JPH01174551A - 塩素含有樹脂組成物 - Google Patents
塩素含有樹脂組成物Info
- Publication number
- JPH01174551A JPH01174551A JP33462987A JP33462987A JPH01174551A JP H01174551 A JPH01174551 A JP H01174551A JP 33462987 A JP33462987 A JP 33462987A JP 33462987 A JP33462987 A JP 33462987A JP H01174551 A JPH01174551 A JP H01174551A
- Authority
- JP
- Japan
- Prior art keywords
- chlorine
- containing resin
- lead
- titanium oxide
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明は塩素含有樹脂組成物に間する。
［従来の技術］
従来、塩素含有樹脂中に無機鉛系安定剤と酸化チタンが
共存する場合、太陽光線や殺菌灯、水銀灯、蛍光灯など
の光に接すると短時間で黒変する欠点を有していた。そ
の理由は詳らかでないが、酸化チタンの鉛による光還元
反応によるものと考えられる。
共存する場合、太陽光線や殺菌灯、水銀灯、蛍光灯など
の光に接すると短時間で黒変する欠点を有していた。そ
の理由は詳らかでないが、酸化チタンの鉛による光還元
反応によるものと考えられる。
２ＴｉＯ□＋ｐｂコ’−＋Ｔｔ ２ｏ ３＋ ｐ ｂ
。
。
また無機鉛系安定剤や酸化チタンはプレートアウト現象
を起こし易く、しかも無機鉛系安定剤と酸化チタンを併
用する場合は、カレンダーロール表面や押出機に無機鉛
系安定剤や酸化チタンが著しく析出し、成型を困難にし
ていたのが現状である。
を起こし易く、しかも無機鉛系安定剤と酸化チタンを併
用する場合は、カレンダーロール表面や押出機に無機鉛
系安定剤や酸化チタンが著しく析出し、成型を困難にし
ていたのが現状である。
［発明が解決しようとする問題点］
本発明者等は塩素含有樹脂中に無機鉛系安定剤と酸化チ
タンが共存しても光に黒変せず、且つプレートアウトの
ない塩素含有樹脂組成物を提供することを目的とした。
タンが共存しても光に黒変せず、且つプレートアウトの
ない塩素含有樹脂組成物を提供することを目的とした。
［問題点を解決するための手段］
本発明は無機鉛系安定剤、酸化チタンを含有する塩素含
有樹脂が光に接しても黒変しなくするため、且つプレー
トアウトを防止するため、更に水酸化マグネシウムを塩
素含有樹脂に含有させることにより、目的を達成し得る
ことを見出し本発明を完成した。
有樹脂が光に接しても黒変しなくするため、且つプレー
トアウトを防止するため、更に水酸化マグネシウムを塩
素含有樹脂に含有させることにより、目的を達成し得る
ことを見出し本発明を完成した。
本発明の塩素含有樹脂とは、塩化ビニル単独重合体また
は塩化ビニルを主体とした樹脂であって、例えば、塩化
ビニルと、酢酸ビニル、塩化ビニリデン、エチレン、プ
ロピレン、メタアクリル酸エステル、ウレタン樹脂との
共重合体やグラフト重合体あるいはこれら樹脂とのブレ
ンド物、等である。
は塩化ビニルを主体とした樹脂であって、例えば、塩化
ビニルと、酢酸ビニル、塩化ビニリデン、エチレン、プ
ロピレン、メタアクリル酸エステル、ウレタン樹脂との
共重合体やグラフト重合体あるいはこれら樹脂とのブレ
ンド物、等である。
無機鉛系安定剤とは、三塩基性硫酸鉛などの多塩基性硫
酸鉛、二塩基性亜硫酸鉛、二塩基性亜燐酸鉛、二塩基性
亜硫酸亜燐酸鉛、二塩基性フタル酸鉛、二塩基性マレイ
ン酸鉛、塩基性炭酸鉛等であり、通常は樹脂に対し、０
．１〜１０ｆｆｉ量部含有させる。
酸鉛、二塩基性亜硫酸鉛、二塩基性亜燐酸鉛、二塩基性
亜硫酸亜燐酸鉛、二塩基性フタル酸鉛、二塩基性マレイ
ン酸鉛、塩基性炭酸鉛等であり、通常は樹脂に対し、０
．１〜１０ｆｆｉ量部含有させる。
水酸化マグネシウムとしては、海水から製造するもので
も鉱物から精製したものでもどちらでも良いが、塩素含
有樹脂に対して容易に分散させるには、０．１〜数ミク
ロンの平均粒子径のものが好ましい、さらに、樹脂への
相溶性を向上させるため、表面に脂肪酸、脂肪酸エステ
ル、シリコンオイル、シランカップリング剤、チタンカ
ップリング剤、ジルコニアカップリング剤、リン系カッ
プリング剤、アルミキレート系カップリング剤、ジルコ
アルミネート系カップリング剤、ボロン系カップリング
剤で処理を施したものが好ましい。これらは、通常樹脂
に対し、０．１〜５重量部含有させる。更に好ましくは
、水酸化マグネシウムの一部を亜鉛化合物に置き変えて
も、あるいは水酸化マグ、ネシウムはそのままで更に亜
鉛化合物をＴｈｏえても、効果が発揮される。酸化チタ
ンは通常樹脂に対し、０゜０１−１０重量部含有する。
も鉱物から精製したものでもどちらでも良いが、塩素含
有樹脂に対して容易に分散させるには、０．１〜数ミク
ロンの平均粒子径のものが好ましい、さらに、樹脂への
相溶性を向上させるため、表面に脂肪酸、脂肪酸エステ
ル、シリコンオイル、シランカップリング剤、チタンカ
ップリング剤、ジルコニアカップリング剤、リン系カッ
プリング剤、アルミキレート系カップリング剤、ジルコ
アルミネート系カップリング剤、ボロン系カップリング
剤で処理を施したものが好ましい。これらは、通常樹脂
に対し、０．１〜５重量部含有させる。更に好ましくは
、水酸化マグネシウムの一部を亜鉛化合物に置き変えて
も、あるいは水酸化マグ、ネシウムはそのままで更に亜
鉛化合物をＴｈｏえても、効果が発揮される。酸化チタ
ンは通常樹脂に対し、０゜０１−１０重量部含有する。
上記の他に通常塩素含有樹脂に加えられる熱安定剤、滑
剤、可塑剤、酸化防止剤、紫外線吸収剤、充填剤、強化
剤、顔料等を適宜添加して良いのは言うまでもない。
剤、可塑剤、酸化防止剤、紫外線吸収剤、充填剤、強化
剤、顔料等を適宜添加して良いのは言うまでもない。
［発明の効果］
以上のように、本発明組成物によれば、光に接しても変
色せず、且つプレートアウトがなくその他の性能も低下
しないのである。
色せず、且つプレートアウトがなくその他の性能も低下
しないのである。
以下実施例により具体的に説明する。
（コンパウンド作成条件）
下記の配合組成物を、スーパーミキサーで樹脂温度１４
０℃まで昇温させて作成した。
０℃まで昇温させて作成した。
（押出条件）
上記のコンパウンドを５０ｍｍ単軸押出機で押出した。
Ｃ，１５０Ｃ２１６０Ｃ３１６０Ｈ１７０Ｄ １９０
ベルトダイ使用 、３０回転 （プレートアウトの評価） ２時間運転後、押出機のスクリュー先端とダイスへの付
着物の多い少ないを肉眼で判定した。
ベルトダイ使用 、３０回転 （プレートアウトの評価） ２時間運転後、押出機のスクリュー先端とダイスへの付
着物の多い少ないを肉眼で判定した。
（配合組成）
ＰＶＣ（Ｐ［１００） １００三塩基性硫酸
鉛 ３ 二塩基性ステアリン酸鉛 ０．５ステアリン酸
鉛 １．５ステアリン酸カルシウム
０．５酸化チタン 表−
１水酸化マグネシウム 表−１（耐光性） 押出機で作成したベルト状のシートをサンシャインウェ
ザ−メータで３００時間曝露後の変色を調べた。
鉛 ３ 二塩基性ステアリン酸鉛 ０．５ステアリン酸
鉛 １．５ステアリン酸カルシウム
０．５酸化チタン 表−
１水酸化マグネシウム 表−１（耐光性） 押出機で作成したベルト状のシートをサンシャインウェ
ザ−メータで３００時間曝露後の変色を調べた。
Claims (1)
- 無機鉛系安定剤、酸化チタン及び水酸化マグネシウムを
含有する、塩素含有樹脂組成物。