JP4507763B2 - 冷間鍛造−軟窒化による機械部品の製造方法 - Google Patents
冷間鍛造−軟窒化による機械部品の製造方法 Download PDFInfo
- Publication number
- JP4507763B2 JP4507763B2 JP2004246236A JP2004246236A JP4507763B2 JP 4507763 B2 JP4507763 B2 JP 4507763B2 JP 2004246236 A JP2004246236 A JP 2004246236A JP 2004246236 A JP2004246236 A JP 2004246236A JP 4507763 B2 JP4507763 B2 JP 4507763B2
- Authority
- JP
- Japan
- Prior art keywords
- cold forging
- soft nitriding
- hardness
- manufacturing
- cold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
C Si Mn Cr Al
SAC72 0.15 − 0.7 1.0 適量
SAC73 0.20 適量 0.9 1.0 適量
C:0.10〜0.40%、Si:0.0.10〜0.70%、Mn:0.20〜1.50%、Cr:0.50〜2.50%、V:0.05〜0.60%、残部が実質的にFe。
1)一次均熱:900±15℃に加熱
2)中間冷却:10℃/秒以下の速度で冷却
3)二次均熱:680±30℃に加熱
冷間鍛造により部品形状を与え、500〜600℃におけるガス軟窒化により表面を硬化させることからなる。
合金組成:
C Si Mn P S Cu Ni Cr s-Al V
0.20 0.10 0.81 0.012 0.015 0.12 0.11 1.03 0.11 0.20
歯車用鍛造素材:
外径:140mm 内径:1040mm 厚さ:30mm
No. 一次処理 二次処理 硬さ(HV)
1)900℃×1時間 → 650℃×1時間 205
2)900℃×1時間 → 650℃×4時間 202
3)900℃×1時間 → 680℃×4時間 189
4)900℃×1時間→風冷、ついで650℃×1時間 190
5)930℃×1時間→風冷、ついで650℃×1時間 200
6)950℃×1時間→風冷、ついで650℃×1時間 243
No. 一次処理 二次処理 硬さ(HV) 平均 σ
7)900℃×1時間→680℃×1時間 150〜170 155 2.5
8)900℃×1時間→650℃×2.5時間 150〜157 152 1.7
9)900℃×1時間→680℃×4時間 148〜157 151 1.2
Claims (3)
- 冷間鍛造−軟窒化により機械部品を製造する方法であって、重量%で、C:0.15〜0.30%、Si:0.2%以下、Mn:0.4〜1.5%、Cr:0.6〜1.5%、s−Al:0.05〜0.20%およびV:0.05〜0.30%を含有し、残部がFeおよび不可避の不純物からなる合金組成を有する窒化鋼を、これを下記の条件で熱処理したのち
1)一次均熱:900±15℃に加熱
2)中間冷却:10℃/秒以下の速度で冷却
3)二次均熱:680±30℃に加熱
冷間鍛造により部品形状を与え、500〜600℃におけるガス軟窒化により表面を硬化させることからなる製造方法。 - 材料とする窒化鋼が、重量%で、C:0.18〜0.22%、Si:0.05〜0.15%、Mn:0.55〜0.90%、Cr:0.90〜1.10%、s−Al:0.10〜0.15%およびV:0.18〜0.23%を含有し、P:0.03%以下、Cu:0.3%以下およびNi:0.25%であって、残部がFeおよび不可避の不純物からなる合金組成を有する冷鍛軟窒化歯車用鋼であり、製造される部品が歯車である請求項1の製造方法。
- 材料とする窒化鋼が、請求項1または2に規定した合金成分に加えて、重量%で、S:0.01〜0.02%を含有する合金組成を有する請求項1または2の製造方法。