JP5553688B2 - 磁性薄膜の製造方法、磁性薄膜及び磁性体 - Google Patents
磁性薄膜の製造方法、磁性薄膜及び磁性体 Download PDFInfo
- Publication number
- JP5553688B2 JP5553688B2 JP2010143834A JP2010143834A JP5553688B2 JP 5553688 B2 JP5553688 B2 JP 5553688B2 JP 2010143834 A JP2010143834 A JP 2010143834A JP 2010143834 A JP2010143834 A JP 2010143834A JP 5553688 B2 JP5553688 B2 JP 5553688B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- thin film
- particles
- solution
- magnetic thin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
ことを特徴とするものである。
2 成膜対象
3 磁性薄膜
(1−1)磁性体の全体構成
図1において、1は、磁性フィルムや磁性基板等の磁性体の一例を示し、PET(ポリエチレンテレフタレート)フィルムや、ガラス基板等の透明な成膜対象2に磁性薄膜3が成膜された構成を有する。この第1の実施の形態における磁性体1は、磁性薄膜3が透明性及び絶縁性を有し、かつ永久磁石として機能するハードフェライト層であり、飽和磁化Msに対する残留磁化Mrの比を示す角形比Mr/Msが0.65以上であることを特徴とする。
(1−2−1)磁性材スラリーの構成
透明性及び絶縁性を有し、かつ永久磁石として機能する磁性薄膜3を形成できる磁性材としての磁性材スラリーは、一般式がε−Fe2O3で表される磁性酸化鉄系化合物を99重量%以上含む磁性粒子(以下、これをε−Fe2O3粒子と呼ぶ)が溶液中に分散するように含有されている。
ここで、例えばロッド形状の磁性粒子を活かした透明高硬度薄膜を得ることを目的とするならば、一般的には、その形状が長軸長100nm〜数百nmであるロッド状とすることが必要条件の一つに挙げられる。ここで、イプシロン型酸化鉄系化合物を99重量%以上含む磁性粒子は、カルシウムイオンによって外形が所定の長軸長(100nm以上)に形成され得るようになされており、この場合、ε−Fe2O3粒子であることが好ましい。
ここで、本発明による磁性材スラリーは、製造過程において、カルシウムイオン等の形状制御剤が添加されないと、磁性粒子の形状が球状に形成され得る。すなわち、磁性材スラリーの製造過程においてカルシウムイオンを添加しないときには、イプシロン型酸化鉄系化合物を99重量%以上含む磁性粒子の形状が球状に形成され、当該磁性粒子を溶液中に含有させることができる。そして、磁性材スラリー内に作製された球状の磁性粒子は、任意の方向に磁化容易軸を有する。
ここでFe3+イオンサイトの一部と置換された元素が1種類であるε−AxFe2−xO3粒子では、ε−Fe2O3の結晶構造を安定に保つため、Aとして、3価の元素を用いることが好ましい。さらにAとしては、Al,Sc,Ti,V,Cr,Ga,In,Yから選択される1種の元素を挙げることができる。
ここでイプシロン型酸化鉄系化合物からなる磁性粒子の形状としては特に限定はなく、例えばロッド状や球状を例示することができるが、イプシロン型酸化鉄系化合物からなる磁性粒子が外部磁場によって配向し易い球状又はロッド状であることが望ましい。なお、磁性材スラリーに含まれる溶媒としては、水溶性溶媒を用いることができる。さらに、必要に応じて添加剤を含んでもよい。
このように透明性及び絶縁性を有し、かつ永久磁石として機能する磁性薄膜を形成できる磁性材スラリーは、例えば、以下のように逆ミセル法及びゾルーゲル法を組み合わせて製造することができる。なお、100nm以下のシリカ被覆水酸化鉄系化合物粒子が合成できるのであれば、その合成方法は特に限定されない。
溶解させることにより、ε−Fe2O3と同じ結晶構造を有しながら、Fe3+イオンサイトの一部が置換されたε−AxFe2−xO3粒子の単相粒子を生成できる。なお、例えばAxとして硝酸アルミニウムを適量溶解させた場合には、イプシロン型酸化鉄系化合物を含有した球状のε−AlxFe2−xO3粒子を生成し得る。
次に、このようにして作製した磁性材スラリーに所定量の水を添加し、塗工液粘度を調整した塗工液を作製する。ここで、磁性材スラリーに含有される磁性粒子としては上述したように球状磁性粒子とロッド状磁性粒子とがある。そのうち球状磁性粒子を含有した磁性材スラリーを用いて作製された塗工液(以下、これを球状粒子含有塗工液と呼ぶ)では、塗工液粘度が所定値以上になると、角形比Mr/Msが下がるため、当該角形比Mr/Msが0.65以上となるように塗工液粘度が所定値以下に調整され得る。なお、ロッド状磁性粒子を含有した磁性材スラリーを用いて作製された塗工液(以下、これをロッド状粒子含有塗工液と呼ぶ)では、塗工液粘度を高くても、角形比Mr/Msが下がることなく、当該角形比Mr/Msが0.65以上となるため、特に塗工液粘度の調整は不要となる(「実施例」において後述する)。
以上の構成において、磁性薄膜3の製造に用いられる磁性材スラリーの製造方法では、ミセル溶液に硝酸鉄(III)を溶解させた原料溶液と、ミセル溶液に中和剤を添加した中和剤溶液とを混合することにより混合溶液を作製し、混合溶液内で水酸化鉄系化合物粒子の沈殿反応を進行させる。次いで、混合溶液内にシラン化合物を添加して水酸化鉄系化合物粒子の表面をシリカで被覆したシリカ被覆水酸化鉄系化合物粒子を生成する。次いで、シリカ被覆水酸化鉄系化合物粒子を混合溶液から分離した後、所定の温度で焼成することにより熱処理粉体を生成する。
この第2の実施の形態は、磁性薄膜3を形成する磁性材スラリーが上述した第1の実施の形態と異なるものであり、図3に示すように、第1の実施の形態による磁性材スラリーの製造工程に有しない、ドライプロセスを経由して作製される点(ステップSP15)のみが第1の実施の形態と相違する。この磁性材スラリーでは、製造過程においてドライプロセスを経由したことにより、第1の実施の形態の磁性材スラリーに比して分散性が劣り、磁性薄膜の透明性が劣るものとなる。
(3−1)外部磁場の影響について
ここでは、実施例として、球状のε−Al0.5Fe1.5O3粒子を5wt%含有した磁性材スラリーと、5wt%のPVA1000水溶液を重量比1:1で混合して溶液(球状粒子含有塗工液)を作製した。
ここでは、上述のようにして作製した球状粒子含有塗工液に一定の外部磁場を印加した後、球状粒子含有塗工液が固化する前に当該外部磁場の印加を停止させたときの磁化を測定した。その結果、図5のような測定結果が得られた。図5に示すように、外部磁場の印加を停止すると、約200s(最低単位)後には、既に磁化が消失していることを確認した。このことから、一旦、球状磁化粒子が磁化方向へ向きを揃えても、球状粒子含有塗工液が固化する前に外部磁場の印加を停止すると、整列していた球状磁性粒子の配向が乱れることが確認できた。
(3−3−1)球状のε−Al0.5Fe1.5O3粒子を含有した塗工液について
次に、塗工液粘度が異なる複数の球状粒子含有塗工液を作製した。そして、先ずは各球状粒子含有塗工液に5Tの外部磁場を印加したときの磁化Msを測定した。その後、各球状粒子含有塗工液に500 Oeの外部磁場を印加したときの磁化M500 Oe(上述ではMrとした)を測定し、各球状粒子含有塗工液の磁化Msに対する磁化M500 Oeの角形比M500 Oe/Msを算出して比較した。この結果は、図6に示すような測定結果が得られた。図6に示すように、塗工液粘度が約50cP以上に上がると、角形比M500 Oe/Msが下がることが分かった。これは塗工液粘度が上昇すると、外部との摩擦により球状磁性粒子自身の回転が起こらず、スピンの回転が起こったためと考えられる。従って、球状磁性粒子自体を磁化方向へ回転させ、規則的な配向を効率よく起こさせるためには、塗工液粘度を100cP以下に保つことが望ましいことが分かった。
次に、上述した原料溶液に形状制御剤としてカルシウムイオン(Ca2+/Fe3+=0.1mol/mol)を添加して、ε−Al0.5Fe1.5O3粒子を含有した磁性材スラリーを作製した。この磁性材スラリーを透過型電子顕微鏡(TEM)にて撮像したところ、図7に示すようなTEM像が得られた。このTEM像から磁性材スラリーは、ロッド状からなるε−Al0.5Fe1.5O3粒子10を含有していることが確認できた。
(3−4−1)球状のε−Al0.5Fe1.5O3粒子を含有した磁性材スラリーの作製
先ず始めに、球状粒子含有塗工液の作製に用いる磁性材スラリーを以下の製造工程により作製した。オクタン183mL、1-ブタノール36mL及び水60mLに、界面活性剤として臭化セチルトリメチルアンモニウム35.2gを溶解してミセル溶液を作製した後、このミセル溶液に硝酸鉄9水和物2.25gと、硝酸アルミニウム9水和物0.6966gとを溶解して原料溶液を作製した。
次に、10wt%のε−Al0.5Fe1.5O3水スラリーと、10wt%のPEG500000水溶液を重量比1:1で混合した。この溶液に水を加え、溶液粘度が56cPになったところで水の添加を終了し、これを塗工液とした。この塗工液を成膜対象としてのPETフィルム上にバーコーティングした後、直ちに外部磁場が2Tの超伝導マグネット内で約30min間、室温で乾燥させて磁性薄膜を作製した。
次に、10wt%のε−Al0.5Fe1.5O3水スラリーと、10wt%のPEG500000水溶液を重量比1:1で混合した。この溶液に水を加え、溶液粘度が99cPになったところで水の添加を終了し、これを塗工液とした。この塗工液をPETフィルム上にバーコーティングした後、直ちに外部磁場が2Tの超伝導マグネット内で30min間、室温で乾燥させて磁性薄膜を作製した。
次に、10wt%のε−Al0.5Fe1.5O3水スラリーと、10wt%のPEG500000水溶液を重量比1:1で混合した。この溶液に水を加え、溶液粘度が164cPになったところで水の添加を終了し、これを塗工液とした。この塗工液をPETフィルム上にバーコーティングした後、直ちに外部磁場が2Tの超伝導マグネット内で約30min間、室温で乾燥させて磁性薄膜を作製した。
次に、10wt%のε−Al0.5Fe1.5O3水スラリーと、10wt%のPEG500000水溶液を重量比1:1で混合した。この溶液に水を加え、溶液粘度が56cPになったところで水の添加を終了し、これを塗工液とした。この塗工液をPETフィルム上にバーコーティングした後、外部磁場を印加せずに、約30min間、室温で乾燥させて磁性薄膜を作製した。
次に、10wt%のε−Al0.5Fe1.5O3水スラリーと、10wt%のPEG500000水溶液を重量比1:1で混合した。この溶液に水を加え、溶液粘度が56cPになったところで水の添加を終了し、これを塗工液とした。この塗工液をPETフィルム上にバーコーティングした後、直ちに外部磁場が1Tの超伝導マグネット内において約30min間、室温で乾燥させて磁性薄膜を作製した。
次に、10wt%のε−Al0.5Fe1.5O3水スラリーと、10wt%のPEG500000水溶液を重量比1:1で混合した。この溶液に水を加え、溶液粘度が56cPになったところで水の添加を終了し、これを塗工液とした。この塗工液をPETフィルム上にバーコーティングした後、直ちに外部磁化が2Tの超伝導マグネット内において約1min間、室温で処理した後、このサンプルを超伝導マグネットから取り出し、そのまま室温で約30min間、乾燥させて磁性薄膜を作製した。
次に、球状のε−Al0.5Fe1.5O3粒子を含有した第1の塗工液と、アスペクト比が異なる3種類のロッド状のε−Fe2O3粒子をそれぞれ含有した第2〜第4の塗工液とを作製した。先ず始めにこれら第1〜第4の塗工液について具体的に説明し、次にこれら第1〜第4の塗工液の磁気特性について説明する。
具体的に第1の塗工液は上述した「(4−1)球状のε−Al0.5Fe1.5O3粒子を含有した磁性材スラリーの作製」に基づいてε−Al0.42Fe1.58O3水スラリーを作製した後、所定量のε−Al0.5Fe1.5O3スラリー水スラリーと、所定量のPEG500000水溶液を所定の重量比で混合した。この溶液に水を加え、塗工液粘度が170cPになったところで水の添加を終了し、これを第1の塗工液とした。
次に、第2の塗工液の製造方法について以下説明する。先ず始めに磁性材スラリーを作製するために、オクタン183mL、1−ブタノール36mL及び水60mLに、界面活性剤として臭化セチルトリメチルアンモニウム35.2gを溶解してミセル溶液を作製した後、硝酸鉄9水和物2.25gと硝酸アルミニウム9水和物0.70gをミセル溶液に溶解すると共に、形状制御剤として硝酸カルシウム4水和物0.176g(Ca2+/(Fe3++Al3+)=0.1)をミセル溶液に溶解して原料溶液を作製した。
第3の塗工液は、硝酸鉄9水和物1.95gと硝酸アルミニウム9水和物0.98gをミセル溶液に溶解すると共に形状制御剤として硝酸カルシウム0.358g(Ca2+/(Fe3++Al3+)=0.2)をミセル溶液に溶解して原料溶液を作製し、この原料溶液を用いて上述した第2の塗工液と同じ作製方法で作製した。
第4の塗工液は、硝酸鉄9水和物3gをミセル溶液に溶解すると共に形状制御剤として硝酸バリウム0.398g(Ba2+/Fe3+=0.2)をミセル溶液に溶解して原料溶液を作製し、この原料溶液を用いて上述した第2の塗工液と同じ作製方法で第4の塗工液を作製した。
このようにして作製した第1〜第4の塗工液について、それぞれ磁気特性を調べた。具体的には、第1〜第4の塗工液に対して約0〜50000 Oeまで外部磁場を印加してゆき、次いで外部磁場を減少させていったときの磁化M emu g−1を測定した。その結果、図10に示すような結果が得られた。
次に、アスペクト比が1.1の球状のε−Al0.5Fe1.5O3粒子21を含有した第1の塗工液の粘度を約5cPに調整し、次いでこの第1の塗工液をPETフィルムに塗布した後、約2T以上の外部磁場を印加しながら第1の塗工液を固化させた配向フィルム(以下、これを球状粒子配向フィルムと呼ぶ)を製造した。これによりPETフィルムには、球状のε−Al0.5Fe1.5O3粒子21を外部磁場によって規則的に磁化方向へ配向させた磁性薄膜が成膜された。
(4−1)磁性薄膜の構成
図14において、31は第3の実施の形態による磁性薄膜を示し、この磁性薄膜31は、イプシロン型酸化鉄系化合物(すなわち、ε−Fe2O3、ε−AxFe2−xO3及びε−ByCzFe2−y−zO3のうちいずれか)を99重量%以上含む磁性粒子を含有した磁性材スラリーから形成されており、絶縁性を有し、かつ永久磁石として機能するハードフェライト層であり、飽和磁化Msに対する残留磁化Mrの比を示す角形比Mr/Msが0.65以上の構成を有する。
次に、この磁性薄膜31の製造方法について、以下、説明する。この場合、先ず初めに、イプシロン型酸化鉄系化合物(すなわち、ε−Fe2O3、ε−AxFe2−xO3及びε−ByCzFe2−y−zO3のうちいずれか)を99重量%以上含む磁性粒子を含有した磁性材スラリーを製造する。この磁性材スラリーは、上述したドライプロセスを経由しない「(1−2−6)磁性材スラリーの製造方法」に従って製造されるか、或いは上述した「(2)第2の実施の形態」における図3に示すように、ドライプロセスを経由して製造され得る。
ここでは、先ず初めに、塗工液を固化する際に外部磁場を印加することなく作製された磁性薄膜が、電磁波吸収能を有しているか否かについて検証した。検証対象として、ε−Ga0.51Fe1.49O3からなり、ポリビニルアルコールをバインダーとした磁性薄膜を製造した。具体的には、ε−Ga0.51Fe1.49O3からなる磁性材スラリー(ε−Ga0.51Fe1.49O3が18.5重量部)と、PVA(ポリビニルアルコール)1000水溶液(完全けん化型 ポリビニルアルコールが10重量部)とを用意した。次いで、これら磁性材スラリーとPVA1000水溶液との固形分の重量比が4:1の割合になるように、磁性材スラリーとPVA1000水溶液を混合し、塗工液を作製した。
Claims (14)
- 絶縁性を有すると共に、永久磁石として機能するイプシロン型酸化鉄系化合物からなる磁性粒子を含有し、前記磁性粒子の透過型電子顕微鏡観察による観察平均粒径に対する動的光散乱法による平均粒径の比が5以下である磁性材スラリーから作製される塗工液を、成膜対象に塗布する塗布工程と、
前記成膜対象に塗布した前記塗工液に対して所定強さの外部磁場を印加した状態で、前記塗工液を固化させて磁性薄膜を形成する形成工程と
を備えることを特徴とする磁性薄膜の製造方法。 - 前記磁性粒子が球状又はロッド状からなる
ことを特徴とする請求項1記載の磁性薄膜の製造方法。 - 前記磁性粒子は球状からなり、
前記塗布工程は、前記溶液粘度が約50cP以下である塗工液を用いる
ことを特徴とする請求項1記載の磁性薄膜の製造方法。 - 前記形成工程は、前記外部磁場の強さが約2T以上である
ことを特徴とする請求項1〜3のうちいずれか1項記載の磁性薄膜の製造方法。 - 前記塗布工程に用いられる前記塗工液は、
前記イプシロン型酸化鉄系化合物を99重量%以上含む磁性粒子が溶液中に分散するように含有されている
ことを特徴とする請求項1〜4のうちいずれか1項記載の磁性薄膜の製造方法。 - 前記イプシロン型酸化鉄系化合物は、ε−Fe2O3、ε−AxFe2−xO3(但し、AはFeを除く元素、0<x<2)及びε−ByCzFe2−y−zO3(但し、B及びCは、A及びFeを除く元素であり、かつ互いに異なる元素、0<y<1、0<z<1)のうち少なくともいずれか1種からなる
ことを特徴とする請求項1〜5のうちいずれか1項記載の磁性薄膜の製造方法。 - 前記塗工液には水溶性高分子又は水分散性高分子が混合されている
ことを特徴とする請求項1〜6のうちいずれか1項記載の磁性薄膜の製造方法。 - 絶縁性を有すると共に、永久磁石として機能するイプシロン型酸化鉄系化合物からなり、透過型電子顕微鏡観察による観察平均粒径に対する動的光散乱法による平均粒径の比が5以下である磁性粒子を含有し、
薄膜形成時に印加された外部磁場に合わせて前記磁性粒子が所定方向に配向されている
ことを特徴とする磁性薄膜。 - 前記磁性粒子が球状又はロッド状からなる
ことを特徴とする請求項8記載の磁性薄膜。 - 前記イプシロン型酸化鉄系化合物を99重量%以上含む磁性粒子が分散するように配置され、10μmまでの膜厚範囲で形成した場合のヘイズが40%以下である
ことを特徴とする請求項8又は9記載の磁性薄膜。 - 前記イプシロン型酸化鉄系化合物は、ε−Fe2O3、ε−AxFe2−xO3(但し、AはFeを除く元素、0<x<2)及びε−ByCzFe2−y−zO3(但し、B及びCは、A及びFeを除く元素であり、かつ互いに異なる元素、0<y<1、0<z<1)のうち少なくともいずれか1種からなる
ことを特徴とする請求項8〜10のうちいずれか1項記載の磁性薄膜。 - 所定領域の磁性粒子は前記所定方向へ配向され、前記所定領域と異なる他領域の磁性粒子は前記所定方向と異なる他方向へ配向されている
ことを特徴とする請求項8〜11のうちいずれか1項記載の磁性薄膜。 - 30〜300GHzのミリ波領域の電磁波を吸収する
ことを特徴とする請求項8〜12のうちいずれか1項記載の磁性薄膜。 - 請求項8〜13のうちいずれか1項記載の前記磁性薄膜を成膜対象に備える
ことを特徴とする磁性体。