JP7294244B2 - 高圧タンクの製造方法 - Google Patents
高圧タンクの製造方法 Download PDFInfo
- Publication number
- JP7294244B2 JP7294244B2 JP2020101573A JP2020101573A JP7294244B2 JP 7294244 B2 JP7294244 B2 JP 7294244B2 JP 2020101573 A JP2020101573 A JP 2020101573A JP 2020101573 A JP2020101573 A JP 2020101573A JP 7294244 B2 JP7294244 B2 JP 7294244B2
- Authority
- JP
- Japan
- Prior art keywords
- resin sheet
- liner
- resin
- liner body
- mouthpiece
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
ここで「ライナの外周に樹脂が含浸した繊維層を形成し」は、予め樹脂が含浸した繊維をライナの外周に巻き付けること、及び、繊維をライナの外周に巻き付けた後に繊維に高圧で樹脂を浸透させることのいずれも含む。
図1には1つの形態にかかる高圧タンク10の外観を模式的に表し、図2には高圧タンク10の軸線に沿った断面を模式的に表した。また、図3には図2にBで示した部分を拡大した図、図4には図1のA-A矢視断面図を表した。
これらの図からわかるように、高圧タンク10はライナ11、及び、補強層15を有している。以下に各構成について説明する。
ライナ11は、高圧タンク10の内部空間を区画する中空の部材である。図5にはライナ11の部分断面図(図5の上部は外表面、図5の下部は断面)を表した。また、図6はライナ11の右側面図である。図1乃至図6からわかるように、本形態でライナ11はライナ本体12、口金13、及び、樹脂シート14を備えている。
ライナ本体12は、内部空間に収容されたものを漏らすことなく保持することができる材料で構成されていればよく、材料は公知のものを用いることができるが、例えばナイロン樹脂、ポリエチレン系の合成樹脂等の樹脂からなるものである。
ライナ本体12の厚さは特に限定されることはないが、軽量化の観点から0.5mm乃至3.0mm程度であることが好ましい。
円板状のうちその一方側の板面13d(ライナ本体12の端部12aに対向する面)は平坦であり、他方側の板面13e(ライナ本体12の端部12aとは反対を向く面)はフランジ部13aの円板の中央に向けてフランジ部13aの板厚が厚くなるように構成されている。
口金本体13bはフランジ部13aの板面13e側の中央に設けられた突出した部位である。
凸部13cはフランジ部13aの板面13d側の中央に設けられた突出した部位である。
また、口金13はフランジ部13a、口金本体13b、及び、凸部13cを通じるように穴13fを有している。ただし、ライナ11に具備される2つの口金13のうち、一方の口金13の穴13fはフランジ部13a、口金本体13b、及び、凸部13cを貫通して口金13を貫通している。これに対して他方の口金13の穴13fは凸部13cを貫通することなく形成されている。
これにより、穴13fが口金13を貫通している口金13では、ライナ11の内部と外部との連通を可能としている。この口金13に対しては例えばバルブ等が取り付け可能とされており、ライナ本体12に収容したものを取り出すことができる。一方、穴13fが口金13を貫通していない口金13では、ライナ11の内部と外部とが連通せず、ライナ本体12に収容したものが漏れないように構成されている。
ここで軟化点は、ISO 306(JIS K7206)B50法により測定したビカット軟化温度(VST:Vicat Softening Temperature)とする。
例えば補強層15の樹脂を硬化する際に補強層15及びライナ11が達する最高温度を160℃とすれば、樹脂シートの軟化点をこれ以上とし、例えば6ナイロン(軟化点180℃)、66ナイロン(軟化点230℃)、ポリエステル(軟化点240℃)を用いることができる。そのなかでも例えばこの樹脂シート14とライナ本体12との材料を同じ(ナイロン樹脂)とすれば、樹脂シート14を配置したときにライナ本体12と樹脂シート14との密着性(溶接性)をより高めることが可能である。
ライナ本体12と口金13とを組み合わせた状態では、図3にCで表したように、フランジ部13aの外周部とライナ本体12との間に間隙Cが生じる。高圧タンク10の作製中に補強層の流動性のある樹脂がこの間隙に入り込むことによる不具合を生じることがある。従って、樹脂シート14は少なくともこの間隙Cを覆うようにその外周及び内周が設けられている。すなわち樹脂シート14は間隙Cを覆いつつ、この間隙Cを覆う部分より外周側はライナ本体12に溶接(樹脂シート14とライナ本体12とがその界面が明確でなくなるように互いに混ざり合っている接合状態)となり、間隙Cを覆う部分より内周側は口金13の面13eに対して接着(物理的なアンカー効果による接合状態)となっている。これにより、間隙Cが樹脂シート14で覆われて間隙Cへの補強層の樹脂の侵入を抑制することができる。
このような異音の発生は、ライナ本体12、補強層15が熱的又は物理的な影響により膨張、収縮すると口金13の面13eと繊維層15との間で相対的に摺動が生じ、このときのスティックスリップによるものである。従来は例えば特許文献4に記載のように口金に潤滑剤を塗布して対策をしていた。
これに対して本開示によれば、樹脂シート14を口金13の面13eと補強層15との間に配置することで当該異音の発生を抑制することができる。これは、口金13の面13eと補強層15との間に弾性的に変形可能な樹脂シート14が配置されることで、スティックスリップが抑制されると考えられる。すなわち、本開示によれば、間隙Cへの補強層15の樹脂の侵入を抑制するという課題に対する解決の他、異音発生を抑制する課題も併せて解決することができる。
異音発生の抑制効果をより顕著に発揮させる観点から、樹脂シート14の内周側は口金本体13bに近い位置にまで達していることが好ましい。具体的には、口金13のフランジ部13aの面13eの径方向の半分以上を覆うことが好ましく、フランジ部13aの面13eの全部を覆うことがさらに好ましく、図3にDで示したようにフランジ部13aの面13e及びフランジ部13aの面13eと口金本体13bとの接続部である入隅部分を覆うことが最も好ましい。
補強層15は、繊維層及び繊維層に含浸され硬化した樹脂を有している。繊維層は、ライナ11の外表面に繊維束が所定の厚さにまで何層にも亘って巻き付けられて構成されている。
このような炭素繊維による繊維束がライナ11の外表面に巻き付けられていることで繊維層が形成されている。
高圧タンクには、上記に加えて必要に応じて保護層を設けてもよい。保護層は補強層の外周に配置されており、ガラス繊維が巻かれ、ここに樹脂が含浸されてなる層である。含浸される樹脂は補強層と同様に考えることができる。これにより高圧タンクに対して耐衝撃性を付与することが可能である。保護層の厚さは特に限定されることはないが、1.0mm乃至1.5mm程度とすることができる。
図7には1つの形態にかかる高圧タンクの製造方法S10の流れを示した。図7からわかるように、高圧タンクの製造方法S10は、樹脂シート切り出しの工程S11、樹脂シート成形の工程S12、樹脂シート溶着の工程S13、樹脂含浸繊維巻き付けの工程S14、及び、樹脂含浸繊維硬化の工程S15を含んでいる。以下各工程について説明する。
樹脂シート切り出しの工程S11(「工程S11」と記載することがある。)では、樹脂シート14を切り出して準備する。図8には切り出した樹脂シート14の正面図(図8の左)、及び、部分断面図(図8の右)を表した。上記したように本形態では樹脂シート14は円環状である。また、工程S11で準備する樹脂シート14はその表裏が平坦である。
また、工程S11で準備する樹脂シート14の材料は上記した通りである。
樹脂シート成形の工程S12(「工程S12」と記載することがある。)では、工程S11で準備した樹脂シート14を、当該樹脂シート14を配置する部分に沿った形状となるように成形する。これにより、樹脂シート14をより精度よく配置することができる。従って、工程S12は必ずしも含める必要はなく、必要に応じて含めればよい。
これにより、図10に示したように、金型21及び金型22を樹脂シート14から離脱すれば、樹脂シート14は配置すべき部位の形状に沿った凹凸面を有する樹脂シート14に成形される。
樹脂シート溶着の工程S13(「工程S13」と記載することがある。)では、工程S12で成形した樹脂シート14(工程S12を含まない場合には工程S11で準備した樹脂シート14)を、口金13が取り付けられたライナ本体12に溶着する。
すなわち、樹脂シート14を該樹脂シート14を構成する材料の軟化点より高い温度に加熱して樹脂シート14を口金13が取り付けられたライナ本体12に押し付けることにより溶着する。樹脂シート14を配置する位置については上記した通りである。ここで「溶着」は、樹脂シート14がライナ本体12に重なる部分については溶接(樹脂シート14とライナ本体12とがその界面が明確でなくなるように互いに混ざり合っている接合状態)となり、樹脂シート14が口金13の面13eに重なる部分については口金13の面13eに対して接着(物理的なアンカー効果による接合状態)となっている状態とすることを意味する。
これによりライナ11が作製される。
樹脂含浸繊維層形成の工程S14(「工程S14」と記載することがある。)では、半硬化状態の樹脂が含浸された繊維束を工程S13で準備したライナ11の外周に巻き付ける。このような繊維束の巻き付け方法は特に限定されることはなく公知の方法によることができ、例えばフィラメントワインディング法を用いることができる。
本開示ではこれに限らず、樹脂が含浸されていない繊維束をライナ11の外周に巻き付け、繊維束のみによる層を形成した後にこの繊維束のみによる層に対して高圧で樹脂を注入して繊維束に樹脂を含浸する方法を適用することもできる。
樹脂含浸繊維硬化の工程S15(「工程S15」と記載することがある。)では、工程S14で形成した樹脂含浸繊維層に含浸された樹脂を硬化させる。当該硬化は例えば加熱炉による加熱が挙げられる。このときの加熱によるライナ11及び樹脂含浸繊維の到達最高温度や加熱炉の最高到達温度を樹脂シート14の軟化点よりも低いものとすれば、樹脂シート14の変形を抑制することができるので好ましい。
なお、含浸された樹脂として熱可塑性樹脂が用いられた場合には、加熱により軟化させて加工し、冷却により硬化するため、この加工温度(加工点温度)を樹脂シート14の軟化点よりも低くすることが好ましい。
本開示によれば上記のように、ライナ本体12と口金13のフランジ部13aの外周部との間隙(図3の間隙C)を樹脂シート14により覆っているので、含浸された樹脂が当該間隙Cに侵入することがなく不具合の発生を抑制することができる。
これにより高圧タンクが作製される。
11 ライナ
12 ライナ本体
13 口金
14 樹脂シート
15 補強層
Claims (2)
- 高圧タンクを製造する方法であって、
円板状のフランジ部を備える口金を有するライナ本体に対して、前記口金の前記フランジ部の外周部と前記ライナ本体との間隙、及び、前記フランジ部の面のうち前記ライナ本体に接する側と反対側の面の全部を覆う樹脂シートを設置し、前記樹脂シートを加熱して前記口金及び前記ライナ本体に溶着してライナを作製する工程、及び、
前記ライナの外周に樹脂が含浸した繊維層を形成し、前記含浸した樹脂を硬化させる工程、を含み、
前記樹脂シートを構成する材料の軟化点は、前記含浸した樹脂の加熱による前記ライナの到達最高温度よりも高く、
前記ライナを作製する工程における前記溶着は前記ライナ本体と前記樹脂シートとの境界が不明となる接合状態とされており、
前記樹脂シートは前記ライナ本体に設置される前に、設置される部位の形状に沿うように予め成形される、
高圧タンクの製造方法。 - 前記樹脂シートがナイロン樹脂からなる、請求項1に記載の高圧タンクの製造方法。