JP7383639B2 - ゴム組成物およびタイヤ - Google Patents
ゴム組成物およびタイヤ Download PDFInfo
- Publication number
- JP7383639B2 JP7383639B2 JP2020561527A JP2020561527A JP7383639B2 JP 7383639 B2 JP7383639 B2 JP 7383639B2 JP 2020561527 A JP2020561527 A JP 2020561527A JP 2020561527 A JP2020561527 A JP 2020561527A JP 7383639 B2 JP7383639 B2 JP 7383639B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- parts
- rubber composition
- rubber
- styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記充填剤(B)が、カーボンブラックを含み、
前記カーボンブラックの量が、前記ゴム成分(A)100質量部に対して、30~90質量部であり、
前記熱可塑性樹脂(C)の量が、前記ゴム成分(A)100質量部に対して、1~85質量部であり、
前記熱可塑性樹脂(C)は、スチレン・アルキレンブロック共重合体を含み、
前記スチレン・アルキレンブロック共重合体のアルキレンブロックが、-(CH2-CH(C2H5))-単位(CA)と-(CH2-CH2)-単位(CB)とを有し、単位(CA)の合計含量が、単位(CA)および単位(CB)の総質量に対して、40質量%以上である、ゴム組成物である。
これにより、ゴム組成物の操縦安定性と、低転がり抵抗性とを高度に両立させることができる。
これにより、タイヤの操縦安定性と、低転がり抵抗性とを高度に両立させることができる。
本発明に係るゴム組成物は、ゴム成分(A)と、充填剤(B)と、熱可塑性樹脂(C)とを含み、
前記充填剤(B)が、カーボンブラックを含み、
前記カーボンブラックの量が、前記ゴム成分(A)100質量部に対して、30~90質量部であり、
前記熱可塑性樹脂(C)の量が、前記ゴム成分(A)100質量部に対して、1~85質量部であり、
前記熱可塑性樹脂(C)は、スチレン・アルキレンブロック共重合体を含み、
前記スチレン・アルキレンブロック共重合体のアルキレンブロックが、-(CH2-CH(C2H5))-単位(CA)と-(CH2-CH2)-単位(CB)とを有し、単位(CA)の合計含量が、単位(CA)および単位(CB)の総質量に対して、40質量%以上である、ゴム組成物である。
本発明において、ゴム成分(A)は、ゴム組成物に用いられる公知のゴム成分を用いることができる。成分(A)としては、例えば、天然ゴム(NR)、合成イソプレンゴム(IR)、スチレンブタジエンゴム(SBR)、ブタジエンゴム(BR)、イソプレンブタジエン共重合体、エチレンブタジエン共重合体、プロピレンブタジエン共重合体、これらの変性体などが挙げられる。
これにより、操縦安定性と、低転がり抵抗性とをより高度に両立させることができる。
本発明において、成分(B)は、カーボンブラックを含み、カーボンブラックの量が、前記ゴム成分(A)100質量部に対して、30~90質量部である。
これにより、低転がり抵抗性と耐破壊特性が高まる。
熱可塑性樹脂(C)は、スチレン・アルキレンブロック共重合体を含む。
成分(C)としてのスチレン・アルキレンブロック共重合体は、スチレン系モノマー由来のブロックと、アルキレンブロックとを有する共重合体である。スチレン・アルキレンブロック共重合体のアルキレンブロックは、-(CH2-CH(C2H5))-単位(CA)と-(CH2-CH2)-単位(CB)とを有し、単位(CA)の合計含量が、単位(CA)および単位(CB)の総質量に対して、40質量%以上である。
これにより、操縦安定性がより高まる。
その他の熱可塑性樹脂としては、例えば、ポリエステルポリオールが挙げられる。ポリエステルポリオールとしては、特に限定されず、公知のポリエステルポリオールを適宜選択して用いることができる。ポリエステルポリオールとしては、例えば、ジカルボン酸、トリカルボン酸などの多価カルボン酸と、多価アルコールとの反応により得られるポリエステルポリオールなどが挙げられる。
前記ポリエステルポリオールの量が、前記ゴム成分(A)100質量部に対して、1~20質量部であることが好ましい。
これにより、操縦安定性と、低転がり抵抗性とをより高度に両立させることができる。
本発明に係るゴム組成物は、前述の成分以外に、ゴム工業界で通常使用される成分、例えば、軟化剤、加硫促進剤、シランカップリング剤、加硫剤、老化防止剤、加硫促進助剤、有機酸化合物などを、本発明の趣旨に反しない範囲で適宜選択して含有することができる。
本発明に係るゴム組成物の調製方法は特に限定されず、公知の混練方法を用いて、成分(A)、成分(B)、成分(C)などの成分を混練すればよい。
これにより、より効果的に、タイヤの操縦安定性と、低転がり抵抗性とを両立させることができる。
本発明に係るタイヤは、上記いずれかに記載のゴム組成物をベーストレッド部に用いた、タイヤである。
これにより、タイヤの操縦安定性と、低転がり抵抗性とを高度に両立させることができる。
NR:Tg=-60℃
SBR:JSR社製の商品名「JSR 1500」、Tg=-55℃
BR:JSR社製の「JSR BR01」、Tg=-100℃
カーボンブラック1:旭カーボン社製の商品名「♯70L」、N2SA=84m2/g
カーボンブラック2:N2SA=69m2/g
カーボンブラック3:キャボット社製の商品名「VULCAN 7H」、N2SA=117m2/g
スチレン・アルキレンブロック共重合体:JSR社製の商品名「DYNARON(登録商標)9901P」(SEBS)、単位(CA)の単位(CA)および単位(CB)の総質量に対する割合70質量%、合計スチレン含量53質量%
ポリエステルポリオール:日本ゼオン社製の商品名「ゼオファイン(登録商標)100M」
WAX:マイクロクリスタリンワックス、日本精蝋社製の商品名「オゾエース0701」
老化防止剤:N-(1,3-ジメチルブチル)-N’-フェニル-p-フェニレンジアミン(6PPD)、大内新興化学工業社製の商品名「ノクラック(登録商標) 6C」
老化防止剤:2,2,4-トリメチル-1,2-ジヒドロキノリン重合体(TMQ)、大内新興化学工業社製の商品名「ノクラック(登録商標) 224」
加硫促進剤:1,3-ジフェニルグアニジン(DPG)、住友化学社製の商品名「ソクシノール(登録商標)D-G」
加硫促進剤:ジ(2-ベンゾチアゾリル)ペルスルフィド(MBTS)、大内新興化学工業社製の商品名「ノクセラー(登録商標)DM」
加硫促進剤:N-シクロヘキシルベンゾチアゾール-2-スルフェンアミド(CBS)、大内新興化学工業社製の商品名「ノクセラー(登録商標)CZ」
表1~3に示す配合処方に従い、通常のバンバリーミキサーを用いて、ゴム組成物を調製し、そのゴム組成物をベーストレッド部に用いて、サイズ195/65R15の乗用車用空気入りラジアルタイヤを作製する。実施例1について、通常のバンバリーミキサーを用いて、ゴム組成物を調製した。また実施例1について、ゴム組成物をベーストレッド部に用いて、サイズ195/65R15の乗用車用空気入りラジアルタイヤを作製した。そのゴム組成物又はタイヤに対して、下記の方法で、操縦安定性、低転がり抵抗性および性能両立を予測評価する。実施例1のゴム組成物およびタイヤに対して、下記の方法で、操縦安定性、転がり抵抗性及び性能両立を評価した。結果を表1~3に示す。
操縦安定性は、コーナリングパワーによって評価した。実施例1についてコーナリングパワーは、フラットベルト式コーナリング試験機を用いて測定した。ベルト速度を100km/hとして、タイヤの転動方向とドラムの円周方向との間のスリップアングル(SA)を1°の状態でコーナリングフォースを測定した。比較例1のコーナリングフォースを100として指数表示した。この指数値が大きいほど、コーナリングパワーが大きく、操縦安定性に優れることを示す。
ゴム組成物を145℃で33分間加硫して得られた加硫ゴムについて、損失正接(tanδ)を、GABO製粘弾性試験機、温度50℃、初期歪2%、動歪1%、周波数15Hzの条件で測定した。比較例1の損失正接の逆数を100として指数表示した。指数値が大きい程、転がり抵抗が低く、低転がり抵抗性に優れることを示す。
操縦安定性と低転がり抵抗性の両立について、以下の基準で評価した。結果を表1~3に合わせて示す。
A:両方の性能が、指数値105以上である場合
B:両方の性能が、指数値100以上であり、かつ、少なくとも一方の性能が、指数値104以下である場合
C:少なくとも一方の性能が指数値99以下である場合
Claims (11)
- ゴム成分(A)と、充填剤(B)と、熱可塑性樹脂(C)とを含み、
前記充填剤(B)が、カーボンブラックを含み、
前記カーボンブラックの量が、前記ゴム成分(A)100質量部に対して、30~90質量部であり、
前記熱可塑性樹脂(C)の量が、前記ゴム成分(A)100質量部に対して、1~85質量部であり、
前記熱可塑性樹脂(C)は、スチレン・アルキレンブロック共重合体を含み、
前記スチレン・アルキレンブロック共重合体のアルキレンブロックが、-(CH2-CH(C2H5))-単位(CA)と-(CH2-CH2)-単位(CB)とを有し、単位(CA)の合計含量が、単位(CA)および単位(CB)の総質量に対して、40質量%以上である、ゴム組成物。 - 前記単位(C A )の合計含量が、前記単位(C A )および前記単位(C B )の総質量に対して、50~90質量%である、請求項1に記載のゴム組成物。
- 前記単位(C A )の合計含量が、前記単位(C A )および前記単位(C B )の総質量に対して、65~80質量%である、請求項1に記載のゴム組成物。
- 前記ゴム成分(A)が、天然ゴム、合成イソプレンゴム、スチレンブタジエンゴムおよびブタジエンゴムからなる群より選択される1種以上である、請求項1~3のいずれか一項に記載のゴム組成物。
- 前記カーボンブラックの窒素吸着比表面積(N2SA)が、40~150m2/gである、請求項1~4のいずれか一項に記載のゴム組成物。
- 前記スチレン・アルキレンブロック共重合体の合計スチレン含量が、40質量%以上である、請求項1~5のいずれか一項に記載のゴム組成物。
- 前記熱可塑性樹脂(C)が、ポリエステルポリオールをさらに含み、
前記ポリエステルポリオールの量が、前記ゴム成分(A)100質量部に対して、1~20質量部である、請求項1~6のいずれか一項に記載のゴム組成物。 - 前記ゴム組成物において、硫黄の量が、前記ゴム成分(A)100質量部に対して、8~11質量部である、請求項1~7のいずれか一項に記載のゴム組成物。
- 前記ゴム組成物において、亜鉛華の量が、前記ゴム成分(A)100質量部に対して、5~9質量部である、請求項1~7のいずれか一項に記載のゴム組成物。
- ベーストレッド部用である、請求項1~9のいずれか一項に記載のゴム組成物。
- 請求項1~10のいずれか一項に記載のゴム組成物をベーストレッド部に用いた、タイヤ。