JPH04190240A - 静電荷像現像用トナー - Google Patents
静電荷像現像用トナーInfo
- Publication number
- JPH04190240A JPH04190240A JP2320240A JP32024090A JPH04190240A JP H04190240 A JPH04190240 A JP H04190240A JP 2320240 A JP2320240 A JP 2320240A JP 32024090 A JP32024090 A JP 32024090A JP H04190240 A JPH04190240 A JP H04190240A
- Authority
- JP
- Japan
- Prior art keywords
- toner
- wax
- good
- temperature
- low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、電子写真法、静電印刷法などにおいて形成さ
れる静電荷像を現像するための乾式トナーに関する。
れる静電荷像を現像するための乾式トナーに関する。
電子写真法、静電印刷法、静電記録法などで形成される
静電荷像は、乾式法の場合、一般に結着樹脂及び着色剤
を主成分とする乾式トナーで現像後、コピー用紙上に転
写、定着される。トナー像の定着法としては種々あるが
、熱効率が高いこと及び高速定着が可能であることから
、熱ローラ定着方式が広く採用されている。このような
熱定着方式で高速定着を行なう場合、トナーには良好な
低温定着性(又は定着下限温度が低いこと)が要求され
、またこのためにバインダー樹脂としては、低軟化点の
ものが使用される。しかし、トナー中に低軟化点樹脂を
含有させると、定着時にトナー像の一部が熱ローラの表
面に付着し、これがコピー用紙上に転移して地汚れを起
こす、いわゆるオフセット現像や、コピー用紙が熱ロー
ラ表面に付着して巻き付く、いわゆる巻き付き現象(特
に熱ローラ温度が低いときに多い、)が発生し易くなる
。
静電荷像は、乾式法の場合、一般に結着樹脂及び着色剤
を主成分とする乾式トナーで現像後、コピー用紙上に転
写、定着される。トナー像の定着法としては種々あるが
、熱効率が高いこと及び高速定着が可能であることから
、熱ローラ定着方式が広く採用されている。このような
熱定着方式で高速定着を行なう場合、トナーには良好な
低温定着性(又は定着下限温度が低いこと)が要求され
、またこのためにバインダー樹脂としては、低軟化点の
ものが使用される。しかし、トナー中に低軟化点樹脂を
含有させると、定着時にトナー像の一部が熱ローラの表
面に付着し、これがコピー用紙上に転移して地汚れを起
こす、いわゆるオフセット現像や、コピー用紙が熱ロー
ラ表面に付着して巻き付く、いわゆる巻き付き現象(特
に熱ローラ温度が低いときに多い、)が発生し易くなる
。
そこで、これらの現象を防止する手段として、特開昭5
1−143333号、同57−148752号、同58
−97056号、同60−247250号公報等では、
離型剤として固形シリコーンワニス、高級脂肪酸、高級
アルコール、各種ワックス等を添加することが提案され
ている。
1−143333号、同57−148752号、同58
−97056号、同60−247250号公報等では、
離型剤として固形シリコーンワニス、高級脂肪酸、高級
アルコール、各種ワックス等を添加することが提案され
ている。
ところが、良好な低温定着性を維持しながら、充分な耐
オフセント性及び耐巻き付き性を示す離型剤は、未だ見
出されていないのが現状である。
オフセント性及び耐巻き付き性を示す離型剤は、未だ見
出されていないのが現状である。
具体的に言うと、従来の低分子量ポリエチレン、低分子
量ポリプロピレン等のポリオレフインワンクヌは、耐オ
フセント性は良好であるが、低温定着性が充分でなく、
カルナウバワックス、キャンデリラワックス等の植物性
ワックスは、耐オフセット性及び低温定着性は良好であ
るが、耐巻は付き性が充分でなく、また固形シリコーン
フェス、固形シリコーンオイル、アミドワックス、高級
脂肪酸、高級アルコール及びモンタンワックスは、低温
定着性は良好であるが、耐オフセット性及び耐巻き付き
性が充分でない。
量ポリプロピレン等のポリオレフインワンクヌは、耐オ
フセント性は良好であるが、低温定着性が充分でなく、
カルナウバワックス、キャンデリラワックス等の植物性
ワックスは、耐オフセット性及び低温定着性は良好であ
るが、耐巻は付き性が充分でなく、また固形シリコーン
フェス、固形シリコーンオイル、アミドワックス、高級
脂肪酸、高級アルコール及びモンタンワックスは、低温
定着性は良好であるが、耐オフセット性及び耐巻き付き
性が充分でない。
しかも、従来の離型剤は、バインダー樹脂への分散性が
悪いため、現像中、離型剤がトナーから遊離して感光体
や現像スリーブに付着する、いわゆるフィルミングが多
く、長期に亘って安定して良質の画像を形成することは
困難であった。
悪いため、現像中、離型剤がトナーから遊離して感光体
や現像スリーブに付着する、いわゆるフィルミングが多
く、長期に亘って安定して良質の画像を形成することは
困難であった。
従って、本発明の目的は、定着時オフセント現象や熱ロ
ーラへの巻き付き現象を発生することなく、低温定着が
可能な上、現像中、フィルミングが少なく、トナー搬送
部材、トナー層厚規制部材、トナー補給補助部材へのト
ナーの融着を起こさず、従って長期に亘って安定して高
品質の画像が形成できる高速定着に好適な長寿命静電荷
像現像用乾式トナーを提供することにある。
ーラへの巻き付き現象を発生することなく、低温定着が
可能な上、現像中、フィルミングが少なく、トナー搬送
部材、トナー層厚規制部材、トナー補給補助部材へのト
ナーの融着を起こさず、従って長期に亘って安定して高
品質の画像が形成できる高速定着に好適な長寿命静電荷
像現像用乾式トナーを提供することにある。
本発明者らは、鋭意研究を重ねた結果、離型剤として特
定の化合物を含有するトナーによって、上記目的が達成
されることを見出し、本発明を完成するに至った。
定の化合物を含有するトナーによって、上記目的が達成
されることを見出し、本発明を完成するに至った。
即ち、本発明によれば、少なくとも低軟化点バインダー
樹脂、着色剤及び離型剤を主成分とするトナーにおいて
、該離型剤として下記の化合物から選びれる少なくとも
1種を用いたものであることを特徴とする静電荷像現像
用トナーが提供される。
樹脂、着色剤及び離型剤を主成分とするトナーにおいて
、該離型剤として下記の化合物から選びれる少なくとも
1種を用いたものであることを特徴とする静電荷像現像
用トナーが提供される。
(i)ポリオキシアルキレンミツロウ誘導体、(i)ア
ルキルグリセリンエーテル、 (iii)セレシンワックス、 (■)イボタワックス、 (V)ホホバワックス。
ルキルグリセリンエーテル、 (iii)セレシンワックス、 (■)イボタワックス、 (V)ホホバワックス。
本発明のトナーは、上記の特定の離型剤を含有するとい
う構成にしたことから、充分な耐オフセット性及び耐巻
き付き性を有し、その上良好な低温定着性を有するので
高速定着が可能であり、しかも離型剤のバインダーへの
分散性も良好なものとなる。従って、本発明のトナーを
用いると、感光体や現像スリーブへのトナーのフィルミ
ングが少なく、長期間に亘って安定した高品質の画像を
得ることができる。
う構成にしたことから、充分な耐オフセット性及び耐巻
き付き性を有し、その上良好な低温定着性を有するので
高速定着が可能であり、しかも離型剤のバインダーへの
分散性も良好なものとなる。従って、本発明のトナーを
用いると、感光体や現像スリーブへのトナーのフィルミ
ングが少なく、長期間に亘って安定した高品質の画像を
得ることができる。
本発明においては、離型剤としてポリオキシアルキレン
ミツロウ誘導体、アルキルグリセリンエーテル、セレシ
ンワックス、イボタワックス及びホホバワックスから選
ばた少なくとも1種が用いられる。
ミツロウ誘導体、アルキルグリセリンエーテル、セレシ
ンワックス、イボタワックス及びホホバワックスから選
ばた少なくとも1種が用いられる。
ミツロウは、蜜蜂の巣を加熱圧搾して採取したロウであ
り、その主成分はバルミチン酸ミリシス、セロチン酸ミ
リシス、ヒボガエン酸ミリシスなどのエステルであり、
他にリグノセリン酸、セロチン酸、モンタン酸、メリシ
ン酸、プシリン酸、ヒボガエン酸などの遊離酸或いは炭
化水素アルコール類を含むものである。本発明に使用す
るポリオキシアルキレンミツロウ誘導体は、ミツロウと
、ポリエチレングリコール、ポリプロピレングリコール
などのポリオキシアルキレン化合物とを混合、加熱する
ことにより得られるものであり、ミツロウ中遊離酸とポ
リオキシアルキレン化合物とが、エステル結合されたも
のである。
り、その主成分はバルミチン酸ミリシス、セロチン酸ミ
リシス、ヒボガエン酸ミリシスなどのエステルであり、
他にリグノセリン酸、セロチン酸、モンタン酸、メリシ
ン酸、プシリン酸、ヒボガエン酸などの遊離酸或いは炭
化水素アルコール類を含むものである。本発明に使用す
るポリオキシアルキレンミツロウ誘導体は、ミツロウと
、ポリエチレングリコール、ポリプロピレングリコール
などのポリオキシアルキレン化合物とを混合、加熱する
ことにより得られるものであり、ミツロウ中遊離酸とポ
リオキシアルキレン化合物とが、エステル結合されたも
のである。
また、セレシンワックスとは、オシケライトを精製した
無定形ロウ状物質をいい、主として一般式Cn2H2n
に相当し、一部CnH2n+2に相当する部分を含むも
のである。なお、イボタワックスとは、別名、虫白蝋、
イボタロウ、シナロウといわれ、イボタカイガラムシの
雌の分泌するロウから構成されるものである。成分とし
ては、脂肪族−塩基性酸のエステル93−95%(リグ
ノセリン酸オクタコシル、リグノセリン酸メリシン2%
、リグノセリン酸セリン]0%、セロチン酸セリル15
%、25−メチルへキサコサン酸、25−メチルへキサ
コサン酸60%、モンタン酸ヤリル、メリシン酸25−
メチルへキサコシル)樹脂1−1.5%、炭化水素2〜
3%(ヘプタコサン)で構成される。更に、ホホバワッ
クスは、ホホバの実から採取したホホバオイル(主成分
は炭素数40〜42の高級不飽和脂肪酸)に水素沁加し
て得られたワックスである。
無定形ロウ状物質をいい、主として一般式Cn2H2n
に相当し、一部CnH2n+2に相当する部分を含むも
のである。なお、イボタワックスとは、別名、虫白蝋、
イボタロウ、シナロウといわれ、イボタカイガラムシの
雌の分泌するロウから構成されるものである。成分とし
ては、脂肪族−塩基性酸のエステル93−95%(リグ
ノセリン酸オクタコシル、リグノセリン酸メリシン2%
、リグノセリン酸セリン]0%、セロチン酸セリル15
%、25−メチルへキサコサン酸、25−メチルへキサ
コサン酸60%、モンタン酸ヤリル、メリシン酸25−
メチルへキサコシル)樹脂1−1.5%、炭化水素2〜
3%(ヘプタコサン)で構成される。更に、ホホバワッ
クスは、ホホバの実から採取したホホバオイル(主成分
は炭素数40〜42の高級不飽和脂肪酸)に水素沁加し
て得られたワックスである。
次に、本発明のトナーに用いられる他の材料について説
明する。
明する。
まず、バインダー樹脂としては、軟化点が150℃以下
の低軟化点熱可塑性樹脂が用いられる。バインダー樹脂
の具体例としては、例えば次のものが挙げられる。
の低軟化点熱可塑性樹脂が用いられる。バインダー樹脂
の具体例としては、例えば次のものが挙げられる。
スチレン、パラクロロスチレン、α−メチルスチレン等
のスチレン類ニアクリル酸メチル、アクリル酸エチル、
アクリル酸n−プロピル、アクリル酸ラウリル、アクリ
ル酸2−エチルヘキシル等のα−メチレン脂肪族モノカ
ルボン酸エステル類;アクリロニトリル、メタアクリロ
ニトリルなどのビニルニトリル、2−ビニルピリジン、
4−ビニルピリジンなどのビニルピリジン類;ビニルメ
チルエーテル、ビニルインブチルエーテルなどのビニル
エーテル類:ビニルメチルケトン、ビニルエチルケトン
、メチルイソプロペニルケトンなどのビニルケトン類:
エチレン、プロピレン、イソプレン、ブタジェン等の不
飽和炭化水素類及びそのノ10ゲン化物、クロロプレン
などのハロゲン系不飽和炭化水素類などの単量体による
重合体、あるいはこれら単量体を2種以上組合せて得ら
れる共重合体、及びこれらの混合物、あるいは例えばロ
ジン変性フェノールホルマリン樹脂、エポキシ樹脂、ポ
リエステル樹脂、ポリウレタン樹脂、ポリアミド樹脂、
セルロース樹脂、ポリエーテル樹脂などの非ビニル縮合
系樹脂あるいはこれらと前記ビニル系樹脂との混合物等
。
のスチレン類ニアクリル酸メチル、アクリル酸エチル、
アクリル酸n−プロピル、アクリル酸ラウリル、アクリ
ル酸2−エチルヘキシル等のα−メチレン脂肪族モノカ
ルボン酸エステル類;アクリロニトリル、メタアクリロ
ニトリルなどのビニルニトリル、2−ビニルピリジン、
4−ビニルピリジンなどのビニルピリジン類;ビニルメ
チルエーテル、ビニルインブチルエーテルなどのビニル
エーテル類:ビニルメチルケトン、ビニルエチルケトン
、メチルイソプロペニルケトンなどのビニルケトン類:
エチレン、プロピレン、イソプレン、ブタジェン等の不
飽和炭化水素類及びそのノ10ゲン化物、クロロプレン
などのハロゲン系不飽和炭化水素類などの単量体による
重合体、あるいはこれら単量体を2種以上組合せて得ら
れる共重合体、及びこれらの混合物、あるいは例えばロ
ジン変性フェノールホルマリン樹脂、エポキシ樹脂、ポ
リエステル樹脂、ポリウレタン樹脂、ポリアミド樹脂、
セルロース樹脂、ポリエーテル樹脂などの非ビニル縮合
系樹脂あるいはこれらと前記ビニル系樹脂との混合物等
。
これらの中でも、高分子量成分と低分子量成分とを含有
し、その数平均分子量Mnに対する重量平均分子量My
の比My/Mn値が3.5以上のスチレン系樹脂やポリ
エステル樹脂は、良好な定着性と共にそれ自体非巻き付
き性を有する点で好ましいものである。
し、その数平均分子量Mnに対する重量平均分子量My
の比My/Mn値が3.5以上のスチレン系樹脂やポリ
エステル樹脂は、良好な定着性と共にそれ自体非巻き付
き性を有する点で好ましいものである。
また1本発明のトナーで用いられる着色剤としては、従
来からトナー用着色剤として使用さてきた顔料及び染料
の全てが適用される。具体的には、カーボンブラック、
ニグロシン染料、ランプ黒、スータンブラックSM、フ
ァースト・イエローG、ベンジジン・イエロー、ピグメ
ント・イエロー、インドファースト・オレンジ、イルガ
ジン・レッド、パラニトロアニリン・レッド、トルイジ
ン・レッド、カーミンFB、パーマネント・ボルドーF
RR、ピグメント・オレンジR、リソール・レッド2G
、レーキ・レッドC、ローダミンFB、ローダミンBレ
ーキ、メチル・バイオレッドBレーキ、フタロシアニン
ブルー、ピグメントブルー、ブリリアント・グリーンB
、フタロシアニングリーン、オイルイエローGG、ザポ
ン・ファーストイエローCGC、カヤセットY963、
カヤセットYG、スミプラストイエローGG、ザポンフ
ァーストオレンジRR、オイル・スカーレソト、スミブ
ラストオレンジ6、オラゾール・ブラウンB。
来からトナー用着色剤として使用さてきた顔料及び染料
の全てが適用される。具体的には、カーボンブラック、
ニグロシン染料、ランプ黒、スータンブラックSM、フ
ァースト・イエローG、ベンジジン・イエロー、ピグメ
ント・イエロー、インドファースト・オレンジ、イルガ
ジン・レッド、パラニトロアニリン・レッド、トルイジ
ン・レッド、カーミンFB、パーマネント・ボルドーF
RR、ピグメント・オレンジR、リソール・レッド2G
、レーキ・レッドC、ローダミンFB、ローダミンBレ
ーキ、メチル・バイオレッドBレーキ、フタロシアニン
ブルー、ピグメントブルー、ブリリアント・グリーンB
、フタロシアニングリーン、オイルイエローGG、ザポ
ン・ファーストイエローCGC、カヤセットY963、
カヤセットYG、スミプラストイエローGG、ザポンフ
ァーストオレンジRR、オイル・スカーレソト、スミブ
ラストオレンジ6、オラゾール・ブラウンB。
ザボンファーストスカーレットCG、アイゼンスピロン
・レッド・BEH、オイルピンクOPなどがある。
・レッド・BEH、オイルピンクOPなどがある。
これら着色剤の使用量は、バインダー樹脂に対し通常、
1−30重量%、好ましくは3−20重量%程度である
。
1−30重量%、好ましくは3−20重量%程度である
。
また、本発明のトナーは、更に磁性材料を含有させ、磁
性トナーとしても使用することができる。
性トナーとしても使用することができる。
本発明の磁性トナー中に含まれる磁性材料としては、マ
グネタイト、ヘマタイト、フェライト等の酸化鉄、鉄、
コバルト、ニッケルのような金属あるいはこれら金属と
アルミニウム、コバルト、銅、鉛、マグネシウム、錫、
亜鉛、アンチモン、ベリリウム、ビスマス、カドミウム
、カルシウム、マンガン、セレン、チタン、タングステ
ン、バナジウムのような金属との合金及びその混合物な
どが挙げられる。
グネタイト、ヘマタイト、フェライト等の酸化鉄、鉄、
コバルト、ニッケルのような金属あるいはこれら金属と
アルミニウム、コバルト、銅、鉛、マグネシウム、錫、
亜鉛、アンチモン、ベリリウム、ビスマス、カドミウム
、カルシウム、マンガン、セレン、チタン、タングステ
ン、バナジウムのような金属との合金及びその混合物な
どが挙げられる。
これらの強磁性体は、平均粒径が0.1−2μm程度の
ものが望ましく、トナー中に含有させる量としては、通
常、トナー重量の15−70重量である。
ものが望ましく、トナー中に含有させる量としては、通
常、トナー重量の15−70重量である。
更に、本発明のトナーには、必要に応じて添加物を混合
することもできる。添加物としては、例えば四フフ化エ
チレン樹脂、ステアリン酸亜鉛のような滑剤あるいは酸
化セリウム、炭化ケイ素等の研磨剤、あるいは例えばコ
ロイダルシリカ、酸化アルミニウムなどの流動性付与剤
、ケーキング防止剤、あるいは例えばカーボンブラック
、酸化錫等の導電性付与剤、あるいは低分子量ポリオレ
フィンなどの定着助剤等がある。
することもできる。添加物としては、例えば四フフ化エ
チレン樹脂、ステアリン酸亜鉛のような滑剤あるいは酸
化セリウム、炭化ケイ素等の研磨剤、あるいは例えばコ
ロイダルシリカ、酸化アルミニウムなどの流動性付与剤
、ケーキング防止剤、あるいは例えばカーボンブラック
、酸化錫等の導電性付与剤、あるいは低分子量ポリオレ
フィンなどの定着助剤等がある。
なお、本発明のトナーは、二成分系現像剤として用いる
場合には、キャリア粉と混合して用いられる。この場合
、キャリアとしては、公知のものがすべて使用可能であ
り、例えば鉄粉、フェライト粉、ニッケル粉のような磁
性を有する粉体、ガラスピーズ等及びこれらの表面を樹
脂などで処理したものなどが挙げられる。
場合には、キャリア粉と混合して用いられる。この場合
、キャリアとしては、公知のものがすべて使用可能であ
り、例えば鉄粉、フェライト粉、ニッケル粉のような磁
性を有する粉体、ガラスピーズ等及びこれらの表面を樹
脂などで処理したものなどが挙げられる。
次に、本発明を実施例により更に詳細に説明するが、本
発明はこれらに限定されるもρではない。
発明はこれらに限定されるもρではない。
なお、以下において示す部はいずれも重量基準である。
実施例I
GBW−25(ソルビットミツロウ(6EO)3
5部カーボンブランク(三菱カーボン社製$44)
10部上記組成の混合物をヘンシェルミキサーで充分混
合した後、2本ロールで70−90℃の温度で約40分
間加熱溶融し、混練し、室温まで冷却した。得られた混
練物を粉砕、分級して粒径5〜IO,mのトナーを得た
。
5部カーボンブランク(三菱カーボン社製$44)
10部上記組成の混合物をヘンシェルミキサーで充分混
合した後、2本ロールで70−90℃の温度で約40分
間加熱溶融し、混練し、室温まで冷却した。得られた混
練物を粉砕、分級して粒径5〜IO,mのトナーを得た
。
本トナー100部に対して、コロイダルシリカ0.3部
を添加して、トナーとした。
を添加して、トナーとした。
このトナーを第1図に示すような現像装置にセントして
画像出しを行ない、定着温度130℃のテフロンローラ
で定着を行なったところ、良好な画像が得られ、その画
像は初期は勿論、10万枚プリント後も良質の画像が形
成された。また、35℃、90%RHと10℃、I5%
RHという高温高湿、低温低湿、環境下でも、常温常湿
環境下のもとての複写と同様の画像が得られ、感光体へ
のフィルミングも認められなかった。
画像出しを行ない、定着温度130℃のテフロンローラ
で定着を行なったところ、良好な画像が得られ、その画
像は初期は勿論、10万枚プリント後も良質の画像が形
成された。また、35℃、90%RHと10℃、I5%
RHという高温高湿、低温低湿、環境下でも、常温常湿
環境下のもとての複写と同様の画像が得られ、感光体へ
のフィルミングも認められなかった。
実施例2
実施例1におけるポリオキシエチレンミツロウ誘導体の
代わりに、ステアリルグリセリンエーテル(バチルアル
コール100)を用いた以外は、実施例1と同様にして
トナーを得た。
代わりに、ステアリルグリセリンエーテル(バチルアル
コール100)を用いた以外は、実施例1と同様にして
トナーを得た。
続いて、このトナーを用いて実施例1と同様にしてコピ
ーテストを行なったところ、実施例1と同様な良好な画
像が得られ、その画像は初期は勿論、 10万枚プリン
ト後も良質の画像が形成された。
ーテストを行なったところ、実施例1と同様な良好な画
像が得られ、その画像は初期は勿論、 10万枚プリン
ト後も良質の画像が形成された。
、 また、35℃、90%RHと10℃、15%RHと
いう高温高湿、低温低湿、環境下でも、常温常温環境下
のもとての複写と同様の画像が得られ、感光体へのフィ
ミングも認められなかった。
いう高温高湿、低温低湿、環境下でも、常温常温環境下
のもとての複写と同様の画像が得られ、感光体へのフィ
ミングも認められなかった。
実施例3
実施例1におけるポリオキシエチレンミツロウ誘導体の
代わりに、七レシンワックス(野田ワックス社製)を用
いた以外は、実施例1と同様にしてトナーを得た。
代わりに、七レシンワックス(野田ワックス社製)を用
いた以外は、実施例1と同様にしてトナーを得た。
続いて、このトナーを用いて実施例1と同様にしてコピ
ーテストを行なったところ、実施例1と同様な良好な画
像が得られ、その画像は初期は勿論、10万枚プリント
後も良質の画像が形成された。
ーテストを行なったところ、実施例1と同様な良好な画
像が得られ、その画像は初期は勿論、10万枚プリント
後も良質の画像が形成された。
また、35℃、90%RHと10℃、15%RHという
高温高湿、低温低湿、環境下でも、常温常湿環境下のも
とての複写と同様の画像が得られ、感光体へのフィミン
グも認められなかった。
高温高湿、低温低湿、環境下でも、常温常湿環境下のも
とての複写と同様の画像が得られ、感光体へのフィミン
グも認められなかった。
実施例4
実施例1におけるポリオキシエチレンミツロウ誘導体の
代わりに、イボタワックス(野田ワックス社製)を用い
た以外は、実施例1と同様にしてトナーを得た。
代わりに、イボタワックス(野田ワックス社製)を用い
た以外は、実施例1と同様にしてトナーを得た。
続いて、このトナーを用いて実施例1と同様にしてコピ
ーテストを行なったところ、実施例1と同様な良好な画
像が得られ、その画像は初期は勿論、lO万枚プリント
後も良質の画像が形成された。
ーテストを行なったところ、実施例1と同様な良好な画
像が得られ、その画像は初期は勿論、lO万枚プリント
後も良質の画像が形成された。
また、35℃、90%RHと10℃、15%RHという
高温高湿、低温低湿、環境下でも、常温常温環境下のも
とての複写と同様の画像が得られ、感光体へのフィミン
グも認められなかった。
高温高湿、低温低湿、環境下でも、常温常温環境下のも
とての複写と同様の画像が得られ、感光体へのフィミン
グも認められなかった。
実施例5
実施例1におけるポリオキシエチレンミツロウ誘導体の
代わりに、ホホバワックス(水添ホホバ油)を用いた以
外は、実施例Iと同様にしてトナーを得た。
代わりに、ホホバワックス(水添ホホバ油)を用いた以
外は、実施例Iと同様にしてトナーを得た。
続いて、このトナーを用いて実施例1と同様にしてコピ
ーテストを行なったところ、実施例1と同様な良好な画
像が得られ、その画像は初期は勿論、10万枚プリント
後も良質の画像が形成された。
ーテストを行なったところ、実施例1と同様な良好な画
像が得られ、その画像は初期は勿論、10万枚プリント
後も良質の画像が形成された。
また、35℃、90%RHと10℃、15%RHという
高温高温、低温低湿、環境下でも、常温常湿環境下のも
とての複写と同様の画像が得られ、感光体へのフィミン
グも認められなかった。
高温高温、低温低湿、環境下でも、常温常湿環境下のも
とての複写と同様の画像が得られ、感光体へのフィミン
グも認められなかった。
実施例6
カーボンブランク(三菱カーボン社製$44) 13
部上記組成の混合物を用いて、実施例1と同様にして粒
径5〜10μmのトナーを得た。このトナーを第1図に
示すような現像装置にセットして画像出し、及び定着温
度130℃のテフロンローラでの定着を行なったところ
、良好な画像が得られ、その画像はlO万枚プリント後
も変わらなかった。
部上記組成の混合物を用いて、実施例1と同様にして粒
径5〜10μmのトナーを得た。このトナーを第1図に
示すような現像装置にセットして画像出し、及び定着温
度130℃のテフロンローラでの定着を行なったところ
、良好な画像が得られ、その画像はlO万枚プリント後
も変わらなかった。
実施例7
実施例6におけるポリオキシエチレンミツロウ誘導体の
代わりに、ステアリルグリセリンエーテル(バチルアル
コールEX)を用いた以外は、実施例6と同様にしてト
ナーを得た。
代わりに、ステアリルグリセリンエーテル(バチルアル
コールEX)を用いた以外は、実施例6と同様にしてト
ナーを得た。
続いて、このトナーを用いて実施例6と同様にしてコピ
ーテストを行なったところ、実施例6と同様に良好な画
像が得られ、その画像は10万枚プリント後も変わらな
かった。
ーテストを行なったところ、実施例6と同様に良好な画
像が得られ、その画像は10万枚プリント後も変わらな
かった。
比較例
実施例1におけるポリオキシエチレンミツロウ誘導体の
代わりに、低分子量ポリプロピレン(三洋化成工業社製
660P)を用いた以外は、実施例1と同様にしてトナ
ーを得た。
代わりに、低分子量ポリプロピレン(三洋化成工業社製
660P)を用いた以外は、実施例1と同様にしてトナ
ーを得た。
本トナー100部に対して、コロイダルシリカ0.3部
を添加して、トナーとした。
を添加して、トナーとした。
次に、このトナーを第1図に示すような現像装置にセッ
トし画像出しを行なったところ、定着温度130℃では
、ローラー巻き付きが生じた。
トし画像出しを行なったところ、定着温度130℃では
、ローラー巻き付きが生じた。
本発明の静電荷像現像用トナーは、前記したように、特
定の離型剤を使用するという構成にしたことから、 (イ)充分なオフセット性と耐巻き付き性を有する、(
ロ)低温定着が可能なので、高速定着ができる、(ハ)
離型剤のバインダー樹脂への分散性が良い、という卓越
した効果を奏する。
定の離型剤を使用するという構成にしたことから、 (イ)充分なオフセット性と耐巻き付き性を有する、(
ロ)低温定着が可能なので、高速定着ができる、(ハ)
離型剤のバインダー樹脂への分散性が良い、という卓越
した効果を奏する。
従って、本発明のトナーを使用すると、現像中感光体や
現像スリーブへのトナーフィルミングが少なく、長期間
に亘って安定して高品質の画像を形成できる。
現像スリーブへのトナーフィルミングが少なく、長期間
に亘って安定して高品質の画像を形成できる。
第1図は本発明の実施例で使用した現像装置の概略図で
ある。 】・静電潜像担持体、2・・トナー搬送部材、3・・ト
ナー層厚規制部材、4・・トナー供給部材、5・撹拌羽
根、6・トナー、7・・トナータンク。 特許出願人 株式会社 リ コ −
ある。 】・静電潜像担持体、2・・トナー搬送部材、3・・ト
ナー層厚規制部材、4・・トナー供給部材、5・撹拌羽
根、6・トナー、7・・トナータンク。 特許出願人 株式会社 リ コ −
Claims (1)
- (1)少なくとも低軟化点バインダー樹脂、着色剤及び
離型剤を主成分とするトナーにおいて、該離型剤として
下記の化合物から選ばれる少なくとも1種を用いたもの
であることを特徴とする静電荷像現像用トナー。 (i)ポリオキシアルキレンミツロウ誘導体、(ii)
アルキルグリセリンエーテル、 (iii)セレシンワックス、 (iv)イボタワックス、 (v)ホホバワックス。