JP2023022055A - 熱収縮性ポリエステル系フィルムロール - Google Patents
熱収縮性ポリエステル系フィルムロール Download PDFInfo
- Publication number
- JP2023022055A JP2023022055A JP2022179001A JP2022179001A JP2023022055A JP 2023022055 A JP2023022055 A JP 2023022055A JP 2022179001 A JP2022179001 A JP 2022179001A JP 2022179001 A JP2022179001 A JP 2022179001A JP 2023022055 A JP2023022055 A JP 2023022055A
- Authority
- JP
- Japan
- Prior art keywords
- film
- thickness
- film roll
- heat
- maximum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
1.温湯中90℃・10秒でのフィルム主収縮方向の収縮率が30%以上である熱収縮性ポリエステル系フィルムが巻き取られてなるフィルムロールで、該熱収縮性ポリエステルフィルム及び該フィルムロールにおいて、下記要件(1)~(5)を満たすことを特徴とする熱収縮性ポリエステル系フィルムロール。
(1)フィルムロール巻長が2000m以上25000m以下
(2)フィルムロール幅が400mm以上2500mm以下
(3)フィルム厚みが5μm以上40μm以下
(4)フィルムロールの表層におけるフィルム幅方向の厚みムラにおいて、厚みパターンが凹部になっている箇所を有し、厚み差の最も大きい凹部(最大凹部)において、該最大凹部における最大厚み差とフィルム平均厚みより求めた最大凹部の厚みムラが10%以下
(5)フィルムロール表層の巻硬度が400以上800以下
2.フィルムロールの表層から巻長1000m間隔でサンプリングした各試料のフィルムの幅方向の厚みムラにおいて、前記最大凹部における最大厚み差とフィルム平均厚みより求めた厚みムラが全ての試料で10%以下である1.に記載の熱収縮性ポリエステル系フィルムからなるフィルムロール。
3.前記最大凹部における凹部の両端のいずれかの最大厚み箇所との幅方向屈折率の差の絶対値が0.01以下である1.~2.のいずれかに記載の熱収縮性ポリエステル系フィルムロール。
4.フィルムロールの幅方向全体の厚みムラが13%以下である1.~3.のいずれかに記載の熱収縮性ポリエステル系フィルムロール。
5.フィルムの巻外面と巻内面の静摩擦係数と動摩擦係数がいずれも0.1以上0.8以下である1.~4.のいずれかに記載の熱収縮性ポリエステル系フィルムロール。
熱収縮率={(収縮前の長さ-収縮後の長さ)/収縮前の長さ}×100(%) ・・式1
凹部の厚みムラ=(凹部の最大高さ厚み-凹部の最小高さ厚み)÷平均厚み
×100(%) ・・式2
{(厚みの最大値―厚みの最小値)÷平均厚み}×100(%) ・・式3
せん断速度
γ=6Q/(W×H2) ・・式4
γ;せん断速度(sec-1)
Q;原料の押出し機からの吐出量(cm3/sec)
W;ダイス出口の開口部の幅(cm)
H;ダイスのLipギャップ(cm)
ドラフト比は高い方が長手方向の厚みムラが良好となり好ましいが、ドラフト比が高いとダイスの樹脂吐出部に樹脂カス等が付着し、生産性が悪くなるので高すぎるのは好ましくない。またドラフト比が低いと、長手方向の厚みムラが悪くなるので好ましくない。ドラフト比は10以上80以下が好ましく、更に好ましくは20以上70以下である。
加えて、以下のスリット条件を採用することによりスリットの際に発生する弛みを低減することが好ましい。
本発明の好ましい様態は、巻長1000m毎に試料を採取して測定し、全ての試料について厚みムラ(最大凹部および幅方向全体の厚みムラ)が所定範囲となることである。フィルムロール全長におけるフィルム幅方向の厚みムラ(最大凹部および幅方向全体の厚みムラ)の好適な範囲は前述の通りである。
フィルムを10cm×10cmの正方形に裁断し、温水温度90℃±0.5℃の温水中において、無荷重状態で10秒間処理して熱収縮させた後、フィルムの横方向(主収縮方向)の寸法を測定し、下記(1)式に従い熱収縮率を求めた。
熱収縮率=((収縮前の長さ-収縮後の長さ)/収縮前の長さ)×100(%) 式(1)
ロールをスリッターに設置した。その後、ロール表層から1m除去した後にフィルムロールを幅方向に全幅、長手方向に40mmにサンプリングし、ミクロン計測器社製の連続接触式厚み計を用いて、5m/sで連続的に幅方向の厚みを測定した。測定時の最大厚みをTmax.、最小厚みをTmin.、平均厚みをTave.とし、下式(2)から、フィルム幅方向の厚みムラを算出した。
厚みムラ={(Tmax.-Tmin.)/Tave.}×100 (%) 式(2)
上記した幅方向の連続接触厚みを求め、図1に示すように最大凹部になっている箇所を探した。下式(3)より最大凹部の厚みムラを求めた。また最大凹部の両端での高さが異なるときは、高い方の値を選択して求めた。
最大凹部の厚みムラ=(最大凹部の最大高さ厚み-最大凹部の最小高さ厚み)÷平均厚み×100(%) 式(3)
ロールをスリッターに設置した。その後、ロール表層から1m除去した後に上述した方法でロール幅方向の最大凹部の厚みムラを測定した。測定後、スリッターで1000m巻返して上述した方法でロール幅方向の凹部の厚みムラを測定した。1000m巻返してロール幅方向の最大凹部の厚みムラを測定を繰り返し行った。
上記した最大凹部と最大凹部両端の厚みが高い方の位置のフィルムの幅方向の屈折率をアッベ屈折計を用いて測定した。そして下式(4)より差を求め、絶対値とした。
最大凹部と最大凹部両端との屈折率の差=|最大凹部の幅方向屈折率―最大凹部の両端の高い方の位置の幅方向屈折率| 式(4)
JIS K-7125に準拠し、引張試験機(ORIENTEC社製テンシロン)を用
い、23℃・65%RH環境下で、フィルムの表面と裏面とを接合させた場合の静摩擦係数と動摩擦係数を求めた。なお、上側のフィルムを巻き付けたスレッド(錘)の重量は、1.5kgであり、スレッドの底面積の大きさは、縦63mm×横63mmであった。また、摩擦測定の際の引張速度は、200mm/min.であった。
フィルムロールから幅方向には全幅、長手方向へは4m以上6m以下にサンプリングし平面台の上にのせた。この時、長手方向へ連続して平面性が他の部分よりも少しでも悪くなっている帯状の箇所が目視で確認されればそれを弛みとした。以下のように評価を行った。
弛み無し : ○
弛みが1箇所以上有り : ×
スイス プロセオ社の硬さ試験機パロテスター2を使用して、ロール幅方向に端部から100mm間隔で測定を行った。ロール幅方向に測定した値の平均値を、測定値として用いた。
合成例1(ポリエステルの合成)
<熱収縮性フィルムの製造方法>
このようにスリットして幅2200mm、1200mm、800mm、巻長15000mのフィルムロールを得た。
そして得られたフィルムの特性を上記した方法によって評価した。評価結果を表3に示す。目標の特性となるフィルムが得られ、弛みが良好な結果であった。なお、弛みについては表3の結果(フィルムロール表層)に加えて1000m毎の試料を全て評価した結果、上記3つのフィルムロールの全ての試料において○(弛み無し)であった。
上記したチップCをチップEに変更した以外は実施例1と同様の方法でフィルムロールを得た。また、この時のTgは69℃であった。
そして得られたフィルムの特性を上記した方法によって評価した。評価結果を表3に示す。得られたフィルムは実施例1同様に良好な結果であった。
そして得られたフィルムの特性を上記した方法によって評価した。評価結果を表3に示す。得られたフィルムは実施例1同様に良好な結果であった。
未延伸フィルムの厚みを83μmとし、得られたフィルム厚みが15μmとなった以外は実施例1と同様の方法でフィルムロールを得た。
そして得られたフィルムの特性を上記した方法によって評価した。評価結果を表3に示す。得られたフィルムは実施例1同様に良好な結果であった。
このようにスリットして幅2200mm、1200mm、800mm、巻長15000mのフィルムロールを得た。
そして得られたフィルムの特性を上記した方法によって評価した。評価結果を表3に示す。凹部の厚みムラが悪く、フィルムに弛みを確認した。
未延伸フィルムの厚みを209μmとし、横延伸での予熱温度を90℃から95℃に変更し、得られたフィルム厚みが38μmとなった以外は比較例1と同様の方法でフィルムロールを得た。
そして得られたフィルムの特性を上記した方法によって評価した。評価結果を表3に示す。得られたフィルムは比較例1同様にフィルムに弛みを確認した。なお、弛みについては表3の結果(フィルムロール表層)に加えて1000m毎の試料を全て評価した結果、上記3つのフィルムロールの全ての試料において×(弛みが1箇所以上有り)であった。
Claims (3)
- フィルムを構成する樹脂層が全てポリエステル樹脂層で、フィルムを構成する全ポリエステル樹脂中における多価アルコール成分100モル%中あるいは多価カルボン酸成分100モル%中の非晶質成分となりうる1種以上のモノマー成分の合計が15モル%以上で、温湯中90℃・10秒でのフィルム主収縮方向の収縮率が30%以上である熱収縮性ポリエステル系フィルムが巻き取られてなるフィルムロールで、該熱収縮性ポリエステルフィルム及び該フィルムロールにおいて、下記要件(1)~(6)を満たすことを特徴とする熱収縮性ポリエステル系フィルムロール。
(1)フィルムロール巻長が2000m以上25000m以下
(2)フィルムロール幅が400mm以上2500mm以下
(3)フィルム厚みが5μm以上40μm以下
(4)フィルムロールの表層におけるフィルム幅方向の厚みムラにおいて、厚みパターンが凹部になっている箇所を有し、厚み差の最も大きい凹部(最大凹部)において、該最大凹部における最大厚み差とフィルム平均厚みより求めた最大凹部の厚みムラが8%以下
(5)フィルムロール表層の巻硬度が400以上800以下
(6)前記最大凹部における凹部の両端のいずれかの最大厚み箇所との幅方向屈折率の差の絶対値が0.008以下である - フィルムロールの表層から巻長1000m間隔でサンプリングした各試料のフィルムの幅方向の厚みムラにおいて、前記最大凹部における最大厚み差とフィルム平均厚みより求めた厚みムラが全ての試料で10%以下である請求項1に記載の熱収縮性ポリエステル系フィルムからなるフィルムロール。
- フィルムロールの幅方向全体の厚みムラが7%以下である請求項1又は2に記載の熱収縮性ポリエステル系フィルムロール。