JP2531722B2 - 金属膜を含む反射防止膜付着透明体 - Google Patents
金属膜を含む反射防止膜付着透明体Info
- Publication number
- JP2531722B2 JP2531722B2 JP63003450A JP345088A JP2531722B2 JP 2531722 B2 JP2531722 B2 JP 2531722B2 JP 63003450 A JP63003450 A JP 63003450A JP 345088 A JP345088 A JP 345088A JP 2531722 B2 JP2531722 B2 JP 2531722B2
- Authority
- JP
- Japan
- Prior art keywords
- refractive index
- oxide
- layer
- antireflection film
- transparent plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 ［産業上の利用分野］ 本発明は、透明基板の光の反射を低減する反射防止膜
付着透明板、特に光を吸収する金属層、または金属合金
層を有する多層反射防止膜付着透明板に関する。
付着透明板、特に光を吸収する金属層、または金属合金
層を有する多層反射防止膜付着透明板に関する。
［従来の技術］ 従来、光を吸収する金属層を有する多層反射防止膜付
着透明板として、透明基板の一方の面に誘電体のみから
なる多層反射防止膜を形成し、もう一方の面に透過率が
30％〜80％となるような厚みの光吸収のある金属層を形
成したものが特開昭62−58202で公知である。この金属
層を有する多層反射防止膜付着透明板は多層反射防止膜
により透明板の反射率を下げると共に金属層により光を
吸収して透明基板の透過率を調整しようとするものであ
る。
着透明板として、透明基板の一方の面に誘電体のみから
なる多層反射防止膜を形成し、もう一方の面に透過率が
30％〜80％となるような厚みの光吸収のある金属層を形
成したものが特開昭62−58202で公知である。この金属
層を有する多層反射防止膜付着透明板は多層反射防止膜
により透明板の反射率を下げると共に金属層により光を
吸収して透明基板の透過率を調整しようとするものであ
る。
［発明が解決しようとする課題］ しかしながら、このような金属層を有する多層反射防
止膜付着透明板は透明基板表面に付着した多層反射防止
膜により、その表面反射は極めて小さくすることができ
るが、透明基体のもう一方の面と金属層との界面の反射
等により、該透明板全体の反射率を約１％程度にしか低
下できず、この金属層を有する多層反射防止膜付着透明
板をCRT等のガラス製ディスプレイに貼付けて使用する
場合でも、その全体の視感度反射率を0.6％程度にまで
しか下げることができなかった。
止膜付着透明板は透明基板表面に付着した多層反射防止
膜により、その表面反射は極めて小さくすることができ
るが、透明基体のもう一方の面と金属層との界面の反射
等により、該透明板全体の反射率を約１％程度にしか低
下できず、この金属層を有する多層反射防止膜付着透明
板をCRT等のガラス製ディスプレイに貼付けて使用する
場合でも、その全体の視感度反射率を0.6％程度にまで
しか下げることができなかった。
［課題を解決するための手段］ この発明は、このような従来の問題点を解決すべくな
されもので有り、透明板全体の反射率を極めて小さくし
た反射防止膜付着透明板を提供することを目的としたも
のである。
されもので有り、透明板全体の反射率を極めて小さくし
た反射防止膜付着透明板を提供することを目的としたも
のである。
この目的を達成するために、この発明は屈折率が1.40
〜1.70の透明基板の表面に光の反射を防止するための反
射防止膜を付着した透明板において、該反射防止膜が1.
37〜1.50の屈折率で、0.5×λ0/4〜1.8×λ0/4（但しλ
０は中心波形、以下同じ）の光学膜厚の第１の低屈折率
誘電体層と、30Å〜75Åのチタン、クロム、ジルコニウ
ム、モリブデン、ニッケル、ニッケル・クロム合金、及
びステンレスのいずれか一つの金属層または合金層と、
2.00〜2.40の屈折率で、0.3×λ0/4〜0.8×λ0/4の光学
膜厚の高屈折率誘電体層と、1.37〜1.50の屈折率で、1.
0×λ0/4〜1.2×λ0/4の光学膜厚の第２の低屈折率誘電
体層とからなり、該各層が該透明基板表面から順次形成
されてなる。
〜1.70の透明基板の表面に光の反射を防止するための反
射防止膜を付着した透明板において、該反射防止膜が1.
37〜1.50の屈折率で、0.5×λ0/4〜1.8×λ0/4（但しλ
０は中心波形、以下同じ）の光学膜厚の第１の低屈折率
誘電体層と、30Å〜75Åのチタン、クロム、ジルコニウ
ム、モリブデン、ニッケル、ニッケル・クロム合金、及
びステンレスのいずれか一つの金属層または合金層と、
2.00〜2.40の屈折率で、0.3×λ0/4〜0.8×λ0/4の光学
膜厚の高屈折率誘電体層と、1.37〜1.50の屈折率で、1.
0×λ0/4〜1.2×λ0/4の光学膜厚の第２の低屈折率誘電
体層とからなり、該各層が該透明基板表面から順次形成
されてなる。
本発明において、屈折率が1.40〜1.70の透明基板とし
ては通常ガラス板、または合成樹脂板が用いられる。合
成樹脂板としてはアクリル樹脂板、ポリカーボネイト樹
脂板、またはポリスチレン樹脂板が好んで用いられる。
ては通常ガラス板、または合成樹脂板が用いられる。合
成樹脂板としてはアクリル樹脂板、ポリカーボネイト樹
脂板、またはポリスチレン樹脂板が好んで用いられる。
また、本発明において前記第１及び第２の低屈折率誘
電体層として、フッ化マグネシウム（MgF2）または酸化
シリコン（SiO2）のいずれかを用いるのが好ましい。
電体層として、フッ化マグネシウム（MgF2）または酸化
シリコン（SiO2）のいずれかを用いるのが好ましい。
更にまた、本発明において、前記第１及び第２の高屈
折率誘電層として、酸化チタン（TiO2）、酸化タンタル
（Ta2O5）、酸化ジルコニウム（ZrO2）、チタン酸プラ
セオジム（PrTiO3）、酸化ハフニウム（HfO2）、硫化亜
鉛（ZnS）、酸化スズ（SnO2）、酸化インジウム（In2O
3）、及び酸化インジウムと酸化スズとの混合物（ITO）
のいずれかを用いることができる。
折率誘電層として、酸化チタン（TiO2）、酸化タンタル
（Ta2O5）、酸化ジルコニウム（ZrO2）、チタン酸プラ
セオジム（PrTiO3）、酸化ハフニウム（HfO2）、硫化亜
鉛（ZnS）、酸化スズ（SnO2）、酸化インジウム（In2O
3）、及び酸化インジウムと酸化スズとの混合物（ITO）
のいずれかを用いることができる。
酸化インジウムと酸化スズとの混合物としては酸化イ
ンジウムと酸化スズとの重量比が95:5の割合のものを用
いるのが好ましい。
ンジウムと酸化スズとの重量比が95:5の割合のものを用
いるのが好ましい。
［作 用］ このような反射防止膜中に光吸収のある金属層または
合金層を組入れた本発明においては透明板に入射する光
は無論、透明板の裏面での反射光がこの金属層、または
合金層で吸収減衰されるため、反射防止膜付着透明板全
体の反射光は小さくなる。
合金層を組入れた本発明においては透明板に入射する光
は無論、透明板の裏面での反射光がこの金属層、または
合金層で吸収減衰されるため、反射防止膜付着透明板全
体の反射光は小さくなる。
［実施例１］ 以下、本発明の実施例について図面を引用して説明す
る。
る。
第１図において、１は屈折率が1.51のガラス板であっ
て、ガラス１の表面に反射防止膜６が形成された。反射
防止膜６はガラス板１側から順次屈折率1.37で、光学膜
厚が1.349×λ0/4（但しλ０＝504nm、以下同じ）のフ
ッ化マグネシウム層２と、膜厚が66Aのステンレス層３
（ステンレスは72重量％のニッケル、16重量％のクロ
ム、及び８重量％の鉄の合金である）と、屈折率が2.40
で、光学膜厚が0.6432×λ0/4の酸化チタン層４と、屈
折率が1.37で、光学膜厚が1.0859×λ0/4のフッ化マグ
ネシウム層５とからなり、各層はガラス板１面上に順次
真空蒸着法で形成された。
て、ガラス１の表面に反射防止膜６が形成された。反射
防止膜６はガラス板１側から順次屈折率1.37で、光学膜
厚が1.349×λ0/4（但しλ０＝504nm、以下同じ）のフ
ッ化マグネシウム層２と、膜厚が66Aのステンレス層３
（ステンレスは72重量％のニッケル、16重量％のクロ
ム、及び８重量％の鉄の合金である）と、屈折率が2.40
で、光学膜厚が0.6432×λ0/4の酸化チタン層４と、屈
折率が1.37で、光学膜厚が1.0859×λ0/4のフッ化マグ
ネシウム層５とからなり、各層はガラス板１面上に順次
真空蒸着法で形成された。
反射防止膜６を形成したガラス板１のガラス面側をガ
ラスと同じ程度の屈折率を有する接着剤を用いて、CRT
のフェースプレートに接着してガラス面側の反射をなく
した。このときの反射防止膜付着ガラス板の反射特性を
第２図に、透過率特性を第３図に、視感度反射率及び視
感度透過率を第１表に夫々示した。
ラスと同じ程度の屈折率を有する接着剤を用いて、CRT
のフェースプレートに接着してガラス面側の反射をなく
した。このときの反射防止膜付着ガラス板の反射特性を
第２図に、透過率特性を第３図に、視感度反射率及び視
感度透過率を第１表に夫々示した。
［実施例２］ 第１図に示したと同様な構成の反射防止膜付着ガラス
板であって、反射防止膜６の多層膜を以下の如く変え
た。
板であって、反射防止膜６の多層膜を以下の如く変え
た。
すなわち、反射防止膜６は屈折率が1.37で、光学膜厚
が1.5757×λ0/4のフッ化マグネシウム層２と、膜厚が4
6Åのニッケル・クロム合金層３（90重量％のニッケル
と10重量％のニッケル・クロム合金）と、屈折率が2.15
で、光学膜厚が0.6959×λ0/4のチタン酸プラセオジム
層と、屈折率が1.37で、光学膜厚が1.1162×λ0/4のフ
ッ化マグネシウム層５とからなり、これらの層はガラス
板１上に順次真空蒸着法により形成された。
が1.5757×λ0/4のフッ化マグネシウム層２と、膜厚が4
6Åのニッケル・クロム合金層３（90重量％のニッケル
と10重量％のニッケル・クロム合金）と、屈折率が2.15
で、光学膜厚が0.6959×λ0/4のチタン酸プラセオジム
層と、屈折率が1.37で、光学膜厚が1.1162×λ0/4のフ
ッ化マグネシウム層５とからなり、これらの層はガラス
板１上に順次真空蒸着法により形成された。
このようにして得られた反射防止膜付着ガラス板を実
施例１と同様にして光学特性を測定したところ、第１表
に示したとおり視感度反射率が0.08％、視感度透過率が
65％であった。
施例１と同様にして光学特性を測定したところ、第１表
に示したとおり視感度反射率が0.08％、視感度透過率が
65％であった。
［実施例３］ 第１図に示したと同様な構成の反射防止膜付着ガラス
板であって、反射防止膜６の多層膜を以下の如くした。
板であって、反射防止膜６の多層膜を以下の如くした。
すなわち、反射防止膜６は屈折率が1.37で、光学膜厚
が0.5969×λ0/4のフッ化マグネシウム層２と、膜厚が3
0Åのステンレス層３（ステンレスは72重量％のニッケ
ルと16重量％のクロムと８重量％の鉄とからなる合金で
ある）と、屈折率が2.40で、光学膜厚が0.3561×λ0/4
の酸化チタン層４と、屈折率が1.37で、光学膜厚が1.14
67×λ0/4のフッ化マグネシウム層５層とからなり、各
層はガラス板１面上に順次真空蒸着法で形成された。
が0.5969×λ0/4のフッ化マグネシウム層２と、膜厚が3
0Åのステンレス層３（ステンレスは72重量％のニッケ
ルと16重量％のクロムと８重量％の鉄とからなる合金で
ある）と、屈折率が2.40で、光学膜厚が0.3561×λ0/4
の酸化チタン層４と、屈折率が1.37で、光学膜厚が1.14
67×λ0/4のフッ化マグネシウム層５層とからなり、各
層はガラス板１面上に順次真空蒸着法で形成された。
このようにして得られた反射防止膜付着ガラス板を実
施例１と同様にして光学特性を測定したところ、第１表
に示したとおり、視感度反射率が0.1％、視感度透過率
が80％であった。
施例１と同様にして光学特性を測定したところ、第１表
に示したとおり、視感度反射率が0.1％、視感度透過率
が80％であった。
［発明の効果］ 以上のように本発明の反射防止膜付着透明板は反射防
止膜中に光吸収のある金属層、または合金層を組入れる
ことにより、CRT等の反射防止板として使用した場合に
は視感度反射率を0.1％以下のきわめて小さくすること
ができる。
止膜中に光吸収のある金属層、または合金層を組入れる
ことにより、CRT等の反射防止板として使用した場合に
は視感度反射率を0.1％以下のきわめて小さくすること
ができる。
従って、CRTの画面が見やすくなり、更に光吸収の金
属層、または合金層によりCRTの蛍光面に入射する光が
吸収されてコントラストがよくなる。また前記金属層ま
たは合金層をアースすることにより、前記透明板に帯電
防止機能を付与することができる。
属層、または合金層によりCRTの蛍光面に入射する光が
吸収されてコントラストがよくなる。また前記金属層ま
たは合金層をアースすることにより、前記透明板に帯電
防止機能を付与することができる。
図面は本発明の実施例を示すものであって、第１図は反
射防止膜付着透明板の断面図、第２図は反射防止膜付着
透明板の反射特性、第３図はその透過率特性である。 1:透明板、2:第１の低屈折率誘電体層、 3:金属層または合金層、 4:高屈折率誘電体層 5:第２の低屈折率誘電体層、 6:反射防止膜
射防止膜付着透明板の断面図、第２図は反射防止膜付着
透明板の反射特性、第３図はその透過率特性である。 1:透明板、2:第１の低屈折率誘電体層、 3:金属層または合金層、 4:高屈折率誘電体層 5:第２の低屈折率誘電体層、 6:反射防止膜
Claims (3)
- 【請求項１】屈折率が1.40〜1.70の透明基板の表面に光
の反射を防止するための反射防止膜を付着した透明板に
おいて、該反射防止膜が1.37〜1.50の屈折率で、0.5×
λ0/4〜1.8×λ0/4（但しλ０は中心波形、以下同じ）
の光学膜厚の第１の低屈折率誘電体層と、30Å〜75Åの
チタン、クロム、ジルコニウム、モリブデン、ニッケ
ル、ニッケル・クロム合金、及びステンレスのいずれか
一つの金属層または合金層と、2.00〜2.40の屈折率で、
0.3×λ0/4〜0.8×λ0/4の光学膜厚の高屈折率誘電体層
と、1.37〜1.50の屈折率で、1.0×λ0/4〜1.2×λ0/4の
光学膜厚の第２の低屈折率誘電体層とからなり、該各層
が該透明基板表面から順次形成されてなる金属層を含む
反射防止膜付着透明板。 - 【請求項２】前記第１及び第２の低屈折率誘電体層がフ
ッ化マグネシウム、または酸化シリコンのいずれかであ
る特許請求の範囲第１項に記載の金属膜を含む含む反射
防止膜付着透明板。 - 【請求項３】前記高屈折率誘電体層が酸化チタン、酸化
タンタル、酸化ジルコニウム、チタン酸プラセオジウ
ム、酸化ハフニウム、硫化亜鉛、酸化スズ、酸化インジ
ウム、及び酸化インジウムと酸化スズとの混合物（IT
O）のいずれかである特許請求の範囲第１項または第２
項に記載の金属膜を含む反射防止膜付着透明板。