JPH0536559B2 - - Google Patents
Info
- Publication number
- JPH0536559B2 JPH0536559B2 JP24079486A JP24079486A JPH0536559B2 JP H0536559 B2 JPH0536559 B2 JP H0536559B2 JP 24079486 A JP24079486 A JP 24079486A JP 24079486 A JP24079486 A JP 24079486A JP H0536559 B2 JPH0536559 B2 JP H0536559B2
- Authority
- JP
- Japan
- Prior art keywords
- paperboard
- activated carbon
- corrosion
- present
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
銀、銅又は鉛等からなる部材や部品を含む物品を
防食包装するための板紙に関する。また、本発明
は、銀、銅又は鉛等からなる部材や部品を含む物
品を防食包装するための方法に関する。 従来の技術 従来、種々の工業製品や部品は、段ボール紙か
らなるケース内に収納されて保管され、或いは運
搬されることが多いが、このような包装によれ
ば、工業製品や部品の一部が腐食したり、或いは
変質したりすることがあることが知られている。
特に、工業製品や部品が銀や銅からなる部材を含
む場合に、この傾向が著しい。このような腐食の
変質は、段ボール紙から発生する硫化水素等のよ
うな還元性イオウ化合物に起因するといわれてい
る。 段ボール原紙は、クラフト法によるクラフトパ
ルプを原料とするクラフト紙を主原料として製造
される。このクラフト法は、木材を水酸化ナトリ
ウムと硫化ナトリウムとの混合溶液中で加圧蒸煮
し、リグニンを除去してパルプ化するものであ
る。従つて、このクラフトパルプから製造される
クラフト紙或いは段ボール原紙中にはイオウ化合
物が残存しており、その結果として、高温多湿の
条件下にクラフト紙や段ボール紙がおかれると
き、紙中から硫化水素等のような還元性イオウ化
合物が発生することがある。ここに、かかる還元
性イオウ化合物は、よく知られているように、殆
どの金属と反応して、一般には、黒色の硫化物を
生成する。電気製品においては、銀や銅が接点、
導線等の主要部材の材料として多用されており、
これら金属は、比較的耐食性にすぐれるものの、
硫化水素による腐食は免れ難い。電気製品におい
ては、接点に僅かの硫化物が生成しても接触抵抗
が増し、また、導線においては、電気抵抗の増大
や断線等が生じるので、電気製品やその部品にお
いては、硫化水素による腐食は致命的な不良発生
の原因となる。 また、ポリ塩化ビニル樹脂等の樹脂製品には、
安定剤として鉛化合物を含むものが多いが、この
鉛化合物も硫化水素と反応して、黒色の硫化鉛を
生成する。従つて、鉛化合物を含有する樹脂から
なる製品や部品も、段ボール紙からなるケース内
で黒色に変色し、品質が劣化し、或いは外観不良
が生じる。 従つて、従来、銀、銅、鉛等からなる部材を含
む部品や製品は、腐食を避けるために、ポリエチ
レンフイルム等にて包装し、これを段ボールケー
スに収容する二重包装を余儀なくされており、手
間を要すると共に、包装費用を高くしている。 他方、活性炭を不織布等の多孔質基材に付着さ
せた所謂吸着性シートが従来より種々提案されて
いる。例えば、特公昭46−21002号公報には、活
性炭を不織布に合成ゴムラテツクスをバインダー
として付着させてなる吸着性シートが記載されて
おり、また、特公昭61−43093号公報には、無機
繊維、活性炭粉末及びバインダーを含む水性スラ
リーを湿式抄紙して、吸着性シートを製造する方
法が記載されている。しかし、これら従来の吸着
性シートは、硫化水素のような還元性イオウ化合
物の吸着性能は十分ではない。 発明が解決しようとする問題点 本発明は、前記したような銀、銅又は鉛等から
なる部材や部品を含む物品の包装における腐食の
問題を解決するためになされたものであつて、硫
化水素のような還元性イオウ化合物の吸着性能に
すぐれ、従つて、上記部材や部品を含む物品を防
食包装するのに好適に用いることができる防食用
板紙を提供することを目的とする。 問題点を解決するための手段 本発明による防食用板紙は、 (a) 活性炭微粉末、 (b) 銅、ニツケル、コバルト、鉄、亜鉛、スズ、
マンガン、バナジウム、モリブデン、白金、ナ
トリウム、カリウム、カルシウム、バリウム及
びカドミウムよりなる群から選ばれる少なくと
も1種の金属又はその化合物、及び (c) バインダー とを含有する組成物を還元性を有するイオウ化合
物を発生する板紙に塗布又は含浸させてなること
を特徴とする。 本発明においては、活性炭微粉末は、通常の方
法、例えば、木材、ヤシ殻、石炭等を原料とし
て、水蒸気又は薬品賦活法等の方法にて製造され
るものが任意に用いられる。しかし、かかる活性
炭微粉末は、BET表面積が400〜2000m2/gの範
囲にあり、粉径が100μm以下であることが好まし
い。 本発明による防食用板紙は、上記活性炭微粉末
と共に、銅、ニツケル、コバルト、鉄、亜鉛、ス
ズ、マンガン、バナジウム、モリブデン、白金、
ナトリウム、カリウム、カルシウム、バリウム及
びカドミウムよりなる群から選ばれる少なくとも
1種の金属又はその化合物が塗布又は含浸されて
いる。ここに、上記化合物としては、例えば、硫
酸塩、塩酸塩、硝酸塩等の無機酸塩、酢酸塩等の
有機酸塩のほか、酸化物、水酸化物等を挙げるこ
とができるが、これらに限定されるものではな
い。 本発明による防食用板紙は、上記活性炭微粉末
と金属又はその化合物と共に、バインダーと水と
必要に応じて分散剤等の添加剤とからなる水性組
成物を板紙に塗布又は含浸した後、乾燥させるこ
とによつて得ることができる。 本発明において用い得る板紙としては、例え
ば、普通紙、加工紙、段ボール原紙、段ボール基
材等を挙げることができる。これら板紙は、クラ
フト紙等、板紙中にイオウ化合物を含有し、還元
性イオウ化合物を発生するものである。また、包
装用途を考慮して、これら板紙は、通常、前記組
成物を塗布又は含浸する前の坪量が60g/m2以上
であることが好ましい。 上記水性組成物に用いるバインダーとしては、
水溶性でも水分散性でもよく、通常、合成ゴムラ
テツクス、ポリ(メタ)アクリル酸エステル又は
これとスチレンや酢残ビニル等との共重合体ラテ
ツクス、ポリビニルアルコール、カルボキシメチ
ルセルロース等の繊維素誘導体、ポリアクリル酸
ナトリウム等の水溶性高分子が好ましく用いられ
る。これらは、水性組成物において、通常、0.1
〜5重量%の割合で用いられる。 また、分散剤としては、非イオン性界面活性
剤、カチオン性界面活性剤、アニオン性界面活性
剤、両性界面活性剤のような各種の界面活性剤が
好ましく用いられる。界面活性剤を用いる場合、
その使用量は、水性組成物において、通常、固形
分として10重量%以下である。 上記水性組成物における水の量は、活性炭微粉
末、前記金属又はその化合物及びバインダーを含
む組成物をクラフト紙や段ボール原紙に塗布又は
含浸させることができれば、何ら限定されるもの
ではない。 板紙への上記水性組成物の塗布又は含浸による
付着量は、特に限定されるもではないが、通常、
1〜100g/m2であり、乾燥重量換算にては0.1
g/m2以上、好ましくは0.5g/m2以上である。 本発明においては、活性炭微粉末は、前記水性
組成物の0.05〜25重量%を占めることが好まし
く、また、前記金属又はその化合物は、前記組成
物の0.5〜50重量%を占めることが好ましい。 また、本発明によれば、以上に説明したような
防食用板紙にて銀、銅、鉛等からなる部材を含む
物品を包装することによつて、その腐食を防止す
ることができ、例えば、物品をポリエチレンで包
装した後、段ボール紙からなるケースに収容する
ような二重包装を不必要とすることができる。 発明の効果 本発明による防食用板紙は、以上のように活性
炭微粉末と共に所定の金属又はその化合物が塗布
又は含浸されており、板紙自体から発生する還元
性イオウ化合物、特に、硫化水素やメルカプタン
類を板紙内に吸着固定し、或いは環境雰囲気中に
硫化水素やメルカプタン類が低濃度にて存在する
場合でも、これらを速やかに吸着固定するので、
これら還元性イオウ化合物による物品、特に、
銀、銅、鉛等からなる部材を含む物品の腐食を効
果的に防止することができる。 更に、本発明の防食用板紙によれば、活性炭及
び上記金属又はその化合物が相乗的に作用して、
硫化水素やメルカプタン類の吸着固定作用が著し
く高められる。 実施例 以下に実施例を挙げて本発明を説明するが、本
発明はこれら実施例によつて何ら限定されるもの
ではない。 実施例 1 乾燥重 含水重 量部 量部 非イオン性界面活性剤 94 327.3 スチレン−ブタジエン ラテツクス 3 6 硫酸銅 37.1 58 活性炭微粉末 (平均粒径10μm) 1.4 1.4 水 − 1166.6 合 計 135.5 1559.3 上記組成を有し、全固形分8.7%、粘度300cps、
PH4.6である水性組成物を坪量150g/m2の段ボー
ル原紙にグラビアコートし、乾燥させて、乾燥重
量換算による上記組成物付着量3.6g/m2の本発
明による防食用板紙を得た。 この板紙を20cm角に裁断し、硫化水素及びメチ
ルメルカプタンをそれぞれ100ppm濃度で含有す
る容量11.4のデシケート中に温度26℃にて放置
した。デシケータ中の上記ガスの濃度の経時変化
を第1表に示す。 比較のために、金属成分を含まない水性組成物
成分を除いた場合。
比較例2:本発明品から活性炭
成分を除いた場合。
同様にして板紙に塗布乾燥させ、これら板紙を用
いて上記と同様にガス濃度の経時変化を調べ、そ
れぞれ比較例1及び2として併せて第1表に示
す。 実施例 2 実施例1において得た本発明による板紙を5cm
角に裁断し、これを銀線1g及び銀電気端子部品
と共にポリフツ化ビニルフイルム(厚さ100μm)
からなる袋内に密封した後、温度70℃にて放置
し、銀の腐食状況を目視にて観察した。結果を第
2表に示す。 比較のために、前記水性組成物を塗布しない板
紙、並びに前記実施例1における比較例1及び2
による板紙を用いて、上記と同じ条件にて銀の腐
食状況を観察した。結果を第2表に示す。
Claims (1)
- 【特許請求の範囲】 1 (a) 活性炭微粉末、 (b) 銅、ニツケル、コバルト、鉄、亜鉛、スズ、
マンガン、バナジウム、モリブデン、白金、ナ
トリウム、カリウム、カルシウム、バリウム及
びカドミウムよりなる群から選ばれる少なくと
も1種の金属又はその化合物、及び (c) バインダー とを含有する組成物を還元性を有するイオウ化合
物を発生する板紙に塗布又は含浸させてなること
を特徴とする防食用板紙。