JP7491342B2 - 両面粘着シート、画像表示装置構成用部材を有する積層体、積層体形成キット及び両面粘着シートの使用 - Google Patents
両面粘着シート、画像表示装置構成用部材を有する積層体、積層体形成キット及び両面粘着シートの使用 Download PDFInfo
- Publication number
- JP7491342B2 JP7491342B2 JP2022090086A JP2022090086A JP7491342B2 JP 7491342 B2 JP7491342 B2 JP 7491342B2 JP 2022090086 A JP2022090086 A JP 2022090086A JP 2022090086 A JP2022090086 A JP 2022090086A JP 7491342 B2 JP7491342 B2 JP 7491342B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- double
- sensitive adhesive
- adhesive sheet
- sided pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このように、より実使用環境下に近い条件下において、折れや剥がれが発生することのない、高い折り曲げ耐性を有する両面粘着シートが求められる。
本発明の両面粘着シート(以下「本両面粘着シート」とも称する。)は、基材レスであって、少なくとも次の(1)~(4)の特性を有する。
なお、基材レスの両面粘着シートとは、支持体となる基材を有さず、粘着剤層だけを有する両面粘着シートをいう。
また、「流れ」とは、屈曲試験後に屈曲線の周辺の粘着シートが盛り上がって見える現象である。
また、前記「流れ」は、せん断貯蔵弾性率(G’)が低く、上下のフィルムによって挟まれた粘着シートが屈曲により押し出され、これが蓄積することによって生じる現象であることを明らかにした。
これらの中でも、少なくとも1つの画像表示装置構成用部材が、フレキシブル部材であることが好ましく、とりわけ、フレキシブル有機EL(Electronic Luminescent)ディスプレイパネルであることが好ましい。
本両面粘着シートは、少なくとも(メタ)アクリル酸エステル(共)重合体(A)を含有する粘着剤組成物(以下「本粘着剤組成物」という。)から形成される。
上記(メタ)アクリル酸エステル(共)重合体(A)としては、例えばアルキル(メタ)アクリレートの単独重合体の他、これと共重合可能なモノマー成分を重合することにより得られる共重合体を挙げることができる。
中でも、(メタ)アクリル酸エステル(共)重合体(A)が、2成分以上の共重合成分を含み、少なくとも1つの共重合成分が、アルキル(メタ)アクリレート及び/又は下記共重合性モノマーA~Hの何れかであることが好ましい。
(2)また、上記共重合性モノマーAを含まず、共重合性モノマーB又はEの何れかもしくは両方を含むことが特に好ましい。共重合性モノマーB又はEの何れか若しくは両方を含むことで、耐腐食特性、接着性及び耐湿熱白化特性の兼備が可能となる。
なお、「共重合性モノマーAを含まない」とは、“実質的に含まない”の意であり、完全に含まない場合のみならず、(メタ)アクリル酸エステル(共)重合体中に、共重合性モノマーAが0.5質量%未満、好ましくは、0.1質量%未満で含むことを包含する。
(3)さらに、上記アルキル(メタ)アクリレートの中でも、(メタ)アクリロイル基と3級炭素原子が結合したアルキル(メタ)アクリートが好ましい。このようなアルキル(メタ)アクリレートを用いることで、本両面粘着シートの高温側(100℃~150℃)のせん断貯蔵弾性率(G’)をフラット化し易くなる。
これらは1種又は2種以上を組み合わせてもよい。
(メタ)アクリル酸エステル(共)重合体(A)が、重合性モノマーAを含むことにより、Tgを低く維持することができるため、共重合性モノマーBの選択の幅が広がり、折り曲げ耐性と、耐湿熱白化性や接着力、耐久性などの基本的な粘着性能とのバランス化が容易になる。
なお、本粘着剤組成物が無溶剤系であって、ホットメルトによって製膜する場合、上記(メタ)アクリル酸エステル(共)重合体(A)の質量平均分子量は、10万~90万であることが好ましく、中でも15万以上或いは75万以下であることがより好ましく、20万以上或いは60万以下であることがもっとも好ましい。
(メタ)アクリル酸エステル(共)重合体(A)の質量平均分子量が、上記範囲にあることで、ホットメルト製膜が可能となる。
以上の点から、(メタ)アクリル酸エステル(共)重合体(A)の質量平均分子量は、中でも15万~75万であることがより好ましく、その中でも20万以上或いは6万以下であることが最も好ましい。
本粘着剤組成物は、上記(メタ)アクリル酸エステル(共)重合体(A)の他、架橋剤(B)を含有するものであることが好ましい。
本粘着剤組成物は、上記(メタ)アクリル酸エステル(共)重合体(A)及び架橋剤(B)の他、光開始剤(C)を含有するものであることが好ましい。
本粘着剤組成物は、上述した(メタ)アクリル酸エステル(共)重合体(A)、架橋剤(B)及び光開始剤(C)の他にも、通常の粘着組成物に配合されている公知の成分を含有してもよい。例えば粘着付与樹脂、酸化防止剤、光安定化剤、金属不活性化剤、防錆剤、老化防止剤、吸湿剤、加水分解防止剤、帯電防止剤、消泡剤、無機粒子などの各種の添加剤を適宜含有させることが可能である。本粘着剤組成物は、中でも、防錆剤を含有することが好ましく、具体的には、ベンゾトリアゾール、イミダゾール、トリアゾール、テトラゾール、チアゾール及びこれらの誘導体からなる群より選択される防錆剤を使用することが好ましい。
本両面粘着シートは、ガラス転移温度(Tg)が、-50℃~-20℃の範囲内にある。
なお、本両面粘着シートが多層の場合、各層全ての粘着剤層のガラス転移温度(Tg)が上記範囲にある必要はなく、複数の粘着剤層から構成された粘着剤層全体、すなわち、本両面粘着シートのガラス転移温度が上記範囲にあれば良い。
本両面粘着シートは、周波数1Hz、温度100℃における貯蔵弾性率G’が、2.0×103~3.0~104Paの範囲内にあるものである。
すなわち、本両面粘着シートが、折り曲げ耐久性を有するには、何万回レベルの繰り返し折り曲げ試験、言い換えると、繰り返し動作に対する耐性を備えなければならない。
このように、高分子材料が繰り返し動作に対する耐性を具備する為には、高分子材料の長時間側の粘弾性挙動、すなわち温度-時間換算則では、高分子材料の高温側の粘弾性挙動が関係してくることになる。
そして、本発明者らは、本粘着シートの高温側の粘弾性挙動に着目して、検討を重ねることにより、温度100℃の領域における粘弾性挙動が折り曲げ耐久性に大きく寄与することを見出したのである。
温度-20℃(低温)でのせん断貯蔵弾性率(G’)が上記の範囲内にあれば、室温での粘着性やタック性を損なうことなく折り曲げ耐性を付与しやすいため、接着力や耐久性、加工時や貼合時のハンドリング性が向上する等の利点を有することができる。
また、上記と同様の理由から、紫外線の照射量は、250mJ/cm2以上とすることが好ましく、500mJ/cm2以上とすることがさらに好ましく、1000mJ/cm2以上とすることが最も好ましい。
フレキシブルディスプレイは、実使用環境下においては、様々な折り曲げ速度に対する耐性を具備しなければならない。
また、屈曲試験においても、屈曲開始から屈曲終了時までは屈曲試験機の構造、フィルム積層体のたわみ等によって、両面粘着シートが屈曲する角速度は常に変化していることが予測される。
このように、屈曲試験においては、両面粘着シートは、さまざまな速度で変形する。このため特に、フレキシブルディスプレイに用いられる両面粘着シートには、想定される様々な速度領域において、上述した「座屈」や「流れ」が生じないことが求められる。
本両面粘着シートの厚みは、10μm以上150μm以下である。
本両面粘着シートの製造方法としては、公知の製造方法を採用することができる。以下に、その一例を示す。
また、本粘着剤組成物は、上述のとおり、溶剤を含まない無溶剤系として使用することできる。無溶剤系として使用することで溶剤が残存せず、耐熱性及び耐光性が高まるという利点も備えることができる。
画像表示装置構成用フレキシブル部材を有する本発明の積層体(以下「本積層体」とも称する。)は、上述した特性を有する本両面粘着シートと、画像表示装置構成用フレキシブル部材とが積層された構成を有するものである。
これらの中でも、少なくとも1つの画像表示装置構成用フレキシブル部材が、フレキシブル部材であることが好ましく、とりわけ、フレキシブル有機EL(Electronic Luminescent)ディスプレイパネルであることが好ましい。
さらに、本積層体は、曲面形状を有していることが好ましい。具体的には、本積層体の外形が円弧状やその他の曲面である場合を挙げることができる。さらに具体的には、円弧状、懸垂線状、放物線状、ベジェ曲線状、スプライン曲線状、たわみ曲線、その他の曲面形状を有する、表面保護パネルを備えた積層体を挙げることができる。
画像表示装置構成用フレキシブル部材の貼合において、上述した本両面粘着シートを用いると、該部材を折り曲げて使用した場合であっても、粘着材がはみ出したり、凝集破壊したりすることなく、また、両面粘着シートに折れ痕が付くこともない。
これらの中でも、少なくとも1つの画像表示装置構成用フレキシブル部材が、フレキシブル部材であることが好ましく、とりわけ、フレキシブル有機EL(Electronic Luminescent)ディスプレイパネルであることが好ましい。
本積層体を形成するための本発明の積層体形成キット(以下、「本キット」とも称する)は、画像表示装置構成用フレキシブル部材と、該フレキシブル部材に貼合するための両面粘着シートとを有し、該両面粘着シートが上述した本両面粘着シートであることを特徴とするものである。
本積層体を形成するための積層体形成キットとは、本積層体を形成するための材料一式の意味であり、材料同士は接合されていない状態での組み合わせである。
これらの中でも、少なくとも1つの画像表示装置構成用フレキシブル部材が、フレキシブル部材であることが好ましく、とりわけ、フレキシブル有機EL(Electronic Luminescent)ディスプレイパネルであることが好ましい。
本明細書において「X~Y」(X,Yは任意の数字)と表現する場合、特にことわらない限り「X以上Y以下」の意と共に、「好ましくはXより大きい」或いは「好ましくはYより小さい」の意も包含する。
また、「X以上」(Xは任意の数字)或いは「Y以下」(Yは任意の数字)と表現した場合、「Xより大きいことが好ましい」或いは「Y未満であることが好ましい」旨の意図も包含する。
一般的に「シート」とは、JISにおける定義上、薄く、その厚さが長さと幅のわりには小さく平らな製品をいい、一般的に「フィルム」とは、長さ及び幅に比べて厚さが極めて小さく、最大厚さが任意に限定されている薄い平らな製品で、通常、ロールの形で供給されるものをいう(日本工業規格JISK6900)。しかし、シートとフィルムの境界は定かでなく、本発明において文言上両者を区別する必要がないので、本発明においては、「フィルム」と称する場合でも「シート」を含むものとし、「シート」と称する場合でも「フィルム」を含むものとする。
なお、以下の実施例及び比較例において、下記の物性測定、処理については、下記条件で行った。
(1)実施例及び比較例で作製した両面粘着シート1~16を、50mm×100mmに裁断し、PETフィルム厚み0.38mm×50mm×100mmに貼合する。
(2)貼合したサンプルをPET(0.1mm×50mm×100mm)と貼合した積層体を作製する。
(3)PET38μmを内側として、作製された積層体を、折り曲げ試験機DLDMLH-FS(ユアサシステム製)を用いて、次の試験条件で試験を行う。
・曲率半径r=3mm
・試験速度=60rpm
・試験回数=10万回
(4)試験後の積層体を目視観察し、両面粘着シートに折れ痕のついているものと、被着体に両面粘着シートの剥がれがあるものを「×」、目視観察で変化のないものを「○」として評価した。
投影機とスクリーンの間に折り曲げ試験後のサンプルを設置し、スクリーンに映った折り曲げ試験後のサンプルに歪みの有無で、両面粘着シートに折れ痕のついているものと、被着体からの両面粘着シートの剥がれを判別した。
実施例及び比較例で作製した両面粘着シート1~16の貯蔵弾性率G’は、レオメトリックス社製の粘弾性測定装置「ダイナミックアナライザー RDAII」を用いて剪断法により、次の条件で測定した。
・治具:Φ25mmパラレルプレート
・歪み:0.5%
・周波数:1Hz
・温度:-70~200℃(-70℃から昇温速度3℃/minで測定)
・試料厚さ:500μm
・治具:Φ25mmパラレルプレート
・歪み:0.5%
・周波数:1Hz
ガラス基板(45mm×45mm)上に、厚さ50Åの銅薄膜を形成し、銅薄膜変色試験用ガラス基板を作製した。
アクリル酸エステル共重合体ポリマーA:100重量部に対し、光開始剤として日本シイベルヘグナー社製の商品名「エザキュア TZT」(4-メチルベンゾフェノン):0.6重量部と、架橋モノマーとして大阪有機化学社製の商品名「ビスコートV260(1,9-ノナンジオールジアクリレート)」:1.0重量部とを添加して紫外線硬化型の粘着剤組成物1を得た。
実施例1で使用した粘着剤組成物1を、厚さ75μmと厚さ100μmのポリエチレンテレフタレート製の離型フィルムとの間に挟んで、厚み0.1mmのシート状にホットメルト成形し、高圧水銀ランプを用いて、該離型フィルム越しに積算光量500mJ/cm2の紫外線を照射させて両面粘着シート2を得た。
実施例1で使用した粘着剤組成物1を、厚さ75μmと厚さ100μmのポリエチレンテレフタレート製の離型フィルムとの間に挟んで、厚み0.1mmのシート状にホットメルト成形し、高圧水銀ランプを用いて、該離型フィルム越しに積算光量1500mJ/cm2の紫外線を照射させて両面粘着シート3を得た。
実施例1で使用した粘着剤組成物1を、厚さ75μmと厚さ100μmのポリエチレンテレフタレート製の離型フィルムとの間に挟んで、厚み0.075mmのシート状にホットメルト成形し、高圧水銀ランプを用いて、該離型フィルム越しに積算光量1000mJ/cm2の紫外線を照射させて両面粘着シート4を得た。
実施例1で使用した粘着剤組成物1を、厚さ75μmと厚さ100μmのポリエチレンテレフタレート製の離型フィルムとの間に挟んで、厚み0.025mmのシート状にホットメルト成形し、高圧水銀ランプを用いて、該離型フィルム越しに積算光量1000mJ/cm2の紫外線を照射させて両面粘着シート5を得た。
アクリル酸エステル共重合体ポリマーB:100重量部に対し、光開始剤として日本シイベルヘグナー社製の商品名「エザキュア TZT」(4-メチルベンゾフェノン):0.6重量部と、架橋モノマーとして大阪有機化学社製の商品名「ビスコートV260(1,9-ノナンジオールジアクリレート)」:1.0重量部と、防錆剤として城北化学社製の商品名「BT-120」(1,2,3-ベンゾトリアゾール):0.5部とを添加して紫外線硬化型の粘着剤組成物2を得た。
前記粘着剤組成物2を用いた以外は、実施例2と同様にして両面粘着シート7を得た。
実施例6で使用した粘着剤組成物2を、厚さ75μmと厚さ100μmのポリエチレンテレフタレート製の離型フィルムとの間に挟んで、厚み0.1mmのシート状にホットメルト成形し、高圧水銀ランプを用いて、該離型フィルム越しに積算光量2000mJ/cm2の紫外線を照射させて両面粘着シート8を得た。
前記粘着剤組成物2を用いた以外は、実施例4と同様にして両面粘着シート9を得た。
前記粘着剤組成物2を用いた以外は、実施例5と同様にして両面粘着シート10を得た。
アクリル酸エステル共重合体ポリマーC:100重量部に対し、光開始剤として日本シイベルヘグナー社製の商品名「エザキュア TZT」(4-メチルベンゾフェノン):1.5重量部と、架橋モノマーとして大阪有機化学社製の商品名「ビスコートV260(1,9-ノナンジオールジアクリレート)」:1.5重量部とを添加して紫外線硬化型の粘着剤組成物3を得た。
実施例1で使用した粘着剤組成物1を、厚さ75μmと厚さ100μmのポリエチレンテレフタレート製の離型フィルムとの間に挟んで、厚み0.1mmのシート状にホットメルト成形し、高圧水銀ランプを用いて、該離型フィルム越しに積算光量250mJ/cm2の紫外線を照射させて両面粘着シート12を得た。
実施例1で使用した粘着剤組成物1を、厚さ75μmと厚さ100μmのポリエチレンテレフタレート製の離型フィルムとの間に挟んで、厚み0.1mmのシート状にホットメルト成形し、高圧水銀ランプを用いて該離型フィルム越しに積算光量2500mJ/cm2の紫外線を照射させて両面粘着シート13を得た。
アクリル酸エステル共重合体ポリマーD:100重量部に対し、光開始剤として日本シイベルヘグナー社製の商品名「エザキュア TZT」(4-メチルベンゾフェノン):0.15重量部とを添加して紫外線硬化型の粘着剤組成物4を得た。
アクリル系接着剤(商品名SKダイン1882:綜研化学社製)1000重量部に対して、イソシアネート系硬化剤(商品名L-45:綜研化学社製)1.85重量部及びエポキシ系硬化剤(商品名E-5XM:綜研化学社製)0.5重量部を均一混合して粘着剤溶液を調製した。
アクリル酸エステル共重合体ポリマーD:100質量部に対して、架橋モノマーとして紫外線硬化樹脂ペンタエリスリトールアクリレート(ダイセルサイテック社製の商品名「PETIA」)20質量部と、光開始剤として4-メチルベンゾフェノン1.5質量部を混合して中間樹脂層用樹脂組成物を調製した。
前記ポリエチレンテレフタレートフィルム越しに、高圧水銀ランプにて積算光量2000mJ/cm2の紫外線を照射して前記中間層用樹脂組成物を架橋させ、中間樹脂層(A-1)を作製した。
また、塗工基材を、剥離処理した、厚み50μmのポリエチレンテレフタレートフィルムに変えた以外は、上記感圧粘着剤層(B-1)と同様に感圧粘着剤層(B-1’)を作製した。
2 折り曲げ試験後のサンプル
3 スクリーン
4 折れ痕
Claims (26)
- 屈曲又は湾曲可能な画像表示装置構成用フレキシブル部材と、基材レスの両面粘着シートとを有する積層体であって、
前記両面粘着シートは、(メタ)アクリル酸エステル(共)重合体(A)、架橋剤(B)及び光開始剤(C)を含有する粘着剤組成物の硬化物からなり、前記架橋剤(B)として多官能(メタ)アクリレートを含み、厚みが10μm以上150μm以下であり、かつ、動的粘弾性のTanδピーク温度で定義される、硬化後のガラス転移温度(Tg)が-50℃~-20℃の範囲内にあり、かつ、硬化後の周波数1Hz、温度100℃における貯蔵弾性率G’(100)が、2.0×103~3.0×104Paの範囲内にあり、かつ、横軸に温度、縦軸に硬化後のせん断貯蔵弾性率(G’)の対数をプロットした貯蔵弾性率-温度グラフにおいて、前記貯蔵弾性率G’(100)と、周波数1Hz、温度150℃における貯蔵弾性率G’(150)との2点間を通る指数曲線を作成したとき、該指数曲線の底の自然対数が-0.010以上となることを特徴とする、積層体。 - 前記(メタ)アクリル酸エステル(共)重合体(A)が、カルボキシル基含有モノマーを(共)重合成分として含まず、かつ、(共)重合成分として、少なくとも水酸基含有モノマー又はアミド基含有モノマーのいずれか若しくは両方を含む、請求項1に記載の積層体。
- 前記(メタ)アクリル酸エステル(共)重合体(A)が、(共)重合成分として、(メタ)アクリロイル基と3級炭素原子が結合した(メタ)アクリル酸アルキルエステルを含む、請求項1又は2に記載の積層体。
- 前記光開始剤(C)が、水素引抜型の光開始剤である、請求項1~3の何れか一項に記載の積層体。
- 前記両面粘着シートは、硬化後の周波数1Hz、温度50℃における貯蔵弾性率G’が、3.0×102~4.0×104Paの範囲内にある、請求項1~4の何れか一項に記載の積層体。
- 前記画像表示装置構成用部材は、表面保護パネル、タッチパネル、光学フィルム及び有機EL(Electronic Luminescent)ディスプレイパネルからなる群のうち2種類以上の組み合わせである、請求項1~5の何れか一項に記載の積層体。
- 曲面形状を有している、請求項1~6の何れか一項に記載の積層体。
- 請求項1~7の何れか一項に記載の積層体を備えた、フレキシブルディスプレイ。
- 基材レスの両面粘着シートであって、
(メタ)アクリル酸エステル(共)重合体(A)、架橋剤(B)及び光開始剤(C)を含有する粘着剤組成物の硬化物からなり、前記架橋剤(B)として多官能(メタ)アクリレートを含み、
動的粘弾性のTanδピーク温度で定義される、硬化後のガラス転移温度(Tg)が、-50℃~-20℃の範囲内にあり、かつ、硬化後の周波数1Hz、温度100℃における貯蔵弾性率G’(100)が、2.0×103~3.0×104Paの範囲内にあり、かつ、厚みが10μm以上150μm以下であり、かつ、横軸に温度、縦軸に硬化後のせん断貯蔵弾性率(G’)の対数をプロットした貯蔵弾性率-温度グラフにおいて、前記貯蔵弾性率G’(100)と、周波数1Hz、温度150℃における貯蔵弾性率G’(150)との2点間を通る指数曲線を作成したとき、該指数曲線の底の自然対数が-0.010以上となることを特徴とする、両面粘着シート。 - 前記(メタ)アクリル酸エステル(共)重合体(A)が、カルボキシル基含有モノマーを(共)重合成分として含まず、かつ、(共)重合成分として、少なくとも水酸基含有モノマー又はアミド基含有モノマーのいずれか若しくは両方を含む、請求項9に記載の両面粘着シート。
- 前記(メタ)アクリル酸エステル(共)重合体(A)が、(共)重合成分として、(メタ)アクリロイル基と3級炭素原子が結合した(メタ)アクリル酸アルキルエステルを含む、請求項9又は10に記載の両面粘着シート。
- 前記光開始剤(C)が、水素引抜型の光開始剤である、請求項9~11の何れか一項に記載の両面粘着シート。
- 周波数1Hz、温度50℃における硬化後の貯蔵弾性率G’が、3.0×102~4.0×104Paの範囲内にある、請求項9~12の何れか一項に記載の両面粘着シート。
- フレキシブルディスプレイを構成する、画像表示装置構成用フレキシブル部材を貼合するために用いる両面粘着シートであって、
請求項9~13の何れか一項に記載の両面粘着シートを用いてなる、フレキシブルディスプレイ用両面粘着シート。 - 請求項1~7の何れか一項に記載の積層体を形成するための積層体形成キットであって、屈曲又は湾曲可能な画像表示装置構成用フレキシブル部材と、該フレキシブル部材に貼合するための両面粘着シートとを含み、
前記両面粘着シートは、(メタ)アクリル酸エステル(共)重合体(A)、架橋剤(B)及び光開始剤(C)を含有する粘着剤組成物の硬化物からなり、前記架橋剤(B)として多官能(メタ)アクリレートを含み、厚みが10μm以上150μm以下であり、かつ、動的粘弾性のTanδピーク温度で定義される、硬化後のガラス転移温度(Tg)が-50℃~-20℃の範囲内にあり、かつ、硬化後の周波数1Hz、温度100℃における貯蔵弾性率G’(100)が、2.0×103~3.0×104Paの範囲内にあり、かつ、横軸に温度、縦軸に硬化後のせん断貯蔵弾性率(G’)の対数をプロットした貯蔵弾性率-温度グラフにおいて、前記貯蔵弾性率G’(100)と、周波数1Hz、温度150℃における貯蔵弾性率G’(150)との2点間を通る指数曲線を作成したとき、該指数曲線の底の自然対数が-0.010以上となることを特徴とする、積層体形成キット。 - 前記(メタ)アクリル酸エステル(共)重合体(A)が、カルボキシル基含有モノマーを(共)重合成分として含まず、かつ、(共)重合成分として、少なくとも水酸基含有モノマー又はアミド基含有モノマーのいずれか若しくは両方を含む、請求項15に記載の積層体形成キット。
- 前記(メタ)アクリル酸エステル(共)重合体(A)が、(共)重合成分として、(メタ)アクリロイル基と3級炭素原子が結合した(メタ)アクリル酸アルキルエステルを含む、請求項15又は16に記載の積層体形成キット。
- 前記光開始剤(C)が、水素引抜型の光開始剤である、請求項15~17の何れか一項に記載の積層体形成キット。
- 前記両面粘着シートは、硬化後の周波数1Hz、温度50℃における貯蔵弾性率G’が、3.0×102~4.0×104Paの範囲内にある、請求項15~18の何れか一項に記載の積層体形成キット。
- 画像表示装置構成用フレキシブル部材の貼合方法としての両面粘着シートの使用であって、
前記両面粘着シートは、基材レスであって、(メタ)アクリル酸エステル(共)重合体(A)、架橋剤(B)及び光開始剤(C)を含有する粘着剤組成物の硬化物からなり、前記架橋剤(B)として多官能(メタ)アクリレートを含み、厚みが10μm以上150μm以下であり、かつ、動的粘弾性のTanδピーク温度で定義される、硬化後のガラス転移温度(Tg)が-50℃~-20℃の範囲内にあり、かつ、硬化後の周波数1Hz、温度100℃における貯蔵弾性率G’(100)が2.0×103~3.0×104Paの範囲内にあり、かつ、横軸に温度、縦軸に硬化後のせん断貯蔵弾性率(G’)の対数をプロットした貯蔵弾性率-温度グラフにおいて、前記貯蔵弾性率G’(100)と、周波数1Hz、温度150℃における貯蔵弾性率G’(150)との2点間を通る指数曲線を作成したとき、該指数曲線の底の自然対数が-0.010以上となることを特徴とする、画像表示装置構成用フレキシブル部材の貼合方法としての両面粘着シートの使用。 - 前記(メタ)アクリル酸エステル(共)重合体(A)が、カルボキシル基含有モノマーを(共)重合成分として含まず、かつ、少なくとも水酸基含有モノマー又はアミド基含有モノマーのいずれか若しくは両方を、共重合成分として含む、画像表示装置構成用フレキシブル部材の貼合方法としての請求項20に記載の両面粘着シートの使用。
- 前記(メタ)アクリル酸エステル(共)重合体(A)が、(共)重合成分として、(メタ)アクリロイル基と3級炭素原子が結合した(メタ)アクリル酸アルキルエステルを含む、画像表示装置構成用フレキシブル部材の貼合方法としての請求項20又は21に記載の両面粘着シートの使用。
- 前記光開始剤(C)が、水素引抜型の光開始剤である、画像表示装置構成用フレキシブル部材の貼合方法としての請求項20~22の何れか一項に記載の両面粘着シートの使用。
- 周波数1Hz、温度50℃における硬化後の貯蔵弾性率G’が、3.0×102~4.0×104Paの範囲内にある、画像表示装置構成用フレキシブル部材の貼合方法としての請求項20~23の何れか一項に記載の両面粘着シートの使用。
- 前記画像表示構成部材は、表面保護パネル、タッチパネル、光学フィルム及び有機ELディスプレイパネルからなる群のうち2種類以上の組み合わせである、画像表示装置構成用フレキシブル部材の貼合方法としての請求項20~24の何れか一項に記載の両面粘着シートの使用。
- 請求項20~25の何れか一項に記載の両面粘着シートの使用による、画像表示装置構成用フレキシブル部材の貼合方法。