JP7342692B2 - 酸化鉱石の製錬方法 - Google Patents
酸化鉱石の製錬方法 Download PDFInfo
- Publication number
- JP7342692B2 JP7342692B2 JP2019233993A JP2019233993A JP7342692B2 JP 7342692 B2 JP7342692 B2 JP 7342692B2 JP 2019233993 A JP2019233993 A JP 2019233993A JP 2019233993 A JP2019233993 A JP 2019233993A JP 7342692 B2 JP7342692 B2 JP 7342692B2
- Authority
- JP
- Japan
- Prior art keywords
- mixture
- metal
- mass
- oxide
- reduction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
酸化鉱石の製錬方法である。
本実施の形態に係る酸化鉱石の製錬方法は、酸化鉱石と炭素質還元剤と酸化アルミニウムと混合する混合工程を経て得られる混合物に還元処理を施すことによって、メタルとスラグとを含む還元物を得るものである。そして、この混合工程では、酸化アルミニウムの質量に対する二酸化ケイ素の質量の比が2.0以上であって、混合物に含まれる、酸化鉄(III)と二酸化ケイ素と酸化アルミニウムとの合計100質量%に対して、二酸化ケイ素の含有率が40質量%以下となるように混合物を得ることを特徴とする。
本実施の形態に係る酸化鉱石の製錬方法は、図1に示すように、酸化鉱石と炭素質還元剤と酸化アルミニウムとを混合して混合物を得る混合工程S1と、得られた混合物に還元処理を施して還元物を得る還元工程S2と、還元工程S2にて生成したメタルとスラグとを分離してメタルを回収する回収工程S3と、を有する。
混合工程S1は、ニッケル酸化鉱石を含む原料粉末と炭素質還元剤と酸化アルミニウムとを混合し、また任意成分の添加剤として、鉄鉱石、フラックス成分、バインダー等の、例えば粒径が0.2~0.8mm程度の粉末を混合して混合物を得る。ここで、ニッケル酸化鉱石を含む原料粉末の混合は、混合機等を用いて行うことができる。
還元工程S2では、得られた混合物に還元処理を施し還元物を得る。還元工程S2における加熱還元処理により、製錬反応(還元反応)が進行して、フェロニッケルメタル(以下、単に「メタル」という)と、フェロニッケルスラグ(以下、単に「スラグ」という)とが分かれて生成する。
回収工程S3は、還元工程S2にて生成したメタルとスラグとを分離してメタルを回収する。部分還元処理を施した場合には、混合物に対する還元加熱処理によって得られた、メタル相(メタル固相)とスラグ相(スラグ固相)とを含む混在物(還元物)からメタル相を分離して回収する。
原料鉱石としてのニッケル酸化鉱石と、鉄鉱石と、フラックス成分である珪砂及び石灰石、バインダー、及び炭素質還元剤(炭素含有量が85重量%であり、平均粒径が約80μmの石炭粉)を、適量の水を添加しながら混合機を用いて混合して試料を得た。炭素質還元剤は、原料鉱石であるニッケル酸化鉱石に含まれる酸化ニッケルと酸化鉄(Fe2O3)とを過不足なく還元するのに必要な量を100%としたときに28%の割合となる量で含有させた。
Claims (2)
- ニッケル酸化鉱石を含む混合物に還元処理を施してフェロニッケルメタルを含む還元物を得るニッケル酸化鉱石の製錬方法であって、
前記ニッケル酸化鉱石と炭素質還元剤と酸化アルミニウムとを混合して混合物を得る混合工程と、
得られた混合物に還元処理を施しフェロニッケルメタルを含む還元物を得る還元工程と、
を有し、
前記混合工程では、前記混合物に含まれる酸化アルミニウムの質量に対する前記混合物に含まれる二酸化ケイ素の質量の比が2.0以上であって、前記混合物に含まれる、酸化鉄(III)と二酸化ケイ素と酸化アルミニウムとの合計100質量%に対して該二酸化ケイ素の含有率が40質量%以下となるように、前記酸化アルミニウムを混合して混合物を得る
ニッケル酸化鉱石の製錬方法。 - 前記還元工程では、前記混合物を移動炉床炉の炉床に載置して、還元処理を施す
請求項1に記載のニッケル酸化鉱石の製錬方法。