JP5342902B2 - 溶接熱影響部の靭性および母材疲労特性に優れた鋼材およびその製造方法 - Google Patents

溶接熱影響部の靭性および母材疲労特性に優れた鋼材およびその製造方法 Download PDF

Info

Publication number
JP5342902B2
JP5342902B2 JP2009058630A JP2009058630A JP5342902B2 JP 5342902 B2 JP5342902 B2 JP 5342902B2 JP 2009058630 A JP2009058630 A JP 2009058630A JP 2009058630 A JP2009058630 A JP 2009058630A JP 5342902 B2 JP5342902 B2 JP 5342902B2
Authority
JP
Japan
Prior art keywords
less
steel material
steel
oxide
rem
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2009058630A
Other languages
English (en)
Japanese (ja)
Other versions
JP2010209433A (ja
Inventor
雅人 金子
哲史 出浦
朋子 杉村
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kobe Steel Ltd
Original Assignee
Kobe Steel Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kobe Steel Ltd filed Critical Kobe Steel Ltd
Priority to JP2009058630A priority Critical patent/JP5342902B2/ja
Priority to CN2010101167954A priority patent/CN101831588B/zh
Priority to KR1020100021272A priority patent/KR101197872B1/ko
Publication of JP2010209433A publication Critical patent/JP2010209433A/ja
Application granted granted Critical
Publication of JP5342902B2 publication Critical patent/JP5342902B2/ja
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Steel (AREA)
  • Treatment Of Steel In Its Molten State (AREA)
JP2009058630A 2009-03-11 2009-03-11 溶接熱影響部の靭性および母材疲労特性に優れた鋼材およびその製造方法 Expired - Fee Related JP5342902B2 (ja)

Priority Applications (3)

Application Number Priority Date Filing Date Title
JP2009058630A JP5342902B2 (ja) 2009-03-11 2009-03-11 溶接熱影響部の靭性および母材疲労特性に優れた鋼材およびその製造方法
CN2010101167954A CN101831588B (zh) 2009-03-11 2010-02-09 焊接热影响部的韧性和母材疲劳特性优异的钢材及其制造方法
KR1020100021272A KR101197872B1 (ko) 2009-03-11 2010-03-10 용접열 영향부의 인성 및 모재 피로 특성이 우수한 강재 및 그의 제조방법

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP2009058630A JP5342902B2 (ja) 2009-03-11 2009-03-11 溶接熱影響部の靭性および母材疲労特性に優れた鋼材およびその製造方法

Publications (2)

Publication Number Publication Date
JP2010209433A JP2010209433A (ja) 2010-09-24
JP5342902B2 true JP5342902B2 (ja) 2013-11-13

Family

ID=42715807

Family Applications (1)

Application Number Title Priority Date Filing Date
JP2009058630A Expired - Fee Related JP5342902B2 (ja) 2009-03-11 2009-03-11 溶接熱影響部の靭性および母材疲労特性に優れた鋼材およびその製造方法

Country Status (3)

Country Link
JP (1) JP5342902B2 (zh)
KR (1) KR101197872B1 (zh)
CN (1) CN101831588B (zh)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3282028A4 (en) * 2015-04-10 2018-11-07 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Steel sheet for high strength line pipe with excellent low temperature toughness and steel pipe for high strength line pipe

Families Citing this family (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5451591B2 (ja) * 2010-12-27 2014-03-26 株式会社神戸製鋼所 二次精錬方法
JP5651090B2 (ja) * 2011-01-18 2015-01-07 株式会社神戸製鋼所 溶接熱影響部の靱性に優れた鋼材およびその製造方法
TWI507538B (zh) 2011-09-30 2015-11-11 Nippon Steel & Sumitomo Metal Corp With excellent burn the attachment strength of the hardenable galvannealed steel sheet, a high strength galvannealed steel sheet and manufacturing method, etc.
JP5780171B2 (ja) * 2012-02-09 2015-09-16 新日鐵住金株式会社 曲げ性に優れた高強度冷延鋼板、高強度亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板とその製造方法
JP5949682B2 (ja) * 2012-07-03 2016-07-13 Ｊｆｅスチール株式会社 脆性亀裂伝播停止特性に優れた大入熱溶接用鋼板の製造方法
JP5958428B2 (ja) * 2012-07-30 2016-08-02 Ｊｆｅスチール株式会社 大入熱溶接用鋼板の製造方法
JP6226542B2 (ja) * 2013-03-22 2017-11-08 株式会社神戸製鋼所 溶接熱影響部の靭性に優れた鋼材
JP5598617B1 (ja) * 2013-03-26 2014-10-01 Ｊｆｅスチール株式会社 脆性亀裂伝播停止特性に優れた大入熱溶接用高強度厚鋼板およびその製造方法
CN105452506B (zh) * 2013-08-16 2018-11-09 新日铁住金株式会社 焊接区质量优异的电焊钢管及其制造方法
JP6228491B2 (ja) * 2013-08-26 2017-11-08 株式会社神戸製鋼所 疲労特性に優れた厚鋼板およびその製造方法
JP6064896B2 (ja) * 2013-12-27 2017-01-25 Ｊｆｅスチール株式会社 耐疲労き裂伝ぱ特性に優れた鋼材およびその製造方法並びに耐疲労き裂伝ぱ特性に優れた鋼材の判定方法
CN103954487B (zh) * 2014-04-28 2016-08-31 浙江大学 用于透射电镜的原位拉伸试样的制备方法
CN104120366B (zh) * 2014-06-21 2016-06-29 首钢总公司 一种压力容器用调质高强度钢板及其生产方法
WO2017094593A1 (ja) * 2015-12-04 2017-06-08 株式会社神戸製鋼所 溶接熱影響部の低温靭性劣化および溶接熱影響部の硬さを抑制した高降伏強度を有する非調質鋼板
JP6245417B1 (ja) * 2016-04-19 2017-12-13 新日鐵住金株式会社 鋼材
KR101908818B1 (ko) * 2016-12-23 2018-10-16 주식회사 포스코 저온에서의 파괴 개시 및 전파 저항성이 우수한 고강도 강재 및 그 제조방법
MX2021006649A (es) * 2018-12-11 2021-07-15 Nippon Steel Corp Lamina de acero de alta resistencia que tiene excelente moldeabilidad y resistencia al impacto, y metodo para fabricar lamina de acero de alta resistencia que tiene excelente moldeabilidad y resistencia al impacto.
WO2020262638A1 (ja) * 2019-06-27 2020-12-30 日本製鉄株式会社 鋼材及びその製造方法
CN111304404B (zh) * 2020-03-31 2021-10-22 鞍钢股份有限公司 一种用于真空感应炉氧化物冶金的包芯线及使用方法
CN114480966A (zh) * 2021-12-30 2022-05-13 南阳汉冶特钢有限公司 一种适于大线能量焊接的海洋工程用钢板eh40及其生产方法

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003213366A (ja) 2002-01-24 2003-07-30 Nippon Steel Corp 母材および大小入熱溶接熱影響部の靭性に優れた鋼材
JP4825057B2 (ja) * 2005-09-12 2011-11-30 株式会社神戸製鋼所 溶接熱影響部の靭性に優れた鋼材およびその製法
JP4825024B2 (ja) * 2006-03-09 2011-11-30 株式会社神戸製鋼所 疲労亀裂進展抑制および溶接熱影響部の靭性に優れた高降伏比高張力鋼板
JP4950529B2 (ja) * 2006-03-16 2012-06-13 株式会社神戸製鋼所 溶接熱影響部の靭性および母材靭性に優れた鋼材およびその製法
JP4058097B2 (ja) * 2006-04-13 2008-03-05 新日本製鐵株式会社 アレスト性に優れた高強度厚鋼板
JP4515427B2 (ja) * 2006-09-29 2010-07-28 株式会社神戸製鋼所 溶接熱影響部の靭性および疲労亀裂進展抵抗性に優れた鋼材およびその製法
CN101294257B (zh) * 2007-04-23 2014-06-18 株式会社神户制钢所 焊接热影响部的韧性优异的钢材及其制造方法
JP5234951B2 (ja) * 2008-11-21 2013-07-10 株式会社神戸製鋼所 溶接熱影響部の靭性および母材低温靭性に優れた鋼材、並びにその製造方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3282028A4 (en) * 2015-04-10 2018-11-07 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Steel sheet for high strength line pipe with excellent low temperature toughness and steel pipe for high strength line pipe

Also Published As

Publication number Publication date
KR20100102557A (ko) 2010-09-24
JP2010209433A (ja) 2010-09-24
CN101831588B (zh) 2013-01-09
KR101197872B1 (ko) 2012-11-05
CN101831588A (zh) 2010-09-15

Similar Documents

Publication Publication Date Title
JP5342902B2 (ja) 溶接熱影響部の靭性および母材疲労特性に優れた鋼材およびその製造方法
JP4950528B2 (ja) 溶接熱影響部の靭性に優れた低降伏比高張力鋼材およびその製法
JP4515430B2 (ja) 溶接熱影響部の靭性および母材靭性に優れた鋼材およびその製法
JP5337412B2 (ja) 脆性亀裂伝播停止特性に優れた厚鋼板およびその製造方法
JP5231042B2 (ja) 溶接熱影響部の靭性に優れた鋼材およびその製造方法
JP5096087B2 (ja) 母材低温靭性に優れた大入熱溶接用高張力鋼板
JP4515427B2 (ja) 溶接熱影響部の靭性および疲労亀裂進展抵抗性に優れた鋼材およびその製法
JP5651090B2 (ja) 溶接熱影響部の靱性に優れた鋼材およびその製造方法
KR20210127736A (ko) 강재 및 그 제조 방법
JP2009138255A (ja) 大入熱溶接時の熱影響部の靭性に優れた溶接用高張力厚鋼板
JP2009019244A (ja) 脆性亀裂伝播停止特性に優れた大入熱溶接用厚鋼板
KR101169866B1 (ko) 용접 열영향부의 인성이 우수한 강재, 및 그 제조 방법
JP5234951B2 (ja) 溶接熱影響部の靭性および母材低温靭性に優れた鋼材、並びにその製造方法
JP4950529B2 (ja) 溶接熱影響部の靭性および母材靭性に優れた鋼材およびその製法
JP2011127220A (ja) 溶接熱影響部の靱性に優れた鋼材の製造方法
JP5234952B2 (ja) 溶接熱影響部の靭性に優れた低降伏比鋼材、およびその製造方法
JP2007254767A (ja) 高張力厚鋼板の溶接継手
JP5520105B2 (ja) 溶接熱影響部の靱性に優れた鋼材およびその製造方法
JP4299769B2 (ja) 入熱２０〜１００ｋＪ／ｍｍの大入熱溶接用高ＨＡＺ靭性鋼材
JP2017082267A (ja) 厚鋼板
JP4515428B2 (ja) 溶接熱影響部の靭性および脆性破壊発生特性に優れた鋼材およびその製法
JP4515429B2 (ja) 溶接熱影響部の靭性および脆性亀裂停止特性に優れた鋼材およびその製法
JP2018024910A (ja) 高強度厚鋼板およびその製造方法
JP2024119238A (ja) 炭素鋼鋳片、および炭素鋼鋳片の製造方法
KR100899053B1 (ko) 용접 열영향부의 인성이 우수한 저항복비 고장력 강재 및그의 제조방법

Legal Events

Date Code Title Description
A621 Written request for application examination

Free format text: JAPANESE INTERMEDIATE CODE: A621

Effective date: 20110901

A977 Report on retrieval

Free format text: JAPANESE INTERMEDIATE CODE: A971007

Effective date: 20130624

TRDD Decision of grant or rejection written
A01 Written decision to grant a patent or to grant a registration (utility model)

Free format text: JAPANESE INTERMEDIATE CODE: A01

Effective date: 20130730

A61 First payment of annual fees (during grant procedure)

Free format text: JAPANESE INTERMEDIATE CODE: A61

Effective date: 20130812

R150 Certificate of patent or registration of utility model

Ref document number: 5342902

Country of ref document: JP

Free format text: JAPANESE INTERMEDIATE CODE: R150

Free format text: JAPANESE INTERMEDIATE CODE: R150

LAPS Cancellation because of no payment of annual fees