JP2562929B2 - 内填物に対する保香特性に優れた性質を有する紙容器における封筒貼り部の形成方法 - Google Patents

内填物に対する保香特性に優れた性質を有する紙容器における封筒貼り部の形成方法

Info

Publication number
JP2562929B2
JP2562929B2 JP63045650A JP4565088A JP2562929B2 JP 2562929 B2 JP2562929 B2 JP 2562929B2 JP 63045650 A JP63045650 A JP 63045650A JP 4565088 A JP4565088 A JP 4565088A JP 2562929 B2 JP2562929 B2 JP 2562929B2
Authority
JP
Japan
Prior art keywords
surface layer
laminated sheet
paper container
layer
back surface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP63045650A
Other languages
English (en)
Other versions
JPH01218823A (ja
Inventor
一樹 山田
裕孝 角田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=12725252&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=JP2562929(B2) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP63045650A priority Critical patent/JP2562929B2/ja
Publication of JPH01218823A publication Critical patent/JPH01218823A/ja
Application granted granted Critical
Publication of JP2562929B2 publication Critical patent/JP2562929B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】 〈産業上の利用分野〉 本発明は内填物に対する保香特性に優れた性質を有す
る紙容器における封筒貼り部の形成方法に関するもの
で、内填物に対する保香特性に優れた性質を有する紙容
器成形用素材による封筒貼り部を、極めて効率良く形成
し得る方法を提供するものである。
〈従来の技術〉 従来の紙容器は、紙容器を得る際に使用される成形用
素材である積層シートの有する熱溶着能によって接合部
が形成されているのが普通であり、一般的には、容器内
の内填物と接する容器内周面層となる層がポリオレフィ
ン系樹脂層で形成されている成形用素材における前記ポ
リオレフィン系樹脂層の有する熱溶着能によって接合部
が形成されている。
〈発明が解決しようとする問題点〉 ところで、前記容器内周面層がポリオレフィン系樹脂
層で構成されている容器は、該容器の成形用素材たる積
層シートを得る際のポリオレフィン系樹脂層の形成時や
該積層シートによる紙容器の成形時に、ポリオレフィン
系樹脂が熱分解を受けて脂肪族炭化水素等の揮発性成分
を生成することとなり、この揮発性成分が容器内に収容
されている内填物内に移行する結果、内填物に変味や異
臭が発生するという弊害を有するばかりでなく、前記紙
容器の内周面層をなすポリオレフィン系樹脂層は、内填
物中の着香成分を吸着し易かったりあるいは透過し易か
ったりするため、容器内の内填物の風味が変化して損な
われ易いという欠点をも有する。
これに対して本発明は、内填物に対する保香性能に優
れた性質を奏する紙容器成形用素材によって紙容器を成
形する際の封筒貼り部を極めて効率良く形成する方法を
提供するものである。
〈問題点を解決するための手段〉 本第１の発明の内填物に対する保香特性に優れた性質
を有する紙容器における封筒貼り部の形成方法は、ポリ
オレフィン系樹脂による表面層と40℃以上のガラス転移
温度を有する低結晶性線状飽和ポリエステル樹脂による
裏面層とを具備する紙容器用積層シートによって、容器
内周面層が前記積層シートによる裏面層すなわち40℃以
上のガラス転移温度を有する低結晶性線状飽和ポリエス
テル樹脂層で構成される紙容器を得る際の封筒貼り部の
形成方法であって、前記積層シートの一方の側辺部上に
他方の側辺部を重畳した状態で、前記紙容器用積層シー
トにおける表面層と裏面層とを熱溶着することからなる
封筒貼り部の形成を、封筒貼り予定部分の接合面となる
紙容器用積層シートの表面層と裏面層とのそれぞれに火
炎処理を施すことによって前記表面層と裏面層とを熱溶
融させた後、両層が熱溶融状態にある間に前記積層シー
トの一方の側辺部と他方の側辺部との重畳部分を加圧す
るものである。
本第２の発明の内填物に対する保香特性に優れた性質
を有する紙容器における封筒貼り部の形成方法は、ポリ
オレフィン系樹脂による表面層とエチレン−ビニルアル
コール系共重合体による裏面層とを具備する紙容器用積
層シートによって、容器内周面層が前記積層シートによ
る裏面層すなわちエチレン−ビニルアルコール系共重合
体層で構成される紙容器を得る際の封筒貼り部の形成方
法であって、前記積層シートの一方の側辺部上に他方の
側辺部を重畳した状態で、前記紙容器用積層シートにお
ける表面層と裏面層とを熱溶着することからなる封筒貼
り部の形成を、封筒貼り予定部分の接合面となる紙容器
用積層シートの表面層と裏面層とのそれぞれに火炎処理
を施すことによって前記表面層と裏面層とを熱溶融させ
た後、両層が熱溶融状態にある間に前記積層シートの一
方の側辺部と他方の側辺部との重畳部分を加圧するもの
である。
前記構成からなる本第１の発明で利用する紙容器用積
層シートにおける裏面層、すなわち、40℃以上のガラス
転移温度を有する低結晶性線状飽和ポリエステル樹脂層
は、該樹脂層を構成している線状飽和ポリエステル樹脂
のガラス転移温度未満の温度雰囲気中で優れた保香性能
を発揮するものであり、一般的に、紙容器内の内填物が
40℃未満に維持されるものであることとの関係で、前記
線状飽和ポリエステル樹脂層による優れた保香性能が利
用し得るものである。
なお、前記線状飽和ポリエステル樹脂層は、低結晶性
の樹脂で形成されているものであるから、例えば、内填
物の充填を熱充填で行なう場合等の加熱を受けても、前
記ポリエステル樹脂層の熱接着特性が損なわれるような
ことがなく、ポリオレフィン系樹脂層との間の熱接着部
に優れた接着強度が得られるものである。
ガラス転移温度が40℃以上の飽和ポリエステル樹脂層
は、例えば、エチレングリコール，プロピレングリコー
ル,1,4−ブタンジオール,1,4−シクロヘキサンジメタノ
ール等のアルコール成分と、アジピン酸，セバシン酸等
の脂肪族ジカルボン酸、テレフタル酸，イソフタル酸，
ジフェニルジカルボン酸等の芳香族ジカルボン酸等によ
るジカルボン酸成分との共縮合重合体によって形成され
ているものであり、具体的には、エチレングリコールと
テレフタル酸，エチレングリコールとイソフタル酸とテ
レフタル酸,1,4−シクロヘキサンジメタノールとエチレ
ングリコールとテレフタル酸，プロピレングリコールと
イソフタル酸とテレフタル酸等の共縮合重合体を利用し
て形成し得るが、酸成分中の脂肪族ジカルボン酸成分が
10重量％以上になる共縮合重合体の場合には、この共縮
合重合体による飽和ポリエステル樹脂層は、その保香性
能が低下する傾向を有するので好ましくない。
なお、前記40℃以上のガラス転移温度を有する低結晶
性線状飽和ポリエステル樹脂層は、これが厚さ５μｍ未
満になると樹脂層の安定性が悪く、ヒートシールによる
密封性が悪くなり、また、200μｍを越えるようになる
と、得られる紙容器用積層シートが固くなって、折り曲
げ加工特性が悪くなることから、通常は、厚さ５〜200
μｍの範囲内で形成されるものである。
また、前記構成からなる本第２の発明で利用する紙容
器用積層シートにおける裏面層、すなわち、エチレン−
ビニルアルコール系共重合体樹脂層は、該樹脂層を構成
するエチレン−ビニルアルコール系共重合体のエチレン
含有量が25モル％未満の場合には、ヒートシールに要す
る温度が極めて高くなるため実用的でなく、またエチレ
ン含有量が60モル％を越える場合には、内填物における
着香成分の吸着傾向が高くなることから、エチレン含有
量が25〜60モル％のエチレン−ビニルアルコール系共重
合体を利用するのが好ましい。
なお、前記エチレン−ビニルアルコール系共重合体樹
脂層の場合には、該層の厚さが５μｍ未満になると樹脂
層の安定性が悪く、また、40μｍを越えるようになると
該樹脂層の耐衝撃性が低下するようになるので、エチレ
ン−ビニルアルコール系共重合体樹脂層は、５〜40μｍ
の範囲内で形成されていることが好ましい。
本各発明で利用する積層シートにおける表面層は、こ
れらの積層シートによって成形される紙容器に外部から
の耐水性を付与するものであると同時に、前述の各積層
シートの裏面層との間に火炎シール法による熱溶着性能
をもたらすものであり、例えば、低密度ポリエチレン，
中密度ポリエチレン，高密度ポリエチレン，エチレン−
酢酸ビニル共重合体，エチレン−アクリル酸共重合体，
エチレン−アクリル酸メチル共重合体，エチレン−α・
オレフィン共重合体，更にはポリプロピレン等によっ
て、厚さ３〜150μｍ程度に形成されているものであ
る。
本各発明で使用される紙容器用積層シートは、前記40
℃以上のガラス転移温度を有する低結晶性線状飽和ポリ
エステル樹脂層またはエチレン−ビニルアルコール系共
重合体樹脂層からなる裏面層と、ポリオレフィン系樹脂
による表面層とが、包装材用基材に積層されているもの
であって、紙容器に成形されるに適した積層シートとな
り得る包装材用基材、例えば、アルミニュウム箔，紙
層，オレフィン系樹脂層，ポリエステル延伸フィルム層
等を利用した厚さ40〜1000μｍ程度の包装材用基材が使
用されるものである。
なお、前述の40℃以上のガラス転移温度を有する低結
晶性線状飽和ポリエステル樹脂層またはエチレン−ビニ
ルアルコール系共重合体樹脂層からなる裏面層は、前記
包装材用基材に対して、例えば、接着性ポリオレフィン
系樹脂やイソシアネート系接着剤等の接着剤層を利用し
て積層されるのが一般的である。
前記各紙容器用積層シートは、例えば、ブリックタイ
プ，ゲーベルトップタイプ，更には円筒体等の紙容器に
成形されるものであり、主として胴貼り部分をなす封筒
貼り予定部分の接合面となる表面層と裏面層とに火炎処
理が施されるものである。
この封筒貼り部分の接合面となる表面層と裏面層とに
施される火炎処理は、通常10mm程度の細幅状からなるシ
ール予定部分に対して施されるものであって、シール部
の温度が180〜200℃程度，ガス圧5mmAq,空気圧35〜60mm
Aq程度の火炎処理装置によって、処理速度200m/min.程
度で実施されるもので、火炎処理された表面層すなわち
ポリオレフィン系樹脂層は、該樹脂層の１部分が溶融，
酸化されて、前記樹脂層の表面張力が当該積層シートの
裏面層の表面張力と同一程度となる程度に火炎処理され
るのが好ましく、また、火炎処理された裏面層すなわち
40℃以上のガラス転移温度を有する低結晶性線状飽和ポ
リエステル樹脂層またはエチレン−ビニルアルコール系
共重合体樹脂層は、前記火炎処理によって樹脂層表面が
荒らされ、微細な多数の凹凸群が前記樹脂層面に生成さ
れるように火炎処理されるのが好ましい。
〈実施例〉 以下、本発明の内填物に対する保香特性に優れた性質
を有する紙容器における封筒貼り部の形成方法の具体的
な構成を実施例をもって説明する。
実施例１ 秤量400g/m2の耐酸紙／厚さ15μｍのアイオノマー樹
脂「ハイミラン1652:三井デュポンポリケミカル（株）
製」層／厚さ９μｍのアルミニュウム箔／厚さ12μｍの
二軸延伸ポリエチレンテレフタレートフィルム層からな
る積層構成の包装材用基材に対して、前記包装材用基材
の耐酸紙面に、厚さ30μｍのポリオレフィン系樹脂「ミ
ラソン16P:三井石油化学工業（株）製」層からなる表面
層を形成し、また、前記包装材用基材の二軸延伸ポリエ
チレンテレフタレートフィルム層面に、厚さ30μｍのエ
チレン−α−オレフィン共重合体樹脂「ウルトゼックス
2020L:三井石油化学工業（株）製」層／厚さ10μｍの接
着性ポリオレフィン樹脂「アドマーAT469C:三井石油化
学工業（株）製」層／厚さ20μｍの線状飽和ポリエステ
ル樹脂「PET G 6763:ガラス転移温度81℃，イーストマ
ンコダック社製」層からなる三層共押し出しフィルム
を、ポリエステル樹脂層が裏面層となるようにして積層
することによって、本第１の発明で使用する紙容器用積
層シートの１実施例品を得た。
次いで、前記積層シートの相対向する１対の側辺部の
幅約10mmに亘る表面層と裏面層とを火炎処理に付した後
に、前記火炎処理が付された表面層と裏面層とを接当さ
せることからなる側辺部同士の重畳部を形成し、更に、
ゴムロールによる加圧を前記重畳部に施すことによっ
て、前記積層シートにおける裏面層が内周面層で構成さ
れている封筒貼り部をエンドレス状に形成した。
なお、前記火炎処理は、積層シートの表面層に対して
は、ガス圧5mmAq,空気圧39mmAqの予備処理用第１バーナ
ーと、ガス圧5mmAq,空気圧47mmAqの第２バーナーとによ
って、また、積層シートの裏面層に対しては、ガス圧5m
mAq,空気圧44mmAqの予備処理用第１バーナーと、ガス圧
5mmAq,空気圧60mmAqの第２バーナーとによって、コンベ
アスピード200m/min.で実施したもので、火炎処理面の
加熱温度は250℃である。
得られた封筒貼り部の接合面の剥離を手指先で行なっ
たところ、紙層内での断層破壊が生じてしまい、積層シ
ートの表面層と裏面層との間の界面を剥離することはで
きなかった。
比較例１ 前記実施例１で使用した紙容器用積層シートと同一の
構成の積層シートによって、前記積層シートにおける裏
面層が内周面積とされている封筒貼り部を、側辺部同士
の重畳部の上，下に320℃のヒートシールバーを接当
し、積層シート面が300℃になるまで、2Kg/cm2の圧力を
付加しながら接着することによって、形成した。
得られた封筒貼り部の接合面の剥離を手指先で行なっ
たところ、積層シートの表面層と裏面層との間の界面で
の剥離が容易に行なえた。
実施例２ 坪量400g/m2の耐酸紙／厚さ15μｍのアイオノマー樹
脂「ハイミラン1652:三井デュポンポリケミカル（株）
製」層／厚さ９μｍのアルミニュウム箔／厚さ12μｍの
二軸延伸ポリエチレンテレフタレートフィルム層からな
る積層構成の包装材用基材に対して、前記包装材用基材
の耐酸紙面に、厚さ30μｍのポリオレフィン系樹脂「ミ
ラソン16P:三井石油化学工業（株）製」層からなる表面
層を形成し、また、前記包装材用基材の二軸延伸ポリエ
チレンテレフタレートフィルム層面に、厚さ30μｍのエ
チレン−α−オレフィン共重合体樹脂「ウルトゼックス
1520L:三井石油化学工業（株）製」層／厚さ15μｍの接
着性ポリオレフィン系樹脂「ノバテック220L:三菱化成
工業（株）製」層／厚さ15μｍのエチレン−ビニルアル
コール系共重合体「エバールG156:（株）クラレ製」層
からなる三層共押し出しフィルムを、該フィルムにおけ
るエチレン−ビニルアルコール系共重合体層が裏面層と
なるようにして積層することにより、本第２の発明で使
用する紙容器用積層シートの１実施例品を得た。
次いで、前記積層シートの相対向する１対の側辺部の
幅約10mmに亘る表面層と裏面層とに対して、前述の実施
例１で施したものと同一の条件による火炎処理を施し、
更にゴムロールによる加圧処理によって、前記積層シー
トにおける裏面層が内周面層で構成されている封筒貼り
部を、エンドレス状に形成した。
得られた封筒貼り部の接合面の剥離を手指先で行なっ
たところ、紙層内での断層破壊が生じてしまい、積層シ
ートの表面層と裏面層との間の界面を剥離することはで
きなかった。
比較例２ 前記実施例２で使用した紙容器用積層シートと同一の
構成の積層シートによって、前記積層シートにおける裏
面層が内周面層とされている封筒貼り部を、側辺部同士
の重畳部の上，下に320℃のヒートシールバーを接当
し、積層シート面が300℃になるまで、2Kg/cm2の圧力を
付加しながら接着することによって、形成した。
得られた封筒貼り部の接合面の剥離を手指先で行なっ
たところ、積層シートの表面層と裏面層との間の界面で
の剥離が容易に行なえた。
〈発明の作用，効果〉 本各発明の内填物に対する保香特性に優れた性質を有
する紙容器における封筒貼り部の形成方法は、ポリオレ
フィン系樹脂による表面層と、40℃以上のガラス転移温
度を有する低結晶性線状飽和ポリエステルまたはエチレ
ン−ビニルアルコール系共重合体樹脂による裏面層とを
具備する紙容器用積層シートによって、容器内周面層が
前記積層シートによる裏面層で構成される紙容器を得る
際に、前記積層シートの一方の側辺部上に他方の側辺部
を重畳した状態で、前記紙容器用積層シートにおける表
面層と裏面層とを熱溶着することからなる紙容器におけ
る封筒貼り部の形成方法において、前記封筒貼り予定部
分の接合面となる紙容器用積層シートの表面層と裏面層
とのそれぞれに火炎処理を施すことによって、前記表面
層と裏面層とを熱溶融させた後、両層が熱溶融状態にあ
る間に前記積層シートの一方の側辺部と他方の側辺部と
の重畳部分を加圧するものである。
しかして、前記本各発明においては、火炎処理された
表面層すなわちポリオレフィン系樹脂層は、該樹脂層の
１部分が溶融，酸化されて、前記樹脂層の表面張力が、
当該積層シートの裏面層の表面張力と同一程度となる程
度となっており、また、火炎処理された裏面層すなわち
40℃以上のガラス転移温度を有する低結晶性線状飽和ポ
リエステル樹脂層、または、エチレン−ビニルアルコー
ル系共重合体樹脂層は、該樹脂層表面が荒らされて微細
な多数の凹凸群が前記樹脂層面に生成されているので、
火炎処理に続く加圧工程で、表面が溶融状態にあるポリ
オレフィン系樹脂層が、低結晶性線状飽和ポリエステル
樹脂層、または、エチレン−ビニルアルコール系共重合
体樹脂層の表面の凹凸の凹部内に深く食い込むようにし
て侵入し、両者の間の強固な接合が得られるものであ
る。
本各発明は、保香性能に優れた性質を有する40℃以上
のガラス転移温度を有する低結晶性線状飽和ポリエステ
ル樹脂層またはエチレン−ビニルアルコール系共重合体
樹脂層と接合される樹脂層として、ポリオレフィン系樹
脂層を選択することによって、初めて、火炎処理を利用
した熱融着法によって、前記異種樹脂層同士の間の強固
な接合が可能となったものであり、火炎処理を利用した
熱融着法によって封筒貼り部を形成するものであるか
ら、内填物に対する保香特性に優れた性質を有する紙容
器における封筒貼り部を、極めて効率の良い熱シール方
法で形成し得るものである。
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 // Ｂ２９Ｋ 23:00 67:00 Ｂ２９Ｌ 9:00 22:00

Claims (2)

    (57)【特許請求の範囲】
  1. 【請求項１】ポリオレフィン系樹脂による表面層と40℃
    以上のガラス転移温度を有する低結晶性線状飽和ポリエ
    ステル樹脂による裏面層とを具備する紙容器用積層シー
    トによって、容器内周面層が前記積層シートによる裏面
    層で構成される紙容器を得る際に、前記積層シートの一
    方の側辺部上に他方の側辺部を重畳した状態で、前記紙
    容器用積層シートにおける表面層と裏面層とを熱溶着す
    ることからなる紙容器における封筒貼り部の形成方法に
    おいて、前記封筒貼り予定部分の接合面となる紙容器用
    積層シートの表面層と裏面層とのそれぞれに火炎処理を
    施すことによって、前記表面層と裏面層とを熱溶融させ
    た後、両層が熱溶融状態にある間に、前記積層シートの
    一方の側辺部と他方の側辺部との重畳部分を加圧するこ
    とを特徴とする内填物に対する保香特性に優れた性質を
    有する紙容器における封筒貼り部の形成方法。
  2. 【請求項２】ポリオレフィン系樹脂による表面層とエチ
    レン−ビニルアルコール系共重合体による裏面層とを具
    備する紙容器用積層シートによって、容器内周面層が前
    記積層シートによる裏面層で構成される紙容器を得る際
    に、前記積層シートの一方の側辺部上に他方の側辺部を
    重畳した状態で、前記紙容器用積層シートにおける表面
    層と裏面層とを熱溶着することからなる紙容器における
    封筒貼り部の形成方法において、前記封筒貼り予定部分
    の接合面となる紙容器用積層シートの表面層と裏面層と
    のそれぞれに火炎処理を施すことによって、前記表面層
    と裏面層とを熱溶融させた後、両層が熱溶融状態にある
    間に、前記積層シートの一方の側辺部と他方の側辺部と
    の重畳部分を加圧することを特徴とする内填物に対する
    保香特性に優れた性質を有する紙容器における封筒貼り
    部の形成方法。
JP63045650A 1988-02-26 1988-02-26 内填物に対する保香特性に優れた性質を有する紙容器における封筒貼り部の形成方法 Expired - Lifetime JP2562929B2 (ja)