JP5192817B2 - 高い比表面積を有する炭酸カルシウムの被覆粒子 - Google Patents
高い比表面積を有する炭酸カルシウムの被覆粒子 Download PDFInfo
- Publication number
- JP5192817B2 JP5192817B2 JP2007540644A JP2007540644A JP5192817B2 JP 5192817 B2 JP5192817 B2 JP 5192817B2 JP 2007540644 A JP2007540644 A JP 2007540644A JP 2007540644 A JP2007540644 A JP 2007540644A JP 5192817 B2 JP5192817 B2 JP 5192817B2
- Authority
- JP
- Japan
- Prior art keywords
- particles
- surface area
- coating agent
- specific surface
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
しかし、先行技術から知られているプラスチゾルは、全ての点を満たさない。
スプレーガンを用いて基体に塗布されるとき、良好なプラスチゾルは、剪断力が低いときは高い粘度、剪断力が高いときは低い粘度を示すべきである。さらに、高い降伏応力及び良好なチキソトロープ性を特徴とするべきである。
本発明の粒子を含有するプラスチゾルは、優れた流体力学的特性、特に高い降伏応力値、良好な粘度及びチキソトロピーを示す。
本発明の好ましい実施態様では、アルカリ土類金属炭酸塩の粒子が、炭酸カルシウム又は炭酸マグネシウムであり、炭酸カルシウムが特に好ましい。
本発明の粒子は、コーティング剤でコーティングされている。いくつかのコーティング剤がこの目的に好適である。
さらに好ましくは、該コーティング剤は、少なくとも有機スルホン酸;アルキル硫酸;ヒドロキシ脂肪酸及びそれらの塩及び脂肪酸からなる群から選択される化合物を含む。
さらに好ましくは、該コーティング剤は、少なくとも有機スルホン酸、アルキル硫酸、ヒドロキシ脂肪酸及びそれらの塩からなる群から選択される化合物を含む。
最も好ましくは、該コーティング剤は、少なくとも有機スルホン酸;アルキル硫酸及びそれらの塩からなる群から選択される化合物を含む。
本明細書では、“アルキル”という用語は、特に明記しない限り、好ましくは1〜30個、さらに好ましくは1〜18個、最も好ましくは1〜12個、及び特に1〜6個の炭素原子を有する直鎖又は分枝アルキル鎖、例えばメチル、エチル、n-プロピル、i-プロピル、n-ブチル、sec-ブチル、イソ-ブチル、tert-ブチル、n-ペンチル、i-ペンチル、n-ヘキシル、i-ヘキシル、n-ヘプチル、i-ヘプチル、n-オクチル、i-オクチル、n-ノニル、i-ノニル、n-デシル、i-デシル、n-ウンデシル、i-ウンデシル、n-ドデシル、i-ドデシルなどを意味する。
本発明の別の好ましい実施態様では、該コーティング剤が少なくとも硫黄有機化合物を含む。好ましくは、該コーティング剤が、アルキルスルホン酸、アリールスルホン酸、アルキルアリールスルホン酸、アルキルスルホコハク酸、アルキルスルホサクシネート、アルキル硫酸及びそれらの塩からなる群から選択される化合物を含む。
本明細書では、“アルキルアリール”という用語は、上記の“アリール”残基に共有結合した上記の“アルキル”残基、例えば-CH2C6H5、-CH2CH2C6H5、-CH2CH2CH2C6H5などを意味する。
R1、R7、R9及びR10は、独立に単結合、-O-、-C1-C18-アルキレン-又は-C2-C18-アルケニレン-(式中、アルキレン-又はアルケニレン-鎖では、任意に1、2又は3つの-CH2-基が-O-に置き換えられ得る)であり;
R2、R3、R4、R5及びR6は、独立に-H、-C1-C18-アルキル(式中、アルキル-鎖では、任意に1、2又は3つの-CH2-基が-O-に置き換えられ得る)、-OH、-F、-Cl、CN、-CO2H、-CO-C1-C6-アルキル、-CO2-C1-C6-アルキル、-O-CO-C1-C6-アルキル、-NO2、NH2、NHC1C6-アルキル又は-N(C1-C6-アルキル)2であり;
R8は-H又は-C1-C6-アルキルであり;及び
R11及びR12は、独立に-H、-C1-C18-アルキル(式中、アルキル-鎖では、任意に1、2又は3つの-CH2-基が-O-に置き換えられ得る)、-NH2、NHC1-C6アルキル又は-N(C1-C6-アルキル)2である。
本明細書では、“アルケニレン”という用語は、二価の直鎖又は分枝アルケニレン鎖、例えば-CH=CH-、-CH2CH=CH-、CH2CH2CH=CH-、-CH=C(CH3)-、-CH2CH=C(CH3)-、-CH=C(CH3)CH2-などを意味する。
R1、R7、R9及びR10が、独立に単結合又は-C1-C6-アルキレン-(式中、アルキレン-鎖では、任意に1又は2つの-CH2-基が-O-で置き換えられ得る)であり;
R2、R3、R4、R5及びR6が、独立に-H又は-C1-C18-アルキル(式中、アルキル-鎖では、任意に1、2又は3つの-CH2-基が-O-で置き換えられ得る)であり;
R8が-H又は-C1-C6-アルキルであり;及び
R11及びR12が、独立に-C1-C12-アルキル(式中、アルキル-鎖では、任意に1、2又は3つの-CH2-基が-O-で置き換えられ得る)である。
R1及びR7が単結合であり;
R2、R3、R5及びR6が-Hであり;
R4が-H又は-C1-C6-アルキルであり;
R8が-Hであり;
R9及びR10が独立に単結合又は-CH2-であり;及び
R11及びR12が独立に-C1-C12-アルコキシである。
最も好ましくは、該コーティング剤が、ベンゼンスルホン酸、トルエンスルホン酸、ジオクチルスルホサクシネート及びそれらの塩からなる群から選択される1種以上の化合物を含む。
dP = 6/(ρSM)
式中、ρは炭酸カルシウムの比質量である。
さらに好ましくは、平均一次粒子サイズは、1〜30nmの範囲内である。
-本発明のコーティングされた粒子;
-少なくとも1種のポリマー、例えばポリ塩化ビニル(PVC)、例えばVestolit、Vinolit;
-任意に少なくとも1種の可塑剤、例えばジオクチルフタレート(DOP)、ジイソノニルフタレート(DINP)、アジペート、セバセート;
-任意に少なくとも1種の溶媒、例えば炭化水素の誘導体;
-任意に少なくとも1種の充填剤、例えばTiO2、SiO2、天然炭酸カルシウム;
-任意に少なくとも1種の促進剤、例えばポリアミン、ポリアミド;
-任意に少なくとも1種の乾燥剤、例えばCaO;及び
-任意にさらなる添加剤、
を含有する。
好ましくは、該コーティング剤は、上記の1種以上の好ましい化合物を含む。
(a)炭酸カルシウム粒子を水酸化カルシウムの懸濁液から50m2g-1よりも大きい比表面積を与える条件下で沈殿させる工程;及び
(b)工程(a)から得られた炭酸カルシウムの粒子を該コーティング剤と接触させる工程、
を含む。
本発明はまた、ポリマー組成物中における充填剤としての上記コーティングされた粒子の使用に関する。
以下の実施例は本発明をさらに説明するが、その範囲を限定するものとは解釈されない。
41〜104m2g-1(コーティング前)の範囲の比表面積を有する炭酸カルシウムの粒子を、WO 03/004414に記載の方法によって得た。
これらの沈降炭酸カルシウム粒子を、Marlon、AOT、ステアリン酸及びヒドロキシステアリンから選択されるコーティング剤でコーティングした。“Marlon”は、85質量%のベンゼンスルホン酸及び15質量%のトルエンスルホン酸のナトリウム塩を含む混合物であり、“AOT”は、ジオクチルスルホコハク酸のナトリウム塩を意味する。該コーティング剤を沈降炭酸ナトリウム粒子に塗布するために、該コーティング剤の溶液又はエマルジョンを加えた。コーティングが溶液形態で塗布されるときは、該コーティング剤を沈降炭酸カルシウムのスラリーに室温で加え、30分間撹拌した後に濾過してオーブンで乾燥した。コーティングがエマルジョン形態で塗布されるときは、該コーティング剤を沈降炭酸カルシウムのスラリーに75〜85℃で加え、30分間撹拌した後に濾過してオーブンで乾燥した。
ポリ塩化ビニル及び実施例1のコーティングされた炭酸カルシウム粒子を含有する2種の異なる製剤を調製した。前記製剤の組成を、以下の表3に要約する。
実施例2から得られた種々の製剤の流体力学的特性を、ISO 3219 normに従って調査した。測定は、可動式DIN 125円錐状シリンダーを備えたレオメータータイプUDS 200で行った。このレオメーターは、所定の速度勾配の関数における剪断力及び粘度の動きを測定する。全ての測定は、25℃で以下の手順:
25℃で5分間熱平衡が達成されるまで調査を保ち、
2分間かけて0〜100s-1まで加速させて120データポイントを測定し、
100s-1で1分間保って20データポイントを測定し、
2分間かけて100〜0s-1まで減速させて120データポイントを測定すること、
に従って行った。
表2に示すように、該製剤におけるコーティングされた沈降炭酸カルシウムの含有量は変化した(100%、75%、65%及び50%)。
該製剤を、それらの調製1日後に試験した。流体力学的試験の実施例を、以下の表4〜14に要約する。
Claims (9)
- 少なくとも1種のコーティング剤で少なくとも部分的にコーティングされ、且つコーティング前に50m2g-1よりも大きい比表面積を有する、アルカリ土類金属炭酸塩の粒子であって、コーティング剤が、ヒドロキシル基で置換されている脂肪酸;有機スルホン酸;アルキル硫酸;及びそれらの塩からなる群から選択される少なくとも1種の化合物を含む、粒子。
- コーティング前に65m2g-1よりも大きい比表面積を有する、請求項1記載の粒子。
- コーティング剤が、ヒドロキシル基で置換されているステアリン酸、ベンゼンスルホン酸、トルエンスルホン酸、ジオクチルスルホサクシネート及びそれらの塩からなる群から選択される1種以上の化合物を含む、請求項1又は2記載の粒子。
- 0.1〜30nmの範囲内の平均一次粒子サイズを有する、請求項1〜3のいずれか1項に記載の粒子。
- 請求項1〜4のいずれか1項に記載の粒子、及び少なくとも1種のポリマーを含む、組成物。
- ポリマーがポリ塩化ビニルを含む、請求項5記載の組成物。
- 50m2g-1よりも大きい比表面積を有するアルカリ土類金属炭酸塩のコーティングされていない粒子を、少なくとも1種のコーティング剤と接触させる工程を含み、コーティング剤が、ヒドロキシル基で置換されている脂肪酸;有機スルホン酸;アルキル硫酸;及びそれらの塩からなる群から選択される少なくとも1種の化合物を含む、請求項1〜4のいずれか1項に記載のコーティングされた粒子の調製方法。
- (a)炭酸カルシウム粒子を、水酸化カルシウムの懸濁液から50m2g-1よりも大きい比表面積を与える条件下で沈殿させる工程;及び
(b)工程(a)から得られる炭酸カルシウム粒子を、コーティング剤と接触させる工程、
を含む、請求項7記載の方法。 - ポリマー組成物における充填剤としての、請求項1〜4のいずれか1項に記載の粒子の使用。