JP6061831B2 - 金属酸化物膜の製造方法及び薄膜トランジスタの製造方法 - Google Patents
金属酸化物膜の製造方法及び薄膜トランジスタの製造方法 Download PDFInfo
- Publication number
- JP6061831B2 JP6061831B2 JP2013205315A JP2013205315A JP6061831B2 JP 6061831 B2 JP6061831 B2 JP 6061831B2 JP 2013205315 A JP2013205315 A JP 2013205315A JP 2013205315 A JP2013205315 A JP 2013205315A JP 6061831 B2 JP6061831 B2 JP 6061831B2
- Authority
- JP
- Japan
- Prior art keywords
- metal oxide
- film
- metal
- oxide film
- nitrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
一方で、簡便に、低温で、かつ大気圧下で高い半導体特性を有する金属酸化物膜を形成することを目的とした、液相プロセスによる金属酸化物膜の作製に関して研究開発が盛んに行われている。
また、金属アルコキシド又は金属塩を主原料として得られる金属酸化物の前駆体ゾルを被塗布物の表面に塗布して被塗布物表面に金属酸化物ゲルの薄膜を形成する工程と、金属酸化物ゲルの薄膜に対して波長が360nm以下である紫外光を照射して金属酸化物ゲルを結晶化させる工程とを複数回繰り返して行う金属酸化物膜の製造方法が開示されている(特許文献2参照)。
また、金属酸化物前駆体皮膜を用意し、酸素雰囲気中で主波長130〜180nmの真空紫外光を照射して結晶性の金属酸化物膜を形成させる方法が開示されている(特許文献3)。
また、溶液を基板上に塗布し、紫外線を用いることで150℃以下の低温で高い輸送特性を有する薄膜トランジスタ(TFT:Thin Film Transistor)を製造する手法が報告されている(非特許文献1参照)。
さらに、基板の少なくとも一方の面に、金属の硝酸塩、硫酸塩等から選ばれる金属塩を含む前駆体層を形成する工程と、前駆体層を紫外線照射及び加熱の少なくとも一方によって、金属酸化物等のガスバリア性層に変換する工程と、を含む、ガスバリア性フィルムの製造方法が開示されている(特許文献4)。
<1> 金属硝酸塩を含む溶液を基板上に塗布し、塗布膜を乾燥させて金属酸化物前駆体膜を形成する工程と、
金属酸化物前駆体膜に対し、250nm以上300nm以下の波長域に照度が10mW/cm 2 以上のピーク成分を1つ以上含み、且つ200nm以上250nm未満の波長域に照度が10mW/cm 2 以上のピーク成分を1つ以上含む紫外線を照射することにより、金属酸化物前駆体膜を金属酸化物膜に転化する工程と、
を含む金属酸化物膜の製造方法。
<2> 金属酸化物前駆体膜を金属酸化物膜に転化する工程における基板の最高到達温度が200℃以下である<1>に記載の金属酸化物膜の製造方法。
<3> 金属酸化物前駆体膜を金属酸化物膜に転化する工程における基板の最高到達温度が120℃以上である<1>又は<2>に記載の金属酸化物膜の製造方法。
<4> 金属硝酸塩を含む溶液が、少なくとも硝酸インジウムを含む<1>〜<3>のいずれかに記載の金属酸化物膜の製造方法。
<5> 硝酸インジウムを含む溶液が、亜鉛、錫、ガリウム及びアルミニウムから選ばれる少なくとも1つの金属原子を含む化合物をさらに含有する<4>に記載の金属酸化物膜の製造方法。
<6> 金属酸化物前駆体膜に紫外線を照射する際に用いる光源が、低圧水銀ランプ及びエキシマランプから選ばれる少なくとも1種である<1>〜<5>のいずれかに記載の金属酸化物膜の製造方法。
<7> 金属酸化物前駆体膜を形成する工程において、金属硝酸塩を含む溶液を、インクジェット法、ディスペンサー法、凸版印刷法、及び凹版印刷法から選択される少なくとも1種の塗布法により塗布する<1>〜<6>のいずれかに記載の金属酸化物膜の製造方法。
<8> 前記金属酸化物膜が金属酸化物半導体膜である<1>〜<7>のいずれかに記載の金属酸化物膜の製造方法。
<9> <1>〜<8>のいずれかに記載の製造方法で製造された金属酸化物膜を含む活性層と、ソース電極と、ドレイン電極と、ゲート絶縁膜と、ゲート電極とを形成する薄膜トランジスタの製造方法。
なお、図中、同一又は対応する機能を有する部材(構成要素)には同じ符号を付して適宜説明を省略する。また、本明細書において「〜」の記号により数値範囲を示す場合、下限値及び上限値が含まれる。
また、本発明に係る金属酸化物膜の導電性は限定されず、本発明は、酸化物半導体膜、酸化物導電膜、又は酸化物絶縁膜の製造に適用することができるが、代表例として、TFTの活性層(半導体層)に適用することができる金属酸化物半導体膜の製造方法について主に説明する。
金属硝酸塩を含む金属酸化物前駆体膜は、300nm以下の紫外線に対して吸収を持っており、紫外線によって前記金属酸化物前駆体膜中のなんらかの構造が変化し、元の金属酸化物前駆体膜とは異なる波長での吸収を持つようになる。そのため、元の金属酸化物前駆体膜の構造変化をもたらす紫外線とは別に、構造変化後の金属酸化物前駆体膜に適した別の波長を有する紫外線を照射することにより、構造変化後の膜の分解及び酸化物形成を効率よく行うことが可能となり結果として金属酸化物膜の緻密化が実現していると考えられる。
本発明の金属酸化体膜の製造方法は、金属硝酸塩を含む溶液を基板上に塗布し、塗布膜を乾燥させて金属酸化物前駆体膜を形成する工程と、金属酸化物前駆体膜に対し、300nm以下の波長域に照度が10mW/cm2以上のピーク成分を2つ以上含む紫外線を照射することにより、金属酸化物前駆体膜を金属酸化物膜に転化する工程と、を含む。
まず、金属酸化物膜を形成するための金属硝酸塩を含む溶液と、金属酸化物膜を形成するための基板を用意し、金属硝酸塩を含む溶液を基板上に塗布し、塗布膜を乾燥させて金属酸化物前駆体膜を形成する。
基板の形状、構造、大きさ等については特に制限はなく、目的に応じて適宜選択することができる。基板の構造は単層構造であってもよいし、積層構造であってもよい。
具体的には、ポリブチレンテレフタレート、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンナフタレート、ポリスチレン、ポリカーボネート、ポリスルホン、ポリエーテルスルホン、ポリアリレート、アリルジグリコールカーボネート、ポリアミド、ポリイミド、ポリアミドイミド、ポリエーテルイミド、ポリベンズアゾール、ポリフェニレンサルファイド、ポリシクロオレフィン、ノルボルネン樹脂、ポリクロロトリフルオロエチレン等のフッ素樹脂、液晶ポリマー、アクリル樹脂、エポキシ樹脂、シリコーン樹脂、アイオノマー樹脂、シアネート樹脂、架橋フマル酸ジエステル、環状ポリオレフィン、芳香族エーテル、マレイミド・オレフィン、セルロース、エピスルフィド化合物等の合成樹脂基板、酸化珪素粒子との複合プラスチック材料、金属ナノ粒子、無機酸化物ナノ粒子、無機窒化物ナノ粒子等との複合プラスチック材料、カーボン繊維、カーボンナノチューブとの複合プラスチック材料、ガラスフェレーク、ガラスファイバー、ガラスビーズとの複合プラスチック材料、粘土鉱物や雲母派生結晶構造を有する粒子との複合プラスチック材料、薄いガラスと上記単独有機材料との間に少なくとも1回の接合界面を有する積層プラスチック材料、無機層と有機層を交互に積層することで、少なくとも1回以上の接合界面を有するバリア性能を有する複合材料、ステンレス基板或いはステンレスと異種金属を積層した金属多層基板、アルミニウム基板或いは表面に酸化処理(例えば陽極酸化処理)を施すことで表面の絶縁性を向上させた酸化皮膜付きのアルミニウム基板等を用いることができる。また、樹脂基板は耐熱性、寸法安定性、耐溶剤性、電気絶縁性、加工性、低通気性、又は低吸湿性等に優れていることが好ましい。樹脂基板は、水分や酸素の透過を防止するためのガスバリア層や、樹脂基板の平坦性や下部電極との密着性を向上するためのアンダーコート層等を備えていてもよい。
金属硝酸塩を含む溶液は、金属硝酸塩等の溶質を、溶液が所望の濃度となるように秤量し、溶媒中で攪拌して溶解させて得られる。攪拌を行う時間は溶質が十分に溶解されれば特に制限はない。
金属硝酸塩以外の金属塩としては、硫酸塩、燐酸塩、炭酸塩、酢酸塩、蓚酸塩等が挙げられ、金属ハロゲン化物としては、塩化物、ヨウ化物、臭化物等が挙げられ、有機金属化合物としては、金属アルコキシド、有機酸塩、金属βジケトネート等が挙げられる。
また、金属酸化物前駆体膜に紫外線を照射して金属酸化物膜に転化する工程において、前駆体膜が紫外光を効率よく吸収することができ、インジウム含有酸化物膜を容易に形成することができる。
なお、インジウムと前記金属元素を含む酸化物半導体及び酸化物導電体として、In−Ga−Zn−O(IGZO)、In−Zn−O(IZO)、In−Ga−O(IGO)、In−Sn−O(ITO)、In−Sn−Zn−O(ITZO)等が挙げられる。
金属硝酸塩を含む溶液(金属酸化物膜形成用塗布液)を基板上に塗布する方法は特に限定されず、スプレーコート法、スピンコート法、ブレードコート法、ディップコート法、キャスト法、ロールコート法、バーコート法、ダイコート法、ミスト法、インクジェット法、ディスペンサー法、スクリーン印刷法、凸版印刷法、及び凹版印刷法等が挙げられる。特に、微細パターンを容易に形成する観点から、インクジェット法、ディスペンサー法、凸版印刷法、及び凹版印刷法から選択される少なくとも一種の塗布法を用いることが好ましい。
金属酸化物膜形成用塗布液を基板上に塗布した後、塗布膜を乾燥させ、金属酸化物前駆体膜を得る。乾燥によって、塗布膜の流動性を低減させ、最終的に得られる酸化物膜の平坦性を向上させることができる。乾燥温度(基板の温度)は、35℃以上100℃以下が好ましい。上記温度範囲であれば、最終的により緻密な金属酸化物膜が得られ易い。乾燥のための加熱処理の方法は特に限定されず、ホットプレート加熱、電気炉加熱、赤外線加熱、マイクロ波加熱等から選択することができる。
乾燥は膜の平坦性を均一に保つ観点から、塗布後、5分以内に開始することが好ましい。
乾燥を行う時間は特に制限はないが、膜の均一性、生産性の観点から15秒以上10分以下であることが好ましい。
また、乾燥における雰囲気に特に制限はないが、製造コスト等の観点から大気圧下、大気中で行うことが好ましい。
次いで、乾燥させて得た金属酸化物前駆体膜に対し、300nm以下の波長域に照度が10mW/cm2以上のピーク成分を2つ以上含む紫外線(UV:Ultraviolet)を照射する。
上記2つ以上のピーク成分は一つの紫外線光源から得てもよく、二つ以上の紫外線光源を用いて得てもよい。紫外線の光源としては、UVランプ、レーザーが挙げられるが、大面積に均一に、安価な設備で紫外線照射を行う観点からUVランプが好ましい。
UVランプとしては、エキシマランプ、重水素ランプ、低圧水銀ランプ、高圧水銀ランプ、超高圧水銀ランプ、メタルハライドランプ、ヘリウムランプ、カーボンアークランプ、カドミウムランプ、無電極放電ランプ等が挙げられ、好ましくは低圧水銀ランプ及びエキシマランプから選ばれる少なくとも1つ、特に低圧水銀ランプとエキシマランプを併用すると容易に金属酸化物前駆体膜から金属酸化物膜への転化が行えることから好ましい。
転化工程における基板の最高到達温度は200℃以下が好ましく、120℃以上がより好ましい。200℃以下であれば耐熱性の低い樹脂基板への適用が容易となり、120℃以上であれば緻密な金属酸化物膜が得られやすい。なお、転化工程における基板の最高到達温度はサーモラベルによって測定することができる。
紫外線処理時の基板温度は、用いる紫外線ランプ等の光源からの輻射熱を用いてもよく、ヒーター等によって基板温度を制御してもよい。紫外線ランプからの輻射熱を用いる際には、ランプ−基板間距離やランプ出力を調整することで制御することができる。
なお、金属酸化物前駆体膜に照射する紫外線の照度は、例えば、紫外線光量計(オーク製作所社製、UV−M10、受光器UV−25)を用いて測定することができる。
尚、上記塗布、乾燥による金属酸化物前駆体膜の形成及び金属酸化物膜への転化を交互に複数回繰り返してもよい。
金属酸化物膜のインジウムの含有量が、金属酸化物膜に含まれる全金属元素の50atom%以上であることが好ましい。インジウム含有量が50atom%以上であれば低温で容易に高い電気伝導性が得られる。
金属酸化物膜は、インジウム以外の金属元素として、亜鉛,錫,ガリウム及びアルミニウムから選ばれる少なくとも1種の金属成分を含むことが好ましい。前記金属元素を適量含むことにより、電気伝導性の向上や、金属酸化物半導体膜を作製した際の閾値電圧制御や電気的安定性の向上効果が得られる。インジウムと前記金属元素を含む酸化物半導体及び酸化物導電体として、In−Ga−Zn−O(IGZO)、In−Zn−O(IZO)、In−Ga−O(IGO)、In−Sn−O(ITO)、In−Sn−Zn−O(ITZO)等が挙げられる。
また、耐熱性の低い樹脂基板に適用できることからフレキシブルディスプレイ等のフレキシブル電子デバイスを安価に作製することが可能となる。特に金属酸化物半導体膜や金属酸化物導電膜に用いた際に極めて電子伝達特性が高い膜を得ることができる。
本発明の実施形態により作製された金属酸化物半導体膜は高い半導体特性を示すことから、薄膜トランジスタ(TFT)の活性層(酸化物半導体層)に好適に用いることができる。以下、本発明の製造方法により作製された金属酸化物膜を薄膜トランジスタの活性層として用いる実施形態について説明する。
尚、実施形態としてはトップゲート型の薄膜トランジスタについて記述するが、本発明の金属酸化物半導体膜を用いた薄膜トランジスタはトップゲート型に限定されることなく、ボトムゲート型の薄膜トランジスタであってもよい。
トップゲート型とは、TFTが形成されている基板を最下層としたときに、ゲート絶縁膜の上側にゲート電極が配置され、ゲート絶縁膜の下側に活性層が形成された形態である。ボトムゲート型とは、ゲート絶縁膜の下側にゲート電極が配置され、ゲート絶縁膜の上側に活性層が形成された形態である。また、ボトムコンタクト型とは、ソース・ドレイン電極が活性層よりも先に形成されて活性層の下面がソース・ドレイン電極に接触する形態である。トップコンタクト型とは、活性層がソース・ドレイン電極よりも先に形成されて活性層の上面がソース・ドレイン電極に接触する形態である。
本実施形態の薄膜トランジスタ10を製造する場合、まず、金属硝酸塩を含む溶液を準備し、溶液を基板12上に塗布して乾燥させることで金属酸化物前駆体膜を形成し、次いで、金属酸化物前駆体膜に対し、300nm以下の波長域に照度が10mW/cm2以上のピーク成分を2つ以上含む紫外線を照射することにより、金属酸化物前駆体膜を金属酸化物膜に転化する。
フォトリソグラフィー及びエッチングによりパターン形成を行うには、金属酸化物半導体膜を形成した後、活性層14として残存させる部分にフォトリソグラフィーによりレジストパターンを形成した後、塩酸、硝酸、希硫酸、又は燐酸、硝酸及び酢酸の混合液等の酸溶液によりエッチングすることにより活性層14のパターンを形成する。
活性層14上にはソース・ドレイン電極16,18のエッチング時に活性層14を保護するための保護層(不図示)を形成することが好ましい。保護層の成膜方法に特に限定はなく、金属酸化物半導体膜を形成した後、パターニングする前に形成してもよいし、金属酸化物膜のパターニング後に形成してもよい。
また、保護層としては金属酸化物層であってもよく、樹脂のような有機材料であってもよい。なお、保護層はソース電極15及びドレイン電極18(適宜「ソース・ドレイン電極」と記す)の形成後に除去しても構わない。
金属酸化物半導体膜で形成される活性層14上にソース・ドレイン電極16,18を形成する。ソース・ドレイン電極16,18はそれぞれ電極として機能するように高い導電性を有するものを用い、Al,Mo,Cr,Ta,Ti,Au,Au等の金属、Al−Nd、Ag合金、酸化錫、酸化亜鉛、酸化インジウム、酸化インジウム錫(ITO)、酸化亜鉛インジウム(IZO)、In−Ga−Zn−O等の金属酸化物導電膜等を用いて形成することができる。
ソース・ドレイン電極16,18及び配線(不図示)を形成した後、ゲート絶縁膜20を形成する。ゲート絶縁膜20は高い絶縁性を有するものが好ましく、例えばSiO2、SiNx、SiON、Al2O3、Y2O3、Ta2O5、HfO2等の絶縁膜、又はこれらの化合物を2種以上含む絶縁膜としてもよい。
ゲート絶縁膜20は、印刷方式、コーティング方式等の湿式方式、真空蒸着法、スパッタリング法、イオンプレーティング法等の物理的方式、CVD、プラズマCVD法等の化学的方式等の中から使用する材料との適性を考慮して適宜選択した方法に従って成膜すればよい。
ゲート絶縁膜20を形成した後、ゲート電極22を形成する。ゲート電極22は高い導電性を有するものを用い、Al,Mo,Cr,Ta,Ti,Au,Au等の金属、Al−Nd、Ag合金、酸化錫、酸化亜鉛、酸化インジウム、酸化インジウム錫(ITO)、酸化亜鉛インジウム(IZO)、IGZO等の金属酸化物導電膜等を用いて形成することができる。ゲート電極22としてはこれらの導電膜を単層構造又は2層以上の積層構造として用いることができる。
ゲート電極22を形成するための金属膜の膜厚は、成膜性、エッチングやリフトオフ法によるパターンニング性、導電性等を考慮すると、10nm以上1000nm以下とすることが好ましく、50nm以上200nm以下とすることがより好ましい。
成膜後、エッチング又はリフトオフ法により所定の形状にパターンニングすることにより、ゲート電極22を形成してもよく、インクジェット法等により直接パターン形成してもよい。この際、ゲート電極22及びゲート配線(不図示)を同時にパターンニングすることが好ましい。
更に本発明により製造される薄膜トランジスタは、X線センサ、イメージセンサ等の各種センサ、MEMS(Micro Electro Mechanical System)等、種々の電子デバイスにおける駆動素子(駆動回路)として好適に用いられる。
本発明の一実施形態である液晶表示装置について、図5にその一部分の概略断面図を示し、図6に電気配線の概略構成図を示す。
本発明の一実施形態に係るアクティブマトリックス方式の有機EL表示装置について、図7に一部分の概略断面図を示し、図8に電気配線の概略構成図を示す。
本発明の一実施形態であるX線センサについて、図9にその一部分の概略断面図を示し、図10にその電気配線の概略構成図を示す。
X線変換層304はアモルファスセレンからなる層であり、TFT10およびキャパシタ310を覆うように設けられている。
上部電極306はX線変換層304上に設けられており、X線変換層304に接している。
以下のような評価用デバイスを作製し、評価を行った。
硝酸インジウム(In(NO3)3・xH2O、4N、高純度化学研究所社製)を2−メトキシエタノール(試薬特級、和光純薬工業社製)中に溶解させ、0.1mol/Lの濃度の硝酸インジウム溶液を作製した。
紫外線照射装置としては、低圧水銀ランプと塩化クリプトンを放電ガスに用いたエキシマランプを一つの処理室内に備えたものを用いた。試料は厚さ40mmのガラス板上にセットし、ランプ−試料間距離を15mmとした。試料位置での波長254nmの紫外照度は、低圧水銀ランプのみを点灯させた状態で紫外線光量計(オーク製作所社製、UV−M10、受光器UV−25)を用いて測定し、波長222nmの紫外照度は、エキシマランプのみを点灯させた状態で紫外線積算光量計(浜松ホトニクス製、C9536、センサヘッドH9535−222)を用いて測定し、ともに10mW/cm2であった。
紫外線照射処理室内に窒素を6L/minで10分間フローさせた後、90分間、低圧水銀ランプ及びエキシマランプを用いて紫外線照射を行った。
紫外線照射中は常に6L/minで窒素をフローさせた。紫外線照射処理時の基板温度をサーモラベルでモニターしたところ、150℃を示した。
実施例1と同様にして熱酸化膜付p型Si 1inch□基板上に金属酸化物半導体前駆体膜を作製した。
得られた金属酸化物半導体前駆体膜を、低圧水銀ランプのみを用いて紫外線照射処理を行ったこと以外は実施例1と同様にして金属酸化物半導体膜への転化を行った。試料位置での波長254nmの紫外照度は、10mW/cm2であった。
実施例1と同様にして熱酸化膜付p型Si 1inch□基板上に金属酸化物半導体前駆体膜を作製した。
得られた金属酸化物半導体前駆体膜を、エキシマランプのみを用いて紫外線照射処理を行ったこと以外は実施例1と同様にして金属酸化物半導体膜への転化を行った。試料位置での波長222nmの紫外照度は、10mW/cm2であった。
実施例1と同様にして熱酸化膜付p型Si 1inch□基板上に金属酸化物半導体前駆体膜を作製した。
得られた金属酸化物半導体前駆体膜に対し、紫外線照射を行わずに基板を150℃で90分間加熱して金属酸化物半導体膜への転化を行った。
実施例1と同様に作製した溶液及び基板を用い、以下のように簡易型のTFTを作製した。
熱酸化膜付p型Si 1inch□基板上に、硝酸インジウム溶液を5000rpmの回転速度で30秒スピンコートした後、60℃に加熱されたホットプレート上で1分間乾燥を行い、金属酸化物半導体前駆体膜を得た。
得られた金属酸化物半導体前駆体膜を、下記条件で紫外線照射処理を行うことで金属酸化物半導体膜への転化を行った。
紫外線照射装置としては、低圧水銀ランプと塩化クリプトンを放電ガスに用いたエキシマランプを一つの処理室内に備えたものを用いた。試料は厚さ40mmのガラス板上にセットし、ランプ-試料間距離を15mmとした。ランプ−試料間に金属グリッドを配置し、試料位置での波長254nm及び222nmの紫外照度を測定したところ、ともに8mW/cm2であった。
紫外線照射処理室内に窒素を6L/minで10分間フローさせた後、90分間、低圧水銀ランプ及びエキシマランプを用いて紫外線照射を行った。紫外線照射中は常に6L/minで窒素をフローさせた。紫外線照射処理時の基板温度をサーモラベルでモニターしたところ、150℃を示した。
Vg−Id特性の測定は、ドレイン電圧(Vd)を+1Vに固定し、ゲート電圧(Vg)を−15V〜+15Vの範囲内で変化させ、各ゲート電圧におけるドレイン電流(Id)を測定することにより行った。しかし、比較例4のTFTはトランジスタ動作が確認されなかった。
(膜密度)
上記実施例及び比較例で得られた金属酸化物半導体膜について、X線反射率測定(X−ray reflectometry:XRR)により膜密度を測定した。
膜密度の算出はXRR測定によって得られるXRRスペクトルから、膜厚、膜密度、表面ラフネスをパラメータとしてフィッティングを行うことによって行われる。実測スペクトルとシミュレーション結果が良い一致を示すか否かは信頼性因子(R値)で見積もることが出来、R値が0.015以下になるように各パラメータを決定する。尚、金属酸化物半導体膜を1層としたモデルによってR値が0.015以下とならない場合においては、金属酸化物半導体膜を2層以上としてフィッティングを行い、その際の膜密度は各層の膜密度を膜厚で乗じた値を加算した後に、金属酸化物半導体膜の全膜厚で除した値、即ち平均膜密度を膜密度として扱う。
実施例1及び比較例1〜4で形成した金属酸化物半導体膜の膜密度を表1に示す。
上記実施例1及び比較例1で得られた金属酸化物半導体膜をフォトリソグラフィーにて3×4mmにパターンニングした後、金属酸化物半導体膜上にソース・ドレイン電極を蒸着により成膜した。ソース・ドレイン電極はメタルマスクを用いたパターン成膜にて作製し、Ti電極を50nmの厚さに成膜した。ソース・ドレイン電極サイズは各々1mm□とし、電極間距離は0.2mmとした。
Vg−Id特性の測定は、ドレイン電圧(Vd)を+1Vに固定し、ゲート電圧(Vg)を−15V〜+15Vの範囲内で変化させ、各ゲート電圧におけるドレイン電流(Id)を測定することにより行った。
図11に実施例1及び比較例1のVg−Id特性を示す。また、実施例1及び比較例1のVg−Id特性から見積もった線形移動度を表2に示す。
尚、比較例2及び比較例3はトランジスタ動作が確認されなかった。
12 基板
14 活性層(酸化物半導体層)
16 ソース電極
18 ドレイン電極
20 ゲート絶縁膜
22 ゲート電極
100 液晶表示装置
200 有機EL表示装置
300 X線センサ
Claims (9)
- 金属硝酸塩を含む溶液を基板上に塗布し、塗布膜を乾燥させて金属酸化物前駆体膜を形成する工程と、
前記金属酸化物前駆体膜に対し、250nm以上300nm以下の波長域に照度が10mW/cm 2 以上のピーク成分を1つ以上含み、且つ200nm以上250nm未満の波長域に照度が10mW/cm 2 以上のピーク成分を1つ以上含む紫外線を照射することにより、前記金属酸化物前駆体膜を金属酸化物膜に転化する工程と、
を含む金属酸化物膜の製造方法。 - 前記金属酸化物前駆体膜を前記金属酸化物膜に転化する工程における前記基板の最高到達温度が200℃以下である請求項1に記載の金属酸化物膜の製造方法。
- 前記金属酸化物前駆体膜を前記金属酸化物膜に転化する工程における前記基板の最高到達温度が120℃以上である請求項1又は請求項2に記載の金属酸化物膜の製造方法。
- 前記金属硝酸塩を含む溶液が、少なくとも硝酸インジウムを含む請求項1〜請求項3のいずれか1項に記載の金属酸化物膜の製造方法。
- 前記硝酸インジウムを含む溶液が、亜鉛、錫、ガリウム及びアルミニウムから選ばれる少なくとも1つの金属原子を含む化合物をさらに含有する請求項4に記載の金属酸化物膜の製造方法。
- 前記金属酸化物前駆体膜に前記紫外線を照射する際に用いる光源が、低圧水銀ランプ及びエキシマランプから選ばれる少なくとも1種である請求項1〜請求項5のいずれか1項に記載の金属酸化物膜の製造方法。
- 前記金属酸化物前駆体膜を形成する工程において、前記金属硝酸塩を含む溶液を、インクジェット法、ディスペンサー法、凸版印刷法、及び凹版印刷法から選択される少なくとも1種の塗布法により塗布する請求項1〜請求項6のいずれか1項に記載の金属酸化物膜の製造方法。
- 前記金属酸化物膜が金属酸化物半導体膜である請求項1〜請求項7のいずれか1項に記載の金属酸化物膜の製造方法。
- 請求項1〜請求項7のいずれか1項に記載の製造方法で製造された金属酸化物膜を含む活性層と、ソース電極と、ドレイン電極と、ゲート絶縁膜と、ゲート電極とを形成する薄膜トランジスタの製造方法。