JP4862343B2 - 磁気転写シート及び磁気記録媒体とその製造方法 - Google Patents
磁気転写シート及び磁気記録媒体とその製造方法 Download PDFInfo
- Publication number
- JP4862343B2 JP4862343B2 JP2005296061A JP2005296061A JP4862343B2 JP 4862343 B2 JP4862343 B2 JP 4862343B2 JP 2005296061 A JP2005296061 A JP 2005296061A JP 2005296061 A JP2005296061 A JP 2005296061A JP 4862343 B2 JP4862343 B2 JP 4862343B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- magnetic
- magnetic recording
- transfer sheet
- ovd
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、磁気記録媒体の製造と同時に、偽造や改竄が困難でその磁気記録媒体の真贋を目視にて確認する事ができる機能を付与した磁気転写シートに関するものである。また、本発明は、この磁気転写シートを使用して製造された磁気記録媒体にも関連する。
反射光の強度が大きく、結果、明るい回折光や干渉光等を観察する事が可能となり、その真贋も容易に判別する事が可能となる。更に、光反射層に重ねて耐薬品保護層を備えている事から、この金属薄膜の腐食を防止して耐久性を向上させる事が可能となる。
次に、本発明に係る転写シートの構造について、図面を参照して説明する。
るもので、その他は図1Aに示す転写シートと同様である。尚、隠蔽層26は、1色の印刷インキ皮膜261で構成されている。
この転写シートを構成する各層の材質と形成方法について説明する。
剥離保護層21としては、樹脂に滑剤を添加したものが使用できる。樹脂としては、熱可塑性樹脂、熱硬化性樹脂、湿気硬化性樹脂、紫外線硬化性樹脂、電子線硬化性樹脂等が使用できる。例えば、アクリル樹脂やポリエステル樹脂、ポリアミドイミド樹脂である。また、滑剤としてはポリエチレンパウダーや、カルナバロウ等のワックスを使用する事ができ、20重量部まで添加する事が可能である。これらは剥離保護層21として、支持体1上にグラビア印刷法やマイクログラビア法等、公知の塗布方法によって形成される。
OVD層22は、OVD形成層221と光反射層222の少なくとも2層を含んで構成されるものである。後述するように、OVD層22には、更にこの他の層を含む事もできる。
OVD形成層221は、レリーフ型回折格子や体積型回折格子等の他、屈折率がおよそ2.0以上の高屈折率の薄膜と屈折率がおよそ1.5程度の低屈折率材料の薄膜とをそれぞれ光学的に適当な膜厚で適宜積層した多層薄膜等が利用できる。
して、回折格子を構成する縞状に露光する事によって形成する事も可能である。この場合には、その干渉縞を1本ごとに制御する事ができるため、ホログラムと同様に任意の立体画像やチェンジング画像を記録する事ができる。また、画像をドット状の画素領域に分割し、この画素領域ごとに異なる回折格子を記録し、これら画祖の集合で全体の画像を表現する事も可能である。画素は円形のドットの他、星形のドットでも良い。
光反射層222は、OVD形成層221に直接接触して設ける必要はないが、OVD形成層221がレリーフ型回折格子の場合には、その凹凸パターンに光反射層222を直接接触して設けられる必要がある。この場合には、この光反射層222によって反射した光がそのまま回折光となる。
その薄膜を形成する事ができる。薄膜の厚みは5〜1000nm程度で良い。
磁気記録層23としては、通常の磁気カードや磁気テープ等に使用されている磁気記録層と同じものが使用できる。例えば、γ−Fe2O3、コバルト被着γ−Fe2O3、バリウムフェライト等の磁性粉をバインダー中に分散して製造した磁性塗料を、公知の方法で均
一に塗布して形成する事ができる。
接着層24としては、熱及び圧力によって被転写基材に接着するものであれば良く、公知の感熱性接着材料を使用する事ができる。
耐薬品保護層25としては、40〜50℃の1.5Nの水酸化ナトリウム水溶液中に60秒間浸漬して、塗膜に変化の生じないものが望ましい。この場合には、全面均一に形成した光反射層222上に耐薬品保護層25を形成し、前記水酸化ナトリウム水溶液をエッチング液として使用し、このエッチング液中に5〜30秒間浸漬する事により、光反射層222を画像パターン状に加工する事ができる。
また、耐薬品保護層25は、ガラス転移温度150℃以上の樹脂を使用する事が望ましい。この場合には、酸やアルカリから保護するだけでなく、高温から光反射層222の変形を守る事も可能となる。このような、耐薬品・耐熱性の樹脂としては、ポリカーボネート樹脂(Tg.140〜150℃)、ポリアリレート樹脂(Tg.193℃)、ポリスルホン樹脂(Tg.190℃)、ポリエーテルスルホン樹脂(Tg.225℃)、ポリエーテルイミド樹脂(Tg.200℃以上)、環状ポリオレフィン共重合体(Tg.171℃)、変性ノルボルネン系樹脂(Tg.171℃)、ポリアミドイミド樹脂(Tg.200℃以上)、ポリイミド樹脂(Tg.250℃以上)等が挙げられる。この他、熱硬化性樹脂、湿気硬化性樹脂、紫外線硬化性または電子線硬化性の樹脂を使用しても良い。
尚、これら樹脂の比重を1とした場合の40重量%を上限として、フィラーや充填剤、着色剤等を添加する事ができる。40重量%を超えて添加した場合には、分散性が悪くなって塗膜強度が低下して耐熱性が劣る事がある。また、塗液の流動性が低くなって版上で乾燥してしまって印刷適性が悪化する事や、塗液中のそれら添加剤が、保存中または塗工中に沈降または凝集してしまう事等がある。
隠蔽層26としては、電気絶縁性で、光透過を防止する不透明な印刷インキを使用する事ができる。このような印刷インキは周知である。
本発明に係る磁気転写シートを被転写基材に重ね、熱圧着により接着した後、支持体1を剥離除去する事により、転写層を転写して磁気記録媒体を製造する事ができる。被転写基材としては、任意のものが利用できるが、例えば、ポリ塩化ビニル樹脂やポリエステル樹脂、ポリエチレンテレフタレート樹脂を材質とするプラスチックカード基材等が挙げられる。また、紙や合成紙等も基材として使用できる。
まず、支持体1として、厚さ25μmの透明なポリエチレンテレフタレート(通称PET)フィルムを使用した。
に保温された1.5Nの水酸化ナトリウム水溶液が入った浴槽に10秒間浸し、前記耐薬品保護層25がマスクとなり、耐薬品保護層25が存在せずにアルミニウム蒸着膜が露出している部位をエッチングで除去した。更に、0.1Nの塩酸水溶液に浸して中和処理を行い、その後、水洗、乾燥した。こうして、独立した画像パターン状にアルミニウム蒸着膜から構成される光反射層222と、この光反射層222に重ねられ、且つ、この光反射層と同一形状を有する耐薬品保護層25を形成した。
ポリアミドイミド樹脂(Tg.250℃) 19.2重量部
ポリエチレンパウダー 0.8重量部
ジメチルアセトアミド 45.0重量部
トルエン 35.0重量部
「OVD形成層インキ組成物」
ウレタン樹脂 20.0重量部
メチルエチルケトン 50.0重量部
酢酸エチル 30.0重量部
「耐薬品保護層インキ組成物」
変性ノルボルネン樹脂(Tg.171℃) 20.0重量部
沈降性硫酸バリウム(比重5.5) 10.0重量部
メチルエチルケトン 40.0重量部
トルエン 30.0重量部
「磁気記録層インキ組成物」
γFe2 O3磁性粉 30.0重量部
塩酢ビ共重合体 3.0重量部
ポリウレタンエラストマー 20.0重量部
メチルエチルケトン 15.0重量部
トルエン 15.0重量部
「接着層インキ組成物」
塩化ビニル酢酸ビニル共重合樹脂 15.0重量部
アクリル樹脂(Tg.20℃) 10.0重量部
シリカ 1.0重量部
メチルエチルケトン 44.0重量部
トルエン 30.0重量部
次に、この磁気転写シートを磁気テープの形状に切断してプラスチックカード基材に重ね、版面温度120℃の熱ロール転写機にて転写してから支持体1を剥離除去し、磁気カードを製造した。
美麗であるばかりでなく、光反射層222と隠蔽層262の位置が精度良く組み合わされている事から、更に偽造を困難なものとしていた。
2 ・・・・転写層
21 ・・・・剥離保護層
221 ・・・・OVD形成層
222 ・・・・光反射層
23 ・・・・磁気記録層
24 ・・・・接着層
25 ・・・・耐薬品保護層
26 ・・・・隠蔽層
261 ・・・・隠蔽層
262 ・・・・隠蔽層
27 ・・・・印刷層
3 ・・・・基材
Claims (5)
- 支持体上の片面に磁気記録層を含む転写層を有し、この転写層を被転写基材に転写すると共に支持体を剥離除去してなる磁気記録媒体を製造する磁気転写シートであり、この転写層には観察する角度に応じて異なる色彩や画像パターンを見る事ができるホログラム等の回折格子や多層薄膜である光学多層干渉膜、またはコレステリック液晶の層等が形成されてなるOVD形成層、及び、前記OVD形成層への入射光を反射する光反射層からなるOVD層を有し、支持体側から見て、剥離保護層、OVD形成層、光反射層、磁気記録層、接着層の順に積層してなる磁気転写シートで、光反射層が画像パターン状に設けられ、且つ、その画像パターンが周囲を電気絶縁性材料に包囲された独立したパターンであり、前記光反射層が金属薄膜から構成されており、更には光反射層と磁気記録層との間にあって光反射層に重ねて、耐薬品保護層を備え、前記耐薬品保護層は40〜50℃の1.5Nの水酸化ナトリウム水溶液中に60秒侵漬して塗膜に変化を生じず、かつ、ガラス点移温度が150℃以上の樹脂を使用した事を特徴とする磁気転写シート。
- 磁気記録層とOVD形成層との間であって、前記光反射層の存在しない部位を覆う領域に、光の透過を遮断する隠蔽層を備える事を特徴とする請求項1に記載の磁気転写シート。
- 転写後に観察可能な位置に印刷層を備える事を特徴とする請求項1または2のいずれかに記載の磁気転写シート。
- 請求項1〜3記載のいずれかに記載の磁気転写シートを、紙やフィルム、カード等に転写した事を特徴とする磁気記録媒体。
- 透明なポリエチレンテレフタレートフィルムからなる支持体の片面に、剥離保護層21を形成する工程、
ロールエンボス法により回折格子形成用のプレス版を熱圧してその表面に回折格子を発生させるための凹凸を形成し、OVD形成層221を形成する工程、
前記OVD形成層221の全面に、光反射層として真空蒸着法にてアルミニウム蒸着膜を均一に形成し、更に、インキを画像パターン状に印刷して、アルミニウム蒸着膜上に耐薬品保護層25を形成する工程、
50℃に保温された1.5Nの水酸化ナトリウム水溶液が入った浴槽に浸し、耐薬品保護層25が存在せずにアルミニウム蒸着膜が露出している部位をエッチングで除去する工程、
更に、塩酸水溶液に浸して中和処理を行い、水洗、乾燥し、前記光反射層が存在しない部位に、スクリーン印刷法により印刷し隠蔽層262とし、光反射層が存在しない部位の全体を覆う領域をスクリーン印刷法にて印刷し、隠蔽層261とする工程、
更に、その全面に磁性インキを塗布・乾燥して磁気記録層23を形成する工程、
接着層24を形成して所望の磁気転写シートを製造する工程、
を具備し、
耐薬品保護層のインキ組成物は、変性ノルボルネン樹脂20.0重量部、沈降性硫酸バリウム10.0重量部、メチルエチルケトン40.0重量部、トルエン30.0重量部からなることを特徴とする磁気転写シートの製造方法。