JP4101180B2 - 変性水添共重合体 - Google Patents
変性水添共重合体 Download PDFInfo
- Publication number
- JP4101180B2 JP4101180B2 JP2003573039A JP2003573039A JP4101180B2 JP 4101180 B2 JP4101180 B2 JP 4101180B2 JP 2003573039 A JP2003573039 A JP 2003573039A JP 2003573039 A JP2003573039 A JP 2003573039A JP 4101180 B2 JP4101180 B2 JP 4101180B2
- Authority
- JP
- Japan
- Prior art keywords
- hydrogenated copolymer
- modified hydrogenated
- weight
- copolymer
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
発明の優れた変性水添共重合体を用いた変性水添共重合体組成物は、引張特性、耐磨耗性等に優れた組成物である。本発明の変性水添共重合体及び変性水添共重合体組成物は、発泡体、各種成形品、建築材料、制振・防音材料及び電線被覆材料などとして有利に用いることができる。
一方、共役ジエンとビニル芳香族炭化水素からなるブロック共重合体の水素添加物は、加硫をしなくても加硫した天然ゴムや合成ゴムと同様の弾性を常温にて有し、しかも高温では熱可塑性樹脂と同様の加工性を有することから、プラスチックの改質、粘接着剤、自動車部品や医療器具等の分野で広く利用されている。近年、かかる特性に似た特性を共役ジエン化合物とビニル芳香族炭化水素からなるランダム共重合体で発現させる試みがなされている。
上記のような水添ジエン系共重合体に関しては、軟質塩化ビニル樹脂が従来用いられているような用途に用いることが試みられている。軟質塩化ビニル樹脂には、燃焼時におけるハロゲンの問題、可塑剤による環境ホルモンの問題等の環境問題があり、その代替材料の開発が急務である。しかし、上記のような水添ジエン系共重合体は、軟質塩化ビニル樹脂が従来用いられているような用途に用いるには、反発弾性,耐傷付き性や耐磨耗性といった特性が不十分であった。
また、上記のような水添ジエン系共重合体を、各種熱可塑性樹脂やゴム状物質と組み合わせて成形材料として使用する場合においても、機械的強度や耐磨耗性の改良が望まれていた。
上記のように、様々な環境上の問題が指摘されている軟質塩化ビニル樹脂の代替材料の開発が急務であるにも関わらず、軟質塩化ビニル樹脂に匹敵する特性(柔軟性や耐傷付き性等)の材料が得られていないのが現実であった。
さらに、塩化ビニル樹脂、及びその代替のために開発されてきた上記の従来の材料は、他の樹脂や金属類との接着性に乏しいという欠点も有しており、その改良が望まれていた。
従って、本発明の1つの目的は、柔軟性に富み、反発弾性と耐傷付き性,耐磨耗性、取り扱い性(耐ブロッキング性)に優れ、且つ他の樹脂や金属等との接着性が良好な変性水添共重合体を提供することにある。
本発明の他の1つの目的は、上記変性水添共重合体を他の熱可塑性樹脂及び/又はゴム状重合体とブレンドして得られる、引張特性、耐磨耗性等に優れた変性水添共重合体組成物を提供することにある。
本発明の上記及びその他の諸目的、諸特徴ならびに諸利益は、添付の図面を参照しながら行う以下の詳細な説明及び請求の範囲の記載から明らかになる
1.共役ジエン単量体単位とビニル芳香族単量体単位とを含む非水添共重合体を水添して得られ、該ビニル芳香族単量体単位の重合体ブロック(H)を少なくとも1つ含有する水添共重合体と、
該水添共重合体に結合した、官能基含有変性剤基、
からなる変性水添共重合体であって、下記式(I)〜式(V)よりなる群から選ばれる式で表される、下記の(1)〜(4)の特性を有することを特徴とする変性水添共重合体。
(2) 該重合体ブロック(H)の含有量が、該非水添共重合体の重量に対して、0.1重量%〜40重量%であり、
(3) 重量平均分子量が10万を越え、100万以下であり、
(4) 該共役ジエン単量体単位の二重結合の水添率が70%以上である。
Nは窒素原子、Siは珪素原子、Oは酸素原子、Cは炭素原子、Hは水素原子を表し、
P1は該水添共重合体を表し、
R1a、R1b、R3、R4、R8〜R10及びR13〜R15は各々独立に炭素数1〜48の炭化水素基を表し、且つ、所望により、各々独立に、水酸基、エポキシ基、アミノ基、シラノール基、炭素数1〜24のアルコキシシラン基よりなる群から選ばれる少なくとも1種の官能基を有してもよく、
R2、R11は各々独立に炭素数1〜48の炭化水素基を表し、
R5〜R7及びR12は各々独立に水素原子又は炭素数1〜48の炭化水素基を表し、
但し、R1a、R1b、R2〜R4及びR8〜R15には、所望により、各々独立に、水酸基、エポキシ基、アミノ基、シラノール基、アルコキシシラン基以外の結合様式で、酸素原子、窒素原子、硫黄原子、珪素原子よりなる群からから選ばれる少なくとも1種の原子が結合していてもよく、
k、l、m、oは各々独立に0以上の整数であり、但し、kとlは同時に0ではなく、nは1以上の整数である。
3.分子量分布が1.5〜5.0であることを特徴とする前項1に記載の変性水添共重合体。
4.式(I)で表される前項1に記載の変性水添共重合体。
5.式(II)で表される前項1に記載の変性水添共重合体。
6.式(III)で表される前項1に記載の変性水添共重合体。
7.式(IV)で表される前項1に記載の変性水添共重合体。
8.式(V)で表される前項1に記載の変性水添共重合体。
9.前項1〜3のいずれかに記載の変性水添共重合体からなる発泡体。
10.前項1〜3のいずれかに記載の変性水添共重合体からなる成形品。
11.前項1〜3のいずれかに記載の変性水添共重合体からなる多層フィルム又は多層シート。
12.押出成形、射出成形、中空成形、圧空成形、真空成形、発泡成形、複層押出成形、複層射出成形、高周波融着成形、スラッシュ成形及びカレンダー成形からなる群より選ばれる方法によって得られる前項1〜3のいずれかに記載の変性水添共重合体からなる成形品。
14.前項1〜3のいずれかに記載の変性水添共重合体からなる制振材料。
15.前項1〜3のいずれかに記載の変性水添共重合体からなる防音材料。
16.前項1〜3のいずれかに記載の変性水添共重合体からなる電線被覆材料。
17.前項1〜3のいずれかに記載の変性水添共重合体を、加硫剤の存在下で架橋することにより得られる架橋変性水添共重合体。
18.前項1〜3のいずれかに記載の変性水添共重合体である成分(a)の、成分(a)と成分(b)の合計100重量部に対して1〜99重量部、及び
該変性水添共重合体(a)以外の熱可塑性樹脂及び該変性水添共重合体(a)以外のゴム状重合体からなる群より選ばれる少なくとも1種の重合体である成分(b)の、成分(a)と成分(b)の合計100重量部に対して99〜1重量部
を包含する変性水添共重合体組成物。
19.前項18に記載の変性水添共重合体組成物からなる発泡体。
20.前項18に記載の変性水添共重合体組成物からなる成形品。
21.前項18に記載の変性水添共重合体組成物からなる多層フィルム又は多層シート。
22.押出成形、射出成形、中空成形、圧空成形、真空成形、発泡成形、複層押出成形、複層射出成形、高周波融着成形、スラッシュ成形及びカレンダー成形からなる群より選ばれる方法によって得られる、前項18に記載の変性水添共重合体組成物からなる成形品。
23.前項18に記載の変性水添共重合体組成物からなる建築材料。
24.前項18に記載の変性水添共重合体組成物からなる制振材料。
25.前項18に記載の変性水添共重合体組成物からなる防音材料。
26.前項18に記載の変性水添共重合体組成物からなる電線被覆材料。
27.前項18に記載の変性水添共重合体組成物を、加硫剤の存在下で架橋することにより得られる架橋変性水添共重合体組成物。
本発明において、重合体を構成する各単量体単位の命名は、該単量体単位が由来する単量体の命名に従っている。例えば、「ビニル芳香族単量体単位」とは、単量体であるビニル芳香族化合物を重合した結果生ずる、重合体の構成単位を意味し、その構造は、置換ビニル基に由来する置換エチレン基の二つの炭素が結合部位となっている分子構造である。また、「共役ジエン単量体単位」とは、単量体である共役ジエンを重合した結果生ずる、重合体の構成単位を意味し、その構造は、共役ジエン単量体に由来するオレフィンの二つの炭素が結合部位となっている分子構造である。
本発明の変性水添共重合体は、共役ジエン単量体単位とビニル芳香族単量体単位とを含む非水添共重合体を水添して得られた水添共重合体と、該水添共重合体に結合した、官能基含有変性剤基(官能基を少なくとも1個有する少なくとも1個の変性剤基)からなる変性水添共重合体である。本発明の変性水添共重合体のビニル芳香族単量体単位の含有量は、該水添共重合体の重量に対して、60重量%を越え、90重量%未満である。ビニル芳香族単量体単位の含有量が60重量%を越えると優れた耐傷付き性を発揮し、90重量%未満であると柔軟性や反発弾性が優れるのみならず、組成物とした場合の引張特性,耐磨耗性が優れる。好ましいビニル芳香族単量体単位の含有量は62〜88重量%、更に好ましくは64〜86重量%である。特に65〜80重量%が好ましい。尚、ビニル芳香族単
量体単位の含有量は、紫外分光光度計を用いて測定することができる。変性水添共重合体のビニル芳香族単量体単位の含有量は、水素添加前の共重合体(非水添共重合体)中のビニル芳香族単量体単位含有量を測定してもかまわない。また、ビニル芳香族単量体単位含有量の測定を行うのは、共重合体の変性の前でも後でもよい。
ビニル芳香族重合体ブロック(H)の含有量(重量%)=(水素添加前の共重合体中のビニル芳香族重合体ブロック(H)の重量/水素添加前の共重合体の重量)×100
ビニル芳香族重合体ブロック(H)の含有量の測定を行うのは、共重合体の変性の前でも後でもよい。
Os値=−0.012(Ns値)2 +1.8(Ns値)−13.0
従って、本発明においてNMR法で水添後の共重合体のビニル芳香族重合体ブロック(H)の含有量を求めた場合には、上記式に基づいてNs値をOs値に換算し、ビニル芳香族重合体ブロック(H)の含有量とした。
本発明の変性水添共重合体の分子量分布は、特に制限はないが、成形加工性の点から1.5〜5.0が好ましく、より好ましくは1.6〜4.5、更に好ましくは1.8〜4.0である。変性水添共重合体の分子量分布は、分子量と同様にGPCによる測定から求めることができ、重量平均分子量(Mw)と数平均分子量(Mn)の比(Mw/Mn)である。
本発明の変性水添共重合体においては、共役ジエン単量体単位に基づく二重結合の70
%以上が水添されている。共役ジエン単量体単位に基づく二重結合の70%以上が水添されていることで、優れた耐傷付き性と耐ブロッキング性を発揮する。水添されている二重結合の量は、好ましくは80%以上、より好ましくは85%以上、更に好ましくは90%以上、特に好ましくは95%以上である。水素添加前の共重合体中の共役ジエン単量体単位に基づくビニル結合含量は、赤外分光光度計(ハンプトン法)を用いて求めることができ、変性水添共重合体の水添率は、核磁気共鳴装置(NMR)を用いて求めることができる。
本発明の変性水添共重合体は、柔軟性に富んでおり、引張試験における100%モジュラスが低いことがひとつの特徴である。100%モジュラスは120kg/cm2 以下、好ましくは90kg/cm2 以下、より好ましくは60kg/cm2 以下であることが推奨される。
ol%、さらに好ましくは12%〜30重量%であることが一般的に推奨され、特に柔
軟性に富んだ共重合体を得るためには、12重量%以上であることが好ましい。共役ジ
エン単量体としてイソプレンを使用した場合又は1,3−ブタジエンとイソプレンを併用した場合には、1,2−ビニル結合と3,4−ビニル結合の合計量は一般に3〜75mol%、好ましくは5〜60重量%であることが推奨される。なお、本発明においては、
1,2−ビニル結合と3,4−ビニル結合の合計量(但し、共役ジエンとして1,3−ブタジエンを使用した場合には、1,2−ビニル結合量)を「ビニル結合量」とする。
添加前の共重合体の重合を、モノマーを逐次的に反応器に供給し、バッチ的に行う場合、モノマーを追加する毎に、その直前の重合体をサンプリングして、ビニル結合量を測定し、得られた値からビニル結合量の最大値と最小値との差を計算する。共重合体鎖中のビニル結合は、均一に分布していてもテーパー状に分布していても良い。ここで、ビニル結合量の差は、重合条件、すなわちビニル結合量調整剤(第3級アミン化合物又はエーテル化合物等)の種類、量及び重合温度などの影響で生ずる。従って、例えば、共重合体鎖中のビニル結合量の最大値と最小値との差は、共役ジエン重合時の重合温度によって制御することができる。第3級アミン化合物又はエーテル化合物等のビニル結合量調整剤の種類と量が一定の場合、共重合中のポリマー鎖に組み込まれるビニル結合量は重合温度によって決まる。従って、この場合、重合温度を一定に保って重合するとビニル結合が均一に分布した重合体となる。これに対し、昇温で重合した重合体は、初期(低温で重合)が高ビニル結合量、後半(高温で重合)が低ビニル結合量といった具合にビニル結合量に差のある重合体となる。従って、本発明の水添重合体を製造する際には、初期と後半の重合温度の差は20℃以下、好ましくは15℃以下、より好ましくは10℃以下とすることが推奨される。
ベース共重合体は、例えば、炭化水素溶媒中で有機アルカリ金属化合物等の重合開始剤を用いてアニオンリビング重合によって製造することができる。炭化水素溶媒としては、例えばn−ブタン、イソブタン、n−ペンタン、n−ヘキサン、n−ヘプタン、n−オクタンなどの脂肪族炭化水素類;シクロヘキサン、シクロヘプタン、メチルシクロヘプタンなどの脂環式炭化水素類;及びベンゼン、トルエン、キシレン、エチルベンゼン等の芳香族炭化水素が挙げられる。
重合開始剤としては、一般的に共役ジエン及びビニル芳香族化合物に対しアニオン重合活性があることが知られている脂肪族炭化水素アルカリ金属化合物、芳香族炭化水素アルカリ金属化合物、有機アミノアルカリ金属化合物等を用いることができる。アルカリ金属としてはリチウム、ナトリウム、カリウム等が挙げられ、好適な有機アルカリ金属化合物としては、炭素数1から20の脂肪族及び芳香族炭化水素リチウム化合物であって、1分子中に1個のリチウムを含む化合物や1分子中に複数のリチウムを含むジリチウム化合物、トリリチウム化合物、テトラリチウム化合物が挙げられる。具体的にはn−プロピルリチウム、n−ブチルリチウム、sec−ブチルリチウム、tert−ブチルリチウム、ジイソプロペニルベンゼンとsec−ブチルリチウムの反応生成物、さらにジビニルベンゼンとsec−ブチルリチウムと少量の1,3−ブタジエンとの反応生成物等が挙げられる。更に、米国特許第5,708,092号明細書、英国特許第2,241,239号明細書、米国特許第5,527,753号明細書等に開示されている有機アルカリ金属化合物も使用することができる。
フェニレンジアミン等である。
またエーテル化合物としては、直鎖状エーテル化合物や環状エーテル化合物を用いることができる。直鎖状エーテル化合物としては、ジメチルエーテル、ジエチルエーテル、ジフェニルエーテル、エチレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、エチレングリコールジブチルエーテル等のエチレングリコールのジアルキルエーテル化合物類;及びジエチレングリコールジメチルエーテル、ジエチレングリコールジエチルエーテル、ジエチレングリコールジブチルエーテル等のジエチレングリコールのジアルキルエーテル化合物類が挙げられる。また、環状エーテル化合物としては、テトラヒドロフラン、ジオキサン、2,5−ジメチルオキソラン、2,2,5,5−テトラメチルオキソラン、2,2−ビス(2−オキソラニル)プロパン、フルフリルアルコールのアルキルエーテル等が挙げられる。
(S−H)n −Y、 (H−S)n −Y、
H−(S−H)n −Y、 S−(H−S)n −Y、
Y−(H−S)n −Y、 Y−H−(S−H)n −Y、
Y−S−(H−S)n −Y、
[(S−H)n ]m −Y、 [ (H−S)n ] m −Y、 [ (S−H)n −S] m −Y、 [ (H−S)n −H] m −Y、
[ (S−H)n] m −Y−(H)p、
[ (H−S)n −H] m −Y−(H)p
(式中、各Sは、各々独立に、共役ジエン単量体単位とビニル芳香族単量体単位とからなるランダム共重合体ブロックを表し、各Hは、各々独立に、ビニル芳香族単量体単位の重合体ブロックを表し、Yは、各々独立に、官能基を少なくとも1個有する変性剤基を表す。mは2以上の整数を表し、好ましくは2〜10の整数を表し、n及びpは、各々独立に、1以上の整数を表し、好ましくは1〜10の整数を表す。Yを後述するメタレーション反応で付加させる場合は、YはS及び/又はHの側鎖に結合している。)
(a) S−H−Y、
(b) H−S−Y、
(c) S−H−S−Y、
(d) H−S−H−Y、
(e) Y−S−H−S−Y、
(f) (S−H)m−Y、
(g) (H−S)m−Y、
(h) (S−H)n−Y−(H)p
(式中、各S、H、Y、m、n、pは上記で定義した通りである。)
上記の一般式において、ランダム共重合体ブロックS中のビニル芳香族炭化水素単量体単位は均一に分布していても、またはテーパー状に分布していてもよい。また該共重合体ブロックSには、ビニル芳香族炭化水素が均一に分布している部分及び/又はテーパー状に分布している部分がそれぞれ複数個共存していてもよい。また該共重合体ブロックSには、ビニル芳香族炭化水素含有量が異なるセグメントが複数個共存していてもよい。共重合体中にS及びHがそれぞれ複数存在する場合、それらの構造は同一でも、異なっていても良い。また、Yに結合しているポリマー鎖の構造は同一でも、異なっていても良い。
本発明の変性水添共重合体は下記式(I)〜式(V)よりなる群から選ばれる式で表されることが好ましい。
上記式(I)〜式(III)及び式(a−1)〜式(j−1)におけるR1a〜R15の具体例は以下の通りである。
(但し、上記のように、R1a、R1b、R3 、R4 、R8 〜R10及びR13〜R15は、所望により、各々独立に、水酸基、エポキシ基、アミノ基、シラノール基、炭素数1〜24のアルコキシシラン基よりなる群から選ばれる少なくとも1種の官能基を有してもよく、また、R1a、R1b、R2 〜R4 及びR8 〜R15には、所望により、各々独立に、水酸基、エポキシ基、アミノ基、シラノール基、アルコキシシラン基以外の結合様式で、酸素原子、窒素原子、硫黄原子、珪素原子よりなる群からから選ばれる少なくとも1種の原子が結合していてもよい。)
。
上記のように、本発明において共重合体を変性する方法としては、リビング重合により得られたベース共重合体のリビング末端を、官能基含有変性剤と付加反応させる方法が挙げられる。変性剤の官能基は公知の方法で保護されていてもよい。他の変性方法としては、リビング末端を有さないベース共重合体に有機リチウム化合物等の有機アルカリ金属化合物を反応(メタレーション反応)させて、有機アルカリ金属が末端に付加した共重合体を得、これに変性剤を付加反応させる方法が挙げられる。後者の方法の場合、まずベース共重合体の水添物を得た後にメタレーション反応させてから、変性剤を反応させてもよい。
変性剤の種類により、変性剤を反応させた段階で一般に水酸基やアミノ基等はアルカリ金属塩となっていることもあるが、その場合には水やアルコール、無機酸等活性水素を有する化合物(活性水素含有化合物)で処理することにより、水酸基やアミノ基等にすることができる。
尚、本発明においては、ベース共重合体のリビング末端に変性剤を反応させた後に、変性されていない共重合体が変性共重合体に混在しても良い。変性共重合体に混在する未変性の共重合体の割合は、好ましくは70wt%以下、より好ましくは60wt%以下、更に好ましくは50wt%以下であることが推奨される。
例えば、式(I)又は式(II)で表される変性水添共重合体を得るために使用される変性剤としては、テトラグリシジルメタキシレンジアミン、テトラグリシジル−1,3−ビスアミノメチルシクロヘキサン、テトラグリシジル−p−フェニレンジアミン、テトラグリシジルジアミノジフェニルメタン、ジグリシジルアニリン、ジグリシジルオルソトルイジン、4,4’−ジグリシジルージフェニルメチルアミン、4,4’−ジグリシジルージベンジルメチルアミン、ジグリシジルアミノメチルシクロヘキサン等のポリエポキシ化合物である。
また、式(V)で表される変性水添共重合体を得るために使用される変性剤としては、γ−グリシドキシエチルトリメトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシブチルトリメトキシシラン、γ−グリシドキシプロピルトリエトキシシラン、γ−グリシドキシプロピルトリプロポキシシラン、γ−グリシドキシプロピルトリブトキシシラン、γ−グリシドキシプロピルトリフェノキシシラン、
また、式(III)で表される変性水添共重合体を得るために使用される変性剤としては、1,3−ジメチル−2−イミダゾリジノン、1,3−ジエチル−2−イミダゾリジノン、N,N’−ジメチルプロピレンウレア、1,3−ジプロピル−2−イミダゾリジノン、1−メチル−3−エチル−2−イミダゾリジノン、1−メチル−3−プロピル−2−イミダゾリジノン、1−メチル−3−ブチル−2−イミダゾリジノン、1−メチル−3−(2−メトキシエチル)−2−イミダゾリジノン、1−メチル−3−(2−エトキシエチル)−2−イミダゾリジノン、1,3−ジ−(2−エトキシエチル)−2−イミダゾリジノン、1,3−ジメチルエチレンチオウレア、N,N’−ジエチルプロピレンウレア、N−
メチル−N’−エチルプロピレンウレア等が挙げられる。
上記の変性剤を共重合体のリビング末端に反応させることにより、官能基含有変性剤基(官能基を少なくとも1個有する少なくとも1個の変性剤基)が結合している変性共重合体が得られる。本発明の変性水添共重合体は、窒素原子や酸素原子、珪素原子を、変性剤基の官能基(例えば水酸基、エポキシ基、アミノ基、シラノール基、アルコキシシラン基、或いはカルボニル基)の形で有しているため、これらの官能基と熱可塑性樹脂及び/又はゴム状重合体、無機充填材、極性基含有添加剤等の極性基間での化学的な結合や、水素結合等の物理的な親和力により相互作用が効果的に発現され、本発明が目的とする優れた効果を発揮できる。
上記の方法で製造した変性共重合体を水素添加することにより、本発明の変性水添共重合体が得られる。水添触媒に特に限定はなく、従来から水添触媒として用いられている以下の化合物を用いることができる。
(1)Ni、Pt、Pd、Ru等の金属をカーボン、シリカ、アルミナ、ケイソウ土等に担持した担持型不均一系水添触媒、
(2)Ni、Co、Fe、Cr等の有機酸塩又はアセチルアセトン塩などの遷移金属塩を有機アルミニウム等の還元剤と共に用いる、いわゆるチーグラー型水添触媒、及び
(3)Ti、Ru、Rh、Zr等の有機金属化合物等のいわゆる有機金属錯体等の均一系水添触媒。
チタノセン化合物としては、特開平8−109219号公報に記載された化合物が使用できる。具体的には、ビスシクロペンタジエニルチタンジクロライド、モノペンタメチルシクロペンタジエニルチタントリクロライド等の(置換)シクロペンタジエニル骨格、インデニル骨格あるいはフルオレニル骨格を有する配位子を少なくとも1つ以上有する化合物が挙げられる。また、還元性有機金属化合物としては、有機リチウム等の有機アルカリ金属化合物、有機マグネシウム化合物、有機アルミニウム化合物、有機ホウ素化合物や有機亜鉛化合物等が挙げられる。
は、バッチプロセス、連続プロセス、或いはそれらの組み合わせのいずれでも用いることができる。
変性共重合体の水添反応によって、変性水添共重合体を含む溶液が得られる。変性水添共重合体を含む溶液から、必要に応じて触媒残査を除去し、変性水添共重合体を溶液から分離する。溶媒を分離する方法としては、例えば水添後の反応液にアセトン又はアルコール等の変性水添共重合体に対する貧溶媒となる極性溶媒を加えて重合体を沈澱させて回収する方法;反応液を撹拌下熱湯中に投入し、スチームストリッピングにより溶媒を除去して回収する方法;又は直接重合体溶液を加熱して溶媒を留去する方法等が挙げられる。
本発明の変性水添共重合体の製造においては、変性を、α、β−不飽和カルボン酸又はその誘導体、例えばその無水物、エステル化物、アミド化物、イミド化物で共重合体をグラフト変性することによって行なうこともできる。この場合は、まずベース共重合体の水添を行ってから、グラフト変性する。α、β−不飽和カルボン酸又はその誘導体の具体例としては、無水マレイン酸、マレイン酸イミド、アクリル酸又はそのエステル、メタアクリル酸又はそのエステル、エンド−シス−ビシクロ〔2,2,1〕−5−ヘプテン−2,3−ジカルボン酸又はその無水物などが挙げられる。α、β−不飽和カルボン酸又はその誘導体の付加量は、水添共重合体100重量部当たり、一般に0.01〜20重量部、好ましくは0.1〜10重量部である。
本発明においては、グラフト変性する場合の反応温度は、好ましくは100〜300℃、より好ましくは120〜280℃である。グラフト変性する方法の詳細については、例えば、特開昭62−79211号公報を参照できる。
本発明の変性水添共重合体である成分(a)の、成分(a)と成分(b)の合計100重量部に対して1〜99重量部、及び該変性水添共重合体(a)以外の熱可塑性樹脂及び該変性水添共重合体(a)以外のゴム状重合体からなる群より選ばれる少なくとも1種の重合体である成分(b)の、成分(a)と成分(b)の合計100重量部に対して99〜1重量部を包含する変性水添共重合体組成物が提供される。
本発明の変性水添共重合体(a)を、熱可塑性樹脂やゴム状重合体などのほかの重合体(b)と組み合わせることで、各種成形材料に適した変性水添共重合体組成物を得ることができる。本発明の変性水添共重合体組成物における、変性水添共重合体(a)(以下、屡々、成分(a)と称する)と熱可塑性樹脂及び/又はゴム状重合体(以下、屡々、成分(b)と称する)の配合割合は、成分(a)/成分(b)の重量比で1/99〜99/1、好ましくは2/98〜90/10、更に好ましくは5/95〜80/20である。
本発明の変性水添共重合体(a)と熱可塑性樹脂(b)をブレンドした場合、機械的特性に優れた変性水添共重合体組成物が得られる。
合体及びその加水分解物などの、エチレンと他の共重合可能なモノマーとからなるエチレン含有量が50重量%以上の共重合体;エチレン−アクリル酸アイオノマーや塩素化ポリエチレンなどのポリエチレン系樹脂;ポリプロピレン;プロピレン−エチレン共重合体、プロピレン−アクリル酸エチル共重合体や塩素化ポリプロピレンなどのポリプロピレン系樹脂、エチレン−ノルボルネン樹脂等の環状オレフィン系樹脂、ポリブテン系樹脂、ポリ塩化ビニル系樹脂、ポリ酢酸ビニル系樹脂及びその加水分解物などの、プロピレンと他の共重合可能な単量体とからなるプロピレン含有量が50重量%以上の共重合体;アクリル酸及びそのエステルやアミドの重合体;ポリアクリレート系樹脂;アクリロニトリル及び/又はメタクリロニトリルの重合体;アクリロニトリル系モノマーと他の共重合可能な単量体とからなるアクリロニトリル系単量体含有量が50重量%以上の共重合体であるニトリル樹脂;ナイロン−46、ナイロン−6、ナイロン−66、ナイロン−610、ナイロン−11、ナイロン−12、ナイロン−6ナイロン−12共重合体などのポリアミド系樹脂;ポリエステル系樹脂;熱可塑性ポリウレタン系樹脂;ポリ−4,4’−ジオキシジフェニル−2,2’−プロパンカーボネートなどのポリカーボネート系重合体;ポリエーテルスルホンやポリアリルスルホンなどの熱可塑性ポリスルホン;ポリオキシメチレン系樹脂;ポリ(2,6−ジメチル−1,4−フェニレン)エーテルなどのポリフェニレンエーテル系樹脂;ポリフェニレンスルフィド、ポリ4,4’−ジフェニレンスルフィドなどのポリフェニレンスルフィド系樹脂;ポリアリレート系樹脂;ポリエーテルケトン重合体又は共重合体;ポリケトン系樹脂;フッ素系樹脂;ポリオキシベンゾイル系重合体;ポリイミド系樹脂;1,2−ポリブタジエン、トランスポリブタジエンなどのポリブタジエン系樹脂などが挙げられる。これらの熱可塑性樹脂(b)のうち、変性水添共重合体(a)との相溶性の観点から好ましいのは、ポリスチレン、ゴム変性スチレン系樹脂等のスチレン系樹脂;ポリプロピレン、プロピレン−エチレン共重合体等のポリプロピレン系樹脂;ポリアミド系樹脂;ポリエステル系樹脂;ポリカーボネート系重合体である。これらの熱可塑性樹脂(b)は、水酸基、エポキシ基、アミノ基、カルボン酸基、酸無水物基、イソシアネート基等の極性基含有原子団が結合しているものでもよい。本発明に用いる熱可塑性樹脂(b)の数平均分子量は通常1,000以上、好ましくは5,000〜500万、更に好ましくは1万〜100万である。尚、熱可塑性樹脂(b)の数平均分子量は、上記した本発明の変性水添共重合体の分子量の測定と同様に、GPCにより測定することができる。
本発明の変性水添共重合体組成物に用いるゴム状重合体(b)としては、ブタジエンゴム及びその水素添加物;スチレン−ブタジエンゴム及びその水素添加物(但し、本発明の変性水添共重合体(a)とは異なる);イソプレンゴム;アクリロニトリル−ブタジエンゴム及びその水素添加物;クロロプレンゴム、エチレン−プロピレンゴム、エチレン−プロピレン−ジエンゴム、エチレン−ブテン−ジエンゴム、エチレン−ブテンゴム、エチレン−ヘキセンゴム、エチレン−オクテンゴム等のオレフィン系エラストマー;EPDMやEPM等を軟質相としたオレフィン系TPE;ブチルゴム;アクリルゴム;フッ素ゴム;シリコーンゴム;塩素化ポリエチレンゴム;エピクロルヒドリンゴム;α,β−不飽和ニトリル−アクリル酸エステル−共役ジエン共重合ゴム;ウレタンゴム;多硫化ゴム;スチレン−ブタジエンブロック共重合体及びその水素添加物;スチレン−イソプレンブロック共重合体及びその水素添加物;スチレン−ブタジエン・イソプレンブロック共重合体及びその水素添加物等の、スチレン含有量が60重量%以下のスチレン系エラストマー;天然ゴムなどが挙げられる。これらのゴム状重合体(b)のうち、変性水添共重合体(a)との相溶性の観点から好ましいのは、スチレン−ブタジエンブロック共重合体及びその水素添加物、スチレン−イソプレンブロック共重合体及びその水素添加物等のスチレン系エラストマーと、エチレン−プロピレンゴム、エチレン−ブテンゴム、エチレン−オクテンゴム等のオレフィン系エラストマーである。これらのゴム状重合体は、官能基(カルボキシ
ル基、カルボニル基、酸無水物基、水酸基、エポキシ基、アミノ基、シラノ−ル基、アルコキシシラン基等)を付与した変性ゴムであっても良い。本発明に用いるゴム状重合体(b)の数平均分子量は好ましくは1万以上、より好ましくは2万〜100万、更に好ましくは3万〜80万である。尚、ゴム状重合体(b)の数平均分子量は、上記した本発明の変性水添共重合体の分子量の測定と同様に、GPCにより測定することができる。
本発明の変性水添共重合体及び変性水添共重合体組成物には、必要に応じて任意の添加剤を配合してもよい。添加剤は、熱可塑性樹脂やゴム状重合体に一般的に配合されるものであれば特に限定はなく、「ゴム・プラスチック配合薬品」(日本国、ラバーダイジェスト社編)などに記載されたものが挙げられる。具体的には、後述する補強性充填剤や硫酸カルシウム、硫酸バリウム等の無機充填剤;カーボンブラック、酸化鉄等の顔料;ステアリン酸、ベヘニン酸、ステアリン酸亜鉛、ステアリン酸カルシウム、ステアリン酸マグネシウム、エチレンビスステアロアミド等の滑剤;ステアリン酸アミド、エルカ酸アミド、オレイン酸アミド、ステアリン酸モノグリセライド、ステアリルアルコール、石油系ワックス(例えば、マイクロクリスタリンワックス)及び低分子量ビニル芳香族系樹脂等のブロッキング防止剤;離型剤;有機ポリシロキサン、ミネラルオイル等の可塑剤;ヒンダードフェノール系酸化防止剤、リン系熱安定剤等の酸化防止剤;ヒンダードアミン系光安定剤、ベンゾトリアゾール系紫外線吸収剤;難燃剤;帯電防止剤;有機繊維、ガラス繊維、炭素繊維、金属ウィスカ等の補強剤;着色剤;及びこれらの混合物等を用いることができる。
上述したように、本発明の変性水添共重合体又は変性水添共重合体組成物を、所望により各種添加剤を配合して様々な用途に用いることができる。本発明の変性水添共重合体及び変性水添共重合体組成物の具体的態様に関しては、( i) 補強性充填剤配合物、( ii) 架橋物、( iii) 発泡体、( iv) 多層フィルム及び多層シートなどの成形品、( v) 建築材料、( vi) 制振・防音材料、( vii) 電線被覆材料、( viii) 高周波融着性組成物、( ix) スラッシュ成形材料、( x) 粘接着性組成物、( xi)アスファルト組成物に好適に用いることができ、特に(ii)架橋物、( iii) 発泡体、( iv) 多層フィルム及び多層シートなどの成形品、( v) 建築材料、( vi) 制振・防音材料、( vii) 電線被覆材料として有利に用いることができる。次に、上記の具体的態様に関して以下に説明する。
本発明の変性水添共重合体又は変性水添共重合体組成物に、シリカ系無機充填剤、金属酸化物、金属水酸化物、金属炭酸化物、カーボンブラックから選ばれる少なくとも1種の
補強性充填剤(以下、屡々、成分(c)と称する)を配合して補強性充填剤配合物を調製することができる。補強性充填剤配合物における成分(c)の配合量は、変性水添共重合体又は変性水添共重合体組成物100重量部に対して0.5〜100重量部、好ましくは5〜100重量部、更に好ましくは20〜80重量部である。本発明の変性水添共重合体組成物を用いて補強性充填剤配合物を調製する場合には、成分(a)である本発明の変性水添共重合体100重量部に対して、0〜500重量部、好ましくは5〜300重量部、更に好ましくは10〜200重量部の熱可塑性樹脂及び/又はゴム状重合体(成分(b))を包含する変性水添共重合体組成物が適している。
補強性充填剤として用いるシリカ系無機充填剤は、化学式SiO2 を構成単位の主成分とする固体粒子であり、例えば、シリカ、クレイ、タルク、カオリン、マイカ、ウォラストナイト、モンモリロナイト、ゼオライト、ガラス繊維等の無機繊維状物質などが挙げられる。また、表面を疎水化したシリカ系無機充填剤や、シリカ系無機充填剤とシリカ系以外の無機充填剤の混合物も使用できる。シリカ系無機充填剤としてはシリカ及びガラス繊維が好ましい。シリカとしては、乾式法ホワイトカーボン、湿式法ホワイトカーボン、合成ケイ酸塩系ホワイトカーボン、コロイダルシリカと呼ばれているもの等が使用できる。平均粒径は0.01〜150μmのものが好ましく、シリカが組成物中に分散し、その添加効果を十分に発揮するためには、平均分散粒子径は0.05〜1μmが好ましく、より好ましくは0.05〜0.5μmである。
補強性充填剤として用いる金属水酸化物は、水酸化アルミニウム、水酸化マグネシウム、水酸化ジルコニウム、水和珪酸アルミニウム、水和珪酸マグネシウム、塩基性炭酸マグネシウム、ハイドロタルサイト、水酸化カルシウム、水酸化バリウム、酸化錫の水和物、硼砂等の無機金属化合物の水和物等の水和系無機充填材であり、中でも水酸化マグネシウムと水酸化アルミニウムが好ましい。
補強性充填剤として用いる金属炭酸化物としては、炭酸カルシウム、炭酸マグネシウムなどが挙げられる。
また、補強性充填剤として、FT、SRF、FEF、HAF、ISAF、SAF等の各クラスのカーボンブラックが使用でき、窒素吸着比表面積が50mg/g以上、DBP(フタル酸ジブチル)吸油量が80ml/100gのカーボンブラックが好ましい。
性充填剤配合物は、加硫剤で加硫して( 即ち架橋して) 加硫組成物としてもよい。加硫剤としては、有機過酸化物及びアゾ化合物などのラジカル発生剤、オキシム化合物、ニトロソ化合物、ポリアミン化合物、硫黄、硫黄化合物(一塩化硫黄、二塩化硫黄、ジスルフィド化合物、高分子多硫化合物など)を用いることができる。加硫剤の使用量は、通常は、変性水添共重合体又は変性水添共重合体組成物100重量部に対し0.01〜20重量部、好ましくは0.1〜15重量部の割合である。
加硫剤として用いる有機過酸化物(以下、屡々、成分(e)と称する)としては、臭気性やスコーチ安定性(各成分の混合時の条件下では架橋しないが、架橋反応条件にした時には速やかに架橋する特性)の点で、2,5−ジメチル−2,5−ジ−(tert−ブチルペルオキシ)ヘキサン、2,5−ジメチル−2,5−ジ−(tert−ブチルペルオキシ)ヘキシン−3、1,3−ビス(tert−ブチルペルオキシイソプロピル)ベンゼン、1,1−ビス(tert−ブチルペルオキシ)−3,3,5−トリメチルシクロヘキサン、n−ブチル−4,4−ビス(tert−ブチルペルオキシ)バレレート、ジ−ter−ブチルパーオキサイドが好ましい。上記以外には、ジクミルペルオキシド、ベンゾイルペルオキシド、p−クロロベンゾイルペルオキシド、2,4−ジクロロベンゾイルペルオキシド、tert−ブチルペルオキシベンゾエート、tert−ブチルペルオキシイソプロピルカーボネート、ジアセチルペルオキシド、ラウロイルペルオキシド、tert−ブチルクミルペルオキシドなども用いることができる。
また上記した有機過酸化物を使用して補強性充填剤配合物を架橋する際には、特に加硫促進剤として硫黄;p−キノンジオキシム、p,p’−ジベンゾイルキノンジオキシム、N−メチル−N−4−ジニトロソアニリン、ニトロソベンゼン、ジフェニルグアニジン、トリメチロールプロパン−N,N’−m−フェニレンジマレイミド等のペルオキシ架橋用助剤(以下、屡々、成分(g)と称する);ジビニルベンゼン、トリアリルシアヌレート、エチレングリコールジメタクリレート、ジエチレングリコールジメタクリレート、ポリエチレングリコールジメタクリレート、トリメチロールプロパントリメタクリレート、アリルメタクリレート等の多官能性メタクリレートモノマー;ビニルブチラート、ビニルステアレート等の多官能性ビニルモノマー(以下、屡々、成分(h)と称する)などを有機過酸化物と併用することもできる。このような加硫促進剤は、通常、変性水添共重合体又は変性水添共重合体組成物100重量部に対し0.01〜20重量部、好ましくは0.1〜15重量部の割合で用いられる。
補強性充填剤配合物の加工性を改良するために、ゴム用軟化剤(以下、屡々、成分(i)と称する)を配合しても良い。ゴム用軟化剤には鉱物油や、液状もしくは低分子量の合成軟化剤が適している。なかでも、一般にゴムの軟化、増容、加工性向上に用いる、ナフテン系及び/又はパラフィン系のプロセスオイル又はエクステンダーオイルが好ましい。鉱物油系ゴム用軟化剤は、芳香族環、ナフテン環及びパラフィン鎖の混合物であり、パラフィン鎖の炭素数が全炭素の50%以上を占めるものがパラフィン系と呼ばれ、ナフテン環の炭素数が30〜45%のものがナフテン系、また芳香族炭素数が30%を超えるものが芳香族系と呼ばれる。補強性充填剤配合物には合成軟化剤を用いてもよく、ポリブテン、低分子量ポリブタジエン、流動パラフィン等が使用可能である。しかし、上記した鉱物油系ゴム用軟化剤が好ましい。補強性充填剤配合物におけるゴム用軟化剤の配合量は、変
性水添共重合体又は変性水添共重合体組成物100重量部に対して0〜100重量部、好ましくは10〜90重量部、更に好ましくは30〜90重量部である。ゴム用軟化剤の量が100重量部を超えるとブリードアウトを生じやすく、組成物表面にベタツキを生ずるおそれがある。
本発明の変性水添共重合体又は変性水添共重合体組成物を含む補強性充填剤配合物は、建築材料、電線被覆材や制振材料、自動車内外装部品材料、家電部品材料、食品包装材料、玩具等の雑貨材料などとして用いることができる。また、その加硫組成物は、その特徴を生かして上記と同様の用途以外に、タイヤ用途や防振ゴム、ベルト、工業用品、はきもの、発泡体などに適用することができる。
本発明の変性水添共重合体又は変性水添共重合体組成物を加硫剤の存在下で架橋して、架橋物(即ち、架橋変性水添共重合体又は架橋変性水添共重合体組成物)とすることができる。本発明の変性水添共重合体又は変性水添共重合体組成物を架橋することにより、耐熱性[高温C−Set(compression set )]や耐屈曲性を向上することができる。本発明の変性水添共重合体組成物の架橋物を調製する場合には、変性水添共重合体(a)と熱可塑性樹脂(b)及び/又はゴム状重合体(b)との配合割合は、成分(a)/成分(b)の重量比率で、10/90〜100/0、好ましくは20/80〜90/10、更に好ましくは30/70〜80/20である。
加硫剤として使用する有機過酸化物としては、前述の成分(e)を使用することができる。有機過酸化物を使用して架橋する際には、加硫促進剤として前述の成分(f)を使用することができ、また前述の成分(g)や成分(h)などを併用することもできる。これらの加硫促進剤の使用量は、通常は、変性水添共重合体又は変性水添共重合体組成物100重量部に対して0.01〜20重量部、好ましくは0.1〜15重量部である。
なるように動的架橋することが推奨される。ゲル含量に関しては、沸騰キシレンを用いてソックスレー抽出器で架橋物1gを10時間リフラックスし、残留物を80メッシュの金網でろ過し、メッシュ上に残留した不溶物の乾燥重量(g)を測定して求められる、試料1gに対する不溶物の割合(重量%)をゲル含量とする。ゲル含量は、加硫剤の種類や量、加硫する時の条件(温度、滞留時間、シェア等)を変えることで調整することができる。
本発明の架橋物は、補強性充填剤配合物の加硫組成物と同様に建築材料、電線被覆材や制振材料、自動車内外装部品材料、家電部品材料、食品包装材料、玩具等の雑貨材料などの他、タイヤ用途や防振ゴム、ベルト、工業用品、はきもの、発泡体などに適用でき、更には医療用器具材料としても用いることができる。
本発明の変性水添共重合体又は変性水添共重合体組成物は、発泡体としても用いることができる。この場合、通常、本発明の変性水添共重合体又は変性水添共重合体組成物に充填剤(以下、屡々、成分(j)と称する)を配合した組成物を調製し、これを発泡させることにより発泡体を得ることができる。本発明の変性水添共重合体組成物を用いて発泡体を調製する場合には、成分(a)の変性水添共重合体に対して5〜95重量%、好ましくは5〜90重量%、更に好ましくは5〜80重量%の熱可塑性樹脂及び/又はゴム状重合体(成分(b))を包含する変性水添共重合体組成物が適している。
また、充填剤(j)の配合量は、発泡体を構成する組成物全体に対して5〜95重量%であり、好ましくは10〜80重量%、更に好ましくは20〜70重量%である。
本発明の発泡体に用いる充填剤(j)としては、前述の補強性充填剤(成分(c))や硫酸カルシウム、硫酸バリウム、チタン酸カリウムウイスカー、マイカ、グラファイト、カーボンファイバー等の無機充填剤;木製チップ、木製パウダー、パルプ等の有機充填剤が挙げられる。充填剤の形状に特に限定はなく、鱗片状、球状、粒状、粉体、不定形状等のものを用いることができる。これらの充填剤は必要に応じ2種以上を併用しても良い。充填剤は、シランカップリング剤等であらかじめ表面処理を行ったものを使用することもできる。
組成物を発泡材料とすることにより、軽量化、柔軟性の向上、意匠性の向上等を図ることができる。無機系発泡剤としては、重炭酸ナトリウム、炭酸アンモニウム、重炭酸アンモニウム、亜硝酸アンモニウム、アジド化合物、ホウ水素化ナトリウム、金属粉等が挙げられる。有機系発泡剤としては、アゾジカルボンアミド、アゾビスホルムアミド、アゾビスイソブチロニトリル、アゾジカルボン酸バリウム、N,N’−ジニトロソペンタメチレンテトラミン、N,N’−ジニトロソ−N,N’−ジメチルテレフタルアミド、ベンゼンスルホニルヒドラジド、p−トルエンスルホニルヒドラジド、p,p’−オキシビスベンゼンスルホニルヒドラジド、p−トルエンスルホニルセミカルバジド等が挙げられる。物理的発泡剤としては、ペンタン、ブタン、ヘキサン等の炭化水素;塩化メチル、塩化メチレン等のハロゲン化炭化水素;窒素、空気等のガス;トリクロロフルオロメタン、ジクロロジフルオロメタン、トリクロロトリフルオロエタン、クロロジフルオロエタン、ハイドロフルオロカーボン等のフッ素化炭化水素等が挙げられる。これらの発泡剤は組み合わせて使用してもよい。発泡剤の配合量は、本発明の変性水添共重合体あるいは変性水添共重合体組成物100重量部に対して0.1〜8重量部、好ましくは0.3〜6重量部、さらに好ましくは0.5〜5重量部である。
い。例えば、前述の「ゴム・プラスチック配合薬品」(日本国、ラバーダイジェスト社編)などに記載された各種添加剤が使用できる。
また、本発明の発泡体は、必要に応じて架橋することもできる。架橋の方法は、過酸化物、イオウ等の架橋剤及び必要に応じて共架橋剤等の添加による化学的方法、電子線、放射線等による物理的架橋法を例示することができる。架橋プロセスとしては、放射線架橋等のような静的な方法(混練しないで架橋する方法)や、動的架橋法等を例示することができる。架橋した発泡体を得るための具体的な方法としては、例えば、ポリマーと発泡剤や架橋剤との混合物を用いてシートを作成し、このシートを160℃くらいに加熱すると、発泡と同時に架橋反応も起き、これにより架橋した発泡体を得ることができる。架橋剤としては、前述の成分(e)である有機過酸化物や成分(f)の加硫促進剤を使用することができ、また前述の成分(g)や成分(h)などを併用することができる。これらの加硫促進剤の使用量は、通常、変性水添共重合体又は変性水添共重合体組成物100重量部に対し0.01〜20重量部、好ましくは0.1〜15重量部である。
本発明の発泡体は、食品包装材料以外に、建築材料、自動車内装部品材料、家電部品材料、玩具等の雑貨材料、履物材料などに使用することができる。
また本発明の発泡体は、日本国特開平6−234133号公報に開示されているようなインサート・型空隙拡大法などの方法による射出成形によって、硬質樹脂成形品と組み合わせたクッション性複合成形品を成形することもできる。
本発明の変性水添共重合体又は変性水添共重合体組成物は、多層フィルム又はシートとして使用することもできる。本発明の変性水添共重合体又は変性水添共重合体組成物からなるフィルムは、その耐熱性、収縮性、ヒートシール性、透明性、防曇性を維持した状態で、各種機能を付与するための他の樹脂層を積層することが可能である。従って、本発明の多層フィルムやシートを用いることで、さらに自己粘着性や耐引き裂き伝播性、突き刺し強度、破断伸び等の機械的強度、延伸性、結束性、弾性回復性、耐突き破れ性、耐引き裂き性、変形回復性、ガスバリアー性に優れた種々の多層フィルムを提供することができる。このような多層フィルム又はシートは、非塩ビ系のストレッチフィルムとしてハンドラッパー又はストレッチ包装機等にも使用可能である。本発明の変性水添共重合体又は変性水添共重合体組成物からなる層を包含する多層フィルム又はシートとしては、下記のものが例示される。
b.2つの最外層(即ち、フィルム又はシートの両表面を形成する層)のうち少なくとも一層が、粘着性樹脂(例えば、エチレン−酢酸ビニル共重合体(EVA))からなることを特徴とする、上記a項の多層フィルム又はシート、
c.少なくとも一層がポリオレフィン系樹脂からなることを特徴とする、上記a項の多層フィルム又はシート、
d.少なくとも一層が、厚さ25μm、温度23℃、湿度65%RHの条件で測定した酸素透過度が100cc/m2 ・24hrs・atm以下であるガスバリアー性樹脂(例
えば、エチレン−ビニルアルコール共重合体(EVOH)、ポリ塩化ビニリデン(PVDC)、ポリアミド系樹脂など)からなることを特徴とする、上記a項の多層フィルム又はシート、
f.最外層以外の少なくとも一層が、接着性樹脂層からなることを特徴とする、上記a〜e項のいずれかに記載の多層フィルム又はシート、
g.上記a〜f項のいずれかに記載の多層フィルム又はシートよりなるストレッチフィルム、そして
h.上記a〜f項のいずれかに記載の多層フィルム又はシートよりなる熱収縮性1軸延伸フィルム又は熱収縮性2軸延伸フィルム。
本発明の多層フィルム又はシートには、必要に応じて充填剤、安定剤、老化防止剤、耐候性向上剤、紫外線吸収剤、可塑剤、軟化剤、滑剤、加工助剤、着色剤、顔料、帯電防止剤、難燃剤、防曇剤、ブロッキング防止剤、結晶核剤、発泡剤等を含ませることができる。上記の添加剤のうち、特にフィルムやシートのブロッキングを抑制するには、エルカ酸アミド、オレイン酸アミド、ステアリン酸モノグリセライド、石油系ワックス(例えば、マイクロクリスタリンワックス)等のブロッキング防止剤の添加が有効である。安定剤、防止剤、耐候性向上剤、紫外線級吸収剤、滑剤、着色剤、顔料、ブロッキング防止剤、結晶核剤等の添加量に特に制限はないが、物性、経済性のバランスから10重量部以下が好ましく、とくに好ましくは5重量部以下である。但し、多量に添加することによって効果を発現する材料についてはこの限りではない。これらの添加剤は、フィルムやシートを製造する前の変性水添共重合体又は変性水添共重合体組成物に添加すればよい。
本発明の多層フィルム又はシートは、必要に応じて、コロナ、オゾン、プラズマ等の表面処理、防曇剤塗布、滑剤塗布、印刷等を実施することができる。本発明の多層フィルム又はシートは必要に応じて1軸又は2軸等の延伸配向を行うことができる。本発明の多層フィルム又はシートは必要に応じて、熱、超音波、高周波等の手法による融着、溶剤による接着等の手法によるフィルム同士、あるいは他の熱可塑性樹脂等の材料と接合することができる。
本発明の多層フィルム又はシートは、本発明の変性水添共重合体又は変性水添共重合体組成物からなる層の他に、物性の改善を目的として他の適当なフィルム、例えば、ポリオレフィン系樹脂、ポリスチレン系樹脂、ポリエチレンテレフタレート系樹脂等のフィルムと多層化されている。ポリオレフィン系樹脂としては、アイソタクティックポリプロピレン、シンジオタクティックポリプロピレン、アタクティックポリプロピレン、直鎖低密度ポリエチレン(L−LDPE)、低密度ポリエチレン(LDPE)、高密度ポリエチレン(HDPE)、エチレン及び/又はプロピレンとブテン、ヘキセン、オクテン等のαーオレフィンとのブロック、ランダム共重合体、ポリメチルペンテン等を例示することができる。
層間の接着力が充分でない場合、接着層を層間に配置してもよい。接着層としては、例えば、エチレン−酢酸ビニル共重合体;エチレン−アクリル酸エチル共重合体;マレイン酸、無水マレイン酸、アクリル酸、メタクリル酸、イタコン酸などで変性されたオレフィン共重合体のような熱可塑性重合体の不飽和カルボン酸変性物もしくは該酸変成物の金属変成物、並びにこれらを含む混合物;熱可塑性ポリウレタンエラストマーのブレンド樹脂などが挙げられる。この層の厚みに特に限定はなく、目的や用途に応じて選択することができるが、好ましくは0.1〜100μm、更に好ましくは0.5〜50μmである。
用いることもできる。ガスバリアー性樹脂としては、例えば厚み25μmのフィルムとした時に、23℃、相対湿度65%の条件下における酸素透過度が100cc/m2 ・24hr・atm以下、好ましくは50cc/m2 ・24hr・atm以下である樹脂が挙げられる。具体的には、塩化ビニリデン共重合体(PVDC)、エチレン/ビニルアルコール共重合体(EVOH)、メタキシリレンジアミンより生成されるポリアミドなどの芳香族ナイロン及び非晶質ナイロン、ポリアクリロニトリル等、アクリロニトリルを主成分とする共重合体を本発明の多層フィルム又はシートに使用可能なガスバリアー性樹脂として例示することができる。また塩化ビニリデン共重合体を主体とし、エチレンと酢酸ビニル、アクリル酸、メタクリル酸又はそれらの不飽和酸のアルキルエステルとの共重合体、又はMBS樹脂の少なくとも1種の共重合体などの混合樹脂組成物、ケン化度が95モル%以上のエチレンとビニルアルコール共重合体を主体とし、ポリエステルエラストマー、ポリアミドエラストマー、エチレンと酢酸ビニル共重合体、エチレンとアクリル酸エステル共重合体、ケン化度が95モル%未満のエチレンとビニルアルコール共重合体などとの混合樹脂組成物、前記芳香族ナイロンや非晶質ナイロンと脂肪族ナイロンなどとの混合樹脂組成物も挙げられる。また、特に柔軟性が必要な場合には、エチレン/ビニルアルコール共重合体系が好ましい。
ガスバリアー層の厚みは、包装する対象物や目的に応じて選択すればよく、特に制限はないが、一般には0.1〜500μm、好ましくは1〜100μm、特に好ましくは5〜50μmである。例えばポリ塩化ビニリデンと共押出する場合には、その層の厚みは熱安定性と耐低温性の点からフィルム全体の30%以下であるのが望ましい。例えば、本願の変性水添共重合体と塩化ビニリデンの二層からなる100μmのフィルムにおいては、塩化ビニリデン層の厚みが20μm程度であればよい。
ガスバリアー樹脂と多層化された本発明の多層フィルム又はシートは、本発明で規定する変性水添共重合体が有する特徴と共に、酸素バリアー性を併せ持つ優れた多層フィルム又はシートである。このような多層フィルム又はシートで食品や精密機器等を包装することで、内容物の劣化、腐敗、酸化等の品質の低下を低減する事が可能となる。このような多層フィルム又はシートを成形することで、酸素バリアー性を有する容器が得られる。
本発明の多層フィルム又はシートを製造するためには、一般にインフレーションフィルム製造装置やTダイフィルム製造装置などを用いる共押出し法、押出しコーティング法(押出しラミネート法ともいう)などの成形方法を採用することができる。またこれらの装置を用いて得た多層又は単層フィルム又はシートを用いてドライラミネート法、サンドラミネート法、ホットメルトラミネーション法等の公知の技術で目的とする多層フィルム又はシートを製造することもできる。また、本発明の多層フィルムが熱収縮フィルムの場合、その製造方法に特に制限は無いが、公知の延伸フィルム製造方法等を用いることができる。例えば、Tダイ法、チューブラー法、インフレーション法等で押出したシート又はフィルムを、1軸延伸、2軸延伸、多軸延伸等の延伸法により得ることができる。1軸延伸の例としては、押出シートを押出方向と直交する方向にテンターで延伸する方法、押出チューブ状フィルムを円周方向に延伸する方法等を挙げることができる。2軸延伸の例としては、押出シートを、押出方向にロールで延伸した後、押出方向と直交する方向にテンター等で延伸する方法、押出チューブ状フィルムを、押出方向及び円周方向に同時又は別々に延伸する方法等が挙げられる。また、必要に応じて、ヒートセット、コロナ処理、プラ
ズマ処理等の後処理を行っても良い。
本発明の多層フィルム又はシートの具体的用途に特に限定はないが、包装用フィルム、バッグ、パウチ等に使用することができる。ストレッチ性を有する多層フィルムの場合は、特に食品包装用ストレッチフィルム、パレットストレッチフィルム、保護フィルム等に好適に使用することができる。バリアー性フィルムの場合は、食品、飲料、精密機器、医薬品等の包装用に使用することができる。熱収縮性フィルムの場合は、シュリンク包装、シュリンクラベル等に使用することができる。
本発明の変性水添共重合体又は変性水添共重合体組成物は建築材料として使用することもできる。この場合、本発明の変性水添共重合体又は変性水添共重合体組成物に充填剤及び/又は難燃剤を配合することが好ましい。このような建築材料は、耐磨耗性、耐傷付き性、引張特性等の優れた特性を持ち、特に、床材、壁材、天井材、シーリング材として好適である。また、本発明の建築材料は、発泡体構造を有する成形品としても利用できる。
本発明の変性水添共重合体組成物を用いて建築材料を調製する場合には、前述の成分(a)と前述の成分(b)の配合割合は、成分(a)/成分(b)の重量比率で100/0〜5/95、好ましくは95/5〜10/90、更に好ましくは95/5〜20/80である。
本発明の建築材料に用いる充填剤としては、「発泡体」の項で例示した充填材(成分(j))を使用することができる。
本発明の建築材料に用いる難燃剤(以下、屡々、成分(l)と称する)としては、主として臭素含有化合物などのハロゲン系難燃剤、主として芳香族系リン含有化合物などのリン系難燃剤、主として金属水酸化物などの無機系難燃剤等が挙げられる。
本発明の建築材料に使用する充填剤及び難燃剤は、シランカップリング剤等であらかじめ表面処理を行ってから使用することもできる。
充填剤及び/又は難燃剤の添加量としては、変性水添共重合体又は変性水添共重合体組成物の重量に対して、5〜95重量%であり、好ましくは10〜80重量%、更に好ましくは20〜70重量%である。充填剤と難燃剤は必要に応じて2種以上を併用しても良い。2種以上の充填剤や2種以上の難燃剤を用いるか、充填剤と難燃剤を併用してもかまわない。充填剤と難燃剤を併用する場合には、その合計量が上記範囲内であることが好ましい。
、好ましくは0.1〜15重量部である。
更に本発明の建築材料は発泡成形体に加工して使用することもできる。本発明の建築材料を発泡成形体とすることにより、軽量化、柔軟性向上、意匠性向上等を図ることができる。本発明の建築材料を発泡する方法には、無機系発泡剤、有機系発泡剤等の化学的発泡剤を用いる化学的方法や、物理発泡剤等を用いる物理的方法等があり、いずれも発泡剤の添加等により材料内部に気泡を分布させることができる。発泡剤としては、上記の「発泡体」の項で例示した発泡剤(成分(k))を使用することができる。発泡剤の配合量は、本発明の変性水添共重合体あるいは変性水添共重合体組成物100重量部に対して0.1〜8重量部、好ましくは0.3〜6重量部、さらに好ましくは0.5〜5重量部である。
本発明の建築材料は、オレフィン系モノマーのみからなる樹脂に比べて優れた印刷性、塗装性を有するが、更に印刷性、塗装性等を向上させる目的で表面処理を行うこともできる。表面処理の方法に特に限定は無く、物理的方法、化学的方法等を使用することができ、例えば、コロナ放電処理、オゾン処理、プラズマ処理、火炎処理、酸・アルカリ処理等を挙げることができる。これらのうち、コロナ放電処理が実施の容易さ、コスト、連続処理が可能等の点から好ましい。
本発明の建築材料の使用形態に特に制限はないが、床材、壁材や天井材として用いる場合には、コンクリート、金属、木材等の構造材料を被覆するための、最外層部分の被覆材料として使用することが可能である。本発明の建築材料を床材、壁材と天井材の製造に用いる際には、シート、フィルム、タイル、ボード等の形状で提供され、接着剤、粘着材、釘、ねじ等の手法により構造材等の基材に接合される。また本発明の建築材料は、シーリング材として、密閉性を向上させるためのガスケット等に用いることもできる。具体的な用途としては、一般住宅、オフィスビル、商業施設、公共施設等において、タイル等の床材、内壁材、天井内壁材、窓枠ガスケット等に用いることができる。
本発明の変性水添共重合体又は変性水添共重合体組成物は制振・防音材料として用いることもできる。この場合、本発明の変性水添共重合体又は変性水添共重合体組成物に充填剤及び/又は難燃剤を配合することが好ましい。本発明の制振・防音材料は、柔軟性に富み、優れた制振性、防音性、耐磨耗性、耐傷付き性、強度等の特性を有する。
本発明の変性水添共重合体組成物を用いて制振・防音材料を調製する場合には、前述の成分(a)と前述の成分(b)の配合割合は、成分(a)/成分(b)の重量比率で100/0〜5/95、好ましくは95/5〜10/90、更に好ましくは95/5〜20/80である。
本発明の制振・防音材料に用いる充填剤としては、「発泡体」の項で例示した充填材(成分(j))を使用することができる。また、難燃剤としては、「建築材料」の項で例示した難燃剤(成分(l))を使用することができる。好ましい難燃剤も建築材料の場合と同様である。
充填剤及び/又は難燃剤の添加量としては、変性水添共重合体又は変性水添共重合体組成物の5〜95重量%であり、好ましくは10〜80重量%、更に好ましくは20〜70重量%である。充填剤と難燃剤は必要に応じ2種以上を併用しても良い。2種以上の充填剤や2種以上の難燃剤を用いるか、充填剤と難燃剤を併用してもかまわない。充填剤と難燃剤を併用する場合には、その合計量が上記範囲内であることが好ましい。
本発明の制振・防音材料には、必要に応じて上記以外の任意の添加剤を配合することができる。添加剤の種類は、熱可塑性樹脂やゴム状重合体の配合に一般的に用いられるものであれば特に制限はない。例えば、前述の「ゴム・プラスチック配合薬品」(日本国、ラバーダイジェスト社編)などに記載された各種添加剤を使用することができる。
本発明の制振・防音材料は、オレフィン系モノマーのみからなる樹脂に比べて優れた印刷性、塗装性を有するが、更に印刷性、塗装性等を向上させる目的で表面処理を行うこともできる。表面処理の方法に特に限定は無く、物理的方法、化学的方法等を使用することができ、例えば、コロナ放電処理、オゾン処理、プラズマ処理、火炎処理、酸・アルカリ処理等を挙げることができる。これらのうち、コロナ放電処理が実施の容易さ、コスト、連続処理が可能等の点から好ましい。
本発明の制振・防音材料を床材、壁材、天井材等のように、フィルム、シート、タイル、ボード等の平面構造を有する成形品の製造に用いる場合、単層構造と多層構造の何れの構造にすることも可能である。他の形状の成形品についても、必要に応じて多層構造とすることができる。多層構造の場合には、組成、組成分布、分子量、分子量分布等の異なる本発明の水添共重合体や水添共重合体組成物、充填剤、難燃剤の種類や配合量の異なる本発明の制振・防音材料、他の樹脂成分や材料等を各層に使用することができる。互いに異なる複数の共重合体を積層することにより、広い温度範囲での制振、防音性能を発揮することができる。
本発明の変性水添共重合体又は変性水添共重合体組成物は電線被覆材料として用いることもできる。この場合、本発明の変性水添共重合体又は変性水添共重合体組成物に充填剤及び/又は難燃剤を配合することが好ましい。本発明の電線被覆材料は電気絶縁性、可とう性、皮むき性に優れるので、電線、電力ケーブル、通信ケーブル、送電用ケーブルなどの被覆用材料として好適である。
本発明の変性水添共重合体組成物を用いて電線被覆材料を調製する場合には、前述の成分(a)と前述の成分(b)の配合割合は、成分(a)/成分(b)の重量比率で100/0〜5/95、好ましくは95/5〜10/90、更に好ましくは95/5〜20/80である。
本発明の電線被覆材料に用いる充填剤としては、「発泡体」の項で例示した充填材(成分(j))を使用することができる。また、難燃剤としては、「建築材料」の項で例示した難燃剤(成分(l))を使用することができる。好ましい難燃剤も建築材料と同様である。
充填剤及び/又は難燃剤の添加量としては、変性水添共重合体又は変性水添共重合体組成物の5〜95重量%であり、好ましくは10〜80重量%、更に好ましくは20〜70重量%である。充填剤と難燃剤は必要に応じ2種以上を併用しても良い。2種以上の充填剤や2種以上の難燃剤を用いるか、充填剤と難燃剤を併用してもかまわない。充填剤と難燃剤を併用する場合には、その合計量が上記範囲内であることが好ましい。
本発明の電線被覆材料には、必要に応じて任意の添加剤を配合することができる。添加剤の種類は、熱可塑性樹脂やゴム状重合体の配合に一般的に用いられるものであれば特に制限はない。例えば、前述の「ゴム・プラスチック配合薬品」(日本国、ラバーダイジェスト社編)などに記載された各種添加剤が使用できる。
更に本発明の電線被覆材料は発泡成形体に加工して使用することもできる。本発明の電線被覆材料を発泡成形体とすることにより、軽量化、柔軟性向上、意匠性向上等を図ることができる。本発明の電線被覆材料を発泡させる方法には、無機系発泡剤、有機系発泡剤等の化学的発泡剤を用いる化学的方法や、物理発泡剤等を用いる物理的方法等があり、いずれも発泡剤の添加等により材料内部に気泡を分布させることができる。発泡剤としては、上記の「発泡体」の項で例示した発泡剤(成分(k))を使用することができる。発泡剤の配合量は、本発明の変性水添共重合体あるいは変性水添共重合体組成物100重量部に対して0.1〜8重量部、好ましくは0.3〜6重量部、さらに好ましくは0.5〜5重量部である。
本発明の変性水添共重合体を用いて、以下のα又はβの組成を有する高周波融着性組成物を調製することができる。
α)本発明の変性水添共重合体100重量部、並びに
エチレン−アクリル酸エステル共重合体、エチレン−酢酸ビニル共重合体、及び分子鎖中に水酸基を有する化合物からなる群より選ばれる少なくとも一種の成分(以下、屡々、成分(m)と称する)1〜50重量部、又は
β)本発明の変性水添共重合体100重量部、成分(m)1〜50重量部、並びに上記成分(m)とは異なる熱可塑性樹脂及びゴム状重合体から選ばれる少なくとも1種の成分5〜150重量部。
高周波融着性組成物とは、高周波又はマイクロ波による融着が可能な組成物、即ち、高周波融着成形可能な組成物である。
本発明の高周波融着性組成物に用いるエチレン−酢酸ビニル共重合体は、最終的な組成物の柔軟性やシール性、特に高周波ウェルダー適性、押出し加工性などの点で、酢酸ビニル含有率が5重量%以上であることが好ましく、特に好ましくは5〜20重量%である。
また、分子鎖中に水酸基を有する化合物としては、多価アルコール化合物、フェノール化合物、ビニルアルコール系樹脂、エポキシ基含有化合物、両末端水酸基含有樹脂及び水酸基グラフトポリオレフィン系樹脂などが挙げられる。
、α−オレフィン成分としてエチレンが用いられており、エチレン−酢酸ビニル樹脂をポリビニルアルコール樹脂と同様に鹸化反応に付して得られるエチレン−ビニルアルコール共重合体樹脂(EVOH)がよく知られている。上記したPVAに関しては、多くのものが市販されており、これらを使用することができる。市販品の例としては、日本国、(株)クラレの「ポバール」(商品名)や、日本国、日本合成化学(株)の「ゴーセノール」(商品名)が挙げられる。また、EVOHとしては、エチレン含有量が15〜90モル%のエチレン−酢酸ビニル共重合体を鹸化して得られる鹸化度が30〜100%の重合体が好ましい。これに相当する市販品の例としては、日本国、(株)クラレの「エバール」(商品名)や日本国、日本合成化学(株)の「ソアノール」(商品名)などが挙げられる。
両末端水酸基含有樹脂とは、ポリブタジエン、ポリイソプレン及び石油樹脂等の両末端にヒドロキシ基、カルボキシ基を含む酸素原子含有炭化水素化物である。その分子量は、10,000以下、好ましくは5,000以下のものが好適である。両末端水酸基含有樹脂についても、市販されているものが使用できる。市販品の例としては、日本国、三菱化成(株)製の「ポリテールH」(商品名)や、日本国、出光石油化学(株)製の「エポール」(商品名)等が挙げられる。
水酸基グラフトポリオレフィン系樹脂とは、ポリプロピレンなどのポリオレフィンに有機過酸化物などを使用して水酸基をグラフトさせたグラフト変性ポリオレフィンであり、日本国、三洋化成(株)製の「ユーメックス」( 商品名)が市販されている。
上記の成分(m)は、単独で使用しても良く、また、2種類以上の混合物として使用してもよい。
本発明の高周波融着性組成物は柔軟性、耐磨耗性、耐傷付き性に優れ、かつ高周波又はマイクロ波による融着が可能である。このような高周波融着性組成物は、そのままでも、或いは各種添加剤を配合した後でも、シート、フィルム、不織布や繊維状の成形品などの各種形状の射出成形品、中空成形品、圧空成型品、真空成形品、押出成形品に活用することもできる。これらの成形品は、食品包装材料、医療用器具材料、家電製品及びその部品、自動車部品・工業部品・家庭用品・玩具等の素材、履物用素材などの用途分野において、基材に高周波融着させて利用できる。
本発明の変性水添共重合体又は変性水添共重合体組成物をスラッシュ成形材料として用いることができる。具体的には、インストルメントパネルなどの自動車内装用の表皮などの表皮材の材料に適した加工性、耐傷つき性を有するスラッシュ成形材料、該スラッシュ成形材料からなるスラッシュ成形用パウダー、及びそれらからなる表皮材を提供する。
本発明のスラッシュ成形材料としては、本発明の変性水添共重合体(a)と熱可塑性樹脂(b)及び/又はゴム状重合体(b)を含有する変性水添共重合体組成物を用いる。変性水添共重合体組成物における成分(b)の配合量は、成分(a)/成分(b)の重量比で、50〜97/50〜3、好ましくは70〜95/30〜5、更に好ましくは80〜90/20〜10である。
本発明のスラッシュ成形材料には、必要に応じて任意の添加剤を配合することができる。添加剤の種類は、熱可塑性樹脂やゴム状重合体の配合に一般的に用いられるものであれば特に制限はない。例えば、前述の「ゴム・プラスチック配合薬品」(日本国、ラバーダ
イジェスト社編)などに記載された各種添加剤が使用できる。
ゲル分率=(W2 /W1 )×100。
架橋剤は、変性水添共重合体組成物に架橋構造を導入させて耐熱性を付与する目的で使用されるものであり、前述の成分(e)の有機過酸化物、成分(f)の加硫促進剤を使用することができ、また前述の成分(g)や成分(h)などを併用することができる。有機過酸化物等の架橋剤の使用量は、通常、変性水添共重合体組成物100重量部に対し、0.1〜7重量部、好ましくは0.5〜5重量部であり、架橋助剤の使用量は、変性水添共重合体組成物100重量部に対し、通常0.03〜5重量部、好ましくは0.05〜4重量部である。
架橋構造を導入するには、例えば、変性水添共重合体組成物と有機過酸化物等の架橋剤と、さらに必要に応じて、架橋助剤とをドライブレンドしたのち、加圧ニーダーを用いて120〜230℃で溶融混練する方法や、2軸押出機で連続的に溶融混練する方法などが挙げられる。
本発明のスラッシュ成形材料及びスラッシュ成形材料からなるスラッシュ成形用パウダーを用いて得られる表皮材は、自動車内装材であるインストルメントパネル、天井、ドア、座席シート、ピラー、ステアリングホイール、取っ手など、家具、雑貨、家屋の内張りなどの表皮材として有用である。
本発明の変性水添共重合体及び変性水添共重合体組成物に粘着付与剤(以下、屡々、成分(n)と称する)を配合し、粘接着性組成物を調製することができる。このような粘接着性組成物は粘着力等の粘着特性のバランス性能や高温加熱下における溶融粘度安定性に優れるので、例えば、粘着性テープ、粘着性シート又はフィルム、粘着性ラベル表面保護シート又はフィルムの粘着層や、接着剤に活用することができる。
本発明の変性水添共重合体組成物を用いて粘接着性組成物を調製する場合には、変性水添共重合体組成物における成分(a)と成分(b)の配合割合は、成分(a)/成分(b)の重量比で50/50〜97/3、好ましくは60/40〜95/5、更に好ましくは70/30〜90/10である。
粘接着性組成物の製造方法に特に限定はなく、公知の混合機、ニーダーなどを用いて加熱下で均一混合する方法で調製することができる。
粘接着性組成物は、良好な溶融粘度、粘着力を示し、また溶融粘度変化率も小さく、粘接着特性において優れたバランス性能を有する。これらの特徴を生かして各種粘着テープ・ラベル類、感圧性薄板、感圧性シート、表面保護シート・フィルム、各種軽量プラスチック成型品固定用裏糊、カーペット固定用裏糊、タイル固定用裏糊、接着剤などに利用でき、特に粘着性テープ用、粘着性シート・フィルム用、粘着性ラベル用、表面保護シート・フィルム用、接着剤用として有用である。
本発明の変性水添共重合体にアスファルト(以下、屡々、成分(o)と称する)を配合することにより、アスファルト組成物を調製することができる。このようなアスファルト組成物は、伸度、高温貯蔵安定性等のアスファルト特性のバランスが良好であり、このような特性を生かして、例えば、道路舗装用アスファルト組成物、ルーフィング・防水シート用アスファルト組成物及びシーラント用アスファルト組成物として活用することができる。
アスファルト組成物に用いるアスファルトは、石油を精製した際の副産物(石油アスファルト)や、天然の産出物(天然アスファルト)として得られるもの、もしくはこれらと石油類を混合したものなどが挙げられ、その主成分は瀝青(ビチューメン)と呼ばれるものである。具体的には、ストレートアスファルト、セミブローンアスファルト、ブローンアスファルト、タール、ピッチ、オイルを添加したカットバックアスファルト、アスファルト乳剤などを使用することができる。これらは2種以上を混合して使用しても良い。
アスファルト組成物には、必要に応じて種々の添加剤を配合することができる。例えば、炭酸カルシウム、炭酸マグネシウム、タルク、シリカ、アルミナ、酸化チタン、ガラス繊維、ガラスビーズ等の無機充填剤;有機繊維、クマロンインデン樹脂等の有機補強剤;有機パーオキサイド、無機パーオキサイド等の架橋剤;チタン白、カーボンブラック、酸化鉄等の顔料;染料;難燃剤;酸化防止剤;紫外線吸収剤;帯電防止剤;滑剤;パラフィン系プロセスオイル、ナフテン系プロセスオイル、芳香族系プロセスオイル、パラフィン、有機ポリシロキサン、ミネラルオイル等の軟化剤;可塑剤;クマロンインデン樹脂、テルペン樹脂などの粘着付与樹脂などを添加剤として加えてもよい。
ー、スポイラー、エアバック装置の収納カバー等が挙げられる。医療用具の具体例としては、血液バッグ、血小板保存バック、輸液(薬液)バック、人工透析用バック、医療用チューブ、カテーテル等が挙げられる。その他、粘接着テープ・シート・フィルム基材、表面保護フィルム基材及び該フィルム用粘接着剤、カーペット用粘接着剤、ストレッチ包装用フィルム、熱収縮性フィルム、被覆鋼管用被覆材、シーラントなどに用いることができる。
上記の各種用途に適応した組成物に関する説明においても成形品について述べているが、次に、複層押出成形品及び複層射出成形品を例に、本発明の成形品について具体的に説明する。
本発明の変性水添共重合体又は変性水添共重合体組成物を用いた複層押出成形品は、本発明の変性水添共重合体、変性水添共重合体組成物又は上記した本発明の他の組成物(例えば、補強性充填剤配合物、架橋物や建築材料)を熱可塑性樹脂及び/又はゴム状重合体と共押出することにより製造した複層シートを熱成形した複層押出成形品である。また、上記の多層フィルム・シートを熱成形したものも複層押出成形品である。
共押出法は1つのダイを共有する2台以上の押出機を使用し、1台以上の押出機に本発明の変性水添共重合体、変性水添共重合体組成物又は本発明の他の組成物を投入し、他方の1台以上の押出機に熱可塑性樹脂及び/又はゴム状重合体を投入して複層シートを製造する。この複層シートを熱成形、例えば真空成形、圧空成形して複層押出成形品を得る。共押出用ダイとしてはマルチマニホールドダイ、コンバイニング、アダプターダイ、マルチスロットダイなどが使用される。マルチマニホールドダイ等を使用して複層中空成形品、多層チューブ状成形品を得ることもできる。
本発明の複層押出成形品において、使用する熱可塑性樹脂及びゴム状重合体としては、本発明の変性水添共重合体組成物に用いる成分(b)として例示したものを使用することができる。
本発明の複層押出成形品は、自動車の内外装部品、家具部品、家電・OA機器関連部品、食品包装材料・容器、医療用材料などに利用できる。特に、多層チューブ状成形品は、医療用チューブ(例えば血液回路チューブ、点滴用輸液チューブ、カテーテルなど)、ガーデンホース類などの家庭用ホース、自動販売機用チューブなどに利用できる。
本発明の変性水添共重合体又は変性水添共重合体組成物を用いた複層射出成形品は、本発明の変性水添共重合体、変性水添共重合体組成物又は上記した本発明の他の組成物(例えば、補強性充填剤配合物、架橋物や建築材料)を熱可塑性樹脂及び/又はゴム状重合体と二色射出成形法や複層インサート射出成形法にて成形した複層射出成形品である。
複層射出成形は2台以上の射出成形機を使用し、1台以上の射出成形機に本発明の変性水添共重合体、変性水添共重合体組成物又は上記した本発明の他の組成物を投入し、他方の1台以上の射出成形機に熱可塑性樹脂及び/又はゴム状重合体を投入して、最初に後者を成形しておく。次にこれを前者を射出成形する金型にインサートして、前者を射出成形して一体化させる。
本発明の複層射出成形品において、使用する熱可塑性樹脂及びゴム状重合体としては、本発明の変性水添共重合体組成物に用いる成分(b)として例示したものを使用すること
ができる。
また、本発明においては、金属部品と組み合わせた複層射出成形品を得ることもできる。本発明の複層射出成形品に用いる金属部品の材質や形状には特に制限はない。代表的なものは鉄、ステンレス、銅、真ちゅう、ニッケル等でできた部品、例えばボルト、金属芯等が含まれる。
本発明の複層射出成形品は相互の密着性が良く、自動車の内外装部品、家具部品、家電・OA機器関連部品などに幅広く利用できる。
I.変性水添共重合体
実施例1〜7及び比較例1においては、変性共重合体を製造し、それを水添して変性水添共重合体を得た。また、比較例2においては、市販の共重合体(市販のスチレン−ブタジエンランダム共重合体)を水添して水添共重合体を得た。
変性水添共重合体や水添共重合体に関する特性や物性は、以下の方法で測定した。
I−1)スチレン含有量
非変性共重合体のスチレン含有量は、紫外分光光度計(装置名:UV−2450;日本国、島津製作所製)を用いて測定した。
I−2)ポリスチレンブロック(H)含有量(Os値)
非変性共重合体のポリスチレンブロック(H)含有量は、I. M. Kolthoff, et al., J.
Polym. Sci. 1, 429 (1946)に記載の四酸化オスミウム分解法で測定した。共重合体の分解にはオスミウム酸の0.1g/125ml第3級ブタノ−ル溶液を用いた。(尚、ここで得られるポリスチレンブロック含有量を「Os値」と称する。)
・ブロックスチレン(St)強度:(6.9〜6.3ppm)積算値/2
・ランダムスチレン(St)強度:(7.5〜6.9ppm)積算値−3(ブロックSt強度)
・エチレン・ブチレン(EB)強度:全積算値−3{(ブロックSt強度)+(ランダムSt強度)}/8
・NMRで得られるポリスチレンブロック含有量(Ns値)=104(ブロックSt強度)/[104{(ブロックSt強度)+(ランダムSt強度)}+56(EB強度)]
・Os値=−0.012(Ns)2 +1.8(Ns)−13.0
非変性共重合体のビニル結合量は,赤外分光光度計(装置名:FT/IR−230;日本国、日本分光社製)を用い、ハンプトン法により算出した。
I−4)重量平均分子量及び分子量分布
変性共重合体や水添共重合体の重量平均分子量及び分子量分布は、GPC装置(米国、ウォーターズ製)を用いて測定した。溶媒にはテトラヒドロフランを用い、35℃で測定した。重量平均分子量と数平均分子量が既知の市販の標準ポリスチレンと標準ポリスチレン系ゲルのカラムを用いて作成した検量線を使用し、重量平均分子量を求めた。また、分
子量分布は、重量平均分子量(Mw)と数平均分子量(Mn)との比(Mw/Mn)である。
I−5)変性率
変性共重合体は、シリカ系ゲルカラムには吸着するが、ポリスチレン系ゲルカラムには吸着しないという特性があるので、この特性を利用して測定する。即ち、試料及び低分子量内部標準ポリスチレンを含む試料溶液に関して、上記I−4)に記載したのと同様に行った標準ポリスチレン系ゲルのカラムのGPCと、シリカ系ゲルカラム(米国、デュポン社製Zorbax)のGPCの両クロマトグラムを測定し、それらの差分より、シリカ系ゲルカラムへの変性共重合体の吸着量を測定し、変性率を求めた。
試料は、変性後の共重合体を用いた。
核磁気共鳴装置(装置名:DPX−400;ドイツ国、BRUKER社製)で測定した。
I−7)結晶化ピーク及び結晶化ピーク熱量
変性水添共重合体や水添共重合体の結晶化ピーク及び結晶化ピーク熱量はDSC(装置名:DSC3200S;日本国、マックサイエンス社製)で測定した。室温から30℃/分の昇温速度で150℃まで昇温し、その後10℃/分の降温速度で−100℃まで降温して結晶化カーブを測定して結晶化ピークの有無を確認した。また、結晶化ピークがある場合、そのピークが現れる温度を結晶化ピーク温度とし、結晶化ピーク熱量を測定した。
I−8)ダンロップ反発弾性率
ダンロップ反発弾性率は、BS903のダンロップ反発弾性試験に準拠して、23℃で測定した。
I−9)耐傷付き性(鉛筆引っかき試験)
JIS K5400の鉛筆引っかき試験に準拠して、耐傷付き性を測定した。硬度HBの鉛筆を使用し、温度が23℃、荷重が200gの条件下で(変性)水添共重合体からなる試料を引っかいた。引っかいた後の状態について、以下の基準に基づき目視で判定した。
100%モジュラスを柔軟性の指標とした。JIS
K6251に準拠して、(変性)水添共重合体の圧縮試験片の引張特性を測定し、100%延伸時の応力(以下、100%モジュラスと呼ぶ)を計測した。100%モジュラスは小さいほど柔軟性が良好であり、120kg/cm2 以下が好ましい。
I−11)耐磨耗性
磨耗試験器(装置名:AB−301型;日本国、テスター産業株式会社製)を用いて、摩擦布カナキン3号綿で成形シート表面(皮シボ加工面)を荷重500gで摩擦し、摩擦後の体積減少量を測定した。耐磨耗性は以下の基準に基づいて判定した。
T型剥離試験による接着強さの測定から接着性を評価した。(接着強さが大きい程,接着性が優れる。)
接着条件と剥離試験条件は下記である。
{接着条件}160℃,5分間予熱
5分間加圧( 1kg荷重/cm2)
{剥離試験}剥離速度:200mm/min.
尚、被着体には、アルミ板(厚み100μ)とPETフィルム(厚み50μ)を用いた。
なお、実施例で用いられる変性剤(後述のM1〜M5)と、得られる変性水添共重合体の構造との関係は次の通りである。
変性剤(M1〜M5)と構造式の関係:
M1: 式(III)においてC1 が式(d−1)の単位と式(e−1)の単位であり、D1 が式(f−1)の単位である構造を有する変性水添共重合体が得られる。
M2: 式(IV)においてC1 が式(d−1)の単位と式(e−1)の単位であり、D1 が式(f−1)の単位である構造を有する変性水添共重合体が得られる。
M3: 式(I)又は式(II)においてA1 が式(a−1)の単位と式(b−1)の単位であり、B1 が式(c−1)の単位である構造を有する変性水添共重合体が得られる。M4: 式(V)においてE1 が式(g−1)の単位であり、F1 が式(h−1)の単位と式(i−1)と式(j−1)の単位である構造を有する変性水添共重合体が得られる。M5: 式(V)においてE1 が式(g−1)の単位であり、F1 が式(h−1)の単位と式(i−1)と式(j−1)の単位である構造を有する変性水添共重合体が得られる。
<水添触媒の調整>
以下の実施例及び比較例において、(変性)共重合体の水添反応に用いた水添触媒は下記の方法で調製した。
窒素置換した反応容器に乾燥、精製したシクロヘキサン2リットルを仕込み、ビス(η145 −シクロペンタジエニル)チタニウムジ−(p−トリル)40ミリモルと分子量が約1000の1,2−ポリブタジエン(1,2−ビニル結合量約85%)150グラムを溶解した後,n−ブチルリチウム60ミリモルを含むシクロヘキサン溶液を添加して、室温で5分間反応させ、直ちにn−ブタノール40ミリモルを添加攪拌して室温で保存した。
内容積が10リットルの攪拌装置及びジャケット付き槽型反応器を2基使用し、共重合体の連続重合を以下の方法で行った。
ブタジエン濃度が24重量%のシクロヘキサン溶液を4.51リットル/hr、スチレン濃度が24重量%のシクロヘキサン溶液を5.97リットル/hr、モノマー(ブタジエンとスチレン合計)100重量部に対するn−ブチルリチウムの量が0.077重量部
となるような濃度に調整したn−ブチルリチウムのシクロヘキサン溶液を2.0リットル/hrで1基目の反応器の底部にそれぞれ供給し、更にN,N,N’,N’−テトラメチルエチレンジアミンの量がn−ブチルリチウム1モルに対して0.44モルとなる供給速度でN,N,N’,N’−テトラメチルエチレンジアミンのシクロヘキサン溶液を供給し、90℃で連続重合した。反応温度はジャケット温度で調整し、反応器の底部付近の温度は約88℃、反応器の上部付近の温度は約90℃であった。重合反応器における平均滞留時間は約45分であり、ブタジエンの転化率は、ほぼ100%、スチレンの転化率は99%であった。
1基目から出たポリマー溶液を2基目の底部へ供給し、それと同時に、スチレン濃度が24重量%のシクロヘキサン溶液を2.38リットル/hrの供給速度で2基目の底部に供給し、90℃で連続重合して共重合体(リビングポリマー)を得た。2基目の出口におけるスチレンの転化率は98%であった。
得られた共重合体を分析したところ、スチレン含有量は67重量%、ポリスチレンブロック(H)含有量が20重量%、ブタジエン部のビニル結合量が14重量%であった。
次に、得られた変性共重合体に、上記水添触媒を変性共重合体に対しチタンとして100ppm添加し、水素圧0.7MPa、温度65℃で水添反応を行った。反応終了後にメタノールを添加し、次に安定剤としてオクタデシル−3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネートを重合体100重量部に対して0.3重量部添加し、変性水添共重合体(ポリマー1)を得た。
ポリマー1の水添率は99%であった。また、NMR法で測定したポリマー1のNs値は21重量%であり、Ns値から求めたポリスチレンブロック含有量(Os値)は20重量%だった。さらに、上記と同じNMR法でスチレン含有量を計算したところ、67重量%であった。また、DSC測定の結果、結晶化ピ−クは無かった。ポリマー1の特性を表1に示した。
内容積が10リットルの攪拌装置及びジャケット付き槽型反応器を1基使用し、共重合体の連続重合を以下の方法で行った。
モノマーとしてブタジエンとスチレンを含有するシクロヘキサン溶液(ブタジエン/スチレンの重量比は30/70、モノマー濃度22重量%)を13.3リットル/hr、モノマー100重量部に対するn−ブチルリチウムの量が0.067重量部となるような濃度に調整したn−ブチルリチウムのシクロヘキサン溶液を1.0リットル/hrでそれぞれ反応器の底部へ供給し、更にN,N,N’,N’−テトラメチルエチレンジアミンの量がn−ブチルリチウム1モルに対して0.82モルとなる供給速度でN,N,N’,N’−テトラメチルエチレンジアミンのシクロヘキサン溶液を供給し、90℃で連続重合し、共重合体を得た。反応温度はジャケット温度で調整し、反応器の底部付近の温度は約87℃、反応器の上部付近の温度は約90℃であった。重合反応器における平均滞留時間は約45分であり、ブタジエンの転化率は、ほぼ100%、スチレンの転化率は約96%であった。
次に、実施例1と同様に変性と水添反応を行い、変性水添共重合体(ポリマー2)を得た。ポリマー2の特性を表1に示した。
モノマーを含有するシクロヘキサン溶液のブタジエン/スチレンの重量比を24/76
に変える以外は、実施例2と同様の方法で連続重合を行い、共重合体を得た。次に、実施例2と同様に変性と水添反応を行い、変性水添共重合体(ポリマー3)を得た。ポリマー3の特性を表1に示した。
[ 実施例4]
n−ブチルリチウムの供給量をモノマ−100重量部に対して0.07重量部となる濃度に変える以外は、実施例1と同様の方法で連続重合を行い、共重合体(リビングポリマー)を得た。
その後、得られたリビングポリマーに対して、変性剤としてN−メチルピロリドン(変性剤M2)を用いる以外は実施例1と同様に変性反応を行い変性共重合体を得た。
次に、実施例1と同様に水添反応を行い、変性水添共重合体(ポリマー4)を得た。尚、水添反応の際、水素供給量を減らし、水添率を85%にコントロ−ルした。ポリマー4の特性を表1に示した。
n−ブチルリチウムの供給量をモノマ−100重量部に対して0.21重量部となる濃度に変える以外は、実施例2と同様の方法で連続重合を行い、共重合体(リビングポリマー)を得た。
その後、得られたリビングポリマーに対して、変性剤としてテトラグリシジル−1,3−ビスアミノメチルシクロヘキサン(変性剤M3)を重合に使用したn−ブチルリチウムに対して0.4モル用いる以外は実施例1と同様に変性反応を行い変性共重合体を得た。
次に、実施例2と同様に水添反応を行い、変性水添共重合体(ポリマー5)を得た。ポリマー5の特性を表1に示した。
[ 実施例6]
内容積が10リットルの攪拌装置及びジャケット付き槽型反応器を1基使用し、共重合体を以下の方法で行った。
シクロヘキサン10重量部を反応器に仕込んで温度70℃に調整した後、n−ブチルリチウムを全使用モノマー(スチレンとブタジエンの合計)100重量部に対して0.072重量部、N,N,N’,N’−テトラメチルエチレンジアミンをn−ブチルリチウム1モルに対して0.8モル添加し、その後モノマーとしてスチレン10重量部を含有するシクロヘキサン溶液(モノマー濃度22重量%)を約3分間かけて添加し、反応器内温を約70℃に調整しながら30分間反応させた。
その後、更にモノマーとしてスチレン10重量部を含有するシクロヘキサン溶液(モノマー濃度22重量%)を約3分間かけて添加し、反応器内温を約70℃に調整しながら30分間反応させて、共重合体(リビングポリマー)を得た。
次に、上記で得られたリビングポリマーに対して、実施例1と同様に変性反応を行い(即ち、変性剤として変性剤M1を重合に使用したn−ブチルリチウムに対して当モル反応させて)変性共重合体を得た。得られた変性共重合体の変性率は85%であった。
次に、得られた変性共重合体を実施例1と同様に水添し、変性水添共重合体(ポリマー6)を得た。
ポリマー6の水添率は97%であった。また、DSC測定の結果、結晶化ピ−クは無かった。ポリマー6の特性を表1に示した。
内容積が10リットルの攪拌装置及びジャケット付き槽型反応器を1基使用し、共重合体を以下の方法で行った。
シクロヘキサン10重量部を反応器に仕込んで温度70℃に調整した後、n−ブチルリ
チウムを全使用モノマー100重量部に対して0.25重量部、N,N,N’,N’−テトラメチルエチレンジアミンをn−ブチルリチウム1モルに対して0.7モル添加し、その後モノマーとしてスチレン22重量部を含有するシクロヘキサン溶液(モノマー濃度22重量%)を約3分間かけて添加し、反応器内温を約70℃に調整しながら30分間反応させた。
次に、ブタジエン34重量部とスチレン44重量部を含有するシクロヘキサン溶液(モノマー濃度22重量%)を60分間かけて一定速度(0.104リットル/min.)で連続的に反応器に供給した。この間、反応器内温は約70℃になるように調整した。こうして、共重合体(リビングポリマー)を得た。
次に、上記で得られた共重合体(リビングポリマー)に対して、実施例5と同様に変性反応を行い(即ち、変性剤として変性剤M3を重合に使用したn−ブチルリチウムに対して0.4モル反応させて)変性共重合体を得た。得られた変性共重合体の変性率は80%であった。
次に、得られた変性共重合体を実施例1と同様に水添反応を行い、変性水添共重合体(ポリマー7)を得た。ポリマー7の特性を表1に示した。
1基目に供給するスチレン溶液の供給量を2.06リットル/hrに変更し、2基目に供給するスチレン溶液の供給量を1.37リットル/hrに変える以外は、実施例1と同様の方法で連続重合を行い、共重合体を得た。次に、実施例1と同様に変性と水添反応を行い、変性水添共重合体(ポリマー8)を得た。ポリマー8の特性を表1に示した。
[ 比較例2]
市販のスチレン−ブタジエンランダム共重合体(商品名:アサプレン6500;日本国、日本エラストマー(株)製)をベースポリマーとして用い、実施例1と同様に水添反応を行い、水添共重合体(ポリマー9)を得た。ポリマー9の特性を表1に示した。尚、ポリマー9に関しては、35℃に
4.7J/gの熱量を有する結晶化ピークが認められた。
実施例8及び比較例3において、樹脂状重合体組成物(即ち、樹脂としての特性を示す組成物)を製造した。
樹脂状重合体組成物の物性は、以下の方法で測定した。
II−1)引張特性(引張強さと伸び)
ASTM D638に準拠して測定した。引張速度は、5mm/分で行った。
[ 実施例8及び比較例3]
熱可塑性樹脂としてHIPS(高衝撃性ポリスチレン)(商品名:475D;日本国、A&Mスチレン(株)製)及びホモPP(ポリプロピレン)(商品名:PL500A;日本国、サンアロマー製)を使用し、ポリマー1を変性水添共重合体として用いた。
実施例8では、70重量部のHIPSと30重量部のホモPPと共に、6重量部のポリマー1を二軸押出機(装置名:PCM30;日本国、池貝鉄工社製)で混練し、ペレット化することにより組成物を得た。比較例3では、変性水添共重合体(ポリマー1)を用い
ないこと以外は実施例8と実質的に同様に組成物を製造した。押出条件は、シリンダー温度220℃、スクリュー回転数250rpmであった。得られた組成物を射出成形して試験片を調製した。
試験片の物性を測定した結果、変性水添共重合体を含む実施例8の組成物は引張強度が330Kg/cm2 、伸びが17%と優れた性能を示した。一方、変性水添共重合体を添加していない比較例3の組成物は、引張強度が270kg/cm2 であるが、伸びはわずか3%であった。
20重量部のポリマー2と熱可塑性樹脂としてポリアミド(商品名:アミランCM1017;日本国、東レ(株)製)80重量部からなる樹脂状重合体組成物(実施例9)、20重量部のポリマー2と熱可塑性樹脂としてポリエステル(商品名:三井PETSA135;日本国、三井化学(株)製)80重量部からなる樹脂状重合体組成物(実施例10)、20重量部のポリマー2とポリカーボネート(商品名:カリバー301−15;日本国、住友ダウ製)80重量部からなる樹脂状重合体組成物(実施例11)を得た。それぞれの組成物は、二軸押出機(装置名:PCM30;日本国、池貝鉄工社製)で混練し、ペレット化することにより得た。実施例9と実施例11での押出条件は、シリンダー温度260℃、スクリュー回転数100rpmであった。実施例10での押出条件は、シリンダー温度250℃、スクリュー回転数100rpmであった。
同様の方法で、変性剤で変性しない以外はポリマー2と同様の方法で得たポリマーを用い、実施例9〜11と同様にして比較例4〜6の樹脂状重合体組成物を得た。比較例4と比較例6での押出条件は、シリンダー温度260℃、スクリュー回転数100rpmであった。実施例5での押出条件は、シリンダー温度250℃、スクリュー回転数100rpmであった。
得られた組成物を射出成形して試験片を調製し、耐衝撃性を測定した。実施例9〜11の組成物は、比較例4〜6の組成物に比較して相容性、耐衝撃性の良好な組成物であった。
実施例12〜18において、ゴム状重合体組成物(即ち、ゴムとしての特性を示す組成物)を製造した。
ゴム状重合体組成物の物性は、以下の方法で測定した。
III−1)100%モデュラス、引張強さ、切断時伸び
JIS K6251(3号ダンベル試験片を使用)に準拠して測定した。日本国、島津製作所製のAGS−100D型引張試験機を用い、引張速度500mm/分にて測定した。
III−2)耐熱性
JIS K6260に準拠した圧縮永久ひずみ試験を行った。数値が小さい程、耐熱性が優れる。
測定条件は、温度70℃で22時間である。
III−3)耐磨耗性
I−11)の方法で測定した。
以下のゴム状重合体成分を用いて、表2に示した組成のゴム状重合体組成物を製造した。
SEBS:スチレンブタジエンブロック共重合体の水素添加物(商品名:タフテックH1221;日本国、旭化成(株)製)、
SEPS:スチレンイソプレンブロック共重合体の水素添加物(商品名:ハイブラー7125;日本国、クラレ(株)製)
変性水添共重合体としては、ポリマー1を用いた。
70重量部のポリマー1と30重量部のゴム状重合体を二軸押出機(装置名:PCM30;日本国、池貝鉄工社製)で混練し、ペレット化することにより組成物を得た。押出条件は、シリンダー温度230℃、スクリュー回転数300rpmであった。得られた組成物を圧縮成形して試験片を得た。
各試験片の引張特性を測定し、その結果を表2に示した。
以下のゴム状重合体成分,熱可塑性樹脂成分を用いて、表3に示した組成のゴム状重合体組成物を製造した。
<ゴム状重合体成分>
SEBS−1:スチレンブタジエンブロック共重合体の水素添加物(商品名:タフテックH1221;日本国、旭化成(株)製)、
SEBS−2: スチレンブタジエンブロック共重合体の水素添加物(商品名:タフテックH1272;日本国、旭化成(株)製)、
<熱可塑性樹脂成分>
PP−1:ランダムポリプロピレン(商品名:PC630A;日本国、サンアロマー製)PP−2:ホモポリプロピレン(商品名:PM801A;日本国、サンアロマー製)
PPE:ポリフェニレンエーテル樹脂[還元粘度が0.54のポリ(2,6−ジメチル−1,4−フェニレン)エーテルを合成した]
ABS:ABS樹脂(商品名:スタイラックABS121;日本国、旭化成(株)製)、<ゴム用軟化剤>
パラフィンオイル(商品名:ダイアナプロセスオイルPW−380;日本国、出光興産(株)製)
また、耐磨耗性に優れた本発明のゴム状重合体組成物は、建築材料及び電線被覆材料にも使用することができる。
[ 実施例19]
実施例14〜18と同様の方法で、表4に示した組成のゴム状重合体組成物を製造した。得られた組成物の特性を表4に示した。
実施例20において、難燃性組成物を製造した。
IV−1)硬さ
JIS K6253に従い、デュロメータタイプAで10秒後の値を測定した。 IV−2)引張強さ、切断時伸び
III−1)と同じ方法で測定した。
IV−3)耐磨耗性
I−11)の方法で測定した。
IV−4)難燃性
UL94に準じた難燃性試験で評価した。具体的には、試験片から短冊片(127mm×12.7mm)を切り出し、UL94に準じて難燃性試験を行った。そして、UL94の判定基準に基づきランク付けをした。
変性水添共重合体としてポリマー1を用い、難燃剤として水酸化マグネシウム(商品名:キスマ5A;日本国、協和化学工業株式会社製)を用いた。40重量部のポリマー1と60重量部の水酸化マグネシウムをヘンシェルミキサーで混合後、二軸押出機(装置名:PCM30;日本国、池貝鉄工社製)にて溶融混練し、組成物のペレットを得た。溶融混練の温度は220℃、スクリューの回転数は250ppmだった。
得られた組成物を圧縮成形して2mm厚の成形シートを作成し、試験片を得た。試験片の物性を測定し,その結果を表5に示した。
更に、実施例20の組成物の動的粘弾性スペクトルをARESダイナミックアナライザー(装置名:ARES-2KFRTN1-FCO-STD;日本国、レオメトリック・サイエンティフィック・エフ・イー(株)製)を用い、ねじりモード(測定周波数:1Hz)で求めた。動的粘弾性スペクトルを図1に示した。
実施例20の組成物の動的粘弾性スペクトルのtanδピークは室温近傍にあり、これは室温近傍での耐振性(振動を吸収・減衰する能力)が良好であることを意味する。このように優れた耐振性を示す組成物は、制振・防音材料や建築材料に使用することができる。
実施例1において、変性剤M1の代わりに変性剤としてN−(1,3−ジメチルブチリデン)−3−(トリエトキシシリル)−1−プロパンアミン(変性剤M4)を用い、実施例1と同様の方法で変性水添共重合体(ポリマー10)を得た。
また、同様に変性剤M1の代わりに変性剤としてγ−グリシドキシプロピルトリエトキシシラン(変性剤M5)を用い、実施例1と同様の方法で変性水添共重合体(ポリマー11)を得た。
これらの変性水添共重合体について、実施例1と同様に評価を行った。その結果、これらの変性水添共重合体はポリマー1と同様に優れた特性を示した。また、DSC測定の結果、結晶化ピークは無かった。
また、これらの変性水添共重合体を使用した以外は実施例14と同様にして組成物を製造し、実施例14と同様に評価を行った。その結果、これらの組成物は実施例14の組成物と同様に優れた性能を示した。
実施例1と同様の方法で、スチレン含有量が62重量%、ポリスチレンブロックの含有量が35重量%、ビニル結合量が15重量%、重量平均分子量13万、分子量分布が2
.2の変性水添共重合体(ポリマー12)を得た。また、DSC測定の結果、ポリマー12の結晶化ピ−クは無かった。
[ 実施例24]
実施例2と同様の方法で、スチレン含有量が85重量%、ポリスチレンブロックの含有量が13重量%、ビニル結合量が18重量%、重量平均分子量35万、分子量分布が2
.0の変性水添共重合体(ポリマー13)を得た。また、DSC測定の結果、ポリマー1
3の結晶化ピ−クは無かった。
ポリマー1と下記成分を使用し、多層フィルムを作製した。
(使用した樹脂)
PE;L2340(日本国、旭化成(株)製)
PP;F- 226D(日本国、グランドポリマー製)
[実施例25]
3層用T−ダイ及び単軸押出し機を組合せた三層フィルム押出成形機を用いて、厚さ60μm,層構成がPE/ポリマー1 /PE(各層の厚み比率は1/3/1)の3層フィルムを製膜した。2枚のフィルムを重ね、15mm幅で130℃でヒートシールを行った。その後,後剥離試験を行った結果、剥離強度1kgの良好なシール性が得られた。
[ 実施例26]
層構成がPP/ポリマー1(各層の厚み比率は1/1)である2層フィルムを実施例25と同様の方法で製膜を行い、厚み30μmのフィルムを得た。2枚のフィルムをポリマー1のヒートシール層同士が内側になるようにして重ね、15mm幅で、120℃でヒートシールを行った。その後剥離試験を行った結果、剥離強度3kgの良好なシール性が得られた。
実施例27において、アスファルト組成物を製造した。
アスファルト組成物の物性は、以下の方法で測定した。
VI−1)軟化点(リング&ボ−ル法)
JIS−K2207に準じて、組成物の軟化点を測定した。規定の環に試料を充填し、環をグリセリン中で水平に支え,試料の中央に3.5gの球を置いた。液温を5℃/分の速さで上昇させ、球の重さで試料が環台の底板に触れた時の温度を測定した。
VI−2)伸度
JIS−K2207に準じて測定した。試料を形枠に流し込んで規定の形状にした後、恒温水浴内で15℃に保持した。次に試料を5cm/分の速度で引っ張り、試料が切れるまでに伸びた距離を測定した。
VI−3)高温貯蔵安定性
製造直後のアスファルト組成物を内径50mm、高さ130mmのアルミ缶の上限まで流し込み、180℃のオーブン中で24時間加熱した。アルミ缶を取り出して自然冷却させ、室温まで下がったアスファルト組成物の下端から4cmと上端から4cmの部分をサンプルとして採取し、それぞれの軟化点を測定した。上層部と下層部の軟化点差を高温貯蔵安定性の尺度とした。軟化点差が小さいほど高温貯蔵安定性は良好である。
表6に示した組成のアスファルト組成物を製造した。750mlの金属缶にストレートアスファルト60−80(日本国、日本石油(株)製)を400g投入し、180℃のオイルバスに金属缶を充分に浸した。次に、溶融状態のアスファルトの中に所定量の変性水添共重合体を攪拌しながら少量づつ投入した。変性水添共重合体を全て投入した後に5,000rpmの回転速度で90分間攪拌してアスファルト組成物を得た。
得られたアスファルト組成物の特性を表6に示した。
使用した成分と評価方法を下記に示す。
(a)粘着付与剤:クリアロンP−105(日本国、ヤスハラケミカル製)
(b)軟化剤:ダイアナ プロセスオイルPW−90(日本国、出光興産製)
VII−1)溶融粘度(cP)
ブルックフィールド型粘度計を使用して、180℃における粘接着性組成物の溶融粘度を測定した。
VII−2)軟化点(リング&ボール法)
JIS−K2207に準じて、粘接着性組成物の軟化点を測定した。規定の環に試料を充填し、水中で水平に支え、試料の中央に3.5gの球を置き、液温を5℃/minの速さで上昇させたとき、球の重さで試料が環台の底板に触れたときの温度を測定した。
VII−3)溶融粘度変化率
ブルックフィールド型粘度計を使用して、180℃における混練直後の粘接着性組成物の溶融粘度をη160 とし、粘接着性組成物を180℃の温度雰囲気下に48時間放置 後の180℃の溶融粘度をη161 としたとき、以下の溶融粘度変化率を求め、熱安定性の尺度とした。
粘接着性組成物を溶融状態で取り出し、アプリケーターでポリエステルフィルムに厚さ50マイクロメートルになるようにコーティングし、粘着テープサンプルを作成し、粘着力を以下の方法で測定した。
25mm幅の粘着テープサンプルをステンレス板に張り付け、引き剥がし速度300mm/minで180度剥離力を測定した。
[ 実施例28]
100重量部のポリマー1に対して、上記粘着付与剤を300重量部、上記軟化剤を100重量部の配合比で配合して、180℃×2時間、1リットルの攪拌機付き容器で溶融混練し、ホットメルト型粘接着性組成物を得た。尚、該粘接着性組成物には、100重量部のポリマ−1に対して、安定剤として2−t−ブチル−6−(3−t−ブチル−2−ヒドロキシ−5−メチルべンジル)−4−メチルフェニルアクリレートを1重量部配合した。
得られた粘接着性組成物の溶融粘度(cP,at.180℃)は13,000(cP)
、軟化点は118℃、溶融粘度変化率(%)は8.0%、粘着力は1,700gf/10mmであった。
Claims (27)
- 共役ジエン単量体単位とビニル芳香族単量体単位とを含む非水添共重合体を水添して得られ、該ビニル芳香族単量体単位の重合体ブロック(H)を少なくとも1つ含有する水添共重合体と、
該水添共重合体に結合した、官能基含有変性剤基、
からなる変性水添共重合体であって、下記式(I)〜式(V)よりなる群から選ばれる式で表される、下記の(1)〜(4)の特性を有することを特徴とする変性水添共重合体。
(1) 該ビニル芳香族単量体単位の含有量が、該水添共重合体の重量に対して、60重量%を越え、90重量%未満であり、
(2) 該重合体ブロック(H)の含有量が、該非水添共重合体の重量に対して、0.1重量%〜40重量%であり、
(3) 重量平均分子量が10万を越え、100万以下であり、
(4) 該共役ジエン単量体単位の二重結合の水添率が70%以上である。
A1は、下記式(a−1)と式(b−1)のいずれかで表される結合単位を表し、
Nは窒素原子、Siは珪素原子、Oは酸素原子、Cは炭素原子、Hは水素原子を表し、
P1は該水添共重合体を表し、
R1a、R1b、R3、R4、R8〜R10及びR13〜R15は各々独立に炭素数1〜48の炭化水素基を表し、且つ、所望により、各々独立に、水酸基、エポキシ基、アミ
ノ基、シラノール基、炭素数1〜24のアルコキシシラン基よりなる群から選ばれる少なくとも1種の官能基を有してもよく、
R2、R11は各々独立に炭素数1〜48の炭化水素基を表し、
R5〜R7及びR12は各々独立に水素原子又は炭素数1〜48の炭化水素基を表し、
但し、R1a、R1b、R2〜R4及びR8〜R15には、所望により、各々独立に、水酸基、エポキシ基、アミノ基、シラノール基、アルコキシシラン基以外の結合様式で、酸素原子、窒素原子、硫黄原子、珪素原子よりなる群からから選ばれる少なくとも1種の原子が結合していてもよく、
k、l、m、oは各々独立に0以上の整数であり、但し、kとlは同時に0ではなく、nは1以上の整数である。 - 該変性水添共重合体に関して得られた示差走査熱量測定(DSC)チャートにおいて、−50〜100℃の範囲に結晶化ピークが実質的に存在しないことを特徴とする請求項1に記載の変性水添共重合体。
- 分子量分布が1.5〜5.0であることを特徴とする請求項1に記載の変性水添共重合体。
- 式(I)で表される請求項1に記載の変性水添共重合体。
- 式(II)で表される請求項1に記載の変性水添共重合体。
- 式(III)で表される請求項1に記載の変性水添共重合体。
- 式(IV)で表される請求項1に記載の変性水添共重合体。
- 式(V)で表される請求項1に記載の変性水添共重合体。
- 請求項1〜3のいずれかに記載の変性水添共重合体からなる発泡体。
- 請求項1〜3のいずれかに記載の変性水添共重合体からなる成形品。
- 請求項1〜3のいずれかに記載の変性水添共重合体からなる多層フィルム又は多層シート。
- 押出成形、射出成形、中空成形、圧空成形、真空成形、発泡成形、複層押出成形、複層射出成形、高周波融着成形、スラッシュ成形及びカレンダー成形からなる群より選ばれる方法によって得られる請求項1〜3のいずれかに記載の変性水添共重合体からなる成形品。
- 請求項1〜3のいずれかに記載の変性水添共重合体からなる建築材料。
- 請求項1〜3のいずれかに記載の変性水添共重合体からなる制振材料。
- 請求項1〜3のいずれかに記載の変性水添共重合体からなる防音材料。
- 請求項1〜3のいずれかに記載の変性水添共重合体からなる電線被覆材料。
- 請求項1〜3のいずれかに記載の変性水添共重合体を、加硫剤の存在下で架橋することにより得られる架橋変性水添共重合体。
- 請求項1〜3のいずれかに記載の変性水添共重合体である成分(a)の、成分(a)と成分(b)の合計100重量部に対して1〜99重量部、及び
該変性水添共重合体(a)以外の熱可塑性樹脂及び該変性水添共重合体(a)以外のゴム状重合体からなる群より選ばれる少なくとも1種の重合体である成分(b)の、成分(a)と成分(b)の合計100重量部に対して99〜1重量部
を包含する変性水添共重合体組成物。 - 請求項18に記載の変性水添共重合体組成物からなる発泡体。
- 請求項18に記載の変性水添共重合体組成物からなる成形品。
- 請求項18に記載の変性水添共重合体組成物からなる多層フィルム又は多層シート。
- 押出成形、射出成形、中空成形、圧空成形、真空成形、発泡成形、複層押出成形、複層射出成形、高周波融着成形、スラッシュ成形及びカレンダー成形からなる群より選ばれる方法によって得られる、請求項18に記載の変性水添共重合体組成物からなる成形品。
- 請求項18に記載の変性水添共重合体組成物からなる建築材料。
- 請求項18に記載の変性水添共重合体組成物からなる制振材料。
- 請求項18に記載の変性水添共重合体組成物からなる防音材料。
- 請求項18に記載の変性水添共重合体組成物からなる電線被覆材料。
- 請求項18に記載の変性水添共重合体組成物を、加硫剤の存在下で架橋することにより得られる架橋変性水添共重合体組成物。