JP4470467B2 - 粒子状人造黒鉛負極材料及びその製造方法、並びにそれを用いたリチウム二次電池用負極及びリチウム二次電池 - Google Patents
粒子状人造黒鉛負極材料及びその製造方法、並びにそれを用いたリチウム二次電池用負極及びリチウム二次電池 Download PDFInfo
- Publication number
- JP4470467B2 JP4470467B2 JP2003399256A JP2003399256A JP4470467B2 JP 4470467 B2 JP4470467 B2 JP 4470467B2 JP 2003399256 A JP2003399256 A JP 2003399256A JP 2003399256 A JP2003399256 A JP 2003399256A JP 4470467 B2 JP4470467 B2 JP 4470467B2
- Authority
- JP
- Japan
- Prior art keywords
- negative electrode
- graphite
- electrode
- secondary battery
- lithium secondary
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
また、本発明の粒子状人造黒鉛負極材料の製造方法によれば、上記の粒子状人造黒鉛負極材料を効率よく安定して製造することができるため、工業上非常に有用である。
本発明の粒子状人造黒鉛負極材料(以下、適宜「本発明の黒鉛材料」という)は、粒子状の人造黒鉛からなる負極材料であって、(a)タップ密度が1.15g/cm3以上であり、(b)X線回折による(002)面の面間隔d002が0.3360nm以下であり、(c)この負極材料を活物質として電極密度1.63±0.05g/cm3で形成した電極の活物質配向比が0.04以上0.20以下であり、且つ、(d)この負極材料を用いて作製したリチウム二次電池の放電容量が345mAh/g以上であることを特徴とする。
本発明の黒鉛材料は、そのタップ密度が、通常1.15g/cm3以上、好ましくは1.18g/cm3以上、また、通常1.6g/cm3以下、好ましくは1.5g/cm3以下である。タップ密度がこの範囲を下回ると、活物質の充填密度を上がり難く、高容量の電池が得難い。一方、この範囲を上回ると、電極中の気孔量が少なくなり、好ましい電池特性が得られ難い。
本発明の黒鉛材料は、X線回折により測定した(002)面の面間隔d002が、通常0.3360nm以下、好ましくは0.3358nm以下である。この範囲を上回る場合、即ち、結晶性が劣る場合には、電極を製造したときに活物質の単位重量当たりの放電容量が小さくなる虞がある。一方、前記の面間隔d002の下限は、理論的限界として通常0.3354nm以上である。
上記のX線回折により測定した面間隔d002及び結晶子の大きさLc004としては、炭素材料学会の学振法に従って測定される値を用いることができる。なお、学振法においては、100nm(1000Å)以上の値は区別されず、すべて「>1000(Å)」と記述される。
本発明の黒鉛材料は、その体積基準平均粒径が、通常5μm以上、好ましくは10μm以上、また、通常60μm以下、好ましくは30μm以下である。この範囲を下回ると、タップ密度が小さくなってしまうため、電極を製造したときに活物質の充填密度が上がり難く、高容量の電池を得難い。一方、この範囲を上回ると、塗布により電極を製造する時に塗工むらが生じ易い。
本発明の黒鉛材料を活物質として、電極密度が1.63±0.05g/cm3、即ち、1.58g/cm3以上1.68g/cm3以下の範囲内となるように形成した電極の活物質配向比は、通常0.04以上、好ましくは0.07以上、また、通常0.20以下、好ましくは0.16以下である。前記範囲を下回ると、電池を作製したときの電池充電時の電極膨張が大きくなり、電極の単位体積当たりの電池容量を大きくできない虞がある。一方、前記範囲を上回ると、電池を作製したときの活物質の結晶性が低くなり、電池の放電容量を大きくできないか、又は、プレス後の電極の充填密度を上げ難い。
(1)電極の形成:
黒鉛材料と、増粘剤としてCMC(カルボキシメチルセルロース)水溶液と、バインダ樹脂としてSBR(スチレンブタジエンゴム)水溶液とを、黒鉛材料とCMCとSBRとの混合物の乾燥後の総重量に対して、CMC及びSBRがそれぞれ1重量%になるように混合撹拌し、スラリーとする。次いで、ドクターブレードを用いて18μm厚さの銅箔上にスラリーを塗布する。塗布厚さは、乾燥後の電極目付(銅箔を除く)が10mg/cm2になるようにギャップを選択する。この電極を80℃で乾燥した後、電極密度(銅箔を除く)が1.63±0.05g/cm3になるようにプレスを行なう。
プレス後の電極について、X線回折により電極の活物質配向比を測定する。具体的手法は特に制限されないが、標準的な方法としては、X線回折により黒鉛の(110)面と(004)面とのチャートを測定し、測定したチャートについて、プロファイル関数として非対称ピアソンVIIを用いてフィッティングすることによりピーク分離を行ない、(110)面と(004)面のピークの積分強度を算出する。得られた積分強度から、(110)面積分強度/(004)面積分強度で表わされる比率を算出し、電極の活物質配向比と定義する。
ターゲット: Cu(Kα線)グラファイトモノクロメーター
スリット : 発散スリット=1度、受光スリット=0.1mm、散乱スリット=1度
測定範囲、及び、ステップ角度/計測時間:
(110)面 : 76.5度≦2θ≦78.5度 0.01度/3秒
(004)面 : 53.5度≦2θ≦56.0度 0.01度/3秒
試料調整 : 硝子板に0.1mm厚さの両面テープで電極を固定
本発明の黒鉛材料は、これを活物質として集電体上に活物質層を形成し、リチウム二次電池用負極として使用した場合に、そのリチウム二次電池の放電容量が、通常345mAh/g以上、好ましくは350mAh/g以上となる。放電容量がこの範囲を下回ると、電池容量の低下が生じる虞がある。また、放電容量は高ければ高い方が好ましいが、その上限は通常365mAh/g程度である。
まず、黒鉛材料を用いた電極を作製する。電極は、集電体として銅箔を用い、この集電体に活物質層を形成することにより作製する。活物質層は、黒鉛材料と、バインダ樹脂としてスチレンブタジエンゴム(SBR)とを混合したものを用いる。バインダ樹脂の量は、電極の重量に対して1重量%とする。また、電極密度は1.45g/cm3〜1.95g/cm3とする。
2極式コインセルの電解液は任意であるが、例えば、エチレンカーボネート(EC)とジエチルカーボネート(DEC)とを、体積比でDEC/EC=1/1となるように混合した混合液、又は、エチレンカーボネートとエチルメチルカーボネート(EMC)とを、体積比でEMC/EC=1/1となるように混合した混合液を用いることができる。
また、2極式コインセルに用いるセパレータも任意であるが、例えば、厚さ15μm〜35μmのポリエチレンシートを用いることができる。
本発明の黒鉛材料のBET比表面積は、特に制限されないが、通常は0.2m2/g以上、好ましくは0.3m2/g以上、特に好ましくは0.6m2/g以上、また、通常は10m2/g以下、好ましくは5m2/g以下、特に好ましくは2.5m2/g以下の範囲である。BET比表面積の値が前記範囲の下限を下回ると、充電時にリチウムの受け入れ性が悪くなり易く、リチウムが電極表面で析出し易くなるため、安全上好ましくない。一方、前記範囲の上限を上回ると、電解液との反応性が増加し、ガス発生が多くなり易く、好ましい電池が得られにくい。
本発明の黒鉛材料の製造方法は特に制限されないが、例えば、以下に挙げる2つの製造方法(以下、適宜「第1の製造方法」「第2の製造方法」等という。これらを区別せずに呼ぶ場合には、「本発明の製造方法」等と略称する。)によって得ることができる。目標とする電池性能や製造コストなどに応じて、いずれの製造方法を採用しても良い。
以下、第1及び第2の製造方法について、それぞれ詳細に説明する。
第1の製造方法は、キノリン不溶分が0.1重量%以下であるピッチ原料を、400℃以上550℃以下で熱処理した後、粉砕し、450℃以上600℃以下で再熱処理し、再粉砕し、焼成し、黒鉛化することを特徴とする。
即ち、第1の製造方法は、キノリン不溶分が特定量以下に低減されたピッチ原料を選択するとともに、粒子内の黒鉛結晶前駆体の配向を乱す様な処理を加えることにより、これまでに得られなかった黒鉛材料の配向性と高結晶性を同時に実現するものである。
本明細書においてピッチ原料とは、ピッチ及びそれに順ずるものであり、適当な処理を行なうことによって黒鉛化することができるものをいう。具体的なピッチ原料の例としては、タールや重質油やピッチなどを用いることができる。タールの具体例としては、コールタール、石油系タールなどが挙げられる。重質油の具体例としては、石油系重質油の接触分解油、熱分解油、常圧残油、減圧残油などが挙げられる。また、ピッチの具体例としては、コールタールピッチ、石油系ピッチ、合成ピッチなどが挙げられる。これらの中でもコールタールピッチが芳香族性に高く好ましい。これらのピッチ原料は、何れか1種を単独で用いても良く、2種以上を任意の組み合わせ及び比率で併用しても良い。
なお、本発明の効果を妨げない限り、原料として上述のピッチ原料に加え、各種の熱硬化性樹脂、熱可塑性樹脂等を併用してもよい。
まず、選択したピッチ原料に熱処理を施し、黒鉛結晶の前駆体であるバルクメソフェーズ(熱処理した黒鉛結晶前駆体。以下適宜、「熱処理黒鉛結晶前駆体」という)を得る。この熱処理黒鉛結晶前駆体を粉砕後、再熱処理する際に、その一部又は全部が溶融するが、ここで熱処理によって揮発分の含量を調整しておくことにより、その溶融状態を適切に制御することができる。なお、熱処理黒鉛結晶前駆体に含まれる揮発分としては、通常、水素、ベンゼン、ナフタレン、アントラセン、ピレン等が挙げられる。
なお、熱処理の温度及び累積時間が前記の範囲内であれば、複数回に分けて熱処理を行なってもよい。
熱処理に用いる装置としては特に制限はないが、例えば、シャトル炉、トンネル炉、電気炉、オートクレーブ等の反応槽、コーカー(コークス製造の熱処理槽)などを用いることができる。
熱処理時には、必要に応じて攪拌を行なってもよい。
次に、熱処理によって得られた黒鉛結晶前駆体を粉砕する。熱処理により大きな単位で同一方向に並びかけている黒鉛結晶前駆体の結晶を微細化するためである。
次に、粉砕により微細化した黒鉛結晶前駆体に再熱処理を施す。粉砕した黒鉛結晶前駆体を再溶融又は融着することにより、微細化した黒鉛結晶前駆体粒子が無配向状態で接触したまま固定化するためである。
再熱処理に用いる装置に特に制限はないが、例えば、シャトル炉、トンネル炉、電気炉などを用いることができる。
ところで、上記の粉砕及び再熱処理の代替処理として、黒鉛結晶前駆体の組織を微細化、無配向化することが可能な処理、例えば、熱処理した黒鉛結晶前駆体が溶融若しくは軟化する様な温度領域で機械的エネルギーを付与する処理を行ないながら再熱処理を行なうことも可能である。
この代替処理としての再熱処理は、通常200℃以上、好ましくは250℃以上、また、通常450℃以下、好ましくは400℃以下で行なう。温度条件が前記範囲を下回ると代替処理中の黒鉛結晶前駆体の溶融、軟化が不十分であり、配向を乱し難くなる。また、上回ると熱処理が急速に進み易く、粉砕時に粒子が針状に割れ、タップ密度の低下を招き易い。
また、その処理時間は、通常30分以上、好ましくは1時間以上、また、通常24時間以下、好ましくは10時間以下で行なう。処理時間が前記範囲を下回ると代替処理をした黒鉛結晶前駆体が不均一となり、製造上好ましくない。また、上回ると生産性が悪く、処理費用が高くなり好ましくない。
また、代替処理に用いる装置としては特に制限はないが、例えば、ミキサー、ニーダー等を用いることができる。
次に、再熱処理を行なった黒鉛結晶前駆体を再粉砕する。再熱処理により組織が微細化、無配向化した状態で溶融又は融着した黒鉛結晶前駆体の塊を、粉砕により目的の粒子径にするためである。
再粉砕後の黒鉛結晶前駆体の粒度は、通常5μm以上、好ましくは10μm以上、また、通常60μm以下、好ましくは30μm以下とする。粒度が前記範囲を下回ると、タップ密度が小さくなってしまうため、電極とした場合に活物質の充填密度が上がり難く、高容量の電池を得難い。一方、前記範囲を上回ると、塗布により電極を作製するときに塗工むらが生じ易く好ましくない。
次に、再粉砕により粉砕された黒鉛結晶前駆体を焼成する。黒鉛化時の黒鉛結晶前駆体粒子の融着を抑制するべく、焼成により黒鉛結晶前駆体の揮発分を除去するためである。
焼成を行なう際の温度条件は、通常600℃以上、好ましくは1000℃以上、また、通常1500℃以下、好ましくは1300℃以下である。温度条件が前記範囲を下回ると、黒鉛化時に黒鉛結晶前駆体が粉体の融着を起こし易く好ましくない。一方、前記範囲を上回ると、焼成設備に費用が掛かるため好ましくない。
焼成を行なう時に、温度条件を上記範囲に保持する保持時間は特に制限されないが、通常30分以上、72時間以下である。
焼成に用いる装置としては特に制限はないが、例えば、シャトル炉、トンネル炉、電気炉、リードハンマー炉、ロータリーキルン等を用いることができる。
次に、焼成を行なった黒鉛結晶前駆体に黒鉛化を施す。電池評価での放電容量を大きくするために、結晶性を向上させるためである。黒鉛化により、本発明の黒鉛材料を得ることができる。
黒鉛化を行なう際の温度条件は、通常2800℃以上、好ましくは3000℃以上、また、通常3200℃以下、好ましくは3100℃以下である。前記範囲を上回ると、電池の可逆容量が小さくなる虞があり、高容量な電池を作り難い。また、前記範囲を上回ると、黒鉛の昇華量が多くなり易く好ましくない。
黒鉛化を行なう時に保持時間は特に制限されないが、通常0分よりも長い時間であり、24時間以下である。
黒鉛化に使用する装置としては特に制限はないが、例えば、直接通電炉、アチソン炉、間接通電式として抵抗加熱炉、誘導加熱炉等が挙げられる。
その他、発明の効果が妨げられない限りにおいて、上記の各処理に加え、分級処理等の各種の処理を行なうことができる。分級処理は、黒鉛化処理後の粒度を目的の粒径にするべく、粗粉や微粉を除去するためのものである。
分級処理に用いる装置としては特に制限はないが、例えば、乾式篩い分けの場合:回転式篩い、動揺式篩い、旋動式篩い、振動式篩い、乾式気流式分級の場合:重力式分級機、慣性力式分級機、遠心力式分級機(クラシファイア、サイクロン等)、湿式篩い分け、機械的湿式分級機、水力分級機、沈降分級機、遠心式湿式分級機等を用いることができる。
続いて、第2の製造方法について詳細に説明する。
第2の製造方法は、キノリン不溶分が0.4重量%以上2.5重量%以下であり、かつ、トルエン不溶分が6重量%以上15重量%以下であるピッチ原料を、450℃以上600℃以下で熱処理した後、粉砕し、焼成し、黒鉛化することを特徴とする。
また、第2の製造方法では、第1の製造方法とは異なり、再熱処理を行なわない。その理由としては、第2の製造方法では、キノリン不溶分及びトルエン不溶分が前記特定な範囲に限定されたピッチ原料を選択し、450℃〜600℃で熱処理を行なうため、熱処理によって得られる黒鉛結晶前駆体中の揮発分及びトルエン可溶分の量が適度な範囲にあり、焼成、黒鉛化時に融着を起こさないので、再熱処理の必要はないからである。
原料としては、第1の製造方法と同様の種類のピッチ原料を使用することができる。ピッチ原料は1種を単独で用いても良く、2種以上を任意の組み合わせ及び比率で併用しても良い。
まず、選択したピッチ原料に熱処理を施し、黒鉛結晶前駆体であるバルクメソフェーズ(熱処理黒鉛結晶前駆体)を得る。この熱処理黒鉛結晶前駆体を粉砕後、再熱処理する際に、その一部又は全部が溶融するが、この熱処理によって揮発分の含量を調整しておくことにより、その溶融状態を適切に制御することができる。
なお、熱処理の温度及び累積時間が前記の範囲内であれば、複数回に分けて熱処理を行なってもよい。
熱処理に用いる装置として制限はないが、例えば、シャトル炉、トンネル炉、電気炉、オートクレーブ等の反応槽、コーカー(コークス製造の熱処理槽)などを用いることができる。
熱処理時には、必要に応じて攪拌を行なってもよい。
また、得られる黒鉛結晶前駆体中のトルエン可溶分は、通常0%以上、また、通常10以下、好ましくは3%以下とする。トルエン可溶分が多過ぎると、焼成時に融着を起こし易く好ましくない。
次に、熱処理により得られた、微細化及び無配向化された結晶構造を有する黒鉛結晶前駆体の塊を、粉砕により目的の粒子径にする。
粉砕後の黒鉛結晶前駆体の粒度は、通常5μm以上、好ましくは10μm以上、また、通常60μm以下、好ましくは30μm以下となるようにする。粒度が前記範囲を下回ると、タップ密度が小さくなってしまうため、電極とした場合に活物質の充填密度が上がり難く、高容量の電池を得難い。一方、前記範囲を上回ると、塗布によって電極を作製する時に塗工むらが生じ易く、好ましくない。
次に、粉砕した黒鉛結晶前駆体から揮発分を除去するべく、通常は焼成を行なう。その条件は、第1の製造方法における再粉砕後の焼成の条件と同様である。また、製造工程の簡略化のため、焼成工程を組み込まずに、直接黒鉛化を行なうことも可能である。
続いて、第1の製造方法と同様の条件で、黒鉛化を行なう。この黒鉛化により、本発明の黒鉛材料を得ることができる。
その他、発明の効果が妨げられない限りにおいて、上記の処理に加え、第1の製造方法と同様に、分級処理等の各種の処理を行なうことができる。
上記2つの製造方法(本発明の製造方法)によって、従来は得られなかった特定の配向性と高結晶性と高タップ密度と大きな放電容量とを同時に実現することができ、上に説明した黒鉛材料(本発明の黒鉛材料)を効率的に製造することができる。
特に、高タップ密度が達成されるメカニズムについては明らかではないが、粉砕前の熱処理温度を最適化し、それによって熱処理後の黒鉛結晶前駆体の揮発分含有量(VM)を適切な値とすることで、熱処理によって得られる黒鉛結晶前駆体が塊状に粉砕されるために、タップ密度を向上させることができるものと推測される。
また、原料ピッチ中のキノリン不溶分が少ないほど、得られる黒鉛材料は高結晶性となるが、電極に用いたときの配向比が低下する傾向がある。第1の製造方法は、再熱処理等の工程を加えることによって、また、第2の製造方法は、キノリン不溶分等の含有量が特定の範囲にある原料ピッチを用いることによって、得られる黒鉛材料の結晶性と電極配向比とのバランスを最適化したものといえる。
また、本発明の第1及び第2の製造方法によれば、上記の特性を有する本発明の黒鉛材料を、効率よく安定して製造することができる。
本発明の黒鉛材料を活物質として含有する活物質層を集電体上に形成することにより、リチウム二次電池用負極を作製することができる。
負極の製造は、常法にしたがって製造すればよい。例えば、負極活物質に、結着剤、増粘剤、導電材、溶媒等を加えてスラリー状とし、集電体に塗布し、乾燥した後にプレスして高密度化する方法が挙げられる。
また、本発明の黒鉛材料に加えて、他の活物質を併用して用いることもできる。
本発明の黒鉛材料は、電池の電極の材料として有用である。特に、リチウムイオンを吸蔵・放出可能な正極及び負極、ならびに電解液を備えたリチウム二次電池電池などの非水系二次電池において、上記負極として、上述した本発明の黒鉛材料を用いることは、極めて有用である。例えば、上記の方法にしたがって製造した粒子状人造黒鉛負極材料を負極として使用し、通常使用されるリチウム二次電池用の金属カルコゲナイド系正極及びカーボネート系溶媒を主体とする有機電解液を組み合わせて構成した非水系二次電池は、容量が大きく、初期サイクルに認められる不可逆容量が小さく、急速充放電容量が高く、またサイクル特性が優れ、高温下での放置における電池の保存性及び信頼性も高く、高効率放電特性及び低温における放電特性に極めて優れたものである。
電解液としては、例えば、非水系溶媒に溶質を溶解したものを用いることができる。溶質としては、アルカリ金属塩や4級アンモニウム塩などを用いることができる。具体的には、LiClO4、LiPF6、LiBF4、LiCF3SO3、LiN(CF3SO2)2、LiN(CF3CF2SO2)2、LiN(CF3SO2)(C4F9SO2)、LiC(CF3SO2)3からなる群から選択される1以上の化合物を用いるのが好ましい。
リチウム二次電池には、電解液、負極、正極の他に、必要に応じて、外缶、セパレータ、ガスケット、封口板、セルケースなどを用いることもできる。
リチウム二次電池の製造方法の例を挙げると、外缶上に負極を乗せ、その上に電解液とセパレータを設け、さらに負極と対向するように正極を乗せて、ガスケット、封口板と共にかしめて電池にすることができる。
電池の形状は特に制限されず、例えば、シート電極及びセパレータをスパイラル状にしたシリンダータイプ、ペレット電極及びセパレータを組み合わせたインサイドアウト構造のシリンダータイプ、ペレット電極及びセパレータを積層したコインタイプ等にすることができる。
キノリン不溶分が0.05重量%以下のコールタールピッチを、反応炉にて460℃で10時間熱処理し、溶融性のある塊状の熱処理黒鉛結晶前駆体(バルクメソフェーズ)を得た。得られた塊状の熱処理黒鉛結晶前駆体を、中間粉砕機(セイシン企業社製オリエントミル)を用いて粉砕し、メジアン径65μm、モード径150μmの微細化した黒鉛結晶前駆体粉末を得た。なお、メジアン径及びモード径は、界面活性剤であるポリオキシエチレン(20)ソルビタンモノラウレートの2体積%水溶液(約1ml)を、微細化した黒鉛結晶前駆体粉末に混合し、イオン交換水を分散媒としてレーザー回折式粒度分布計(堀場製作所社製LA−700)を用いて体積基準で測定した値を用いた。
この固化した黒鉛結晶前駆体の塊を粗砕機(吉田製作所製ロールジョークラッシャー)で再粉砕、更に微粉砕機(マツボー社製ターボミル)を用いて微粉砕した後、風力式分級機(セイシン企業社製OMC−100)を用いて分級し、メジアン径19μm、モード径19μmの粉末を得た。
更に、焼成した粉末を黒鉛坩堝に移し替え、直接通電炉を用いて3000℃で5時間かけて黒鉛化し、粒子状人造黒鉛負極材料(実施例1の黒鉛材料)を得た。
また、X線回折法にてその結晶性を測定したところ、d002=0.3358nm、Lc004>1000Å(100nm)であった。
更に、実施例1の黒鉛材料を用いて、下記の方法に従ってリチウム二次電池を作製し、放電容量の測定を行なった。また、同様にリチウム二次電池を作製し、充電状態で解体して電極の厚みを測定することにより、充電膨張率の測定を行なった。結果を表1に示す。
黒鉛材料と、増粘剤としてCMC水溶液と、バインダ樹脂としてSBR水溶液とを、乾燥後の黒鉛材料に対してCMC及びSBRがそれぞれ1重量%になるように混合撹拌してスラリーとし、ドクターブレードを用いて銅箔上にこのスラリーを塗布した。塗布厚さは、乾燥後の電極目付(銅箔除く)が10mg/cm2になるようにギャップを選択した。
上記の電極作製方法で作製した電極を110℃で真空乾燥した後、グローブボックスへ移し、アルゴン雰囲気下で、電解液としてエチレンカーボネート(EC)/ジエチルカーボネート(DEC)=1/1の混合液を溶媒とした1M−LiPF6電解液と、セパレータとしてポリエチレンセパレータと、対極としてリチウム金属対極とを用い、コイン電池(リチウム二次電池)を作製した。
0.2mA/cm2の電流密度でリチウム対極に対して5mVまで充電し、更に、5mVの一定電圧で電流値が0.02mAになるまで充電し、負極中にリチウムをドープした後、0.4mA/cm2の電流密度でリチウム対極に対して1.5Vまで放電を行なう充放電サイクルを3サイクル繰り返し、3サイクル目の放電値を放電容量として測定した。
放電容量の測定において3サイクル充放電後、4サイクル目の充電終止条件を300mAh/gの定容量充電で行なった。充電状態のコイン電池をアルゴングローブボックス中で短絡させないように解体し、電極を取り出して、充電時の電極の厚み(銅箔除く)を測定した。電池作製前のプレス電極の厚み(銅箔除く)を基準として、次式に基づいて充電膨張率を求めた。
(充電電極厚み−プレス電極厚み)/プレス電極厚み×100=充電膨張率(%)
実施例1と同様の手順で得られた溶融性のある塊状の熱処理黒鉛結晶前駆体を、粗砕機(吉田製作所製ロールジョークラッシャー)で粉砕後、粉砕機(マツボー社製ターボミル)を用いて粉砕し、メジアン径20μm、モード径24μmの微細化した黒鉛結晶前駆体粉末を得た。その後は実施例1と同様の手順で再熱処理以降の処理を行ない、粒子状人造黒鉛負極材料(実施例2の黒鉛材料)を得た。
また、実施例2の黒鉛材料を用いて、実施例1と同様の手順で電極を作製し、電極の活物質配向比を求めたところ、0.09であった。
更に、実施例2の黒鉛材料を用いて、実施例1と同様の手順でリチウム二次電池を作製し、放電容量及び充電膨張率の測定を行なった。結果を表1に示す。
キノリン不溶分が2重量%、トルエン不溶分が9.5重量%のコールタールピッチを、反応炉にて500℃で10時間熱処理し、溶融性の無い塊状の熱処理黒鉛結晶前駆体を得た。
この塊状の熱処理黒鉛結晶前駆体を粗砕機で粉砕し、更に微粉砕機を用いて微粉砕した後、風力式分級機を用いて分級し、メジアン径19μm、モード径19μmの粉末を得た。
更に、焼成した粉末を黒鉛坩堝に移し替え、直接通電炉を用いて3000℃で5時間かけて黒鉛化し、粒子状人造黒鉛負極材料(実施例3の黒鉛材料)を得た。
また、実施例3の黒鉛材料を用いて、実施例1と同様の手順で電極を作製し、電極の活物質配向比を求めたところ、0.12であった。
更に、実施例3の黒鉛材料を用いて、実施例1と同様の手順でリチウム二次電池を作製し、放電容量及び充電膨張の測定を行なった。結果を表1に示す。
キノリン不溶分が10重量%のコールタールピッチを、反応炉にて460℃で10時間熱処理し、溶融性のある塊状の熱処理黒鉛結晶前駆体を得た。その後は実施例1と同様の方法で粉砕、再熱処理、再粉砕、焼成、黒鉛化を行ない、粒子状人造黒鉛負極材料(比較例1の黒鉛材料)を得た。
また、比較例1の黒鉛材料を用いて、実施例1と同様の手順で電極を作製し、電極の活物質配向比を求めたところ、0.28であった。
更に、比較例1の黒鉛材料を用いて、実施例1と同様の手順でリチウム二次電池を作製し、放電容量及び充電膨張の測定を行なった。結果を表1に示す。
実施例1の黒鉛材料の製造手順において、熱処理の際の温度を500℃にし、熱処理によって溶融性の無い塊状の熱処理黒鉛結晶前駆体を得た後、その熱処理黒鉛結晶前駆体に対して再熱処理を行なわずに粉砕と再粉砕とをまとめて行ない、更に分級して、メジアン径22μm、モード径24μmの粉末を得た他は、実施例1と同様の手順により粒子状人造黒鉛負極材料(比較例2の黒鉛材料)を得た。
また、比較例2の黒鉛材料を用いて、実施例1と同様の手順で電極を作製し、活物質配向比を求めたところ、0.02であった。
更に、比較例2の黒鉛材料を用いて、実施例1と同様の手順でリチウム二次電池を作製し、放電容量及び充電膨張の測定を行なった。結果を表1に示す。
実施例1の黒鉛材料の製造手順において、塊状の熱処理黒鉛結晶前駆体を粉砕する際に、粗砕機で3〜10cmに粉砕した他は、実施例1と同様の手順により粒子状人造黒鉛負極材料(比較例3の黒鉛材料)を得た。
また、比較例3の黒鉛材料を用いて、実施例1と同様の手順にて電極を作製し、活物質配向比を求めたところ、0.03であった。
更に、比較例3の黒鉛材料を用いて、実施例1と同様の手順でリチウム二次電池を作製し、放電容量及び充電膨張の測定を行なった。結果を表1に示す。
キノリン不溶分が5重量%、トルエン不溶分が12重量%のコールタールピッチを、反応炉にて、500℃で10時間熱処理し、溶融性の無い塊状の熱処理黒鉛結晶前駆体を得た。この塊状の熱処理黒鉛結晶前駆体を用いて、実施例3と同様の手順で粉砕処理以降の各処理を行ない、粒子状人造黒鉛負極材料(比較例4の黒鉛材料)を得た。
また、比較例4の黒鉛材料を用いて、実施例1と同様の手順にて電極を作製し、電極の活物質配向比を求めたところ、0.16であった。
更に、比較例4の黒鉛材料を用いて、実施例1と同様の手順にてリチウム二次電池を作製し、放電容量及び充電膨張の測定を行なった。結果を表1に示す。
Claims (6)
- 粒子状の人造黒鉛からなる負極材料であって、
(a)タップ密度が1.15g/cm3以上であり、
(b)X線回折による(002)面の面間隔d002が0.3360nm以下であり、
(c)該負極材料を活物質として電極密度1.63±0.05g/cm3で形成した電極の活物質配向比が0.04以上0.20以下であり、且つ、
(d)該負極材料を用いて作製したリチウム二次電池の放電容量が345mAh/g以上である
ことを特徴とする、粒子状人造黒鉛負極材料。 - キノリン不溶分が0.1重量%以下であるピッチ原料を、400℃以上550℃以下で熱処理した後、粉砕して粒度を1μm以上10mm以下とし、450℃以上600℃以下で再熱処理し、再粉砕し、焼成し、黒鉛化する
ことを特徴とする、粒子状人造黒鉛負極材料の製造方法。 - キノリン不溶分が0.4重量%以上2.5重量%以下であり、かつ、トルエン不溶分が6重量%以上15重量%以下であるピッチ原料を、450℃以上600℃以下で熱処理した後、粉砕し、焼成し、黒鉛化する
ことを特徴とする、粒子状人造黒鉛負極材料の製造方法。 - 集電体と、該集電体上に形成された活物質層とを備えるとともに、
該活物質層が、請求項1記載の粒子状人造黒鉛負極材料を含有する
ことを特徴とする、リチウム二次電池用負極。 - 集電体と、該集電体上に形成された活物質層とを備えるとともに、
該活物質層が、請求項2又は請求項3に記載の製造方法によって製造された粒子状人造黒鉛負極材料を含有する
ことを特徴とする、リチウム二次電池用負極。 - リチウムイオンを吸蔵・放出可能な正極及び負極、ならびに電解質を備えるとともに、
該負極が、請求項4又は請求項5に記載のリチウム二次電池用負極である
ことを特徴とする、リチウム二次電池。