JP6566954B2 - 無機結合材のレオロジー改善用添加剤 - Google Patents
無機結合材のレオロジー改善用添加剤 Download PDFInfo
- Publication number
- JP6566954B2 JP6566954B2 JP2016541494A JP2016541494A JP6566954B2 JP 6566954 B2 JP6566954 B2 JP 6566954B2 JP 2016541494 A JP2016541494 A JP 2016541494A JP 2016541494 A JP2016541494 A JP 2016541494A JP 6566954 B2 JP6566954 B2 JP 6566954B2
- Authority
- JP
- Japan
- Prior art keywords
- structural unit
- polycondensate
- mol
- units
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(I)少なくとも1個の構造単位、この構造単位は、アルキレングリコール単位、好ましくはC2〜C5アルキレングリコール単位、より好ましくはC2〜C3アルキレングリコール単位を有するポリエーテル側鎖を有する芳香族部分であり、ただし、前記側鎖におけるエチレングリコール単位の数は、9〜41であり、かつエチレングリコール単位の含分は、前記ポリエーテル側鎖中の全てのアルキレングリコール単位に対して80mol%超、好ましくは85mol%超、より好ましくは90mol%超、最も好ましくは95mol%超であり、
(II)少なくとも1個の構造単位、この構造単位は、少なくとも1個のリン酸エステル基及び/又はその塩、好ましくは少なくとも1個のリン酸モノエステル及び/又はその塩を有する芳香族部分であり、ただし、(I)対(II)のモル比の値は、0.3〜4であり、
(III)少なくとも1個のメチレン単位(−CH2−)、このメチレン単位は、2個の芳香族構造単位Yに結合しており、
ここで、この芳香族構造単位Yは、相互に独立して、同一であるか又は異なり、構造単位(I)、構造単位(II)、又は任意で、(IV)前記構造単位(I)及び前記構造単位(II)とは異なる、前記重縮合物の芳香族構造単位によって表される、
を含有する、重縮合物によって達成され、前記単位(I)、(II)、(III)、及び任意で(IV)を含有する重縮合物の重縮合度は、10〜75の範囲、好ましくは20〜70の範囲、より好ましくは30〜65の範囲にある。リン酸エステル基は好ましくは、リン酸と、芳香族部分を有するアルコールとのエステルである。
前記式中、
Aは、同一であるか、又は異なり、C原子を5〜10個、好ましくは芳香族構造内に原子を5〜10個、より好ましくは芳香族構造内に炭素原子を5〜6個、最も好ましくは芳香族構造内に炭素原子を6個有する、置換若しくは非置換の芳香族若しくは複素環式芳香族化合物によって表され、かつベンゼン、又はベンゼンの置換された誘導体であり、
前記式中、
Bは、同一であるか、又は異なり、N、NH、又はOによって表され、
前記式中、
BがNであれば、nは2であり、BがNH又はOであれば、nは1であり、
前記式中、
R1、及びR2は相互に独立して、同一であるか、又は異なり、分枝鎖状若しくは直鎖状のC1〜C10アルキル基、C5〜C8シクロアルキル基、アリール基、ヘテロアリール基、又はHであり、ただし、ポリエーテル側鎖におけるエチレングリコール単位(R1及びR2はHである)の数は、9〜41であり、エチレングリコール単位の含分は、ポリエーテル側鎖中の全てのアルキレングリコールに対して80mol%超であり、
前記式中、
aは、同一であるか、又は異なり、12〜50の整数、好ましくは9〜35の整数によって表され、
前記式中、
Xは、同一であるか、又は異なり、直鎖状若しくは分枝鎖状のC1〜C10アルキル基、C5〜C8シクロアルキル基、アリール基、ヘテロアリール基、又はHによって表され、好ましくはHである。
前記式中、
Dは、同一であるか、又は異なり、C原子を5〜10個、好ましくは芳香族構造内に5〜10個、より好ましくは芳香族構造内に炭素原子を5〜6個、最も好ましくは芳香族構造内に炭素原子を6個有する、置換若しくは非置換の複素環式芳香族化合物によって表され、かつベンゼン、又はベンゼンの置換された誘導体であり、
前記式中、
Eは、同一であるか、又は異なり、N、NH、又はOによって表され、
前記式中、
EがNであれば、mは2であり、EがNH又はOであれば、mは1であり、
前記式中、
R3及びR4は相互に独立して、同一であるか、又は異なり、直鎖状若しくは分枝鎖状のC1〜C10アルキル基、C5〜C8シクロアルキル基、アリール基、ヘテロアリール基、又はHであり、好ましくはHであり、より好ましくはR3及びR4はともにHであり、
前記式中、
bは、同一であるか、又は異なり、0〜10の整数、好ましくは1〜5の整数、より好ましくは1〜2の整数、好ましくは1によって表され、
前記式中、
Mは、相互に独立して、同一であるか、又は異なり、H又はカチオン等価物である。
PD=Mw/[(Σi(ni×Mi))/(Σini)]
PD=Mw/[重縮合物中における全ての構造単位の平均分子量]
Mwは、GPCにより特定される重縮合物の平均分子量である:
カラムの組み合わせ:OH-Pak SB-G、OH-Pak SB 804 HQ、及びOH-Pak SB 802.5 HQ(日本国、Shodex社製);溶離剤:80体積%のHCO2NH4水溶液(0.05mol/l)、及び20体積%のアセトニトリル;注入体積100μl;流速0.5ml/分。分子量の較正は、UV検知器についてはポリ(スチレンスルホネート)標準で、RI検知器についてはポリ(エチレンオキシド)標準で行った。両方の標準は、ドイツ国のPSS Polymer Standards Serviceから購入した。ポリマーの分子量を特定するために、UV検知を254nmで使用した。なぜならUV検知機は、芳香族化合物に対してのみ信頼でき、無機不純物を感知しないからである(さもなくば、分子量についての結果をゆがめることになりかねない)。
例1.
一般式(I)の構造単位(2種の合計として)対一般式(II)の構造単位のモル比は、2/1である。構造単位(I)の第一の種類の分子量は500g/molであり、構造単位(I)の第二の種類の分子量は1,000g/molであり、2種類のモノマー(I)のモル比は、1/1である。(II)の分子量は200g/molであり、重縮合物の分子量は20,000g/molである(GPCによる)。
この場合にPD値は、以下のようになる:
68.9=20,000g/mol/[(1mol×500g/mol+1mol×1,000+1mol×200g/mol+3mol×14g/mol)/(1mol+1mol+1mol+3mol)]。
Mw=22,000g/mol
モノマー(I):質量が1,000g/mol(構造単位(I)としては998g/molに等しい)のエトキシ化フェノール
モノマー(II):質量が218g/mol(構造単位(II)としては216g/molに等しい)のフェノキシエタノールリン酸エステル
モノマー(I)/(II)のモル比は1/2。構造単位(IV)は、存在しない。
PD=89.7。
Mw=20,000g/mol
モノマー(I):質量が1,000g/mol(構造単位(I)としては998g/molに等しい)のエトキシ化フェノール
モノマー(II):質量が218g/mol(構造単位(II)としては216g/molに等しい)のフェノキシエタノールホスフェート。モノマー(I)/(II)のモル比は1/2。
PD=91.8。
(V) −[C6H3−O−(AO)n−H]−
nは、9〜41の整数、好ましくは9〜35の整数、より好ましくは12〜23の整数であり、Aは、2〜5個の炭素原子、好ましくは2〜3個の炭素原子を有するアルキレンであり、ただし、エチレングリコール単位の含分(A=エチレン)は、ポリエーテル側鎖(AO)n中にある全てのアルキレングリコール単位に対して80mol%超、好ましくは85mol%超、より好ましくは90mol%超、最も好ましくは95mol%超である。
(VI) −[C6H3−O−(AO)n−PO3M2]−
(VII) −[[M2O3P−(AO)n]−O−C6H2−O−[(AO)n−PO3M2]]−
両方の式においてnは、1〜5の整数、好ましくは1〜2の整数、好ましくは1であり、両方の式においてAは、炭素原子を2〜5個、好ましくは2〜3個有するアルキレンであり、Mは相互に独立して同一であるか又は異なり、H、又はカチオン等価物である。Aは好ましくは、エチレンである。
a)スルホン化メラミンホルムアルデヒド縮合物、
b)リグノスルホン酸塩、
c)スルホン化ケトン/ホルムアルデヒド縮合物、
d)スルホン化ナフタレン/ホルムアルデヒド縮合物(BNS)、
e)ポリカルボキシレートエーテル(PCE)、
f)水硬性セメント及び水を含有するセメント混合物について、ワーカビリティーを延長させるための非イオン性コポリマー、ここでこのコポリマーは、少なくとも以下のモノマーの残渣:
・セメント混合物中で加水分解可能な部分を有するエチレン系不飽和カルボン酸エステルモノマーを含有する、成分A、ここで、加水分解されたモノマー残渣は、セメント混合物の成分に対して活性結合箇所を有し、及び
・1〜350単位のC2〜4オキシアルキレン側基を少なくとも1個有する、エチレン系不飽和のカルボン酸エステル又はアルケニルエーテルモノマーを含有する、成分B
を含有し、又は
g)下記式:
R−(OA)n−N−[CH2−PO(OM2)2]2
に記載の分散剤を含有するリン酸塩、
前記式中、
Rは、H、又は飽和若しくは不飽和の炭化水素基であり、好ましくはC1〜C15アルキル基であり、
Aは、同一であるか、又は異なり、相互に独立して2〜18個の炭素原子を有するアルキレン、好ましくはエチレン及び/又はプロピレン、最も好ましくはエチレンであり、
nは、5〜500の整数、好ましくは10〜200の整数、最も好ましくは10〜100の整数であり、
Mは、H、アルカリ金属、1/2アルカリ土類金属、及び/又はアミンであり、ここで上記さらなる分散剤a)〜g)のあらゆる組み合わせがあり得る。
・不飽和モノカルボン酸エステル誘導体、例えばポリエチレングリコールモノ(メタ)アクリレート、ポリプロピレングリコール(メタ)アクリレート、ポリブチレングリコール(メタ)アクリレート、ポリエチレングリコールポリプロピレングリコールモノ(メタ)アクリレート、ポリエチレングリコールポリブチレングリコールモノ(メタ)アクリレート、ポリプロピレングリコールポリブチレングリコールモノ(メタ)アクリレート、ポリエチレングリコールポリプロピレングリコールポリブチレングリコールモノ(メタ)アクリレート、メトキシポリエチレングリコールモノ(メタ)アクリレート、メトキシポリプロピレングリコールモノ(メタ)アクリレート、メトキシポリブチレングリコールモノ(メタ)アクリレート、メトキシポリエチレングリコールポリプロピレングリコールモノ(メタ)アクリレート、メトキシポリエチレングリコールポリブチレングリコールモノ(メタ)アクリレート、メトキシポリプロピレングリコールポリブチレングリコールモノ(メタ)アクリレート、メトキシポリエチレングリコールポリプロピレングリコールポリブチレングリコールモノ(メタ)アクリレート、エトキシポリエチレングリコールモノ(メタ)アクリレート、エトキシポリプロピレングリコールモノ(メタ)アクリレート、エトキシポリブチレングリコールモノ(メタ)アクリレート、エトキシポリエチレングリコールポリプロピレングリコールモノ(メタ)アクリレート、エトキシポリエチレングリコールポリブチレングリコールモノ(メタ)アクリレート、エトキシポリプロピレングリコールポリブチレングリコールモノ(メタ)アクリレート、エトキシポリエチレングリコールポリプロピレングリコールポリブチレングリコールモノ(メタ)アクリレート、及び上記ポリアルオキシアルキレンの高級アルコキシ誘導体、
・ビニルアルコール誘導体、例えばポリエチレングリコールモノ(メタ)ビニルエーテル、ポリプロピレングリコールモノ(メタ)ビニルエーテル、ポリブチレングリコールモノ(メタ)ビニルエーテル、ポリエチレングリコールポリプロピレングリコールモノ(メタ)ビニルエーテル、ポリエチレングリコールポリブチレングリコールモノ(メタ)ビニルエーテル、ポリプロピレングリコールポリブチレングリコールモノ(メタ)ビニルエーテル、ポリエチレングリコールポリプロピレングリコールポリブチレングリコールモノ(メタ)ビニルエーテル、メトキシポリエチレングリコールモノ(メタ)ビニルエーテル、メトキシポリプロピレングリコールモノ(メタ)ビニルエーテル、メトキシポリブチレングリコールモノ(メタ)ビニルエーテル、メトキシポリエチレングリコールポリプロピレングリコールモノ(メタ)ビニルエーテル、メトキシポリエチレングリコールポリブチレングリコールモノ(メタ)ビニルエーテル、メトキシポリプロピレングリコールポリブチレングリコールモノ(メタ)ビニルエーテル、メトキシポリエチレングリコールポリプロピレングリコールポリブチレングリコールモノ(メタ)ビニルエーテル、エトキシポリエチレングリコールモノ(メタ)ビニルエーテル、エトキシポリプロピレングリコールモノ(メタ)ビニルエーテル、エトキシポリブチレングリコールモノ(メタ)ビニルエーテル、エトキシポリエチレングリコールポリプロピレングリコールモノ(メタ)ビニルエーテル、エトキシポリエチレングリコールポリブチレングリコールモノ(メタ)ビニルエーテル、エトキシポリプロピレングリコールポリブチレングリコールモノ(メタ)ビニルエーテル、エトキシポリエチレングリコールポリプロピレングリコールポリブチレングリコールモノ(メタ)ビニルエーテルなど;
・(メタ)アリルアルコール誘導体、例えばポリエチレングリコールモノ(メタ)アリルエーテル、ポリプロピレングリコールモノ(メタ)アリルエーテル、ポリブチレングリコールモノ(メタ)アリルエーテル、ポリエチレングリコールポリプロピレングリコールモノ(メタ)アリルエーテル、ポリエチレングリコールポリブチレングリコールモノ(メタ)アリルエーテル、ポリプロピレングリコールポリブチレングリコールモノ(メタ)アリルエーテル、ポリエチレングリコールポリプロピレングリコールポリブチレングリコールモノ(メタ)アリルエーテル、メトキシポリエチレングリコールモノ(メタ)アリルエーテル、メトキシポリプロピレングリコールモノ(メタ)アリルエーテル、メトキシポリブチレングリコールモノ(メタ)アリルエーテル、メトキシポリエチレングリコールポリプロピレングリコールモノ(メタ)アリルエーテル、メトキシポリエチレングリコールポリブチレングリコールモノ(メタ)アリルエーテル、メトキシポリプロピレングリコールポリブチレングリコールモノ(メタ)アリルエーテル、メトキシポリエチレングリコールポリプロピレングリコールポリブチレングリコールモノ(メタ)アリルエーテル、エトキシポリエチレングリコールモノ(メタ)アリルエーテル、エトキシポリプロピレングリコールモノ(メタ)アリルエーテル、エトキシポリブチレングリコールモノ(メタ)アリルエーテル、エトキシポリエチレングリコールポリプロピレングリコールモノ(メタ)アリルエーテル、エトキシポリエチレングリコールポリブチレングリコールモノ(メタ)アリルエーテル、エトキシポリプロピレングリコールポリブチレングリコールモノ(メタ)アリルエーテル、エトキシポリエチレングリコールポリプロピレングリコールポリブチレングリコールモノ(メタ)アリルエーテルなど;
・1〜350モルのアルキレンオキシドと、不飽和アルコールとの付加生成物、例えば3−メチル−3−ブテン−1−オール、3−メチル−2−ブテン−1−オール、2−メチル−3−ブテン−2−オール、2−メチル−2−ブテン−1−オール、及び2−メチル−3−ブテン−1−オール、それぞれ単独で、又は相互に組み合わせて、以下のものを含むが、これらに制限されず、ポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテル、ポリエチレングリコールモノ(3−メチル−2−ブテニル)エーテル、ポリエチレングリコールモノ(2−メチル−3−ブテニル)エーテル、ポリエチレングリコールモノ(2−メチル−2−ブテニル)エーテル、ポリエチレングリコールモノ(1,1−ジメチル−2−プロペニル)エーテル、ポリエチレンポリプロピレングリコールモノ(3−メチル−3−ブテニル)エーテル、ポリプロピレングリコールモノ(3−メチル−3−ブテニル)エーテル、メトキシポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテル、エトキシポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテル、1−プロポキシポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテル、シクロヘキシルオキシポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテル、1−アシルオキシポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテル、ノニルアルコキシポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテル、ラウリルアルコキシポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテル、ステアリルアルコキシポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテル、及びフェノキシポリエチレングリコールモノ(3−メチル−3−ブテニル)エーテルなど。ポリエーテル側鎖を有するエチレン系不飽和モノマー(それぞれポリアルキレングリコール側鎖を有する)についての上記例のリストは、分散f)又はf−1)中に含有される成分Bについても当てはまる。C2〜4オキシアルキレン基の少なくとも80質量%が、C2オキシアルキレン基(エチレン基)であるのが好ましい。
・セメント混合物中で加水分解可能な部分を有するエチレン系不飽和カルボン酸エステルモノマー、好ましくはアクリル酸エステルモノマー、より好ましくはヒドロキシアルキルアクリル酸モノエステル及び/又はヒドロキシアルキルジエステル、最も好ましくはヒドロキシプロピルアクリレート及び/又はヒドロキシエチルアクリレートを含有する、成分A、ここで、加水分解されたモノマー残渣は、セメント混合物の成分に対して活性結合箇所を有し、及び
・1〜350単位、好ましくは10〜120単位、特に10〜70単位のC2〜4オキシアルキレン側基を少なくとも1個有する、エチレン系不飽和のカルボン酸エステル又はアルケニルエーテルモノマーを含有する、成分B。好ましくは、C2〜4オキシアルキレン側基の少なくとも80質量%が、C2オキシアルキレン基(エチレン基)である。
カラムの組み合わせ:OH-Pak SB-G、OH-Pak SB 804 HQ、及びOH-Pak SB 802.5 HQ(日本国、Shodex社製);溶離剤:80体積%のHCO2NH4水溶液(0.05mol/l)、及び20体積%のアセトニトリル;注入体積100μl;流速0.5ml/分。分子量の較正は、UV検知器についてはポリ(スチレンスルホネート)標準で、RI検知器についてはポリ(エチレンオキシド)標準で行った。両方の標準は、ドイツ国のPSS Polymer Standardsから購入した。ポリマーの分子量を特定するために、UV検知を254nmで使用した。なぜならUV検知機は、芳香族化合物に対してのみ信頼でき、無機不純物を感知しないからである(さもなくば、分子量についての結果をゆがめることになりかねない)。
Me−O−(C2H4O)n−CH2CH(Me)−N−[CH2−PO(OM)2]2
Mは、H、アルカリ金属、(有機)アンモニウムイオン、又は1/2アルカリ土類金属であり、nは5〜70の整数、好ましくは10〜50の整数である。
・セメント混合物中で加水分解可能な部分を有するエチレン系不飽和カルボン酸エステルモノマーを含有する成分A、ここで加水分解されたモノマー残渣は、セメント混合物の成分のための活性結合箇所を有する、及び
・10〜70単位、好ましくは10〜30単位のC2〜4オキシアルキレン側基を少なくとも1個有する、エチレン系不飽和のカルボン酸エステル又はアルケニルエーテルモノマーを含有する、成分B。好ましくは、C2〜4オキシアルキレン側基の少なくとも80質量%が、C2オキシアルキレン基(エチレン基)である。
本発明による重縮合物は、以下の一般的なリン酸化、及び重縮合手順により製造した:
加熱部と撹拌機を備える反応器に、ポリリン酸(P2O5含分は85%と特定)127gを装入する。内容物を60〜100℃に加熱する。撹拌反応混合物に、1〜3時間にわたりアルコール1molを添加する。添加が終了後、反応混合物をさらに一時間、撹拌する。
撹拌機及び温度制御部を備える、耐圧性で耐蝕性の反応器(内側がガラスの鋼製、タンタル鋼、又はハステロイ製の反応器)に、以下に挙げる出発材料を、以下の順序で装入する(1)のアルコールと、2)リン酸化生成物の順序は変えてもよい):
1.ポリ(エチレンオキシド)モノフェニルエーテル(Ph−PEG)、
2.リン酸化フェノキシエタノール(PPE)、
3.調製溶液(37%、反応種A)、又はパラホルムアルデヒド+水(反応種B)、
4.96%の硫酸、又は70%のメタンスルホン酸。
コンクリートは粒状の系であるため、そのレオロジーは、ビンガムモデル(Bingham model)によって記載することができる。よって降伏応力により、コンクリートが自身の重量により流れ始める値が決まる。この値は、流下試験により容易に測定することができる。コンクリート又はモルタルの流動性は、降伏応力(τ0)と相関関係にある。塑性粘度(μ)により、成形又はポンピング中のコンクリートの流下時間又は速度が決まる。この値は、コンクリートがどれだけ容易に型枠に移動、又は充填できるかを示すものである(混練性、移動性、塗布性、噴霧性、ポンパビリティー、又は流動性)。さらに、コンクリートの流動特性は、チキソトロピー(ずり減粘)によって影響を受ける。静的条件では、コンクリートは粘稠(粘性)のままであるが、一定時間にわたり振動させる、撹拌する、又はその他の応力を与えると、より流動性に(より薄く、低粘度)なる。機械的な応力を停止すると、系が初期の粘性状態に戻るには、一定の時間を要する。
V漏斗試験におけるコンクリートの性質を評価するために、3種の異なるコンクリート調合設計(調合設計A、B、及びC)を使用して、非常に粘着性のコンシステンシーのコンクリートを作製した。
粉砕骨材994kg/m3、砂635kg/m3、CEM I 42.5 R 300kg/m3、フライアッシュ75kg/m3、高炉スラグ120kg/m3(4000ブレイン)、石灰岩粉末40kg/m3、水/結合材比0.38。
粉砕骨材997kg/m3、砕砂633kg/m3、CEM I 42.5 R 300kg/m3、フライアッシュ75kg/m3、高炉スラグ120kg/m3(4000ブレイン)、石灰岩粉末40kg/m3、水/セメント比0.62。
Claims (18)
- (I)少なくとも1個の構造単位、該構造単位は、アルキレングリコール単位を有するポリエーテル側鎖を有する芳香族部分であり、ただし、前記側鎖におけるエチレングリコール単位の数は、9〜41であり、かつエチレングリコール単位の含分は、前記ポリエーテル側鎖中の全てのアルキレングリコール単位に対して80mol%超であり、
(II)少なくとも1個の構造単位、該構造単位は、少なくとも1個のリン酸エステル基及び/又はその塩を有する芳香族部分であり、ただし、(I)対(II)のモル比の値は、0.3〜4であり、
(III)少なくとも1個のメチレン単位(−CH2−)、該メチレン単位は、2個の芳香族構造単位Yに結合しており、ここで該芳香族構造単位Yは、相互に独立して、同一であるか又は異なり、構造単位(I)、構造単位(II)、又は任意で、(IV)前記構造単位(I)及び前記構造単位(II)とは異なる、前記重縮合物の芳香族構造単位によって表される、
を含有する、重縮合物であって、
前記単位(I)、(II)、(III)、及び任意で(IV)を含有する重縮合物の重縮合度は、10〜75の範囲にある、前記重縮合物。 - 前記構造単位(I)のポリエーテル側鎖におけるエチレングリコール単位の数が、9〜35である、請求項1に記載の重縮合物。
- 前記重縮合物の平均分子量が、5,000g/mol〜25,000g/molである、請求項1又は2に記載の重縮合物。
- 前記構造単位(I)が、前記ポリエーテル側鎖の端部にヒドロキシ基を有する、アルコキシ化された芳香族アルコールモノマーから誘導されている、請求項1から3までのいずれか1項に記載の重縮合物。
- 前記構造単位(II)が、芳香族アルコールモノマーから誘導されており、該芳香族アルコールモノマーは、第一の工程でアルコキシ化されたものであり、こうして得られた、前記ポリエーテル側鎖の端部にヒドロキシ基を有するアルコキシ化された芳香族アルコールモノマーを、第二の工程でリン酸化してリン酸エステル基にしたものである、請求項1から4までのいずれか1項に記載の重縮合物。
- 前記構造単位(I)が、フェニルポリアルキレングリコールである、請求項1から5までのいずれか1項に記載の重縮合物。
- 前記構造単位(II)が、下記一般構造(VI)及び/又は(VII):
(VI) −[C6H3−O−(AO)n−PO3M2]−
(VII) −[[M2O3P−(AO)n]−O−C6H2−O−[(AO)n−PO3M2]]−
に記載のアルコキシ化されたフェノールリン酸エステル、又はアルコキシ化されたヒドロキノンリン酸エステルから成る群から選択されており、
両方の式中でnは1〜5の整数、好ましくは1〜2の整数、最も好ましくは1であり、
両方の式中でAは、炭素原子を2〜5個、好ましくは2〜3個有するアルキレンであり、
Mは相互に独立して、同一であるか又は異なり、H、又はカチオン等価物である、
請求項1から6までのいずれか1項に記載の重縮合物。 - 前記構造単位(I)からのエチレングリコール単位対、前記構造単位(II)からのリン酸エステル単位のモル比の値が、11〜40である、請求項1から7までのいずれか1項に記載の重縮合物。
- 前記構造単位(I)及び(II)の合計対、前記構造単位(IV)のモル比の値が、1超/1、好ましくは2超/1である、請求項1から8までのいずれか1項に記載の重縮合物。
- 前記構造単位(I)及び(II)の合計対、前記構造単位(IV)のモル比の値が10未満/1であり、前記構造単位(IV)が、アルキレングリコール単位を有するポリエーテル側鎖を有する芳香族部分であり、ただし、前記構造単位(IV)の側鎖におけるエチレングリコール単位の数は、42〜120であり、エチレングリコール単位の含分は、前記構造単位(IV)のポリエーテル側鎖中の全てのアルキレングリコール単位に対して80mol%超である、請求項9に記載の重縮合物。
- 前記構造単位(I)及び(II)の合計対、前記構造単位(III)のモル比の値が、0.8/1から1/0.8である、請求項1から10までのいずれか1項に記載の重縮合物。
- 請求項1から11までのいずれか1項に記載の重縮合物であって、
該重縮合物は、以下のa)〜g):
a)スルホン化メラミンホルムアルデヒド縮合物、
b)リグノスルホン酸塩、
c)スルホン化ケトン/ホルムアルデヒド縮合物、
d)スルホン化ナフタレン/ホルムアルデヒド縮合物(BNS)、
e)ポリカルボキシレートエーテル(PCE)、
f)水硬性セメント及び水を含有するセメント混合物について、ワーカビリティーを延長させるための非イオン性コポリマー、ここで該コポリマーは、少なくとも以下のモノマーの残渣:
・セメント混合物中で加水分解可能な部分を有するエチレン系不飽和カルボン酸エステルモノマーを含有する、成分A、ここで、加水分解されたモノマー残渣は、セメント混合物の成分に対して活性結合箇所を有し、及び
・1〜350単位のC2〜4オキシアルキレン側基を少なくとも1個有する、エチレン系不飽和のカルボン酸エステル又はアルケニルエーテルモノマーを含有する、成分B
を含有し、又は
g)下記式:
R−(OA)n−N−[CH2−PO(OM2)2]2
に記載の分散剤を含有するリン酸塩、
前記式中、
Rは、H、又は飽和若しくは不飽和の炭化水素基であり、好ましくはC1〜C15アルキル基であり、
Aは、同一であるか、又は異なり、相互に独立して2〜18個の炭素原子を有するアルキレン、好ましくはエチレン及び/又はプロピレン、最も好ましくはエチレンであり、
nは、5〜500の整数、好ましくは10〜200の整数、最も好ましくは10〜100の整数であり、
Mは、H、アルカリ金属、1/2アルカリ土類金属、及び/又はアミンである、
の群から選択されるさらなる分散剤とともに調製物中にあり、ここで上記さらなる分散剤a)〜g)のあらゆる組み合わせがあり得る、前記重縮合物。 - 調製物中のさらなる分散剤は、f−1)水硬性セメント、及び水を含有するセメント混合物についてワーカビリティーを延長するための、質量平均分子量Mwが5,000g/mol〜25,000g/mol未満である非イオン性コポリマーであり、ここで該コポリマーは、少なくとも以下のモノマーの残渣:
・セメント混合物中で加水分解可能な部分を有するエチレン系不飽和カルボン酸エステルモノマーを含有する、成分A、ここで、加水分解されたモノマー残渣は、セメント混合物の成分に対して活性結合箇所を有し、及び
・10〜70単位のC2〜4オキシアルキレン側基を少なくとも1個有する、エチレン系不飽和のカルボン酸エステル又はアルケニルエーテルモノマーを含有する、成分B
を含有する、請求項12に記載の重縮合物。 - 請求項1から13までのいずれか1項に記載の重縮合物1種以上と、α−硫酸カルシウム半水和物、β−硫酸カルシウム半水和物、無水石膏の形態の硫酸カルシウム、スラグ砂、フライアッシュ、フュームドシリカ、高炉スラグ、天然ポゾラン、オイルシェール燃焼物、及び/又は(ポルトランド)セメントの群から選択される無機結合材1種以上を含有し、ここで(ポルトランド)セメントについては、前記無機結合材の合計量に対して40質量%超の割合で存在するのが好ましい、建築材料混合物。
- 骨材、及び(ポルトランド)セメント、及び任意で、スラグ砂、フライアッシュ、フュームドシリカ、高炉スラグ、天然ポゾラン、又はオイルシェール燃焼物の群から選択されるさらなる結合材を含有し、ここで上記結合材のあらゆる組み合わせがあり得る、請求項14に記載の建築材料混合物。
- 請求項1から13までのいずれか1項に記載の重縮合物の使用であって、α−硫酸カルシウム半水和物、β−硫酸カルシウム半水和物、無水石膏の形態の硫酸カルシウム、スラグ砂、フライアッシュ、フュームドシリカ、高炉スラグ、天然ポゾラン、オイルシェール燃焼物、及び/又は(ポルトランド)セメントの群から選択される無機結合材を分散させるための、ここで(ポルトランド)セメントについては、前記無機結合材の合計量に対して40質量%超の割合で存在するのが好ましい、前記使用。
- 請求項1から13までのいずれか1項に記載の重縮合物の使用であって、コンクリートの塑性粘度を低下させるための、前記使用。
- 微細物の含分が300kg/m3〜700kg/m3である自己充填コンクリートのための、請求項1から13までのいずれか1項に記載の重縮合物の使用であって、前記微細物の定義は、EN 933-1に従って0.125mmの開口部を有する篩いを通過するあらゆる粒子であり、前記自己充填コンクリートは、水、骨材、及び(ポルトランド)セメント、及び任意で、スラグ砂、フライアッシュ、フュームドシリカ、高炉スラグ、天然ポゾラン、又はオイルシェール燃焼物の群から選択されるさらなる結合材を含有するものであり、ここで上記結合材のあらゆる組み合わせがあり得る、前記使用。