JP4583795B2 - MgO−C質レンガ廃材を含有する乾式振動施工用耐火物 - Google Patents
MgO−C質レンガ廃材を含有する乾式振動施工用耐火物 Download PDFInfo
- Publication number
- JP4583795B2 JP4583795B2 JP2004107217A JP2004107217A JP4583795B2 JP 4583795 B2 JP4583795 B2 JP 4583795B2 JP 2004107217 A JP2004107217 A JP 2004107217A JP 2004107217 A JP2004107217 A JP 2004107217A JP 4583795 B2 JP4583795 B2 JP 4583795B2
- Authority
- JP
- Japan
- Prior art keywords
- refractory
- mass
- binder
- mgo
- construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
まずMgO-C質レンガ廃材について説明し、次いでその他の耐火性原料、熱硬化性バインダー及び外割り添加するその他の成分について説明する。
MgO-C質レンガ廃材は50 mm以下の粒径に整粒する。すなわち、耐火物中のMgO-C質レンガ廃材の最大粒径を50 mmとする。MgO-C質レンガ廃材の粒径が50 mmを超えると耐火物を充填した時に偏析し易い。MgO-C質レンガ廃材の粒径は40 mm以下であるのが好ましい。ただし74μm以下の粒径のMgO-C質レンガ廃材微粒子の含有量は8質量%以下が好ましい。MgO-C質レンガ廃材中に占める74μm以下の微粒子の含有量が8質量%を超えると、MgO-C質レンガ廃材中に含まれる難焼結性の黒鉛が微粉として混入する割合が高くなるため、得られる施工体の強度が低下し、かつ酸化も起こしやすくなる。
MgO-C質レンガ廃材以外の耐火性原料(その他の耐火性原料)としては、アルミナ、ブラウンアルミナ、ボーキサイト、黒鉛、酸化クロム、ジルコニア、チタニア、スピネル及びマグネシアからなる群から選ばれた少なくとも一種が使用でき、必要に応じて2種以上を併用してもよい。但しMgO-C質レンガ廃材は塩基性耐火性原料であるMgOを主成分とするため高融点であるが、酸性成分であるSiO2を含むと低融点物の生成等により耐食性及び耐火性が低下する。このため、珪石、シリカフューム、蝋石等のSiO2を多く含有する耐火性原料は使用しないか、使用してもできるだけ少量であるのが好ましい。具体的には、SiO2を含有する酸性耐火成分の含有量は、耐火性原料及び熱硬化性バインダーの合計を100質量%として3質量%以下とするのが好ましい。またSiCはスラグに対して濡れ難く耐食性に優れているが、高温下で徐々に酸化が進行してSiO2に変化し、これがMgOと反応して低融点物を生成する。そのためSiCは使用しないか、使用してもできるだけ少量であるのが好ましい。具体的には、SiCの含有量は、耐火性原料及び熱硬化性バインダーの合計を100質量%として5質量%以下が好ましい。その他の耐火性原料の粒度に特に制限はなく、従来の乾式振動施工用耐火物に使用可能な公知の粒度範囲であればよい。
本発明の乾式振動施工用耐火物に使用する熱硬化性バインダーとして、有機バインダー及び金属バインダーを使用するのが好ましい。必要に応じて低融点無機バインダーを有機バインダー及び金属バインダーと併用してもよい。
乾式振動施工用耐火物には、得られる施工体の耐食性及び加熱強度等を損なわない範囲で、その他の成分を添加してもよい。例えば乾式振動施工用耐火物を投入する際に発生する多量の粉塵を防止するために、発塵防止剤を添加するのが好ましい。発塵防止剤としては、灯油、真空ポンプオイル等の鉱物油が好ましい。また施工体の強度向上のための無機又は金属の繊維、炭化ホウ素等の酸化防止剤等を添加しても良い。
乾式振動施工用耐火物を施工する方法は特に限定されず、例えば(a) 乾式振動施工用耐火物を粉末状のまま施工部位に投入し、加圧しながら加振充填する方法(加圧加振充填法)、(b) 乾式振動施工用耐火物を型枠に敷き詰め、型枠を加振することにより充填する方法(型枠加振充填法)等が挙げられる。
表1に示す主要化学成分を有するMgO-C質レンガ廃材(転炉用レンガの廃材)を用いて、表2に示す配合割合の乾式振動施工用耐火物を作製した。得られた各乾式振動施工用耐火物を所定の型枠に充填し、これらを振動テーブル上に置いて6G(58.8 m/s2)の振動加速度で3分間加振した。型枠に充填した各耐火物を300℃の温度で2時間加熱し、脱枠して試験片を作製した。加振充填後/加振充填前の容積比は0.72〜0.80であった。
表2に示す配合割合の各乾式振動施工用耐火物を用いた以外は実施例1と同様にして試験片を作製した。
表2に示す配合割合の流し込み材を混練した後、型枠に流し込み、20℃の温度で24時間養生し、脱枠した後、110℃の温度で24時間乾燥して試験片を作製した。
表2続き
上底が5.8 cmであり、下底が11.5 cmであり、高さが5 cmの台形断面を有し、長さが23 cmの柱状試験片を作製し、誘導炉の壁に各試験片をセットして、1550〜1600℃の温度の高炉スラグ及び溶銑に5時間曝す侵食試験を行った。試験後、各試験片の溶損部の断面積を測定することにより溶損量を求め、参考例1の場合を100として溶損指数で示した。溶損指数が大きいほど耐食性が劣る。
4cm×4cm×16 cmの試験片を作製し、各試験片を還元雰囲気下(蓋付きのアルミナ製ボックスに各試験片を入れ、黒鉛粉で充填)、300℃、1000℃及び1450℃の温度で3時間加熱した後、JIS R 2213により加熱後曲げ強度を測定した。1450℃加熱後の試験片についてはJIS R 2208による残存線変化率も調べた。得られた残存線変化率が(+)の場合は残存膨張を表し、(−)の場合は残存収縮を表す。
表3続き
2・・・乾式振動施工用耐火物
3・・・電動ランマー
3a・・・振動モーター
3b・・・振動板
4・・・型枠
Claims (2)
- 少なくとも耐火性原料及び熱硬化性バインダーを含有し、粉末状のまま施工部位に投入し、加振充填して施工するための乾式振動施工用耐火物であって、前記耐火性原料及び前記熱硬化性バインダーの合計を100質量%として、前記耐火性原料は、50 mm以下の粒径に整粒したMgO-C質レンガ廃材を5〜20質量%未満含有し、SiO 2 を含有する酸性耐火成分の含有量が3質量%以下及びSiCの含有量が5質量%以下であり、かつ前記熱硬化性バインダーはピッチ(石油系及び/又は石炭系)及び/又はフェノール樹脂からなる有機バインダーを1〜7質量%、並びに金属アルミニウム粉及び/又はアルミニウム−マグネシウム合金粉からなる金属バインダーを1〜6質量%含有することを特徴とする乾式振動施工用耐火物。
- 少なくとも耐火性原料及び熱硬化性バインダーを含有し、粉末状のまま施工部位に投入し、加振充填して施工するための乾式振動施工用耐火物であって、前記耐火性原料及び前記熱硬化性バインダーの合計を100質量%として、前記耐火性原料は、50 mm以下の粒径に整粒したMgO-C質レンガ廃材を20〜80質量%含有し、SiO 2 を含有する酸性耐火成分の含有量が3質量%以下及びSiCの含有量が5質量%以下であり、かつ前記熱硬化性バインダーはピッチ(石油系及び/又は石炭系)及び/又はフェノール樹脂からなる有機バインダーを1〜7質量%、金属アルミニウム粉及び/又はアルミニウム−マグネシウム合金粉からなる金属バインダーを1〜6質量%、並びに硼酸、硼砂、硼珪酸ガラス、珪酸ガラス及びリン酸ガラスからなる群から選ばれた少なくとも一種からなる低融点無機バインダーを0.5〜2質量%含有することを特徴とする乾式振動施工用耐火物。