JP2022177186A - 感熱記録体 - Google Patents
感熱記録体 Download PDFInfo
- Publication number
- JP2022177186A JP2022177186A JP2022148797A JP2022148797A JP2022177186A JP 2022177186 A JP2022177186 A JP 2022177186A JP 2022148797 A JP2022148797 A JP 2022148797A JP 2022148797 A JP2022148797 A JP 2022148797A JP 2022177186 A JP2022177186 A JP 2022177186A
- Authority
- JP
- Japan
- Prior art keywords
- group
- urea compound
- heat
- recording material
- sensitive recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
近年、感熱記録体は、各種チケット用、レシート用、ラベル用、銀行のATM用、ガスや電気の検針用、車馬券等の金券用など多様な用途にも拡大してきており、そのため、耐水性、画像部の耐可塑剤性、白紙部の耐熱性、耐油性、過酷な条件下における画像部及び白紙部の保存性など様々な性能が必要とされてきている。
このような要求に対して、特定の2種類の顕色剤を組み合わせて用いることにより、耐水性、画像部の耐可塑剤性、白紙部の耐熱性などを向上させた感熱記録体(特許文献1)や、感熱記録体の発色濃度、白色度、及び印字部の保存性などの要求性能を向上させるための顕色剤としてのウレア化合物(特許文献2、3)が開示されている。
また、感熱記録体の保存安定性を向上させる方法として、感熱記録層の上に保護層を設ける方法が知られている。
この感熱記録層や保護層にシラン変性アクリル樹脂を含有させることにより、印刷時のヘッド摩耗を改善したり、感熱記録体の画像保存性や耐水性を改善させることが知られている(特許文献4、5等)。
更に、保護層に、ガラス転移点(Tg)が50℃より高く95℃以下であるアクリル系樹脂を含有させることにより、感熱記録体が十分な耐水性等を有することが知られている(特許文献6等)。
すなわち、本発明は、支持体上に、無色ないし淡色の電子供与性ロイコ染料及び電子受容性顕色剤を含有する感熱記録層及び該感熱記録層上に保護層を有する感熱記録体において、該感熱記録層が、電子受容性顕色剤として、下記(1)又は(2)で表されるウレア化合物を含有し、該保護層が、下記(4)又は(5)で表されるアクリル系樹脂を含有し、該保護層中の該アクリル系樹脂の含有量が15.0~50.0重量%であり、該アクリル系樹脂の最低造膜温度(MFT)が0℃~25℃である、感熱記録体である。
(1)下記一般式(化5)で表されるウレア化合物、
(2)下記一般式(化3)で表される第2のウレア化合物、
(4)ガラス転移点(Tg)が50℃より高く95℃以下である非コアシェル型アクリル系樹脂
(5)下記(a1)、(a2)及び(a3)を(b)の存在下で重合させて成る共重合体Aから成るコアと、下記(a1)及び(a2)を(b)の存在下で重合させて成る共重合体Bから成るシェルとから成るコアシェル型粒子の水性エマルジョンである、シラン変性アクリル系樹脂。
(a1)少なくとも1種の(メタ)アクリル酸エステル
(a2)アルコキシシリル基及びエチレン性二重結合を有する単量体
(a3)カルボキシル基及びエチレン性二重結合を有する単量体
(b)アリル基及びポリオキシエチレン鎖を有する硫酸塩を含有する重合性界面活性剤
以下、本発明の感熱記録体の感熱記録層で使用される各種材料を例示するが、バインダー、架橋剤、顔料などは上記課題に対する所望の効果を阻害しない範囲で、必要に応じて設けられた各塗工層にも使用することが可能である。
(1)下記一般式(化5)で表される第1のウレア化合物、
(2)下記一般式(化3)で表される第2のウレア化合物、
(3)下式(化4)で表される第3のウレア化合物
一般式(化5)中、R3は、置換若しくは無置換であってもよい、アルキル基、アラルキル基又はアリール基を表す。このアルキル基は、例えば、直鎖状、分岐鎖状若しくは脂環状のアルキル基であり、炭素数は好ましくは1~12である。このアラルキル基の炭素数は好ましくは7~12であり、このアリール基炭素数は好ましくは6~12のである。また、これらが置換されている場合、その置換基は、好ましくは、炭素数1~12のアルキル基、炭素数1~12のアルコキシ基、炭素数6~12のアリール基又はハロゲン原子である。また、複数のR3は、同じであっても異なっていてもよい。
一般式(化5)のベンゼン環中のR3-SO2-O-の位置は、同じであっても異なってもよく、好ましくは、3位、4位又は5位である。
一般式(化2)のベンゼン環中のR2の位置は、同じであっても異なってもよく、好ましくは3位、4位又は5位である。
一般式(化6)のベンゼン環中のR9の位置は、同じであっても異なってもよく、好ましくは3位、4位又は5位、好ましくは4位である。
このアルキル基(アルキルカルボニルオキシ基、アルキルカルボニルアミノ基、アルキルスルホニルアミノ基、モノアルキルアミノ基、ジアルキルアミノ基に含まれるものを含む。)、及びアリール基(アリールオキシ基、アリールカルボニルオキシ基、アリールカルボニルアミノ基、アリールスルホニルアミノ基、アリールアミノ基に含まれるものを含む。)については、上記一般式(化2)中のアルキル基及びアリール基と同様に定義される。
このアルコキシ基は、例えば、直鎖状、分岐鎖状若しくは脂環状のアルコキシ基であり、炭素数は好ましくは1~12である。
一般式(化3)のベンゼン環中の-O-(CONH)m-SO2-置換フェニル基の位置は、好ましくは、3位、4位又は5位である(下記一般式(化7)及び一般式(化8)においても同じ。)。
一般式(化3)中、mは0~2、好ましくは0~1の整数を表す。
本発明の感熱記録層中の前記第1のウレア化合物の同含有量は、1.0~50.0重量%、好ましくは5.0~40.0重量%である。また、前記第2のウレア化合物の同含有量は、5.0~50.0重量%、好ましくは5.0~40.0重量%である。
3,3-ビス(p-ジメチルアミノフェニル)-6-ジメチルアミノフタリド〔別名クリスタルバイオレットラクトン〕、3,3-ビス(p-ジメチルアミノフェニル)フタリド〔別名マラカイトグリーンラクトン〕
3-ジエチルアミノ-6-メチルフルオラン、3-ジエチルアミノ-6-メチル-7-アニリノフルオラン、3-ジエチルアミノ-6-メチル-7-(o,p-ジメチルアニリノ)フルオラン、3-ジエチルアミノ-6-メチル-7-クロロフルオラン、3-ジエチルアミノ-6-メチル-7-(m-トリフルオロメチルアニリノ)フルオラン、3-ジエチルアミノ-6-メチル-7-(o-クロロアニリノ)フルオラン、3-ジエチルアミノ-6-メチル-7-(p-クロロアニリノ)フルオラン、3-ジエチルアミノ-6-メチル-7-(o-フルオロアニリノ)フルオラン、3-ジエチルアミノ-6-メチル-7-(m-メチルアニリノ)フルオラン、3-ジエチルアミノ-6-メチル-7-n-オクチルアニリノフルオラン、3-ジエチルアミノ-6-メチル-7-n-オクチルアミノフルオラン、3-ジエチルアミノ-6-メチル-7-ベンジルアミノフルオラン、3-ジエチルアミノ-6-メチル-7-ジベンジルアミノフルオラン、3-ジエチルアミノ-6-クロロ-7-メチルフルオラン、3-ジエチルアミノ-6-クロロ-7-アニリノフルオラン、3-ジエチルアミノ-6-クロロ-7-p-メチルアニリノフルオラン、3-ジエチルアミノ-6-エトキシエチル-7-アニリノフルオラン、3-ジエチルアミノ-7-メチルフルオラン、3-ジエチルアミノ-7-クロロフルオラン、3-ジエチルアミノ-7-(m-トリフルオロメチルアニリノ)フルオラン、3-ジエチルアミノ-7-(o-クロロアニリノ)フルオラン、3-ジエチルアミノ-7-(p-クロロアニリノ)フルオラン、3-ジエチルアミノ-7-(o-フルオロアニリノ)フルオラン、3-ジエチルアミノ-ベンゾ〔a〕フルオラン、3-ジエチルアミノ-ベンゾ〔c〕フルオラン、3-ジブチルアミノ-6-メチル-フルオラン、3-ジブチルアミノ-6-メチル-7-アニリノフルオラン、3-ジブチルアミノ-6-メチル-7-(o,p-ジメチルアニリノ)フルオラン、3-ジブチルアミノ-6-メチル-7-(o-クロロアニリノ)フルオラン、3-ジブチルアミノ-6-メチル-7-(p-クロロアニリノ)フルオラン、3-ジブチルアミノ-6-メチル-7-(o-フルオロアニリノ)フルオラン、3-ジブチルアミノ-6-メチル-7-(m-トリフルオロメチルアニリノ)フルオラン、3-ジブチルアミノ-6-メチル-7-クロロフルオラン、3-ジブチルアミノ-6-エトキシエチル-7-アニリノフルオラン、3-ジブチルアミノ-6-クロロ-7-アニリノフルオラン、3-ジブチルアミノ-6-メチル-7-p-メチルアニリノフルオラン、3-ジブチルアミノ-7-(o-クロロアニリノ)フルオラン、3-ジブチルアミノ-7-(o-フルオロアニリノ)フルオラン、3-ジ-n-ペンチルアミノ-6-メチル-7-アニリノフルオラン、3-ジ-n-ペンチルアミノ-6-メチル-7-(p-クロロアニリノ)フルオラン、3-ジ-n-ペンチルアミノ-7-(m-トリフルオロメチルアニリノ)フルオラン、3-ジ-n-ペンチルアミノ-6-クロロ-7-アニリノフルオラン、3-ジ-n-ペンチルアミノ-7-(p-クロロアニリノ)フルオラン、3-ピロリジノ-6-メチル-7-アニリノフルオラン、3-ピペリジノ-6-メチル-7-アニリノフルオラン、3-(N-メチル-N-プロピルアミノ)-6-メチル-7-アニリノフルオラン、3-(N-メチル-N-シクロヘキシルアミノ)-6-メチル-7-アニリノフルオラン、3-(N-エチル-N-シクロヘキシルアミノ)-6-メチル-7-アニリノフルオラン、3-(N-エチル-N-キシルアミノ)-6-メチル-7-(p-クロロアニリノ)フルオラン、3-(N-エチル-p-トルイディノ)-6-メチル-7-アニリノフルオラン、3-(N-エチル-N-イソアミルアミノ)-6-メチル-7-アニリノフルオラン、3-(N-エチル-N-イソアミルアミノ)-6-クロロ-7-アニリノフルオラン、3-(N-エチル-N-テトラヒドロフルフリルアミノ)-6-メチル-7-アニリノフルオラン、3-(N-エチル-N-イソブチルアミノ)-6-メチル-7-アニリノフルオラン、3-(N-エチル-N-エトキシプロピルアミノ)-6-メチル-7-アニリノフルオラン、3-シクロヘキシルアミノ-6-クロロフルオラン、2-(4-オキサヘキシル)-3-ジメチルアミノ-6-メチル-7-アニリノフルオラン、2-(4-オキサヘキシル)-3-ジエチルアミノ-6-メチル-7-アニリノフルオラン、2-(4-オキサヘキシル)-3-ジプロピルアミノ-6-メチル-7-アニリノフルオラン、2-メチル-6-p-(p-ジメチルアミノフェニル)アミノアニリノフルオラン、2-メトキシ-6-p-(p-ジメチルアミノフェニル)アミノアニリノフルオラン、2-クロロ-3-メチル-6-p-(p-フェニルアミノフェニル)アミノアニリノフルオラン、2-クロロ-6-p-(p-ジメチルアミノフェニル)アミノアニリノフルオラン、2-ニトロ-6-p-(p-ジエチルアミノフェニル)アミノアニリノフルオラン、2-アミノ-6-p-(p-ジエチルアミノフェニル)アミノアニリノフルオラン、2-ジエチルアミノ-6-p-(p-ジエチルアミノフェニル)アミノアニリノフルオラン、2-フェニル-6-メチル-6-p-(p-フェニルアミノフェニル)アミノアニリノフルオラン、2-ベンジル-6-p-(p-フェニルアミノフェニル)アミノアニリノフルオラン、2-ヒドロキシ-6-p-(p-フェニルアミノフェニル)アミノアニリノフルオラン、3-メチル-6-p-(p-ジメチルアミノフェニル)アミノアニリノフルオラン、3-ジエチルアミノ-6-p-(p-ジエチルアミノフェニル)アミノアニリノフルオラン、3-ジエチルアミノ-6-p-(p-ジブチルアミノフェニル)アミノアニリノフルオラン、2,4-ジメチル-6-〔(4-ジメチルアミノ)アニリノ〕-フルオラン
3,6,6'-トリス(ジメチルアミノ)スピロ〔フルオレン-9,3'-フタリド〕、3,6,6'-トリス(ジエチルアミノ)スピロ〔フルオレン-9,3'-フタリド〕
3,3-ビス-〔2-(p-ジメチルアミノフェニル)-2-(p-メトキシフェニル)エテニル〕-4,5,6,7-テトラブロモフタリド、3,3-ビス-〔2-(p-ジメチルアミノフェニル)-2-(p-メトキシフェニル)エテニル〕-4,5,6,7-テトラクロロフタリド、3,3-ビス-〔1,1-ビス(4-ピロリジノフェニル)エチレン-2-イル〕-4,5,6,7-テトラブロモフタリド、3,3-ビス-〔1-(4-メトキシフェニル)-1-(4-ピロリジノフェニル)エチレン-2-イル〕-4,5,6,7-テトラクロロフタリド
3-(4-ジエチルアミノ-2-エトキシフェニル)-3-(1-エチル-2-メチルインドール-3-イル)-4-アザフタリド、3-(4-ジエチルアミノ-2-エトキシフェニル)-3-(1-オクチル-2-メチルインドール-3-イル)-4-アザフタリド、3-(4-シクロヘキシルエチルアミノ-2-メトキシフェニル)-3-(1-エチル-2-メチルインドール-3-イル)-4-アザフタリド、3,3-ビス(1-エチル-2-メチルインドール-3-イル)フタリド、3,6-ビス(ジエチルアミノ)フルオラン-γ-(3'-ニトロ)アニリノラクタム、3,6-ビス(ジエチルアミノ)フルオラン-γ-(4'-ニトロ)アニリノラクタム、1,1-ビス-〔2',2',2'',2''-テトラキス-(p-ジメチルアミノフェニル)-エテニル〕-2,2-ジニトリルエタン、1,1-ビス-〔2',2',2'',2''-テトラキス-(p-ジメチルアミノフェニル)-エテニル〕-2-β-ナフトイルエタン、1,1-ビス-〔2',2',2'',2''-テトラキス-(p-ジメチルアミノフェニル)-エテニル〕-2,2-ジアセチルエタン、ビス-〔2,2,2',2'-テトラキス-(p-ジメチルアミノフェニル)-エテニル〕-メチルマロン酸ジメチルエステル
酸金属塩、ワックス類、シリコーン樹脂類などが挙げられる。
本発明においては、このアクリル樹脂として、好ましくは、シラン変性アクリル系樹脂又は高Tgアクリル系樹脂を用いる。
このシラン変性アクリル系樹脂は、下記(a1)、(a2)及び(a3)を(b)の存在下で重合させて成る共重合体Aから成るコアと、下記(a1)及び(a2)を(b)の存在下で重合させて成る共重合体Bから成るシェルとから成るコアシェル型粒子の水性エマルジョンである。
(a1)少なくとも1種の(メタ)アクリル酸エステル
(a2)アルコキシシリル基及びエチレン性二重結合を有する単量体
(a3)カルボキシル基及びエチレン性二重結合を有する単量体
(b)アリル基、及びポリオキシエチレン鎖を有する硫酸塩を含有する重合性界面活性剤
この共重合体Aは、前記(a1)、(a2)及び(a3)にスチレンモノマーを加えて(b)の存在下で重合させて成ってもよく、及び/又は共重合体Bが、前記(a1)及び(a2)にスチレンモノマーを加えて(b)の存在下で重合させて成ってもよい。
本明細書では、「(メタ)アクリル酸」とは、アクリル酸とメタクリル酸の双方を示し、アクリル酸及びメタクリル酸の少なくとも1種を含むことを意味する。
「(メタ)アクリル酸エステル」とは(メタ)アクリル酸のエステル、すなわち(メタ)アクリレートをいう。(メタ)アクリレートとは、アクリレート、メタクリレートの双方を示し、アクリレート及びメタクリレートの少なくとも1種を含むことを意味する。
尚、ビニル基と酸素が結合した構造を有するビニルエステル、例えば酢酸ビニル等は、本明細書において、(メタ)アクリレートに含まれない。
これらは単独で又は2種以上併せて用いることができる。
アルコキシシリル基及びエチレン性二重結合を有する単量体とは、乳化重合反応によって得られる水性樹脂エマルション樹脂に、アルコキシシリル基を付与することができる化合物をいい、本発明に係る水性樹脂エマルションを得ることができるものであれば特に制限されるものではない。
アルコキシシリル基及びエチレン性二重結合を有する単量体は、アルコキシシリル基とエチレン性二重結合を共に有し、アルコキシシリル基とエチレン性二重結合は、例えば、エステル結合、アミド結合及びアルキレン基等の他の官能基を介して結合してよい。
ここで「アルコキシシリル基」とは、加水分解することによってケイ素に結合するヒドロキシル基(Si-OH)を与えるケイ素含有の官能基をいう。「アルコキシシリル基」として、例えば、トリメトキシシル基、トリエトキシシリル基、ジメトキシシリル基、ジメトキシメチルシリル基、ジエトキシシリル基、モノエトキシシリル基、及びモノメトキシシリル基等のアルコキシシルリ基を例示できる。特に、トリメトキシシリル基及びトリエトキシシリル基が好ましい。
尚、アルコキシシリル基及びエチレン性二重結合を有する単量体は、上述の(メタ)アクリル酸エステルに含まれない。
R11Si(OR12)(OR13)(OR14) (1)
式中、R11はエチレン性二重結合を有する官能基であり、R12、R13及びR14は、炭素数1~5のアルキル基である。R12、R13及びR14は、相互に同一でも異なってもよい。
R11のエチレン性二重結合を有する官能基として、例えば、ビニル基、(メタ)アリル基、(メタ)アクリロイルオキシ基、2-(メタ)アクリロイルオキシエチル基、2-(メタ)アクリロイルオキシプロピル基、3-(メタ)アクリロイルオキシプロピル基、2-(メタ)アクリロイルオキシブチル基、3-(メタ)アクリロイルオキシブチル基、4-(メタ)アクリロイルオキシブチルを例示できる。
「アルコキシシリル基を含有しエチレン性二重結合を有する単量体」として、ビニルトリメトキシシラン、ビニルトリエトキシシラン及びビニルトリn-ブトキシシランなどのビニルトリアルコキシシランが挙げられる。
具体的には、3-(メタ)アクリロイルオキシプロピルトリメトキシシラン及び3-(メタ)アクリロイルオキシプロピルトリエトキシシランが好ましく、特に、3-メタクリロキシプロピルトリメトキシシランが好ましい。
これらのアルコキシシリル基を含有しエチレン性二重結合を有する単量体は、単独で又は組み合わせて使用することができる。
カルボキシル基を有する単量体としては、(メタ)アクリル酸が挙げられる。上述したように、(メタ)アクリル酸とは、アクリル酸及びメタクリル酸の両方を意味する。(メタ)アクリル酸として、アクリル酸を用いることが特に好ましい。
「エチレン性二重結合」については、上述の通りである。
アリル基及びポリオキシエチレン基を有する硫酸塩としては、アリル基及びポリオキシエチレン基を有する硫酸エステルアンモニウム塩、アリル基及びポリオキシエチレン基を有する硫酸エステルナトリウム塩、アリル基及びポリオキシエチレン基を有する硫酸エステルカリウム塩が挙げられる。具体的には、ポリオキシエチレン-1-(アリルオキシメチル)アルキルエーテル硫酸エステルアンモニウム塩、ポリオキシエチレン-1-(アリルオキシメチル)アルキルエーテル硫酸エステルナトリウム塩、ポリオキシエチレン-1-(アリルオキシメチル)アルキルエーテル硫酸エステルカリウム塩;α-〔1-〔(アリルオキシ)メチル〕-2-(ノニルフェノキシ)エチル〕-ω-ポリオキシエチレン硫酸エステルアンモニウム塩、α-〔1-〔(アリルオキシ)メチル〕-2-(ノニルフェノキシ)エチル〕-ω-ポリオキシエチレン硫酸エステルナトリウム塩、α-〔1-〔(アリルオキシ)メチル〕-2-(ノニルフェノキシ)エチル〕-ω-ポリオキシエチレン硫酸エステルカリウム塩;等が挙げられる。これら硫酸塩は、単独でも複数で用いられても良い。
アリル基及びポリオキシエチレン基を有する硫酸塩の市販品として、例えば、ポリオキシエチレン-1-(アリルオキシメチル)アルキルエーテル硫酸エステルアンモニウム塩である第一工業製薬社製の「アクアロンKH-10」(商品名、ポリオキシエチレン鎖長10)、「アクアロンKH-1025」(商品名、「アクアロンKH-10」の25%水溶液);α-〔1-〔(アリルオキシ)メチル〕-2-(ノニルフェノキシ)エチル〕-ω-ポリオキシエチレン硫酸エステル塩である旭電化工業社製の「アデカリアソープ(商標)SR-1025」等が挙げられる。
「その他の単量体」の一例を以下に示すが、以下に限定されるものではない。スチレン及びスチレンスルホン酸等のスチレン系単量体;イタコン酸、フマール酸、マレイン酸等の不飽和カルボン酸及びそのエステル;及び (メタ)アクリルアミド、ダイアセトン(メタ)アクリルアミド等のアクリルアミド。
本発明のシラン変性アクリル系樹脂(水性樹脂エマルション)は、界面活性剤の存在下で、重合性不飽和単量体が多段階乳化重合することで得られる。
本発明の一つの実施態様において、重合性不飽和単量体を複数段階(実質2段階)の工程で乳化重合する。最終段以外の重合時に用いられる重合性不飽和単量体(上記a1、a2、a3及びb)を重合性不飽和単量体Aとし、得られた重合体を共重合体Aといい、最終段階の重合時に用いられる重合性不飽和単量体(上記a1、a2及びb)を重合性不飽和単量体Bとし、得られた重合体を共重合体Bという。
多段階乳化重合によって最終的に得られる水性樹脂エマルションは、重合性不飽和単量体Aが重合して得られるプレエマルションに、重合性不飽和単量体Bを重合させることで得られる。
本発明では、多段階乳化重合に用いられる重合性不飽和単量体Aは、最終段階以外で用いる重合性不飽和単量体Aと最終段階で用いる重合性不飽和単量体Bとを有し、重合性不飽和単量体Bと重合性不飽和単量体Aとの質量比(重合性不飽和単量体B/重合性不飽和単量体A)が30/70~70/30が好ましく、特に40/60~60/40が好ましい。
重合性不飽和単量体Bと重合性不飽和単量体Aとの質量比が上記割合であることによって、本発明の水性樹脂組成物(水性樹脂エマルション)は、塗工性と耐久性(耐水性、耐溶剤性)のバランスに優れたものとなる。
共重合体B中、上記a1及びa2の重合性不飽和単量体の合計重量に対する、上記a2重合性不飽和単量体の割合は、好ましくは0.01~1.0重量%、より好ましくは0.1~0.4重量%であり、残部はa1重合性不飽和単量体であるが、上記a1及びa2の重合性不飽和単量体の合計重量に対する、上記a1重合性不飽和単量体の割合は、好ましくは85~99.9重量%、より好ましくは95~99.9重量%である。
なお、共重合体A及びB(即ち、シラン変性アクリル系樹脂)の合成における、上記a1、a2及びa3の重合性不飽和単量体の合計重量に対する、(b)アリル基及びポリオキシエチレン鎖を有する硫酸塩を含有する重合性界面活性剤の割合は、該合成工程における総量で、好ましくは0.5~5重量%である。
本発明のシラン変性アクリル系樹脂(水性樹脂エマルション)は、例えば、ヘンケルジャパン株式会社から商品名:AQUENCE EPIX BC 21066として入手可能である。
先ず、反応容器に、(a1)(メタ)アクリル酸エステル 、(a2)アルコキシシリル基及びエチレン性二重結合を有する単量体 及び(a3)カルボキシル基を有する単量体を均一に混合し、重合性不飽和単量体Aの混合物を調製する。
アリル基及びポリオキシエチレン基を有する硫酸塩に水(若しくは水性媒体)を加えて水溶液とし、この水溶液に重合性不飽和単量体Aの混合物を添加し、単量体乳化物Aを調製する。
別の容器内に、単量体乳化物Aとは別に、単量体乳化物Bを調製する。単量体乳化物Bの調製は、単量体乳化物Aの調製と同様で差し支えない。具体的には、(a1)(メタ)アクリル酸エステル及び(a2)アルコキシシリル基及びエチレン性二重結合を有する単量体 を有する単量体を均一に混合し、重合性不飽和単量体Bの混合物を調製する。
アリル基及びポリオキシエチレン基を有する硫酸塩の水溶液に重合性不飽和単量体Bの混合物を添加し、単量体乳化物Bとする。
このプレエマルションに、単量体乳化物Bと触媒を滴下して重合することで、最終生成物である水性樹脂エマルションを多段階乳化重合で合成する。
ここで用いる触媒としては、例えば、過硫酸アンモニウム、過硫酸ナトリウム、過硫酸カリウム、t-ブチルペルオキシベンゾエート、2,2-アゾビスイソブチトニトリル(AIBN)及び2,2-アゾビス(2-アミジノプロパン)ジヒドロクロリド、及び2,2-アゾビス(2,4-ジメチルバレロニトリル) 等を例示することができ、特に、過硫酸アンモニウム、過硫酸ナトリウム、過硫酸カリウムが好ましい。
また、本発明で用いるアクリル系樹脂の最低造膜温度(MFT)は好ましくは25℃以下であり、より好ましくは、0℃~25℃である。最低造膜温度(MFT)が0℃~25℃の場合、特に溶剤バリア性が良好となる。
なお、アクリル系樹脂のガラス転移点(Tg)及び最低造膜温度(MFT)は示差走査熱量測定(DSC)によって測定する。
この高Tgアクリル系樹脂は、(メタ)アクリル酸、及び(メタ)アクリル酸と共重合可能な単量体成分を含み、(メタ)アクリル酸が非コアシェル型アクリル系樹脂100重量部中1~10重量部であることが好ましい。(メタ)アクリル酸は、アルカリ可溶性であり、中和剤の添加により非コアシェル型アクリル系樹脂を水溶性樹脂にする特性を有している。非コアシェル型アクリル系樹脂を水溶性樹脂に変化させることによって、特に保護層中に顔料を含有する場合、顔料への結合性が著しく向上し、多量の顔料含有下でも優れた強度を有する保護層を形成することができる。(メタ)アクリル酸と共重合可能な成分としては、例えば(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸プロピル、(メタ)アクリル酸ブチル、(メタ)アクリル酸イソブチル、(メタ)アクリル酸ペンチル、(メタ)アクリル酸ヘキシル、(メタ)アクリル酸-2-エチルへキシル、(メタ)アクリル酸オクチルなどのアクリル酸アルキル樹脂及びエポキシ樹脂、シリコーン樹脂、スチレン又はその誘導体によって変性された上記アクリル酸アルキル樹脂などの変性アクリル酸アルキル樹脂、(メタ)アクリロニトリル、アクリル酸エステル、ヒドロキシアルキルアクリル酸エステルを例示できるが、特に(メタ)アクリロニトリル及び/又はメタクリル酸メチルを配合することが好ましい。(メタ)アクリロニトリルは非コアシェル型アクリル系樹脂100部中15~70部配合することが好ましい。また、メタクリル酸メチルは非コアシェル型アクリル系樹脂100部中20~80部含むことが好ましい。(メタ)アクリロニトリル及びメタクリル酸メチルを含む場合、(メタ)アクリロニトリルを非コアシェル型アクリル系樹脂100部中15~18部、メタクリル酸メチルを非コアシェル型アクリル系樹脂100部中20~80部配合することが好ましい。
保護層中のバインダーの量又はバインダーと顔料の総量は、固形分で、通常80.0~100.0重量%、好ましくは90.0~100.0重量%であり、顔料100重量部に対してバインダーは30.0~300.0重量部程度であることが好ましい。
本発明の保護層中のアクリル系樹脂の含有量は、好ましくは5.0~80.0重量%、より好ましくは5.0~60.0重量%、更に好ましくは15.0~50.0重量%である。
また、本発明の保護層中のシラン変性アクリル系樹脂の含有量は、好ましくは10.0~70.0重量%、より好ましくは30.0~60.0重量%であり、該保護層中の高Tgアクリル系樹脂の含有量は、好ましくは5.0~50.0重量%、より好ましくは10.0~40.0重量%である。
その外の成分は、それぞれ保護層中15.0重量%、好ましくは10.0重量%を超えない。
ウムなどを例示することができる。
本発明において、保護層中に、架橋剤としてエピクロロヒドリン系樹脂及びポリアミン/ポリアミド系樹脂を、それぞれ含有させると、耐水性が特に良好となるため好ましい。
下塗り層に用いるバインダーとしては、一般的に使用されている水溶性高分子あるいは疎水性高分子のエマルジョン等が適宜使用可能である。具体例としては、ポリビニルアルコール、ポリビニルアセタール、ヒドロキシエチルセルロース、メチルセルロース、カルボキシメチルセルロース、等のセルロース誘導体、デンプンとその誘導体、ポリアクリル酸ソーダ、ポリビニルピロリドン、アクリル酸アミド/アクリル酸エステル共重合体、アクリル酸アミド/アクリル酸エステル/メタクリル酸共重合体、スチレン/無水マレイン酸共重合体アルカリ塩、イソブチレン/無水マレイン酸共重合体アルカリ塩、ポリアクリルアミド、アルギン酸ソーダ、ゼラチン、カゼイン等の水溶性高分子、ポリ酢酸ビニル、ポリウレタン、スチレン/ブタジエン共重合体、ポリアクリル酸、ポリアクリル酸エステル、塩化ビニル/酢酸ビニル共重合体、ポリブチルメタクリレート、エチレン/酢酸ビニル共重合体、スチレン/ブタジエン/アクリル系共重合体等の疎水性高分子のエマルジョンを用いることができる。これらのバインダーは1種又は2種以上用いてもよい。
下塗り層中の顔料は、全固形分100重量部に対して、通常50~95重量部、好ましくは70~90重量部である。
下塗り層の塗工液には必要に応じて、分散剤、可塑剤、pH調整剤、消泡剤、保水剤、防腐剤、着色染料、紫外線防止剤等の各種助剤を適宜配合してもよい。
感熱記録層及び感熱記録層以外の塗工層の塗工量は、要求される性能及び記録適性に従って決定され、特に限定されるものではないが、感熱記録層の一般的な塗工量は固形分で2~12g/m2程度であり、保護層の塗工量は固形分で0.5~5.0g/m2が好ましい。
また、各塗工層の塗工後にスーパーカレンダー掛けなどの平滑化処理を施すなど、感熱記録体分野における各種公知の技術を必要適宜付加することができる。
以下の製造例で、水性エマルションを(A)単量体乳化物(共重合体A)及び(B)単量体乳化物(共重合体B)から調製した。(A)及び(B)を製造するための重合性不飽和単量体、界面活性剤、及び各添加剤について以下に記載する。
尚、重合性不飽和単量体のホモポリマーTgは、文献値であり、(a)重合性不飽和単量体の共重合体のTgと(b)重合性不飽和単量体の共重合体のTgは、理論計算式で算出された値である。
メタクリル酸メチル(メチルメタクリレート、以下、「MMA」という、富士フイルム和光純薬社製、ホモポリマーのTg=105℃)
アクリル酸2-エチルヘキシル(2-エチルヘキシルアクリレート、以下、「2EHA」という、富士フイルム和光純薬社製、ホモポリマーのTg=-70℃)
アクリル酸n-ブチル(n-ブチルアクリレート、以下、「n-BA」という、富士フイルム和光純薬社製、ホモポリマーのTg=-54℃)
メタクリル酸n-ブチル(n-ブチルメタクリレート、以下、「n-BMA」という、富士フイルム和光純薬社製、ホモポリマーのTg=20℃)
メタクリル酸シクロヘキシル(シクロヘキシルメタクリレート、以下、「CHMA」という、富士フィルム和光純薬製、ホモポリマーのTg=83℃)
3-メタクリロキシプロピルトリメトキシシラン(富士フィルム和光純薬製社製)
アクリル酸(以下、「AA」という、富士フイルム和光純薬社製、ホモポリマーのTg=106℃)
スチレン(以下、「St」という、富士フイルム和光純薬社製、ホモポリマーのTg=100℃)
ポリオキシエチレン-1-(アリルオキシメチル)アルキルエーテル流酸エステルアンモニウム塩(第一工業製薬社製、アクアロンKH10)(以下「b」で表す)
複数の重合性不飽和単量体から単量体乳化物を調製し、その後、単量体乳化物からプレエマルションを調製し、プレエマルションから水性樹脂エマルションを合成した。具体的な工程は以下のとおりである。
表1に示されるように、(a1-1)MMA5質量部、(a1-3)BA23質量部、(a1-4)BMA10質量部、(a1-5)CHMA10質量部、(a2)3-メタクリロキシプロピルトリメトキシシラン0.3質量部、(a3)AA2質量部を均一に混合し、重合性不飽和単量体溶液(50.3質量部)を調製した。
水14質量部、(b)ポリオキシエチレン-1-(アリルオキシメチル)アルキルエーテル硫酸エステルアンモニウム塩0.1質量部が均一に混合された溶液に、上記重合性不飽和単量体溶液を添加し、攪拌機でこれら混合溶液を攪拌して(A)単量体乳化物を得た。
(A)表1に示されるように、(a1-1)MMA16.6質量部、(a1-3)BA13質量部、(a1-4)BMA10質量部、(a1-5)CHMA10質量部、(a2)3-メタクリロキシプロピルトリメトキシシラン0.1質量部を均一に混合し、重合性不飽和単量体溶液を調製した。
水14質量部、(b)ポリオキシエチレン-1-(アリルオキシメチル)アルキルエーテル硫酸エステルアンモニウム塩0.1質量部が均一に混合された溶液に、上記重合性不飽和単量体溶液を添加し、攪拌機でこれら混合溶液を攪拌して(B)単量体乳化物を得た。
攪拌機、コンデンサー及び温度計を備えた反応器に、水78質量部及び(b)ポリオキシエチレン-1-(アリルオキシメチル)アルキルエーテル硫酸エステルアンモニウム塩1.25質量部を仕込み、系内を窒素ガスで置換した後、その仕込み液を80℃に加熱した。
その後、その仕込み液に、(A)単量体乳化物(重合性不飽和単量体を50.3質量部含み、その重合性不飽和単量体の10.1質量部に相当する部分)、1質量%の過硫酸ナトリウム(以下、「SPS」ともいう)水溶液2質量部を添加した。
さらに10分後、反応器内の温度を80℃に保ったまま、上述の(A)単量体乳化物の残り((a)重合性不飽和単量体40.2質量部に相当する部分)及び重合触媒であるSPSの1%水溶液4質量部を各々同時に2時間かけて滴下し、プレエマルジョン((a)重合性不飽和単量体に基づく水性樹脂エマルション)を得た。
反応器内の温度を80℃に保ち、滴下終了から30分後、上述の(B)単量体乳化物(不飽和重合性単量体を49.7質量部含む)、SPSの1%水溶液4質量部を、各々同時に2時間かけて上述のプレエマルションに滴下し、水性樹脂エマルションを得た。
得られた水性樹脂エマルジョンをアンモニア水でpH8.0に調整した。水性樹脂エマルションは、(A)重合性不飽和単量体(共重合体A)ガラス転移温度が-3.8℃、(B)重合性不飽和単量体(共重合体B)のガラス転移温度が26.7℃、固形分濃度が45質量%であった。固形分は、105℃のオーブン中で3時間乾燥し、乾燥前の質量に対する残留する部分の質量百分率である。
得られた水性樹脂エマルションをシラン変性アクリル系樹脂1と呼ぶ。
表1に示す原料の単量体を用いて製造例1と同様に合成した。表中の配合に関する数字は重量部を表す。得られた水性樹脂エマルションをそれぞれシラン変性アクリル系樹脂2~3と呼ぶ。
[各塗工液の調製]
下記配合からなる配合物を攪拌分散して、下塗り層用塗工液を調製した。
<下塗り層用塗工液>
焼成カオリン(BASF社製、商品名:アンシレックス90)
100.0部
スチレン・ブタジエン共重合体ラテックス(日本ゼオン社製、
商品名:ST5526、固形分48%) 10.0部
水 50.0部
下記配合からなる配合物を攪拌分散して、下塗り層用塗工液を調製した。
<下塗り層用塗工液>
焼成カオリン(BASF社製、商品名:アンシレックス90)
100.0部
スチレン・ブタジエン共重合体ラテックス(日本ゼオン株式会社製、
商品名:ST5526、固形分48%) 10.0部
水 50.0部
N,N'-ジ-[3-(p-トルエンスルホニルオキシ)フェニル]尿素
(以下、「ウレア化合物1」という。) 6.0部
完全ケン化型ポリビニルアルコール水溶液(クラレ社製、商品名:
PVA117、固形分10%) 5.0部
水 1.5部
顕色剤分散液(A2液)
N-[2-(3-フェニルウレイド)フェニル]ベンゼンスルホンアミド
(以下、「ウレア化合物2」という。) 6.0部
完全ケン化型ポリビニルアルコール水溶液(PVA117) 5.0部
水 1.5部
顕色剤分散液(A3液)
下記化学式(化9)で表されるウレア化合物
(以下、「ウレア化合物3」という。) 6.0部
水 1.5部
式(化13)で表されるウレアウレタン系化合物
(ファインエース社製UU) 6.0部
水 1.5部
顕色剤分散液(A5液)
4-ヒドロキシ-4'-イソプロポキシジフェニルスルホン
(三菱ケミカル株式会社制、NYDS) 6.0部
完全ケン化型ポリビニルアルコール水溶液(PVA117) 5.0部
水 1.5部
3-ジブチルアミノ-6-メチル-7-アニリノフルオラン
(山本化成株式会社製、商品名:ODB-2) 6.0部
完全ケン化型ポリビニルアルコール水溶液(PVA117) 5.0部
水 1.5部
1,2-ジ(3-メチルフェノキシ)エタン
(三光社製、商品名:KS232) 6.0部
完全ケン化型ポリビニルアルコール水溶液(PVA117) 5.0部
水 1.5部
<感熱記録層用塗工液>
顕色剤分散液(A1液) 18.0部
顕色剤分散液(A2液) 18.0部
ロイコ染料分散液(B液) 18.0部
増感剤分散液(C液) 9.0部
完全ケン化型ポリビニルアルコール水溶液(PVA117) 25.0部
<保護層用塗工液1>
水酸化アルミニウム分散液(マーティンスベルグ社製、
商品名:マーティフィンOL、固形分50%) 9.0部
シラン変性アクリル系樹脂1(Tg18℃、MFT22℃、
固形分40%) 10.0部
ステアリン酸亜鉛(中京油脂社製、商品名:ハイドリンZ-7-30、
固形分30%) 2.0部
水酸化アルミニウム分散液(マーティフィンOL) 9.0部
非コアシェル型アクリル系樹脂(シラン変性なし、スチレンアクリル、
Tg55℃、MFT18℃、固形分18%) 22.2部
ステアリン酸亜鉛(ハイドリンZ-7-30) 2.0部
<保護層用塗工液3>
水酸化アルミニウム分散液(マーティフィンOL) 9.0部
完全ケン化型ポリビニルアルコール水溶液(PVA117) 40.0部
ステアリン酸亜鉛(ハイドリンZ-7-30) 2.0部
グリオキザール水溶液(日本合成化学社製、固形分40%) 3.0部
<保護層用塗工液4>
カルボキシ変性ポリビニルアルコール水溶液(クラレ社製、商品名:
KL118、固形分10%<重合度:約1700、鹸化度:
95~99モル%、酢酸ナトリウム:3%以下) 40.0部
ポリアミドエピクロロヒドリン樹脂(星光PMC社製、商品名:
WS4020、固形分25%) 4.0部
変性ポリアミン樹脂(田岡化学社製、商品名:スミレーズレジン
SPI-102A、固形分45%) 2.2部
水酸化アルミニウム分散液(マーティフィンOL) 9.0部
ステアリン酸亜鉛(ハイドリンZ-7-30) 2.0部
支持体(坪量47g/m2の上質紙)の片面に、下塗り層用塗工液を、固形分で塗工量10.0g/m2となるようにベントブレード法で塗工した後、乾燥を行ない、下塗り層塗工紙を得た。
この下塗り層塗工紙の下塗り層上に、感熱記録層用塗工液を、固形分で塗工量6.0g/m2となるようにロッドブレード法で塗工した後、乾燥を行い、感熱記録体を得た。
次いで、この感熱記録層塗工紙の感熱記録層上に、保護層塗工液1を、固形分で塗工量3.0g/m2となるようにカーテン法で塗工した後、乾燥を行ない、スーパーカレンダーで平滑度が100~500秒になるように処理して感熱記録層体を得た。
[参考例2]
保護層用塗工液1において、シラン変性アクリル系樹脂1をシラン変性アクリル系樹脂2に変更した以外は、参考例1と同様にして感熱記録体を作製した。
保護層用塗工液1において、シラン変性アクリル系樹脂1をシラン変性アクリル系樹脂3に変更した以外は、参考例1と同様にして感熱記録体を作製した。
[参考例4]
感熱記録層用塗工液において、A2液をA3液に変更した以外は、参考例1と同様にして感熱記録体を作製した。
[参考例5]
感熱記録層用塗工液において、A1液をA3液に変更した以外は、参考例1と同様にして感熱記録体を作製した。
[参考例6]
保護層用塗工液1を保護層用塗工液2に変更した以外は、参考例1と同様にして感熱記録体を作製した。
[参考例7]
感熱記録層用塗工液において、A1液の配合部数を9部に変更し、A4液9部を追加した以外は、参考例1と同様にして感熱記録体を作製した。
[実施例8]
感熱記録層用塗工液において、A2液を配合せず、A1液を36部に変更した以外は、参考例1と同様にして感熱記録体を作製した。
[実施例9]
感熱記録層用塗工液において、A1液を配合せず、A2液の配合部数を36部に変更した以外は、参考例1と同様にして感熱記録体を作製した。
[参考例10]
感熱記録層用塗工液において、A1液とA2液を配合せず、A3液36部を追加した以外は、参考例1と同様にして感熱記録体を作製した。
保護層用塗工液1を保護層用塗工液3に変更した以外は、参考例4と同様にして感熱記録体を作製した。
[比較例2]
保護層用塗工液1を保護層用塗工液4に変更した以外は、参考例4と同様にして感熱記録体を作製した。
[比較例3]
保護層を設けない外は、参考例4と同様にして感熱記録体を作製した。
[比較例4]
保護層を設けない以外は、実施例8と同様にして感熱記録体を作製した。
[比較例5]
保護層を設けない以外は、参考例1と同様にして感熱記録体を作製した。
[比較例6]
保護層を設けない以外は、参考例5と同様にして感熱記録体を作製した。
[比較例7]
感熱記録層用塗工液において、A1液とA2液を配合せず、A5液36部を追加した以外は、参考例1と同様にして感熱記録体を作製した。
<発色性能(印字濃度)>
作製した感熱記録体について、大倉電機社製のTH-PMD(感熱記録紙印字試験機、京セラ社製サーマルヘッドを装着)を用い、印字速度50mm/secで、印加エネルギー0.41mJ/dotで市松模様を印字した。印字部の印字濃度をマクベス濃度計(RD-914、アンバーフィルター使用)で測定し、発色性能(印字濃度)を評価した。
<印字走行性(耐ヘッドカス性)>
作製した感熱記録体について、サトー社製ラベルプリンタ(レスプリR-8)にて長さ60cmの格子印字を行い、印字後のサーマルヘッドに付着したカス(ヘッドカス)を目視にて下記の基準で評価した。
優:ヘッドカスの付着がほとんど見られなかった。
可:ヘッドカスの付着が少し見られたが、形成された画像の抜け及びカスレが見られず、実用上問題のない程度であった。
不可:ヘッドカスの付着が多く見られ、形成された画像の抜け及びカスレが見られた。
作製した感熱記録体について、ゼブラ社製ラベルプリンタ140XiIIIを用い、印字レベル+10、印字速度25.4cm/秒(10インチ/秒)で、バーコード(CODE39)を縦方向(プリンタヘッドの移動方向とバーコードが直交)に印字した。
次いで、印字されたバーコードをバーコード検証機(Honeywell社製、QCPC600、光源640nm)で読み取り試験を実施し、バーコード読み取り適性を評価した。評価結果をANSI規格のシンボルグレードで記した。
シンボルグレード:バーコードをバーと垂直方向に10分割して、各箇所1回ずつ読み取り試験を実施し、その平均値を(優)A、B、C、D、F(劣)の5段階評価で表す。
<耐油性>
作製した感熱記録体について、大倉電機社製のTH-PMD(感熱記録紙印字試験機、京セラ社製サーマルヘッドを装着)を用い、印加エネルギー0.41mJ/dot、印字速度50mm/secで市松模様を印字した。
印字した感熱記録体に、サラダ油を綿棒で塗布し、24時間放置した後、印字部の印字濃度をマクベス濃度計(RD-914、アンバーフィルター使用)で測定した。
作製した感熱記録体の白紙部に、エタノール(99.5%)を綿棒で塗布し、23℃×50%RH環境条件下に24時間静置した後、以下の基準で目視評価した。
優:全く発色しない
可:僅かに発色する
不可:強く発色する
<湿潤摩擦>
作製した感熱記録体について、水道水を指につけて、保護層の表面を80往復摩擦し、保護層及び感熱記録層の剥がれを以下の基準で目視評価した。
優:保護層及び感熱記録層の剥がれが全くない
可:保護層が僅かに剥がれるが、感熱記録層の剥がれはない
不可:保護層及び感熱記録層が剥がれる
作製した感熱記録体について、保護層の表面に10mlの水道水を滴下し、保護層の表面が内側になるように二つ折りにして、20gf/cm2の加重を掛けて24時間静置した後に剥がし、水を滴下した部分の保護層及び感熱記録層の剥がれを以下の基準で目視評価した。
優:ブロッキングが全く発生せず、保護層及び感熱記録層の剥がれが全くない
可:ブロッキングが発生し、保護層が僅かに剥がれるが、感熱記録層の剥がれはない
不可:強いブロッキングが発生し、保護層及び感熱記録層が剥がれる
又は、剥がす際に感熱記録体が破壊される
<浸漬摩擦>
作製した感熱記録体について、水道水に10分間浸漬し、保護層の表面を指で20往復摩擦し、保護層及び感熱記録層の剥がれを以下の基準で目視評価した。
優:保護層及び感熱記録層の剥がれが全くない
可:保護層が僅かに剥がれるが、感熱記録層の剥がれはない
不可:保護層及び感熱記録層が剥がれる
すなわち、本発明は、支持体上に、無色ないし淡色の電子供与性ロイコ染料及び電子受容性顕色剤を含有する感熱記録層及び該感熱記録層上に保護層を有する感熱記録体において、該感熱記録層が、電子受容性顕色剤として、下記(1)又は(2)で表されるウレア化合物を含有し、該保護層が、下記(4)又は(5)で表されるアクリル系樹脂を含有し、該保護層中の該アクリル系樹脂の含有量が15.0~50.0重量%であり、該アクリル系樹脂の最低造膜温度(MFT)が0℃~25℃である、感熱記録体である。
(1)下記一般式(化5)で表される第1のウレア化合物、
(2)下記一般式(化3)で表される第2のウレア化合物、
(4)ガラス転移点(Tg)が50℃より高く95℃以下である非コアシェル型アクリル系樹脂
(5)下記(a1)、(a2)及び(a3)を(b)の存在下で重合させて成る共重合体Aから成るコアと、下記(a1)及び(a2)を(b)の存在下で重合させて成る共重合体Bから成るシェルとから成るコアシェル型粒子の水性エマルジョンである、シラン変性アクリル系樹脂。
(a1)少なくとも1種の(メタ)アクリル酸エステル
(a2)アルコキシシリル基及びエチレン性二重結合を有する単量体
(a3)カルボキシル基及びエチレン性二重結合を有する単量体
(b)アリル基及びポリオキシエチレン鎖を有する硫酸塩を含有する重合性界面活性剤
Claims (9)
- 支持体上に、無色ないし淡色の電子供与性ロイコ染料及び電子受容性顕色剤を含有する感熱記録層及び該感熱記録層上に保護層を有する感熱記録体において、該感熱記録層が、電子受容性顕色剤として、下記(1)又は(2)で表されるウレア化合物を含有し、該保護層が、下記(4)又は(5)で表されるアクリル系樹脂を含有し、該保護層中の該アクリル系樹脂の含有量が15.0~50.0重量%であり、該アクリル系樹脂の最低造膜温度(MFT)が0℃~25℃である、感熱記録体。
(1)下記一般式(化5)で表されるウレア化合物、
(2)下記一般式(化3)で表される第2のウレア化合物、
(4)ガラス転移点(Tg)が50℃より高く95℃以下である非コアシェル型アクリル系樹脂
(5)下記(a1)、(a2)及び(a3)を(b)の存在下で重合させて成る共重合体Aから成るコアと、下記(a1)及び(a2)を(b)の存在下で重合させて成る共重合体Bから成るシェルとから成るコアシェル型粒子の水性エマルジョンである、シラン変性アクリル系樹脂。
(a1)少なくとも1種の(メタ)アクリル酸エステル
(a2)アルコキシシリル基及びエチレン性二重結合を有する単量体
(a3)カルボキシル基及びエチレン性二重結合を有する単量体
(b)アリル基及びポリオキシエチレン鎖を有する硫酸塩を含有する重合性界面活性剤 - 前記第1のウレア化合物において、R9が炭素数が1~4のアルキル基を表し、oが0~1の整数を表し、ベンゼン環中のR9の位置が4位である、請求項2に記載の感熱記録体。
- 前記感熱記録層中のウレア化合物の含有量(固形分)の総量が1.0~70.0重量%である、請求項1~4のいずれか一項に記載の感熱記録体。
- 前記感熱記録層中の前記第1のウレア化合物の含有量(固形分)が1.0~50.0重量%である、請求項5に記載の感熱記録体。
- 前記感熱記録層中の前記第2のウレア化合物の含有量(固形分)が5.0~50.0重量%である、請求項5又は6に記載の感熱記録体。
- 前記感熱記録層が、第1のウレア化合物及び第2のウレア化合物以外の顕色剤を含有し、前記感熱記録層中に含有される全顕色剤に対する、第1のウレア化合物及び第2のウレア化合物の合計含有量(固形分)が90重量%以上である、請求項1~7のいずれか一項に記載の感熱記録体。
- 前記保護層中のアクリル樹脂の含有量(固形分)が15.0~50.0重量%である、請求項1~8のいずれか一項に記載の感熱記録体。