JP6920620B2 - 硬化性樹脂組成物、その硬化物およびその硬化物で接合された接合体 - Google Patents
硬化性樹脂組成物、その硬化物およびその硬化物で接合された接合体 Download PDFInfo
- Publication number
- JP6920620B2 JP6920620B2 JP2018542052A JP2018542052A JP6920620B2 JP 6920620 B2 JP6920620 B2 JP 6920620B2 JP 2018542052 A JP2018542052 A JP 2018542052A JP 2018542052 A JP2018542052 A JP 2018542052A JP 6920620 B2 JP6920620 B2 JP 6920620B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- acrylate
- component
- compound
- curable resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(A)成分:イソシアネート基含有ウレタンプレポリマー、
(B)成分:25℃で固体であるポリアミン化合物の粉体、
(C)成分:脂環構造を有する単官能(メタ)アクリレート化合物、芳香族環を有する単官能(メタ)アクリレート化合物、加水分解性シリル基を有する単官能(メタ)アクリレート化合物、および多官能(メタ)アクリレート化合物からなる群から選択される少なくとも1種。
(A)成分:イソシアネート基含有ウレタンプレポリマー、
(B)成分:25℃で固体であるポリアミン化合物の粉体、
(C)成分:脂環構造を有する単官能(メタ)アクリレート化合物、芳香族環を有する単官能(メタ)アクリレート化合物、加水分解性シリル基を有する単官能(メタ)アクリレート化合物、および多官能(メタ)アクリレート化合物からなる群から選択される少なくとも1種。
本発明の第一の形態に係る硬化性樹脂組成物は、(A)成分であるイソシアネート基含有ウレタンプレポリマーを含む。
前記(a−1)成分におけるポリオール化合物とは、1分子中に水酸基を2以上有する化合物である。ポリオール化合物としては、特に制限されないが、例えば、ポリエーテルポリオール、ポリエステルポリオール、ヒマシ油系ポリオール、水素添加ヒマシ油系ポリオール、ポリカーボネートポリオール、ポリブタジエンポリオール、ポリイソプレンポリオール、水素添加ポリイソプレンポリオール等が挙げられる。また、これらの中でも、ポリカーボネート(PC)との密着力が優れるとの観点から、ヒマシ油系ポリオール、水素添加ヒマシ油系ポリオール、ポリカーボネートポリオール、ポリイソプレンポリオール、水素添加ポリイソプレンポリオールが好ましく、ヒマシ油系ポリオール、水素添加ヒマシ油系ポリオール、ポリカーボネートポリオールがより好ましい。そして、これらの中でも、より優れたポリカーボネートとの密着力が得られるとの観点から、水素添加ヒマシ油系ポリオール、ヒマシ油系ポリオールが特に好ましい。また、ポリオール化合物は、1種単独で用いてもよく、2種以上を併用しても差し支えない。
前記(a−2)成分は、ポリイソシアネート化合物であれば特に限定されない。ポリイソシアネート化合物としては、例えば、1分子中にイソシアネート基を2つ以上含有する化合物であればよく、芳香族、鎖状脂肪族または環状脂肪族に属する任意のものが使用できる。具体的には、特に限定されないが、例えば、トリレンジイソシアネート(TDI)、ジフェニルメタンジイソシアネート(MDI)、3,3’−ジメチル−4,4’−ビフェニレンジイソシアネート、1,4−フェニレンジイソシアネート、キシリレンジイソシアネート、テトラメチルキシリレンジイソシアネート、ナフチレンジイソシアネート、ジシクロヘキシルメタン−4,4’−ジイソシアネート、ポリメチレン・ポリフェニルイソシアネート、イソホロンジイソシアネート、ヘキサメチレンジイソシアネート、水素化キシリレンジイソシアネート、これらの異性体、イソシアヌレート化物、カルボジイミド化物、ビューレット化物等が挙げられる。これらの中でも、トリレンジイソシアネート(TDI)、ジフェニルメタンジイソシアネート(MDI)が好ましい。また、ポリイソシアネート化合物は、1種単独で用いてもよく、または2種以上の混合物を使用に供してよい。
本発明の第一の形態に係る硬化性樹脂組成物は、(B)成分である25℃で固体であるポリアミン化合物の粉体を含む。
本発明の第一の形態に係る硬化性樹脂組成物は、(C)成分である、脂環構造を有する単官能(メタ)アクリレート化合物、芳香族環を有する単官能(メタ)アクリレート化合物、加水分解性シリル基を有する単官能(メタ)アクリレート化合物、および多官能(メタ)アクリレート化合物からなる群から選択される少なくとも1種を含む。
本発明の第一の形態に係る硬化性樹脂組成物は、光ラジカル開始剤を実質的に含まない。
本発明の第一の形態に係る硬化性樹脂組成物は、(D)成分であるグリシジル基を有する化合物をさらに含むことが好ましい。(D)成分は、貯蔵安定性および耐湿後の硬化物のポリカーボネートとの密着性をより向上させる機能を有する。
本発明の第一の形態に係る硬化性樹脂組成物には、本発明の特性を損なわない範囲において、1分子内に1以上のイソシアネート基を有する化合物であるイソシアネート化合物(上記(A)成分を除く);チイラン樹脂;カップリング剤;有機錫系触媒、ビスマス系触媒、チタン系触媒等の湿気重合触媒;ジシアンアミド、アミン−エポキシアダクト、尿素型アダクト、固形イミダゾール等のエポキシ潜在性触媒;リン酸エステル、ホウ酸エステル等の保存性向上剤;顔料、染料などの着色剤;炭酸カルシウム、タルク、シリカ、アルミナ、水酸化アルミニウム、水酸化マグネシウム、カーボン等の無機充填剤およびその表面を有機酸やカップリング剤で表面処理された無機充填剤;難燃剤;アクリルゴムやシリコンゴム等の有機充填剤;可塑剤;分子中にアクリル基等の反応性官能基を含む反応性可塑剤;酸化防止剤;紫外線吸収剤;消泡剤;脱水剤;レベリング剤;レオロジーコントロール剤等の各種添加剤を、目的に応じてさらに適量配合しても良い。これらの添加により、より柔軟性、樹脂強度、接着強さ、難燃性、熱伝導性、作業性等の所望の特性により優れる硬化性樹脂組成物およびその硬化物が得られる。
本発明の第三の形態は、本発明の第一の形態に係る硬化性樹脂組成物の硬化方法に関する。
本発明の第四の形態は、本発明の第一の形態に係る硬化性樹脂組成物の硬化物に関する。
本発明の第六の形態は、本発明の第一の形態に係る硬化性樹脂組成物を使用して被着体を接着してなる接合体に関する。すなわち、本発明の第六の形態は、本発明の第四の形態に係る硬化物と被着体とを含む接合体に関するものであり、より詳細には、第一の被着体と、本発明の第四の形態に係る硬化物と、第二の被着体とがこの順に積層され、かつ、第一の被着体および第二の被着体の表面と前記硬化物の表面とがそれぞれ接着している接合体に関する。
本発明の一形態に係る硬化型樹脂組成物は、特定の用途に限定されず、様々な用途に使用可能である。これらの中でも、本発明の一形態に係る硬化型樹脂組成物は、加熱により速やかに耐久性に優れた柔軟な硬化物が得られ、プラスチックや鉄等に対して優れた接着力を有することから、接着、封止、注型、塗装、コーティング材、光学部品の成形等の用途が好ましい。特に、貯蔵安定性と硬化物のポリカーボネートとの密着性に優れることから、接着剤用途が好ましい。
加熱温度調節装置を備えた容量3リットルのプラネタリー撹拌装置に、(a−1)成分として水素添加ヒマシ油系ポリオール(URIC 1815U、伊藤製油株式会社製、1分子当りの平均水酸基数2個)800.0gと、(a−2)成分としてジフェニルメタン−4,4’−ジイソシアネート(コスモネート(登録商標)PH、三井化学ポリウレタン株式会社製)161.0gと、を投入した。次いで、これらの混合物を窒素雰囲気下40℃にて1時間、60℃にて5時間撹拌反応させ、粘度142Pa・s(25℃)の(A)成分であるウレタンプレポリマー1を得た。
加熱温度調節装置を備えた容量3リットルのプラネタリー撹拌装置に、(a−1)成分としてヒマシ油系ポリオール(URIC H−56、伊藤製油株式会社製、1分子当りの平均水酸基数2個)600.0gと、(a−2)成分としてトリレンジイソシアネート(コスモネート(登録商標)T100、三井化学ポリウレタン株式会社製)148.0gと、を投入した。次いで、これらの混合物を窒素雰囲気下40℃にて1時間、60℃にて5時間撹拌反応させ、粘度7.3Pa・s(25℃)のウレタンプレポリマー2を得た。
加熱温度調節装置を備えた容量3リットルのプラネタリー撹拌装置に、(a−1)成分として数平均分子量2000のポリカーボネートポリオール(デュラノール(登録商標)T5652、旭化成ケミカルズ株式会社製、1分子当りの平均水酸基数2個)400質量部と、(a−2)成分としてトリレンジイソシアネート(コロネート(登録商標)T−80 日本ポリウレタン工業株式会社製)69.6質量部と、を投入した。次いで、これらの混合物を60℃にて8時間撹拌反応させ、粘度1350Pa・s(25℃)の(A)成分であるウレタンプレポリマー3を得た。
結晶塊状態の1,10−デカンジアミン(融点62℃)を破砕造粒整粒機で粗粉砕後、ジェットミルで粉砕することにより平均粒径5μm、最大粒径17μmのアミン微粉体であるポリアミン粉1を得た。ここで、粒径の測定にはレーザー回折・散乱式粒度分布測定器(株式会社セイシン企業製 LMS−30)を用いた。
実施例1〜12および比較例1〜5の各硬化性樹脂組成物を調製するため、下記成分を準備した。
a1:ウレタンプレポリマー1、
a2:ウレタンプレポリマー2、
a3:ウレタンプレポリマー3。
b1:ポリアミン粉1、
b2:平均粒径2μm、融点120℃の1,3−ビス(ヒドラジノカルボノエチル)−5−イソプロピルヒダントイン(アミキュア(登録商標)VDH−J 味の素ファインケミカル株式会社)。
c1:フェノキシエチルアクリレート(ライトアクリレート(登録商標)PO−A、共栄社化学株式会社製)、
c2:フェノキシエチルメタクリレート(ライトエステルPO、共栄社化学株式会社製)、
c3:イソボルニルアクリレート(ライトアクリレート(登録商標)IB−XA、共栄社化学株式会社製)、
c4:イソボルニルメタクリレート(ライトエステルIB−X、共栄社化学株式会社製)、
c5:3−メタクリロキシプロピルトリメトキシシラン(KBM−503、信越化学工業株式会社製)
c6:トリメチロールプロパントリメタクリレート(NKエステル(登録商標)TMPT、新中村化学工業株式会社製)、
c7:トリメチロールプロパントリアクリレート(NKエステル(登録商標)A−TMPT、新中村化学工業株式会社製)、
c8:イソシアヌル酸EO変性ジアクリレートおよびイソシアヌル酸EO変性トリアクリレートの混合物(アロニックス(登録商標)M−313、東亞合成株式会社製)
c9:ジペンタエリスリトールヘキサアクリレート(DPHA、ダイセル・オルネクス株式会社製)。
c’1:イソノニルアクリレート(INAA、大阪有機化学工業株式会社製)、
c’2:2−ヒドロキシエチルアクリレート(ライトアクリレート(登録商標)HOA、共栄社化学株式会社製)、
c’3:2−ヒドロキシプロピルアクリレート(ライトアクリレート(登録商標)HOP−A、共栄社化学株式会社製)、
c’4:2−イソシアナトエチルメタクリレート(カレンズMOI(登録商標)、昭和電工株式会社製)。
容量20mlのガラス瓶に各硬化性樹脂組成物を入れて蓋を閉めた状態で、25℃に設定した室内に7日間静置した。その後、各硬化性樹脂組成物を先端が尖った棒で接触して流動性を確認し、下記評価基準に基づき評価した。結果を下記表1〜3に示す。
○(良) :流動性が確認できた場合、
×(不良):ゲル化して流動しなくなっていた場合。
厚み5mm×幅25mm×長さ50mmのポリカーボネート製試験片2枚を十字になるように各硬化性樹脂組成物で貼り合わせた。次いで、ポリカーボネート製試験片(第一の被着体)、硬化性樹脂組成物、ポリカーボネート製試験片(第二の被着体)がこの順に積層されてなる各積層体について、それぞれ治具で固定した状態で80℃にて30分加熱し、その後、室温で1時間放置して、各テストピースを作製した。ここで、各テストピースは、第一の被着体および第二の被着体の表面と硬化性樹脂組成物の硬化物の表面とがそれぞれ接着された構造を有しており、前記硬化物は2つの被着体を接合する接着層となっていた。そして、引っ張り試験器を用いてクロスヘッドにより、2つのポリカーボネート製試験片(被着体)が分離するまで各テストピースを押圧した。その後、各被着体上の接着層(硬化物)の状態を観察し、以下の基準に基づき評価した。その結果を下記表1〜3に示す。なお、本試験では、接着層の密着力が高いほど凝集破壊を生じ、接着剤層の密着力が低いほど界面破壊を生じることとなる。評価結果としては、○または◎であることが実用上の観点から好ましい。また、測定不可能とは、硬化せず評価ができなかったものである。なお、比較例3、4に係る硬化性樹脂組成物を用いた評価としては、当該硬化性樹脂組成物の貯蔵安定性が著しく劣るため本試験を行うことはできなかったことから、評価結果の欄に未測定と表記している。
◎(良好):接着層がすべて凝集破壊であった場合、
○(良) :接着層が凝集破壊した部分と界面破壊した部分とがあった場合、
×(不良):接着層がすべて界面破壊であった場合。
実施例13〜25および比較例6の各硬化性樹脂組成物を調製するため、上記(A)成分、上記(B)成分および上記(C)成分に加えて、下記(D)成分をさらに準備した。ここで、実施例25は、実施例13〜24の(D)成分の効果を確認するための参考例として考えることもできる。
d1:3−グリシドキシプロピルトリメトキシシラン(KBM−403、信越化学工業株式会社製)、
d2:ビスフェノールF型エポキシ樹脂(jER(登録商標)807、三菱ケミカル株式会社製)。
容量20mlのガラス瓶に各硬化性樹脂組成物を入れて蓋を閉めた状態で、25℃に設定した室内に7日間静置した。その後、各硬化性樹脂組成物を先端が尖った棒で接触して流動性を確認し、下記評価基準に基づき評価した。結果を下記表4に示す。
○(良) :流動性が確認できた場合、
×(不良):ゲル化して流動しなくなっていた場合。
厚み5mm×幅25mm×長さ50mmのポリカーボネート製試験片2枚を十字になるように各硬化性樹脂組成物で貼り合わせた。次いで、ポリカーボネート製試験片(第一の被着体)、硬化性樹脂組成物、ポリカーボネート製試験片(第二の被着体)がこの順に積層されてなる各積層体について、それぞれ治具で固定した状態で80℃にて30分加熱し、その後、各積層体を60℃相対湿度95%RHに設定した高温高湿槽に96時間入れた後、高温高湿槽から取り出し、室温で1時間放置して、各テストピースを作製した。ここで、各テストピースは、第一の被着体および第二の被着体の表面と硬化性樹脂組成物の硬化物の表面とがそれぞれ接着された構造を有しており、前記硬化物は2つの被着体を接合する接着層となっていた。そして、引っ張り試験器を用いてクロスヘッドにより、2つのポリカーボネート製試験片(被着体)が分離するまで各テストピースを押圧した。その後、各被着体上の接着層(硬化物)の破壊状態を観察し、以下の基準に基づき評価した。また、引っ張り試験器により各テストピースの強度(MPa)を測定した。評価結果と引っ張り試験器により測定される強度(MPa)を下記表4〜表6に示す。なお、本試験では、接着層の密着力が高いほど凝集破壊を生じ、接着剤層の密着力が低いほど界面破壊を生じることとなる。評価結果としては、○または◎であることが実用上の観点から好ましい。また、本発明において、引っ張り試験器により測定される強度は、特に制限されないが、1.0MPa以上であることが特に好ましい。
◎(良好):接着層がすべて凝集破壊であった場合、
○(良) :接着層が凝集破壊した部分と界面破壊した部分とがあった場合、
×(不良):接着層がすべて界面破壊であった場合。
Claims (9)
- 下記の(A)〜(C)成分を含み、光ラジカル開始剤を実質的に含まず、かつ、脂肪族炭化水素基に結合するイソシアネート基と加水分解性シリル基および(メタ)アクリロイル基からなる群から選ばれる少なくとも1種とを有するイソシアネート基含有化合物を含まない硬化性樹脂組成物;
(A)成分:イソシアネート基含有ウレタンプレポリマー、
(B)成分:25℃で固体であるポリアミン化合物の粉体、
(C)成分:脂環構造を有する単官能(メタ)アクリレート化合物、芳香族環を有する単官能(メタ)アクリレート化合物、加水分解性シリル基を有する単官能(メタ)アクリレート化合物、および多官能(メタ)アクリレート化合物からなる群から選択される少なくとも1種。 - 下記の(A)〜(C)成分を含み、光ラジカル開始剤を実質的に含まない硬化性樹脂組成物;
(A)成分:イソシアネート基含有ウレタンプレポリマー、
(B)成分:25℃で固体であるポリアミン化合物の粉体、
(C)成分:脂環構造を有する単官能(メタ)アクリレート化合物、芳香族環を有する単官能(メタ)アクリレート化合物、加水分解性シリル基を有する単官能(メタ)アクリレート化合物、および多官能(メタ)アクリレート化合物からなる群から選択される少なくとも1種、
ここで、前記多官能(メタ)アクリレート化合物は、エチレングリコールジ(メタ)アクリレート、1,4−ブタンジオールジ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ)アクリレート、1,9−ノナンジオールジ(メタ)アクリレート、1,10−デカンジオールジ(メタ)アクリレート、ジエチレングリコールジ(メタ)アクリレート、トリエチレングリコールジ(メタ)アクリレート、ポリエチレングリコールジ(メタ)アクリレート、ジプロピレングリコールジ(メタ)アクリレート、トリプロピレングリコールジ(メタ)アクリレート、ポリプロピレングリコールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、ポリテトラメチレングリコールジ(メタ)アクリレート、ネオペンチルグリコールアジペートジ(メタ)アクリレート、ヒドロキシピバリン酸ネオペンチルグリコールジ(メタ)アクリレート、ジシクロペンタニルジ(メタ)アクリレート、ジメチロールトリシクロデカンジ(メタ)アクリレート、カプロラクトン変性ジシクロペンテニルジ(メタ)アクリレート、エチレンオキシド変性リン酸ジ(メタ)アクリレート、イソシアヌレートジ(メタ)アクリレート、アリル化シクロヘキシルジ(メタ)アクリレート、イソシアヌル酸EO変性ジ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ジペンタエリスリトールトリ(メタ)アクリレート、プロピオン酸変性ジペンタエリスリトールトリ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、エチレンオキシド変性トリメチロールプロパントリ(メタ)アクリレート、プロピレンオキシド変性トリメチロールプロパントリ(メタ)アクリレート、トリス(アクリロキシエチル)イソシアヌレート、イソシアヌル酸EO変性トリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ジトリメチロールプロパンテトラ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、プロピオン酸変性ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、カプロラクトン変性ジペンタエリスリトールヘキサ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、プロピオン酸変性ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、およびカプロラクトン変性ジペンタエリスリトールヘキサ(メタ)アクリレートからなる群より選択される少なくとも1種である。 - 前記脂環構造を有する単官能(メタ)アクリレート化合物は、シクロヘキシル(メタ)アクリレート、ジシクロペンタニル(メタ)アクリレート、ジシクロペンテニル(メタ)アクリレート、ジシクロペンテニルオキシ(メタ)アクリレート、イソボルニル(メタ)アクリレート、およびアダマンチル(メタ)アクリレートからなる群より選択される少なくとも1種であり、
前記芳香族環を有する単官能(メタ)アクリレート化合物は、フェノキシエチル(メタ)アクリレート、ベンジル(メタ)アクリレート、フェニル(メタ)アクリレート、フェノキシジエチレングリコール(メタ)アクリレート、フェノキシテトラエチレングリコール(メタ)アクリレート、およびノニルフェノキシエチル(メタ)アクリレートからなる群より選択される少なくとも1種であり、
前記加水分解性シリル基を有する単官能(メタ)アクリレート化合物は、3−(メタ)アクリロキシプロピルトリメトキシシラン、3−(メタ)アクリロキシプロピルトリエトキシシラン、3−(メタ)アクリロキシプロピルメチルジメトキシシラン、および3−(メタ)アクリロキシプロピルメチルジエトキシシランからなる群より選択される少なくとも1種であることを特徴とする請求項2に記載の硬化性樹脂組成物。 - 前記(B)成分の平均粒径が0.1〜100μmであることを特徴とする請求項1〜3のいずれか1項に記載の硬化性樹脂組成物。
- 前記(A)成分100質量部に対して、前記(B)成分を0.1〜100質量部含むことを特徴とする請求項1〜4のいずれか1項に記載の硬化性樹脂組成物。
- (D)成分であるグリシジル基を有する化合物をさらに含むことを特徴とする請求項1〜5のいずれか1項に記載の硬化性樹脂組成物。
- 前記(D)成分の配合量は、前記(A)成分100質量部に対して、0.1〜10質量部であることを特徴とする請求項6に記載の硬化性樹脂組成物。
- 請求項1〜7のいずれか1項に記載の硬化性樹脂組成物の硬化物。
- 第一の被着体と、請求項8に記載の硬化物と、第二の被着体とがこの順に積層され、かつ、前記第一の被着体および前記第二の被着体の表面と前記硬化物の表面とがそれぞれ接着している接合体。