水200重量部、ドデシルジフェニルエーテ
ルジスルホン酸ナトリウム2重量部、過硫酸カリウム0
.1重量部、硫酸ナトリウム0.5重量部およびブチル
アクリレート80重量部を仕込み、十分窒素置換したの
ち、ブタジェン20重量部を投入し、50℃まで昇温し
で30時間重合した。
次に、この反応混合物に、イオン交換水80重量部、硫
酸第一鉄0.01重量部、ナトリウムホルムアルデヒド
スルホキシレート0.3重量部、クメンハイドロパーオ
キサ41011重量部を添加、溶解、混合し、50℃に
保ちながら、アクリロニトリル10重量部およびスチレ
ン30重量部の混合物を4時間かけて連続添加し、その
後、3時間重合して反応を完了させた。
酸第一鉄0.01重量部、ナトリウムホルムアルデヒド
スルホキシレート0.3重量部、クメンハイドロパーオ
キサ41011重量部を添加、溶解、混合し、50℃に
保ちながら、アクリロニトリル10重量部およびスチレ
ン30重量部の混合物を4時間かけて連続添加し、その
後、3時間重合して反応を完了させた。
反応終了後の上記ラテックスを0.05重量%硫酸アル
ミニウム水溶液に投入し、凝固させた。凝固に際し、ヒ
ンダードフェノール系酸化防止剤・イルガノックス10
76 (チバガイギー社製、商品名)をポリマーに対し
0.5重量部添加した。
ミニウム水溶液に投入し、凝固させた。凝固に際し、ヒ
ンダードフェノール系酸化防止剤・イルガノックス10
76 (チバガイギー社製、商品名)をポリマーに対し
0.5重量部添加した。
凝固したゴムは、水洗乾燥して、平均粒径0.18μm
の所定のグラフト共重合体を得た。
の所定のグラフト共重合体を得た。
製造例1において、アクリロニトリル10重量部とスチ
レン30重量部との混合物の代わりに、アクリロニトリ
ル10重量部とスチレン30重量部とジビニルベンゼン
0.5重量部との混合物を用いた以外は、製造例1と全
く同様にしてグラフト共重合体を製造した。
レン30重量部との混合物の代わりに、アクリロニトリ
ル10重量部とスチレン30重量部とジビニルベンゼン
0.5重量部との混合物を用いた以外は、製造例1と全
く同様にしてグラフト共重合体を製造した。
実施例1〜6
ビスフェノールA系ポリカーボネート樹脂(出光石油化
学■製、商品名「タフロンA−22001粘度平均分子
量21,500)100重量部に対し、製造例1.2で
得たアクリレート・ブタジエン系グラ”7)共重合体を
別表に示す割合で配合し、これを270℃で混練してペ
レット化した。
学■製、商品名「タフロンA−22001粘度平均分子
量21,500)100重量部に対し、製造例1.2で
得たアクリレート・ブタジエン系グラ”7)共重合体を
別表に示す割合で配合し、これを270℃で混練してペ
レット化した。
このペレットについての試験結果を数表に示す。
比較例1〜7
実施例において、グラフト共重合体の種類および使用量
を別表に示すように変えた以外は、実施例と同様にして
ペレットを作成した。
を別表に示すように変えた以外は、実施例と同様にして
ペレットを作成した。
このペレットについての試験結果を数表に示す。
なお、使用したグラフト共重合体の種類を次に示す。
W529:三菱レーヨン■製「メタブレンW52j
アクリルゴムにスチレンおよびメタク
リル酸メチルをグラフトした重合体
(MAS樹脂)
KM33010−ム&ハース社製rパラロイドK330
J MAS樹脂 HIA15:呉羽化学工業■製’HIA15aオクチル
アクリレートとブタジェン を共重合させて得られるゴムラテッ クスに、スチレン、メタクリル酸メ チルを添加し、グラフト重合させて 得られたグラフト共重合体(MAB S樹脂) 以下余白 〔発明の効果〕 本発明のポリカーボネート樹脂組成物は、ポリカーボネ
ート樹脂に、特定の組成を有するアクリレート・ブタジ
エン系グラフト共重合体を配合したものであうで、熱安
定性、低温耐衝撃性、漆黒性、耐溶剤性などに優れてお
り、例えば自動車バンパーなどの自動車分野成形品や家
電分野成形品などの材料として好適に用いられる。
J MAS樹脂 HIA15:呉羽化学工業■製’HIA15aオクチル
アクリレートとブタジェン を共重合させて得られるゴムラテッ クスに、スチレン、メタクリル酸メ チルを添加し、グラフト重合させて 得られたグラフト共重合体(MAB S樹脂) 以下余白 〔発明の効果〕 本発明のポリカーボネート樹脂組成物は、ポリカーボネ
ート樹脂に、特定の組成を有するアクリレート・ブタジ
エン系グラフト共重合体を配合したものであうで、熱安
定性、低温耐衝撃性、漆黒性、耐溶剤性などに優れてお
り、例えば自動車バンパーなどの自動車分野成形品や家
電分野成形品などの材料として好適に用いられる。
Claims (1)
- 1、(A)ポリカーボネート樹脂100重量部に対し、
(B)(イ)アクリル酸エステル55〜95重量%とブ
タジエン45〜5重量%とからなる共重合体100重量
部の存在下に、(ロ)アクリル酸エステル、メタクリル
酸エステル、芳香族モノビニル化合物およびシアン化ビ
ニル化合物の中から選ばれたビニル系単量体の1種また
は2種以上20〜100重量部および(ハ)多官能性ビ
ニル単量体0〜5重量部を重合させてなるアクリレート
・ブタジエン系グラフト共重合体1〜80重量部を配合
したことを特徴とするポリカーボネート樹脂組成物。