JP6363049B2 - ゴム組成物及びタイヤ - Google Patents
ゴム組成物及びタイヤ Download PDFInfo
- Publication number
- JP6363049B2 JP6363049B2 JP2015154872A JP2015154872A JP6363049B2 JP 6363049 B2 JP6363049 B2 JP 6363049B2 JP 2015154872 A JP2015154872 A JP 2015154872A JP 2015154872 A JP2015154872 A JP 2015154872A JP 6363049 B2 JP6363049 B2 JP 6363049B2
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- modified polymer
- group
- carbon
- phosphorus atom
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
しかし、シリカはジエン系ゴムとの親和性が低く、また、シリカ同士の凝集性が高いため、ジエン系ゴムに単にシリカを配合してもシリカが分散せず、タイヤの転がり抵抗を低減する効果が十分に得られないという問題があった。また、シリカの凝集により、加硫後のゴムの靭性が低下するという問題もあった。
これに対し、シリカと一緒にシランカップリング剤を配合することで、シリカの分散性を向上させる技術が知られている(例えば特許文献1)。
すなわち、本発明者らは、以下の構成により上記課題が解決できることを見出した。
上記変性ポリマーが、リン原子を含むリン原子含有基と炭素−炭素二重結合とを有し、
上記リン原子が、上記変性ポリマーの主鎖及び/又は側鎖を構成する炭素原子に直接結合し、
上記ジエン系ゴム中の上記変性ポリマーの含有量が、1.0〜100質量%であり、
上記ジエン系ゴム100質量部に対する上記無機充填剤の含有量が、150質量部以下である、ゴム組成物。
(2) 上記リン原子含有基が、後述する式(X)で表される基である、上記(1)に記載のゴム組成物。
(3) 上記式(X)中のR1及びR2が、それぞれ独立に、炭素数20以下の炭化水素基である、上記(1)又は(2)に記載のゴム組成物。
(4) 上記ジエン系ゴムが、ポリイソプレン、ポリブタジエン、芳香族ビニル−共役ジエン共重合ゴム、ブチルゴム、エチレンプロピレンゴム、エチレンプロピレンジエンゴム及び天然ゴムからなる群から選ばれる少なくとも1種である、上記(1)〜(3)のいずれかに記載のゴム組成物。
(5) 上記(1)〜(4)のいずれかに記載のゴム組成物を用いたタイヤ。
なお、本明細書において「〜」を用いて表される数値範囲は、「〜」の前後に記載される数値を下限値および上限値として含む範囲を意味する。
本発明のゴム組成物(以下、「本発明の組成物」とも言う)は、変性ポリマーを含むジエン系ゴムと、無機充填剤とを含有する。
ここで、上記変性ポリマーは、リン原子を含むリン原子含有基と炭素−炭素二重結合とを有し、上記リン原子は、上記変性ポリマーの主鎖及び/又は側鎖を構成する炭素原子に直接結合する。
また、上記ジエン系ゴム中の上記変性ポリマーの含有量は、1.0〜100質量%であり、上記ジエン系ゴム100質量部に対する上記無機充填剤の含有量は、150質量部以下である。
本発明の組成物はこのような構成をとるため、加硫後の靭性および低発熱性に優れるものと考えられる。その理由は明らかではないが、変性ポリマーのリン原子含有基がシリカなどの無機充填剤と相互作用することで、その分散性を向上させるためと推測される。
本発明の組成物に含有されるジエン系ゴムは、後述する変性ポリマーを含む。
ここで、ジエン系ゴム中の上記変性ポリマーの含有量は、1.0〜100質量%である。なかでも、5質量%以上であることが好ましく10質量%以上であることが好ましい。
なお、本明細書において、数平均分子量(Mn)および重量平均分子量(Mw)は、テトラヒドロフランを溶媒とするゲルパーミエーションクロマトグラフィー(GPC)により標準ポリスチレン換算により測定するものとする。
変性ポリマーは、リン原子を含むリン原子含有基と炭素−炭素二重結合(C=C)とを有する。ここで、上記リン原子は、上記変性ポリマーの主鎖及び/又は側鎖を構成する炭素原子に直接結合する。なお、本明細書において、「主鎖を構成する炭素原子」は、末端を構成する炭素原子を含まない。
リン原子含有基はリン原子を含有する基であれば特に制限されないが、下記式(X)で表される基であるのが好ましい。
上記脂肪族炭化水素基は、直鎖状、分岐鎖状、環状のいずれであってもよい。上記脂肪族炭化水素基の具体例としては、アルキル基(特に、炭素数1〜30)、アルケニル基(特に、炭素数2〜30)、アルキニル基(特に、炭素数2〜30)などが挙げられる。
上記芳香族炭化水素基としては、例えば、炭素数6〜24のアリール基が挙げられる。
炭化水素基は、例えば、酸素、窒素、硫黄、ハロゲン(例えば、フッ素、塩素、臭素、ヨウ素)、ホウ素原子のようなヘテロ原子を含む官能基を有していても良い。
上記アルキル基としては、例えば、メチル基、エチル基、オクチル基、2−エチルヘキシル基、デシル基、ドデシル基、トリデシル基、オクタデシル基、エイコシル基、オレイル基、ラウリル基が挙げられる。なかでも、エチル基、2−エチルヘキシル基、オクタデシル基、オレイル基、ラウリル基が好ましい。
上記アリール基としては、例えば、フェニル基、トリル基、ノニルフェニル基、ナフチル基などが挙げられる。
上記置換基としては、1価の置換基であれば特に制限されないが、例えば、ハロゲン原子、ヒドロキシ基、ニトロ基、カルボキシ基、アルコキシ基、アミノ基、メルカプト基、アシル基、イミド基、ホスフィノ基、ホスフィニル基、シリル基、ヘテロ原子を有していてもよい炭化水素基などが挙げられる。上記ハロゲン原子としては、例えば、フッ素原子、塩素原子、臭素原子、ヨウ素原子などが挙げられる。
変性ポリマーが炭素−炭素二重結合を有する位置は、特に制限されず、主鎖、側鎖などが挙げられる。
変性ポリマーの重量平均分子量は特に制限されないが、2,000〜3,000,000であることが好ましく、3,000〜2,000,000であることがより好ましい。
ここで、変性率は、変性ポリマーを構成する全構成ユニットのモル数に対する結合構造(リン原子含有基が結合したユニット)のモル数の比率であり、例えば、変性ポリマーの骨格が天然ゴムの場合、全イソプレンユニットのモル数と結合構造のモル数との合計に対する結合構造のモル数の比率である。
本発明の変性ポリマーを製造する方法は特に制限されないが、炭素−炭素二重結合を有するポリマーに、後述する式(M)で表される化合物(以下、「変性剤」とも言う)を反応させる方法(以下、「本発明の方法」とも言う)が好ましい。
本発明の方法で使用されるポリマーは炭素−炭素二重結合(C=C)を有するポリマーであれば特に制限されない。上記ポリマーが炭素−炭素二重結合を有する位置は、特に制限されず、主鎖、側鎖などが挙げられる。
上記ポリマーの具体例および好適な態様は、上述したジエン系ポリマーと同じである。
上記ポリマーは液状であっても、固体状であっても構わない。
また、上記ポリマーの分子量の好適な態様は上述した変性ポリマーと同じである。
本発明の方法で使用される変性剤は、下記式(M)で表される化合物である。下記式(M)で表される化合物は、ホスホン酸エステルである。
ホスホン酸ジメチル、ホスホン酸ジエチル、ホスホン酸ジブチル、ホスホン酸ジヘキシル、ホスホン酸ジオクチル、ホスホン酸ジ(2−エチルヘキシル)、ホスホン酸ジデシル、ホスホン酸ジドデシル(ホスホン酸ジラウリル)、ホスホン酸ジオクタデシルのようなハイドロゲンホスホン酸ジアルキルエステル;
ホスホン酸ジオレイルのようなハイドロゲンホスホン酸ジアルケニルエステル;
ホスホン酸ジフェニル、ホスホン酸ジトリルのような、ハイドロゲンホスホン酸ジ芳香族系エステル;
ホスホン酸モノ−2−エチルヘキシル、ホスホン酸モノオクチル、ホスホン酸モノ−1−メチルヘプチルのようなハイドロゲンホスホン酸モノアルキルエステル;
ホスホン酸モノオレイルのようなハイドロゲンホスホン酸モノアルケニルエステル;
ホスホン酸モノ−p−ノニルフェニルのようなハイドロゲンホスホン酸モノ芳香族系エステルなどが挙げられる。
本発明の方法では、マンガン触媒(特に、2価又は3価のマンガン触媒)などの触媒を用いるのが好ましい。
マンガン触媒としては、例えば、マンガンの、水酸化物、酸化物(複合酸化物を含む)、ハロゲン化物(フッ化物、塩化物、臭化物、ヨウ化物)、オキソ酸塩(例えば、硝酸塩、硫酸塩、リン酸塩、ホウ酸塩、炭酸塩など)、又は、オキソ酸、イソポリ酸、ヘテロポリ酸若しくはこれらの塩などの無機化合物;有機酸塩(例えば、酢酸塩、プロピオン酸塩、青酸塩、ナフテン酸塩、ステアリン酸塩など)、錯体などの有機化合物が挙げられる。上記錯体を構成する配位子としては、OH(ヒドロキソ)、アルコキシ(メトキシ、エトキシ、プロポキシ、ブトキシなど)、アシル(アセチル、プロピオニルなど)、アルコキシカルボニル(メトキシカルボニル、エトキシカルボニルなど)、アセチルアセトナート、シクロペンタジエニル基、ハロゲン原子(塩素、臭素など)、CO、CN、酸素原子、H2O(アコ)、ホスフィン(トリフェニルホスフィンなどのトリアリールホスフィンなど)のリン化合物、NH3(アンミン)、NO、NO2(ニトロ)、NO3(ニトラト)、エチレンジアミン、ジエチレントリアミン、ピリジン、フェナントロリンなどの窒素含有化合物などが挙げられる。
本発明の方法において、ポリマーに変性剤を反応させる方法は特に制限されないが、例えば、有機溶剤中で、ポリマーと、変性剤と、マンガン触媒とを混合し、加熱する方法などが挙げられる。
上記有機溶剤は特に制限されないが、例えば、酢酸、プロピオン酸などの有機酸;ベンゾニトリルなどのニトリル類;ホルムアミド、アセトアミド、ジメチルホルムアミド(DMF)、ジメチルアセトアミドなどのアミド類;ヘキサン、オクタンなどの脂肪族炭化水素;トルエンのような芳香族炭化水素;クロロホルム、ジクロロメタン、ジクロロエタン、四塩化炭素、クロロベンゼン、トリフルオロメチルベンゼンなどのハロゲン化炭化水素;ニトロベンゼンなどのニトロ化合物;これらの混合溶媒などが挙げられる。
また、触媒を使用する場合、変性剤の量に対する触媒の量の割合は特に制限されないが、5〜100質量%であることが好ましく、10〜100質量%であることがより好ましい。
本発明の組成物は、無機充填剤を含有する。
無機充填剤としては特に制限されないが、例えば、シリカ、炭酸カルシウム、炭酸マグネシウム、層状又は板状粘土鉱物、アルミナ、水酸化アルミニウム、酸化チタン、硫酸カルシウムなどの無機充填剤が挙げられ、こちらのうち1種を単独で用いても、2種以上を併用してもよい。なお、本明細書において、カーボンブラックは無機充填剤に該当しないものとする。
上記シリカは特に制限されないが、タイヤ等の用途でゴム組成物に配合されている従来公知の任意のシリカを用いることができる。
シリカの具体例としては、湿式シリカ、乾式シリカ、ヒュームドシリカ、珪藻土などが挙げられる。なかでも、湿式シリカが好ましい。上記シリカは、1種のシリカを単独で用いても、2種以上のシリカを併用してもよい。
本発明の組成物は、更にカーボンブラックを含有するのが好ましい。
上記カーボンブラックは特に制限されず、SAF−HS、SAF、ISAF−HS、ISAF、ISAF−LS、IISAF−HS、HAF−HS、HAF、HAF−LS、FEF、GPF、SRF等の各種グレードのものを使用することができる。
本発明の組成物は、必要に応じて、その効果や目的を損なわない範囲でさらに添加剤を含有することができる。
上記添加剤としては、例えば、シランカップリング剤、酸化亜鉛(亜鉛華)、ステアリン酸、接着用樹脂、素練り促進剤、老化防止剤、ワックス、加工助剤、アロマオイル、液状ポリマー、テルペン系樹脂、熱硬化性樹脂、加硫剤(例えば、硫黄)、加硫促進剤などのゴム組成物に一般的に使用される各種添加剤が挙げられる。
本発明の組成物の製造方法は特に限定されず、その具体例としては、例えば、上述した各成分を、公知の方法、装置(例えば、バンバリーミキサー、ニーダー、ロールなど)を用いて、混練する方法などが挙げられる。本発明の組成物が硫黄または加硫促進剤を含有する場合は、硫黄および加硫促進剤以外の成分を先に高温で混合し、冷却してから、硫黄または加硫促進剤を混合するのが好ましい。
また、本発明の組成物は、従来公知の加硫または架橋条件で加硫または架橋することができる。
本発明の組成物はタイヤに好適に用いられる。
本発明のタイヤは、上述した本発明の組成物を用いたタイヤである。
図1に、本発明のタイヤの実施態様の一例を表すタイヤの部分断面概略図を示すが、本発明のタイヤは図1に示す態様に限定されるものではない。
また、左右一対のビード部1間においては、繊維コードが埋設されたカーカス層4が装架されており、このカーカス層4の端部はビードコア5およびビードフィラー6の廻りにタイヤ内側から外側に折り返されて巻き上げられている。
また、タイヤトレッド部3においては、カーカス層4の外側に、ベルト層7がタイヤ1周に亘って配置されている。
また、ビード部1においては、リムに接する部分にリムクッション8が配置されている。
なお、タイヤトレッド部3は上述した本発明の組成物により形成されている。
600cc小型混合機(東洋精機製作所製ラボプラストミルB600型)で天然ゴム(SIR20、408.1g)とホスホン酸ジエチル(東京化成工業社製;3.4g)、トリス(2,4−ペンタンジオナト)マンガン(III)(東京化成工業社製;2.2g)を、10分間混合、150℃で放出してホスホン酸ジエチル変性天然ゴム(変性ポリマー1)を得た。反応生成物のNMRスペクトルから、ホスホン酸エステル基が、ポリマーの主鎖を構成する炭素原子に定量的に導入されたことを確認した。平均変性率は、NMRから算出した。
ホスホン酸ジエチル変性天然ゴム(変性ポリマー1)の31P−NMR(20℃),d=32.3(br).平均変性率:0.4mol%
600cc小型混合機(東洋精機製作所製ラボプラストミルB600型)で天然ゴム(SIR20、404.3g)とホスホン酸ジオクチル(東京化成工業社製;7.3g)、トリス(2,4−ペンタンジオナト)マンガン(III)(東京化成工業社製;2.2g)を、10分間混合、150℃で放出してホスホン酸ジオクチル変性天然ゴム(変性ポリマー2)を得た。反応生成物のNMRスペクトルから、ホスホン酸エステル基が、ポリマーの主鎖を構成する炭素原子に定量的に導入されたことを確認した。平均変性率は、NMRから算出した。
ホスホン酸ジオクチル変性天然ゴム(変性ポリマー2)の31P−NMR(20℃),d=32.3(br).平均変性率:0.4mol%
600cc小型混合機(東洋精機製作所製ラボプラストミルB600型)で天然ゴム(SIR20、401.5g)とホスホン酸ジラウリル(東京化成工業社製;10.1g)、トリス(2,4−ペンタンジオナト)マンガン(III)(東京化成工業社製;2.1g)を、10分間混合、150℃で放出してホスホン酸ジラウリル変性天然ゴム(変性ポリマー3)を得た。反応生成物のNMRスペクトルから、ホスホン酸エステル基が、ポリマーの主鎖を構成する炭素原子に定量的に導入されたことを確認した。平均変性率は、NMRから算出した。
ホスホン酸ジラウリル変性天然ゴム(変性ポリマー3)の31P−NMR(20℃),d=32.3(br).平均変性率:0.4mol%
下記表1に示される成分を、下記表1に示される割合(質量部)で配合した。
具体的には、表1に示す配合(質量部)において、加硫系(イオウ、加硫促進剤)を除く成分を接線式ミキサーで約5分30秒間混練した後、3分間リミル混合を行い、オープンロールで、加硫系を加えて混練し、ゴム組成物を得た。
得られたゴム組成物を所定の金型中148℃で30分間プレス加硫して、加硫ゴム試験片を調製した。得られた加硫ゴム試験片について以下のとおり切断時伸び及びtanδ(60℃)の評価を行った。
なお、比較例4については、加工性が著しく悪化し、加硫ゴム試験片を調製することができなかったため、切断時伸び及びtanδ(60℃)の評価を行わなかった。
JIS K−6251:2010に準拠し、室温にて切断時伸びを測定した。結果は、標準例の値を100とする指数で表した。値が大きいほど靭性に優れることを示す。
岩本製作所(株)製の粘弾性スペクトロメーターを用い、伸張変形歪率10±2%、振動数20Hz、温度60℃の条件にてtanδ(60℃)を測定した。結果は、標準例の値を100とする指数で表した。値が小さいほど低発熱性に優れることを示す。
・NR:NUSIRA SIR20
・変性ポリマー1:上述のとおり合成した変性ポリマー1
・変性ポリマー2:上述のとおり合成した変性ポリマー2
・変性ポリマー3:上述のとおり合成した変性ポリマー3
・カーボンブラック:昭和キャボット ショウブラックN550
・シリカ:Rhodia SilicaKorea ZEOSIL 165G
・カップリング剤:Degussa SI69
・酸化亜鉛:正同化学 亜鉛華3号
・ステアリン酸:日本油脂 ステアリン酸
・老化防止剤1:住友化学 アンチゲン6C
・老化防止剤2:大内新興化学 ノクラック
・せっけん:川口化学工業 エクストンL−2−G
・ワックス:大内新興化学 サンノック
・イオウ:軽井沢精錬所 油処理硫黄
・含硫黄加硫促進剤1:大内新興化学 ノクセラー
・含硫黄加硫促進剤2:住友化学 ソクシノールD−G
実施例1〜3および4〜6の対比から、炭素数が10以下である実施例1〜2および4〜5はより優れた低発熱性を示した。そのなかでも、炭素数が5以上である実施例2および5はより優れた靭性を示した。
2 サイドウォール部
3 タイヤトレッド部
4 カーカス層
5 ビードコア
6 ビードフィラー
7 ベルト層
8 リムクッション
Claims (4)
- 変性ポリマーを含むジエン系ゴムと、シリカとを含有し、
前記変性ポリマーが、リン原子を含むリン原子含有基と、ジエン系ゴムからなる炭素−炭素二重結合とを有し、
前記リン原子が、前記変性ポリマーの主鎖及び/又は側鎖を構成する炭素原子に直接結合し、
前記変性ポリマーの変性率が0.01〜70mol%であり、前記ジエン系ゴム中の前記変性ポリマーの含有量が、10〜100質量%であり、前記ジエン系ゴム100質量部に対する前記シリカの含有量が、150質量部以下であり、
前記リン原子含有基が、下記式(X)で表される基である、
ゴム組成物。
ここで、変性ポリマーの変性率は、変性ポリマーを構成する全構成ユニットのモル数に対する結合構造(リン原子含有基が結合したユニット)のモル数の比率をいう。
- 前記式(X)中のR1及びR2が、それぞれ独立に、炭素数20以下の炭化水素基である、請求項1に記載のゴム組成物。
- 前記ジエン系ゴムが、ポリイソプレン、ポリブタジエン、芳香族ビニル−共役ジエン共重合ゴム、ブチルゴム、エチレンプロピレンゴム、エチレンプロピレンジエンゴム及び天然ゴムからなる群から選ばれる少なくとも1種である、請求項1または2に記載のゴム組成物。
- 請求項1〜3のいずれか1項に記載のゴム組成物を用いたタイヤ。