JPS62246789A - 光記録媒体 - Google Patents
光記録媒体Info
- Publication number
- JPS62246789A JPS62246789A JP61089947A JP8994786A JPS62246789A JP S62246789 A JPS62246789 A JP S62246789A JP 61089947 A JP61089947 A JP 61089947A JP 8994786 A JP8994786 A JP 8994786A JP S62246789 A JPS62246789 A JP S62246789A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic particles
- optical recording
- recording medium
- layer
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明はレーザー光によって情報を記録再生することの
できる光記録媒体に関し、さらに詳しくは半導体レーザ
ーの発振波長の光エネルギーにより物質状態の変化を利
用して記録を行なう光記録媒体に関するものである。
できる光記録媒体に関し、さらに詳しくは半導体レーザ
ーの発振波長の光エネルギーにより物質状態の変化を利
用して記録を行なう光記録媒体に関するものである。
［従来の技術］
従来、光記録媒体としてＴｅ合金、Ｔｅ酸化物、バブル
形成媒体↓よび有機色素等が用いられてきた。
形成媒体↓よび有機色素等が用いられてきた。
しかしながら、Ｔｅ合金は比較的書き込み感度が高いが
、化学的に不安定て空気中で容易に劣化する欠点がある
。
、化学的に不安定て空気中で容易に劣化する欠点がある
。
一方、 Ｔｅ酸化物はＴｅ合金よりも安定であるが、光
学特性が酸化状態に敏感に依存するために、媒体形成時
の酸化条件を厳しく制御しなければならないという欠点
がある。
学特性が酸化状態に敏感に依存するために、媒体形成時
の酸化条件を厳しく制御しなければならないという欠点
がある。
また、バブル形成媒体は高感度な媒体であるが、多層構
成のため成膜回数の多いこと、Ｊ＆脱膜時条件を厳しく
行なわなければならないという欠点がある。
成のため成膜回数の多いこと、Ｊ＆脱膜時条件を厳しく
行なわなければならないという欠点がある。
他方、有機色素媒体は溶媒塗布により成膜を容易に行な
うことができるが、書き込み感度が低く、かつ反射率が
低いという欠点がある。
うことができるが、書き込み感度が低く、かつ反射率が
低いという欠点がある。
［発明が解決しようとする問題点］
本発明は上記の従来の技術の欠点を改良し、半導体レー
ザーの波長領域において、高感度で化学的に安定な光記
録媒体を提供することを目的とするものである。
ザーの波長領域において、高感度で化学的に安定な光記
録媒体を提供することを目的とするものである。
［問題点を解決するための手段］
すなわち１本発明は高分子層中に形状異方性を有する磁
性粒子を−・方向に配向して分散せしめてなる記録層を
有することを特徴とする光記録媒体′Ｃある。
性粒子を−・方向に配向して分散せしめてなる記録層を
有することを特徴とする光記録媒体′Ｃある。
以下、本発明の詳細な説明する。
第１図は本発明の光記録媒体の１例を示す説明図である
。同第１図において、本発明の光記録媒体は高分子層２
中に、形状異方性を有する磁性粒子３を」−下方向の一
方向に配向して分散せしめて記録層４を形成し、該記録
層４を基板ｌの上に設けてなるものである。
。同第１図において、本発明の光記録媒体は高分子層２
中に、形状異方性を有する磁性粒子３を」−下方向の一
方向に配向して分散せしめて記録層４を形成し、該記録
層４を基板ｌの上に設けてなるものである。
本発明に用いられる磁性粒子としては磁性をもつ金属、
合金、金属化合物であれば如何なるものでも用いること
ができ、例えばγ−Ｆｅ＝０３、Ｃｏ−γ−Ｆｅ２０．
等が挙げられる。
合金、金属化合物であれば如何なるものでも用いること
ができ、例えばγ−Ｆｅ＝０３、Ｃｏ−γ−Ｆｅ２０．
等が挙げられる。
また磁性粒子は平均粒径１ｇｍ以下で、形状は六 特に
限定することはなく、断面が円形、だ円形、正方形、矩
形、多角形等の如何なるものでも用いることかできるか
、形状異方性を有するものが好ましく、几体的には長袖
０．５ｏｎ＋以下で長軸：短軸の比かｌ・１〜１０：ｌ
、好ましくは長袖０．０１川ｌ〜０．５蒔１、長軸：短
軸の比が２＝１〜１０：１のものが望ましい。
限定することはなく、断面が円形、だ円形、正方形、矩
形、多角形等の如何なるものでも用いることかできるか
、形状異方性を有するものが好ましく、几体的には長袖
０．５ｏｎ＋以下で長軸：短軸の比かｌ・１〜１０：ｌ
、好ましくは長袖０．０１川ｌ〜０．５蒔１、長軸：短
軸の比が２＝１〜１０：１のものが望ましい。
さらに、本発明において用いられる磁性粒子は結晶を容
易に製造できること、保存時の光学濃度の変化等の経時
変化の少ないこと、および半導体レーザーの波長領域で
の光反射率の高いこと等の特性を有するものが好ましい
。
易に製造できること、保存時の光学濃度の変化等の経時
変化の少ないこと、および半導体レーザーの波長領域で
の光反射率の高いこと等の特性を有するものが好ましい
。
本発明において、磁性粒子を分散せしめる高分子層とし
ては半導体レーザー光の照射による熱で容易に変形する
高分子物質からなるものであればよく、例えば酢酸ビニ
ルアルコール、ポリ塩化ビニル（ｐｖｃ）、ポリメチル
メタクリレート（ＰＭＭＡ）。
ては半導体レーザー光の照射による熱で容易に変形する
高分子物質からなるものであればよく、例えば酢酸ビニ
ルアルコール、ポリ塩化ビニル（ｐｖｃ）、ポリメチル
メタクリレート（ＰＭＭＡ）。
ポリビニルブチラール（ＰＶ［ｌＲ） 、ポリエチレン
（ＰＥ）、ポリスチレン（ｐｓ）等が挙げられる。
（ＰＥ）、ポリスチレン（ｐｓ）等が挙げられる。
本発明に用いられる基板としてはポリカーボネイト（ｐ
ｃ） 、ポリエチレンテレフタレート（ＰＥＴ）等のプ
ラスチック、ガラス、セラミック、紙、板状又は箔状の
金属等を用いることができるが、これ等は高分子媒体に
不溶性であることが望ましい。′また基板は半導体レー
ザー光の波長の光に対し透明、不透明、あるいは反射性
のいずれであってもよい。
ｃ） 、ポリエチレンテレフタレート（ＰＥＴ）等のプ
ラスチック、ガラス、セラミック、紙、板状又は箔状の
金属等を用いることができるが、これ等は高分子媒体に
不溶性であることが望ましい。′また基板は半導体レー
ザー光の波長の光に対し透明、不透明、あるいは反射性
のいずれであってもよい。
また、本発明の光記録媒体には必要に応じて保護層を設
けることができる。保護層としてはＳｉＯ□、 Ｓｉｎ
、八ｐ２０３ 等の無機材料、ポリスチレン、 ＩＩ
ＥＴ等の有機材料等の半導体レーザー光の波長の光に対
して透明な物質であれば、いずれの物質でも用いること
がてきる。
けることができる。保護層としてはＳｉＯ□、 Ｓｉｎ
、八ｐ２０３ 等の無機材料、ポリスチレン、 ＩＩ
ＥＴ等の有機材料等の半導体レーザー光の波長の光に対
して透明な物質であれば、いずれの物質でも用いること
がてきる。
次に、本発明の光記録媒体を製造する方法について説明
すると、第２図に示す様に、先ず磁性粒子３を高分子層
２を形成するプラスチック又は高分子の液に分散し、基
板ｌに塗布する。次いで塗布層中の磁性粒子３が流動可
能な時点で外部磁場（図示せず）を印加することにより
、磁性粒子の存在状態に規則性を付与した状態で、高分
子の塗布層を硬化せしめることにより容易に得ることが
てきる。
すると、第２図に示す様に、先ず磁性粒子３を高分子層
２を形成するプラスチック又は高分子の液に分散し、基
板ｌに塗布する。次いで塗布層中の磁性粒子３が流動可
能な時点で外部磁場（図示せず）を印加することにより
、磁性粒子の存在状態に規則性を付与した状態で、高分
子の塗布層を硬化せしめることにより容易に得ることが
てきる。
基板りに磁性粒子を含む高分子を塗布する方法としては
、浸漬法、スピン被覆法、ドクターの刃を用いる方法等
により行うことがてきる。
、浸漬法、スピン被覆法、ドクターの刃を用いる方法等
により行うことがてきる。
高分子層の厚さは高分子の種類、磁性粒子の種類によっ
てきまるが、顕微鏡的なピンホールが存在しないことが
必要であり、通常０．１〜１００ ＩＬｔａ、好ましく
は１〜１０μｍが望ましい。
てきまるが、顕微鏡的なピンホールが存在しないことが
必要であり、通常０．１〜１００ ＩＬｔａ、好ましく
は１〜１０μｍが望ましい。
また、高分子層中の磁性粒子の含有量は高分子１００重
量部に対して１０〜１００重量部、好ましくは１０〜５
０重量ｉが望ましい。
量部に対して１０〜１００重量部、好ましくは１０〜５
０重量ｉが望ましい。
本発明の光記録媒体への情報の書き込み（記録）は半導
体レーザーを照射すると、その発振波長の光エネルギー
により、第３図に示す様に照射部にビット５が形成され
情報の記録を行うことができる。
体レーザーを照射すると、その発振波長の光エネルギー
により、第３図に示す様に照射部にビット５が形成され
情報の記録を行うことができる。
また、記録時に光記録媒体の全体に磁場をかけてもよい
。ピットが形成された所は光反射率が低下するので光反
射率の変化を利用して情報の読み取り再生を行うことが
できる。
。ピットが形成された所は光反射率が低下するので光反
射率の変化を利用して情報の読み取り再生を行うことが
できる。
［作用］
本発明の光記録媒体は記録層の高分子層中に形状異方性
を有する磁性粒子が−・方向に配向して分散しているの
で、記録層の熱伝導率が低下するとともに強度が増加し
、高感度で安定な記録・再生を行うことかてきるものと
推定される。
を有する磁性粒子が−・方向に配向して分散しているの
で、記録層の熱伝導率が低下するとともに強度が増加し
、高感度で安定な記録・再生を行うことかてきるものと
推定される。
［実施例］
以下、実施例を示し本発明をさらに具体的に説明する。
実施例１
ｆ均粒径０．２ＪＬｌｌのｙ−Ｆｅ２０３ｔｏ重量部と
１０重隘％ポリ酢酸ビニル溶液１００重量部をボールミ
ルを用いて２時間粉砕混合して分散液を調整した。
１０重隘％ポリ酢酸ビニル溶液１００重量部をボールミ
ルを用いて２時間粉砕混合して分散液を調整した。
次に、厚さ３００ ＪＬｍの透明のＰＥＴ基板上に上記
分散液をバーコードで塗布した。その後に磁場を加えな
がら基板全体を約８０９Ｃまで赤外線ランプで加熱して
光記録媒体を得た。次に該光記録媒体に波長８３０ｎ−
の半導体レーザー光ビームをビームレンズで約１０μ寵
に集光させて、１０ｍ／ｓｅｃの走査速度て走査させて
記録を行った。該記録層に照射するレーザーパワー１０
ｍＷにおいて、Ｓ／Ｎ比として４１１ ｄ ｂを得た。
分散液をバーコードで塗布した。その後に磁場を加えな
がら基板全体を約８０９Ｃまで赤外線ランプで加熱して
光記録媒体を得た。次に該光記録媒体に波長８３０ｎ−
の半導体レーザー光ビームをビームレンズで約１０μ寵
に集光させて、１０ｍ／ｓｅｃの走査速度て走査させて
記録を行った。該記録層に照射するレーザーパワー１０
ｍＷにおいて、Ｓ／Ｎ比として４１１ ｄ ｂを得た。
実施例２
実施例１において、酢酸ビニルアルコールの代りに、ポ
リビニルブチラールを用いて、同様に試料を作成し、実
施例１と同様に記録を行ったところ、Ｓ／Ｎ比として約
１１０ｄｂを得た。
リビニルブチラールを用いて、同様に試料を作成し、実
施例１と同様に記録を行ったところ、Ｓ／Ｎ比として約
１１０ｄｂを得た。
実施例３
実施例１のＰＥＴ基板に代って、２００ｇｍ厚のＰＣ板
を基板に用いて実施例１と同様な方法で記録層を基板上
に形成した。
を基板に用いて実施例１と同様な方法で記録層を基板上
に形成した。
実施例１と同様な方法で記録を行ったところ。
Ｓ／Ｎ比として約４０ｄｂを得た。
比較例１
実施例１において、磁性粒子であるγ−Ｆｅ２Ｏ３を使
用しないで同様の方法によって得た光記録媒体に、実施
例１と同様の記録を行ったところＳ／Ｎ比として３０ｄ
ｂを得た。
用しないで同様の方法によって得た光記録媒体に、実施
例１と同様の記録を行ったところＳ／Ｎ比として３０ｄ
ｂを得た。
比較例２
実施例１において、磁性粒子であるγ−Ｆｅ２Ｏ３に磁
場を印加しないて同様の方法によって得た光記録媒体に
、実施例１と同様の記録を行ったところＳｌＮ比として
：＋ｏｄｂＸ！ｉ−得た。
場を印加しないて同様の方法によって得た光記録媒体に
、実施例１と同様の記録を行ったところＳｌＮ比として
：＋ｏｄｂＸ！ｉ−得た。
［発明の効果］
本発明の光記録媒体は高分子中に形状異方性を有する磁
性粒子を一定方向に配向して分散してなる記録層を有す
るので比較的高温・高湿の環境条件でも安定である。ま
た一般の有機色素と同様に低い熱伝導率を有し、従って
、レーザー記録時の媒体中の熱の拡散が少なくなり高感
度でＳ／Ｎ比の良い値を得ることができる。その１均−
な表面を作ることができ、表面ノイズによるＳ／Ｎ比の
低下を避けることができる等の優れた効果がある。
性粒子を一定方向に配向して分散してなる記録層を有す
るので比較的高温・高湿の環境条件でも安定である。ま
た一般の有機色素と同様に低い熱伝導率を有し、従って
、レーザー記録時の媒体中の熱の拡散が少なくなり高感
度でＳ／Ｎ比の良い値を得ることができる。その１均−
な表面を作ることができ、表面ノイズによるＳ／Ｎ比の
低下を避けることができる等の優れた効果がある。
第１図は本発明の光記録媒体の１例を示す説明図、第２
図は磁性粒子を含有する高分子を基板上に塗布した状態
を示す説明図および第３図はレーザー光により書き込ま
れた状態を示す説明図である。 ｉ −・・基板 ２・・・高分子層 ３・・・磁性粒子 ４・・・記録層 ５・・・ピッｌへ 第１図 第２図 第３図
図は磁性粒子を含有する高分子を基板上に塗布した状態
を示す説明図および第３図はレーザー光により書き込ま
れた状態を示す説明図である。 ｉ −・・基板 ２・・・高分子層 ３・・・磁性粒子 ４・・・記録層 ５・・・ピッｌへ 第１図 第２図 第３図
Claims (1)
- 高分子層中に形状異方性を有する磁性粒子を一方向に配
向して分散せしめてなる記録層を有することを特徴とす
る光記録媒体。