JP6830542B2 - 製鉄工程の副産物を用いた無機繊維及びその製造方法 - Google Patents
製鉄工程の副産物を用いた無機繊維及びその製造方法 Download PDFInfo
- Publication number
- JP6830542B2 JP6830542B2 JP2019539720A JP2019539720A JP6830542B2 JP 6830542 B2 JP6830542 B2 JP 6830542B2 JP 2019539720 A JP2019539720 A JP 2019539720A JP 2019539720 A JP2019539720 A JP 2019539720A JP 6830542 B2 JP6830542 B2 JP 6830542B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- slag
- inorganic fiber
- oxide
- producing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1.無機繊維の製造
転炉スラグとフェロニッケルスラグを1:1の重量比で配合し、配合物を1480℃の温度で溶融して液状につくった。
上記1.の配合物の組成による溶融配合物の粘度変化を確認するために、酸化アルミニウム(Al2O3)、二酸化ケイ素(SiO2)、鉄酸化物(Fe2O3)、カルシウム酸化物(CaO)、及びマグネシウム酸化物(MgO)の含量を変化させながら、約1500度(℃)の温度で粘度変化を測定した。
2 ブッシング(bushing)
3 ワインダー(winder)
Claims (8)
- 無機繊維であって、
該無機繊維は、20〜40重量%の二酸化ケイ素(SiO2)、10〜30重量%の鉄酸化物(Fe2O3)、1〜5重量%の酸化アルミニウム(Al2O3)、15〜40重量%のカルシウム酸化物(CaO)、及び15〜35重量%のマグネシウム酸化物(MgO)を含有する、無機繊維。 - 前記繊維の平均直径は5μm〜50μmの範囲である、請求項1に記載の無機繊維。
- 鋼の製造工程中に発生したスラグを用意する過程と、
前記スラグの組成を測量し、組成比を20〜40重量%の二酸化ケイ素(SiO2)、10〜30重量%の鉄酸化物(Fe2O3)、1〜5重量%の酸化アルミニウム(Al2O3)、15〜40重量%のカルシウム酸化物(CaO)、及び15〜35重量%のマグネシウム酸化物(MgO)を含むように制御した配合物を製造する過程と、
前記配合物を溶融させる過程と、
溶融物を繊維状に繊維化する過程と、
を含む、無機繊維の製造方法。 - 前記スラグは、フェロニッケルスラグ、転炉スラグ、脱燐炉スラグ、高炉スラグ、高マンガン鋼スラグ、製鋼スラグ、及び電気炉スラグの少なくともいずれか一つを含む、請求項3に記載の無機繊維の製造方法。
- 前記溶融させる過程は、電気炉、水素エネルギー、及びブラウンガスからなるグループから選択される少なくとも一つを用いて行われる、請求項3に記載の無機繊維の製造方法。
- 前記溶融させる過程は、1300℃〜1650℃の温度範囲で行われる、請求項3に記載の無機繊維の製造方法。
- 前記繊維化する過程は、溶融した原料が入槽される容器が回転して紡糸方式で行われる、請求項3に記載の無機繊維の製造方法。
- 巻き取りのためのワインダーの回転速度は、5rpm〜2000rpmである、請求項7に記載の無機繊維の製造方法。