JP5257802B2 - 新規液晶表示装置及び有用な液晶組成物 - Google Patents
新規液晶表示装置及び有用な液晶組成物 Download PDFInfo
- Publication number
- JP5257802B2 JP5257802B2 JP2012536399A JP2012536399A JP5257802B2 JP 5257802 B2 JP5257802 B2 JP 5257802B2 JP 2012536399 A JP2012536399 A JP 2012536399A JP 2012536399 A JP2012536399 A JP 2012536399A JP 5257802 B2 JP5257802 B2 JP 5257802B2
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- display device
- substrate
- crystal display
- crystal composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
しかし、VAIPS方式においては、これらの一般的な計算式は当てはまらず、液晶材料の選択の基準が無いことから、性能の改善が進まず、結果として液晶表示装置としての応用は遅れていた。
液晶表示装置には明るい輝度でより高い黒レベルにすることでメガコントラスト(CR)を目指す課題もある。LCDの画素表示面積を大きく出来るように開口率を改善したり、DBEFやCLCなどの輝度向上フィルムを適用したり、液晶の垂直配向させる場合に突起などによる光漏れを低減するなどの提案がされている。更に、タッチパネル方式における押圧力にも乱れにくい表示も求められている。
前記液晶組成物が一般式(LC1)から一般式(LC5)
数4からセル構成としては、dgapをなるべく小さく、dITOをなるべく大きくすることにより、低駆動電圧化が図れ、使用する液晶組成物としてはΔεの絶対値が大きく、K33が小さいものを選択することにより、低駆動電圧化が図れることが分かった。これら知見をもとに、上記液晶表示装置に適切な負の誘電異方性液晶を見出した。
A1及びA2はそれぞれ独立して、1,4−シクロヘキシレン基、1,4−フェニレン基、3−フルオロ−1,4−フェニレン基又は3,5−ジフルオロ−1,4−フェニレン基が好ましく、
X1〜X5はそれぞれ独立してH又はFが好ましく、YはF、CF3又はOCF3が好ましく、
Z1〜Z4はそれぞれ独立して単結合、−C≡C−、−CH2CH2−、−OCH2−、−CH2O−、−OCF2−又は−CF2O−が好ましく、存在するZ1〜Z4の一つが−C≡C−、−CH2CH2−、−OCH2−、−CH2O−、−OCF2−又は−CF2O−であり、Z1〜Z4の内、他に存在する置換基がある場合にはこれらの置換基は単結合であることが好ましく、
m1及びm2はそれぞれ独立して0〜2の整数を表すことが好ましく、m1+m2は1又は2が好ましい。
一般式(LC1)から一般式(LC5)で表される液晶化合物は、より好ましくは一般式(LC1)が一般式(LC1)−1から一般式(LC1)−4
一般式(LC2)が下記一般式(LC2)−1から一般式(LC2)−10
一般式(LC3)が下記一般式(LC3)−1から一般式(LC3)−34
一般式(LC4)が下記一般式(LC4)−1から一般式(LC4)−8であり、一般式(LC5)が下記一般式(LC5)−1から一般式(LC5)−6
一般式(LC1)及び一般式(LC2)においてR1はアルケニルであり及び/又はR2がアルコキシ基又はアルケニルオキシ基であることが好ましく、一般式(LC3)〜(LC5)においてR1及びR2の少なくとも一方がアルケニルであることが好ましく、一般式(LC3)においてZ1及びZ2の少なくとも一方が−OCH2−又は−CH2O−である化合物が好ましい。
Sp1及びSp2がそれぞれ独立してアルキレン基を表し、該アルキレン基は1つ以上のハロゲン原子又はCNにより置換されていても良く、この基中に存在する1つ又は2つ以上のCH2基はO原子が直接隣接しないように−O−、−S−、−NH−、−N(CH3)−、−CO−、−COO−、−OCO−、−OCOO−、−SCO−、−COS−又は−C≡C−により置き換えられていてもよく、
P1及びP2がそれぞれ独立して以下の一般式(PC1−a)〜一般式(PC1−d)
TN-I :ネマチック相−等方性液体相転移温度(℃)を液晶相上限温度
Δε :誘電率異方性
Δn :屈折率異方性
Vsat :周波数1KHzの矩形波を印加した時の透過率が90%変化する印加電圧
τr+d/msec:dITO=10μm、dgap=10μm、第1基板、第2基板とも配向膜SE−5300のセルを使用した際の応答速度
化合物記載に下記の略号を使用する。
-2- -CH2CH2-
-1O- -CH2O-
-O1- -OCH2-
-V- -CO-
-VO- -COO-
-CFFO- -CF2O-
-F -F
-Cl -Cl
-CN -C≡N
-OCFFF -OCF3
-CFFF -CF3
-OCFF -OCHF2
-On -OCnH2n+1
-T- -C≡C-
ndm- CnH2n+1-HC=CH-(CH2)m-1-
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に表1に示す正の誘電異方性を有する液晶組成物を挟持して実施例1の液晶表示装置を作成した。(dcell=4.0μm、dITO=10μm、dgap=10μm、配向膜SE−5300)この液晶表示装置の物性値を表1に併せて示す。
実施例1で用いた液晶組成物を用いて従来のTN液晶表示装置を作製しその物性値を測定した。その結果を表2に示す。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に表1に示す正の誘電異方性を有する液晶組成物を挟持して実施例2の液晶表示装置を作成した。(dcell=4.0μm、dITO=10μm、dgap=10μm、配向膜SE−5300、AL−1051)
該液晶表示装置は同じ正の誘電異方性液晶を狭持した従来のECB液晶表示装置等と比較して、より高速な応答速度、より多い透過光量、外圧による光漏れの低減、より広範囲な視野角、より大きなコントラスト比を実現した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に表1に示す正の誘電異方性を有する液晶組成物に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して実施例3の液晶表示装置を作成した。(dcell=4.0μm、dITO=10μm、dgap=10μm、配向膜SE−5300)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に表1に示す正の誘電異方性を有する液晶組成物に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%を添加した組成物を挟持して実施例4の液晶表示装置を作成した。(dcell=4.0μm、dITO=10μm、dgap=10μm、配向膜SE−5300、AL−1051)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
実施例1と同様に表2に示す正の誘電異方性液晶を狭持して比較例2の液晶表示装置を作製しその物性値を測定し、その結果を表2に示す。
実施例1と同様に表3に示す正の誘電異方性液晶を狭持して実施例5の液晶表示装置を、実施例1と同様に実施例6の液晶表示装置及び実施例1と同様に実施例7の液晶表示装置を作成した。
実施例1と同様に表4に示す正の誘電異方性液晶を狭持して実施例8の液晶表示装置を、実施例1と同様に実施例9の液晶表示装置及び実施例1と同様に実施例10の液晶表示装置を作成した。
実施例1と同様に表5に示す正の誘電異方性液晶を狭持して実施例11の液晶表示装置を、実施例1と同様に実施例12の液晶表示装置及び実施例1と同様に実施例13の液晶表示装置を作成した。
実施例1と同様に表6に示す正の誘電異方性液晶を狭持して実施例14の液晶表示装置を、実施例1と同様に実施例15の液晶表示装置、実施例1と同様に実施例16の液晶表示装置及び実施例1と同様に表7に示す正の誘電異方性液晶を狭持して実施例17の液晶表示装置を作成した。
dcell=3.0μm、dITO=10μm、dgap=10μmとした以外は実施例1と同様に表8に示す正の誘電異方性液晶を狭持して実施例18の液晶表示装置を、実施例1と同様に実施例19の液晶表示装置、実施例1と同様に実施例20の液晶表示装置及び実施例1と同様に実施例21の液晶表示装置を作成した。
dcell=3.5μm、dITO=10μm、dgap=10μmとした以外は実施例1と同様に表9に示す正の誘電異方性液晶を狭持して実施例22の液晶表示装置を及び実施例1と同様に実施例23の液晶表示装置を作成した。
実施例1と同様に表10に示す正の誘電異方性液晶を狭持して実施例24の液晶表示装置及び実施例1と同様に実施例25の液晶表示装置を作成した。
dITO=4μm、dgap=4μmとしたセルに実施例5、12又は17で使用した正の誘電異方性液晶組成物を狭持して、それぞれ実施例26から28の液晶表示装置を作成し、応答速度を測定したところ、下記の結果を得た。
実施例26:τr+d=1.6msec(実施例5の液晶組成物)
実施例27:τr+d=1.3msec(実施例12の液晶組成物)
実施例28:τr+d=0.9msec(実施例17の液晶組成物)
実施例26から28の液晶表示装置は応答が極めて速い特性を有していた。また、本実施例で作成した液晶表示装置に押圧を加えたところ、従来のVA表示では生じていた光漏れがほとんど見られなかった。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に表11に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)
実施例29と同様に表12に示す正の誘電異方性液晶を狭持して比較例3の液晶パネルを作製しその物性値を測定した。その結果を前記表12に示す。
実施例29・比較例3と同様に第一の基板と第二の基板の間に表13に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。
実施例29・比較例3と同様に第一の基板と第二の基板の間に表14に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例29〜38及び比較例3に示した正の誘電異方性液晶を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)
実施例29〜38に示した正の誘電異方性液晶を狭持した該液晶パネルは比較例3に示した正の誘電異方性液晶を狭持した該液晶パネルと比較して、より高速な応答速度、より多い透過光量、外圧による光漏れの低減、より広範囲な視野角、より大きなコントラスト比を実現した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例29〜38及び比較例3に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例29〜38及び比較例3に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に表15に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)
実施例42〜45に示した正の誘電異方性液晶を狭持した該液晶パネルは従来の正の誘電異方性液晶を狭持した該液晶パネルと比較して、より高速な応答速度、より多い透過光量、外圧による光漏れの低減、より広範囲な視野角、より大きなコントラスト比を実現した。
実施例42と同様に第一の基板と第二の基板の間に表16に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。
実施例42と同様に第一の基板と第二の基板の間に表17に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例42〜51及び比較例1〜3に示した正の誘電異方性液晶を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)
実施例42〜51に示した正の誘電異方性液晶を狭持した該液晶パネルは比較例1〜3に示した正の誘電異方性液晶を狭持した該液晶パネルと比較して、より高速な応答速度、より多い透過光量、外圧による光漏れの低減、より広範囲な視野角、より大きなコントラスト比を実現した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例42〜51及び比較例1〜3に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例42〜51及び比較例1〜3に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に表18に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)
実施例55と同様に表19に示す正の誘電異方性液晶を狭持して比較例4の液晶パネルを作製しその物性値を測定した。その結果を前記表19に示す。
実施例55・比較例4と同様に第一の基板と第二の基板の間に表20に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例55〜59及び比較例4に示した正の誘電異方性液晶を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)
実施例55〜59に示した正の誘電異方性液晶を狭持した該液晶パネルは比較例4に示した正の誘電異方性液晶を狭持した該液晶パネルと比較して、より高速な応答速度、より多い透過光量、外圧による光漏れの低減、より広範囲な視野角、より大きなコントラスト比を実現した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例55〜59及び比較例4に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例55〜59及び比較例4に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に表21に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)
実施例63と同様に表22に示す正の誘電異方性液晶を狭持して比較例5の液晶パネルを作製しその物性値を測定した。その結果を前記表22に示す。
実施例63・比較例5と同様に第一の基板と第二の基板の間に表23に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例63〜67及び比較例5に示した正の誘電異方性液晶を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)
実施例63〜67に示した正の誘電異方性液晶を狭持した該液晶パネルは比較例5に示した正の誘電異方性液晶を狭持した該液晶パネルと比較して、より高速な応答速度、より多い透過光量、外圧による光漏れの低減、より広範囲な視野角、より大きなコントラスト比を実現した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例63〜67及び比較例5に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例63〜67及び比較例5に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に表24に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)
実施例71と同様に表25に示す正の誘電異方性液晶を狭持して比較例6の液晶パネルを作製しその物性値を測定した。その結果を前記表25に示す。
実施例71・比較例6と同様に第一の基板と第二の基板の間に表26に示す正の誘電異方性液晶を狭持して液晶パネルを作成した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例71〜75及び比較例6に示した正の誘電異方性液晶を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)
実施例71〜75に示した正の誘電異方性液晶を狭持した該液晶パネルは比較例6に示した正の誘電異方性液晶を狭持した該液晶パネルと比較して、より高速な応答速度、より多い透過光量、外圧による光漏れの低減、より広範囲な視野角、より大きなコントラスト比を実現した。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側に垂直配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例71〜75及び比較例6に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
図4に示す電極構造を第二の基板に作成し、電極構造を設けない第一の基板を使用し各々の対向側の片方に垂直配向性の配向膜を形成し、他方に水平配向性の配向膜を形成し、第一の基板と第二の基板の間に実施例71〜75及び比較例6に示した正の誘電異方性液晶に各々2−メチルーアクリル酸4‘−{2−[4−(2−アクリロイルオキシーエチル)―フェノキシカルボニル]―エチル}―ビフェニル−4−イルエステルを0.3質量%添加した組成物を挟持して液晶パネルを作成した。(dITO=4μm、dgap=4μm、配向膜SE−5300、AL−1051)電極間に駆動電圧を印加したまま、紫外線を600秒間照射(3.0J/cm2)し、重合処理を行った。
Claims (22)
- 第一の基板と、第二の基板と、前記第一の基板と第二の基板間に挟持された正の誘電率異方性を有する液晶組成物層からなる液晶表示装置であって、前記液晶表示装置は、複数の画素を有し、前記画素のそれぞれは、独立的に制御可能であって、前記画素は一対の画素電極と共通電極を有し、この両電極が前記第一と第二の両基板の少なくとも一方の基板に設けられ、前記液晶組成物層の液晶分子の長軸が前記基板面に略垂直に配向しているか又は、ハイブリッド配向しており、
前記液晶組成物が一般式(LC1)−1から一般式(LC1)−4
一般式(LC2)−4から一般式(LC2)−10
一般式(LC3)−1から一般式(LC3)−5、一般式(LC3)−7から一般式(LC3)−27、及び一般式(LC3)−29
- 液晶組成物が、さらに、一般式(LC6)
- 液晶組成物が、重合性化合物を1種又は2種以上含有する請求項1〜5いずれか一項に記載の液晶表示装置。
- 請求項6に記載の重合性化合物が、ベンゼン誘導体、トリフェニレン誘導体、トルキセン誘導体、フタロシアニン誘導体又はシクロヘキサン誘導体を分子の中心の母核とし、直鎖のアルキル基又は直鎖のアルコキシ基がその側鎖として放射状に置換した構造である円盤状液晶化合物である、液晶表示装置。
- 請求項6又は7における液晶組成物が開始剤を実質的に含まない液晶組成物を使用したことを特徴とする請求項6又は7記載の液晶表示装置。
- 重合性化合物を0.1〜2.0質量%含有する液晶組成物を使用したことを特徴とする請求項6〜8のいずれか一項に記載の液晶表示装置。
- さらに酸化防止剤を1種又は2種以上含有した液晶組成物を使用したことを特徴とする請求項1〜9のいずれか一項に記載の液晶表示装置。
- さらにUV吸収剤を1種又は2種以上含有した液晶組成物を使用したことを特徴とする請求項1〜10のいずれか一項に記載の液晶表示装置。
- 液晶組成物の屈折率異方性(Δn)と表示装置の第一の基板と、第二の基板との間隔(d)の積(Δn・d)が0.33〜0.40である請求項1〜11のいずれか一項に記載の液晶表示装置。
- 液晶組成物の屈折率異方性(Δn)と表示装置の第一の基板と、第二の基板との間隔(d)の積(Δn・d)が0.34〜0.44である請求項1〜12のいずれか一項に記載の液晶表示装置。
- 表示装置の第一の基板と、第二の基板上の液晶組成物と接する面にポリイミド(PI)、カルコン、シンナメートからなる配向膜を設けた請求項1〜13のいずれか一項に記載の液晶表示装置。
- 表示装置の第一の基板と、第二の基板上の液晶組成物と接する面に光配向技術を用いて作成した配向膜を設けた請求項1〜14のいずれか一項に記載の液晶表示装置。
- 基板と液晶組成物のチルト角が85〜90°である請求項1に記載の液晶表示装置。
- 第一の基板又は第二の基板と液晶組成物のチルト角が85〜90°であり、残りの基板と液晶組成物のチルト角が3〜20°である請求項1に記載の液晶表示装置。
- 液晶組成物が、さらに一般式(LC1)−1、(LC2)−1、(LC3)−4、(LC3)−5及び(LC3)−6から選ばれる1種又は2種以上の化合物を含有する請求項1〜17のいずれか一項に記載の液晶表示装置。
- 液晶組成物が、さらに一般式(LC1)−2、(LC1)−3、(LC1)−4、(LC2)−4、(LC2)−5、(LC2)−6、(LC2)−7、(LC2)−8、(LC2)−9及び(LC2)−10から選ばれる1種又は2種以上の化合物を含有する請求項1〜17のいずれか一項に記載の液晶表示装置。
- 液晶組成物が、さらに一般式(LC3)−3、(LC3)−22、(LC3)−23、(LC3)−24及び(LC3)−25から選ばれる1種又は2種以上の化合物を含有する請求項1〜17のいずれか一項に記載の液晶表示装置。
- 液晶組成物が、さらに一般式(LC6)−1、(LC6)−5及び(LC6)−14から選ばれる1種又は2種以上の化合物を含有する請求項1〜17のいずれか一項に記載の液晶表示装置。
- 液晶組成物が、さらに一般式(LC6)−4、(LC6)−12及び(LC6)−15から選ばれる1種又は2種以上の化合物を含有する請求項1〜17のいずれか一項に記載の液晶表示装置。