JP5442114B2 - 銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料 - Google Patents

銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料 Download PDF

Info

Publication number
JP5442114B2
JP5442114B2 JP2012514341A JP2012514341A JP5442114B2 JP 5442114 B2 JP5442114 B2 JP 5442114B2 JP 2012514341 A JP2012514341 A JP 2012514341A JP 2012514341 A JP2012514341 A JP 2012514341A JP 5442114 B2 JP5442114 B2 JP 5442114B2
Authority
JP
Japan
Prior art keywords
reduction
copper
ceramic
temperature
sintered
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2012514341A
Other languages
English (en)
Other versions
JP2012529412A (ja
Inventor
宋▲べい▼▲べい▼
宋永生
莫方策
李娟�
王孝国
郭精華
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Fenghua Advanced Tech Holding Co Ltd
Original Assignee
Guangdong Fenghua Advanced Tech Holding Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Fenghua Advanced Tech Holding Co Ltd filed Critical Guangdong Fenghua Advanced Tech Holding Co Ltd
Publication of JP2012529412A publication Critical patent/JP2012529412A/ja
Application granted granted Critical
Publication of JP5442114B2 publication Critical patent/JP5442114B2/ja
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

発明の詳細な説明
〔技術分野〕
本発明は、セラミック媒体材料及びそれによって得られたコンポーネントの製備方法に係り、特にＣＯＧ特性を満足し、且つ銅内電極と整合できる１つの高周波低温において焼結されたセラミック媒体材料に係る。
〔背景技術〕
製品の高性能、低コストという市場ニーズにつれて、セラミックコンデンサのメーカーが生産コストを下げることもでき、より高い性能要求も満足できる代替材料を絶えず捜し求めなければならないことは、かれたちが面する重大な挑戦の１つである。現在の積層セラミックコンデンサ（以下、ＭＬＣＣと称する）は既に基本的にベースメタル化が実現され、８０％以上のＭＬＣＣがベースメタル内電極材料（ニッケルを主とする）によってパラジウム銀を取って代わり、略４０％の生産コストを有効に下げることができる。更なる研究として、銅電極の使用が検討し始められ、その他のベースメタルに対して、銅は価格上の優勢を有するのみでなく、より重要なのは高周波分野において、銅の電気性能がより優秀であることもある。しかし、銅はニッケルと比べると、より酸化しやすく、且つ銅の融点（１０８３℃）がニッケルの融点（１４５３℃）より低く、また、当面の汎用セラミックスの焼結温度が非常に高くて、銅電極と整合されにくいため、ＭＬＣＣの電気性能に影響する。もし銅を内電極の材料として使用すれば、まず要求を満足するセラミック媒体材料を必然的に獲得しなければならない。
〔発明の開示〕
本発明の解決しようとする技術問題は、ＣＯＧセラミック媒体の特性を満足し、材料の分散性が高く、成型プロセスが良く、ＲｏＳＨ条例の要求を満足する１つの銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料を提供することである。
上記技術問題を解決するために、本発明の提供する技術手段は下記の通りである。銅内電極と整合する１種の耐還元性高周波低温焼結セラミック媒体材料であって、主結晶相と、改質添加剤と、焼結フラックスとから組成され、主結晶相の構造式がＭｇｘＢａ（１−ｘ）ＺｒｙＳｉ（１−ｙ）Ｏ３で、そのうち、０．８≦ｘ≦０．９５、０．０５≦ｙ≦０．２で、前記改質添加剤がＭｎＯ２、ＣａＯ、Ｌｉ２Ｏ、Ｂｉ２Ｏ３、ＴｉＯ２のうちの１種または複数種で、前記焼結フラックスがＢ２Ｏ３、ＳｉＯ２、ＺｎＯ、ＣｕＯ、Ｋ２Ｏ、ＢａＯのうちの１種または複数種である。
さらに、上記銅内電極と整合する耐還元性高周波セラミック媒体材料は、モル百分率で、主結晶相が８０〜９５ｍｏｌ％で、改質添加剤が１．２〜１０ｍｏｌ％で、焼結フラックスが２．５〜１８ｍｏｌ％で、モル百分率で、改質添加剤が銅内電極と整合する耐還元性高周波セラミック媒体材料全体における組成は、ＭｎＯ２が０．２〜０．５ｍｏｌ％、ＣａＯが０〜１．０ｍｏｌ％、Ｌｉ２Ｏが１．０〜３．０ｍｏｌ％、Ｂｉ２Ｏ３が０〜５．０ｍｏｌ％、ＴｉＯ２が０〜１．０ｍｏｌ％で、モル百分率で、前記焼結フラックスが銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料全体における組成は、Ｂ２Ｏ３が１．０〜３．０ｍｏｌ％、ＳｉＯ２が０〜６．０ｍｏｌ％、ＺｎＯが１．５〜６．０ｍｏｌ％、ＣｕＯが０〜１．０ｍｏｌ％、Ｋ２Ｏが０〜１．０ｍｏｌ％、ＢａＯが０〜１．０ｍｏｌ％で、前記主結晶相をＭｇ（ＯＨ）２、ＳｉＯ２、ＢａＣＯ３及びＺｒＯ２でボールミル混合した後、１０５０℃〜１１７０℃の温度において予備焙焼することによって作製されることが特徴である。
上記組成において、主成分は良好な高周波性能を有する複合物であるＭｇｘＢａ（１−ｘ）ＺｒｙＳｉ（１−ｙ）Ｏ３を選択し、該複合物が比較的に低い誘電率、比較的に低い媒体損失係数値、及び直線性に近い誘電‐温度特性を有し、これらはすべて主材料から本発明の材料によって作製されたＭＬＣＣが優良な電気性能を有することを保証できる。改質添加剤材料の加入は、材料の誘電率を約１０に維持させることを保証でき、且つセラミック媒体材料の温度係数を非常に良く調節されるため、誘電‐温度特性が直線性に近いようにさせると共に、さらにセラミック体結晶粒の異常な生成を抑制することができ、結晶粒の生成を均一にさせて、これは媒体材料の耐圧強度向上に対し非常に良い役割を果たし、且つ最終的に本発明において獲得されたＭＬＣＣが高い信頼性を有するようにさせる。焼結フラックスの主な役割の１つは、本発明のセラミック材料の焼結温度を下げて、材料が１１００℃以下の温度において緻密な焼結を行い、焼結後のセラミック体結晶粒の生成が均一で高い緻密度を有するようにさせて、さらに作製されたＭＬＣＣが高い信頼性を有することを保証することである。本発明は、還元雰囲気において焼結されたＭｇｘＢａ（１−ｘ）ＺｒｙＳｉ（１−ｙ）Ｏ３体系の非強誘電性銅電極媒体セラミックスを採用しており、焼結温度が１１００℃より低く、セラミック材料が銅（Ｃｕ）内電極スラリー材料と整合でき、セラミック材料の性能が優越である。
上記高周波低温焼結セラミック媒体材料によってＭＬＣＣを製備する方法において、慣用セラミック材料生産プロセスフローによりＭＬＣＣセラミック材料を作製することは、セラミックスラリーの製備と、媒体ダイヤフラムの作製と、内電極及び媒体層の交替重畳印刷と、母材の乾燥と、積層と、切断と、バインダ除去と、焼結と、面取りと、エンドキャッピングと、エンドケーキングとのプロセスを含む。すなわち、シート式ＭＬＣＣの作製フローにより有機接着剤やエチルアルコールなどの溶剤を加入し、これによってスラリー材料を形成し、スラリー材料を流延してダイヤフラムに作製し、ダイヤフラムに銅Ｃｕ内電極を印刷し、所要層数を交替で積層し、母材ＭＬＣＣチップを形成し、その後、有機接着剤と溶剤を排除するように、２００〜３００℃の温度において母材ＭＬＣＣチップを熱処理し、１０００〜１１００℃の温度においてＭＬＣＣチップを２．５〜５時間焼結し、その後、表面処理を経て、外部電極を内部電極と連結させるように、さらにチップの両端に１対の外部銅Ｃｕ電極をキャップし、８３０〜９００℃の温度範囲内において外電極を熱処理し、さらに電気めっき処理などのプロセスを経て、ＭＬＣＣ製品を得ることができる。該製備方法において、製品の焼結温度が低く、プロセス設備に対する要求が簡単で、セラミック媒体材料の粒度分布が均一で、焼結中においてセラミック体結晶粒の生成が均一、緻密で、ＭＬＣＣ製品の電気性能が優良である。
〔発明を実施するための形態〕
本発明の主旨は下記の通りである。ＭｇｘＢａ（１−ｘ）ＺｒｙＳｉ（１−ｙ）Ｏ３体系を材料の主結晶相として採用し、性能を調節するように改質添加剤を加入し、且つ焼結温度の降下を助けるため焼結フラックスを加入し、慣用のプロセスを採用して所要粉体に作製し、ＣＯＧセラミック媒体の特性を満足し、材料の分散性が高く、成型プロセスが良い低温焼結セラミック媒体材料を得、且つＭＬＣＣ製品を作製するときに、焼結温度が低く、結晶粒の生成が均一、緻密で、製品に欠陥を有せず、または欠陥が小さい。次に実施例と合わせて本発明の内容に対しさらに詳しい説明を行い、実施例において言及する内容は本発明に対する限定でなく、材料の配合についての選択は、地元の条件により結果に対し実質上影響を与えないように適当な措置を取ることができる。
まず、本発明の材料の配合の一般的な提案を下記の通り簡単に記述する。銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料であって、主結晶相と、改質添加剤と、焼結フラックスとから組成され、主結晶相の構造式がＭｇｘＢａ（１−ｘ）ＺｒｙＳｉ（１−ｙ）Ｏ３で、そのうち、０．８≦ｘ≦０．９５、０．０５≦ｙ≦０．２で、前記改質添加剤がＭｎＯ２、ＣａＯ、Ｌｉ２Ｏ、Ｂｉ２Ｏ３、ＴｉＯ２のうちの１種または複数種で、前記焼結フラックスがＢ２Ｏ３、ＳｉＯ２、ＺｎＯ、ＣｕＯ、Ｋ２Ｏ、ＢａＯのうちの１種または複数種である。
〔実施例１〕
銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料であって、純度が９９．５％以上の原材料を採用し、０．８ｍｏｌのＭｇ（ＯＨ）２、０．８ｍｏｌのＳｉＯ２、０．２ｍｏｌのＢａＣＯ３及び０．２ｍｏｌのＺｒＯ２という混合比率により、均一にボールミルし、１１５０℃の温度において該混合物を３時間焙焼してから、主結晶相がＭｇ０．８Ｂａ０．２Ｓｉ０．８Ｚｒ０．２Ｏ３である材料を得る。その後、所定比率により表１に示す改質添加剤と焼結フラックスを添加する。
Figure 0005442114
当業者常用のセラミック材料生産プロセスフローによりセラミック媒体材料を作製し、その後、常用のＭＬＣＣの作製フローにより有機接着剤とエチルアルコールなどの溶剤を加入し、これによってスラリー材料を形成し、スラリー材料を流延してダイヤフラムに作製し、ダイヤフラムに銅Ｃｕ内電極を印刷し、所要層数を交替で積層し、母材ＭＬＣＣチップを形成し、その後、有機接着剤と溶剤を排除するように、２００〜３００℃の温度において母材ＭＬＣＣチップを熱処理する。１０００〜１１００℃の温度においてＭＬＣＣチップを２．５〜５時間焼結し、表面バフ研磨処理を経て、外部電極を内部電極と連結させるように、さらにチップの両端に１対の外部銅Ｃｕ電極をキャップし、８３０〜９００℃の温度範囲内において外電極を熱処理する。さらに電気めっき処理などのプロセスを経て、ＭＬＣＣ製品を得ることができる。該ＭＬＣＣ製品は、容量が安定で、性能が良いなどの特徴を有する。室温２５℃のときに、ＨＰ４２７８電気ブリッジを利用して、１ＭＨｚ、１．０Ｖ（ＡＣ）において本ＭＬＣＣ製品の容量、損失を試験し、ＳＦ２５１２快速絶縁機を利用して、１００ＶのＤＣ定格電圧を１０秒印加し、絶縁電気抵抗を試験し、高低温チャンバを利用して、−５５〜＋１２５℃の間において、誘電率‐温度係数を試験し、ＨＰ４９９１Ａを利用して本ＭＬＣＣ製品の周波数特性などを試験し、製品性能試験パラメータは、表２に示される１〜１０号材料の配合と対応するＭＬＣＣ試験パラメータである。
Figure 0005442114
〔実施例２〕
銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料であって、純度が９９．５％以上の原材料を採用し、０．９ｍｏｌのＭｇ（ＯＨ）２、０．９ｍｏｌのＳｉＯ２、０．１ｍｏｌのＢａＣＯ３及び０．１ｍｏｌのＺｒＯ２という混合比率により、均一にボールミルし、１１５０℃の温度において該混合物を３時間焙焼してから、主結晶相がＭｇ０．９Ｂａ０．１Ｓｉ０．９Ｚｒ０．１Ｏ３である材料を得る。その後、所定比率により表３に示す改質添加剤と焼結フラックスを添加する。
Figure 0005442114
実施例１の方法によりＭＬＣＣの電気性能を製造、試験し、試験結果が表４に示される。
Figure 0005442114
〔実施例３〕
銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料であって、純度が９９．５％以上の原材料を採用し、０．９５ｍｏｌのＭｇ（ＯＨ）２、０．９５ｍｏｌのＳｉＯ２、０．０５ｍｏｌのＢａＣＯ３及び０．０５ｍｏｌのＺｒＯ２という混合比率により、均一にボールミルし、１１５０℃の温度において該混合物を３時間焙焼してから、主結晶相がＭｇ０．９５Ｂａ０．０５Ｓｉ０．９５Ｚｒ０．０５Ｏ３である材料を得る。その後、所定比率により表５に示す改質添加剤と焼結フラックスを添加する。
Figure 0005442114
実施例１の方法によりＭＬＣＣの電気性能を製造、試験し、試験結果が表６に示される。
Figure 0005442114

Claims (5)

  1. 主結晶相と、改質添加剤と、焼結フラックスとから組成される銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料において、
    主結晶相の構造式がＭｇｘＢａ（１−ｘ）ＺｒｙＳｉ（１−ｙ）Ｏ３で、そのうち、０．８≦ｘ≦０．９５、０．０５≦ｙ≦０．２で、前記改質添加剤がＭｎＯ２、ＣａＯ、Ｌｉ２Ｏ、Ｂｉ２Ｏ３、ＴｉＯ２のうちの１種または複数種で、前記焼結フラックスがＢ２Ｏ３、ＳｉＯ２、ＺｎＯ、ＣｕＯ、Ｋ２Ｏ、ＢａＯのうちの１種または複数種であり、
    モル百分率で、主結晶相が８０〜９５ｍｏｌ％で、改質添加剤が１．２〜１０ｍｏｌ％で、焼結フラックスが２．５〜１８ｍｏｌ％である、ことを特徴とする銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料。
  2. 前記主結晶相がＭｇｘＢａ（１−ｘ）ＺｒｙＳｉ（１−ｙ）Ｏ３で、そのうち、０．８≦ｘ≦０．９５、０．０５≦ｙ≦０．２で、比率によりＭｇ（ＯＨ）２、ＢａＣＯ３、ＺｒＯ２、ＳｉＯ２で均一にボールミル混合した後、１０５０℃〜１１７０℃の温度において予備焙焼することによって作製される、ことを特徴とする請求項１に記載の銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料。
  3. モル百分率で、改質添加剤が銅内電極と整合する耐還元性高周波セラミック媒体材料全体における組成は、ＭｎＯ２が０．２〜０．５ｍｏｌ％、ＣａＯが０〜１．０ｍｏｌ％、Ｌｉ２Ｏが１．０〜３．０ｍｏｌ％、Ｂｉ２Ｏ３が０〜５．０ｍｏｌ％、ＴｉＯ２が０〜１．０ｍｏｌ％である、ことを特徴とする請求項１に記載の銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料。
  4. モル百分率で、前記焼結フラックスが銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料全体における組成は、Ｂ２Ｏ３が１．０〜３．０ｍｏｌ％、ＳｉＯ２が０〜６．０ｍｏｌ％、ＺｎＯが１．５〜６．０ｍｏｌ％、ＣｕＯが０〜１．０ｍｏｌ％、Ｋ２Ｏが０〜１．０ｍｏｌ％、ＢａＯが０〜１．０ｍｏｌ％である、ことを特徴とする請求項１に記載の銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料。
  5. 該セラミック媒体材料によって作製されたセラミックコンデンサは還元雰囲気において焼結されることができ、セラミックコンデンサ内電極材料が銅を使用することができ、焼結温度が１０００〜１１００℃で、獲得したセラミックコンデンサの電気性能が高周波ＣＯＧ類セラミック材料の特性を満足することができる、ことを特徴とする請求項１〜４に記載の銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料。
JP2012514341A 2009-12-22 2010-12-20 銅内電極と整合する耐還元性高周波低温焼結セラミック媒体材料 Active JP5442114B2 (ja)