JP7318872B2 - 無機材料製の遮熱材、これを製造するための材料セット、下地層用材料及び製造方法。 - Google Patents
無機材料製の遮熱材、これを製造するための材料セット、下地層用材料及び製造方法。 Download PDFInfo
- Publication number
- JP7318872B2 JP7318872B2 JP2021509938A JP2021509938A JP7318872B2 JP 7318872 B2 JP7318872 B2 JP 7318872B2 JP 2021509938 A JP2021509938 A JP 2021509938A JP 2021509938 A JP2021509938 A JP 2021509938A JP 7318872 B2 JP7318872 B2 JP 7318872B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- glaze layer
- underlayer
- glaze
- base layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
建材のなかでも、特に屋根瓦に代表される黒色系のものの遮熱性を向上させることが求められている。例えば、日本ヒートアイランド対策協議会では、L*値≦40の黒色系遮熱釉薬について、赤外線反射率40%以上、かつ日射反射率30%を達成することを目標に掲げている。
本件発明は無機材料からなる遮熱材を対象としているが、有機材料からなる塗料においても同様な課題があり、本件発明に関連する技術が例えば特許文献1に開示されている。
特許文献2には高い遮熱性の顔料が提案されている。
非特許文献1には90%以上の日射反射率を示すエンゴーベが開示されている。
しかし、日本ヒートアイランド対策協議会が掲げる、L*値≦40において、NIR≧以上40%、かつTSR≧30%という目標はクリアしていない。
かかる知見に基づき、基材の表面の光反射率を高めれば釉薬層としてのNIRが向上し、もってそのTSRを向上させられるのでないかと考えた。
そこで、基材の表面を、これより光反射率の高い材料(下地層)で被覆してそのTSRを測定した。その結果を図1に示す。図1の結果より、下地層の赤外線反射率NRIが高くなるにしたがって遮熱材全体としての、即ち下地層と釉薬層との複合層としての日射反射率TSRも高くなることがわかる。
そして、実施例1の黒色顔料を用いたとき、下地層のTSRを80%以上とすると遮熱材全体の日射反射率TSRがほぼ30%以上になることがわかった。実施例1の黒色顔料はもともと45%なるNIRを備えているので、ここに、日本ヒートアイランド対策協議会の求める目標がクリアされたこととなる。
基材:
材料;陶磁器質
厚さ;5~20mm
下地層:
材料(組成);ゼーゲル式で、RO:0.1~0.5、R2O:0.5~0.9、Al2O3:2.2~10.2、SiO2:7.2~29.2、TiO:0.0~0.5、ZrSiO4:0.0~5.5、SiO2/Al2O3:0.7~23.8、ただしRO=MgO、CaO又はBaO、R2O=Li2O、Na2O又はK2O
厚さ;100μm
下地層のTSRの下地層を単独で(、即ち何ら釉薬層を積層することなく)焼成したときの値であり、配合調整により変化を与えた。また、基材のTSRは50%である。即ち、横軸50%は下地層がないときを示す。
材料;黒色顔料(実施例1:製品名:42-710A(カサイ工業)を含む釉薬
注) 黒色顔料(実施例1):CrとFeとの比(モル比)を93~97:7~3又はCrとFeとの比(モル比)を80~97:20~3として、かつ非スピネル構造をとる(Cr、Fe)2O3固溶体
釉薬層のL*値: 30以下
焼成条件:
焼成温度;1,130~1,150℃
保持時間;1~3時間
TSRの測定条件:
測定器:日本分光株式会社製の紫外可視光赤外分光光度計V-670
比較例1の釉薬層は黒色釉薬として製品名:Cブラック(カサイ工業)を用いる以外は実施例1と同じ条件である。
比較例2の釉薬層は黒色釉薬として製品名:ブラックマット(カサイ工業)を用いる以外は実施例1と同じ条件である。
なお、実施例2の黒色顔料を含む釉薬層においても、下地層のTSRが上昇するにつれ、遮熱材全体の、即ち下地層と釉薬層との複合層のTSRも上昇することがわかる。
他方、比較例1及び比較例2の黒色顔料を含む釉薬層においては、下地層のTSRの変改が遮熱材全体のTSRにほとんど影響を与えなかった。
実施例2並びに比較例1及び2のL*はいずれも30以下であった。
その表面の日射反射率(TSR)が80%以上の下地部材と、
該下地部材の表面に積層された釉薬層であって、CrとFeとの比(モル比)を93~97:7~3又はCrとFeとの比(モル比)を80~97:20~3として、かつ非スピネル構造をとる(Cr、Fe)2O3固溶体からなり、L*値が30以下の黒色系顔料を含む釉薬層と、
を備えてなる、遮熱材。
このように構成される遮熱材によれば、日射反射率(TSR)が30%以上となる。もちろん、赤外線反射率(NIR)も40%以上である。
ところで、赤外線を透過させる有機塗料があることは特許文献1に記載の通りである。有機塗料の場合、高いTSRを備えた有機下地層を形成し、これを乾燥した後に当該有機塗料を塗布することとなる。このとき、有機下地層と塗料層とは層分離しており両者の材料が混じりあったり、反応したりすることはない。
これに対し、無機材料からなる遮熱材には下記の課題があった。
また、無機材料からなる遮熱材の場合、一般的には下地層のスラリーの上に釉薬のスラリーを積層し、両者を同時に焼成する。この焼成温度で釉薬層の材料は完全にガラス化する。他方下地層の材料はガラス化しない。換言すれば、下地層の材料はこれを構成する粒子が焼結された状態、即ち、当該粒子の表面が融解して相互に結合した状態である。
下地層を単独で焼成すれば、その材料は全体的に均一に焼結され、その表面は高い光反射率を有することとなるが、釉薬層を積層した状態で焼結すると、釉薬層の材料がそのガラス化温度を超えて加熱されて流動化し、下地層の材料の粒子の間に浸み込んで、そこで下地層の材料と反応する。焼結工程が終了して冷やされると、反応した釉薬層の材料と下地層の材料とはガラス化した反応領域を形成する。かかるガラス化した反応領域は光を透過させるので高い光反射率を確保できなくなる。
即ち、この発明の第1の局面は次のように規定される。
基材と
該基材の上に積層される下地層と
該下地層の上に積層される釉薬層と、を備えてなる無機材料製の遮熱材であって、
前記釉薬層は前記下地層を視認できない厚さを有し、かつ赤外線を透過させ、
前記下地層は、該下地層の材料と前記釉薬層の材料との反応領域及び前記釉薬層の材料が存在しない主反射領域を備える、遮熱材。
図2に、この発明の遮熱材1の基本構造を示す。図2に示す通り、下地層の主反射領域に十分な厚みがあれば、釉薬層及び下地層を透過してきた赤外線をこの主反射領域で確実に反射させることができる。
これにより、図1の各実施例に示すように、下地層の持つ光反射特性(TSR)を利用可能となる。
図1の実施例1で用いた黒色顔料について、下地層の厚さを30μmとしたもの(比較例3)の下地層TSRと遮熱材全体のTSRとの関係を、図1において点線で示す。
比較例3では、下地層が薄いのでその全域に釉薬層の材料が浸み込んでおり、即ち下地層全体が反応領域になっている。その結果、釉薬層及び下地層を透過した赤外線は専ら基材2の表面で反射されている。
比較例3の例では、遮熱材のTSR特性において下地層は何ら効果を発揮していない。
そこで、本発明者らは、下地層の材料の上に釉薬層を積層して焼成したとき、下地層中にこのような主反応領域を確保する方法につき、鋭意検討した。
本発明者らの検討によれば、下記(1)~(3)の方法が考えられる。
(1)下地層自体に十分な厚さを確保する。
図4には、上記実施例で用いた下地層の膜厚とそのTSRとの関係を示す。このとき、下地層の上には何ら釉薬層は積層されておらず、下地層は露出した状態である。図4の関係から、下地層の膜厚は70μm以上とすることが好ましいことがわかる。その膜厚が70μm未満となると、もっぱら下地層の膜厚が不均一になるため、その薄い部分を赤外線及びその他の波長の光が優先的に透過するおそれがある。
なお、下地層の材料を選択すれば、赤外線の透過率を減少させたり、膜厚の均一性を確保したり、更にはその密度を上げることにより、本発明者らの検討によれば、下地層として50μm以上の厚さを確保しておけば、釉薬層の一般的な焼成条件において、釉薬層の材料と下地層の材料との反応領域以外の領域、即ち主反射領域に10μm以上の厚さを確保できる。
(2)焼成した下地層の上に釉薬層のスラリーを積層し、その後焼成する。
下地層を予め焼成しておけば、その後釉薬層を焼成しても両者の材料は殆ど反応しない。よって、この場合、下地層の全域が主反射領域と機能するので、これに十分な厚さを確保できる。
(3)釉薬層と焼成温度との関係
下地層のスラリーの上に釉薬層のスラリーを積層して焼成したとき、両材料が反応して反応領域が形成されることは避けらない。しかしながら、釉薬層の材料を選択することで、反応領域の形成を抑制することができる。
即ち、焼成温度が定められておれば、釉薬層のガラス化温度をできる限り当該焼成温度に近づけることで釉薬層の材料の流動化が抑えられる。これにより、釉薬層の材料が下地層に浸み込みがたくなり、もって反応領域の形成が抑制される。
なお、下地層を複数の材料から構成することができる。例えば、下地層において釉薬側の層をより高い反射率の材料製としたり、基材層側の層をより結合性の高い材料製としたりすることができる。
釉薬層を複数の材料層からなるものとすることができる。
図5に実施例3~実施例7の釉薬の溶融曲線を示す。
実施例3~実施例7の釉薬のHTは次の通りであった。
実施例3:1141℃
実施例4:1121℃
実施例5:1088℃
実施例6:1053℃
実施例7:1035℃
またHT(半球温度)もHesse Instruments社製のHeating Microscope EM301で測定した。
HMS測定とは、高温加熱顕微鏡法により釉薬の溶融挙動を確認する手法である。
昇温条件は、500℃まで60℃/分、500~1,000℃は10℃/分、1,000℃以上は5℃/分。
HT(半球温度)は、測定試料高さがベース幅の半分になった時の温度で、DIN51730 Bestimmug des Asche-Schmelzverhaltensの規格に準ずる。
分光反射率曲線は日本分光株式会社社製の紫外可視光赤外分光光度計V-670で測定した。
図6~図10及び表1の結果より、釉薬層のHTの温度は焼成温度以下から焼成温度より100℃以下にすることが好ましく、更に好ましくは50℃以下であり、最も好ましくは上記HTと焼成温度とを等しくする。なお、実施例3~7の焼成温度は1140℃である。なお、実施例3~7においては、その流出温度(流動体となる温度)は焼成温度より100℃高いものであった。
流出温度が焼成温度より100℃を超えて高い釉薬材料のとき、例えばその流出温度が焼成温度より150℃以上高い釉薬材料のときは、HTが焼成温度より100℃を超えて低いとき、例えば150℃を以下のときでも、主反射層を確保できる。
もちろん、流出温度が焼成温度に近いほうが焼成コストを抑制できる。
以上換言すれば、釉薬層の材料としてそのガラス化温度が焼成温度にほぼ等しいものを採用し、焼成温度まで加熱されたときの流動性をできるかぎり抑制することが好ましい。
反射率を損なわない範囲で以下の成分が含まれても構わない。かかる成分として、クロム、マンガン、鉄、コバルト、ニッケル、銅、亜鉛、スズ、ジルコン等を挙げることができる。
反射率を損なわない範囲で以下の成分が含まれても構わない。かかる成分として、クロム、マンガン、鉄、コバルト、ニッケル、銅、亜鉛、スズ等を挙げることができる。
図11の結果を得たX線回折装置はブルカー社製、型番D2 PHASERである。
図11の結果から、下地層のTSRを80%以上とするには、ハロー高さを230cps以下とすることが好ましいことがわかる。
一般的に、ハロー高さが小さいほど、ガラス化がされていないことを示している。したがって、下地層における主反射領域はそのハロー高さを230cps以下とすることが好ましい。
Claims (6)
- 基材と、
該基材の上に積層され、前記基材よりTSR(日射反射率)が大きい下地層と
該下地層の上に積層される釉薬層と、を備えてなる無機材料製の遮熱材であって、
前記釉薬層は前記下地層を視認できない厚さを有し、かつ赤外線を透過させ、
前記下地層は、前記釉薬層と反応しない、前記釉薬層を透過した前記赤外線を反射させる機能を有する主反射領域を有するとともに、当該主反射領域の厚さが10μm以上である、遮熱材。 - 前記下地層の材料は、ゼーゲル式で、RO:0.1~0.5、R2O:0.5~0.9、B2O3:0.0~1.0、Al2O3:2.2~10.2、SiO2:7.2~29.2、TiO:0.0~0.5、ZrSiO4:0.0~5.5、SiO2/Al2O3:0.7~23.8、ただしRO=MgO、CaO又はBaO、R2O=Li2O、Na2O又はK2Oと表せる、請求項1に記載の遮熱材。
- 前記釉薬層の材料は、ゼーゲル式でRO:0.5~0.9、R2O:0.1~0.5、B2O3:0.0~1.0、Al2O3:0.3~1.0、SiO2:1.3~3.7、SiO2/Al2O3:3.4~6.9、ただしRO=MgO、CaO又はBaO、R2O=Li2O、Na2O又はK2Oと表せるものである、請求項1又は2に記載の遮熱材。
- 基材と、
TSR(日射反射率)が80%以上の下地層と
CrとFeとの比(モル比)を93~97:7~3又はCrとFeとの比(モル比)を80~97:20~3として、かつ非スピネル構造をとる(Cr、Fe)2O3固溶体を含み、そのL*値が30以下の釉薬層とを備え、
前記釉薬層は前記下地層を視認できない厚さを有し、かつ赤外線を透過させ、
前記下地層は、前記釉薬層と反応しない、前記釉薬層を透過した前記赤外線を反射させる機能を有する主反射領域を有するとともに、当該主反射領域の厚さが10μm以上である、遮熱材。 - 基材と、
該基材の上に積層される下地層と、
該下地層の上に積層される釉薬層と、を備えてなる無機材料製の遮熱材であって、
前記下地層の材料は、ゼーゲル式で、RO:0.1~0.5、R2O:0.5~0.9、B2O3:0.0~1.0、Al2O3:2.2~10.2、SiO2:7.2~29.2、TiO:0.0~0.5、ZrSiO4:0.0~5.5、SiO2/Al2O3:0.7~23.8、ただしRO=MgO、CaO又はBaO、R2O=Li2O、Na2O又はK2Oと表せ、かつ、前記下地層は、前記釉薬層と反応しない、前記釉薬層を透過した赤外線を反射させる機能を有する主反射領域を有するとともに、当該主反射領域の厚さが10μm以上である、遮熱材。 - 前記釉薬層の材料のHMS測定(ヒーティングマイクロスコープによる測定)のHT(半球温度)は、予定されている焼成温度より100℃以内に収まる温度である、請求項5に記載の遮熱材。